Patent Grant
7498066
This invention relates to methods and apparatus for enhanced plasma-assisted coating, and particularly for coating one or more objects using an electromagnetic radiation-induced plasma with a plasma catalyst and an energized coating material.
Conventional plasma-assisted coating processes normally involve igniting a plasma in a partial vacuum, for example, during magnetron or radio-frequency sputter deposition. In some instances, material-processing flexibility is limited because of the fixed shape and size of the sputter deposition chamber and the need to maintain a vacuum seal. When coating large parts, large containers have been required, but such containers can make it difficult to maintain a reliable vacuum, which can significantly increase costs and slow down the process speed. Thus, vacuum integrity and the object size can affect efficiency and throughput during a plasma-assisted coating process.
Another plasma-assisted coating method is plasma spray deposition. During this method, material is reportedly deposited on a surface by compounding a buildup of “splats” of molten material on the surface. The heat of the plasma either melts or vaporizes material injected into path of the plasma ejected from a nozzle, and the material impinges on the surface of a work piece at high velocity. Typical coatings that have been reported by this method are thermal barrier coatings and oxide coatings. However, when coating an object with raised or depressed surface features, or an object with a complex shape, such as a gear or fan blade, the object must be positioned and appropriately rotated in the path of the plasma spray produced by a focused nozzle. Also, plasma spray deposition typically requires expensive equipment and can only be used on a limited range of materials because of the relatively high heat and thermal shock inherent in this technique.
Methods and apparatus for coating a surface area of an object can be provided. In one embodiment, a catalyzed coating plasma can be formed in a cavity by subjecting a gas to an amount of electromagnetic radiation in the presence of a plasma catalyst, placing at least one coating material in a position that is separate from the plasma and in fluid communication with it, energizing at least a portion of the at least one coating material so that the energized portion can be added to the plasma, and allowing the at least one coating material to deposit on the surface area of the object to form a coating.
In another embodiment, a material deposition system for fabricating coatings is provided. The system can include a first vessel in which a first cavity is formed, an electromagnetic radiation source coupled to the cavity such that the electromagnetic radiation source can direct electromagnetic radiation into the first cavity during the deposition process, a gas source coupled to the first cavity so that a gas can flow into the cavity during the deposition process, an energy source configured to energize at least one coating material placed in communication with or in the cavity so that the energized portion can be added to the plasma, and at least one plasma catalyst in the presence of the radiation (e.g., located either in the first cavity, near the first cavity, or in and near the first cavity).
Plasma catalysts for initiating, modulating, and sustaining plasmas can also be provided. The plasma catalyst may be passive or active. A passive plasma catalyst can include any object capable of inducing a plasma by deforming a local electric field (e.g., an electromagnetic field) consistent with this invention, without necessarily adding additional energy. An active plasma catalyst can be any particle or high energy wave packet capable of transferring a sufficient amount of energy to a gaseous atom or molecule to remove at least one electron from the gaseous atom or molecule in the presence of electromagnetic radiation. In both the passive and active cases, a plasma catalyst can improve, or relax, the environmental conditions required to ignite a coating plasma.
Additional plasma catalysts, and methods and apparatus for igniting, modulating, and sustaining a plasma for enhanced coating of objects consistent with this invention are also provided.
Further aspects of the invention will be apparent upon consideration of the following detailed description, taken in conjunction with the accompanying drawings, in which like reference characters refer to like parts throughout, and in which:
This invention can relate to methods and apparatus for initiating, modulating, and sustaining a plasma for a variety of enhanced coating applications, including, for example, generating high temperatures for heat-treating, synthesizing and depositing carbides, nitrides, borides, oxides, and other materials, as well as for applications that relate to manufacturing of coated objects, such as automobile or other vehicular components.
This invention can be used for controllable plasma-assisted coating processes that may lower energy costs and increase deposition efficiency and manufacturing flexibility.
One coating method consistent with this invention can include adding a gas, a plasma catalyst, and electromagnetic radiation to a cavity for catalyzing a coating plasma. As used herein, any plasma formed with a plasma catalyst for the purpose of coating one or more objects is a “catalyzed coating plasma,” or more simply, “a coating plasma.” The catalyst can be passive or active. A passive plasma catalyst can include any object capable of inducing a plasma by deforming a local electric field (e.g., an electromagnetic field) consistent with this invention without necessarily adding additional energy through the catalyst, such as by applying a voltage to create a spark. An active plasma catalyst, on the other hand, may be any particle or high energy wave packet capable of transferring a sufficient amount of energy to a gaseous atom or molecule to remove at least one electron from the gaseous atom or molecule, in the presence of electromagnetic radiation.
The following commonly owned, concurrently filed U.S. patent applications are hereby incorporated by reference in their entireties: U.S. patent application Ser. No. 10/513,221, PCT Application U.S. 03/14132, now expired, U.S. patent application Ser. No. 10/513,394, U.S. patent application Ser. No. 10/513,305, U.S. patent application Ser. No. 10/513,607, U.S. patent application Ser. No. 10/449,600, PCT Application U.S. 03/14034, now expired, U.S. patent application Ser, No. 10/430,416, U.S. patent application Ser. No. 10/430,415, PCT Application U.S. 03/14133, now expired, U.S. patent application Ser. No. 10/513,606, U.S. patent application Ser. No. 10/513,309, U.S. patent application Ser. No. 10/513,220, PCT Application U.S. 03/14122, U.S. patent application Ser. No. 10/513,397, U.S. patent application Ser. No. 10/513,605, PCT Application U.S. 03/14137, now expired, U.S. patent application Ser. No. 10/430,426, PCT Application U.S. 03/14121, now expired, U.S. patent application Ser. No. 10/513,604, and PCT Application U.S. 03/14135, now expired.
Illustrative Plasma System
In one embodiment, cavity 12 is formed in a vessel made of ceramic. Due to the extremely high temperatures that can be achieved with plasmas consistent with this invention, the upper temperature limit for processing is restricted only by the melting point of the ceramic used to make the vessel. In one experiment, for example, a ceramic capable of withstanding about 3,000 degrees Fahrenheit was used. For example, the ceramic material can include, by weight, 29.8% silica, 68.2% alumina, 0.4% ferric oxide, 1% titania, 0.1% lime, 0.1% magnesia, 0.4% alkalis, which is sold under Model No. LW-30 by New Castle Refractories Company, of New Castle, Pa. It will be appreciated by those of ordinary skill in the art, however, that other materials, such as quartz, and those different (e.g., those having higher melting temperatures) from the ceramic material described above, can also be used consistent with the invention.
In one successful experiment, a plasma was formed in a partially open cavity inside a first brick and topped with a second brick. The cavity had dimensions of about 2 inches by about 2 inches by about 1.5 inches. At least two holes were also provided in the brick in communication with the cavity: one for viewing the plasma and at least one hole for providing the gas. The size of the cavity can depend on the desired plasma process being performed. Also, the cavity should at least be configured to prevent the plasma from rising/floating away from the primary processing region, even though the plasma may not contact the object being coated.
Cavity 12 can be connected to one or more gas sources 24 (e.g., a source of argon, nitrogen, hydrogen, xenon, krypton, etc.) by line 20 and control valve 22, which may be powered by power supply 28. Line 20 may be tubing (e.g., between about 1/16 inch and about ¼ inch, such as about ⅛″), but could be any device capable of supplying gas. Also, if desired, a vacuum pump can be connected to the chamber to remove any undesirable fumes that may be generated during plasma processing. In one embodiment, gas can flow in and/or out of cavity 12 through one or more gaps in a multi-part vessel. Thus, gas ports consistent with this invention need not be distinct holes and can take on other forms as well, such as many small distributed holes.
A radiation leak detector (not shown) was installed near source 26 and waveguide 30 and connected to a safety interlock system to automatically turn off the electromagnetic radiation power supply if a leak above a predefined safety limit, such as one specified by the FCC and/or OSHA (e.g., 5 mW/cm2), was detected.
Electromagnetic radiation source 26, which can be powered by electrical power supply 28, directs electromagnetic radiation into chamber 14 through one or more waveguides 30. It will be appreciated by those of ordinary skill in the art that electromagnetic source 26 can be connected directly to chamber 14 or cavity 12, thereby eliminating waveguide 30. The electromagnetic radiation entering chamber 14 or cavity 12 is used to ignite a plasma within the cavity. This catalyzed plasma can be substantially modulated or sustained and confined to the cavity by coupling additional electromagnetic radiation with the catalyst.
Electromagnetic radiation can be supplied through circulator 32 and tuner 34 (e.g., 3-stub tuner). Tuner 34 can be used to minimize the reflected power as a function of changing ignition or processing conditions, especially before the catalyzed plasma has formed because electromagnetic radiation will be strongly absorbed by the plasma after its formation.
As explained more fully below, the location of electromagnetic radiation-transmissive cavity 12 in chamber 14 may not be critical if chamber 14 supports multiple modes, and especially when the modes are continually or periodically mixed. As also explained more fully below, motor 36 can be connected to mode-mixer 38 for making the time-averaged electromagnetic radiation energy distribution substantially uniform throughout chamber 14. Furthermore, window 40 (e.g., a quartz window) can be disposed in one wall of chamber 14 adjacent to cavity 12, permitting temperature sensor 42 (e.g., an optical pyrometer) to be used to view a process inside cavity 12. In one embodiment, the optical pyrometer output can increase from zero volts as the temperature rises to within the tracking range. The pyrometer can be used to sense radiant intensities at two or more wavelengths and to fit those intensities using Planck's law to determine the temperature of the work piece. The pyrometer can also establish the temperature of a species present in the plasma by monitoring its excited state population distribution from the emission intensities at two discrete transitions.
Sensor 42 can develop output signals as a function of the temperature or any other monitorable condition associated with a work piece (not shown) within cavity 12 and provide the signals to controller 44. Dual temperature sensing and heating, as well as automated cooling rate and gas flow controls can also be used. Controller 44 in turn can be used to control operation of power supply 28, which can have one output connected to electromagnetic radiation source 26 as described above and another output connected to valve 22 to control gas flow into cavity 12.
The invention has been practiced with equal success employing electromagnetic radiation sources at both 915 MHz and 2.45 GHz, provided by Communications and Power Industries (CPI), although radiation having any frequency less than about 333 GHz can be used. The 2.45 GHz system provided continuously variable electromagnetic radiation power from about 0.5 kilowatts to about 5.0 kilowatts. Consistent with one embodiment of the present invention, the electromagnetic radiation power density during deposition may be between about 0.05 W/cm3 and about 100 W/cm3. For example, about 2.5 W/cm3 was successfully used. A 3-stub tuner allowed impedance matching for maximum power transfer and a dual directional coupler was used to measure forward and reflected powers. Also, optical pyrometers were used for remote sensing of the work piece temperature.
As mentioned above, radiation having any frequency less than-about 333 GHz can be used consistent with this invention. For example, frequencies, such as power line frequencies (about 50 Hz to about 60 Hz), can be used, although the pressure of the gas from which the plasma is formed may be lowered to assist with plasma ignition. Also, any radio frequency or microwave frequency can be used consistent with this invention, including frequencies greater than about 100 kHz. In most cases, the gas pressure for such relatively high frequencies need not be lowered to ignite, modulate, or sustain a plasma, thereby enabling many plasma-processes to occur at atmospheric pressures and above.
The equipment was computer controlled using LabVIEW® 6i software, which provided real-time temperature monitoring and electromagnetic radiation power control. LabVIEW® graphical development environment was used to automate data acquisition, instrument control, measurement analysis, and data presentation. LabVIEW® is available from the National Instruments Corporation, of Austin, Tex.
Noise was reduced by using sliding averages of suitable number of data points. Also, to improve speed and computational efficiency, the number of stored data points in the buffer array were limited by using shift-registers and buffer-sizing. The pyrometer measured the temperature of a sensitive area of about 1 cm2, which was used to calculate an average temperature. The pyrometer sensed radiant intensities at two wavelengths and fit those intensities using Planck's law to determine the temperature. It will be appreciated, however, that other devices and methods for monitoring and controlling temperature are also available and can be used consistent with this invention. Control software that can be used consistent with this invention is described, for example, in commonly owned, concurrently filed PCT Application U.S. 03/14135, now expired, which is hereby incorporated by reference in its entirety.
Chamber 14 had several glass-covered viewing ports with electromagnetic radiation shields and one quartz window for pyrometer access. Several ports for connection to a vacuum pump and a gas source were also provided, although not necessarily used.
System 10 also included a closed-loop de-ionized water cooling system (not shown) with an external heat exchanger cooled by tap water. During operation, the de-ionized water first cooled the magnetron, then the load-dump in the circulator (used to protect the magnetron), and finally the electromagnetic radiation chamber through water channels welded on the outer surface of the chamber.
Plasma Catalysts
As mentioned previously, a plasma catalyst consistent with this invention can include one or more different materials and may be either passive or active. A plasma catalyst can be used, among other things, to ignite, modulate, and/or sustain a coating plasma at a gas pressure that is less than, equal to, or greater than atmospheric pressure.
One method of forming a plasma consistent with this invention can include subjecting a gas in a cavity to electromagnetic radiation having a frequency less than about 333 GHz in the presence of a passive plasma catalyst. A passive plasma catalyst consistent with this invention can include any object capable of inducing a plasma by deforming a local electric field (e.g., an electromagnetic field) consistent with this invention, without necessarily adding additional energy through the catalyst, such as by applying an electric voltage to create a spark.
A passive plasma catalyst consistent with this invention can also be a nano-particle or a nano-tube. As used herein, the term “nano-particle” can include any particle having a maximum physical dimension less than about 100 nm that is at least electrically semi-conductive. Also, both single-walled and multi-walled carbon nanotubes, doped and undoped, can be particularly effective for igniting plasmas consistent with this invention because of their exceptional electrical conductivity and elongated shape. The nanotubes can have any convenient length and can be a powder fixed to a substrate. If fixed, the nanotubes can be oriented randomly on the surface of the substrate or fixed to the substrate (e.g., at some predetermined orientation) while the plasma is ignited or sustained.
A passive plasma catalyst can also be a powder consistent with this invention, and need not be made of nano-particles or nano-tubes. It can be formed, for example, from fibers, dust particles, flakes, sheets, etc. When in powder form, the catalyst can be suspended, at least temporarily, in a gas. By suspending the powder in the gas, the powder can be quickly dispersed throughout the cavity and more easily consumed, if desired.
In one embodiment, the powder catalyst can be carried into the cavity and at least temporarily suspended with a carrier gas. The carrier gas can be the same or different from the gas that forms the plasma. Also, the powder can be added to the gas prior to being introduced to the cavity. For example, as shown in
In one experiment, a coating plasma was ignited in a cavity by placing a pile of carbon fiber powder in a copper pipe that extended into the cavity. Although sufficient electromagnetic (microwave) radiation was directed into the cavity, the copper pipe shielded the powder from the radiation and no plasma ignition took place. However, once a carrier gas began flowing through the pipe, forcing the powder out of the pipe and into the cavity, and thereby subjecting the powder to the electromagnetic radiation, a plasma was nearly instantaneously ignited in the cavity.
A powder plasma catalyst consistent with this invention can be substantially non-combustible, thus it need not contain oxygen, or burn in the presence of oxygen. Thus, as mentioned above, the catalyst can include a metal, carbon, a carbon-based alloy, a carbon-based composite, an electrically conductive polymer, a conductive silicone elastomer, a polymer nanocomposite, an organic-inorganic composite, and any combination thereof.
Also, powder catalysts can be substantially uniformly distributed in the plasma cavity (e.g., when suspended in a gas), and plasma ignition can be precisely controlled within the cavity. Uniform ignition can be important in certain applications, including those applications requiring brief plasma exposures, such as in the form of one or more bursts. Still, a certain amount of time can be required for a powder catalyst to distribute itself throughout a cavity, especially in complicated, multi-chamber cavities. Therefore, consistent with another aspect of this invention, a powder catalyst can be introduced into the cavity through a plurality of ignition ports to more rapidly obtain a more uniform catalyst distribution therein (see below).
In addition to powder, a passive plasma catalyst consistent with this invention can include, for example, one or more microscopic or macroscopic fibers, sheets, needles, threads, strands, filaments, yarns, twines, shavings, slivers, chips, woven fabrics, tape, whiskers, or any combination thereof, In these cases, the plasma catalyst can have at least one portion with one physical dimension substantially larger than another physical dimension. For example, the ratio between at least two orthogonal dimensions should be at least about 1:2, but could be greater than about 1:5, or even greater than about 1:10.
Thus, a passive plasma catalyst can include at least one portion of material that is relatively thin compared to its length. A bundle of catalysts (e.g., fibers) may also be used and can include, for example, a section of graphite tape. In one experiment, a section of tape having approximately thirty thousand strands of graphite fiber, each about 2-3 microns in diameter, was successfully used. The number of fibers in and the length of a bundle are not critical to igniting, modulating, or sustaining the plasma. For example, satisfactory results have been obtained using a section of graphite tape about one-quarter inch long. One type of carbon fiber that has been successfully used consistent with this invention is sold under the trademark Magnamite®, Model No. AS4C-GP3K, by the Hexcel Corporation of Salt Lake City, Utah. Also, silicon-carbide fibers have been successfully used.
A passive plasma catalyst consistent with another aspect of this invention can include one or more portions that are, for example, substantially spherical, annular, pyramidal, cubic, planar, cylindrical, rectangular or elongated.
The passive plasma catalysts discussed above include at least one material that is at least electrically semi-conductive. In one embodiment, the material can be highly conductive., For example, a passive plasma catalyst consistent with this invention can include a metal, an inorganic material, carbon, a carbon-based alloy, a carbon-based composite, an electrically conductive polymer, a conductive silicone elastomer, a polymer nanocomposite, an organic-inorganic composite, or any combination thereof. Some of the possible inorganic materials that can be included in the plasma catalyst include carbon, silicon carbide, molybdenum, platinum, tantalum, tungsten, carbon nitride, and aluminum, although other electrically conductive inorganic materials are believed to work just as well.
In addition to one or more electrically conductive materials, a passive plasma catalyst consistent with this invention can include one or more additives (which need not be electrically conductive) . As used herein, the additive can include any material that a user wishes to add to the plasma. For example, in doping semiconductors and other materials, one or more dopants can be added to the plasma through the catalyst. See, e.g., commonly owned, concurrently filed U.S. patent application Ser. No. 10,513,397, which is hereby incorporated by reference in its entirety. The catalyst can include the dopant itself, or it can include a precursor material that, upon decomposition, can form the dopant. Thus, the plasma catalyst can include one or more additives and one or more electrically conductive materials in any desirable ratio, depending on the ultimate desired composition of the plasma and the process using the plasma.
The ratio of the electrically conductive components to the additives in a passive plasma catalyst can vary over time while being consumed. For example, during ignition, the plasma catalyst could desirably include a relatively large percentage of electrically conductive components to improve the ignition conditions. On the other hand, if used while sustaining the plasma, the catalyst could include a relatively large percentage of additives. It will be appreciated by those of ordinary skill in the art that the component ratio of the plasma catalyst used to ignite and sustain the plasma could be the same and that the ratio can be customized to deposit any desired coating composition.
A predetermined ratio profile can be used to simplify many plasma processes. In many conventional plasma processes, the components within the plasma are added as necessary, but such addition normally requires programmable equipment to add the components according to a predetermined schedule. However, consistent with this invention, the ratio of components in the catalyst can be varied, and thus the ratio of components in the plasma itself can be automatically varied. That is, the ratio of components in the plasma at any particular time can depend on which of the catalyst portions is currently being consumed by the plasma. Thus, the catalyst component ratio can be different at different locations within the catalyst. And, the current ratio of components in a plasma can depend on the portions of the catalyst currently and/or previously consumed, especially when the flow rate of a gas passing through the plasma chamber is relatively slow.
A passive plasma catalyst consistent with this invention can be homogeneous, inhomogeneous, or graded. Also, the plasma catalyst component ratio can vary continuously or discontinuously throughout the catalyst. For example, in
Alternatively, as shown in
Another way to vary the ratio of components in a sustained plasma is by introducing multiple catalysts having different component ratios at different times or different rates. For example, multiple catalysts can be introduced at approximately the same location or at different locations within the cavity. When introduced at different locations, the plasma formed in the cavity can have a component concentration gradient determined by the locations of the various catalysts. Thus, an automated system can include a device by which a consumable plasma catalyst is mechanically inserted before and/or during plasma igniting, modulating, and/or sustaining.
A passive plasma catalyst consistent with this invention can also be coated. In one embodiment, a catalyst can include a substantially non-electrically conductive coating deposited on the surface of a substantially electrically conductive material. Alternatively, the catalyst can include a substantially electrically conductive coating deposited on the surface of a substantially electrically non-conductive material.
A single plasma catalyst can also include multiple coatings. If the coatings are consumed during contact with the plasma, the coatings could be introduced into the plasma sequentially, from the outer coating to the innermost coating, thereby creating a time-release mechanism. Thus, a coated plasma catalyst can include any number of materials, as long as a portion of the catalyst is at least electrically semi-conductive.
Consistent with another embodiment of this invention, a plasma catalyst can be located entirely within an electromagnetic radiation chamber to substantially reduce or prevent electromagnetic radiation energy leakage. In this way, the plasma catalyst does not electrically or magnetically couple with the radiation chamber, the vessel containing the cavity, or to any electrically conductive object outside the cavity. This can prevent sparking at the ignition port and prevents electromagnetic radiation from leaking outside the chamber during the ignition and possibly later if the plasma is sustained. In one embodiment, the catalyst can be located at a tip of a substantially electrically non-conductive extender that extends through an ignition port.
In another embodiment, shown in
Another method of forming a coating plasma consistent with this invention includes subjecting a gas in a cavity to electromagnetic radiation having a frequency less than about 333 GHz in the presence of an active plasma catalyst, which generates or includes at least one ionizing particle.
An active plasma catalyst consistent with this invention can be any particle or high energy wave packet capable of transferring a sufficient amount of energy to a gaseous atom or molecule to remove at least one electron from the gaseous atom or molecule in the presence of electromagnetic radiation. Depending on the source, the ionizing particles can be directed into the cavity in the form of a focused or collimated beam, or they may be sprayed, spewed, sputtered, or otherwise introduced.
For example,
Examples of ionizing particles consistent with this invention can include x-ray particles, gamma ray particles, alpha particles, beta particles, neutrons, protons, and any combination thereof. Thus, an ionizing particle catalyst can be charged (e.g., an ion from an ion source) or uncharged and can be the product of a radioactive fission process. In one embodiment, the vessel in which the plasma cavity is formed could be entirely or partially transmissive to the ionizing particle catalyst. Thus, when a radioactive fission source is located outside the cavity, the source can direct the fission products through the vessel to ignite the plasma. The radioactive fission source can be located inside the electromagnetic radiation chamber to substantially prevent the fission products (i.e., the ionizing particle catalyst) from creating a safety hazard.
In another embodiment, the ionizing particle can be a free electron, but it need not be emitted in a radioactive decay process. For example, the electron can be introduced into the cavity by energizing the electron source (such as a metal), such that the electrons have sufficient energy to escape from the source. The electron source can be located inside the cavity, adjacent the cavity, or even in the cavity wall. It will be appreciated by those of ordinary skill in the art that the any combination of electron sources is possible. A common way to produce electrons is to heat a metal, and these electrons can be further accelerated by applying an electric field.
In addition to electrons, free energetic protons can also be used to catalyze a plasma. In one embodiment, a free proton can be generated by ionizing hydrogen and, optionally, accelerated with an electric field.
Multi-Mode Electromagnetic Radiation Cavities
An electromagnetic radiation waveguide, cavity, or chamber is designed to support or facilitate propagation of at least one electromagnetic radiation mode. As used herein, the term “mode” refers to a particular pattern of any standing or propagating electromagnetic wave that satisfies Maxwell's equations and the applicable boundary conditions (e.g., of the cavity). In a waveguide or cavity, the mode can be any one of the various possible patterns of propagating or standing electromagnetic fields. Each mode is characterized by its frequency and polarization of the electric field and/or magnetic field vectors. The electromagnetic field pattern of a mode depends on the frequency, refractive indices or dielectric constants, and waveguide or cavity geometry.
A transverse electric (TE) mode is one whose electric field vector is normal to the direction of propagation. Similarly, a transverse magnetic (TM) mode is one whose magnetic field vector is normal to the direction of propagation. A transverse electric and magnetic (TEM) mode is one whose electric and magnetic field vectors are both normal to the direction of propagation. A hollow metallic waveguide does not typically support a normal TEM mode of electromagnetic radiation propagation. Even though electromagnetic radiation appears to travel along the length of a waveguide, it may do so only by reflecting off the inner walls of the waveguide at some angle. Hence, depending upon the propagation mode, the electromagnetic radiation may have either some electric field component or some magnetic field component along the axis of the waveguide (often referred to as the z-axis).
The actual field distribution inside a cavity or waveguide is a superposition of the modes therein. Each of the modes can be identified with one or more subscripts (e.g., TE10 (“tee ee one zero”). The subscripts normally specify how many “half waves” at the guide wavelength are contained in the x and y directions. It will be appreciated by those skilled in the art that the guide wavelength can be different from the free space wavelength because electromagnetic radiation propagates inside the waveguide by reflecting at some angle from the inner walls of the waveguide. In some cases, a third subscript can be added to define the number of half waves in the standing wave pattern along the z-axis.
For a given electromagnetic radiation frequency, the size of the waveguide can be selected to be small enough so that it can support a single propagation mode. In such a case, the system is called a single-mode system (i.e., a single-mode applicator). The TE10 mode is usually dominant in a rectangular single-mode waveguide.
As the size of the waveguide (or the cavity to which the waveguide is connected) increases, the waveguide or applicator can sometimes support additional higher order modes forming a multi-mode system. When many modes are capable of being supported simultaneously, the system is often referred to as highly moded.
A simple, single-mode system has a field distribution that includes at least one maximum and/or minimum. The magnitude of a maximum largely depends on the amount of electromagnetic radiation supplied to the system. Thus, the field distribution of a single mode system is strongly varying and substantially non-uniform.
Unlike a single-mode cavity, a multi-mode cavity can support several propagation modes simultaneously, which, when superimposed, results in a complex field distribution pattern. In such a pattern, the fields tend to spatially smear and, thus, the field distribution usually does not show the same types of strong minima and maxima field values within the cavity. In addition, as explained more fully below, a mode-mixer can be used to “stir” or “redistribute” modes (e.g., by mechanical movement of an electromagnetic radiation reflector). This redistribution desirably provides a more uniform time-averaged field (and therefore plasma) distribution within the cavity.
A multi-mode cavity consistent with this invention can support at least two modes, and may support many more than two modes. Each mode has a maximum electric field vector. Although there may be two or more modes, one mode may be dominant and has a maximum electric field vector magnitude that is larger than the other modes. As used herein, a multi-mode cavity may be any cavity in which the ratio between the first and second mode magnitudes is less than about 1:10, or less than about 1:5, or even less than about 1:2. It will be appreciated by those of ordinary skill in the art that the smaller the ratio, the more distributed the electric field energy between the modes, and hence the more distributed the electromagnetic radiation energy is in the cavity.
The distribution of a coating plasma within a cavity may strongly depend on the distribution of the applied electromagnetic radiation. For example, in a pure single mode system, there may only be a single location at which the electric field is a maximum. Therefore, a strong plasma may only form at that single location. In many applications, such a strongly localized plasma could undesirably lead to non-uniform plasma treatment or heating (i.e., localized overheating and underheating).
Whether or not a single or multi-mode cavity is used consistent with this invention, it will be appreciated by those of ordinary skill in the art that the cavity in which the plasma is formed can be completely closed or partially open. For example, in certain applications, such as in plasma-assisted furnaces, the cavity could be entirely closed. See, for example, commonly owned, concurrently filed PCT Application U.S. 03/14133, now expired, which is fully incorporated herein by reference.
In other applications, however, it may be desirable to flow a gas through the cavity, and therefore the cavity must be open to some degree. In this way, the flow, type, and pressure of the flowing gas can be varied over time. This may be desirable because certain gases with lower ionization potentials, such as argon, are easier to ignite but may have other undesirable properties during subsequent plasma processing.
Mode-Mixing
For many applications, a cavity containing a uniform plasma is desirable. However, because electromagnetic radiation can have a relatively long wavelength (e.g., in the case of microwave radiation, several tens of centimeters), obtaining a uniform distribution can be difficult to achieve. As a result, consistent with one aspect of this invention, the radiation modes in a multi-mode cavity can be mixed, or redistributed, over a period of time. Because the field distribution within the cavity must satisfy all of the boundary conditions set by the inner surface of the cavity, those field distributions can be changed by changing the position of any portion of that inner surface.
In one embodiment consistent with this invention, a movable reflective surface can be located inside the electromagnetic radiation cavity. The shape and motion of the reflective surface should, when combined, change the inner surface of the cavity during motion. For example, an “L” shaped metallic object (i.e., “mode-mixer”) when rotated about any axis will change the location or the orientation of the reflective surfaces in the cavity and therefore change the electromagnetic radiation distribution therein. Any other asymmetrically shaped object can also be used (when rotated), but symmetrically shaped objects can also work, as long as the relative motion (e.g., rotation, translation, or a combination of both) causes some change in the location or orientation of the reflective surfaces. In one embodiment, a mode-mixer can be a cylinder that can be rotated about an axis that is not the cylinder's longitudinal axis.
Each mode of a multi-mode cavity may have at least one maximum electric field vector, but each of these vectors could occur periodically across the inner dimension of the cavity. Normally, these maxima are fixed, assuming that the frequency of the electromagnetic radiation does not change. However, by moving a mode-mixer such that it interacts with the electromagnetic radiation, it is possible to move the positions of the maxima. For example, mode-mixer 38 can be used to optimize the field distribution within cavity 12 such that the plasma ignition conditions and/or the plasma sustaining conditions are optimized. Thus, once a plasma is excited, the position of the mode-mixer can be changed to move the position of the maxima for a uniform time-averaged plasma process (e.g., heating).
Thus, consistent with this invention, mode-mixing can be useful during plasma ignition. For example, when an electrically conductive fiber is used as a plasma catalyst, it is known that the fibers orientation can strongly affect the minimum plasma-ignition conditions. It has been reported, for example, that when such a fiber is oriented at an angle that is greater than 60° to the electric field, the catalyst does little to improve, or relax, these conditions. By moving a reflective surface either in or near the cavity, however, the electric field distribution can be significantly changed.
Mode-mixing can also be achieved by launching the radiation into the applicator chamber through, for example, a rotating waveguide joint that can be mounted inside the applicator chamber. The rotary joint can be mechanically moved (e.g., rotated) to effectively launch the radiation in different directions in the radiation chamber. As a result, a changing field pattern can be generated inside the applicator chamber.
Mode-mixing can also be achieved by launching radiation in the radiation chamber through a flexible waveguide. In one embodiment, the waveguide can be mounted inside the chamber. In another embodiment, the waveguide can extend into the chamber. The position of the end portion of the flexible waveguide can be continually or periodically moved (e.g., bent) in any suitable manner to launch the radiation (e.g., microwave radiation) into the chamber at different directions and/or locations. This movement can also result in mode-mixing and facilitate more uniform plasma processing (e.g., heating) on a time-averaged basis. Alternatively, this movement can be used to optimize the location of a plasma for ignition or other plasma-assisted process.
If the flexible waveguide is rectangular, a simple twisting of the open end of the waveguide will rotate the orientation of the electric and the magnetic field vectors in the radiation inside the applicator chamber. Then, a periodic twisting of the waveguide can result in mode-mixing as well as rotating the electric field, which can be used to assist ignition, modulation, or sustaining of a plasma.
Thus, even if the initial orientation of the catalyst is perpendicular to the electric field, the redirection of the electric field vectors can change the ineffective orientation to a more effective one. Those skilled in the art will appreciate that mode-mixing can be continuous, periodic, or preprogrammed.
In addition to plasma ignition, mode-mixing can be useful during subsequent plasma processing to reduce or create (e.g., tune) “hot spots” in the chamber. When an electromagnetic radiation cavity only supports a small number of modes (e.g., less than 5), one or more localized electric field maxima can lead to “hot spots” (e.g., within cavity 12). In one embodiment, these hot spots could be configured to coincide with one or more separate, but simultaneous, plasma ignitions or coating processes. Thus, in one embodiment, a plasma catalyst can be located at one or more of those ignition or coating positions.
Multi-Location Plasma Ignition
A plasma can be ignited using multiple plasma catalysts at different locations. In one embodiment, multiple fibers can be used to ignite the plasma at different points within the cavity. Such multi-point ignition can be especially beneficial when a uniform plasma ignition is desired. For example, when a coating plasma is modulated at a high frequency (i.e., tens of Hertz and higher), or ignited in a relatively large volume, or both, substantially uniform instantaneous striking and re-striking of the plasma can be improved. Alternatively, when plasma catalysts are used at multiple points, they can be used to sequentially ignite a plasma at different locations within a plasma chamber by selectively introducing the catalyst at those different locations. In this way, a plasma ignition gradient can be controllably formed within the cavity, if desired.
Also, in a multi-mode cavity, random distribution of the catalyst throughout multiple locations in the cavity increases the likelihood that at least one of the fibers, or any other passive plasma catalyst consistent with this invention, is optimally oriented with the electric field lines. Still, even where the catalyst is not optimally oriented (not substantially aligned with the electric field lines), the ignition conditions are improved.
Furthermore, because a catalytic powder can be suspended in a gas, it is believed that each powder particle may have the effect of being placed at a different physical location within the cavity, thereby improving ignition uniformity within the cavity.
Dual-Cavity Plasma Igniting/Sustaining
A dual-cavity arrangement can be used to ignite and sustain a plasma consistent with this invention. In one embodiment, a system includes at least ignition cavity 280 and plasma processing cavity 285 in fluid communication with each other, for example, as shown in
Additional cavities 290 and 295 are optional, and can be kept in fluid communication with cavity 285 by channel 605, for example. An object to be coated, such as work piece 250, can be placed in any of cavities 285, 290, or 295 and can be supported by any type of supporting device, such as support 260, which optionally moves or rotates work piece 250 during the coating procedure.
In one embodiment of this invention, cavity 280 can be very small and designed primarily, or solely for plasma ignition. In this way, very little electromagnetic radiation energy may be required to ignite plasma 600, permitting easier ignition, especially when a plasma catalyst is used consistent with this invention. It will also be appreciated that the cavities used in the plasma system consistent with the present invention can have a variable size, and a deposition controller can be used to control the size of the cavity.
In one embodiment, cavity 280 can be a substantially single mode cavity and cavity 285 can be a multi-mode cavity. When cavity 280 only supports a single mode, the electric field distribution may strongly vary within the cavity, forming one or more precisely located electric field maxima. Such maxima are normally the first locations at which plasmas ignite, making them ideal points for placing plasma catalysts. It will be appreciated, however, that when a plasma catalyst is used to ignite plasma 600, the catalyst need not be placed in the electric field maximum and, many cases, need not be oriented in any particular direction.
Illustrative Coating Methods and Apparatus
In one embodiment, laser 500 can produce a beam of light having a wavelength between about 150 nm and 20 μm, although any other convenient wavelength can also be used. Laser 500 can also be a high peak power pulsed laser beam that continually, periodically, or in a preprogrammed fashion energizes coating material 510. A gas, such as Ar (not shown), can direct the energized (e.g., vaporized) coating material toward plasma 615 to form a coating on work piece 250. It will be appreciated that the uniformity of the coating can be increased by moving (e.g., rotating) work piece 250 using support 260 (e.g., a turntable). In addition, as described more fully below, voltage supply 275 can supply a continuous or pulsed electric bias (e.g., negative or positive, DC or AC) to work piece 250. The bias is believed to accelerate ionized atomic or molecular species of coating material 510 toward work piece 250, which may provide an improved bond between coating 247 and work piece 250, and increase deposition rates. Voltage supply 275 can apply an opposite bias to electrode 270 or to any other part of chamber 232.
Thus, coating plasma 615, which can be catalyzed from a gas using plasma catalyst 240 can be enhanced by adding coating material 510 by energizing the material with laser 500. It will be appreciated that although
It will be appreciated by one of ordinary skill in the art that a plasma-assisted coating system consistent with this invention can include any electronic or mechanical means for introducing a catalyst to a plasma cavity. For example, a fiber can be mechanically inserted before or during the formation of the coating plasma. It will also be appreciated that plasma 600 can also be triggered by a spark plug, pulsed laser, or even by a burning match stick introduced in cavity 230 before, during, or after the presence of electromagnetic radiation.
It will be further appreciated that material 510 can be separated from plasma 615 during a coating procedure to better control the introduction of the material into the plasma. For this purpose, one or more walls or screens (not shown) can be placed between coating material 510 in crucible 515 and plasma 615. Other electromagnetic radiation or plasma shielding methods may also be used.
Plasma 615 can absorb an appropriate level of electromagnetic radiation energy to achieve any predetermined temperature profile (e.g., any selected temperature). The gas pressure in the cavity can be less than, equal to, or greater than atmospheric pressure. At least one additional coating material (not shown) can be added to plasma 615, thereby allowing it to form a multi-component coating on the surface of work piece 250.
Work piece 250 can be any object that may need a coating, such as a low carbon steel. For example, the work piece may be an automotive part, such as a brake banjo block, a cam lobe, a gear, a seat component, a rail lever, a socket fastener, or a parking brake part. Work piece 250 can also be, for example, a semiconductor substrate, a metal part, a ceramic, a glass, etc.
In one embodiment, as mentioned above, a bias can be applied to work piece 250 to produce a more uniform and rapid coating process. For example, as shown in
In addition, mount 260 can be heated or cooled by any means (e.g., a heat exchanger) to keep work piece 250 at a desirable temperature. For example, a cooling fluid (e.g., gas) can be used to cool work piece 250 before, during, or after a deposition. When the temperature of work piece 250 is modified with a gas, such as with nitrogen, or by contact with a liquid, coating 252 on work piece 250 may have improved electrical, thermal, and mechanical properties.
It will be appreciated that the coating material passing through aperture 410 may be combined with one or more other materials or gases (not shown), inside or outside cavity 292, to achieve any desired coating composite or composition.
Laser 500 and coating material 510 can be part of any single cavity system (e.g. as shown in
As mentioned above, energizing (e.g., vaporizing, subliming, sputtering, etc.) coating material 510 can be accomplished by means other than laser 500. For example, coating material 510 can be exposed to a particle beam passing through window 505, where the particle beam may be a concentrated group of particles, such as electrons, protons, charged particles, photons, or any combination thereof.
Although igniting, modulating, or sustaining a coating plasma consistent with this invention and exposing coating material 510 With laser 500 can occur at atmospheric pressure, a coating can be deposited onto work piece 250 at any desirable pressure, including below, at, or above atmospheric pressure. Furthermore, plasma pressure and temperature can be varied as desired, and the deposition rate can be regulated by the strength of the energy source. For example, using a system (like the one shown in
Since the plasma may not be sustained in a region with a gap less than about λ/4 (below, e.g., surface 300), a coating may not deposit there. On the other hand, the plasma may be sustained below surface 310, and a coating may be deposited there. It will be appreciated that the pattern shown in
It will also be appreciated that the plasma-formation dependency on wavelength results from the boundary conditions imposed by electrically-conductive surfaces, such as an inner metallic surface of a cavity. When non-metallic surfaces are used, the size of the local plasma volume can be increased or decreased beyond the λ/4. In general, controlling the plasma volume in the proximity of a coating surface can be used to control the energy flux delivered to that surface by the plasma and any resulting plasma-assisted coating process.
Although
Surface features present on work piece 250 can effectively act like a mask during deposition of the coating material described previously. This “mask” can be the work piece itself, or it can be a photo resist, for example, like that used in the semiconductor industry, or it can be any other material used to alter the deposition process (e.g., a sacrificial film designed to prevent coating on the sides of a gear, for example, thereby allowing the coating to deposit only on the gear teeth). Masks, for example, can be negative or positive photo resists, deposited metals, oxides, or other materials used in a permanent or sacrificial manner to effectuate a desired coating pattern.
Whether or not a pattern is desired, one or more components can be added to the plasma for deposition on work piece 250. The coating materials (i.e., components) added to the plasma can be provided using a nitrogen source, an oxygen source, a carbon source, an aluminum source, an arsenic source, a boron source, chromium source, a gallium source, a germanium source, an indium source, a phosphorous source, a magnesium source, a silicon source, a tantalum source, a tin source, a titanium source, a tungsten source, a yttrium source, a zirconium source, and any combination thereof. Such a source can be a pure elemental source, but can also be a combination of one or more elements, including, for example, any carbide, oxide, nitride, phosphide, arsenide, boride, and any combination thereof.
In addition, other materials can be used, such as tungsten carbide, tungsten nitride, tungsten oxide, tantalum nitride, tantalum oxide, titanium oxide, titanium nitride, silicon oxide, silicon carbide, silicon nitride, aluminum oxide, aluminum nitride, aluminum carbide, boron nitride, boron carbide, boron oxide, gallium phosphide, aluminum phosphide, chromium oxide, tin oxide, yttria, zirconia, silicon-germanium, indium tin oxide, indium gallium arsenide, aluminum gallium arsenide, boron, chromium, gallium, germanium, indium, phosphorous, magnesium, silicon, tantalum, tin, titanium, tungsten, yttrium, and zirconium. Again, many other materials can also be formed, depending on the source materials.
When deposited, the materials provided by these sources can form nearly any type of coating, which may be deposited on nearly any substrate. For example, carbides, nitrides, borides, oxides, and other materials can be synthesized and deposited on a substrate consistent with this invention, including various combinations, such as silicon carbide (SiC), titanium carbide (TiC), titanium carbon nitride (TiCN), titanium aluminum nitride (TiAlN), titanium boron nitride (TiBN), chromium nitride (CrN), tungsten carbide (WC), aluminum nitride (AlN), silicon nitride (Si3N4), titanium diboride (TiB2), cubic-boron nitride (cBN), boron carbide (B4C), alumina (Al2O3), boron oxide, and diamond. Other materials mentioned previously may also be synthesized, including any combination of the materials listed above. It will be appreciated that hydrogen may also be added to the plasma to reduce the formation of oxides.
Thus, consistent with this invention, one or more components can be added to a catalyzed plasma and then deposited on a substrate to form coatings, including powders.
For example, to form SiC, a source of silicon (e.g., any organosilane precursor, such as SiCl4, SiH4, SiF4, SiH2Cl2, or any combination thereof) and any carbon source (e.g., a hydrocarbon, such as alcohol, propane, ethane, methane, as well as carbon powder, fiber, vapor, etc.) can be added to the plasma. Some of the many possible organosilane precursors include trimethylsilane, tetramethylsilane, and silacyclobutane. Silane gas can also be used as a source of silicon. Also consistent with this invention, it will be appreciated that a source of SiC (e.g., used as a coating material) can be exposed to a laser to selectively energize the SiC so that it can be added to the plasma and deposited as a coating on work piece 250.
An advantage of depositing coatings, like those described above, using this catalyzed plasma process may include a higher growth rate due to the very high concentration of species that may exist above work piece 250 during coating, even at relatively high pressures. Also, it is believed that the number of pinholes formed in the coating using this invention will be reduced compared with conventional chemical vapor deposition techniques. It will be appreciated that SiC thin films fabricated with this invention can be used, for example, in making high-temperature electronic chips, or in providing high-strength coatings for automotive and other types of parts.
It will also be appreciated that other high-strength coatings can be formed consistent with this invention using the plasma system described herein. To form TiC, for example, a source of titanium (e.g., TiCl4, TiO2, and any combination thereof) and any carbon source (e.g., see above) can be added to the plasma. An appropriate amount of hydrogen can also be added, such as about 10% by volume to prevent oxidation. The cavity temperature can be operated at any convenient temperature, such as between about 1,000 degrees Celsius and about 1,200 degrees Celsius. In a similar fashion, WC can be formed using a source of W (e.g., tungsten oxide, tungsten fluoride, and any combination thereof) and a source of carbon (e.g., see above).
In addition to TiC and WC, other coatings, including Ti, Cr, and/or Si, are also possible. To form TiN, for example, a source of titanium (e.g., see above) and any nitrogen source (e.g., N2, NH3, and any combination thereof) can be added to the plasma. Once again, the cavity temperature can be held at any convenient temperature, such as between about 1,000 degrees Celsius and about 1,200 degrees Celsius although other temperatures can be used. Similarly, to form TiCN, a source of titanium (e.g., see above), a carbon source (e.g., see above), and a nitrogen source (e.g., see above) can be added to the plasma.
Furthermore, to form TiAlN, for example, a source of titanium (e.g., see above), a source of aluminum (e.g., AlCl3, trimethylaluminum, elemental aluminum (e.g., powder), etc.), and any nitrogen source (e.g., see above) can be added to a plasma. Also, to form TiBN, a source of titanium (e.g., see above), a source of boron (e.g., BCl3, NaBH4, (CNBH2)n, and any combination thereof) and any nitrogen source (e.g., see above) can be added to the plasma. Further, to form CrN, a source of Cr (e.g., atomic Cr) and any source of nitrogen (e.g., see above) can be added to a plasma. Moreover, to form AlN, a source of Al (e.g., see above) and any source of nitrogen (e.g., see above) can be added to the plasma. In addition, to form Si3N4, a source of silicon (e.g., see above) and any source of nitrogen (e.g., see above) can be added to a plasma. It will be appreciated that silicon nitride can be used, for example, for many applications that require increased strength or improved optical properties.
Various borides and oxides can also be deposited consistent with this invention. For example, to form TiB2, a source of titanium (e.g., TiCl4, TiO2, and any combination thereof) and a source of boron (e.g., see above) can be added to the plasma. Hydrogen and/or trichloroethane can also be added to the plasma in suitable quantities to improve yields. To form cBN, a source of boron (e.g., see above) and any nitrogen source (see above) can be added to the plasma. Also, to form B4C, a source of boron (e.g., see above) and any carbon source (e.g., see above) can be added to the plasma. B4C, for example, can be used to coat tool bits. To form Al2O3, a source of Al (e.g., see above) and any source of oxygen, including pure oxygen, can be added to the plasma. To encourage oxidation, hydrogen may not be desirable for this reaction. It will be appreciated that other oxides can be synthesized in a similar manner.
In addition to the many exemplary alloys discussed above, carbon films, such as diamond films, can be synthesized consistent with this invention. To form diamond, a source of carbon (e.g., a hydrocarbon or carbon powder or fiber) can be added to the plasma. By adding hydrogen to the plasma, formation of graphite can be substantially suppressed and formation of diamond can be encouraged. For example, a combination of CH4, H2, Ar, and carbon fibers in the presence of a nickel catalyst (e.g., in the form of a plate) with a cavity temperature at about 600 degrees Celsius can be used to form diamond. Ni powder, for example, can also be used as catalyst.
It will be appreciated that other single and multi-element coatings not discussed above can also be formed consistent with this invention.
In the foregoing described embodiments, various features are grouped together in a single embodiment for purposes of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed invention requires more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment. Thus, the following claims are hereby incorporated into this Detailed Description of Embodiments, with each claim standing on its own as a separate preferred embodiment of the invention.
Priority is claimed to U.S. Provisional Patent Application No. 60/378,693, filed May 8, 2002, No. 60/430,677, filed Dec. 4, 2002, and No. 60/435,278, filed Dec. 23, 2002, all of which are fully incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US03/14124 | 5/7/2003 | WO | 00 | 5/23/2005 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO03/095699 | 11/20/2003 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3432296 | McKinnon et al. | Mar 1969 | A |
| 3612686 | Braman et al. | Oct 1971 | A |
| 3731047 | Mullen et al. | May 1973 | A |
| 4004934 | Prochazka | Jan 1977 | A |
| 4025818 | Giguere et al. | May 1977 | A |
| 4090055 | King | May 1978 | A |
| 4147911 | Nishitani | Apr 1979 | A |
| 4151034 | Yamamoto et al. | Apr 1979 | A |
| 4213818 | Lemons et al. | Jul 1980 | A |
| 4230448 | Ward et al. | Oct 1980 | A |
| 4265730 | Hirose et al. | May 1981 | A |
| 4307277 | Maeda et al. | Dec 1981 | A |
| 4339326 | Hirose et al. | Jul 1982 | A |
| 4404456 | Cann | Sep 1983 | A |
| 4473736 | Bloyet et al. | Sep 1984 | A |
| 4479075 | Elliott | Oct 1984 | A |
| 4500564 | Enomoto | Feb 1985 | A |
| 4504007 | Anderson, Jr. et al. | Mar 1985 | A |
| 4609808 | Bloyet et al. | Sep 1986 | A |
| 4611108 | Leprince et al. | Sep 1986 | A |
| 4624738 | Westfall et al. | Nov 1986 | A |
| 4664937 | Ovshinsky et al. | May 1987 | A |
| 4666775 | Kim et al. | May 1987 | A |
| 4687560 | Tracy | Aug 1987 | A |
| 4698234 | Ovshinsky | Oct 1987 | A |
| 4760230 | Hassler | Jul 1988 | A |
| 4767902 | Palaith et al. | Aug 1988 | A |
| 4772770 | Matsui et al. | Sep 1988 | A |
| 4792348 | Pekarsky | Dec 1988 | A |
| 4840139 | Takei | Jun 1989 | A |
| 4871581 | Yamazaki | Oct 1989 | A |
| 4877589 | O'Hare | Oct 1989 | A |
| 4877938 | Rau et al. | Oct 1989 | A |
| 4883570 | Efthimion et al. | Nov 1989 | A |
| 4888088 | Slomowitz | Dec 1989 | A |
| 4891488 | Davis et al. | Jan 1990 | A |
| 4897285 | Wilhelm | Jan 1990 | A |
| 4908492 | Okamoto et al. | Mar 1990 | A |
| 4919077 | Oda et al. | Apr 1990 | A |
| 4924061 | Labat et al. | May 1990 | A |
| 4946547 | Palmour et al. | Aug 1990 | A |
| 4956590 | Phillips | Sep 1990 | A |
| 4963709 | Kimrey, Jr. | Oct 1990 | A |
| 4972799 | Misumi et al. | Nov 1990 | A |
| 5003152 | Matsuo | Mar 1991 | A |
| 5010220 | Apte et al. | Apr 1991 | A |
| 5017404 | Paquet et al. | May 1991 | A |
| 5023056 | Aklufi et al. | Jun 1991 | A |
| 5058527 | Ohta et al. | Oct 1991 | A |
| 5072650 | Phillips | Dec 1991 | A |
| 5074112 | Walton et al. | Dec 1991 | A |
| 5085885 | Foley et al. | Feb 1992 | A |
| 5087272 | Nixdorf | Feb 1992 | A |
| 5103715 | Phillips | Apr 1992 | A |
| 5120567 | Frind et al. | Jun 1992 | A |
| 5122633 | Moshammer et al. | Jun 1992 | A |
| 5131993 | Suib et al. | Jul 1992 | A |
| 5164130 | Holcombe et al. | Nov 1992 | A |
| 5202541 | Patterson et al. | Apr 1993 | A |
| 5223308 | Doehler | Jun 1993 | A |
| 5224117 | Kruger et al. | Jun 1993 | A |
| 5227695 | Pelletier et al. | Jul 1993 | A |
| 5271963 | Eichman et al. | Dec 1993 | A |
| 5276297 | Nara | Jan 1994 | A |
| 5276386 | Watanabe et al. | Jan 1994 | A |
| 5277773 | Murphy | Jan 1994 | A |
| 5284544 | Mizutani et al. | Feb 1994 | A |
| 5304766 | Baudet et al. | Apr 1994 | A |
| 5307892 | Phillips | May 1994 | A |
| 5310426 | Mori | May 1994 | A |
| 5311906 | Phillips | May 1994 | A |
| 5316043 | Phillips | May 1994 | A |
| 5321223 | Kimrey, Jr. et al. | Jun 1994 | A |
| 5349154 | Harker et al. | Sep 1994 | A |
| 5366764 | Sunthankar | Nov 1994 | A |
| 5370525 | Gordon | Dec 1994 | A |
| 5423180 | Nobue et al. | Jun 1995 | A |
| 5435698 | Phillips | Jul 1995 | A |
| 5449887 | Holcombe et al. | Sep 1995 | A |
| 5505275 | Phillips | Apr 1996 | A |
| 5514217 | Niino et al. | May 1996 | A |
| 5520740 | Kanai et al. | May 1996 | A |
| 5521360 | Johnson et al. | May 1996 | A |
| 5523126 | Sano et al. | Jun 1996 | A |
| 5527391 | Echizen et al. | Jun 1996 | A |
| 5536477 | Cha et al. | Jul 1996 | A |
| 5587205 | Saito et al. | Dec 1996 | A |
| 5597456 | Maruyama et al. | Jan 1997 | A |
| 5607509 | Schumacher et al. | Mar 1997 | A |
| 5616373 | Karner et al. | Apr 1997 | A |
| 5645897 | Andra | Jul 1997 | A |
| 5651825 | Nakahigashi et al. | Jul 1997 | A |
| 5662965 | Deguchi et al. | Sep 1997 | A |
| 5670065 | Bickmann et al. | Sep 1997 | A |
| 5671045 | Woskov et al. | Sep 1997 | A |
| 5682745 | Phillips | Nov 1997 | A |
| 5689949 | DeFreitas et al. | Nov 1997 | A |
| 5712000 | Wei et al. | Jan 1998 | A |
| 5714010 | Matsuyama et al. | Feb 1998 | A |
| 5715677 | Wallman et al. | Feb 1998 | A |
| 5734501 | Smith | Mar 1998 | A |
| 5735451 | Mori et al. | Apr 1998 | A |
| 5741364 | Kodama et al. | Apr 1998 | A |
| 5755097 | Phillips | May 1998 | A |
| 5794113 | Munir et al. | Aug 1998 | A |
| 5795628 | Wisard et al. | Aug 1998 | A |
| 5796080 | Jennings et al. | Aug 1998 | A |
| 5808282 | Apte et al. | Sep 1998 | A |
| 5828338 | Gerstenberg | Oct 1998 | A |
| 5841237 | Alton | Nov 1998 | A |
| 5847355 | Barmatz et al. | Dec 1998 | A |
| 5848348 | Dennis | Dec 1998 | A |
| 5859404 | Wei et al. | Jan 1999 | A |
| 5868871 | Yokose et al. | Feb 1999 | A |
| 5874705 | Duan | Feb 1999 | A |
| 5904993 | Takeuchi et al. | May 1999 | A |
| 5939026 | Seki et al. | Aug 1999 | A |
| 5945351 | Mathuni | Aug 1999 | A |
| 5961773 | Ichimura et al. | Oct 1999 | A |
| 5961871 | Bible et al. | Oct 1999 | A |
| 5973289 | Read et al. | Oct 1999 | A |
| 5976429 | Chen et al. | Nov 1999 | A |
| 5980843 | Silversand | Nov 1999 | A |
| 5980999 | Goto et al. | Nov 1999 | A |
| 5989477 | Berger | Nov 1999 | A |
| 5993612 | Rostaing et al. | Nov 1999 | A |
| 5998774 | Joines et al. | Dec 1999 | A |
| 6011248 | Dennis | Jan 2000 | A |
| 6028393 | Izu et al. | Feb 2000 | A |
| 6038854 | Penetrante et al. | Mar 2000 | A |
| 6054693 | Barmatz et al. | Apr 2000 | A |
| 6054700 | Rokhvarger et al. | Apr 2000 | A |
| 6096389 | Kanai | Aug 2000 | A |
| 6101969 | Niori et al. | Aug 2000 | A |
| 6103068 | Merten et al. | Aug 2000 | A |
| 6122912 | Phillips | Sep 2000 | A |
| 6131386 | Trumble | Oct 2000 | A |
| 6132550 | Shiomi | Oct 2000 | A |
| 6149985 | Grace et al. | Nov 2000 | A |
| 6152254 | Phillips | Nov 2000 | A |
| 6153868 | Marzat | Nov 2000 | A |
| 6183689 | Roy et al. | Feb 2001 | B1 |
| 6186090 | Dotter, II et al. | Feb 2001 | B1 |
| 6189482 | Zhao et al. | Feb 2001 | B1 |
| 6204606 | Spence et al. | Mar 2001 | B1 |
| 6224836 | Moisan et al. | May 2001 | B1 |
| 6228773 | Cox | May 2001 | B1 |
| 6238629 | Barankova et al. | May 2001 | B1 |
| 6248206 | Herchen et al. | Jun 2001 | B1 |
| 6264812 | Raaijmakers et al. | Jul 2001 | B1 |
| 6284202 | Cha et al. | Sep 2001 | B1 |
| 6287430 | Matsumoto et al. | Sep 2001 | B1 |
| 6287980 | Hanazaki et al. | Sep 2001 | B1 |
| 6287988 | Nagamine et al. | Sep 2001 | B1 |
| 6297172 | Kashiwagi | Oct 2001 | B1 |
| 6297595 | Stimson et al. | Oct 2001 | B1 |
| 6329628 | Kuo et al. | Dec 2001 | B1 |
| 6342195 | Roy et al. | Jan 2002 | B1 |
| 6345497 | Penetrante | Feb 2002 | B1 |
| 6348158 | Samukawa | Feb 2002 | B1 |
| 6358361 | Matsumoto | Mar 2002 | B1 |
| 6362449 | Hadidi et al. | Mar 2002 | B1 |
| 6365885 | Roy et al. | Apr 2002 | B1 |
| 6367412 | Ramaswamy et al. | Apr 2002 | B1 |
| 6370459 | Phillips | Apr 2002 | B1 |
| 6372304 | Sano et al. | Apr 2002 | B1 |
| 6376027 | Lee et al. | Apr 2002 | B1 |
| 6383333 | Haino et al. | May 2002 | B1 |
| 6383576 | Matsuyama | May 2002 | B1 |
| 6388225 | Blum et al. | May 2002 | B1 |
| 6392350 | Amano | May 2002 | B1 |
| 6407359 | Lagarde et al. | Jun 2002 | B1 |
| 6488112 | Kleist | Dec 2002 | B1 |
| 6512216 | Gedevanishvili et al. | Jan 2003 | B2 |
| 6522055 | Uemura et al. | Feb 2003 | B2 |
| 6575264 | Spadafora | Jun 2003 | B2 |
| 6592664 | Frey et al. | Jul 2003 | B1 |
| 6610611 | Liu et al. | Aug 2003 | B2 |
| 6712298 | Kohlberg et al. | Mar 2004 | B2 |
| 6717368 | Sakamoto et al. | Apr 2004 | B1 |
| 6870124 | Kumar et al. | Mar 2005 | B2 |
| 20010027023 | Ishihara et al. | Oct 2001 | A1 |
| 20010028919 | Liu et al. | Oct 2001 | A1 |
| 20020034461 | Segal | Mar 2002 | A1 |
| 20020036187 | Ishll et al. | Mar 2002 | A1 |
| 20020104483 | Misiano et al. | Aug 2002 | A1 |
| 20020124867 | Kim et al. | Sep 2002 | A1 |
| 20020135308 | Janos et al. | Sep 2002 | A1 |
| 20020140381 | Golkowski et al. | Oct 2002 | A1 |
| 20020190061 | Gerdes et al. | Dec 2002 | A1 |
| 20020197882 | Niimi et al. | Dec 2002 | A1 |
| 20030071037 | Sato et al. | Apr 2003 | A1 |
| 20030111334 | Dodelet et al. | Jun 2003 | A1 |
| 20030111462 | Sato et al. | Jun 2003 | A1 |
| 20040001295 | Kumar et al. | Jan 2004 | A1 |
| 20040004062 | Kumar et al. | Jan 2004 | A1 |
| 20040070347 | Nishida et al. | Apr 2004 | A1 |
| 20040089631 | Blalock et al. | May 2004 | A1 |
| 20040107796 | Kumar et al. | Jun 2004 | A1 |
| 20040107896 | Kumar et al. | Jun 2004 | A1 |
| 20040118816 | Kumar et al. | Jun 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 222 348 | May 1985 | DE |
| 195 42 352 | May 1997 | DE |
| 100 05 146 | Aug 2001 | DE |
| 0 335 675 | Oct 1989 | EP |
| 0 228 864 | Mar 1991 | EP |
| 0 420 101 | Apr 1991 | EP |
| 0 435 591 | Jul 1991 | EP |
| 0 436 361 | Jul 1991 | EP |
| 435591 | Jul 1991 | EP |
| 0 520 719 | May 1996 | EP |
| 0 670 666 | Jun 1998 | EP |
| 0 724 720 | May 2000 | EP |
| 1 093 846 | Apr 2001 | EP |
| 1 427 265 | Jun 2004 | EP |
| 56-140021 | Nov 1981 | JP |
| 57-119164 | Jul 1982 | JP |
| 58-025073 | Feb 1983 | JP |
| 59-169053 | Sep 1984 | JP |
| 62-000535 | Jan 1987 | JP |
| 04-74858 | Mar 1992 | JP |
| 06-345541 | Dec 1994 | JP |
| 07-153405 | Jun 1995 | JP |
| 08-217558 | Aug 1996 | JP |
| 08-281423 | Oct 1996 | JP |
| 09-017597 | Jan 1997 | JP |
| 09-023458 | Jan 1997 | JP |
| 09-027459 | Jan 1997 | JP |
| 09-027482 | Jan 1997 | JP |
| 09-078240 | Mar 1997 | JP |
| 09-102400 | Apr 1997 | JP |
| 09-102488 | Apr 1997 | JP |
| 09-111461 | Apr 1997 | JP |
| 09-137274 | May 1997 | JP |
| 09-157048 | Jun 1997 | JP |
| 09-223596 | Aug 1997 | JP |
| 09-235686 | Sep 1997 | JP |
| 09-251971 | Sep 1997 | JP |
| 09-295900 | Nov 1997 | JP |
| 10-066948 | Mar 1998 | JP |
| 10-081588 | Mar 1998 | JP |
| 10-081970 | Mar 1998 | JP |
| 10-087310 | Apr 1998 | JP |
| 10-204641 | Aug 1998 | JP |
| 10-259420 | Sep 1998 | JP |
| 10-294306 | Nov 1998 | JP |
| 11-031599 | Feb 1999 | JP |
| 11-106947 | Apr 1999 | JP |
| 11-145116 | May 1999 | JP |
| 11-186222 | Jul 1999 | JP |
| 11-228290 | Aug 1999 | JP |
| 11-265885 | Sep 1999 | JP |
| 11-273895 | Oct 1999 | JP |
| 11-297266 | Oct 1999 | JP |
| 2000-012526 | Jan 2000 | JP |
| 2000-173989 | Jun 2000 | JP |
| 2000-203990 | Jul 2000 | JP |
| 2000-269182 | Sep 2000 | JP |
| 2000-288382 | Oct 2000 | JP |
| 2000-306901 | Nov 2000 | JP |
| 2000-310874 | Nov 2000 | JP |
| 2000-310876 | Nov 2000 | JP |
| 2000-317303 | Nov 2000 | JP |
| 2000-323463 | Nov 2000 | JP |
| 2000-348897 | Dec 2000 | JP |
| 2001-013719 | Jan 2001 | JP |
| 2001-053069 | Feb 2001 | JP |
| 2001-058127 | Mar 2001 | JP |
| 2001-093871 | Apr 2001 | JP |
| 2001-149754 | Jun 2001 | JP |
| 2001-149918 | Jun 2001 | JP |
| 2001-196420 | Jul 2001 | JP |
| 2001-303252 | Oct 2001 | JP |
| 2001-332532 | Nov 2001 | JP |
| 2001-351915 | Dec 2001 | JP |
| 2002-022135 | Jan 2002 | JP |
| 2002-028487 | Jan 2002 | JP |
| 2002-069643 | Mar 2002 | JP |
| 2002-075960 | Mar 2002 | JP |
| 2002-126502 | May 2002 | JP |
| 2002-273161 | Sep 2002 | JP |
| 2002-273168 | Sep 2002 | JP |
| 2003-075070 | Mar 2003 | JP |
| 2003-264057 | Sep 2003 | JP |
| WO 95-11442 | Apr 1995 | WO |
| WO 9606700 | Mar 1996 | WO |
| WO 9638311 | Dec 1996 | WO |
| WO 97-13141 | Apr 1997 | WO |
| WO 01-55487 | Aug 2001 | WO |
| WO 01-58223 | Aug 2001 | WO |
| WO 01-82332 | Nov 2001 | WO |
| WO 02-26005 | Mar 2002 | WO |
| WO 02-061165 | Aug 2002 | WO |
| WO 02-061171 | Aug 2002 | WO |
| WO 02-062114 | Aug 2002 | WO |
| WO 02-062115 | Aug 2002 | WO |
| WO 02-067285 | Aug 2002 | WO |
| WO 02-067285 | Aug 2002 | WO |
| WO 03-018862 | Mar 2003 | WO |
| WO 03-018862 | Mar 2003 | WO |
| WO 03-028081 | Apr 2003 | WO |
| WO 03-095058 | Nov 2003 | WO |
| WO 03-095089 | Nov 2003 | WO |
| WO 03-095090 | Nov 2003 | WO |
| WO 03-095130 | Nov 2003 | WO |
| WO 03-095591 | Nov 2003 | WO |
| WO 03-095699 | Nov 2003 | WO |
| WO 03-095807 | Nov 2003 | WO |
| WO 03-096369 | Nov 2003 | WO |
| WO 03-096370 | Nov 2003 | WO |
| WO 03-096380 | Nov 2003 | WO |
| WO 03-096381 | Nov 2003 | WO |
| WO 03-096382 | Nov 2003 | WO |
| WO 03-096383 | Nov 2003 | WO |
| WO 03-096747 | Nov 2003 | WO |
| WO 03-096749 | Nov 2003 | WO |
| WO 03-096766 | Nov 2003 | WO |
| WO 03-096768 | Nov 2003 | WO |
| WO 03-096770 | Nov 2003 | WO |
| WO 03-096771 | Nov 2003 | WO |
| WO 03-096772 | Nov 2003 | WO |
| WO 03-096773 | Nov 2003 | WO |
| WO 03-096774 | Nov 2003 | WO |
| WO 2004-050939 | Jun 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060078675 A1 | Apr 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60435278 | Dec 2002 | US | |
| 60430677 | Dec 2002 | US | |
| 60378693 | May 2002 | US |