Patent Grant
10737835
This application is a National Stage of International Application No. PCT/JP2015/078605 filed Oct. 8, 2015, claiming priority based on Japanese Patent Application No. 2014-220663, filed Oct. 29, 2014, the contents of all of which are incorporated herein by reference in their entirety.
The present invention relates to a plastic molded body having a surface comprising a non-fluororesin.
Since plastics are generally molded easily as compared with glass and metals and can be easily molded into various shapes, they are used for various purposes. Among them, the package field of containers such as bottles and caps attached to containers is the typical application field of plastics.
By the way, when a liquid is contained in the above container, there is always a dripping problem and a device which prevents the liquid from dripping along the outer wall of the mouth portion of the container when the liquid contained in the container is poured out from the mouth portion is required.
According to the type of the liquid in contact with the surface of the container, there is also a liquid adhesion problem. For example, in a container for containing a highly viscous liquid, the liquid adheres to the inner wall of the container, thereby causing a problem with the dischargeability of the liquid from the container. That is, even when the container is inclined, the liquid is not discharged smoothly (low drop-off properties) or it is difficult to discharge all the amount of the liquid in the container, whereby a considerable amount of the liquid remains in the container. Therefore, means for suppressing liquid adhesion to the surface is required.
To prevent liquid dripping and liquid adhesion, liquid repellency should be provided to enhance slipping properties for a liquid on the surface of a plastic molded body, and it is conceivable that to improve liquid repellency, a fluorine-containing resin such as polytetrafluoroethylene is used as a plastic. However, as the fluorine-containing resin is very expensive and difficult to be molded, its use is greatly limited. Therefore, it is desired that the liquid repellency of a plastic molded body formed by using a non-fluororesin containing no fluorine such as a polyolefin or polyester should be improved.
In general, to improve liquid repellency, means for forming a liquid repellent film on the surface and means for forming irregularities on the surface are typical, and means combining them has recently been proposed.
That is, means for forming a liquid repellent thin film (for example, a film comprising a compound or resin containing fluorine or silicon) on the surface is to prevent liquid dripping or liquid adhesion by making a liquid repellent substance existent on the surface. In this means, there is limitation to liquid repellency, for example, liquid repellency is not satisfactory in terms of improving slipping properties for a liquid so that liquid dripping cannot be effectively prevented or the liquid drop-off properties are not fully enhanced. Since it is difficult to form a film which is uniform in thickness, liquid repellency is apt to vary.
The means for forming irregularities on the surface is to physically provide liquid repellency by surface shape. That is, when a liquid flows over an irregular surface, airs pockets are formed in concave portions, the contact state between the irregular surface and the liquid becomes solid-liquid contact and gas-liquid contact, and a gas (air) is a most hydrophobic substance. Therefore, by suitably setting the crude density of irregularities, extremely high liquid repellency is developed, thereby making it possible to improve drainability, prevent liquid dripping effectively and further improve liquid drop-off properties effectively. However, even in this means, when the liquid flows over the irregular surface repeatedly, the liquid gradually accumulates in the concave portions, and air pockets are gradually lost with the result that drainability and liquid drop-off properties gradually deteriorate.
In recent years, technology which combines the above means for making a liquid repellent substance existent on the surface and the above means for forming irregularities on the surface has been proposed. That is, the technology aims to effectively avoid inconvenience that the liquid accumulates in the concave portions by making the liquid repellent substance existent on a surface having irregularities, thereby maintaining liquid repellency for a long period of time.
For example, Patent Document 1 proposes the production of a water- and oil-repellent film by forming an inorganic hard film such as a silicon oxide film on the surface of a plastic film, making fine irregularities on this surface and forming a chemisorption monomolecular film containing fluorine on the irregular surface by using a compound containing a hydrocarbon fluoride group and a chlorosilyl group.
Patent Document 2 proposes a water- and oil-repellent resin molded body having fine irregularities on the surface of a resin molded body containing a fluoroalkyl-based surfactant having water- and oil-repellency.
However, even the above Patent Documents 1 and 2 do not succeed in maintaining drainability and liquid drop-off properties stably.
For example, in Patent Document 1, the chemisorption monomolecular film containing fluorine is gradually removed by bringing it into contact with a liquid repeatedly, whereby the liquid gradually accumulates in the concave portions, thereby gradually losing drainability and liquid drop-off properties.
In Patent Document 2, since the fluoroalkyl-based surfactant bleeds out onto the surface, water repellency and liquid repellency are developed. However, when the liquid is brought into contact with the surface repeatedly, the bleeding fluoroalkyl-based surfactant is gradually removed with the result that drainability and liquid drop-off properties gradually deteriorate.
Further, the inventors of the present invention previously proposed a plastic molded body having a fractal hierarchical surface irregular structure that primary irregularities are formed on the surface and secondary fine irregularities are formed on at least some of the primary irregularities (JP-A 2013-220998).
As secondary finer irregularities are formed within the area of the primary irregularities in this molded body, the entry of a liquid into the primary irregularities is effectively suppressed, and liquid repellency obtained by the primary irregularities is maintained stably.
However, even this means has limitation to the suppression of the deterioration of drainability and liquid drop-off properties. That is, the entry of the liquid into the secondary irregularities cannot be prevented completely, drainability and liquid drop-off properties obtained by the air pockets formed in the secondary irregularities gradually deteriorate, and therefore the liquid gradually enters the primary irregularities with the result that the deterioration of drainability and liquid drop-off properties cannot be avoided.
Even when the molded body is brought into contact with a liquid repeatedly, drainability and liquid drop-off properties must be maintained stably.
It is therefore an object of the present invention to provide a plastic molded body which maintains excellent liquid repellency for a long period of time and has a surface exhibiting the same levels of drainability and liquid drop-off properties as the initial levels even when it is brought into contact with a liquid repeatedly.
It is another object of the present invention to provide a plastic molded body having a surface which prevents dripping and liquid adhesion effectively by the above drainability and liquid drop-off properties.
According to the present invention, there is provided a plastic molded body having a surface comprising a non-fluororesin and a rough surface formed on the surface, wherein a fluorine atom is incorporated into the molecular chain of a non-fluororesin forming the rough surface.
In the plastic molded body of the present invention, preferably,
The plastic molded body of the present invention is formed from a non-fluororesin such as a polyolefin or polyester, a rough surface having fine irregularities is formed on the surface, and a fluorine atom is incorporated into the molecular chain of the non-fluororesin forming this rough surface. That is, when a liquid flows over this rough surface (fine irregular surface), the formation (gas-liquid contact) of air pockets by the rough surface and the improvement of liquid repellency by the fluorine atom are combined to ensure high drainability and liquid drop-off properties. However, since this fluorine atom is incorporated into the molecular chain of the non-fluororesin of the surface, it does not drop off from the surface (rough surface) and is existent on the surface (rough surface) stably. Therefore, even when a liquid is let flow repeatedly, stable liquid repellency is obtained.
That is, as shown in Examples which will be described hereinafter, in the plastic molded body of the present invention having the above rough surface, in a test for measuring the contact angle of a liquid (sauce) after the surface was inclined at a predetermined angle)(25° to drop the liquid repeatedly to contaminate the surface, even when dropping was repeated 100 times or more, the contact angle was almost the same as the initial value and liquid repellency was thus maintained. This is because a fluorine atom is incorporated into the molecular chain of the non-fluororesin forming the rough surface, whereby even when the molded body is brought into contact with the liquid repeatedly, the fluorine atom which exhibits liquid repellency is not removed.
For example, in the case of a rough surface as the surface, when this rough surface is treated with a silane coupling agent having a fluorine atom, or when the non-fluororesin forming the surface is mixed with a fluorine-containing surfactant, the fluorine atom-containing component is dropped on the rough surface after the surface is brought into contact with a liquid repeatedly, thereby gradually deteriorating liquid repellency.
Since the plastic molded body of the present invention has a rough surface which maintains liquid repellency stably as described above, this rough surface is formed at a suitable position according to the shape and purpose of the plastic molded body, thereby making it possible to develop stable drainability and to discharge a content liquid without dripping and swiftly without adhering or leaving the content liquid on the wall due to stable water repellency.
The present invention is effectively applied in the package field in which dripping, adhesion, retention and dischargeability (drop-off properties) at the time of discharging a content liquid become big problems, for example, caps, spouts or package materials such as containers including bottles.
In
The liquid repellency of a liquid on the above rough surface 100 will be described with reference to
That is, in
The theoretical formula (1) of the contact angle of the rough surface 100 in the Cassie mode is given below.
θE: contact angle
θ*: apparent contact angle
ϕs: area ratio (projection area of solid-liquid interface per unit area)
As understood from this theoretical formula, as ϕs becomes smaller, the apparent contact angle θ* becomes closer to 180° to exhibit super liquid repellency.
Meanwhile, when a droplet enters concave portions in a rough surface 1a, the droplet is not in composite contact but in contact only with a solid, which is represented by a Wenzel mode. In this Wenzel mode, the contact radius R at the contact interface of the droplet is large, and the theoretical formula (2) of the contact angle of the irregular surface is given below.
cos θ*=r cos θE (2)
θE: contact angle
θ*: apparent contact angle
R: irregularity degree (actual contact area/projection area of droplet)
As understood from this theoretical formula, as “r” becomes larger, the apparent contact angle θ* becomes closer to 180° to exhibit super liquid repellency.
Although it is known that liquid repellency is improved in both the Wenzel mode and the Cassie mode as described above, to improve drop-off properties and repeated drop-off properties, not the Wenzel mode but the Cassie mode is maintained stably. That is, the inventors of the present invention think that it is necessary to maintain the air pockets in the concave portions stably. That is, the interface between a liquid phase and a solid phase is large in the Wenzel mode with the result that physical adsorption force applied to the interface is large, whereby the contact angle is large to repel a liquid but a droplet does not easily drop off. It is considered that since the interface is small in the Cassie mode, an energy barrier which must be overcome when a droplet drops off is so low that the droplet drops off easily and repeatedly.
In the present invention, liquid repellency is chemically provided by incorporating a fluorine atom into the molecular chain of the non-fluororesin forming the rough surface 100 in order to effectively keep the contact of a droplet in the above Cassie mode. That is, when the liquid enters the concave portions in the rough surface 100, the contact pattern of the droplet becomes the Wenzel mode with the result that super liquid repellency in the Cassie mode is impaired. In the present invention, since liquid repellency is chemically provided to this rough surface 1a by incorporating a fluorine atom into the molecular chain, the entry of the liquid into the concave portions is effectively suppressed, thereby maintaining super liquid repellency in the Cassie mode stably.
In addition, in the present invention, in at least part of the rough surface 100, for example, the tops of the convex portions or the bottoms of the concave portions, a fluorine atom for developing chemical liquid repellency is incorporated into the molecular chain of the non-fluororesin forming this surface. Therefore, even when the liquid comes into contact with this rough surface 100 repeatedly, the fluorine atom is not removed and chemical liquid repellency is maintained stably with the result that super liquid repellency in the Cassie mode is not degraded and is maintained at the same high level as the initial level. Making use of this, excellent drainability (dripping prevention) and liquid drop-off properties (liquid dischargibility) can be maintained for a long period of time.
Further, since a film containing a fluorine atom is not formed but a fluorine atom is incorporated into the molecular chain of the non-fluororesin of the surface, the control of film thickness is not necessary and there are no variations in liquid repellency according to film thickness.
As for the irregularity degree of the above rough surface 100, to fully develop liquid repellency in the Cassie mode, the area ratio θs represented by the area of the top “S” of the convex portion per unit area in the rough surface 100 is not less than 0.05, preferably not less than 0.08 and not more than 0.8, particularly preferably not more than 0.5 from the viewpoints of moldability and mechanical strength. For example, when a droplet is dropped on the rough surface 100, the area ratio ϕs represented by the projection area of a solid-liquid interface per unit area is preferably 0.05 to 0.8, more preferably 0.08 to 0.5 so that the Cassie mode is preferably maintained stably.
The depth “d” in the rough surface 100 is preferably 5 to 200 μm, particularly preferably 10 to 50 μm.
The rough surface 100 may have an irregular structure shown in
That is, a droplet is supported by a Laplace pressure (Δp) represented by the irregular point angle α and the ½ pitch R0 of irregularities according to the formula (3) to form an air pocket. That is, when the irregular point angle α becomes small, the ½ pitch R0 becomes small and the irregular structure becomes like a frog, the Laplace pressure becomes so large that a droplet hardly enter irregularities, thereby developing liquid repellency.
Therefore, as understood from
Δp=−γ cos(θ−α)/(R0+h cosα) (3)
In the present invention, the rough surface 100 which has the above fine irregularities can be easily formed by a transfer method using a metal stamper. That is, a stamper having a rough surface part corresponding to the above fine irregularities obtained by a resist method is heated at a suitable temperature and pressed against a predetermined part of the surface of a plastic molded body to transfer the rough surface part, thereby making it possible to form the above rough surface 100 on the surface of the plastic molded body. Therefore, the irregular surface of the stamper is formed on the surface 1 of the plastic molded body in such a manner that the irregularities are reversed.
In
Further, incorporation into the molecular chain of the non-fluororesin forming the surface is carried out by etching using fluorine plasma.
This fluorine plasma etching may be carried out by a method known per se. For example, a CF4 gas or SiF4 gas is used, the surface of a plastic molded body on which the rough surface 100 is to be formed is arranged between a pair of electrodes, and a high-frequency electric field is applied to produce fluorine atom plasma (atomic fluorine) which is then collided with apart for forming the rough surface 100, whereby the fluorine atom is incorporated into the molecular chain of the non-fluororesin forming the surface (rough surface 1a). That is, the resin of the surface is gasified or decomposed and the fluorine atom is incorporated at the same time.
Therefore, super fine irregularities are formed by etching in an area where the fluorine atom is incorporated. The arithmetic average roughness Ra of the super fine irregularities is generally not more than 100 nm and Ra/RSm 5×10−3.
Conditions such as the high-frequency voltage to be applied and the etching time are set to suitable ranges according to the roughness (area ratio ϕs) of the rough surface 100. For example, in a liquid repellent durability test which is carried out in Examples to be described hereinafter, when the contact angle is measured after a droplet (sauce) is dropped 100 times, a contact angle which is not less than 90% of the initial contact angle should be obtained. The conditions under which this contact angle is obtained should be set by a preliminary laboratory test. Depending on the roughness of the rough surface 100, in general, when the element ratio (F/C) of a fluorine atom and a carbon atom per unit area is not less than 40%, specifically 50 to 300%, stable super high liquid repellency like the above liquid repellency can be secured without impairing surface strength. The element ratio can be calculated by analyzing the elemental composition of the surface with an X-ray photoelectron spectroscope.
In the above-described present invention, the rough surface 100 is not limited to those shown in
For example, as shown in
On the rough surface 100 having this hierarchical structure, the secondary irregularities 165 on the surface of the primary irregularities 160 should have a surface roughness that ensures the formation of the secondary air pockets which prevent a droplet on the secondary irregularities 165 from entering the concave portions 160b of the primary irregularities 160. For example, the ratio Ra/RSm of the arithmetic average roughness and the average length is preferably not less than 50×10−3, particularly preferably not less than 200×10−3.
The above primary irregularities 160 should have the same area ratio ϕ and the same depth “d” of the irregularities as those of the rough surface 100 shown in
Although the second irregularities 165 are most preferably formed on the entire surface of the primary irregularities 160 from the viewpoint of preventing the droplet 170 from entering the concave portions 160b of the primary irregularities 160 more effectively, they should be formed at the upper ends of at least the convex portions 160a of the primary irregularities 160.
The rough surface 100 having the above hierarchical structure can be formed by forming a fine secondary irregular surface on the irregular surface of a stamper for forming primary irregularities by blasting and transferring the fine secondary irregular surface by using the stamper.
In the present invention, in at least part of an area on the primary irregularities 160 on which the secondary irregularities 165 have been formed as described above, specifically, portions which become the tops of the convex portions 160a of the primary irregularities 160 and portions which become the bottom portions of the concave portions 160b, a fluorine atom is incorporated into the molecular chain of the non-fluororesin forming the surface by fluorine plasma etching. In that area, tertiary irregularities which are finer than the secondary irregularities are formed by etching at the time of incorporating the fluorine atom. The arithmetic average roughness Ra of the tertiary irregularities is not more than 100 nm like the super fine irregularities formed by the above-described etching and Ra/RSm 5×10−3.
In the above-described present invention, although the surface of this plastic molded body is formed by using the non-fluororesin, as this non-fluororesin, that is, a resin containing no fluorine, any thermoplastic resin, thermosetting resin or photocurable resin may be used as long as the rough surface 100 having the above irregularities can be formed and the fluorine atom can be incorporated into the molecular chain by fluorine plasma etching. A suitable resin may be selected according to the purpose of this molded body and may have a multi-layer structure.
In general, in the package field, olefin-based resins typified by polyethylene, polypropylene and a copolymer of ethylene or propylene and another olefin, and polyesters such as polyethylene terephthalate (PET), polyethylene isophthalate and polyethylene naphthalate are typical resins for forming the surface.
The plastic molded body of the present invention may be various in form, making use of the long service life and excellent liquid repellency of the above-described rough surface 100 and can be effectively used as a package for containing drinks, seasoning liquids and drug liquids due to excellent drainability.
In
In this package, although not shown in this plastic bottle, the lower part of the mouth portion 1 is connected to a curved shoulder portion connected to a barrel portion whose lower end is closed by a bottom portion.
In this plastic bottle, a screw thread 5 for holding the cap 3 is formed on the outer surface, an annular projection 7 is formed below the screw thread 5, and a support ring 9 for holding the bottle at the time of transport is formed below the annular projection 7.
Meanwhile, the cap 3 has a top panel portion 10 and a cylindrical side wall 11 extending downward from the periphery of the top panel portion 10, a sealing liner 13 is formed on the inner surface (especially a peripheral portion) of the top panel portion 10, and a screw thread 15 to be mated with the screw thread 5 of the mouth portion 1 of the bottle is formed on the inner surface of the cylindrical side wall 11.
That is, the cap 3 is attached to the mouth portion 1 by screw mating, and the upper part of the mouth portion 1 comes into close contact with the liner 13 when the cap 3 is attached, thereby sealing the inside of the bottle.
To ensure this sealing, the liner 13 has a relatively long inner ring 13a and a relatively short outer ring 13b, the upper end part of the mouth portion 1 enters a space between them, and the inner side face, the upper end face and the outer side face of this upper end part come into close contact with the liner 13 to ensure sealability.
Not shown in
In the above package, after the cap 3 is removed from the mouth portion 1 of the bottle, a liquid contained in the bottle is poured out from the mouth portion 1 by inclining the bottle. As understood from this, the spout of the package to which the cap 3 (threaded cap) is attached is the upper end face X of the mouth portion 1 of the bottle.
That is, when the plastic molded body of the present invention is applied to this plastic bottle, the above-described irregular surface 100 is formed on the upper end face (may be simply referred to as “spout” hereinafter) X of the mouth portion 1 of the bottle.
Further, although the mouth portion 1 of the bottle is the spout X in the above-described example, the plastic molded body of the present invention may be applied to a cap.
In
That is, the cap 50 includes a cap body 51 which is fixed by fitting onto the mouth portion 1 of the bottle and a hinge lid 55 which is hinge connected to the cap body 51 through a hinge band 53.
The cap body 51 includes a top panel 61 and a cylindrical side wall 63 extending downward from the periphery of the top panel 61, and an annular projection 65 extending downward is formed on the inner surface of the top panel 61 with a space between it and the cylindrical side wall 63. That is, the upper part of the bottle mouth portion 1 is fitted in the space between the cylindrical side wall 63 and the annular projection 65 by plugging, whereby the cap body 51 is firmly fixed to the bottle mouth portion 1.
An opening 67 which is a flow channel at the time of pouring out a content liquid is formed in the center part of the top panel 61, and a spouting cylinder 69 is formed upright around the opening 67 on the top surface of the top panel 61.
In general, this opening 67 is closed before it is sold and used after the package is produced, and the wall of this part is peeled off to form the opening 67 when a general consumer pours out the content liquid from the bottle for the first time.
Meanwhile, the hinge lid 55 includes a top panel portion 71 and a skirt portion 73 extending from the periphery of the top panel portion 71, and the end part of the skirt portion 73 is connected to the hinge band 53 which is connected to the upper end of the cylindrical side wall 63 of the cap body 51. The hinge lid 55 is opened and closed by turning with the hinge band 53 as a fulcrum point.
A seal ring 75 is formed on the inner wall (top wall in
That is, when the hinge lid 55 is closed, the outer surface of the seal ring 75 comes into close contact with the inner surface of the spouting cylinder 69, thereby ensuring sealability when the opening 67 for pouring out the content liquid is formed.
The sealing flange 77 is provided to facilitate turning for opening and closing the hinge lid 55.
Since the content liquid is poured out from the spouting cylinder 69 by opening the hinge lid 55 in this hinge cap, the upper end of the spouting cylinder 69 expands a little outward like a trumpet.
The upper end part of this spouting cylinder 69, especially a part on a side opposite to the hinge band 53 is a spout X. That is, since the opened hinge lid 55 is existent on the side where the hinge band 53 is existent, the content liquid is poured out to the side opposite to the side where the hinge band 53 is existent.
As understood from the above explanation, in this hinge cap, the above-described rough surface 100 is formed in a part which becomes at least the spout X of the upper end of the spouting cylinder 69.
The rough surface 100 may extend downward on the inner surface of the spouting cylinder 69, preferably not to a part in close contact with the seal ring 75 of the above-described hinge lid 55. When the rough surface 100 extends up to this part, sealability may deteriorate.
In
In the above example, a plastic material forming the plastic bottle having the mouth portion 1 is not particularly limited and various thermoplastic resins, for example, olefin-based resins such as polyethylene and polypropylene and polyester resins typified by polyethylene terephthalate (PET) may be used like known plastic bottles. Since the upper end surface of the mouth portion 1 of this bottle becomes the spout X and the rough surface 100 composed of an irregular surface is formed on this part, a polyester resin is most preferred from the viewpoints of the shape stability and strength of the irregular surface 100.
When the irregular surface 100 is formed on the spout X which is on the cap side, this bottle may be made of glass or metal.
Further, a plastic material forming the caps 3 and 50 is not particularly limited and various thermoplastic resins, for example, olefin-based resins such as polyethylene and polypropylene may be used like known plastic caps.
When the rough surface 100 is formed on the spout X which is on the bottle side, this cap may be a screw cap made of metal.
Further, the liner material 13 formed on the cap 3 is formed from a known elastic material, for example, an ethylene-propylene copolymer elastomer or thermoplastic elastomer such as styrene-based elastomer.
To form the above-described rough surface 100 on the spout X of the mouth portion 1 of the above-described bottle or the spouts X of the caps 3 and 50, a predetermined stamper is pressed against this spout X to form predetermined irregularities and then fluorine plasma etching is carried out.
As shown in
In
Further, to form the rough surface 100 on the above-described bottles and caps, the bottle and the cap are molded by predetermined means in advance and the rough surface 100 is formed at a predetermined site by transfer using the above-described stamper.
The shapes of the irregularities on the rough surface 100 are arbitrary as long as they are designed to ensure that a liquid flows over the irregularities.
Since the plastic molded body of the present invention maintains excellent liquid repellency for a long period of time and has a rough surface which exhibits the same levels of drainability and drop-off properties as the initial levels even when it is brought into contact with a liquid repeatedly, it is effectively applied to a package material such as a cap or container. By forming the above-described rough surface 100 on the spout, it can discharge a liquid without dripping. When the above-described rough surface 100 is formed on the entire inner surface of the container, a viscous paste-like product typified by ketchup or mayonnaise can be discharged smoothly and completely without leaving it in the container.
The following examples are provided to explain the excellent characteristic properties of the present invention.
(1) Substrate;
Grade: LJ8041 (Japan Polyethylene Corporation)
* Primary irregularity stamper
A master was produced by photolithography to obtain a stamper having primary irregularities engraved by Ni electroforming.
Primary irregularities
ϕs=0.2 (s=20 μm, d=30 μm, pitch=100 μm)
Secondary Irregularity Stamper
The master produced by Cu electroforming was wet etched to form a rough surface so as to obtain a stamper having secondary irregularities engraved by Ni electroforming.
Secondary Irregularities
Fractal stamper having primary irregularities+secondary irregularities
Shot blast was made on the above primary irregularity stamper to obtain a stamper having secondary irregularities engraved on the primary irregularities.
Primary Irregularities
The stamper was heated at 240° C. by infrared radiation heating with a halogen lamp and pressed against the substrate for 1 second and then the substrate was cooled to transfer mold primary irregularities and secondary irregularities.
(4) Carbon Fluoride Plasma Treatment
Discharge system: surface wave plasma
Power source: 1500 W@2.45 GHz
Treatment conditions
Degree of vacuum: 4 Pa
Raw material gas: CF4 100 sccm
Plasma irradiation time: 20 seconds, 200 seconds
(5) Evaluation of Performance
(5-1) Evaluation of Irregular Shape
For the transferred surface of the substrate, primary irregularities and secondary irregularities were measured with a white light interferometer, and third irregularities were measured with an atomic force microscope (AFM) to calculate the area ratio ϕs, arithmetic average roughness Ra and average length RSm.
Measurement instrument: New View 7300 of ZYGO Corporation
50-times objective lens
2.0-times eyepiece lens
Long wavelength cut-off value λc=13.846155 μm
Short wavelength cut-off value λs=346.155 nm
Measurement instrument: Nano Scope III of Veeco Instruments Inc.
Long wavelength cut-off value λc=0.0824 μm
(5-2) Evaluation of Fluorine Atom Content
The wide-band spectrum of the surface of the substrate was analyzed by using an X-ray photoelectron spectroscope to measure the amounts of elements existent on the surface so as to calculate the ratio (F/C) of the fluorine atom and the carbon atom.
4 μL of a real liquid was dropped on the surface of the substrate to take a picture of a droplet shape from the side. The contact angle was measured by image analysis.
The surface of the substrate was gradually inclined to take an inclination angle when the droplet dropped off as a drop-off angle.
Real liquid
Water
Soy sauce
Sauce
cooking oil
When the contact angle is 130° or more, it is judged that the molded body has liquid repellency. When the drop-off angle is 20° or less, it is judged that the molded body has drop-off properties.
(5-4) Evaluation of Liquid Repellent Durability
A 40 μL droplet of the real liquid was dropped on the substrate inclined at 25° an arbitrary number of times to contaminate the surface of the substrate.
The contact angle of the real liquid with the surface of the contaminated substrate was measured (amount of a droplet: 4 μL).
Real liquid
Sauce
Cooking oil
By comparing the contact angle θ0 when the number of dropping times is 0 and the contact angle θ100 when the number of dropping times is 100 from the relationship between the number of dropping times and the contact angle, when θ100/θ0≥0.9, it is judged that the molded body has liquid repellent durability.
The evaluation results are shown in Table 1.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2014-220663 | Oct 2014 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2015/078605 | 10/8/2015 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2016/067875 | 5/6/2016 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5324566 | Ogawa | Jun 1994 | A |
| 20130235120 | Hirabayashi et al. | Sep 2013 | A1 |
| 20140332570 | Akutsu et al. | Nov 2014 | A1 |
| 20150314554 | Fujiwara et al. | Nov 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 102963130 | Mar 2013 | CN |
| 63-035632 | Feb 1988 | JP |
| 8-054006 | Feb 1996 | JP |
| 3358131 | Dec 2002 | JP |
| 3487888 | Jan 2004 | JP |
| 2010-174079 | Aug 2010 | JP |
| 2014-065175 | Apr 2014 | JP |
| 10-2012-0067448 | Jun 2012 | KR |
| 2013077380 | May 2013 | WO |
| 2014087695 | Jun 2014 | WO |
| Entry |
|---|
| Translation of JPH0854006. (Year: 1996). |
| Translation of JP2010-174079. (Year: 2010). |
| Translation of JP 3487888 (also JPH07197017A). (Year: 2004). |
| International Search Report of PCT/JP2015/078605, dated Dec. 22, 2015 (PCT/ISA/210). |
| Communication dated May 30, 2018 from the European Patent Office in counterpart Application No. 15854211.8. |
| Communication dated Aug. 1, 2019, from the State Intellectual Property Office of the P.R.C in corresponding Chinese Patent Application No. 201580059189.4. |
| Number | Date | Country | |
|---|---|---|---|
| 20180257817 A1 | Sep 2018 | US |