Claims
- 1. A pigmented polymer blend comprising from about 60 parts to about 99.9 by weight of a pigmented, non-transparent, non-translucent thermoplastic resin wherein there is present from about 0.1 part by weight to about 30 parts by weight of pigment, per 100 parts of resin, said thermoplastic resin being selected from the class consisting of polyesters, polycarbonates and mixtures thereof, and from 0.1 part to about 40 parts of a sequentially produced multi-stage polymer comprising;
- (a) A polymer core of at least about 10 parts, based on the weight of the multi-stage polymer, said core being polymerized from a styrenic monomer or a mixture of a styrenic monomer and a second monomer which is a non-styrenic monovinylidene comonomer and wherein there is at least about 50 percent by weight of said styrenic monomer in said core said core being crosslinked;
- (b) A second stage comprising a polymeric soft stage polymerized from an alkyl acrylate monomer or a mixture of an alkyl acrylate and up to 50 percent of a non-crosslinking vinylidene comonomer, said soft stage being crosslinked and graftlinked; and
- (c) A rigid thermoplastic outer stage polymerized from at least one monovinylidene monomer.
- 2. A polymer blend according to claim 1 wherein said core is crosslinked with a crosslinker which is present in an amount of from about 0.1 to about 10 percent based on the weight of the core.
- 3. A polymer blend according to claim 2 wherein said crosslinker is selected from the class consisting of polyvinyl benzene, divinyl esters of di or tri-basic acids, dialkyl esters of polyfunctional acids, diallyl esters of polyfunctional acids, divinyl esters of polyhydric alcohols, di or tri methacrylic acid esters of polyhydric alcohols, di or tri acrylic acid esters of polyhydric alcohols, and mixtures thereof.
- 4. A polymer blend according to claim 2 wherein said crosslinker is selected from the class consisting of trimethylol propane triacrylate, divinyl adipate, dialkyl phthalate, diallyl maleate, diallyl fumarate, divinyl ether of ethylene glycol, ethylene glycol dimethacrylate, propylene glycol dimethacrylate, 1,3-butylene glycol dimethacrylate, 1,4-butylene glycol dimethacrylate, ethylene glycol diacrylate, propylene glycol diacrylate, 1,3-butylene glycol diacrylate, 1,4-butylene glycol diacrylate, divinyl benzene, trivinyl benzene, and mixtures thereof.
- 5. A polymer blend according to claim 1 wherein said styrenic monomer is selected from the class consisting of styrene, alpha-methyl styrene, monochlorostyrene, t-butylstyrene, vinyl toluene, p-isopropyl styrene, 3,4-dimethyl styrene, p-bromostyrene, 3,4-dichlorostyrene, and mixtures thereof.
- 6. A polymer blend according to claim 1 wherein at least one additional stage, intermediate said soft stage and said outer stage, is present.
- 7. A polymer blend according to claim 6 wherein said additional stage is polymerized from a styrenic monomer.
- 8. A polymer blend according to claim 6 wherein said additional stage is polymerized from a styrenic monomer and a crosslinker.
- 9. A polymer blend according to claim 1 wherein said second monomer is a non-styrenic non-crosslinking monovinylidene monomer.
- 10. A polymer blend according to claim 1 wherein said second monomer is an alkyl methacrylate.
- 11. A polymer blend according to claim 1 wherein said second monomer is a vinyl ester.
- 12. A polymer blend acording to claim 1 wherein said second monomer is acrylonitrile.
- 13. A polymer blend according to claim 1 wherein said second monomer is methacrylic acid.
- 14. A polymer blend according to claim 1 wherein said second monomer is acrylic acid.
- 15. A polymer blend according to claim 1 wherein said second monomer is an alkyl methacrylate having from 1 to about 8 carbon atoms in the alkyl portion.
- 16. A polymer blend according to claim 15 wherein said alkyl methacrylate is methyl methacrylate.
- 17. A polymer blend according to claim 1 wherein said second monomer is an alkyl acrylate having from 1 to about 8 carbon atoms in the alkyl portion.
- 18. A polymer blend according to claim 17 wherein said alkyl acrylate is selected from the class consisting of methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate and mixtures thereof.
- 19. A polymer blend according to claim 1 wherein said second monomer is present in an amount of from about 1 percent to about 20 percent.
- 20. A polymer blend according to claim 2 wherein said crosslinker is present in an amount of from about 0.1 to about 5 percent based on the weight of the core.
- 21. A polymer blend according to claim 1 wherein said core comprises from about 10 to about 40 parts by weight, based on the weight of the multi-stage polymer.
- 22. A polymer blend according to claim 1 wherein said core comprises from about 10 to about 30 parts by weight, based on the weight of the multi-stage polymer, and an additional styrenic stage is present and is intermediate said soft stage and said outer stage.
- 23. A polymer blend according to claim 1 wherein said soft stage comprises from about 40 to about 80 parts by weight, based on the weight of the multi-stage polymer.
- 24. A polymer blend according to claim 1 wherein said soft stage comprises from about 60 to about 80 parts by weight, based on the weight of the multi-stage polymer.
- 25. A polymer blend according to claim 1 wherein said soft stage is polymerized from an alkyl acrylate monomer having from 1 to about 8 carbon atoms in the alkyl portion thereof.
- 26. A polymer blend according to claim 25 wherein said alkyl acrylate is selected from the class consisting of ethyl acrylate, n-butyl acrylate, 2-ethylhexyl acrylate and isobutyl acrylate.
- 27. A polymer blend according to claim 25 wherein there is present a crosslinker in an amount of from about 0.1 to about 10 percent based on the weight of the soft stage.
- 28. A polymer blend according to claim 25 wherein there is present a graftlinker in an amount of from 0.1 to about 10 percent based on the weight of the soft stage.
- 29. A polymer blend according to claim 1 wherein said soft stage contains from about 0.1 to about 10 percent of a crosslinker and from about 0.1 to about 10 percent of a graftlinker, both separately based on the weight of the soft stage.
- 30. A polymer blend according to claim 1 wherein said comonomer of said soft stage is selected from the class consisting of acrylonitrile, alkyl methacrylates having from 1 to about 8 carbon atoms in the alkyl portion, styrenics, isoprene, chloroprene, and mixtures thereof.
- 31. A polymer blend according to claim 1 wherein said outer stage is polymerized from a C.sub.1 to about C.sub.8 alkyl methacrylate.
- 32. A polymer blend according to claim 1 wherein said outer stage is polymerized from the class consisting of methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, t-butyl methacrylate, acrylonitrile, isobornyl methacrylate, and mixtures thereof.
- 33. A polymer blend according to claim 1 wherein said outer stage comprises from about 10 to about 35 parts based on the weight of the multi-stage polymer.
- 34. A polymer blend according to claim 1 wherein said polyester is a poly(C.sub.1 to C.sub.8)alkylene terephthalate.
- 35. A polymer blend according to claim 1 wherein said polyester is poly(butylene terephthalate).
- 36. A polymer blend according to claim 1 wherein said polycarbonate is an aromatic polycarbonate.
- 37. A polymer blend according to claim 1 wherein said polycarbonate is derived from bisphenol A.
- 38. A polymer blend according to claim 1 wherein said pigmented thermoplastic resin is a mixture of a polyester and a polycarbonate and a pigment.
- 39. A polymer blend according to claim 1 wherein said pigmented thermoplastic resin is a mixture of an aromatic polycarbonate and poly(butylene terephthalate) and a pigment.
- 40. A polymer blend according to claim 39 wherein there are about equal weight amounts of said aromatic polycarbonate and said poly(butylene terephthalate).
- 41. A polymer blend according to claim 1 wherein said pigment is present in an amount of from about 0.1 to about 15 parts by weight per 100 parts of thermoplastic resin.
- 42. A polymer blend according to claim 1 wherein said pigment is present in an amount of from about 2 to about 5 parts by weight per 100 parts of thermoplastic resin.
- 43. A polymer blend according to claim 1 wherein said polycarbonate is present in an amount of from about 25 percent to about 75 percent and said polyester is present in an amount of from about 75 percent to about 25 percent based on the total weight of non-pigmented thermoplastic resin.
- 44. In a process for enhancing the intensity of the color of a pigmented non-transparent and non-translucent thermoplastic polymer resin wherein said pigmented resin is present in an amount of from about 60 parts to about 99.9 parts by weight and said pigment is present in an amount of from about 0.1 part by weight to about 30 parts by weight, per 100 parts of resin, said thermoplastic resin being selected from the class consisting of polyesters, polycarbonates and mixtures thereof, and said resin contains an impact modifier, the improvement comprising blending with said resin, as the impact modifier, from 0.1 part to about 40 parts of a sequentially produced multi-stage polymer comprising;
- (a) A polymer core of at least about 10 parts, based on the weight of the multi-stage polymer, said core being polymerized from a styrenic monomer or a mixture of a styrenic monomer and a second monomer which is a non-styrenic monovinylidene comonomer and wherein there is at least about 50 percent by weight of said styrenic monomer in said core said core being crosslinked;
- (b) A second stage comprising a polymeric soft stage polymerized from an alkyl acrylate monomer or a mixture of an alkyl acrylate and up to 50 percent of a non-crosslinking vinylidene comonomer, said soft stage being crosslinked and graftlinked; and
- (c) A rigid thermoplastic outer stage polymerized from at least one monovinylidene monomer whereby the intensity of the color of said pigmented resin is enhanced while substantially maintaining the impact resistance of articles molded from said pigmented resin.
Parent Case Info
This is a continuation of application Ser. No. 594,161 filed Mar. 30, 1984, now abandoned, which is in turn a continuation-in-part of application Ser. No. 513,741 filed July 22, 1983, now abandoned.
US Referenced Citations (9)
Foreign Referenced Citations (1)
Number |
Date |
Country |
53-018661 |
Feb 1978 |
JPX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
594161 |
Mar 1984 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
513741 |
Jul 1983 |
|