Polycrystalline Diamond Cutting Tool with Coated Body

Abstract
A cutting tool for machining metal workpieces using polycrystalline diamond cutting surfaces with interspersed guide surfaces and chip evacuation surfaces. When machining holes in cast aluminum alloy workpieces it is found that aluminum machining chips adhere to guide surfaces and chip evacuation surfaces and mar the machined surface. It is found that when the guide and chip evacuation surfaces are coated with a diamond-like carbon material, aluminum chips do not mar the machined surfaces.
Description
TECHNICAL FIELD

This disclosure pertains to cutting tools for machining surfaces of aluminum alloy workpieces. More specifically, this invention pertains to a practice for coating body surfaces of such cutting tools to avoid aluminum transfer to the tool, maximize the tool life, and minimize marring of machined surfaces.


BACKGROUND OF THE INVENTION

Many articles of manufacture are made from metal castings with surfaces that are machined to a specified shape and to specified dimensions. Often such machining includes drilling or finishing of holes in the preformed body. Many automotive vehicle powertrain components are made of aluminum alloy castings that require hole drilling or hole finishing operations. Reaming is an example of a hole finishing operation. In this operation, a small amount of stock is removed from the inner diameter of the hole with a special tool called a reamer. Reamers are used in finishing operations for holes in cast aluminum alloy valve bodies for vehicle transmissions and in engine cylinder blocks and cylinder heads. The range of cutting operations is wide, requiring the use of many cutting tools and metal machining operations. The design of the cutting tools is important in maintaining machining operations without stopping for tool replacement or tool refurbishing.


Cutting tools with polycrystalline diamond inserts are used widely in machining of aluminum, its alloys, and other non-ferrous materials. In particular, round rotatable cutting tools with polycrystalline diamond (PCD) inserts are used in finishing operations to machine holes in aluminum alloy castings to final dimensions and roundness. The PCD insert is a body that provides a hard, durable cutting tip or edge for a machining operation. PCD-tipped tools are typically formed of a body of strong tool steel or metal carbide composition with one or more pairs of PCD cutting edges. The PCD cutting inserts comprise an inter-grown mass of randomly oriented, hard diamond particles sintered in a suitable matrix material. The cutting edges formed by the hard PCD material improve the effective life of the cutting tool and provide a better surface quality.


In addition to the PCD cutting edges, the tool body (for example, a tool intended to rotate in shaping a hole) may also have guide surfaces and/or edges that help position the tool with respect to the workpiece and reduce the tool round out. In particular, a PCD-tipped reamer may have surfaces and/or edges that follow the finished hole and help maintain concentricity of the tool and the hole, while the cutting surfaces remove aluminum alloy chips or particles. Sometimes these reamers have one or more pairs of radially extending guide surfaces and/or edges. In other cases, these reamers may have three radially extending guide surfaces and/or edges. The reamers are usually machined so that the guide surfaces and/or edges follow closely the machined hole but do not damage it and do not remove additional material. This is achieved by making the diameter of the guiding surfaces and/or edges a few microns smaller than the diameter of the PCD cutting edges. Guide surfaces and/or edges on a rapidly rotating tool engage and follow along the machined surface and reduce vibration of the cutting tool.


In addition to the guide surfaces and/or edges and the PCD cutting edges, the tool may also have chip evacuation surfaces to evacuate chips along the tool body and from the hole being cut. In reamers, these surfaces form flutes and sometimes have the shape of a circular spiral groove in the body of the tool. In other cases, these surfaces may be straight. In still other cases, these surfaces may have a combination of spiral and straight surfaces.


Thus, during the operation of the cutting tool, aluminum alloy chips are removed from the machined surface by the PCD cutting edges and removed from the cutting zone by sliding along chip evacuation surfaces. Sometimes, however, aluminum chips accumulate momentarily on the rotating guide surfaces and/or edges or chip evacuation surfaces. When chips adhere to and accumulate on the chip evacuation surfaces, the passages for the sequential chips are obstructed, resulting in material buildup, which scratches and/or mars the surface being machined. This accumulation of debris on tool surfaces is more rapid when the tool has been used for a period of time and has been worn. Left uncorrected, this accumulation of debris on tool surfaces can lead to decreased surface quality of the machined holes and/or to breakage of the tool. Thus, this condition may require untimely refurbishing of the cutting tool.


The cutting speeds are usually high during machining with PCD cutting tools. As a result, the removed chips are hot, which increases the probability that the chip will adhere momentarily to the non-cutting tool surfaces, such as guiding surfaces and/or edges or chip evacuation surfaces, resulting in chip accumulation and marring the surface. There is a need to minimize accumulation of aluminum material on guide surfaces and/or chip evacuation surfaces of PCD cutting tools.


SUMMARY OF THE INVENTION

A representative cutting tool may, for example, be a reamer, a tool that is rotated for enlarging or shaping holes. The body of the tool may be formed of a high-speed tool steel or a cemented carbide. The cemented carbide material may be made by sintering particles of tungsten carbide using cobalt as a binder.


When the reamer is used for finishing holes in aluminum, it may be shaped to have a holder portion and cutter body portion. The holder portion of the cutting tool is placed and secured in the spindle of a powered machine that locates and rotates the cutting tool. The cutter body portion of the tool carries opposed polycrystalline diamond (PCD) cutting edges that remove stock from the inner diameter of a hole in the workpiece in a metal removing cutting operation.


In an embodiment of this invention the guide surfaces/edges and the chip evacuation surfaces of the cutting tool are coated with a hydrogenated diamond-like carbon (DLC) material. It is found that the aluminum chips do not stick to the diamond-like carbon material and the chips are carried away from the machined surface and out of cutting zone by the rotating tool and machining fluid or by other means.


In one DLC coating embodiment of the invention, the whole body of the tool is coated with a film of hydrogenated diamond-like carbon material. Since the temperature and local wear is the highest near the cutting edges, and since the DLC is much softer than the PCD cutting edge, the DLC is readily abraded from the vicinity of the polycrystalline diamond cutting edges of the tool. More importantly, however, the adherent DLC coating remains on the guide surfaces and edges, chip evacuation surfaces, and other cutter body surfaces of the tool, where the temperatures and the pressures are much lower. As the aluminum chips do not adhere to the DLC coating, the cutting operations may be continued for longer operating periods without tool refurbishing.


Diamonds consist of true, long range crystalline (generally of cubic crystal structure) arrangements of carbon atoms which have sp3 bonds. Generally diamond-like carbon materials are amorphous, mixed clusters of carbon atoms connected with sp2 and sp3 bonds. In hydrogenated diamond-like carbons, hydrogen atoms are bonded to some of the carbon atoms. The hydrogenated diamond-like carbon materials are often somewhat softer and more flexible than hydrogen-free amorphous carbons, and more chemically inert to aluminum. These diamond-like carbons may be prepared by different suitable methods. For example, plasma assisted chemical vapor deposition techniques employing radio frequency or direct current glow discharges in hydrocarbon gas mixtures produce smooth amorphous carbon and hydrocarbon films which have mixed sp2 and sp3 bonds. The films may be deposited on substrates such as cutting tool bodies. Other methods may be used to deposit hydrogenated diamond-like carbon films on cutting tool bodies in the practice of this invention. These adherent and durable carbon films serve as slippery pathways to shed and evacuate aluminum machining chips and exclude adhesion of aluminum to the tool, thus minimizing the scoring of the machined aluminum alloy surface.


Other objects and advantages of the invention will be apparent from a description of further illustrative embodiments of the invention which follow.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is an axonometric drawing of a reamer illustrating cutting surfaces, chip evacuation surfaces and guide surfaces.



FIG. 2 is a cross-section of the cutting tool of FIG. 1, taken at 2-2, illustrating the location of diamond-like coating on guide surfaces of the tool.





DESCRIPTION OF PREFERRED EMBODIMENTS

When many like machining operations are being performed with metal cutting tools on like workpieces it is often a manufacturing strategy to employ tool designs and materials that enable many repeated machining operations to be performed before it is necessary to refurbish the tool. The selection of the tool shape and material will often depend on the composition of the metal workpiece. This invention pertains to such tool designs and materials.


Practices of this invention are applicable to cutting tools that have a combination of cutting edges and non-cutting surfaces and edges. Examples of the non-cutting surfaces and edges include guide surfaces or edges and chip-evacuation surfaces. According to one embodiment, the non-cutting surfaces of the tool may be coated with DLC. In cutting tools, the cutting surfaces remove metal chips from a workpiece surface. The guide surfaces space the tool from the workpiece surface. The chip evacuation surfaces provide paths for chip evacuation from the cutting zone.


The tool may be made of a suitably hard metal such as high speed steel, a tool steel, or a metal compound such as tungsten carbide. The cutting surfaces of the tool may have a brazed, relatively thin, deposit of polycrystalline diamond material for prolonged tool life. This deposit for cutting is sometimes called an “insert.” Obviously, the tool may be formed in many different shapes and other materials may be used in making the cutting tool. In various embodiments, the tool may be, for example, but not limited to, a drill, reamer, milling cutter, boring tool, or lathe cutter.


In one embodiment, the tool may be a rotating reamer. The reamer may be used for finishing holes in a metal workpiece such as an aluminum alloy casting of an automotive vehicle transmission valve body, a vehicle cylinder block, or a cylinder head. Such a reamer is illustrated in FIGS. 1 and 2. FIG. 1 presents an axonometric view of the reamer. FIG. 2 presents a cross-sectional view of a portion of the cutting tip of the reamer 10 taken along line 2-2 of FIG. 1. The reamer 10 may rotate in a counter-clockwise direction as shown by the arrow in FIG. 2.


Referring to FIG. 1, reamer 10 has a round holder portion or shank 12 with a center of rotation and with an axially extending cutter body 14. The reamer 10 is designed and shaped for finishing (to a specified roundness and dimension) many like holes in aluminum alloy castings. Except as described below, holder portion 12 and cutter body 14 are formed as a single piece, suitably of sintered tungsten carbide, or the like. The round holder portion 12 is adapted to be secured by chuck jaws of a powered rotary machine, not shown. Holder portion 12 may have a flat surface 16 for engagement by the rotating spindle of the machine to prevent slippage of the reamer in the holding mechanism of the machine. Cutting edges 22 are provided to remove aluminum chips as the reamer 10 is rotated in a hole in a casting.


Referring to FIGS. 1 and 2, the cutter body 14 is shaped with a set of opposed slots or grooves 15, also called chip evacuation flutes. As best seen in FIG. 2, flutes 15 are formed by the removal of arcuate portions along the axis of the cutter body. Flutes 15 have flat radial surfaces 18 and 19 that shape the flutes and provide chip evacuation surfaces in impellers. The radial chip evacuation surfaces 18 and 19 may extend from a center portion of the tool to the outer circumference of cutter body 14. In operation of the tool, the flutes 15 may also be confined by the surface of the machined hole in the workpiece.


As seen in FIG. 2, a layer 20 of sintered polycrystalline diamond material (PCD) is attached to the chip evacuation surface 18 of the chip evacuation flute 15. The outermost corners of the PCD layers 20 form the cutting edges 22 of the reamer 10. The cutting edges 22 remove aluminum chips (not shown) which are carried along the PCD layer 20 and axially along the chip evacuation surface 18 of the chip evacuation flute 15, and eventually out of the machined hole.


Cutter body 14 is also shaped with two diametrically opposed guides 24. One guide 24 is shown in FIG. 1 and both guides 24 are seen in FIG. 2. In this embodiment, guides 24 are spaced ninety degrees from cutting edges 22. The diameter of guides 24 is made a few microns smaller than the diameter swept by the cutting edges 22. The diameter of guides 24 may be, for example, six microns smaller than the diameter swept by the cutting edges, leaving a gap of three microns between the machined hole surface and the guides 24 on each side of the reamer 10.


In a machining operation, the reamer 10 is rotating (e.g., at 4,000 to 10,000 rpm) in a workpiece hole. As the cutting edges 22 engage the workpiece, the cutter body 14 flexes and the guides 24 come into contact with workpiece surfaces and machine chips.


In accordance with this invention, the outer radius surfaces 26 of the guide 24 are provided with a coating 28 of DLC material. In preferred embodiments of the invention, a hydrogenated diamond-like carbon material is deposited on the outer surfaces 26. Preferably, the thickness of the coating 28 is between one and three microns.


In many embodiments of the invention the DLC material will be deposited from a vapor using plasma. In such embodiments, it may be easier and preferred to coat much of the outer surface of the cutter body 14. Such extended coating is indicated by dashed line coating 28′ in FIG. 2. DLC coating 28′ is not shown in FIG. 1 for more clarity in illustration of cutter body 14 and its features. Extended coating 28′ may also be applied over the polycrystalline diamond layer 20. But any DLC coating 28, 28′ on the polycrystalline diamond layer 20 may be gradually abraded away and removed from the machined hole.


A function of DLC coating 28, 28′ on cutter body 14, including guides 24 and flute 15 (which also serves to evacuate the chips), is to minimize sticking of aluminum machining chips. It is found that when aluminum chips are wedged between the guides 24 and the machined hole surface, or between chip evacuation surfaces 18 and the machined hole surface, then scoring or other damage to the finished surface of the hole may occur. DLC coating 28, 28′ permits the aluminum chips to slide over cutter body 14 surfaces (including guides 24 and flutes 15) and be removed from the machined hole.


The DLC coating acts like a low friction coating to which aluminum chips display low adhesion during metal cutting of aluminum and aluminum alloy surfaces. There are other low-friction coating materials that may be employed in place of DLC or in combination with DLC on cutter tool bodies to prevent the build up of aluminum machining chips as a result of adhesion with the cutting tool surfaces. For example, metal-containing diamond-like carbon coatings, titanium diboride (TiB2) coatings, or nanocomposite tungsten carbide/carbon coatings may be applied to a cutting tool body to facilitate removal of aluminum machining chips and minimize their accumulation on cutting tool surfaces.


Practices of the invention have been shown by examples that are presented as illustrations and not limitations of the invention.

Claims
  • 1. A metal cutting tool for non-ferrous alloy workpieces comprising: a cutting edge, for removal of metal machining chips from a workpiece to form a machined surface; anda non-cutting surface along which machining chips are removed from the workpiece, the non-cutting surface comprising a coating to prevent adherence of the machining chips; andwherein the coating comprises at least one material selected from the group consisting of diamond material, diamond-like carbon material, metal-containing diamond-like carbon material, titanium diboride material, and nanocomposite tungsten carbide/carbon material.
  • 2. A metal cutting tool as recited in claim 1 wherein the non-cutting surface comprise a guide surface.
  • 3. A metal cutting tool as recited in claim 1 wherein the non-cutting surface comprises a chip evacuation surface.
  • 4. A metal cutting tool as recited in claim 1 wherein the cutting edge comprises polycrystalline diamond.
  • 5. A metal cutting tool as recited in claim 1 wherein the workpiece is made of an aluminum alloy.
  • 6. A metal cutting tool as recited in claim 1 wherein the non-cutting surface is designed and machined to guide the tool along the machined surface.
  • 7. A tool for machining inner diameters of holes in non-ferrous alloy workpieces, the tool being rotatable at a machining rate of rotation, the tool comprising: a round body with an axis of rotation, a tool holder portion at one end of the round body, and a machining portion at the other end of the round body;the machining portion comprising:opposing cutting surfaces in the circumference of the machining portion for removal of machining chips from the workpiece,guide surfaces for guiding the tool in the hole, andchip removal flutes,wherein at least one of the guide surfaces and the chip removal flutes are coated with diamond-like carbon material or hydrogenated diamond-like carbon material to prevent adherence of the metal machining chips to the guide surfaces and the chip removal flutes.
  • 8. A tool as recited in claim 7 wherein the guide surfaces are up to six microns smaller in diameter than the diameter swept by the cutting edges.
  • 9. A tool as recited in claim 7 wherein the cutting surfaces comprise polycrystalline diamond.
  • 10. A tool as recited in claim 7 wherein the workpiece is made of an aluminum alloy.
  • 11. A tool as recited in claim 7 wherein the chip removal flutes comprise chip evacuation surfaces for removal of the chips from the workpiece, the chip evacuation surfaces being coated with diamond-like carbon material to reduce adherence of the metal machining chips to the chip evacuation surfaces.
  • 12. A tool as recited in claim 7 wherein the tool comprises at least two cutting surfaces, periodically spaced around the circumference of the tool and comprising polycrystalline diamond; and wherein the tool comprises at least two guide surfaces, periodically spaced around the circumference of the tool and coated with diamond-like carbon.
  • 13. A tool as recited in claim 12 comprising two cutting surfaces spaced 180° circumferentially and two guide surfaces spaced 90° circumferentially from the cutting surfaces.
  • 14. A tool as recited in claim 12 comprising three cutting surfaces spaced 120° circumferentially and three guide surfaces spaced 60° circumferentially from the cutting surfaces.
  • 15. A tool as recited in claim 12 wherein the cutting surfaces form a spiral on the external surfaces of the tool, and the guide surfaces form a spiral offset from the cutting surfaces.
  • 16. A tool as recited in claim 7 wherein the tool comprises one of a reamer, drill, milling cutter, boring tool, or lathe cutter.
  • 17. A method of machining cast non-ferrous alloy workpieces with a rotating cutting tool comprising cutting edges for removing machining chips from the workpiece, guide surfaces to guide the tool along the machined surface, and chip evacuation surfaces for evacuation of the chips, the method comprising: coating at least one of the guide surfaces and the chip evacuation surfaces of the rotating cutting tool with diamond-like carbon to reduce adherence of machining chips to the guide and chip evacuation surfaces; and, thereaftermachining the non-ferrous alloy workpieces with the rotating cutting tool having coated guide and chip evacuation surfaces.
  • 18. A method of machining cast non-ferrous alloy workpieces as recited in claim 17 wherein the rotating cutting tool comprises one of a reamer, drill, milling cutter, boring tool, or lathe cutter.
  • 19. A method of machining cast non-ferrous alloy workpieces as recited in claim 17 wherein the rotating cutting tool is a reamer for finishing holes in the workpieces.
  • 20. A method of machining cast non-ferrous alloy workpieces as recited in claim 17 wherein the rotating cutting tool is a reamer comprising at least one set of diametrically-opposed cutting edges comprising polycrystalline diamond and at least one set of diametrically-opposed guide surfaces coated with diamond-like carbon.
Parent Case Info

This application claims the benefit of U.S. Provisional Application No. 60/984,427, titled “Polycrystalline Diamond Cutting Tool With Coated Body”, and filed Nov. 1, 2007.