Patent Grant
7770274
1. Field of the Invention
The present invention relates to piezoelectric thin film devices used in piezoelectric devices, and particularly to piezoelectric thin film devices used in high frequency bands, and a manufacturing method for the same.
2. Description of the Related Art
Recently, high frequency bands in the GHz range are being used in wireless communication systems such as mobile communication devices, and local area network (LAN) systems transferring data between computers at high transfer rates. Piezoelectric thin film devices are receiving attention in applications such as high frequency (RF) devices of high frequency electronics of such wireless communications systems. Applications as devices such as resonators, variable capacitors, and micro switches, for example, are expected uses for piezoelectric thin film devices. Piezoelectric thin film devices according to micro electro mechanical system (MEMS) technology are manufactured using thin film micro fabrication processes in the same manner as for semiconductor devices such as metal insulated semiconductor (MIS) integrated circuits. Therefore, it is possible to integrate MEMS piezoelectric thin film devices and semiconductor devices on a common semiconductor substrate.
Surface acoustic wave (SAW) devices, for example, are generally used as high frequency resonators. However, the resonant frequency of SAW devices exhibits an inversely proportional relationship to the gap distance between comb type electrodes. Since, at a frequency range exceeding 1 GHz, the gap distance between comb type electrodes of SAW devices is 1 μm or less, it is difficult to correspond to recent higher usage frequencies demands.
In place of SAW devices, a film bulk acoustic wave resonator (FBAR), which makes use of a mode of longitudinal vibration in the thickness direction of a piezoelectric film, has recently been receiving attention as a resonator. The FBAR, which uses a piezoelectric film, is also occasionally referred to as a bulk acoustic wave (BAW) device. In the FBAR, resonant frequency is regulated by the acoustic velocity and film thickness of the piezoelectric device. For example, the piezoelectric film corresponds to an average film thickness of about 1 μm to about 2 μm at a band of 2 GHz, or a film thickness of about 0.4 μm to about 0.8 μm at a band of 5 GHz. By thinning the piezoelectric film further, it is possible to increase frequency by several tens of GHz.
In the structure of a current representative FBAR, a piezoelectric film of a material such as aluminum nitride (AlN) or zinc oxide (ZnO) is sandwiched between two opposing electrodes, more specifically, a top electrode and a bottom electrode. For improved performance, a resonator of the FBAR type is disposed so as to be suspended above a cavity. A fabrication method for an FBAR having a cavity is disclosed (refer to Japanese published unexamined application No. 2000-69594). For example, a hollow portion can be formed by anisotropic etching on a silicon (Si) substrate. Next, a sacrificial layer of an easily etched material, such as boron and phosphorous doped silicon glass (BPSG), for example, is filled into the hollow portion and planarized. A bottom electrode, a piezoelectric film, and a top electrode, respectively, are then stacked in sequence on top of the planarized sacrificial layer. Afterward, a hole is bored from the top electrode, which is formed above the sacrificial layer, to extend to the sacrificial layer. The sacrificial layer is removed by selective etching, forming the cavity.
Piezoelectric characteristics of a piezoelectric film used in FBARs are dependant upon orientation. In AlN piezoelectric films, for example, there is a strong mutual relationship between a full width at half maximum (FWHM) of c-axis orientation of an AlN crystal and an electromechanical coupling constant (refer to Rajan S. Naik et al., “Measurements of Bulk, C-Axis Electromechanical Coupling Constant as a Function on AlN Film Quality”, IEEE transactions on ultrasonics, ferroelectrics, and frequency control, Vol. 47, No. 1, pp. 292-296, January 2000). In order to attain desired piezoelectric qualities, it is essential to form a piezoelectric film so that the c-axis direction is oriented along the direction in which the bottom electrode and the top electrode oppose each other. However, there are limits on the orientation of the AlN piezoelectric film formed on top of the sacrificial layer, which raises the problem of a small electromechanical coupling constant.
In order to improve the orientation of piezoelectric crystal, there is a manufacturing method of an FBAR by epitaxially growing a piezoelectric film on a substrate (refer to Japanese published unexamined patent application No. 2001-94373). In the method disclosed in Japanese published unexamined patent application No. 2001-94373, an AlN piezoelectric film is epitaxially grown in (0001) orientation, more specifically, in the c-axis direction, on an Si substrate of (111) orientation. A top electrode is formed on top of the AlN piezoelectric film. Afterward, the Si substrate is removed by anisotropic etching from the underside of the substrate until the AlN piezoelectric film is exposed, forming a via hole. After the AlN piezoelectric film has been exposed, the bottom electrode is formed from the underside of the substrate. Thus, a resonator using the epitaxial AlN piezoelectric film is formed above the cavity.
In the above mentioned manufacturing method, in order to orient the AlN piezoelectric film along the c-axis, it is essential to use a Si substrate in the (111) orientation. It may be a problem to use the (111) orientated substrate, which is different from the (100) orientated substrate used in general manufacturing methods of semiconductor devices.
Additionally, piezoelectric thin film devices such as variable capacitors or micro switches, have a movable electrode provided on an actuator, and a fixed electrode provided on a surface of a substrate which opposes the actuator. The actuator is supported on one end so as to be suspended over a substrate. The actuator changes the distance between the movable electrode and the fixed electrode. Piezoelectric actuators using an electrostriction effect or a reverse piezoelectric effect of a piezoelectric film, as a driving force, are currently being tested.
Lead zirconate-titanate (PZT) is a material known as a piezoelectric film having a large electrostriction effect. On PZT, in order to attain a film of good quality, it is essential to execute annealing at a temperature of about 600° C. after forming the film at room temperature. Because volume contraction occurs due to the annealing, the residual distortion of the PZT film will inevitably increase. The piezoelectric actuator is suspended in the air, and has a long and thin beam structure, which contains a piezoelectric layer sandwiched by the top and bottom electrodes. Therefore, it is difficult to suppress warpage occurring on the PZT piezoelectric film by residual distortion. Because a piezoelectric film of materials such as AlN, or ZnO can be deposited at near room temperature, it is possible to precisely control residual stress by film deposition conditions, compared to the PZT piezoelectric film. However, the electrostriction effect of materials such as AlN, or ZnO is small compared with PZT. Therefore, it is possible to have a small electromechanical coupling constant of the piezoelectric film, which may not be sufficient to ensure a sufficient drive range of the piezoelectric actuator.
It is an object of the present invention to provide a piezoelectric thin film device having an electromechanical coupling constant that can be improved, as well as a manufacturing method for the same.
A first aspect of the present invention inheres in a piezoelectric thin film device including an amorphous metal film disposed above a substrate; and a piezoelectric film disposed on the amorphous metal, and one of crystal axis of the piezoelectric film being aligned in a direction perpendicular to a surface of the amorphous metal.
A second aspect of the present invention inheres in a method for manufacturing a piezoelectric thin film device, including forming an amorphous metal film above a substrate; forming a piezoelectric film on the amorphous metal, so that one of crystal axis of the piezoelectric film is aligned in a direction perpendicular to a surface of the amorphous metal; and forming a top metal film on a surface of the piezoelectric film, the top metal film facing the amorphous metal film so as to sandwich the piezoelectric film.
Various embodiments of the present invention will be described with reference to the accompanying drawings. It is to be noted that the same or similar reference numerals are applied to the same or similar parts and devices throughout the drawings, and the description of the same or similar parts and devices will be omitted or simplified.
As shown in
The performance of the piezoelectric film 15 can be expressed by the electromechanical coupling constant Kt2, which indicates the magnitude of the piezoelectric effect, and the quality factor Q, which is an indicator of the sharpness of mechanical oscillation in a resonant frequency. For improving the electromechanical coupling constant of the piezoelectric film 15, it is important to align a polarization axis of a piezoelectric crystal in the thickness direction of the piezoelectric film 15. Also, by aligning the crystal orientation of the piezoelectric film 15 in the polarization direction using a high purity piezoelectric crystal, a large quality factor Q can be attained.
For example, in an RF filter or a voltage controlled oscillator (VCO) using FBARs, bandwidth can be increased as much as the electromechanical coupling constant is large. The quality factor Q relates to an insertion loss of the RF filter, and a degree of oscillation purity of the VCO. There are various phenomenon of elastic wave absorption relating to the quality factor Q. Additionally, in piezoelectric actuators, because the drive range increases as much as the electromechanical coupling constant of the piezoelectric film is large, it is possible to achieve a low drive voltage and a large variable range for an actuator.
A piezoelectric crystal of a material such as AlN or ZnO used as the piezoelectric film 15 is hexagonal. A hexagonal crystal has an inherent crystal habit to easily align in the c-axis orientation. It is possible to align a polarization axis by orienting the piezoelectric film 15 singularly in the c-axis, more specifically, the (0001) direction, which is the polarization direction of the piezoelectric crystal. As a result, it is possible to ensure the electromechanical coupling constant and quality factor Q of the piezoelectric film.
AlN and ZnO piezoelectric films are formed on top of various underlying layers, and orientations of the piezoelectric films are evaluated using a technique such as XRD. All of the underlying layers and the piezoelectric films are deposited at room temperature by magnetron sputtering. Thickness of each piezoelectric film is about 500 nm. As shown in
Additionally, in samples E to H, which use amorphous insulating layers of material such as silicon oxide (SiO2) and aluminum oxide (Al2O3) for underlying layers, AlN and ZnO piezoelectric films are oriented in the c-axis orientation. The FWHM of the orientation for each of the samples E to H is in a range from about 4.1° to about 5.1°, which is broader, and orientation is inferior compared to the samples A to D. Further, in samples I to L, which use Al polycrystal metal and polycrystal Si semiconductor (poly-Si) for underlying layers AlN and ZnO piezoelectric films are not singularly oriented but become a polycrystal film with a little or no orientation. Thus, the effects of the amorphous metal under layers on increasing orientation characteristics of piezoelectric film are extremely large.
A surface of polycrystal metal is formed by crystal grains having many orientations respectively, and there are many cases of surface irregularities depending on crystal grains. Correspondingly, an amorphous metal is formed with a uniformly amorphous surface. Root mean square roughness detected by techniques such as surface roughness measurement and atomic force microscopes (AFM) is, for example, 3 nm and above in a case of polycrystal metal surfaces, and 3 nm and below in a case of amorphous surfaces. Thus, because an extremely flat and uniform surface is attained with an amorphous metal, a hexagonal crystal such as AlN and ZnO can be grown with orientation in the c-face [0001], which is an inherent face of the hexagonal crystal formed by crystal habit. As a result, it is possible to improve orientation of AlN or ZnO piezoelectric film formed on top of an amorphous metal film.
Additionally, when compared with amorphous insulating layers of SiO2 and the like, which are normally used as an underlying layer or a sacrificial layer on a surface of a substrate, the surface energy of an amorphous metal is generally higher than the amorphous insulation layers. By nature, a crystal provided on an amorphous metal film tends to grow in a layer so as to decrease the surface energy. Therefore, orientation of the piezoelectric film may be further improved on the amorphous metal film.
Additionally, as shown in
Al metal films and AlN piezoelectric films are formed on top of various underlying layers, and orientations of the piezoelectric films are evaluated using a technique such as XRD. The underlying layers, the metal films, and the piezoelectric films are all deposited at room temperature by magnetron sputtering. Thickness of each piezoelectric film is about 500 nm. As shown in
Additionally, in samples O and P, which use amorphous insulating layers of material such as SiO2 and Al2O3 for underlying layers, Al metal films are oriented in the (111) orientation with FWHM of 4.2° and 4.0°, respectively, and AlN piezoelectric films are oriented in the c-axis direction with an FWHM of 4.6° and 4.1°, respectively. The FWHM of the orientation for each of the Al metal films and AlN piezoelectric films of the samples O and P is inferior compared to the samples M and N. Further, in samples Q to R, which use an Al polycrystal metal or a poly-Si for an underlying layer, an Al metal film and an AlN piezoelectric film are not oriented but become a polycrystal film with singularly little or no orientation.
Thus, by providing the orientation metal film 23 between the amorphous metal film 22 and the piezoelectric film 15, it is possible to further highly orient the piezoelectric film.
An FBAR as a piezoelectric thin film device according to a first embodiment of the present invention includes a bottom electrode 14 of an amorphous metal film provided on a surface of a substrate 11, a piezoelectric film 15 provided on a surface of the bottom electrode 14, and a top electrode (top metal film) 16 provided on top of a surface of the piezoelectric film 15, as shown in
Additionally, as shown in
In the piezoelectric film 15 of the resonator 20, a high frequency signal is transmitted by the vibration of the bulk acoustic waves excited by the high frequency signal applied to the bottom or top electrodes 14, 16. For example, a GHz range high frequency signal applied from the bottom electrode 14 is transmitted to the top electrode 16 through the piezoelectric film 15. On the amorphous bottom electrode 14, the piezoelectric film 15 is highly oriented in the c-axis direction, which is the polarization direction of the piezoelectric crystal. Consequently, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15.
According to the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction, and to improve the electromechanical coupling constant and the quality factor Q. As a result, it is possible to achieve desirable resonant characteristics of the resonator 20 of the FBAR.
Next, a manufacturing method of the FBAR according to the first embodiment will be described with reference to the cross section views shown in
A strontium lutetium oxide (SrRuO3) layer is formed at a thickness of about 1 μm on a surface of a Si substrate 11 by RF magnetron sputtering and the like. As shown in
An amorphous metal layer of Al0.4Ta0.6 or the like is deposited on top of the substrate 11 by RF magnetron sputtering and the like. As shown in
A piezoelectric layer of AlN and the like is deposited at a thickness of about 1.4 μm on the substrate 11 by reactive RF magnetron sputtering and the like. As shown in
As shown in
In the manufacturing method of the FBAR according to the first embodiment, the amorphous metal film is used as the bottom electrode 14. The piezoelectric film 15 is deposited on the surface of the bottom electrode 14, in an area corresponding to the resonator 20. As a result, the piezoelectric film 15 in the area of the resonator 20 is highly oriented in the c-axis direction, which is the polarization direction.
Frequency characteristics of the manufactured FBAR are measured using a network analyzer and the like. For example, a resonant frequency of the FBAR according to the first embodiment is about 2.1 GHz. Additionally, an electromechanical coupling constant and a quality factor Q of the piezoelectric film 15 are evaluated from the resonance characteristics of the FBAR. For example, the electromechanical coupling constant is about 6.4%. The quality factor Q is about 700 at a resonance point, and about 620 at an antiresonance point. The electromechanical coupling constant and the quality factor Q are roughly the same compared to an FBAR using an epitaxially grown single crystal piezoelectric film. Thus, the piezoelectric film 15 of the FBAR according to the first embodiment may provide desirable piezoelectric characteristics.
According to the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated growth technology such as epitaxial growth. Thus, it is possible to achieve an FBAR in which the electromechanical coupling constant and quality factor Q are improved.
(First Modification Of The First Embodiment)
An FBAR according to a first modification of the first embodiment of the present invention includes a bottom electrode 14 provided on an insulating film 32 on a surface of a substrate 11, a piezoelectric film 15 provided on top of a surface of the bottom electrode 14, and a top electrode 16 provided on top of a surface of the piezoelectric film 15, as shown in
The first modification of the first embodiment differs from the first embodiment in that the amorphous metal film 22 is provided so as to surround the cavity 17 and faces the bottom electrode 14. Other configurations are as in the first embodiment, so duplicated descriptions are omitted.
A metal such as Al, which is capable of being selectively removed with respect to a metal material used for the bottom electrode 14, is formed on the amorphous metal film 22. On the amorphous metal film 22, the Al metal film can be highly aligned in the (111) orientation in a direction vertical to the surface of the amorphous metal film 22. Mo, used for the bottom electrode 14, may highly align in the (110) orientation on the Al metal film of the (111) orientation. On the bottom electrode 14 that is highly (110) oriented, the piezoelectric film 15 may highly align with the c-axis direction, which is the polarization direction of a piezoelectric crystal. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15.
A manufacturing method of an FBAR according to the first modification of the first embodiment will be described referring to the cross section views as shown in
As shown in
A metal layer of Al or the like, having a thickness of about 0.1 μm, is deposited by RF magnetron sputtering and the like. The Al metal layer is selectively removed by photolithography, RIE using a chloride based gas, and the like, as shown in
A metal layer such as Mo is deposited by RF magnetron sputtering and the like. As shown in
A piezoelectric layer such as AlN is deposited at a thickness of about 1.4 μm by RF magnetron sputtering and the like. As shown in
As shown in
In the first modification of the first embodiment, since the sacrificial layer 12a on the amorphous metal layer 22 is highly oriented, a highly oriented piezoelectric film 15 can be formed even around the resonator 20. As a result, it is possible to highly orient the piezoelectric film 15 in the c-axis direction in the entire region over the cavity 17, and to increase the mechanical strength of the piezoelectric film 15.
Frequency characteristics of the manufactured FBAR are measured using a network analyzer and the like. For example, a resonant frequency of the FBAR is about 2.1 GHz. Additionally, an electromechanical coupling constant and a quality factor Q of the piezoelectric film 15 are evaluated from the resonance characteristics of the FBAR. For example, the electromechanical coupling constant is about 6.5%. The quality factor Q is about 800 at a resonance point, and about 750 at an antiresonance point. The electromechanical coupling constant and the quality factor Q increase. Thus, the piezoelectric film 15 of the FBAR according to the first modification of the first embodiment may provide desirable piezoelectric characteristics.
According to the first modification of the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated growth technology such as epitaxial growth. Thus, it is possible to achieve an FBAR in which the electromechanical coupling constant and quality factor Q are improved.
(Second Modification Of The First Embodiment)
An FBAR according to a second modification of the first embodiment of the present invention includes a bottom electrode 14 having an amorphous metal film 22 provided on a surface of an insulating film 32 and an orientation metal film 23 provided on a surface of the amorphous metal film 22, as shown in
The amorphous metal film 22 of the bottom electrode 14 is, for example, AlTa. The orientation metal film 23 is Al or the like, which is oriented in the (111) orientation perpendicular to the surface of the amorphous metal film 22.
The second modification of the first embodiment is different from the first modification of the first embodiment in that the bottom electrode 14 including the amorphous metal film 22 and the orientation metal film 23 is placed on the cavity 17a provided in the substrate 11 and the insulating film 32. Other configurations are as in the first embodiment and the first modification of the first embodiment, so duplicated descriptions are omitted.
In the second modification of the first embodiment, the orientation metal film 23 such as Al, which is oriented in the (111) orientation direction, is provided on the amorphous metal film 22 of the bottom electrode 14. The piezoelectric film 15 formed on the oriented orientation metal film 23 can be strongly aligned in the c-axis direction. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15. In addition, since the bottom electrode 14 extends to a location on the insulating film 32 over the entire area of the cavity 17a, the mechanical strength of the piezoelectric film 15 may structurally increase. Additionally, above the cavity 17a, the piezoelectric film 15 is evenly formed away from a step of an end portion of the bottom electrode 14. Therefore, it is possible to prevent deterioration of orientation of the piezoelectric film 15 in vicinity of the resonator 20, and to prevent the generation of spurious vibrations in the resonance characteristics of the FBAR.
Next, a manufacturing method of an FBAR according to the second modification of the first embodiment will be described with reference to the cross section views as shown in
An insulating film 32, 32a such as SiO2 is formed on top and back surfaces of a substrate 11 at a thickness of about 1 μm by thermal oxidation or the like, as shown in
As shown in
A piezoelectric film 15 such as AlN is deposited at a thickness of about 1.7 μm by RF magnetron sputtering and the like, as shown in
By photolithography, etching and the like, the insulating film 32a is selectively removed to form an opening in which the bottom surface of the substrate 11 is exposed below the bottom electrode 14. As shown in
In the second modification of the first embodiment, the amorphous metal layer 22 is evenly deposited on the surface of the insulating film 32. On the surface of the even amorphous metal layer 22, the orientation metal film 23 such as Al can be deposited so as to be highly oriented in the (111) orientation direction. Thus, it is possible to deposit the piezoelectric film 15 to be highly oriented in the c-axis direction. Additionally, since the bottom electrode 14 is formed to cover the cavity 17a, it is possible to increase the mechanical strength of the piezoelectric film 15. The end portion of the bottom electrode 14 is spaced from the upward region of the cavity 17a. Therefore, it is possible to uniformly deposit the piezoelectric film 15 over the cavity 17a.
Frequency characteristics of the manufactured FBAR are measured using a network analyzer and the like. For example, a resonant frequency of the FBAR is about 2.1 GHz. Additionally, an electromechanical coupling constant and a quality factor Q of the piezoelectric film 15 are evaluated from the resonance characteristics of the FBAR. For example, the electromechanical coupling constant is about 6.8%. The quality factor Q is about 950 at a resonance point, and about 900 at an antiresonance point. The electromechanical coupling constant and the quality factor Q are increased. Thus, the piezoelectric film 15 of the FBAR according to the second modification of the first embodiment may provide desirable piezoelectric characteristics.
According to the second modification of the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated growth technology such as epitaxial growth. Thus, it is possible to achieve an FBAR in which the electromechanical coupling constant and quality factor Q are improved.
(Third Modification Of The First Embodiment)
An FBAR according to a third modification of the first embodiment of the present invention includes a bottom electrode 14 having an amorphous metal film 22 provided on a surface of an insulating film 32 and an orientation metal film 23 provided on a surface of the amorphous metal film 22, as shown in
The amorphous metal film 22 of the bottom electrode 14 is, for example, AlTa. The orientation metal film 23 is an orientation metal film of Al or the like, oriented in the (111) orientation direction perpendicular to the surface of the amorphous metal film 22.
The third modification of the first embodiment is different from the second modification of the first embodiment in that the bottom electrode 14 including the amorphous metal film 22 and the orientation metal film 23 is placed on the cavity 17b provided in the substrate 11 and the insulating film 32. Other configurations are as in the second modification of the first embodiment, so duplicated descriptions are omitted.
In the third modification of the first embodiment, the orientation metal film 23 such as Pt, which is oriented, for example, in the (111) orientation direction, is provided on the amorphous metal film 22 of the bottom electrode 14. The piezoelectric film 15 formed on the oriented orientation metal film 23 can be highly aligned in the c-axis direction. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15. In addition, since the bottom electrode 14 extends to a location on the insulating film 32 over the entire area of the cavity 17b, the mechanical strength of the piezoelectric film 15 may structurally increase. Additionally, above the cavity 17b, the piezoelectric film 15 is evenly formed spaced from a step of an end portion of the bottom electrode 14. Therefore, it is possible to prevent deterioration of orientation of the piezoelectric film 15 in the vicinity of the resonator 20, and to prevent the generation of spurious vibrations in the resonance characteristics of the FBAR.
Next, a manufacturing method of an FBAR according to the third modification of the first embodiment will be described with reference to the cross section views shown in
An insulating film 32, 32a such as SiO2 is formed on top and bottom surfaces of a substrate 11 at a thickness of about 1 μm by thermal oxidation or the like, as shown in
A metal layer such as Pt is deposited by RF magnetron sputtering and the like. As shown in
A piezoelectric layer such as AlN is deposited at a thickness of about 1.7 μm by RF magnetron sputtering and the like. As shown in
The substrate 11 is thinned by polishing from the insulating film 32a on the bottom surface of the substrate 11 to a thickness of about 200 μm. As shown in
In the third modification of the first embodiment, the amorphous metal layer 22 is evenly deposited on the surface of the insulating film 32. On the surface of the even amorphous metal layer 22, the orientation metal film 23 such as Pt can be deposited so as to be highly oriented in the (111) orientation direction. Thus, it is possible to deposit the highly oriented piezoelectric film 15 in the c-axis direction. Additionally, since the bottom electrode 14 is formed to cover the cavity 17b, it is possible to increase the mechanical strength of the piezoelectric film 15. The end portion of the bottom electrode 14 is spaced from the upward region of the cavity 17b. Therefore, it is possible to uniformly deposit the piezoelectric film 15 over the cavity 17b.
Frequency characteristics of the manufactured FBAR are measured using a network analyzer and the like. For example, a resonant frequency of the FBAR is about 2.1 GHz. Additionally, an electromechanical coupling constant and a quality factor Q of the piezoelectric film 15 are evaluated from the resonance characteristics of the FBAR. For example, the electromechanical coupling constant is about 6.7%. The quality factor Q is about 900 at a resonance point, and about 950 at an antiresonance point. The electromechanical coupling constant and the quality factor Q are increased. Thus, the piezoelectric film 15 of the FBAR according to the third modification of the first embodiment may provide desirable piezoelectric characteristics.
According to the third modification of the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated growth technology such as epitaxial growth. Thus, it is possible to achieve an FBAR in which the electromechanical coupling constant and quality factor Q are improved.
(Fourth Modification Of The First Embodiment)
An FBAR according to a fourth modification of the first embodiment of the present invention includes a bottom electrode 14 having an amorphous metal film 22 extending from the substrate 11 onto the top of a cavity 17 provided in the substrate 11 and an orientation metal film 23 provided on a surface of the amorphous metal film 22, as shown in
The amorphous metal film 22 of the bottom electrode 14 is, for example, AlTa. The orientation metal film 23 is Pt or the like, oriented in the (111) orientation perpendicular to the surface of the amorphous metal film 22.
The fourth modification of the first embodiment differs from the first and second modifications of the first embodiment in that an end of the bottom electrode 14 is located on the cavity 17 provided in the substrate 11. Other configurations are as in the first and second modifications of the first embodiment, so duplicated descriptions are omitted.
In the fourth modification of the first embodiment, the orientation metal film 23 such as Pt, which is oriented, for example, in the (111) orientation direction, is provided on the amorphous metal film 22 of the bottom electrode 14. The piezoelectric film 15 formed on the oriented orientation metal film 23 can be strongly aligned in the c-axis direction. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15. In addition, the end of the bottom electrode 14 is located on the cavity 17. Thus, it is possible to prevent formation of a capacitor structure in which the piezoelectric film 15 is sandwiched between the bottom and top electrodes 14, 16, except for a region of the resonator 20. As a result, it is possible to prevent deterioration of the resonance characteristics of the FBAR in a high frequency region.
Next, a manufacturing method of an FBAR according to the fourth modification of the first embodiment will be described in reference to the cross section views as shown in
As shown in
As shown in
As shown in
As shown in
The piezoelectric film 15 is selectively removed by photolithography, RIE using a chloride based gas, and the like, to form a via hole (not illustrated) so as to expose the sacrificial layer 12 above the surface of the substrate 11. As shown in
In the fourth modification of the first embodiment, the amorphous metal layer 22 is evenly deposited on the surface of the even substrate 11 in which the sacrificial layer 12 is embedded. The orientation metal film 23 such as Pt can be deposited to highly align in the (111) orientation direction on the even surface of the amorphous metal film 22. As a result, it is possible to deposit the highly oriented piezoelectric film 15 in the c-axis direction. The end portion of the bottom electrode 14 is spaced from the upward region of the cavity 17. Therefore, it is possible to uniformly deposit the piezoelectric film 15 over the cavity 17.
Frequency characteristics of the manufactured FBAR are measured using a network analyzer and the like. For example, a resonant frequency of the FBAR is about 2.1 GHz. Additionally, an electromechanical coupling constant and a quality factor Q of the piezoelectric film 15 are evaluated from the resonance characteristics of the FBAR. For example, the electromechanical coupling constant is about 6.9%. The quality factor Q is about 1100 at a resonance point, and about 1150 at an antiresonance point. The electromechanical coupling constant and the quality factor Q are increased. Thus, the piezoelectric film 15 of the FBAR according to the fourth modification of the first embodiment may provide desirable piezoelectric characteristics.
According to the fourth modification of the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated growth technology such as epitaxial growth. Thus, it is possible to achieve an FBAR in which the electromechanical coupling constant and quality factor Q are improved.
(Fifth Modification Of The First Embodiment)
In an FBAR according to a fifth modification of the first embodiment of the present invention, a bottom electrode 14, a piezoelectric film 15 and a top electrode 16 are provided on an acoustic reflection layer 38 provided on a substrate 11, as shown in
In the acoustic reflection layer 38, first acoustic impedance layers 36a, 36b having a high acoustic impedance and second acoustic impedance layers 37a, 37b having a low acoustic impedance are alternately laminated. The thickness of each of the first and second acoustic impedance layers 36a, 37a, 36b, 37b is about ¼ the wavelength of the bulk acoustic wave excited by the resonator 20. The bulk acoustic wave is reflected by the first and second acoustic impedance layers 36a, 37a, 36b, 37b periodically placed at a thickness of about ¼ the wavelength of the acoustic wave. The acoustic impedance is determined by the density and the elastic constant of a material. A suitable example of material having high acoustic impedance includes an insulator such as AlN, tantalum oxide (Ta2O5) or Al2O3, and a metal such as W, Mo, Pt, Ir, Ru, rhodium (Rh) or Ta. A suitable example of material having low acoustic impedance includes an insulator such as SiO2 or Si3N4, a semiconductor such as Si, and a metal such as Al or titanium (Ti).
For the acoustic reflection layer 38, the first and second acoustic impedance layers 36a, 36b, 37a, 37b are laminated. However, the number of lamination layers of the acoustic reflection layer 38 is not limited. The number of lamination layers may be determined depending on a material to be used so that the quality factor Q increases to a maximum extent.
The fifth modification of the first embodiment is different from the fourth modification of the first embodiment in that the resonator 20 is provided on the acoustic reflection layer 38 on the substrate 11. The other configurations are as in the fourth modification of the first embodiment, so duplicated descriptions are omitted.
In the fifth modification of the first embodiment, a piezoelectric vibration excited in the piezoelectric film 15 is reflected and effectively confined within the resonator 20 by the acoustic reflection layer 38 provided below the resonator 20. Therefore, it is possible to prevent deterioration of the resonance characteristics of the resonator 20. Additionally, the highly orientation metal film 23 is provided on the amorphous metal film 22 of the bottom electrode 14. The piezoelectric film 15 provided on the oriented orientation metal film 23 can be strongly aligned in the c-axis direction. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15. Furthermore, since the bottom electrode 14 is placed on the even acoustic reflection layer 38, the mechanical strength of the piezoelectric film 15 may structurally increase.
Next, a manufacturing method of an FBAR according to the fifth modification of the first embodiment will be described with reference to the cross section views as shown in
As shown in
As shown in
As shown in
As shown in
The orientation of the Ni orientation metal film 23 deposited on the surface of the amorphous metal film 22 is determined by XRD. This confirms that the Ni orientation metal film 23 is highly aligned in the (111) orientation direction at an orientation FWHM of about 0.7°.
In the fifth modification of the first embodiment, the even amorphous metal layer 22 is deposited on the even amorphous metal film 22 surface. On the even surface of the amorphous metal film 22, the orientation metal film 23 such as Ni can be deposited to highly align in the (111) orientation direction. Thus, it is possible to deposit the piezoelectric film 15 to be highly oriented in the c-axis direction. Additionally, since the bottom electrode 14 is formed on the even surface of the acoustic reflection layer 38, it is possible to structurally increase the mechanical strength of the piezoelectric film 15.
Frequency characteristics of the manufactured FBAR are measured using a network analyzer and the like. For example, a resonant frequency of the FBAR is about two GHz. Additionally, an electromechanical coupling constant and a quality factor Q of the piezoelectric film 15 are evaluated from the resonance characteristics of the FBAR. For example, the electromechanical coupling constant is about 6.5% to about 6.7%. The quality factor Q is about 900 to about 1000 at a resonance point, and about 800 to about 900 at an antiresonance point. The electromechanical coupling constant and the quality factor Q are increased compared to an FBAR using an epitaxially grown single crystal piezoelectric film. Thus, the piezoelectric film 15 of the FBAR according to the fifth modification of the first embodiment may provide desirable piezoelectric characteristics.
According to the fifth modification of the first embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated deposition technology such as epitaxial growth. Thus, it is possible to achieve fin FBAR in which the electromechanical coupling constant and quality factor Q are improved.
(Sixth Modification Of The First Embodiment)
An FBAR according to a sixth modification of the first embodiment of the present invention includes a bottom electrode 14 having a low resistance metal film 21 placed on a surface of an insulating film 32, an amorphous metal film 22 placed on the surface of the low resistance metal film 21, and an orientation metal film 23 placed on a surface of the amorphous metal film 22, as shown in
The low resistance metal film 21 of the bottom electrode 14 is a metal having a low resistivity. The resistivity of the low resistance metal film 21 at room temperature is in a range from about 1×10−8 Ωm to about 10×10−8 Ωm, desirably about 1×10−8 Ωm to about 5×10−8 Ωm, and more desirably about 1×10−8 Ωm to about 3×10−8 Ωm. As the low resistance metal film 21, such a metal including Al, Cu, Au, Ag, Ir, Ni, Pt, Mo, W, and the like, may be used. Additionally, an alloy that contains a low resistivity metal such as Al, Cu, Au, or Ag, in major proportions with the addition of about 10% or less by composition, desirably about 5% or less of metals such as Ni, Pt, Mo, W, and the like, by composition, may be used. Furthermore, it may be permissible to add Si, carbon (C), and the like, to the alloy in an amount of about 5% or less by composition.
The sixth modification of the first embodiment differs from the third modification of the first embodiment in that, on the insulating film 32 surface, the bottom electrode 14 including the low resistance metal film 21, the amorphous metal film 22 and the orientation metal film 23 is placed on the cavity 17b provided in the substrate 11 and the insulating film 32. Other configurations are as in the third modification of the first embodiment, so duplicated descriptions are omitted.
In the sixth modification of the first embodiment, the oriented orientation metal film 23 is provided on the amorphous metal film 22 of the bottom electrode 14. The piezoelectric film 15 formed on the oriented orientation metal film 23 can be strongly aligned in the c-axis direction. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15. In addition, since the low resistance metal film 21 provided under the amorphous metal film 22 may be of low resistance, it is possible to prevent deterioration of high frequency characteristics.
Next, a manufacturing method of an FBAR according to the sixth modification of the first embodiment will be described with reference to the cross section views shown in
As shown in
As shown in
A piezoelectric layer such as AlN is deposited to a desired thickness by sputtering and the like. As shown in
An Al alloy layer is deposited on the piezoelectric film 15 by sputtering and the like. As shown in
The substrate 11 is thinned by polishing or the like from the bottom surface of the substrate 11 to a thickness of about 200 μm. As shown in
After the Al alloy layer of the low resistance layer 21, or the AlTa amorphous metal layer of the amorphous metal film 22 is deposited, the processing substrate 11 may be exposed once to the atmosphere to form an oxide film on a surface of the Al alloy layer or the AlTa amorphous metal layer. The formation of the surface oxide film may improve the orientation of an Al metal film of the orientation metal film 23 and an AlN piezoelectric layer of the piezoelectric film 15.
Additionally, the exposed amorphous metal film 22 that is not covered by the piezoelectric film 15 may be removed. The exposed amorphous metal 22 may be removed for example, by RIE or chemical dry etching (CDE) or the like, continuously after etching of the piezoelectric film 15.
According to the above descriptions, the low resistance metal film 21 is deposited at a thickness of about 200 nm. As the thickness of the low resistance metal film 21 is increased, the resistance is decreased. Therefore, a thicker film is desirable for the low resistance metal film 21. Additionally, the amorphous metal film 22 is deposited at a thickness of about 100 nm. The amorphous metal layer 22 can be used as an etching stop layer in etching of the piezoelectric film 15. For instance, the selectivity of etching for AlN to AlTa is varied depending on etching conditions. Thus, the thickness of the amorphous metal film 22 may be determined according to the selectivity of etching for the piezoelectric film 15 to the amorphous metal film 22. In addition, to ensure evenness of the amorphous metal film 22, a thickness of about 5 nm may be desirable. Furthermore, the orientation metal film 23 is deposited at a thickness of about 5 nm. The thickness of the orientation metal film 23, however, is not limited. The orientation metal film 23 may be in a thickness range from about 3 nm to about 10 nm.
When a resonance frequency of the FBAR, and metals used for the bottom and top electrodes 14, 16 are determined, the electrode thicknesses of the bottom and top electrodes 14, 16 are substantially uniquely determined by the density and the elastic constant of the metal. When both the density and elastic constant of the metal are small, the electrode thickness can be large. Therefore, in order to decrease the resistances of the bottom and top electrodes 14, 16, a metal having low resistivity, with a small density and a small elastic constant is desirable. For example, a metal such as Al and Cu, and an alloy containing Al, Cu. and the like, in major proportions, may be desirable.
Resistivity of AlTa used as the amorphous metal film 22 is about two orders of magnitude higher than a low resistivity metal such as Al. The orientation metal film 23 directly below the piezoelectric film 15 is removed during etching of the piezoelectric film 15. Since the amorphous metal film 22 serves as an etching stop layer in the etching of the piezoelectric film 15, the low resistance metal layer 21 under the amorphous metal layer 22 is not etched. In the sixth modification of the first embodiment, as the low resistance metal film 21, the Al alloy having a low resistivity, with a small density and a small elastic constant is used. Thus, the electrode thickness may be increased so as to lower the resistance of the bottom and top electrodes 14, 16. Therefore, it is possible to prevent deterioration of resonance characteristics in a high frequency region.
In the sixth modification of the first embodiment, the low resistance metal film 21 and the amorphous metal layer 22 are evenly deposited on the insulating film 32 surface. On the even surface of the amorphous metal film 22, the orientation metal film 23 such as Al can be deposited to highly align in the (111) orientation direction. As a result, it is possible to deposit the piezoelectric film 15 to be highly oriented in the c-axis direction. Additionally, since the bottom electrode 14 is formed to cover the cavity 17b, it is possible to increase the mechanical strength of the piezoelectric film 15.
(Seventh Modification Of The First Embodiment)
An FBAR according to a seventh modification of the first embodiment of the present invention includes a bottom electrode 14 having a low resistance metal film 21a embedded in the insulating film 32 via a barrier film 34, an amorphous metal film 22 placed on even surfaces of the embedded low resistance metal film 21a and insulating film 32, and an orientation metal film 23 placed on a surface of the amorphous metal film 22, as shown in
The seventh modification of the first embodiment is different from the sixth modification of the first embodiment in that the low resistance metal film 21a is provided by being embedded in the insulating film 32. Other configurations are as in the sixth modification of the first embodiment, so duplicated descriptions are omitted.
In the seventh modification of the first embodiment, the oriented orientation metal film 23 is provided on the amorphous metal film 22 of the bottom electrode 14. The piezoelectric film 15 formed on the oriented orientation metal film 23 can be highly oriented in the c-axis direction. Therefore, it is possible to ensure a large electromechanical coupling constant and a high quality factor Q of the piezoelectric film 15. In addition, since the low resistance metal film 21 is embedded in the insulating film 32, a step section of a inclined end portion of the bottom electrode 14 may decrease. Therefore, it is possible to prevent deterioration of orientation of the piezoelectric film 15 in the vicinity of the resonator 20, and to prevent the generation of a spurious vibration in the resonance characteristics of the FBAR.
Next, a manufacturing method of an FBAR according to the seventh modification of the first embodiment will be described with reference to the cross section views as shown in
As shown in
As shown in
As shown in
As shown in
The substrate 11 is thinned by polishing or the like from the bottom surface of the substrate 11 to a thickness of about 200 μm. As shown in
In the seventh medication of the first embodiment, as the low resistance metal film 21a, a Cu alloy having a low resistivity, with a small density and a small elastic constant is used. Thus, the electrode thickness may be thicken to lower the resistance of the bottom and top electrodes 14, 16. Therefore, it is possible to prevent deterioration of resonance characteristics in a high frequency region.
(Application Of The First Embodiment)
As an application of FBARs according to the first embodiment of the present invention, a phase locked loop (PLL) circuit will be described. The PLL circuit generates the reference frequency of a frequency synthesizer used for cellular phones and the like.
As shown in
The VCO 141 feeds back to the input of the amplifier 131 only the frequency components passing through the frequency variable filter 130. The VCO 141 has a plurality of FBARs 120a, 120b, 120c and 120d, and a plurality of variable capacitors C1, C2. As the FBARs 120a to 120d, the FBARs according to the first embodiment and the first to seventh modifications of the first embodiment may be used.
For instance, as shown in
For instance, as shown in
As shown in
The PLL circuit uses a frequency variable filter 130a identical to the frequency variable filter 130 of VCO 141 as a band-pass filter for filtering a communication signal. For example, an input RF signal is transmitted to LNA 146. An amplified signal in LNA 146 is sent to the frequency variable filter 130a. A filtered RF signal in the frequency variable filter 130a is sent to an input terminal of the down-conversion mixer 147.
On the other hand, a reference signal generated in the VCO 141 is transmitted as a local oscillation (LO) signal to another input terminal of the mixer 147. The mixer 147 produces a difference between the RF signal and the LO signal, so as to down-convert the RF signal to a base band signal in intermediate frequency (IF).
In the application of the first embodiment, the same DC control voltage Vctrl generated by the loop filter 145 is added to both the frequency variable filter 130a and the frequency variable filter 130 in the VOC 141. As a result, it is possible for the oscillation frequency of the VCO 141 to correspond with the central frequency of the passing band of the frequency variable filter 130a.
A variable capacitor as a piezoelectric thin film device according to a second embodiment of the present invention includes a piezoelectric actuator 40 and a fixed electrode 46, as shown in
The piezoelectric actuator 40 includes a bottom electrode 14, a piezoelectric film 15, a top electrode 16, and a supporting film. The bottom electrode 14 is provided to extend to a location above the fixed electrode 46 from a surface of the anchor 42. The piezoelectric film 15 is placed on a surface of the bottom electrode 14. The top electrode 16 faces the bottom electrode 14 to sandwich the piezoelectric film 15 with the bottom electrode 14. The supporting film 19 is placed on a surface of the top electrode 16. The fixed electrode 46 includes a dielectric film 45 and a conductor film 44 covered by the dielectric film 45.
For the anchor 42, the supporting film 19 and the dielectric film 45, an insulator such as Si3N4 or SiO2 is used. For the bottom electrode 14, an amorphous metal such as AlTa is used. For the piezoelectric film 15, a piezoelectric material such as AlN or ZnO is used. Additionally, for the top electrode 16 and the conductor film 44, a metal such as Al, Au, Pt, Cu, Ir, W, and Mo, which has a low resistance and can be easily processed, is desirably used.
The piezoelectric actuator 40 of the variable capacitor according to the second embodiment differs from the structure of the FBAR according to the first embodiment in that the piezoelectric actuator includes the supporting film 19 on the top electrode 16. The structures of the bottom electrode 14, the piezoelectric film 15, and the top electrode 16 are the same as the first embodiment, so duplicated descriptions are omitted.
The variable capacitor according to the second embodiment uses tunable capacitance Cvar between the conductor film 44 and the working end portion 49 of the bottom electrode 14. The capacitance Cvar varies depending on a change between the fixed electrode 46 and the bottom electrode 24 that is a movable electrode. When applying a voltage between the bottom electrode 14 and the top electrode 16 of the piezoelectric actuator 40, the piezoelectric film 15 distorts to expand or to contract due to the piezoelectric effect. The supporting film 19 provided on the top electrode 16 does not exhibit the piezoelectric effect. Thus, by expansion or contraction of the piezoelectric film 15, the piezoelectric actuator 40 is displaced in the direction perpendicular to the surface of the substrate 11. For instance, by expansion of the piezoelectric film 15 caused by tensile stress with applied voltage, the piezoelectric actuator 40 bends in the direction away from the surface of the substrate 11. On the other hand, by contraction of the piezoelectric film 15 caused by compression stress, the piezoelectric actuator 40 bends toward the surface of the substrate 11.
A movable range of the piezoelectric actuator 40 depends on the electromechanical coupling constant of the piezoelectric film 15. In the piezoelectric actuator 40, when the electromechanical coupling constant is large, the working end portion 49 can have a large displacement with a low driving voltage.
In the piezoelectric actuator 40 according to the second embodiment, since the piezoelectric film 15 is provided on the surface of the bottom electrode 14 of the amorphous metal film, the piezoelectric film 15 is highly oriented in the c-axis direction, which is a polarization direction. As a result, the electromechanical coupling constant increases to extend a movable range of the piezoelectric actuator 40. Therefore, a variable capacitance range of the variable capacitor using the piezoelectric actuator 40 may increase.
Next, a manufacturing method of a variable capacitor according to the second embodiment will be described with reference to the cross section views as shown in
As shown in
A metal layer such as Al is deposited on the surface of the insulating film 32 by sputtering and the like. The Al metal film is selectively removed by photolithography, etching and the like to form a conductor film 44. A dielectric layer such as Si3N4 is deposited on the insulating film 32. The dielectric layer is selectively removed by photolithography, etching and the like to form a dielectric film 45 covering the conductor film 44. Thus, a fixed electrode 46 is formed.
As shown in
As shown in
In the second embodiment, the bottom electrode 14 of the even amorphous metal film is deposited on the surface of the sacrificial layer 12b planarized to a level of the surface of the anchor 42. On the even surface of the amorphous metal film, the piezoelectric film 15 can be highly oriented in the c-axis direction. The deposited piezoelectric film 15 is evaluated by XRD to determine the orientation FWHM. The measurement results show that the piezoelectric film 15 has an orientation FWHM of about 2.1°. Thus, it is determined that the piezoelectric film 15 is highly oriented in the c-axis direction.
Variable characteristics for capacitance of the manufactured variable capacitor are measured. For example, a tuning voltage of the piezoelectric actuator 40 is applied between the bottom and top electrodes 14, 16 in a range from 0 V to 3 V. Capacitance between the fixed electrode 46 and the bottom electrode 14 varies from the minimum of 0.34 pF to the maximum of 51 pF. A capacitance ratio of the maximum to the minimum is about 150. Thus, a large variable capacitance range is achieved.
According to the second embodiment, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated deposition technology such as epitaxial growth. Thus, it is possible to achieve a variable capacitor in which a variable capacitance range that can be increased by a low tuning voltage.
In addition, in the second embodiment, the piezoelectric actuator 40 is used in a variable capacitor which includes the fixed electrode 46 having the conductor film 44 covered with the dielectric film 45, as a piezoelectric thin film device. However, it may be possible to apply the piezoelectric actuator 40 to a micro switch which includes a fixed electrode having a conductor film alone.
(Modification Of The Second Embodiment)
A micro switch as a piezoelectric thin film device according to a modification of the second embodiment of the present invention includes a piezoelectric actuator 40a and a fixed electrode 46a, as shown in
The piezoelectric actuator 40a includes a bottom electrode 14, a piezoelectric film 15, a top electrode 16, and a supporting film. The bottom electrode 14 is provided to extend to a location above the fixed electrode 46a from a surface of the anchor 42. The piezoelectric film 15 is placed on a surface of the bottom electrode 14. The top electrode 16 faces the bottom electrode 14 to sandwich the piezoelectric film 15 with the bottom electrode 14. The supporting film 19 is placed on the top electrode 16. The bottom electrode 14 has an amorphous metal film 22 and an orientation metal film 23.
The amorphous metal film 22 of the bottom electrode 14 is an amorphous metal such as AlTa. The orientation metal film 23 is a metal which is easily oriented in the (111) orientation or in the (110) orientation direction, such as an fcc metal or a bcc metal. The fixed electrode 46a is a metal which has a low resistance and is easily processed, such as Al, Au, Pt, Cu, Ir, W, or Mo.
The piezoelectric actuator 40a of the micro switch according to the modification of the second embodiment differs from the second embodiment in that the bottom electrode 14 includes the amorphous metal film 22 and the orientation metal film 23. Other configurations are as in the second embodiment, so duplicated descriptions are omitted.
When applying a voltage between the bottom electrode 14 and the top electrode 16 of the piezoelectric actuator 40a, the piezoelectric film 15 distorts to expand or to contract due to the piezoelectric effect. For example, by contraction of the piezoelectric film 15 caused by compressive stress of an applied voltage, the piezoelectric actuator 40a bends toward the surface of the substrate 11. The bottom electrode 14 of the piezoelectric actuator 40a comes into contact with the fixed electrode 46a to switch the micro switch into a conducting state.
A movable range of the piezoelectric actuator 40a depends on the electromechanical coupling constant of the piezoelectric film 15. When the electromechanical coupling constant is large, the working end portion 49 can be greatly displaced by a low driving voltage in the piezoelectric actuator 40a.
In the piezoelectric actuator 40a according to the modification of the second embodiment, since the piezoelectric film 15 is provided on the surface of the orientation metal film 23 which is highly aligned in the (111) orientation or in the (110) orientation direction on the amorphous metal film 22, the piezoelectric film 15 is highly oriented in the c-axis direction, which is the polarization direction. As a result, the electromechanical coupling constant increases to expand a movable range of the piezoelectric actuator 40a. Therefore, it is possible to drive the micro switch having the piezoelectric actuator 40a at a low control voltage.
Next, a manufacturing method of a micro switch according to the modification of the second embodiment will be described with reference to the cross section views as shown in
As shown in
As shown in
An amorphous metal layer such as Al0.4Ta0.6, a bottom metal layer such as Al, a piezoelectric layer such as AlN, a top metal layer such as Al, and an insulator layer such as SiO2 are deposited on a surface of the sacrificial layer 12b by magnetron sputtering and the like. As shown in
As shown in
In the modification of the second embodiment, the even amorphous metal film is deposited on the surface of the sacrificial layer 12b planarized to a level of the surface of the anchor 42. On the even surface of the amorphous metal layer 22, the orientation metal film 23 can be deposited to be highly oriented in the (111) orientation direction. As a result, the piezoelectric film 15 can be highly oriented in the c axis direction. The deposited piezoelectric film 15 is evaluated by XRD to determine the orientation FWHM. The measurement results show that the piezoelectric film 15 has an orientation FWHM of about 2.4°. Thus, it is determined that the piezoelectric film 15 is highly oriented in the c-axis direction.
Electrical characteristics of the manufactured micro switch are measured. For example, a control voltage of the piezoelectric actuator 40a is applied between the top and bottom electrodes 14, 16 to evaluate an insulation resistance and “ON” resistance at a frequency of 2 GHz. At a control voltage of 0 V, the insulation resistance between the fixed electrode 46a and the bottom electrode 14 is about 28 dB. At a control voltage of 3 V, the “ON” resistance between the fixed electrode 46a and the bottom electrode 14 is about 0.3 dB. Thus, in a micro switch according to the modification of the second embodiment, low control voltage driving, a small “ON” resistance, and a high insulation resistance may be achieved in a high frequency region.
According to the modification of the second embodiments, it is possible to highly orient the piezoelectric film 15 in the c-axis direction without using an expensive and complicated deposition technology such as epitaxial growth. Thus, it is possible to achieve a micro switch having improved high-frequency characteristics and driven by a low control voltage.
In the modification of the second embodiment, the piezoelectric actuator 40a is used in a micro switch having a metal film as the fixed electrode 46a. However, it may be possible to apply the piezoelectric actuator 40a to a variable capacitor having a fixed electrode in which a conductor film is covered by a dielectric film as shown in
The present invention has been described as mentioned above. However the descriptions and drawings that constitute a portion of this disclosure should not be perceived as limiting this invention. Various alternative embodiments and operational techniques will become clear to persons skilled in the art from this disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-020132 | Jan 2004 | JP | national |
| 2005-001346 | Jan 2005 | JP | national |
| 2005-007850 | Jan 2005 | JP | national |
This application is a divisional of U.S. application Ser. No. 11/043,257, filed on Jan. 27, 2005 and is based upon and claims the benefit of priority from prior Japanese patent application P2004-020132 filed on Jan. 28, 2004, P2005-001346 filed on Jan. 6, 2005, and P2005-007850 filed on Jan. 14, 2005; the entire contents of which are incorporated by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4965611 | Pan et al. | Oct 1990 | A |
| 5187561 | Hasunuma et al. | Feb 1993 | A |
| 6054770 | Toyoda et al. | Apr 2000 | A |
| 6060818 | Ruby et al. | May 2000 | A |
| 6350017 | Kamada | Feb 2002 | B1 |
| 6384697 | Ruby | May 2002 | B1 |
| 6466105 | Lobl et al. | Oct 2002 | B1 |
| 6601276 | Barber | Aug 2003 | B2 |
| 6711793 | Sumi | Mar 2004 | B2 |
| 7489067 | Metzger et al. | Feb 2009 | B2 |
| 20020008437 | Inoue et al. | Jan 2002 | A1 |
| 20040012463 | Kawakubo et al. | Jan 2004 | A1 |
| 20040125970 | Kawakubo | Jul 2004 | A1 |
| 20040172798 | Ruby et al. | Sep 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 60-147180 | Aug 1985 | JP |
| 62-156265 | Jul 1987 | JP |
| 6-295181 | Oct 1994 | JP |
| 07-187894 | Jul 1995 | JP |
| 9-45973 | Feb 1997 | JP |
| 11-330388 | Nov 1999 | JP |
| 2000-69594 | Mar 2000 | JP |
| 2000-156624 | Jun 2000 | JP |
| 2000-334956 | Dec 2000 | JP |
| 2001-94373 | Apr 2001 | JP |
| 2002-140075 | May 2002 | JP |
| 2002-372974 | Dec 2002 | JP |
| 2003-198319 | Jul 2003 | JP |
| 2004-64785 | Feb 2004 | JP |
| 2004-64786 | Feb 2004 | JP |
| 2004-208221 | Jul 2004 | JP |
| 2005-109702 | Apr 2005 | JP |
| WO9945598 | Sep 1999 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20080072408 A1 | Mar 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11043257 | Jan 2005 | US |
| Child | 11946910 | US |