The present invention relates to a novel organic silver complex prepared by reacting a silver compound with an ammonium carbamate compound or an ammonium carbonate compound and a preparation method thereof.
According to Ullmann's Encyclopedia of Ind. Chem., Vol. A24, 107 (1993), silver is a precious metal resistant to oxidation, with superior electrical and thermal conductivity and catalytic and antibiotic activity. Thus, silver and silver compounds are widely used in alloys, plating, medicine, photography, electricity and electronics, fibers, detergents, household appliances, and so forth.
Silver compounds can be used as catalyst in synthesis of organic compounds and polymers. Especially, with the recent regulation of use of lead in electric and electronic circuits, use of silver in low-resistance metal wirings, printed circuit boards (PCB), flexible printed circuit boards (FPC), antennas for radio frequency identification (RFID) stags, plasma display panels (PDP), liquid crystal displays (TFT-LCD), organic light emitting diodes (OLED), flexible displays and organic thin-film transistors (OTFT) as metal patterns or electrodes is on the increase.
Mostly, silver is used in the form of a paste comprising silver powder, a binder and a solvent. Or, a silver compound such as silver nitrate is reacted with another compound in an aqueous solution or an organic solvent to obtain a variety of silver compounds or organic silver compounds containing nanoparticles. These organic silver compounds are used to form metal patterns by chemical vapor deposition (CVD), plasma vapor deposition, sputtering, electroplating, photolithography, electron beam technique, laser technique, etc.
The most common coordinator for organic silver complexes is carboxylic acid (Prog. Inorg. Chem., 10, p. 233 (1968)). However, because silver-containing metal carboxylate complexes are generally sensitive to light, hardly soluble in organic solvents (J. Chem. Soc., (A), p. 514 (1971), U.S. Pat. No. 5,534,312 (Jul. 9, 1996)) and have a high decomposition temperature, they are limited in application in spite of easiness in preparation. To solve this problem, several methods have been proposed in J. Inorg. Nucl. Chem., 40, p. 1599 (1978), Ang. Chem., Int. Ed. Engl., 31, p. 770 (1992), Eur. J. Solid State Inorg. Chem., 32, p. 25 (1995), J. Chem. Cryst., 26, p. 99 (1996), Chem. Vapor Deposition, 7, 111 (2001), Chem. Mater., 16, 2021 (2004), U.S. Pat. No. 5,705,661 (Jan. 6, 1998) and Korean Patent No. 2003-0085357 (Nov. 5, 2003). Among them are the methods of using carboxylic acid compounds having long alkyl chains or including amine compounds or phosphine compounds. However, the silver derivatives known thus far are limited and have insufficient stability or solubility. Moreover, they have a high decomposition temperature to be applied for pattern formation and are decomposed slowly.
U.K. Patent No. 609,807 published in 1948 discloses a method of reacting ammonium carbonate or ammonium carbamate with a transition metal salt to obtain a transition metal salt coordinated by ammonia as carbon dioxide is generated. The patent mentions that silver complexes coordinated by ammonia can be prepared by the method. However, surprisingly, the present inventors found out that when ammonium carbonate or ammonium carbamate is added to a silver compound such as silver oxide, a stable silver complex is obtained without generation of carbon dioxide. They also confirmed that the silver complex is isolated as solid and can be easily prepared into thin film.
The silver complexes of the present invention are characterized in that, because they can be prepared under various reaction conditions, they have superior stability and solubility, can be easily prepared into thin film, thus enabling ease metal patterning, and are decomposed at low temperature, thus being easily prepared into thin film or powder.
It is an object of the present invention to provide a novel organic silver complex obtained by reacting a silver compound with an ammonium carbamate compound or an ammonium carbonate compound and a preparation method thereof.
It is another object of the present invention to provide a novel organic silver complex having superior stability and solubility and being easily prepared into thin film and a preparation method thereof.
It is still another object of the present invention to provide a novel organic silver complex which enables formation of high-purity metal film since it is decomposed at low temperature and a preparation method thereof.
In order to attain the objects, the present inventors invented novel organic silver complexes by reacting the silver compound represented by the formula 2 below with the ammonium carbamate compound or ammonium carbonate compound represented by the formula 3, 4 or 5 below:
wherein, in the formula 2, n is an integer from 1 to 4, X is oxygen, sulfur, halogen, cyano, cyanate, carbonate, nitrate, nitrite, sulfate, phosphate, thiocyanate, chlorate, perchlorate, tetrafluoroborate, acetylacetonate or carboxylate (For example, the silver compound may be silver oxide, thiocyanate, silver sulfide, silver chloride, silver cyanide, silver cyanate, silver carbonate, silver nitrate, silver nitrite, silver sulfate, silver phosphate, silver perchlorate, silver tetrafluoroborate, silver acetylacetonate, silver acetate, silver lactate, silver oxalate or a derivative thereof. Silver oxide or silver carbonate is preferred with regard to reactivity or post-treatment, although not limited to them), and
in the formulas 3 to 5, each of R1, R2, R3, R4, R5 and R6 is independently hydrogen, C1-C30 aliphatic or cycloaliphatic alkyl, aryl or aralkyl, substituted alkyl or aryl, where R1 and R2 and, independently, R4 and R5 may form an alkylene ring containing or not containing a hetero atom, a polymer compound or a derivative thereof (Although not limiting the present invention, it is preferred that each of R1 and R4 is C1-C14 aliphatic alkyl and each of R3, R4, R5 and R6 is hydrogen or C1-C14 aliphatic alkyl).
Specifically, in the formulas 3 to 5, each of R1, R2, R3, R4, R5 and R6 may be hydrogen, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, amyl, hexyl, ethylhexyl, heptyl, octyl, isooctyl, nonyl, decyl, dodecyl, hexadecyl, octadecyl, docodecyl, cyclopropyl, cyclopentyl, cyclohexyl, allyl, hydroxy, methoxy, methoxyethyl, methoxypropyl, cyanoethyl, ethoxy, butoxy, hexyloxy, methoxyethoxyethyl, methoxyethoxyethoxyethyl, hexamethyleneimine, morpholine, piperidine, piperazine, ethylenediamine, propylenediamine, hexamethylenediamine, triethylenediamine, pyrrole, imidazole, pyridine, carboxymethyl, trimethoxysilylpropyl, triethoxysilylpropyl, phenyl, methoxyphenyl, cyanophenyl, phenoxy, tolyl, benzyl, a derivative thereof, a polymer compound such as polyallylamine and polyethyleneimine or a derivative thereof, but not particularly limited to them.
The ammonium carbamate compound represented by the formula 3 may be, for example, ammonium carbamate, ethylammonium ethylcarbamate, isopropylammonium isopropylcarbamate, n-butylammonium n-butylcarbamate, isobutylammonium isobutylcarbamate, t-butylammonium t-butylcarbamate, 2-ethylhexylammonium 2-ethylhexylcarbamate, octadecylammonium octadecylcarbamate, 2-methoxyethylammonium 2-methoxyethylcarbamate, 2-cyanoethylammonium 2-cyanoethylcarbamate, dibutylammonium dibutylcarbamate, dioctadecylammonium dioctadecylcarbamate, methyldecylammonium methyldecylcarbamate, hexamethyleneiminium hexamethyleneiminecarbamate, morpholinium morpholinecarbamate, pyridinium ethylhexylcarbamate, triethylenediaminium isopropylbicarbamate, benzylammonium benzylcarbamate, triethoxysilylpropylammonium triethoxysilylpropylcarbamate, etc.
For the ammonium carbamate compound of the present invention, one substituted by primary amine is preferred to those substituted by secondary or tertiary amine in terms of reactivity and stability.
The ammonium carbonate compound represented by the formula 4 or formula 5 may be, for example, ammonium carbonate, ammonium bicarbonate, ethylammonium ethylcarbonate, isopropylammonium isopropylcarbonate, isopropylammonium bicarbonate, n-butylammonium n-butylcarbonate, isobutylammonium isobutylcarbonate, t-butylammonium t-butylcarbonate, t-butylammonium bicarbonate, 2-ethylhexylammonium 2-ethylhexylcarbonate, 2-ethylhexylammonium bicarbonate, 2-methoxyethylammonium 2-methoxyethylcarbonate, 2-methoxyethylammonium bicarbonate, 2-cyanoethylammonium 2-cyanoethylcarbonate, 2-cyanoethylammonium bicarbonate, octadecylammonium octadecylcarbonate, dibutylammonium dibutylcarbonate, dioctadecylammonium dioctadecylcarbonate, dioctadecylammonium bicarbonate, methyldecylammonium methyldecylcarbonate, hexamethyleneiminium hexamethyleneiminecarbonate, morpholinium morpholinecarbonate, benzylammonium benzylcarbonate, triethoxysilylpropylammonium triethoxysilylpropylcarbonate, pyridinium bicarbonate, triethylenediaminium isopropylcarbonate, triethylenediaminium bicarbonate or a derivative thereof.
The ammonium carbamate compound, the ammonium carbonate compound and preparation method thereof are not particularly limited. For example, J. Am. Chem. Soc., 70, p. 3865 (1948), J. Am. Chem. Soc., 73, p. 1829 (1951), J. Prakt. Chem., 9, p. 217 (1959), J. Am. Chem. Soc., 123, p. 10393 (2001), Langmuir, 18, 7124 (2002) and U.S. Pat. No. 4,542,214 (Sep. 17, 1985) disclose that the compounds can be prepared from primary amine, secondary amine, tertiary amine or a mixture thereof and carbon dioxide. According to the disclosure, an ammonium carbonate compound is obtained if 0.5 mole of carbon dioxide is used per 1 mole of amine and an ammonium bicarbonate compound is obtained if more than 1 mole of carbon dioxide is used per 1 mole of amine. The preparation may be performed under normal pressure or applied pressure with or without a solvent. When a solvent is used, an alcohol such as methanol, ethanol, isopropanol and butanol, a glycol such as ethylene glycol and glycerine, an acetate such as ethyl acetate, butyl acetate and carbitol acetate, an ether such as diethyl ether, tetrahydrofuran and dioxane, a ketone such as methyl ethyl ketone and acetone, a hydrocarbon solvent such as hexane and heptane, an aromatic solvent such as benzene and toluene, a halogen-substituted solvent such as chloroform, methylene chloride and carbon tetrachloride, etc. may be used. Carbon dioxide may be bubbled in the gas phase or solid dry ice may be used. The reaction may be performed in the supercritical state. Any other known methods can be applied for the preparation of the ammonium carbamate derivative and the ammonium carbonate derivative, as long as the structure of the target compound is the same. That is, preparation solvent, reaction temperature, concentration, catalyst, etc. are not particularly limited. And, the preparation yield is irrelevant of the preparation method.
Such prepared ammonium carbamate compound or ammonium carbonate compound is reacted with the silver compound to obtain the organic silver complex. For example, at least one silver compound represented by the formula 2 may be reacted with at least one ammonium carbamate derivative or ammonium carbonate derivative represented by the formulas 3 to 5 under nitrogen atmosphere at normal pressure or applied pressure with or without a solvent. When a solvent is used, an alcohol such as methanol, ethanol, isopropanol and butanol, a glycol such as ethylene glycol and glycerine, an acetate such as ethyl acetate, butyl acetate and carbitol acetate, an ether such as diethyl ether, tetrahydrofuran and dioxane, a ketone such as methyl ethyl ketone and acetone, a hydrocarbon solvent such as hexane and heptane, an aromatic solvent such as benzene and toluene, halogen-substituted solvent such as chloroform, methylene chloride and carbon tetrachloride, etc. may be used. However, the solvent used in the preparation of the organic silver complex of the present invention needs not be particularly limited. That is, any other solvent may be used as long as the structure of the target compound is the same.
The silver complex of the present invention has the structure represented by the following formula 1:
Ag[A]m (1)
where A is the compound represented by the formula 3, 4 or 5 and 0.7≦m≦2.5.
The silver complexes of the present invention are isolated as white solid. When decomposed by heating, the resultant compounds contain conductive, non-valent silver, not in the oxidized state. The IR spectrums (
The silver complexes of the present invention show specific melting points and decomposition patterns as seen in the TGA thermograms and the DSC thermograms (
The organic silver complex of the present invention is highly soluble in a variety of solvents including ones used to prepare the organic silver complex, for example, an alcohol such as methanol, an ester such as ethyl acetate, an ether such as tetrahydrofuran, etc. Thus, the silver complex can be readily used in coating or printing and can be stably stored in the form of solution for over 3 months.
The organic silver complex solution may be prepared into thin film by coating on a substrate of glass, silicon wafer, polymer film like polyester and polyimide, paper, etc. or printed directly. The thin film formation may be performed by spin coating, roll coating, spray coating, dip coating, flow coating, etc. And, the printing may be performed by ink-jet printing, offset printing, screen printing, gravure printing, flexo printing, etc.
The prepared thin film may be oxidized, reduced or heat-treated or the organic silver complex may be treated with chemical vapor deposition (CVD), plasma vapor deposition, sputtering, electroplating, lithography, IR, electron beam or laser to obtain a metal or metal oxide pattern. The heat treatment may be performed under inert gas atmosphere, as usually, but also may be performed in air or using a mixture gas of hydrogen and air or other inert gas.
Hereinafter, the present invention is described in further detail through examples. However, the following examples are only for the understanding of the present invention and the present invention is not limited to or by them.
In a 50 mL Schlenk flask equipped with a stirrer, 3.25 g (10.75 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter to remove unreacted silver oxide. Then, the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 4.22 g of a silver complex (yield=99.4%). The silver complex had a melting point of 57-58° C. (DSC=57.26° C.) and a silver content of 22.0 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 1.11-1.19 (m, —CH3) 1.51-1.69 (m, —CH2, —CH), 2.91-2.92, 3.23-3.25 (d, —NCH2), 5.13 (s, —NH2), 13C NMR (CD3OD, ppm), 166.09, 47.60, 44.24, 31.76, 30.12, 24.77, 24.30, 14.64, 11.15
In a 50 mL Schlenk flask equipped with a stirrer, 1.74 g (10.75 mmol) of n-propylammonium n-propylcarbamate (viscous liquid, melting point: 74-76° C.) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature for 2 hours while stirring. A colorless, transparent complex solution was obtained as in Example 1. The resultant solution was filtered with a 0.45 micron membrane filter to remove and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.42 g of a silver complex (yield=88.3%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 38.4 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 0.98-1.02 (t, —CH3) 1.59-1.65 (m, —CH2), 2.76-2.80 (t, —NCH2), 13C NMR (CD3OD, ppm), 47.03, 27.84, 11.53
In a 50 mL Schlenk flask equipped with a stirrer, 1.60 g (10.75 mmol) of isopropylammonium isopropylcarbamate (white solid, melting point: 78-80° C.) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.48 g of a silver complex (yield=95.5%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 37.2 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 1.13-1.22 (d, —CH3), 3.22-3.31 (m, CH), 13C NMR (CD3OD, ppm), 45.78, 26.06
In a 50 mL Schlenk flask equipped with a stirrer, 2.04 g (10.75 mmol) of n-butylammonium n-butylcarbamate (white solid, melting point: 82-84° C.) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.79 g of a silver complex (yield=92.0%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 33.2 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 0.92-0.97 (t, —CH3), 1.37-1.46 (m, —CH2), 1.52-1.59 (m, —CH2), 2.75-2.79 (t, —NCH2), 13C NMR (CD3OD, ppm), 161.46, 44.76, 36.94, 21.05, 14.38
In a 50 mL Schlenk flask equipped with a stirrer, 2.04 g (10.75 mmol) of isobutylammonium isobutylcarbamate (white solid, melting point: 80-82° C.) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.87 g of a silver complex (yield=94.4%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 32.4 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 0.96-0.98 (d, —CH3), 1.67-1.74 (m, —CH), 2.59-2.88 (dd, —CH2), 13C NMR (CD3OD, ppm), 161.48, 52.69, 33.16, 30.45, 20.42
In a 50 mL Schlenk flask equipped with a stirrer, 2.04 g (10.75 mmol) of t-butylammonium t-butylcarbamate (white solid) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.94 g of a silver complex (yield=97.0%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 31.4 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 1.27 (s, —CH3), 13C NMR (CD3OD, ppm), 161.52, 50.94, 32.28
In a 50 mL Schlenk flask equipped with a stirrer, 3.27 g (10.80 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (3.60 mmol) of silver carbonate was added. The reaction solution was initially a yellow slurry but it turned transparent as reaction proceeded. After 5 hours of reaction, a yellow, transparent solution was obtained, which confirmed production of a complex. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 4.18 g of a silver complex (yield=97.89%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 18.66 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 1.11-1.19 (m, —CH3) 1.51-1.69 (m, —CH2, —CH—), 2.91-2.92, 3.23-3.25 (d, —NCH2), 5.13 (t, —NHx), 13C NMR (CD3OD, ppm), 166.09, 47.60, 44.24, 31.76, 30.12, 24.77, 24.30, 14.64, 11.15
In a 50 mL Schlenk flask equipped with a stirrer, 2.17 g (11.18 mmol) of 2-methoxyethylammonium 2-methoxyethylcarbamate (white solid, melting point: 41-42° C.) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain brown, viscous liquid. The liquid was dried and weighed to obtain 2.58 g of a silver complex (yield=81.4%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 35.9 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 2.93-2.96 (t, —NCH2), 3.39 (s, —OCH3), 3.48-3.50 (t, OCH2), 13C NMR (CD3OD, ppm), 161.48, 74.11, 59.35, 44.34
In a 50 mL Schlenk flask equipped with a stirrer, 1.78 g (12.90 mmol) of 2-hydroxyethylammonium 2-hydroxyethylcarbamate was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain brown, viscous liquid. The liquid was dried and weighed to obtain 2.50 g of a silver complex (yield=90.1%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 37.1 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 2.82-2.85 (t, —NCH2), 3.61-3.64 (t, OCH2), 13C NMR (CD3OD, ppm), 166.16, 63.70, 46.12
In a 50 mL Schlenk flask equipped with a stirrer, 2.40 g (12.90 mmol) of 2-cyanoethylammonium 2-cyanoethylcarbamate (white solid, melting point: 70-72° C.) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.06 g of a silver complex (yield=90.0%). About 60% of the silver complex was decomposed below 150° C. to leave metallic silver and unreacted organic materials. Most of the silver complex was decomposed below 250° C. to leave metallic silver. The silver content was 28.7 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.81 g (12.90 mmol) of morpholinium morpholinecarbamate was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain gray solid. The solid was dried and weighed to obtain 3.29 g of a silver complex (yield=86.4%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 28.3 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.13 g (12.90 mmol) of hexamethyleneiminium hexamethyleneiminecarbamate was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain brown liquid. The liquid was dried and weighed to obtain 3.29 g of a silver complex (yield=86.8%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 25.9 wt % (TGA analysis).
In a 250 mL Schlenk flask equipped with a stirrer, 6.71 g (86 mmol) of ammonium carbamate and 15 g of isopropylamine (0.25 mol) were dissolved in 50 mL of methanol. 10.0 g (43.1 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 3 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 26.90 g of a silver complex (yield=84.9%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 42.0 wt % (TGA analysis).
In a 250 mL Schlenk flask equipped with a stirrer, 3.36 g (43 mmol) of ammonium carbamate and 15 g of isopropylamine (0.25 mol) were dissolved in 50 mL of methanol. 11.88 g (43.1 mmol) of silver carbonate was added and reaction was performed at room temperature. The reaction solution was initially a yellow slurry but it turned transparent as complex was produced. After 6 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 25.60 g of a silver complex (yield=84.5%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 45.8 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.25 g (10.75 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of tetrahydrofuran (THF). 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.58 g of a silver complex (yield=88.23%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 25.97 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.25 g (10.75 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of ethyl acetate. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained.
The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.53 g of a silver complex (yield=83.17%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 26.34 wt % (TGA analysis).
To a 50 mL Schlenk flask equipped with a stirrer was added 3.90 g (12.90 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid). 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and kept at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.58 g of a silver complex (yield=88.23%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 25.97 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 1.763 g (10.75 mmol) of aminoethylammonium aminoethylcarbamate (white solid) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain black, viscous liquid. The liquid was dried and weighed to obtain 2.21 g of a silver complex (yield=79.99%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 42.12 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.07 g (10.80 mmol) of a 6:1 (molar ratio) mixture of 2-ethylhexylammonium 2-ethylhexylcarbamate and aminoethylammonium aminoethylcarbamate was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain orange, viscous liquid. The liquid was dried and weighed to obtain 3.85 g of a silver complex (yield=94.59%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 24.20 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.42 g (8.00 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of methanol. 1.0 g (3.2 mmol) of silver sulfate was added and reaction was performed at room temperature. The reaction solution was initially a white slurry but it turned transparent as complex was produced. After 2 hours, a completely transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 3.15 g of a silver complex (yield=92.3%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 21.35 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.23 g (7.37 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of methanol. 1.0 g (5.9 mmol) of silver nitrate was added and reaction was performed at room temperature. The reaction solution was initially a white slurry but it turned transparent as complex was produced. After 2 hours, a completely transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 2.76 g of a silver complex (yield=85.6%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 22.73 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.83 g (9.37 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of dimethylsulfoxide (DMSO). 1 g (7.5 mmol) of silver cyanide was added and reaction was performed at room temperature. The reaction solution was initially a white slurry but it turned transparent as complex was produced. After 2 hours, a completely transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 3.15 g of a silver complex (yield=82.42%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 25.43 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.72 g (11.61 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbamate (viscous liquid) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter to remove unreacted silver oxide particles and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 4.02 g of a silver complex (yield=85.2%). The silver complex had a melting point of 55-57° C. (DSC=57.34° C.) and a silver content of 21.43 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 0.87-0.99 (m, —CH3) 1.31-1.47 (m, —CH2, —CH—), 2.69-2.70, 3.01-3.02 (d, —NCH2), 4.90 (s, —NH2), 13C NMR (CD3OD, ppm), 165.00, 47.70, 44.25, 31.73, 30.90, 24.73, 24.29, 14.68, 11.16
In a 50 mL Schlenk flask equipped with a stirrer, 4.86 g (25.37 mmol) of 2-ethylhexylammonium bicarbonate (viscous liquid) was dissolved in 10 mL of methanol. 1.0 g (4.31 mmol) of silver oxide was added and reaction was performed at room temperature. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 4.33 g of a silver complex (yield=73.9%). The silver complex had a melting point of 56-57° C. (DSC=57.66° C.) and a silver content of 21.48 wt % (TGA analysis).
1H NMR (CD3OD, ppm), 0.93-1.08 (m, —CH3) 1.31-1.64 (m, —CH2, —CH—), 2.93-2.94, 3.25-3.26 (d, —NCH2), 5.13 (s, —NH2), 13C NMR (CD3OD, ppm), 165.56, 47.73, 44.23, 31.713, 30.08, 24.72, 24.28, 14.69, 11.17
In a 50 mL Schlenk flask equipped with a stirrer, 2.01 g (11.18 mmol) of isopropylammonium isopropylcarbonate was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.41 g of a silver complex (yield=80.2%). Most of the silver complex was decomposed below 130° C. and the silver content was 38.6 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.07 g (11.52 mmol) of isopropylammonium isopropylcarbonate was dissolved in 10 mL of methanol and 1.0 g (3.60 mmol) of silver carbonate was added. The reaction solution was initially a yellow slurry but it turned transparent as complex was produced. After 6 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.42 g of a silver complex (yield=78.8%). Most of the silver complex was decomposed below 130° C. and the silver content was 32.23 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.46 g (14.4 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (3.60 mmol) of silver carbonate was added. The reaction solution was initially a yellow slurry but it turned transparent as complex was produced. After 6 hours, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 4.15 g of a silver complex (yield=93.04%). Most of the silver complex was decomposed below 130° C. and the silver content was 18.79 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.97 g (24.51 mmol) of isopropylammonium bicarbonate (melting point: 53-54° C.) was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 2.41 g of a silver complex (yield=60.7%). The silver complex had a melting point of 68-70° C. (DSC=70.49° C.). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 38.58 wt % (TGA analysis).
In a 250 mL Schlenk flask equipped with a stirrer, 8.26 g (86 mmol) of ammonium carbonate and 15 g (0.25 mol) of isopropyl amine were dissolved in 50 mL of methanol and 10.0 g (43.1 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 28.38 g of a silver complex (yield=85.5%). The silver complex had a melting point (DSC) of 63.38° C. Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 46.3 wt % (TGA analysis).
In a 250 mL Schlenk flask equipped with a stirrer, 4.13 g (43 mmol) of ammonium carbonate and 15 g (0.25 mol) of isopropyl amine were dissolved in 50 mL of methanol and 11.88 g (43.1 mmol) of silver carbonate was added. The reaction solution was initially a yellow slurry but it turned transparent as complex was produced. After 6 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 26.71 g of a silver complex (yield=85.9%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 47.8 wt % (TGA analysis).
In a 250 mL Schlenk flask equipped with a stirrer, 6.8 g (86 mmol) of ammonium bicarbonate and 15 g (0.25 mol) of isopropyl amine were dissolved in 50 mL of methanol and 10.0 g (43.1 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 3 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 26.55 g of a silver complex (yield=83.5%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 46.8 wt % (TGA analysis).
In a 250 mL Schlenk flask equipped with a stirrer, 3.4 g (43 mmol) of ammonium bicarbonate and 15 g (0.25 mol) of isopropyl amine were dissolved in 50 mL of methanol and 11.88 g (43.1 mmol) of silver carbonate was added. The reaction solution was initially a yellow slurry but it turned transparent as complex was produced. After 6 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 26.20 g of a silver complex (yield=86.2%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 48.2 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.24 g (23.65 mmol) of 2-methoxyethylammonium bicarbonate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain yellow, viscous liquid. The liquid was dried and weighed to obtain 3.01 g of a silver complex (yield=70.75%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 31.08 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.78 g (27.54 mmol) of 2-methoxyethylammonium bicarbonate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (3.60 mmol) of silver carbonate was added. The reaction solution was initially a yellow slurry but it turned transparent as complex was produced. After 2 hours, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain yellow, viscous liquid. The liquid was dried and weighed to obtain 3.28 g of a silver complex (yield=68.61%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 23.78 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.07 g (24.73 mmol) of octylammonium bicarbonate (white solid) was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.81 g of a silver complex (yield=93.61%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 24.40 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.20 g (23.65 mmol) of isobutylammonium bicarbonate (white solid) was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.21 g of a silver complex (yield=76.42%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 28.97 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.20 g (23.65 mmol) of viscous n-butylammonium bicarbonate was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 6 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.49 g of a silver complex (yield=83.09%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 26.72 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.53 g (23.65 mmol) of morpholinium bicarbonate (white solid) was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.16 g of a silver complex (yield=69.75%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 29.49 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 4.13 g (12.90 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) was dissolved in 10 mL of tetrahydrofuran (THF) and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 4.05 g of a silver complex (yield=78.84%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 22.96 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 4.13 g (12.90 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) was dissolved in 10 mL of ethyl acetate and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.96 g of a silver complex (yield=77.19%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 23.48 wt % (TGA analysis).
Into a 50 mL Schlenk flask equipped with a stirrer were added 4.13 g (12.90 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) and 1.0 g (4.31 mmol) of silver oxide. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a yellow, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was dried and weighed to obtain 3.96 g of a silver complex (yield=77.19%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 23.48 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.35 g (12.90 mmol) of aminoethylammonium aminoethylcarbonate (white solid) was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain black, viscous liquid. The liquid was dried and weighed to obtain 2.42 g of a silver complex (yield=72.23%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 38.45 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.87 g (12.9 mmol) of a 6:1 (molar ratio) mixture of 2-ethylhexylammonium 2-ethylhexylcarbonate and aminoethylammonium aminoethylcarbonate was dissolved in 10 mL of methanol and 1.0 g (4.31 mmol) of silver oxide was added. The reaction solution was initially a black slurry but it turned transparent as complex was produced. After 2 hours of reaction, a colorless, transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain orange, viscous liquid. The liquid was dried and weighed to obtain 3.05 g of a silver complex (yield=78.85%). Most of the silver complex was decomposed below 130° C. to leave metallic silver. The silver content was 30.41 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.07 g (9.60 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (3.2 mmol) of silver sulfate was added. The reaction solution was initially a white slurry but it turned transparent as complex was produced. After 2 hours, a completely transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 3.55 g of a silver complex (yield=87.2%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 19.52 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 2.84 g (8.86 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (5.9 mmol) of silver nitrate was added. The reaction solution was initially a white slurry but it turned transparent as complex was produced. After 2 hours, a completely transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 3.12 g of a silver complex (yield=81.34%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 19.88 wt % (TGA analysis).
In a 50 mL Schlenk flask equipped with a stirrer, 3.59 g (11.20 mmol) of 2-ethylhexylammonium 2-ethylhexylcarbonate (viscous liquid) was dissolved in 10 mL of methanol and 1.0 g (7.5 mmol) of silver cyanide was added. The reaction solution was initially a white slurry but it turned transparent as complex was produced. After 2 hours, a completely transparent solution was obtained. The resultant solution was filtered with a 0.45 micron membrane filter and the solvent was removed at vacuum to obtain white solid. The solid was recrystallized in ethyl acetate, dried and weighed to obtain 3.93 g of a silver complex (yield=85.62%). Most of the silver complex was decomposed below 130° C. to leave metallic silver and the silver content was 20.37 wt % (TGA analysis).
From the silver contents of the prepared compounds, m values were calculated. They are given in Table 1 below.
4 g of the silver complex prepared in Example 1 was dissolved in 5 g of butyl alcohol. After adjusting the viscosity to 500 cps, pattering was performed on a coated paper (ITP20HPG or ITP20SPH; InkTec) on a silk screen patterned to 320 meshes using a stainless steel (SUS) wire cloth. After heat treatment at 100° C. for 5 minutes and then at 130° C. for 10 minutes, a metal pattern having a conductivity of 400-500 mΩ/□ was obtained.
4 g of the silver complex prepared in Example 1 was dissolved in 10 g of isopropyl alcohol. After adjusting the viscosity to 13 cps, pattering was performed on a PET film for one time using an ink-jet printer. After heat treatment at 80° C. for 5 minutes and then at 130° C. for 10 minutes, a metal pattern having a conductivity of 200-300 mΩ/□ was obtained.
4 g of the silver complex prepared in Example 23 was dissolved in 5 g of 2-hexyl alcohol. After adjusting the viscosity to 500 cps, pattering was performed on a coated paper (ITP20HPG or ITP20SPH; InkTec) on a 320-mesh patterned silk screen. After heat treatment at 100° C. for 5 minutes and then at 130° C. for 10 minutes, a metal pattern having a conductivity of 400-500 mΩ/□ was obtained.
4 g of the silver complex prepared in Example 24 was dissolved in 10 g of butyl alcohol. After adjusting the viscosity to 13 cps, pattering was performed on a PET film for one time using an ink-jet printer. After heat treatment at 80° C. for 5 minutes and then at 130° C. for 10 minutes, a metal pattern having a conductivity of 200-300 mΩ/□ was obtained.
The present invention provides a useful organic silver complex by reacting the silver compound represented by the formula 2 with the ammonium carbamate compound or the ammonium carbonate compound represented by the formula 3, 4 or 5.
As the TGA analysis shows, the organic silver complex of the present invention is decomposed at a very low temperature to give pure metal film or powder. So, it can be processed into a variety of metallic silver films or formed into an ultrathin film by deposition under high vacuum. Thus, it can be used in plating, medicine, photography, electricity and electronics, fibers, detergents, household appliances, organics and polymer synthesis as catalyst or may be used in preparation of silver powder, paste and nanoparticle. Particularly, it may be utilized in low-resistance metal wirings, printed circuit boards (PCB), flexible printed circuit boards (FPC), antennas for radio frequency identification (RFID) tags, plasma display panels (PDP), liquid crystal displays (TFT-LCD), organic light emitting diodes (OLED), flexible displays, organic thin-film transistors (OTFT), electrodes, etc. as precursor material for metal patterning by chemical vapor deposition (CVD), plasma vapor deposition, sputtering, electroplating, lithography, electron beam, laser, etc. In addition, the organic silver complex solution of the present invention may be spin coated, roll coated, spray coated, dip coated, flow coated, ink-jet printed, offset printed, screen printed, gravure printed or flexo printed on such a substrate as glass, silicon wafer and polymer film like polyester or polyimide, paper, etc. and reduced, oxidized or heat-treated to form a metal or metal oxide pattern.
While the present invention has been described in detail with reference to the preferred embodiments, those skilled in the art will appreciate that various modifications and substitutions can be made thereto without departing from the spirit and scope of the present invention as set forth in the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2005-0011478 | Feb 2005 | KR | national |
| 10-2005-0011631 | Feb 2005 | KR | national |
| 10-2006-0011083 | Feb 2006 | KR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/KR2006/000451 | 2/7/2006 | WO | 00 | 8/7/2007 |