Patent Application
20190211153
Polyimides (PIs), and in particular polyetherimides (PEIs), are amorphous, transparent, high performance polymers having a high glass transition temperature. Polyetherimides further have high strength, heat resistance, and modulus, and broad chemical resistance, and thus are widely used in applications as diverse as automotive, telecommunication, aerospace, electrical/electronics, transportation, and healthcare. Moreover, PEIs can be recycled, whereas some PIs are thermosets that cannot be recycled.
Accordingly, there remains a continuing need for thermoplastic polyimides and polyetherimides that have high thermal stability and superior mechanical properties.
Provided is a polyimide oligomer of the formula
wherein G is a group having a valence of t, each Q is independently the same or different, and is a substituted or unsubstituted divalent C1-60 hydrocarbon group, —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—, each M is independently the same or different, and is a substituted or unsubstituted divalent C1-60 hydrocarbon group, —O—, —C(O)—, —OC(O)—, —OC(O)O—, —NHC(O), —(O)CNH—, —S—, —S(O)—, or —S(O)2—, D is a phenylene, each V is independently the same or different, and is a tetravalent C4-40 hydrocarbon group, each R is independently the same or different, and is a C1-30 divalent bridging group, a C1-20 alkylene-X, or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Cs, Mg, Ca, Sr, Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Ge, Sn, Pb, As, or Sb, provided that at least one R is C1-20 alkylene-X or C6-30 arylene-X, q is 0 or 1, m is 0 or 1, d is 0 or 1, p is 1 or 2, t is 1 to 6, and each n is independently the same or different, and is 1 to 1,000, provided that the total of all values of n is greater than 4, and wherein the polyimide oligomer is a thermoplastic.
Also provided is a method for the manufacture of the polyimide oligomer, comprising reacting a diamine of the formula H2N—R1—NH2 with a dianhydride of the formula
and optionally a polyamine of the formula
in a solvent and under conditions effective to provide an anhydride-capped oligomer; and reacting the anhydride-capped oligomer with a metalated amino compound of the formula H2N—R2 under conditions effective to provide the polyimide oligomer, wherein R1 is a C1-30 divalent bridging group, R2 is a C1-20 alkylene-X or a C6-30 arylene-X.
Also provided is a method for the manufacture of a polyetherimide oligomer, comprising reacting a diamine of the formula H2N—R1—NH2 with an anhydride of the formula
and optionally a polyamine of the formula
wherein X is a nitro group or halogen, to provide intermediate bis(phthalimide)s of the formulas
and optionally
reacting the bis(phthalimide)s with an alkali metal salt of a dihydroxy aromatic compound of the formula AMO—Z—OAM wherein AM is an alkali metal, to provide an anhydride-capped oligomer; and reacting the anhydride-capped oligomer with a metalated amino compound of the formula H2N—R2 under conditions effective to provide the polyetherimide oligomer, wherein R1 is a C1-20 divalent hydrocarbon group, R2 is a C1-20 alkylene-X or a C6-30 arylene-X.
Further provided are a polymer composition comprising the polyimide oligomer and a second polymer different from the polyimide oligomer, and an article comprising the polyimide oligomer.
The above described and other features are exemplified by the following figures, detailed description, and examples.
The following figures are exemplary.
PIs and PEIs having desirable physical properties often have high molecular weights and glass transition temperatures (Tg) that can necessitate the use of high temperatures to achieve practical flow rates for applications like injection molding. PIs and PEIs having a higher molecular weight can have better physical properties, but as molecular weight increases, so can Tg, and thus melt flow decreases. Thus, there is a continuing need for thermoplastic PIs and PEIs having certain desirable properties, including thermo-oxidative stability, melt stability, and rheology.
Provided herein are PIs and PEIs having terminal groups including metal cation-anion complexes that can be prepared by polymerizing a dianhydride, a diamine, and optionally a poly-functional aryl amine (polyamine), and subsequent endcapping of the intermediate product with a metalated amine. The resulting linear or branched oligomers have terminal end groups that include metal salts of oxides, carboxylates, carbonates, sulfides, sulfonates, phosphates, or the like. The synthesized PIs and PEIs terminated with metal salts exhibit excellent thermo-oxidative stability, melt stability, and rheological properties that can be tuned based on valency and size of the metal cations. The disclosed oligomers surprisingly resulted in a high Tg and good melt flow properties, which can provide a clear advantage over other thermoplastic PIs and PEIs that require lowering molecular weight, with concomitant loss of Tg and physical properties, in order to increase melt flow.
The thermoplastic polyimide oligomers are of formula (1)
wherein G is a group having a valence of t, and q is 0 or 1, m is 0 or 1, d is 0 or 1, p is 1 or 2, t is 1 to 6. Each n is independently the same or different, and is 1 to 1,000, preferably 2 to 500, more preferably 3 to 100, provided that the total of all values of n is greater than 4, or greater than 10, or greater than 20, or greater than 50, or greater than 100, or greater than 250. For example, the total of all values of n can be 4 to 4,000, or 4 to 400, or 4 to 200, or 10 to 1,000, or 10 to 100, or 50 to 1,000, or 50 to 500.
Each Q is independently the same or different, and is a substituted or unsubstituted divalent C1-60 hydrocarbon group, —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—. For example, Q is —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—. In a particular aspect, m is 0, t is 1 or 2, and Q is —C(O)O— or —S(O3)—.
Each M is independently the same or different, and is a substituted or unsubstituted divalent C1-60 hydrocarbon group, —O—, —C(O)—, —OC(O)—, —OC(O)O—, —NHC(O), —(O)CNH—, —S—, —S(O)—, or —S(O)2—. For example, q is 1, Q is a C6-20 arylene, m is 1, and M is —O—.
Each D is phenylene. For example, each D is the same or different phenylene, such as m-phenylene, p-phenylene, bis(4,4′-phenylene)sulfone, bis(3,4′-phenylene)sulfone, or bis(3,3′-phenylene)sulfone.
Each V is independently the same or different, and is a tetravalent C4-40 hydrocarbon group. For example, V can be a C6-20 aromatic hydrocarbon group. Exemplary aromatic hydrocarbon groups include any of those of formulas (2):
wherein W is —O—, —S—, —C(O)—, —SO2—, —SO—, —P(Ra)(═O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (which includes perfluoroalkylene groups), or a group of the formula —O—Z—O— as described in formula (1a) and (1a′) below.
Each R is independently the same or different, and is a C1-30 divalent bridging group, a C1-20 alkylene-X, or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Cs, Mg, Ca, Sr, Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Ge, Sn, Pb, As, or Sb, provided that at least one R is C1-20 alkylene-X or C6-30 arylene-X. For example, the C1-30 divalent bridging group of R is the same or different C6-20 organic bridging group or a halogenated derivative thereof, a straight or branched chain C2-20 alkylene group or a halogenated derivative thereof, or a C3-8 cycloalkylene group or halogenated derivative thereof, or in particular a divalent group of any of formulas (3):
wherein Q1 is —O—, —S—, —C(O)—, —SO2—, —SO—, —P(Ra)(═O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (which includes perfluoroalkylene groups), or —(C6H10)z— wherein z is an integer from 1 to 4. In an embodiment R is m-phenylene, p-phenylene, or a diarylene sulfone.
G is a group of valence t and can be, for example, a cation such as Li, Na, K, Cs, Mg, Ca, Sr, Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Ge, Sn, Pb, As, Sb, Ti, or Zr. G can also be —O—, —C(O)—, —OC(O)—, —(O)CO—, —NHC(O), —(O)CNH—, —S—, —S(O)—, —S(O)2—, —P(Ra)(O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, or a substituted or unsubstituted C1-60 hydrocarbon group having a valence of t. In an aspect, t is 1, G is Li, Na, K, Li, Na, K, Mg, Ca, Sr, or Zn, Q is —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn. In another aspect, t is 2, G is Mg, Ca, Sr, or Zn, Q is —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein M′ is Li, Na, K, Mg, Ca, Sr, or Zn. In still another aspect, t is 2, G is —O—, —C(O)—, —OC(O)—, —(O)CO—, —NHC(O), —(O)CNH—, —S—, —S(O)—, —S(O)2—, or —P(Ra)(O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein M′ is Li, Na, K, Mg, Ca, Sr, or Zn.
When t is greater than 2, G is Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Sn, Pb, As, Sb, Ti, Zr, Ge, Sn, or a substituted or unsubstituted C1-60 hydrocarbon group having a valence of t, G is present in an amount of 0.01 to 20 mol %, preferably 0.5 to 10 mol %, more preferably 1 to 5 mol %, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn. Exemplary substituted or unsubstituted C1-60 hydrocarbon groups include a substituted or unsubstituted C1-20 alkylene, a substituted or unsubstituted C3-8 cycloalkylene, a substituted or unsubstituted C6-20 arylene, or a substituted or unsubstituted C3-12 heteroarylene.
Thus, when t is greater than 2, G is a branching group that is present in an amount of 0.01 to 20 mol %, preferably 0.5 to 10 mol %, more preferably 1 to 5 mol %. In other words, the polyimide oligomer is derived from 0.01 to 20 mol %, or 0.5 to 10 mol %, or 1 to 5 mol % of a branching polyamine of formula (8) based on the total moles of amine precursors, wherein the polyamine is described in further detail herein. In other words, when G is a branching group, the polyimide can include from 0.01 to 20 mole percent (mol %), or 0.5 to 10 mol %, or 1 to 5 mol % of G end groups, based on the total moles of repeating units in the oligomer. More specifically, the polyimide can include from 0.01 to 20 mol % of diimide units containing G end groups, based on the total moles of repeating diimide units in the polyimide oligomer.
The cations described herein can optionally include one or more additional ligands that can be anionic or neutral, including but not limited to halide, hydroxide, carbonate, cyanide, nitrate, ammonia, water, a coordinating solvent (e.g., an ether or carbonyl), a C1-6 alkoxide, a C1-6 carboxylate, a C1-6 alkylamine, or the like.
For example, m is 0, t is 2, Q is —C(O)O— or —S(O3)—, and G is Mg, Ca, Sr, or Zn. In another example, m is 0, t is 2, Q is —C(O)O— or —S(O3)—, G is Mg, Ca, Sr, or Zn, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —C(O)O-M′ or —S(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn. In still another example, m is 0, t is 1, Q is —C(O)O— or —S(O3)—, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —C(O)O-M′ or —S(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn. In a specific example, q is 1, Q is a C6-20 arylene, m is 1, and M is —O—.
The polyimide oligomer can be a polyetherimide of formula (1a)
wherein G, Q, M, D, R, q, m, d, n, p, and t are as defined in formula (1), and wherein the divalent bonds of the —O—Z—O— group are in the 3,3′, 3,4′, 4,3′, or the 4,4′ positions. The group Z in —O—Z—O— of formula (1a) is a divalent organic group, and can be an aromatic C6-24 monocyclic or polycyclic moiety, optionally substituted with 1 to 6 C1-8 alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded. Exemplary groups Z include groups derived from a dihydroxy compound of formula (5)
wherein Ra and Rb can each be the same or different and are a halogen atom or a monovalent C1-8 alkyl group, for example; p′ and q′ are each independently integers of 0 to 4; c is 0 to 4; and Xa is a bridging group connecting the hydroxy-substituted aromatic groups, where the bridging group and the hydroxy substituent of each C6 arylene group are disposed ortho, meta, or para (preferably para) to each other on the C6 arylene group. The bridging group Xa can be a single bond, —O—, —S—, —S(O)—, —S(O)2—, —C(O)—, or a C1-18 organic bridging group. The C1-18 organic bridging group can be cyclic or acyclic, aromatic or non-aromatic, and can further comprise heteroatoms such as oxygen, nitrogen, sulfur, silicon, or phosphorous, and can be optionally substituted with 1 to 8 halogen atoms. The C1-18 organic group can be disposed such that the C6 arylene groups connected thereto are each connected to a common alkylidene carbon or to different carbons of the C1-18 organic bridging group. A specific example of a group Z is a divalent group of formula (5a)
wherein J is —O—, —S—, —C(O)—, —SO2—, —SO—, or —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (including a perfluoroalkylene group). In a specific embodiment Z is a derived from bisphenol A, such that J in formula (5a) is 2,2-isopropylidene.
In formula (1a) each R is the same or different, and is m-phenylene or p-phenylene, bis(4,4′-phenylene)sulfone, bis(3,4′-phenylene)sulfone, bis(3,3′-phenylene)sulfone, a C1-20 alkylene-X, or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn, and at least one R is C1-20 alkylene-X or C6-30 arylene-X. For example, R can be m-phenylene, p-phenylene, a C1-20 alkylene-X, or a C6-30 arylene-X, Z is of formula (5a), and J is 2,2-isopropylidene, and at least one R is phenylene-X wherein —X is —S(O)3-M′ and each M is independently Li, Na, K, Mg, Ca, Sr, or Zn.
The polyimide or polyetherimide can be a copolymer, for example a polyetherimide sulfone copolymer comprising structural units of formulas (1) or (1a) wherein at least 50 mol % of the R groups are of formula (3) wherein Q1 is —SO2—, and the remaining R groups are each independently p-phenylene, m-phenylene, C1-20 alkylene-X, C6-30 arylene-X, or a combination thereof; and Z is 2,2′-(4-phenylene)isopropylidene, provided that at least one R is C1-20 alkylene-X or C6-30 arylene-X. The polyetherimide copolymer can optionally comprise additional structural imide units, for example imide units wherein V of formulas
wherein W is a single bond, —O—, —S—, —C(O)—, —SO2—, —SO—, —P(Ra)(═O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, or —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof (which includes perfluoroalkylene groups). These additional structural imide units can comprise less than 20 mol % of the total number of units, or 0 to 10 mol % of the total number of units, or 0 to 5 mol % of the total number of units, or 0 to 2 mol % of the total number of units. In some embodiments, no additional imide units are present in the polyimides other than polyetherimide units.
The polyimide oligomers (which as indicated above include polyimide oligomer (1) and the polyetherimide oligomer (1a)), can be prepared by methods known in the art, including a polycondensation or ether-forming polymerization.
For example, the polyimide oligomer can be prepared by polycondensation, which includes an imidization of a dianhydride of formula (6) or formula (6a)
or a chemical equivalent thereof, with a diamine of formula (7)
H2N—R1—NH2 (7)
and optionally a branching polyamine of formula (8)
in a solvent and under conditions effective to provide an anhydride-capped oligomer; and reacting the anhydride-capped oligomer with a metalated amino compound of formula (9)
H2N—R2 (9)
under conditions effective to provide the polyimide oligomer, wherein R1 is a C1-30 divalent bridging group, R2 is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is as defined in formulas (1) and (1a). The optional branching polyamine (8) can be present in the reaction in an amount of 0.1 to 20 mol %, or 0.5 to 10 mol %, but preferably 1 to 5 mol %, or 1.5 to 4 mol % to achieve increased branching and increased PDI. Accordingly, when the polyamine (8) is used, G in the resulting polyimide oligomer is derived from the polyamine, and G is therefore present in the polyimide oligomer in an amount of 0.1 to 20 mol %, or 0.5 to 10 mol %, but preferably 1 to 5 mol %, or 1.5 to 4 mol %, based on the total moles of diamine (7) and polyamine (8).
Exemplary dianhydrides of formula (6) include 3,3-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-bis(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride; 2,2-bis[4-(2,3-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl ether dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)benzophenone dianhydride; 4,4′-bis(2,3-dicarboxyphenoxy)diphenyl sulfone dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl-2,2-propane dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl ether dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfide dianhydride; 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)benzophenone dianhydride; and, 4-(2,3-dicarboxyphenoxy)-4′-(3,4-dicarboxyphenoxy)diphenyl sulfone dianhydride, or a combination thereof.
Specific examples of diamines of formula (7) include hexamethylenediamine, polymethylated 1,6-n-hexanediamine, heptamethylenediamine, octamethylenediamine, nonamethylenediamine, decamethylenediamine, 1,12-dodecanediamine, 1,18-octadecanediamine, 3-methylheptamethylenediamine, 4,4-dimethylheptamethylenediamine, 4-methylnonamethylenediamine, 5-methylnonamethylenediamine, 2,5-dimethylhexamethylene-diamine, 2,5-dimethylheptamethylenediamine, 2,2-dimethylpropylenediamine, N-methyl-bis (3-aminopropyl) amine, 3-methoxyhexamethylenediamine, 1,2-bis(3-aminopropoxy) ethane, bis(3-aminopropyl) sulfide, 1,4-cyclohexanediamine, bis-(4-aminocyclohexyl) methane, m-phenylene diamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diaminotoluene, m-xylylenediamine, p-xylylenediamine, 2-methyl-4,6-diethyl-1,3-phenylene-diamine, 5-methyl-4,6-diethyl-1,3-phenylene-diamine, benzidine, 3,3′-dimethylbenzidine, 3,3′-dimethoxybenzidine, 1,5-diaminonaphthalene, bis(4-aminophenyl) methane, bis(2-chloro-4-amino-3,5-diethylphenyl) methane, bis(4-aminophenyl) propane, 2,4-bis(p-amino-t-butyl) toluene, bis(p-amino-t-butylphenyl) ether, bis(p-methyl-o-aminophenyl) benzene, bis(p-methyl-o-aminopentyl) benzene, 1, 3-diamino-4-isopropylbenzene, bis(4-aminophenyl) sulfide, bis-(4-aminophenyl) sulfone (also known as 4,4′-diaminodiphenyl sulfone (DDS)), and bis(4-aminophenyl) ether. Any regioisomer of the foregoing compounds can be used. Combinations of these compounds can also be used. For example, the diamine is m-phenylenediamine, p-phenylenediamine, 4,4′-diaminodiphenyl sulfone, or a combination thereof.
Exemplary polyamines (8) can include those of formulas (8a)-(8t).
In formula (80, Z is a divalent C1-60 hydrocarbon group, or a C6-40 aromatic hydrocarbon group, a C2-20 aliphatic group, or a C4-8 cycloaliphatic group. Other exemplary branching amines are ionic polyamines, for example any of formula (8u) to (8z).
wherein Xp is Mg, Ca, Sr, Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Sn, Pb, As, or Sb, preferably Mg, Ca, Sr, or Zn; and YP is Cr, Bi, Mn, Fe, Co, Ni, B, Al, Ga, In, Sn, Pb, As, or Sb. Xp or Yp optionally include one or more additional ligands, including but not limited to halide, hydroxide, carbonate, cyanide, nitrate, ammonia, water, a coordinating solvent (e.g., an ether or carbonyl), a C1-6 alkoxide, a C1-6 carboxylate, a C1-6 alkylamine, or the like. Thus, Xp and Yp correspond to group G in the branching polyamine of formula (8).
Methods for the synthesis of the polyamines are known in the art. An exemplary method for the synthesis of the polyamine of formula (8) uses a two-step sequence. The first step is a nucleophilic aromatic substitution of a halogenated aromatic nitro compound (e.g., 1-chloro-4-nitrobenzene) with a polyphenol (e.g., 1,1,1-tris(4-hydroxyphenyl) ethane) that is converted to a polyphenoxide in-situ, providing a sufficiently nucleophilic oxygen to displace the activated halide. A polar aprotic solvent (e.g., dimethylacetamide) can promote the substitution reaction to afford a poly(nitrophenyl) compound (e.g., 1,1,1-tris((p-nitrophenoxy)phenyl) ethane). The second step is a reduction of the poly(nitrophenyl) compound to the polyamine of formula (8) using, for example, a palladium catalyst with a reducing agent, an iron-based catalyst, vasicine, zinc, samarium, and hydrazine.
A catalyst can be present during imidization. Exemplary catalysts include sodium aryl phosphinates, guanidinium salts, pyridinium salts, imidazolium salts, tetra(C7-24 arylalkylene) ammonium salts, dialkyl heterocycloaliphatic ammonium salts, bis-alkyl quaternary ammonium salts, (C7-24 arylalkylene)(C1-16 alkyl) phosphonium salts, (C6-24 aryl)(C1-16 alkyl) phosphonium salts, phosphazenium salts, and combinations thereof. The anionic component of the salt is not particularly limited, and can be, for example, chloride, bromide, iodide, sulfate, phosphate, acetate, maculate, tosylate, and the like. A combination of different anions can be used. A catalytically active amount of the catalyst can be determined by one of skill in the art without undue experimentation, and can be, for example, more than 0 to 5 mol % percent, or 0.01 to 2 mol %, or 0.1 to 1.5 mol %, or 0.2 to 1.0 mol % of the moles of amines.
Conditions effective to provide the polyimides and polyetherimides are generally known. Polymerization is generally carried out in a solvent, for example relatively non-polar solvents with a boiling point above 100° C., or above 150° C., for example o-dichlorobenzene, dichlorotoluene, 1,2,4-trichlorobenzene, dimethylacetamide, diphenyl sulfone, or a monoalkoxybenzene such as anisole, veratrole, diphenylether, N-methylpyrrolidone, or phenetole. The polymerization is generally at least 110° C., or 150 to 275° C., or 175 to 225° C. for solution polymerization. Atmospheric or super-atmospheric pressures can be used, for example up to 5 atmospheres, to facilitate the use of high temperatures without causing solvent to be lost by evaporation. Effective times depend on the particular reactants and reaction conditions, and can be 0.5 hours to 3 days, for example, for 0.5 to 72 hours, or 1 to 30 hours or 1 to 20 hours. Advantageously, the reaction is complete 20 hours or less, preferably 10 hours or less, more preferably 3 hours or less.
The metalated amino compound (9) can be added to the reaction mixture after a period of time, for example 1 to 24 hours, or 1 to 20 hours, or 1 to 18 hours, after the polymerization reaction begins. After addition of the metalated amino compound (9), the reaction mixture is subjected to continued heating, for example at 150 to 275° C., or 175 to 225° C., for an additional 1 to 10 hours, or 1 to 5 hours. In an embodiment, after the step of continued heating, the reaction mixture is subsequently heated at 200 to 450° C., or 300 to 400° C., for a period of 10 minutes to 2 hours, or 20 minutes to 90 minutes, or 30 minutes to 60 minutes. The metalated amino compound (9) can be added in any suitable amount, depending on the desired product. In an embodiment, the metalated amino compound (9) is 0 to 95 mol %, or 1 to 90 mol %, or 5 to 80 mol %, or 5 to 50 mol %, or 5 to 20 mol %, or 1 to 10 mol %, based on the total amount of dianhydride (6).
The molar ratio of dianhydride (6) to a combination of the optional polyamine (8) and organic diamine (7) can be 0.9:1 to 1.1:1, or 1:1. While other ratios can be used, a slight excess of dianhydride or diamine may be desirable. A proper stoichiometric balance between the dianhydride and combination of optional polyamine (8) and organic diamine (7) is maintained to allow for the production of the desired molecular weight of the polymer, or prevent the formation of polymer with significant amounts of amine end groups.
An endcapping agent, in addition to the metalated amino compound of formula (9), can be present during imidization, in particular a monofunctional compound that can react with an amine or anhydride. Exemplary compounds include monofunctional aromatic anhydrides such as phthalic anhydride, an aliphatic monoanhydride such as maleic anhydride, or monofunctional aldehydes, ketones, esters isocyanates, aromatic monoamines such as aniline, or C1-C18 linear or cyclic aliphatic monoamines. A monofunctional bisphthalimide can also be added before or during imidization. If an amine-containing endcapping agent is used, the amount can be more than 0 to 10 mol % based on the total amount of dianhydride. If an anhydride-containing endcapping agent is used, the amount can be in the range of more than 0 to 20 mol %, or 1 to 10 mol % based on the amount of the optional polyamine (8) and diamine (7) combined.
The polyimide oligomer can be a polyetherimide oligomer that is synthesized by an ether-forming polymerization, which proceeds via an imidization, i.e., reaction of a diamine of formula (7) with an anhydride of formula (10)
wherein X is a nitro group or halogen, and optionally the polyamine of formula (8), to provide intermediate bis(phthalimide)s of formulas (11a) and optionally (11b)
wherein G, Q, M, q, m, p, and t are as described in formula (1) and X is as described in formula (10). An optional catalyst or monofunctional chain terminating agent as described above can be present during imidization.
The bis(phthalimide)s (11a) and (11b) are reacted with an alkali metal salt of a dihydroxy aromatic compound of formula (12)
AMO—Z—OAM (12)
wherein AM is an alkali metal and Z is a group as defined herein, to provide the anhydride-capped oligomer; and the anhydride-capped oligomer is reacted with the metalated amino compound (9) under conditions effective to provide the polyetherimide oligomer. Polymerization conditions effective to provide the polyetherimides are generally known, and can be conducted in a solvent as described above. This polymerization can also be conducted in the melt, for example at 250 to 350° C., where a solvent is generally not present.
The polyimide oligomer can have a Tg of greater than 160° C., preferably from 160 to 395° C., more preferably from 180 to 280° C., even more preferably from 200 to 250° C. In an example, the PEI-SAA-K and PEI-SAA-Sr oligomers with from 8 to 16 kDa can have a Tg from 206 to 216° C., preferably 208 to 214° C., more preferably 208 to 212° C. In another example, the PEI-SAA-Li, PEI-SAA-Na, PEI-SAA-Mg, and PEI-SAA-Ca oligomers with from 8 to 16 kDa can have a Tg from 210 to 220° C., preferably 212 to 220° C., more preferably 214 to 218° C.
The polyimide oligomers can have one or more of the following properties: a weight average molecular weight (Mw) of 1,000 to 150,000 g/mol, or 10,000 to 80,000 g/mol, or 20,000 to 60,000 g/mol, as determined by size exclusion chromatography (SEC) or proton nuclear magnetic resonance; a viscosity of greater than 25,000 Pascal·seconds at a frequency of 0.1 radians per second; a polydispersity of 1.5 to 3, preferably 1.5 to 2.4, more preferably 1.6 to 2.1, as determined by SEC; a melt index of 0.1 to 10 grams per minute (g/min), as measured by ASTM D1238 at 340 to 370° C., using a 6.7 kilogram (kg) weight; an intrinsic viscosity greater than 0.2 deciliters per gram (dL/g), preferably, 0.35 to 0.7 dL/g, as measured in m-cresol at 25° C.; a thermal decomposition temperature of greater than 450° C., preferably 480 to 600° C., more preferably 500 to 600° C., as determined at a 5% weight loss by thermogravimetric analysis (TGA).
Also provided is a polyimide composition comprising the polyimide oligomer as defined herein. The polyimide composition can have a tensile strength of greater than 70 megapascals (MPa), or 70 to 160 MPa, preferably 80 to 140 MPa, more preferably 90 to 130 MPa, as determined by ASTM D638. The polyimide composition can have an elongation at break of greater than 3%, or 3 to 6%, preferably 4 to 6%, more preferably 4.5 to 6%, as determined by ASTM D638. The polyimide composition can have an elastic modulus of 3 to 5 gigapascals (GPa), preferably 3.1 to 3.8 GPa, more preferably 3.2 to 3.6 GPa, as determined by ASTM D882.
The polyimide oligomer or polyimide composition can have a UL94 rating of V-1 or better, as measured following the procedure of Underwriter's Laboratory Bulletin 94 entitled “Tests for Flammability of Plastic Materials for Parts in Devices and Appliances” (ISBN 0-7629-0082-2), Fifth Edition, Dated Oct. 29, 1996, incorporating revisions through and including Dec. 12, 2003. For example, the polyimide can have a UL94 rating of V-0 or V-1 at a thickness of 0.3, 0.5, 0.75, 0.9, 1, 1.5, 2, or 3 mm.
As described above, during the synthesis of the polyimide, the optional polyamine (8) and organic diamine (7), can be reacted in combination to achieve increased branching and increased PDI. Under these conditions, it is possible that both branched and unbranched polyimides are formed, to provide a polyimide composition comprising branched polyimides and a second polyimide that is not the same as the branched polyimide. This second polyimide is generally an unbranched polyimide that comprises more than 1, for example 5 to 1000, or 5 to 500, or 10 to 100, structural units of formula (14)
wherein V and R are as described in formula (1).
Also provided is a polymer composition comprising the polyimide and a second polymer that is not the same as the polyimide. Such polymer compositions can include 1 to 99 wt % of the polyimide or polyetherimide composition and 1 to 99 wt % of the second polymer, or 10 to 90% of the polyimide or polyetherimide composition and 10 to 90 wt % of the second polymer.
Illustrative examples of second polymers include polyacetal, poly(C1-6 alkyl)acrylate, polyacrylamide, polyacrylonitrile, polyamide, polyamideimide, polyanhydride, polyarylene ether, polyarylene ether ketone, polyarylene ketone, polyarylene sulfide, polyarylene sulfone, polybenzothiazole, polybenzoxazole, polybenzimidazole, polycarbonate, polyester, poly(C1-6 alkyl)methacrylate, polymethacrylamide, cyclic olefin polymer, polyolefin, polyoxadiazole, polyoxymethylene, polyphthalide, polysilazane, polysiloxane, polystyrene, polysulfide, polysulfonamide, polysulfonate, polythioester, polytriazine, polyurea, polyurethane, vinyl polymer, or a combination thereof.
The compositions can include various additives ordinarily incorporated into compositions of these types, with the proviso that any additive is selected so as to not significantly adversely affect the desired properties of the composition. Exemplary additives include antioxidants, thermal stabilizers, light stabilizers, ultraviolet light (UV) absorbing additives, quenchers, plasticizers, lubricants, mold release agents, antistatic agents, visual effect additives such as dyes, pigments, and light effect additives, flame resistances, anti-drip agents, and radiation stabilizers. Other useful additives include carbon nanotubes, exfoliated nanoclays, carbon nanowires, carbon nanospheres, carbon-metal nanospheres, carbon nanorods, carbon-metal nanorods, nanoparticles, or insoluble polymers. Combinations of additives can be used. The foregoing additives can be present individually in an amount from 0.005 to 10 wt %, or combined in an amount from 0.005 to 20 wt %, preferably 0.01 to 10 wt %, based on the total weight of the composition. Particulate fillers and reinforcing fillers can also be present.
Also provided herein is an article that includes the polyimide, polyimide composition, or polymer composition. A wide variety of articles can be manufactured, for example articles of utility in automotive, telecommunication, aerospace, electrical/electronics, battery manufacturing, wire coatings, transportation, food industry, and healthcare applications. Such articles can include films, membranes, fibers, foams, thin sheets, small parts, coatings, fibers, preforms, matrices for polymer composites, or the like. In a particular aspect, the article is an open or closed cell foam, preferably a closed cell foam. Another particular example is a separator for a lithium ion battery. The articles can be extruded or molded, for example by injection molding. The articles can be made by an additive manufacturing method, for example three dimensional printing. Components for electronic devices and components for sterilizable medical articles are especially useful. Thin-wall components manufactured by injection molding are useful, such as a wall having a thickness from 0.1 to 10 mm, or 0.2 to 5 mm, or 0.5 to 2 mm. For example, a film can be manufactured by solution-casting or melt processing the polyimide, the polyimide compositions, the polyetherimide compositions, and the polymer compositions described herein.
The disclosure further illustrated by the following non-limiting examples.
The components in Table 1 were used in the Examples.
Proton nuclear magnetic resonance (1H NMR) spectroscopy characterization was performed on a Varian Unity 400 at 399.98 MHz in CDCl3 or DMSO-d6.
Thermogravimetric analysis (TGA) was used to determine thermal degradation temperatures with a Discovery TGA 5500 (TA Instruments). The samples were heated to 600° C. at a heating rate of 10° C./min in a stream of nitrogen (25 mL/min).
Differential scanning calorimetry (DSC) was used to measure the glass transition temperatures (Tg) with a Discovery DSC 2500 (TA Instruments). The samples were heated at a rate of 10° C./min in a stream of nitrogen (25 mL/min). Tg was determined at the midpoint of the transition in the second heating ramp. The polymers were hot-pressed between two Kapton sheets at 315° C. using two 0.254-mm-thick shims to control the film thickness. A mold releasing agent (provided by REXCO) was applied on the Kapton sheets to prevent the polymers from sticking. The polymer films were stepwise hot-pressed at a force of 1, 5, 7, 10, and 10 tons for one minute and released after each pressing (five pressing-releasing cycles in total).
Size exclusion chromatography-multiple angle light scattering (SEC-MALS) was used to characterize weight average molecular weight (Mw), number average molecular weight (Mn), and polydispersity (PDI) using an EcoSECHLC-8320 instrument (Tosoh Bioscience) equipped with a Wyatt MiniDAWN TREOS MALS detector and a differential refractive index detector (DRI). Samples were dissolved in DMF, the mobile phase was 0.5 molar (M) LiBr in DMF, and the flow rate was 0.5 mL min−1. The column set included a SuperH-H guard column (4.6 mm ID×3.5 cm, 4 μm), a SuperH-H guard column (6.0 mm ID×15 cm, 4 μm), and two SuperH-H guard columns (6.0 mm ID×15 cm, 4 μm). Both the detectors and columns were maintained at 50° C. Polystyrene standards were used as reference.
Melt rheological tests were performed on an AR-G2 rheometer (TA Instruments) with two 25-mm-diameter parallel plates. Dynamic time sweeps (1% oscillatory strain, 1 Hz, 1 h, under air) were used to evaluate changes in storage moduli (G′), the loss moduli (G″), and the complex viscosities of polymer melts at a constant temperature of 340° C. The storage modulus, loss modulus, and viscosity responses over a wide range of frequencies were recorded by stepwise frequency sweep tests in a temperature range of 250-340° C. (10° C./step, 1% oscillatory strain, 1-100 rad/s). The time-temperature superposition (TTS) master curves were generated at a reference temperature (Tr) of 300° C. using TRIOS (TA Instruments).
Scheme 1 illustrates the general procedure and reaction conditions for synthesizing the PEI-DA oligomers from BPADA and mPD with a stoichiometric imbalance.
The first reaction step is the synthesis of a dianhydride-terminated PEI oligomer (PEI-DA). Subsequent reaction with a metalated sulfanilate salt or aniline provides the sulfonate-terminated PEI oligomers (PEI-SAA-M, M=Li, Na, K, Mg, Ca, Sr, or Zn, when X═SO3Li, SO3Na, 503K, SO3Mg1/2, SO3Ca1/2, SO3Sr1/2, or SO3Zn1/2, respectively) and phenyl-terminated PEI oligomer (PEI-Ph, when X═H), respectively.
A typical synthesis procedure for PEI-DA with a target number average molecular weight (Mn) of 8 kDa (8 k-PEI-DA, n=20) is described as follows. A 500-mL three-neck round-bottom flask was equipped with an overhead stirring-rod, a Dean-Stark trap, and a nitrogen inlet. The flask was charged with BPADA (17.389 g, 33.409 mmol), mPD (3.335 g, 30.84 mmol), and oDCB (80 mL) and then purged with nitrogen. Subsequently, the slurry was heated at 180° C. for 12 hours (h) under constant stirring and then at 380° C. for 0.5 h without stirring in a metal bath. The entire reaction was conducted under a stream of nitrogen.
To a 100-mL two-neck round-bottom flask with a stirring bar, SAA-H (3.464 g, 20.00 mmol), Li2CO3 (0.977 g, 12.0 mmol), and deionized (DI) water (100 mL) were combined and heated at reflux for 1 hour. The reaction was conducted under a stream of nitrogen. The product was then filtered using a filtering paper and the filtrate was placed under vacuum to remove the water. A white powder was collected and dried in vacuo at 100° C. 1H NMR (400 MHz, DMSO-d6, δ): 7.29-7.24 ppm (m, 2H, —C6H4SO2—), 6.47-6.42 ppm (m, 2H, —C6H4SO2—), 5.22 ppm (br s, 2H, —NH2).
To a 100-mL two-neck round-bottom flask with a stirring bar, SAA-H (3.464 g, 20.00 mmol), ZnO (0.977 g, 12.00 mmol), and DI water (100 mL) were combined and heated at reflux for 1 hour. The product was then filtered using a filtering paper and the filtrate was placed under vacuum to remove the water. A white powder was collected and dried in vacuo at 100° C. 1H NMR (400 MHz, DMSO-d6, δ): 7.31-7.26 ppm (m, 2H, —C6H4SO2—), 6.48-6.43 ppm (m, 2H, —C6H4SO2—), 5.22 ppm (br s, 2H, —NH2). SAA-Zn: 1H NMR (400 MHz, DMSO-d6, δ): 7.27-7.22 ppm (m, 2H, —C6H4SO2—), 6.46-6.41 ppm (m, 2H, —C6H4SO2—), 5.17 ppm (br s, 2H, —NH2).
Additional metal sulfanilates were prepared according to the procedure of Example 2, except by reacting SAA-H with K2CO3, MgO, CaCO3, or SrCO3 to obtain the corresponding SAA-M (M=K, Mg, Ca, or Sr) products.
Sulfonate-terminated PEIs were prepared by reacting PEI-DA oligomers with SAA-M in NMP (Scheme 1). For example, the synthesis of the 8 k-PEI-SAA-Na oligomer is described as follows. To the flask containing the 8 k-PEI-DA oligomer as described above, SAA-Na (1.003 g, 5.139 mmol) and NMP (60 mL) were added. The mixture was heated at 180° C. for 6 h under constant stirring and then at 300° C. for 0.5 h without stirring in a metal bath. The entire reaction was conducted in a constant N2 stream. The product was dissolved in DMF and precipitated into acetone. The precipitate was filtered, washed sequentially with DI water and acetone, and then dried in vacuo at 180° C. for at least 8 h.
Additional metalosulfonate-terminated PEI oligomers (M=Li, K, Mg, Ca, Sr, and Zn) were prepared by the same procedure using the appropriate SAA-M reactant.
Similar to the PEI-SAA-M oligomers, the PEI-Ph oligomers were prepared by reacting the PEI-DA oligomer with aniline in oDCB (Scheme 1).
Table 2 shows the Mn, Mw, and PDI for PEI oligomers as prepared with a target Mn of 8,000 kDa (8 k), 10,000 kDa (10 k), and 12,0000 kDa (12 k).
Tables 3 and 4 summarize the decomposition (Td,5%) and glass transition (Tg) temperatures for the 8 k-, 10 k-, and 12 k-PEI oligomers.
As shown in Tables 3 and 4, and in
Rheological time sweeps were used to compare the melt stabilities of the 12 k-PEI oligomers with various end groups at 340° C.
The melt rheology of the PEI-SAA-M (M=Li, Na, and K) showed the impact of the alkali metal cations on the flow characteristics of the PEIs.
This disclosure is further illustrated by the following non-limiting aspects.
Aspect 1. A polyimide oligomer of the formula (1), wherein G is a group having a valence of t, each Q is independently the same or different, and is a substituted or unsubstituted divalent C1-60 hydrocarbon group, —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—, each M is independently the same or different, and is a substituted or unsubstituted divalent C1-60 hydrocarbon group, —O—, —C(O)—, —OC(O)—, —OC(O)O—, —NHC(O), —(O)CNH—, —S—, —S(O)—, or —S(O)2—, D is a phenylene, each V is independently the same or different, and is a tetravalent C4-40 hydrocarbon group, each R is independently the same or different, and is a C1-30 divalent bridging group, a C1-20 alkylene-X, or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Cs, Mg, Ca, Sr, Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Ge, Sn, Pb, As, or Sb, provided that at least one R is C1-20 alkylene-X or C6-30 arylene-X, q is 0 or 1, m is 0 or 1, d is 0 or 1, p is 1 or 2, t is 1 to 6, and each n is independently the same or different, and is 1 to 1,000, preferably 2 to 500, or 3 to 100, provided that the total of all values of n is greater than 4, or greater than 10, or greater than 20, or greater than 50, or greater than 100, or greater than 250, and wherein the polyimide oligomer is a thermoplastic.
Aspect 2. The polyimide oligomer of aspect 1, wherein t is 1, G is Li, Na, K, Mg, Ca, Sr, or Zn, Q is —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn; or t is 2, G is Mg, Ca, Sr, or Zn, Q is —O—, —C(O)O—, —OC(O)O—, —S—, —S(O3)—, —OS(O)3—, or —OP(O)3—, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein M′ is Li, Na, K, Mg, Ca, Sr, or Zn; or t is 2, G is —O—, —C(O)—, —OC(O)—, —(O)CO—, —NHC(O), —(O)CNH—, —S—, —S(O)—, —S(O)2—, or —P(Ra)(O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein M′ is Li, Na, K, Mg, Ca, Sr, or Zn; or t is greater than 2, G is Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, B, Al, Ga, In, Sn, Pb, As, Sb, Ti, Zr, Ge, Sn, or a substituted or unsubstituted C1-60 hydrocarbon group having a valence of t, G is present in an amount of 0.01 to 20 mol %, preferably 0.5 to 10 mol %, more preferably 1 to 5 mol %, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn.
Aspect 3. The polyimide oligomer of aspect 1 or 2, wherein the C1-30 divalent bridging group of R is the same or different C6-20 organic bridging group or a halogenated derivative thereof, a straight or branched chain C2-20 alkylene group or a halogenated derivative thereof, or a C3-8 cycloalkylene group or halogenated derivative thereof preferably wherein the C1-30 divalent bridging group of R is each independently a group of formulas (3) wherein Q1 is —O—, —S—, —C(O)—, —SO2—, —SO—, —P(Ra)(═O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof.
Aspect 4. The polyimide oligomer of any one or more of the preceding aspects, wherein m is 0, t is 2, Q is —C(O)O— or —S(O3)—, and G is Mg, Ca, Sr, or Zn.
Aspect 5. The polyimide oligomer of any one or more of the preceding aspects, wherein m is 0, t is 2, Q is —C(O)O— or —S(O3)—, G is Mg, Ca, Sr, or Zn, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —C(O)O-M′ or —S(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn.
Aspect 6. The polyimide oligomer of any one or more of aspects 1 to 3, wherein m is 0, t is 1, Q is —C(O)O— or —S(O3)—, and at least one R is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X is —C(O)O-M′ or —S(O)3-M′, and wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn.
Aspect 7. The polyimide oligomer of any one or more of aspects 1 to 3, wherein G is —O—, a substituted or unsubstituted C1-20 alkylene, a substituted or unsubstituted C3-8 cycloalkylene, a substituted or unsubstituted C6-20 arylene, or a substituted or unsubstituted C3-12 heteroarylene.
Aspect 8. The polyimide oligomer of any one or more of aspects 1 to 3 or 7, wherein q is 1, Q is a C6-20 arylene, m is 1, and M is —O—.
Aspect 9. The polyimide oligomer of any one or more of the preceding aspects, wherein V is a group of formulas (2) wherein W is —O—, —S—, —C(O)—, —SO2—, —SO—, —P(Ra)(═O)— wherein Ra is a C1-8 alkyl or C6-12 aryl, —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof, or a group of the formula —O—Z—O— wherein Z is an aromatic C6-24 monocyclic or polycyclic moiety optionally substituted with 1 to 6 C1-8 alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded.
Aspect 10. The polyimide oligomer of any one or more of the preceding aspects, wherein the polyimide oligomer is a polyetherimide oligomer of formula (1a) wherein each Z is independently an aromatic C6-24 monocyclic or polycyclic moiety optionally substituted with 1 to 6 C1-8 alkyl groups, 1 to 8 halogen atoms, or a combination thereof, provided that the valence of Z is not exceeded.
Aspect 11. The polyimide oligomer of aspect 10, wherein Z is a divalent group of formula (5a) wherein J is —O—, —S—, —SO—, or —CyH2y— wherein y is an integer from 1 to 5 or a halogenated derivative thereof, preferably isopropylidene; and each R is the same or different, and is m-phenylene or p-phenylene, bis(4,4′-phenylene)sulfone, bis(3,4′-phenylene)sulfone, bis(3,3′-phenylene)sulfone, a C1-20 alkylene-X, or a C6-30 arylene-X wherein —X is —O-M′, —C(O)O-M′, —OC(O)O-M′, —S-M′, —S(O)2-M′, —S(O)3-M′, —OS(O)3-M′, or —OP(O)3-M′, wherein each M′ is independently Li, Na, K, Mg, Ca, Sr, or Zn, and at least one R is C1-20 alkylene-X or C6-30 arylene-X.
Aspect 12. The polyimide oligomer of aspect 11, wherein J is isopropylidene, at least one R is m-phenylene, and at least one R is phenylene-X wherein —X is —S(O)3-M′ and each M is independently Li, Na, K, Mg, Ca, Sr, or Zn.
Aspect 13. The polyimide oligomer of any one or more of the preceding aspects, having one or more of: a Tg greater than 160° C., preferably 160 to 395° C., more preferably 180 to 280° C., even more preferably 200 to 250° C.; or a thermal decomposition temperature of greater than 450° C., preferably 480 to 600° C., more preferably 500 to 600° C., as determined at a 5% weight loss by thermogravimetric analysis; or a polydispersity of 1.5 to 3, preferably 1.5 to 2.4, more preferably 1.6 to 2.1, as determined by size exclusion chromatography multi-angle light scattering.
Aspect 14. A method for the manufacture of the polyimide oligomer of any one or more of the preceding aspects, the method comprising reacting a diamine of the formula (7) with a dianhydride of the formula (6) and optionally a polyamine of the formula (8) in a solvent and under conditions effective to provide an anhydride-capped oligomer; and reacting the anhydride-capped oligomer with a metalated amino compound of the formula (9) under conditions effective to provide the polyimide oligomer, wherein R1 is a C1-30 divalent bridging group, R2 is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X, G, Q, M, D, V, q, m, d, p, and t are as defined herein.
Aspect 15. A method for the manufacture of the polyimide oligomer of any one or more of aspects 1 to 13, wherein the polyimide oligomer is a polyetherimide oligomer, the method comprising: reacting a diamine of the formula (7) with an anhydride of the formula (10) and optionally a polyamine of the formula (8) wherein X is a nitro group or halogen, to provide intermediate bis(phthalimide)s of the formulas (11a) and optionally (11b); reacting the bis(phthalimide)s with an alkali metal salt of a dihydroxy aromatic compound of the formula (12) wherein AM is an alkali metal, to provide an anhydride-capped oligomer; and reacting the anhydride-capped oligomer with a metalated amino compound of the formula (9) under conditions effective to provide the polyetherimide oligomer, wherein R1 is a C1-20 divalent hydrocarbon group, R2 is a C1-20 alkylene-X or a C6-30 arylene-X wherein —X, G, Q, M, D, V, q, m, d, p, and t are as defined herein.
Aspect 16. A polymer composition comprising: the polyimide oligomer of any one or more of aspect; and a second polymer different from the polyimide oligomer.
Aspect 17. The polymer composition of aspect 16, wherein the second polymer is a polyacetal, poly(C1-6 alkyl)acrylate, polyacrylamide, polyacrylonitrile, polyamide, polyamideimide, polyanhydride, polyarylene ether, polyarylene ether ketone, polyarylene ketone, polyarylene sulfide, polyarylene sulfone, polybenzothiazole, polybenzoxazole, polybenzimidazole, polycarbonate, polyester, polyetherimide, polyimide, poly(C1-6 alkyl)methacrylate, polymethacrylamide, cyclic olefin polymer, polyolefin, polyoxadiazole, polyoxymethylene, polyphthalide, polysilazane, polysiloxane, polystyrene, polysulfide, polysulfonamide, polysulfonate, polythioester, polytriazine, polyurea, polyurethane, vinyl polymer, or a combination thereof.
Aspect 18. An article comprising the polyimide oligomer of any one or more of the preceding aspects.
Aspect 18a. The article of aspect 18, wherein the article is a film, a foam, a membrane, a conducting part, a fiber, a lens, a varnish, or a composite; more preferably wherein the article is an open cell foam, a closed cell foam, a nano-foam, a battery separator, an ion exchange membrane, tubing, a capillary, a coating, or a scratch resistant part.
Aspect 19. The article of aspect 18, wherein the article is a foam, preferably a closed cell foam.
Aspect 20. A method for manufacturing the article of any one or more of the preceding aspects, preferably wherein the method comprises melt processing; more preferably melt extrusion, injection molding, thermoforming, roto-molding, additive manufacturing, or a combination thereof.
The compositions, methods, and articles can alternatively comprise, consist of, or consist essentially of, any appropriate components or steps herein disclosed. The compositions, methods, and articles can additionally, or alternatively, be formulated so as to be devoid, or substantially free, of any steps, components, materials, ingredients, adjuvants, or species that are otherwise not necessary to the achievement of the function or objectives of the compositions, methods, and articles.
The singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. “Combinations” is inclusive of blends, mixtures, alloys, reaction products, and the like. “Or” means “and/or” unless clearly indicated otherwise by context. Reference throughout the specification to “an embodiment” means that a particular element described in connection with the embodiment is included in at least one embodiment described herein, and may or may not be present in other embodiments. The described elements may be combined in any suitable manner in the various embodiments. “Combination thereof” is an open term that includes one or more of the named elements, optionally together with a like element not named.
The endpoints of all ranges directed to the same component or property are inclusive and independently combinable (e.g., ranges of “less than or equal to 25 wt %, or 5 wt % to 20 wt %,” is inclusive of the endpoints and all intermediate values of the ranges of “5 wt % to 25 wt %,” etc.). Disclosure of a narrower range or more specific group in addition to a broader range is not a disclaimer of the broader range or larger group.
As used herein, the term “alkyl” refers to a straight or branched chain, saturated monovalent hydrocarbon group; “alkylene” refers to a straight or branched chain, saturated, divalent hydrocarbon group; “alkylidene” refers to a straight or branched chain, saturated divalent hydrocarbon group, with both valences on a single common carbon atom; “alkenyl” refers to a straight or branched chain monovalent hydrocarbon group having at least two carbons joined by a carbon-carbon double bond; “cycloalkyl” refers to a non-aromatic monovalent monocyclic or multicyclic hydrocarbon group having at least three carbon atoms, “cycloalkenyl” refers to a non-aromatic cyclic divalent hydrocarbon group having at least three carbon atoms, with at least one degree of unsaturation; “aryl” refers to an aromatic monovalent group containing only carbon in the aromatic ring or rings; “arylene” refers to an aromatic divalent group containing only carbon in the aromatic ring or rings; “alkylarylene” refers to an aryl group that has been substituted with an alkyl group as defined above, with 4-methylphenyl being an exemplary alkylarylene group; “arylalkylene” refers to an alkyl group that has been substituted with an aryl group as defined above, with benzyl being an exemplary arylalkylene group; “acyl” refers to an alkyl group as defined above with the indicated number of carbon atoms attached through a carbonyl carbon bridge (—C(═O)—); “alkoxy” refers to an alkyl group as defined above with the indicated number of carbon atoms attached through an oxygen bridge (—O—); and “aryloxy” refers to an aryl group as defined above with the indicated number of carbon atoms attached through an oxygen bridge (—O—).
Unless otherwise indicated, each of the foregoing groups can be unsubstituted or substituted, provided that the substitution does not significantly adversely affect synthesis, stability, or use of the compound. The term “substituted” as used herein means that at least one hydrogen on the designated atom or group is replaced with another group, provided that the designated atom's normal valence is not exceeded. Exemplary groups that can be present on a “substituted” position include, but are not limited to, cyano; hydroxyl; nitro; azido; alkanoyl (such as a C2-6 alkanoyl group such as acyl); carboxamido; C1-6 or C1-3 alkyl, cycloalkyl, alkenyl, and alkynyl groups; C1-6 or C1-3 alkoxy; C6-10 aryloxy such as phenoxy; C1-6 alkylthio; C1-6 or C1-3 alkylsulfinyl; C1-6 or C1-3 alkylsulfonyl; aminodi(C1-6 or C1-3)alkyl; C6-12 aryl having at least one aromatic ring (e.g., phenyl, biphenyl, naphthyl, or the like, each ring either substituted or unsubstituted aromatic); or C7-19 arylalkylene having 1 to 3 separate or fused rings.
Unless specified to the contrary herein, all test standards are the most recent standard in effect as of the filing date of this application, or, if priority is claimed, the filing date of the earliest priority application in which the test standard appears. Unless defined otherwise, technical and scientific terms used herein have the same meaning as is commonly understood by one of skill in the art to which this invention belongs. All cited patents, patent applications, and other references are incorporated herein by reference in their entirety.
While particular embodiments have been described, alternatives, modifications, variations, improvements, and substantial equivalents that are or may be presently unforeseen may arise to applicants or others skilled in the art. Accordingly, the appended claims as filed and as they may be amended are intended to embrace all such alternatives, modifications variations, improvements, and substantial equivalents.
This application is a continuation-in-part of International Application PCT/US2017/068974, filed on Dec. 29, 2017, which claims priority to U.S. Provisional Application Ser. No. 62/441,226, filed on Dec. 31, 2016, the contents of which are incorporated by reference herein in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| 62441226 | Dec 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/US2017/068974 | Dec 2017 | US |
| Child | 16236717 | US |