The present disclosure relates to a method for predicting photostability of an organic material within a short time using LA-DART-MS.
The photostability of an organic material is related to the degradation of the organic material by a light source, is an important factor that influences the long-life operation of the light emitting system when the organic material is used in the light emitting system, which is a physical property that should be considered importantly in applying to devices such as displays.
When the photostability of an organic material having light emitting properties is deteriorated, the phenomenon of photobleaching occurs. Photobleaching refers to a phenomenon in which, after an organic material is excited via external energy, it does not exhibit normal emission but loses its emission properties due to the formation of new bonds in the organic material, the structural degradation, the reaction with other materials, and the like. If the photostability of the organic material is deteriorated, degradation products or insoluble particles may be formed by a light source. Because degradation products can have absorption properties similar to those of organic materials, it interferes with the absorption of organic materials, and the insoluble particles induce scattering of the light source, resulting in photobleaching.
The evaluation of photostability is generally performed by measuring changes in absorption or emission spectrum after long exposure to an evaluation light source similar to the light source used for products to which organic materials are applied, or by measuring the reduction rate of the absorption or emission photons. Thereafter, the degree of degradation of the material, the structure of the degradation product and the like are analyzed through offline GC, LC/MS analysis and the like. However, such a process for measuring photostability and confirming the degradation products has a drawback in that the physical properties of the material are predicted due to long irradiation time (hundreds to thousands of hours) and offline analysis for the evaluation light source, and it takes a long time to confirm the degradation products that cause the deterioration of physical properties.
Therefore, in order to develop an organic material having excellent physical properties, there is a need to develop an analytical method capable of predicting the photostability within a short time.
It is one object of the present disclosure to provide an analytical method capable of predicting the photostability of an organic material within a short time using LA-DART-MS.
In order to achieve the above object, according to the present disclosure, there is provided a method for predicting photostability of an organic material as follows:
Degradation yield = (Sum of peak intensities of fragment ions) / (Sum of peak intensities of (molecular ions + fragment ions))
The present disclosure is directed to evaluating photostability among the physical properties of organic materials, and the organic material of interest is not particularly limited. Particularly, the photostability is a physical property that should be considered importantly in a light emitting material, and from this viewpoint, the organic material of the present disclosure includes an organic light emitting material having light emitting properties, and its photostability is predicted.
The present disclosure predicts photostability of an organic material by using LA-DART-MS instead of using an evaluation light source for the evaluation of the photostability of conventional organic materials, and the present disclosure is characterized in that components desorbed from an organic material by laser beam irradiation is ionized with ion sources to obtain a mass spectrum, and then the photostability is predicted through spectral analysis.
Although not theoretically limited, irradiation with an evaluation light source and irradiation with a laser beam are similar in the degradation of organic materials, and therefore, the photostability of organic materials can be predicted within a shorter time from the correlation thereof.
In particular, in the present disclosure, LA-DART-MS is used, and the photostability can be predicted within a shorter time compared to evaluating photostability with a conventional evaluation light source. In order to evaluate photostability with a conventional evaluation light source as described later, the organic material must be exposed to the evaluation light source for hundreds to thousands of hours. However, when LA-DART-MS is used as in the present disclosure, the mass spectrum of the degraded products can be obtained directly, which can be analyzed to predict the photostability, and as a result, there is an advantage in that the photostability of the organic material can be predicted within a few seconds to a few minutes.
The term “LA-DART-MS (Laser ablation-direct analysis in real time-mass spectrometry)” as used herein refers to an analytical method that performs the molecular weight and structure analysis of a material by irradiating a specimen with a laser beam to desorb the analyte, and then ionizing the desorbed analyte with a heated metastable helium gas beam from the DART ion source and reactive ions generated therefrom. The system for the LA-DART-MS is schematically shown in
Step 1 of the present disclosure is a step of irradiating a specimen containing an organic material with a laser beam, through which the organic material is degraded in the same manner as in the case where an organic substance is irradiated to an evaluation light source.
First, a system for LA-DART-MS will be described in relation to the step 1. As shown in
In the DART ionization unit 10, a laser beam is irradiated from the laser unit 40, the analyte desorbed from the specimen 2 mounted on the specimen mounting unit 30 is ionized using a helium beam of the DART ionization unit 10 and reactive ions generated therefrom. Specifically, a helium beam is emitted from an outlet 11 of the DART ionization unit 10 to ionize the analyte desorbed from a specimen 2 mounted on the specimen mounting unit 30.
The mass spectrometer 20 receives the ionized analyte and performs the molecular weight and structure analysis of the ionized analyte. The specimen mounting unit 30 is located between an outlet 11 of the DART ionization unit 10 and an inlet 21 of the mass spectrometer 20. Since the analyte desorbed from the specimen 2 mounted on the specimen mounting unit 30 flows into the inlet of the mass spectrometer 20, the specimen mounting unit 30 is located at a place lower than the path between the outlet 11 of the DART ionization unit 10 and the inlet 21 of the mass spectrometer 20. The inlet 21 of the mass spectrometer 20 may be a hole or a protruding pipe that is formed in the mass spectrometer 20 in order for the analyte outside the mass spectrometer 20 to flow into the internal space of the mass spectrometer 20 for analysis. For example, the inlet 21 of the mass spectrometer 20 may be an orifice or a transfer tube protruding and extending from the orifice.
The laser unit 40 irradiates the specimen 2 with a laser beam to desorb the analyte from the specimen. Further, while the analyzer confirms the mass spectrum in real time, the relative position of the laser unit 40 or the irradiation angle and power of the laser beam can be adjusted so that the ion peak intensity of the analyte derived from the specimen 2 is maximized.
Further, the LA-DART-MS system 1 may include an interface unit 100 located in the path between the outlet 11 of the DART ionization unit 10 and the inlet 21 of the mass spectrometer 20. The interface unit 100 has a tubular body which is opened in both end parts. One end of both end parts of the interface unit 100 may overlap or be disposed adjacent to the distal end of the outlet 11 of the DART ionization unit 10. And, the other end part is fitted into the outer surface of the inlet 21 of the mass spectrometer 20, or may make contact with the inlet 21 of the mass spectrometer 20 or may be connected to the inlet 21 so as to be spaced apart by a predetermined distance (about 2 mm). When the interface unit 100 is used, it is possible to effectively collect the components desorbed and ionized by the laser and increase the transmission toward the mass spectrometer, thereby improving detection sensitivity and signal stability.
When the specimen 2 mounted on the specimen mounting unit 30 is irradiated with a laser beam using the LA-DART-MS system as described above, components that are desorbed from the specimen containing the organic material are generated, and ionized by using a helium beam from the DART ionization unit 10 and reactive ions generated therefrom. A helium beam is emitted from the outlet 11 of the DART ionization unit 10 to ionize the analyte desorbed from the specimen 2 mounted on the specimen mounting unit 30, and the ionized analyte flows into the mass spectrometer 20, and mass spectra obtained from analytes can be analyzed as in step 2 described later.
The laser beam can be appropriately adjusted depending on the organic material.
Specifically, the laser may be a continuous wave (CW) or a pulsed laser.
Further, the power of the laser beam may be 0.001 mW to 10 W. When the power of the laser beam is less than 0.001 mW, the power of the laser beam is weak, so that the components desorbed from the specimen containing the organic material are generated in a small amount, which may make it difficult to analyze the mass spectrum. When the power of the laser beam is greater than 10 W, the power of the laser beam is so strong that it can damage or severely destroy specimens containing organic materials, which may make it difficult to analyze the mass spectrum. Preferably, the power of the laser beam may be 0.001 mW to 1 W.
Further, the wavelength of the laser beam may be 200 nm to 3000 nm. The above is a range analyzed as a range of the absorption wavelength of a general organic material, and can be appropriately adjusted in consideration of the absorption wavelength of the organic material to be analyzed.
Further, the irradiation time of the laser beam may be set from the irradiation time of the laser beam to the time when a specific peak is no longer observed in a mass spectrum described later. Preferably, the time sufficient to obtain an effective mass spectrum is 30 minutes or less, more preferably 10 minutes or less. In particular, the irradiation time of the laser beam is significantly shorter than the irradiation time of several hundreds to several thousand hours, which is the irradiation time required for measuring the photostability with a conventional evaluation light source, through which it is possible to predict the photostability within a quick time.
Step 2 of the present disclosure is a step of obtaining a mass spectrum of components desorbed and ionized from the specimen by the step 1.
When a specimen containing an organic material is irradiated with a laser beam according to the step 1, the organic material is desorbed from the specimen, and a part of the organic material is also degraded to generate a degradation product. Since the degree of degradation of such an organic material is related to the photostability, the mass spectrum in the present disclosure is analyzed in order to confirm the degree of degradation of the organic material.
On the other hand, for the mass spectrum analysis, in order to directly detect components desorbed and ionized by the ion source during the laser beam irradiation in step 1, as described above, the specimen containing the organic material is located between the outlet 11 of the DART ionization unit 10 and the inlet 21 of the mass spectrometer 20, more preferably, the specimen mounting unit 30 is located at a place lower than the path between the outlet 11 of the DART ionization unit 10 and the inlet 21 of the mass spectrometer 20.
Moreover, a mass spectrum can be directly obtained through the step 2, and the mass spectrum includes information on degradation products of organic materials. Thus, there is an advantage in that the analysis of degradation products, for example, the molecular weight and structural analysis can also be performed quickly.
When photostability is evaluated with a conventional evaluation light source, not only the organic material must be exposed to the evaluation light source for a long time, but also it took a long time to confirm the molecular weight and structure of the degradation products because it is necessary to go through the sample pretreatment process again and perform GC or LC/MS analysis to confirm the molecular weight and structure. However, through step 2 of the present disclosure, the mass spectrum of the components desorbed and ionized from the specimen can be directly obtained, and the sample pretreatment process and the like are not required, whereby it is possible to analyze the degradation products of organic materials within a significantly shorter time as compared with a conventional one.
Step 3 of the present disclosure is a step of calculating the degradation yield of the mathematical expression 1 from the mass spectrum obtained in step 2.
Just as the organic material is irradiated to the evaluation light source, it is similarly degraded by irradiating the organic material with a laser beam, and therefore, the degree of this degradation can be analyzed to predict the photostability of the organic material.
The mathematical expression 1 calculates a degradation yield in order to analyze it, and mathematically expressed as follows. In the following, “I” means the intensity of each peak. In the peak detected in the mass spectrum, a molecular ion peak of an undegraded organic material and a peak of fragment ions generated by degrading an organic material exist, and thus, the degradation yield can be calculated through the mathematical expression 1.
Degradation yield = ∑ I (fragment ions) / ∑ I (parent + fragment ions)
The lower the degradation yield obtained according to the above, the lower the degree of degradation of the organic material by the laser beam, which can be predicted that the photostability of the organic material is excellent. On the contrary, the higher the degradation yield, the greater the degree of degradation, which can be predicted that the photostability of the organic material is deteriorated.
By applying the above, the relative photostability between organic materials can be evaluated. For example, if the photostability is to be compared with that of a specific organic material, the degradation yields of the specific organic material and the other organic material can be measured according to the steps 1 to 3, and compared with each other to compare the photostability.
The present disclosure may further include a step of linearly regression-analyzing the photostability data (X) of the organic material and the degradation yield (Y) obtained in step 3 to derive a prediction expression of the photostability of the organic material, if necessary.
When the degradation yield of each of the plurality of organic materials is obtained by the above-mentioned steps 1 to 3, a relational expression between the degradation yield (Y) and the photostability data (X) of the plurality of organic materials can be derived therefrom through regression analysis, the degradation yields of other organic materials can be obtained from this relational expression to predict the photostability thereof.
On the other hand, the photostability data of the plurality of organic materials is obtained by exposing the organic material to an evaluation light source for a long time, then measuring the change in absorption or emission spectrum, or by measuring the reduction rate of the absorption or emission photons. Thereafter, the degree of degradation of the material and the structure of the degradation product can be analyzed through offline GC and LC/MS analysis.
As in Examples described later, the photostability data of the plurality of organic light emitting materials in the present disclosure is obtained by exposing the organic light emitting material to an evaluation light source for 500 hours, and measuring the number of photons in the absorption or emission wavelength region with a luminance meter. It could be confirmed that this correlates with the degradation yield measured according to the present disclosure.
As described above, the method for predicting photostability of an organic material according to the present disclosure can predict the photostability within a shorter time than the conventional method for measuring the photostability of an organic material.
Hereinafter, embodiments of the present disclosure will be described in more detail by way of examples. However, the following examples are only provided for illustrative purposes, and the contents of the present disclosure are not limited by these examples.
The following five compounds were used as experimental materials, and the substituents of each compound are shown in Table 1 below.
For each of the organic light emitting materials 1 to 5, 0.5 mg of the organic light emitting material in powder form was loaded onto an aluminum plate, and then crimped using a pellet tool to prepare a specimen having a diameter of about 3 mm.
The LA-DART-MS system as shown in
Each of the prepared specimens was irradiated with a laser, and the laser, ion source temperature, and mass spectrum measurement conditions were as follows.
After laser irradiation for each specimen, the intensities of parent ions and fragment ions were calculated based on the mass spectrum obtained for 1 minute, and then the degradation yield was measured according to the mathematical expression 1. Three mass spectra were obtained for each specimen, and the average value and error were calculated. Typically, the mass spectrum of the organic light emitting material 1 is shown in
The photostability was measured by a method in which an organic light emitting material was exposed to an evaluation light source for a long time. Specifically, each of the organic light emitting materials 1 to 5 was exposed to an evaluation light source (400 to 450 nm) for 500 hours, and the number of photons in the absorption or emission wavelength region was measured with a luminance meter. At this time, a ratio that decreases with time compared to the initial value was obtained as the photostability data.
The experimental results are shown in
As shown in
Further, when the graph of
Accordingly, the photostability of the organic light emitting material can be predicted within a significantly shorter time (1 minute) than 500 hours, which is the measurement time of light resistance according to the evaluation light source of the organic light emitting material.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2020-0135280 | Oct 2020 | KR | national |
| 10-2021-0138930 | Oct 2021 | KR | national |
The present application is a national stage entry under 35 U.S.C. §371 of International Application No. PCT/KR2021/014541 filed on Oct. 19, 2021, which claims priority from Korean Patent Applications No. 10-2020-0135280 filed on Oct. 19, 2020, and No. 10-2021-0138930 filed on Oct. 19, 2021, all the disclosures of which are incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2021/014541 | 10/19/2021 | WO |