Patent Application
20090092759
The present invention relates to polyimide-titania hybrid materials, their preparation, and film prepared from the materials.
Organic-inorganic hybrid materials have been recognized as a new class of advanced materials because of their versatile synthetic approaches and molecular tailing properties.1-10 The present inventors are particularly interested in the hybrid materials for optical applications, such as high refractive index materials, optical waveguides, antireflection films, etc. For such optical applications, the inorganic domains must be well controlled around 20 nm or less to maintain the optical transparence besides their high refractive index characteristics.
Polymer-titania hybrid materials have been extensively studied as high refractive index materials, including poly(silsesquioxanes),7-8 poly(methyl methacrylate) (PMMA),9-15 and polyimide (PI)16-18, etc. For controlling the titania domain and maintaining good miscibility with polymer moiety in the hybrid materials, sol-gel processing is commonly employed strategy to prepare such hybrid materials. In these systems, the major challenge is to generate specific intermolecular interaction with each other in order to get homogeneous hybrid optical films. The present inventors have successfully prepared trialkoxysilane-capped PMMA-titania hybrid optical thin films by an in situ sol-gel process.9-10 The prepared hybrid thin films exhibit tunable high refractive index in the range of 1.505-1.876 and very high optical transparence in the visible region. Wang et al further investigated the crystallinity of titania and nonlinear optical behavior after further hydrothermal treatment.11,13 However, the thermal stability of the PMMA moiety is limited and restricted the applications on optoelectronic devices. Replacing the PMMA moiety in the hybrid materials with a highly thermal stable polymer, such as polyimide, may resolve the problem.
The formation of polyimides containing titania by the incorporation of titanium alkoxide compounds into the precursor polyamic acid (PAA) has been reported.19 For titanium alkoxide compounds (Ti(OR)4), however, they are very reactive due to the presence of highly electronegative OR groups that render titanium very susceptible to nucleophilic attack and result uncontrolled aggregation. Therefore, a nonhomogeneous distribution of the titania clusters with markedly high concentration and large titania particles with sizes>100 nm, are often observed. In addition, when titanium alkoxide compounds are blend with multifunctional acids of PAA, a fast gelation would occur due to the coordination reaction. To overcome these shortcomings, various approaches to prevent the aggregation and phase separation of titania in the evolving polyimides have been investigated. Chemical modification of titanium with chelating ligands, such as acetylacetone (acac), is one of the commonly employed methods to control the condensation pathway of titanium alkoxide compounds. Various coupling agents, such as 3-aminopropyl trimethoxysilane and 3-methacryloxypropyl trimethoxysilane, are the other ways to stabilize the titanium precursors. These agents are desired to generate the covalent bonding force to connect the organic-inorganic moieties using the heterogeneous condensation (Ti—O—Si). Although polyimides-titania hybrid materials with well-controlled morphologies have been successfully fabricated from the above studies, several drawbacks exist. The additional coupling agents and chelating ligands would still remain in these materials after curing to affect important thermal/mechanical/optical properties. Besides, polyimide-titania materials could be also synthesized using the concept of site isolation.19 The alkoxides of titanium are known to react with carboxylic acids, leading to the replacement of one or more alkoxides by carboxylate groups. Thus, it is reasonable to expect that the titanium precursors would bind to the polymeric backbones. The coordination of polyimide carbonyl groups to the titanium particles could prevent the aggregation of titania. However, note that there is an upper limit (14%) for the titanium concentration due to the multifunctional acid groups of PAA and the coordination number of titanium is greater than one. Over the limited value, a tridimensional gel is formed. In acrylic-titanium polymers, the polymer containing a well-know ratio of acidic functions is used to get the organotitanium acrylate polymers.20-22 An excess of titanium alkoxide compounds should be used to obtain the esterified organotitanium acrylate polymers, which are soluble in the organic solvents.
Thus in the present invention, a new synthetic method was developed to prepare synthesize polyimides-nanocrystalline titania hybrid materials with a relatively high titania content.
The present invention relates to polyimide-titania hybrid material film having relatively good surface planarization, excellent thermal properties (400<Td<550° C.), tunable refractive index (1.571<n<1.993), and highly optical transparency in the visible range.
The present also relates to a method for preparing polyimide-titania hybrid materials, which comprises producing a polyimide containing pendent and/or terminal carboxylic acid, coordinating the carboxylic acid with titanium of titanium alkoxide and sol-gel reacting of titanium alkoxide, to enhance the interaction between polyimide and titania and produce the polyimide-titania hybrid materials without macrophase separation.
The present invention thus relates a method for preparing polyimide-titania hybrid materials, which comprises the steps of:
(a) reacting an aromatic dianhydride monomer with an aromatic diamine monomer and optionally carboxylic acid-substituted aromatic diamine monomer in a mole ratio (x/y) of (moles of aromatic dianhydride)(in terms of x)/(total moles of aromatic diamine and carboxylic acid-substituted aromatic diamine)(in terms of y) is more than 1 to subject the dianhydride to a ring-opening reaction to obtain polyamic acid having terminal anhydride groups;
(b) further subjecting the polyamic acid having terminal anhydride groups from step (a) to ring-opening by adding aniline and/or aminobenzoic acid to obtain a polyamic acid having pendent and/or terminal carboxylic acid group, wherein the total amount of the aniline and/or aminobenzoic acid is 2×(x−y) in moles;
(c) subjecting the polyamic acid having pendent and/or terminal carboxylic acid group from step (b) to imidization (cyclization) to obtain a polyimide having pendent and/or terminal carboxylic acid group; and
(d) reacting the polyimide having pendent and/or terminal carboxylic acid group from step (c) with titanium alkoxide to coordinate the carboxylic acid group with titanium atom, then subjecting to hydrolysis and condensation to obtain the polyimide-titania hybrid materials.
According to the method of the present invention, the polyimide having pendent and/or terminal carboxylic acid group from step (c) has an acid number in a range of from 20 mg KOH/g to 200 mg KOH/g.
The polyimide-titania hybrid materials prepared by the present method can be further applied on a substrate to form a film. The resultant film has relatively good surface planarization, excellent thermal properties (400<Td<550° C.), tunable refractive index (1.571<n<1.993), and highly optical transparency in the visible range.
The present invention is illustrated more detail by reference to the accompanying drawings, wherein:
The method for preparing the polyimide-titania hybrid material can be illustrated by reference to the following schemes 1 and 2.
In the above scheme 1, the Rs are the same or different and each represents H or carboxylic acid group (—COOH), Ar, Ar′ and Ar″ are the same or different and each represents a phenylene (-Ph-), a naphthalene, biphenylene, or the group of formula -Ph-X-Ph- (wherein X represents the group of formula —O-Ph-O—, —O—, —CO—, —S—, —SO—, —SO2—, or a C1-4 alkylene group which may be substituted with a halogen(s); m represents a number of from 1 to 30, preferably from 2 to 10; and x/Y>1.
Wherein R's represent a straight or branched C1-6 alkyl group.
In the method for preparing polyimide-titania hybrid materials according to the present invention, the carboxylic acid-substituted aromatic diamine is optional used in the step (a). In the case of not using the carboxylic acid-substituted aromatic diamine in the step (a), to obtain polyimide having carboxylic acid group finally, the step (b) should be carried out in the presence of aminobenzoic acid. In the case of using the carboxylic acid-substituted aromatic diamine in the step (a), the step (b) could be carried out in the presence of either aminobenzoic acid or aniline, or the both. When using the carboxylic acid-substituted aromatic diamine in the step (a), the ratio of the aromatic diamine to the carboxylic acid-substituted aromatic diamine is not limited, as long as the acid number of the polyimide having pendent and/or terminal carboxylic acid group obtained from step (c) falls in the range of from 20 mg KOH/g to 200 mg KOH/g. Similarly, when using both aminobenzoic acid and aniline in the step (b), their ratio is not limited as long as the acid number of the polyimide having pendent and/or terminal carboxylic acid group obtained from step (c) falls in the range of from 20 mg KOH/g to 200 mg KOH/g.
According to the method of the present invention, since polyimide contains free carboxylic acid group at terminal and/or pendent, by coordinating the carboxylic acid group with titanium atom of titanium alkoxide, it can obtain polyimide-titania hybrid material homogenous solution without using coupling agent or chelating agent, it is also easily to produce polyimide-titania hybrid film from the polyimide-titania hybrid material homogenous solution.
The term “polyamic acid” used herein refers to a product containing both functional groups of —NH—CO— and —COOH (carboxylic acid functional group), which are generated from reaction of the diamine and the dianhydride. The term “polyimide” used herein refers to a product obtained from dehydrating and cyclizing the functional group —NH—CO— with the carboxylic acid functional group both contained in the polyamic acid to form polyimide.
Examples of the aromatic dianhydride used in the present method are, for example, but not limited to, 4,4′-(Hexafluoroisopropylidene) diphthalic anhydride (6FDA), pyromellitic dianhydride, 4,4′-oxy-diphthalic anhydride, 3,3′,4,4′-biphenyltetracarboxylic dianhydride, 3,3′,4,4′-benzophenone-tetracarboxylic dianhydride, ethylene-tetra-carboxylic dianhydride, butanetetracarboxylic dianhydride, cyclopentane-tetracarboxylic dianhydride, 2,2′,3,3′-benzophenonetetracarboxylic dianhydride, 2,2′,3,3′-biphenyl-tetracarboxylic dianhydride, 2,2-bis-(3,4-dicarboxyphenyl)propane dianhydride, 2,2-bis(2,3-dicarboxyphenyl)-propane dianhydride, bis(3,4-dicarboxyphenyl)ether dianhydride, bis-(3,4-dicarboxyphenyl)sulfone dianhydride, 1,1-bis(2,3-dicarboxyphenyl)ethane dianhydride, bis(2,3-dicarboxyphenyl)methane dianhydride, bis-(3,4-dicarboxyphenyl)methane dianhydride, 4,4′-(p-phenylenedioxy)-diphthalic dianhydride, 4,4′-(m-phenylenedioxy)-diphthalic dianhydride, 2,3,6,7-naphthalene-tetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 1,2,5,6-naphthalenetetracarboxylic dianhydride, 1,2,3,4-benzene-tetra-carboxylic dianhydride, 3,4,9,10-perylenetetracarboxylic dianhydride, 2,3,6,7-anthracenetetracarboxylic dianhydride, and 1,2,7,8-phenanthrenetetracarboxylic dianhydride. The foregoing dianhydrides can be used alone or in combination of two or more.
Examples of the aromatic diamine used in the present method are, for example, but not limited to, 4,4′-(hexa-fluoroisopropylidene) dianiline (6FpDA), p-phenylene diamine, 4,4-oxydianiline, 1,3-bis(4-aminophenoxy)benzene, 1,3-bis(3-amino-phenoxy)benzene, 2,2-bis[4-(4-aminophenoxy)phenyl]propane, bis[4-(4-aminophenoxy)phenyl]sulfone, 4,4′-bis(4-aminophenoxy)-3,3′-dihydroxybiphenyl, bis[4-(3-aminophenoxy)phenyl]methane, 1,1-bis-[4-(3-aminophenoxy)phenyl]ethane, 1,2-bis[4-(3-aminophenoxy)-phenyl]ethane, 2,2-bis[4-(3-aminophenoxy)phenyl]propane, 2,2′-bis-[4-(3-aminophenoxy)phenyl]butane, 2,2-bis[4-(3-amino-phenoxy)-phenyl]-1,1,1,3,3,3-hexafluoropropane, 4,4′-bis(3-aminophenoxy)-biphenyl, bis[4-(3-aminophenoxy)phenyl]ketone, bis[4-(3-aminophenoxy)phenyl]sulfide, bis[4-(3-aminophenoxy)phenyl]-sulfoxide, bis[4-(3-aminophenoxy)phenyl]sulfone, and bis[4-(3-aminophenoxy)phenyl]ether. The foregoing diamines can be used alone or in combination of two or more.
Example of the carboxy-substituted aromatic diamine used in the present method includes 3,5-diaminobenzoic acid.
In the method of the present invention, the copolymerization in the steps (a) and (b) are carried out under the conventional conditions for preparing polyamic acid and polyimide. The copolymerization is usually carried out in the presence of solvent which has no adverse effect on the reaction, at a temperature of from ambient temperature to 90° C., preferably at a temperature of from 30° C. to 75° C. The solvents can be any kind of aprotic solvent as long as it is inert to the reaction. Examples of the solvent include, but not limit to, N,N-dimethylacetamide (DMAc), 1-methylpyrrolidone (NMP), N,N-dimethylformamide (DMF), tetrahydrofuran (THF), dioxane, methyl ethyl ketone (MEK), chloroform (CHCl3), methylene chloride, and the like. Among them, 1-methylpyrrolidone (NMP) and N,N-dimethylacetamide (DMAc) are preferred. The solvents can be used in one kind or in a mixture of two or more kinds.
In the method of the present invention, the imidization (cyclization) in the step (c) is also carried out in the presence of solvent which has no adverse effect on the reaction, at an elevated temperature, for example, from 120° C. to 220° C., preferably at a temperature of from 150° C. to 220° C. The solvent can use those listed in the above steps (a) and (c). The solvent used in each step can be the same or different, for easily operating, the solvent is preferably the same in each step.
In the method of the present invention, the coordination, hydrolysis, and condensation in the step (d) are carried out under a condition that mole ratio of [Ti]/[COOH] is more than 3, preferably more than 8, in the solvent used in steps (a)˜(c), in the presence of water. However, during the reactions, it is preferable that the titanium alkoxide is first dissolved in alkanol solvent. The alkanol solvent is selected depending on the kind of the titanium alkoxide to be reacted. To avoid the alcohol interchange reaction with the alkoxide during the reaction, the alkanol preferably has the same carbon atom number as alkoxide of the titanium alkoxide to be reacted. For example, if the titanium alkoxide is titanium butoxide, butanol is used as the alkanol solvent.
In the present invention, the polyimide-titania hybrid materials can be applied on a substrate and then cured to form a polyimide-titania hybrid film. Applying the hybrid materials on a substrate can be conducted by any coating method well known in this art, including rolling coating method, flow coating method, dip coating method, spray coating method, spin coating method, curtain coating method, and the like. For obtaining an even film, the spin coating method is preferable.
In the formation of film, curing the coated film is conveniently conducted by a baking method, preferably by a multi-stage baking method at a gradient elevated temperature. By the multi-stage baking method, the solvent contained in the coated film would be evaporated slowly to avoid the crack of film. The multi-stage baking method includes, but not limit to, baking the coated film at a temperature of 50 to 70° C. for 15 to 25 minutes, then baking the film at a temperature of 140 to 160° C. for 15 to 25 minutes, then curing it in an oven at a temperature of 290 to 310° C. under a nitrogen atmosphere for several hours, and finally curing it at a temperature of 390 to 420° C. for several hours.
In the present invention, the concept of site isolation was used to synthesize polyimides-titania hybrid materials and without any additional coupling agents or chelating ligands were used. The basic idea is to synthesize and maintain the titania clusters in the endgroups of the polymeric backbone. Firstly, organo-soluble polyimides with carboxylic acid endgroups are synthesized by step polymerization and solution imidization (cyclolization). The weight average molecular weight and the acid value were controlled at from 3000˜30000 and from 20˜200 mgKOH/g, respectively. Secondly, titanium alkoxide (Ti(OR′)4) monomers are added into the polyimides solution then coordination reaction between carboxylic acid and titanium would occur simultaneously. A threshold value of the molar ratio Ti/COOH must exceed 3 to obtain a homogeneous and meta-stable precursor. Appropriate amount of water and acid catalyst ([H+]=0.1 mole/Kg and [H2O]/[Ti]=2) are added dropwise to proceed the hydrolysis-condensation reaction of Ti(OR′)4. In the present invention, appropriate mix solvents system (n-butyl alcohol (BuOH):N,N′-dimethylacetamide (DMAc)=1:1) is preferably chosen to prevent from precipitation and gelation. Following spin-coating and thermal curing, highly homogeneous hybrid films with different content of titania could be obtained. These films possess relatively good surface planarization, excellent thermal properties (400<Td<550° C.), tunable refractive index (1.571<n<1.993), and highly optical transparency in the visible range. AFM and SEM investigated the effects of the two kind interactions on morphological changes. TEM results demonstrated that the titania nanoclusters were homogeneous dispersed in polyimide matrices.
4,4′-(hexafluoroisopropylidene) diphthalic anhydride (6FDA) and 4,4′-(hexafluoroisopropylidene) dianiline (6FpDA) were obtained from Chriskev company (USA) with a purity level of 99%. 4-aminobenzoic acid (4ABA), aniline, and titanium n-butoxide (Ti(OBu)4) were obtained from ACROS (Belgium) with purity levels of 99, 99.5, and 99%. All monomers were purchased and used without purification. Solvent, 1-methyl-2-pyrrolidinone (NMP), 1,3-dichlorobenzene (DCB), N,N′-dimethyl-acetamide (DMAc), and n-butyl alcohol (BuOH) were obtained from TEDIA. The acid catalyst of titanium n-butoxide, 37.5 wt % HCl, was used as received from Scharlau Chemie.
A solution-imidization technique was employed to synthesize the organo-soluble polyimide (6FDA-6FpDA-4ABA) with carboxylic acid endgroups as show in Scheme 323. The molecular weight and endgroup functionality could be achieved by controlling the reactant stoichiometry.
Firstly, 4,4′-(hexafluoroisopropylidene) dianiline (6FpDA, 3.34 g, 0.01 mol) was added into a 150 ml three-necked round bottom flask and 48 g of NMP was used to dissolve the reactants. 4,4′-(Hexafluoroisopropylidene) diphthalic anhydride (6FDA, 8.88 g, 0.02 mole) was slowly added into the above solution with vigorous stirring and nitrogen purge. The mixture solution was allowed to react for 8 h at room temperature. Secondly, 2.88 g (0.021 mole) of 4-aminobenzoic acid (4ABA) and 12 g of 1,3-dichlorobenzene (DCB) were added into the above solution. The 20 wt % polyamic acid (PAA) solution was formed after constantly stirring the reactants for 16 h at room temperature. Then, the PAA solution was thermally imidization in a 180° C. silicon oil bath for another 12 h and cooled to room temperature. The homogeneous 6FDA-6FpDA-4ABA solution was precipitated with 500 ml of methanol and redissolved in 30 ml of THF for twice times. A white-gray precipitate was recovered and subsequently dried in a vacuum oven at 150° C. for 24 h to yield 4.62 g (28.2 wt %). The acid value of 6FDA-6FpDA-4ABA was 40 mgKOH/g using titration. The concentration of measured polyimide was 0.5 wt % in toluene and 0.1 N KOH in ethanol was used as titrants. The average molecular weight estimated by acid value was 3000. The weight-average molecular weight estimated by GPC was 3667 with the polydispersity index of 1.2028.
The same procedure as above was followed, except that 1.96 g (0.021 mole) of aniline was used in place of 2.88 g (0.021 mole) 4ABA. The yield of 6FDA-6FpDA-Aniline was 24 wt % and acid value was about 0 mgKOH/g using titration. The weight-average molecular weight estimated by GPC was 3443 with the polydispersity index of 1.2584.
The reaction scheme of polyimide-titania hybrid precursors and preparation of the TP-series hybrid thin films were shown in Scheme 4.
TP50 (which means a polyimide-titania hybrid materials containing 50 wt % of titania) as example, firstly, 1.0625 g (3.125×10−3 mole) of Ti(OBu)4 (0.25 g of TiO2) and 2.5 ml butanol were added into 25 ml round bottom flask. Butanol was used to avoid alcohol interchange reaction with titanium n-butoxide. 0.25 g (1.78×10−4 mole [COOH]) of 6FDA-6FpDA-4ABA dissolved in 2.5 ml DMAc were added dropwise into the above solution by syringe. Secondly, 0.0625 g (37 wt %) of HCl aqueous solution, 0.073 g of H2O, and 1.25 ml butanol were mixed very well to get homogeneous solution. The above solution was very slowly added into the PI/TiO2 solution and stirred at room temperature for 30 minutes. To prepare the TP50 hybrid thin film, the precursor solution was filtered by a 0.2 μm PTFE filter prior to use and spin-coated on silicon wafer at 2000 rpm for 20 seconds. Then, the substrates coated with the films were softened-baked at 60° C. on a hot plate for 10 minutes, cured at 150° C. for 30 minutes, and then 300° C. for 1 hour.
FTIR spectra of the materials on the doubly polished silicon wafers were obtained with a Perkin Elmer PARAGON 1000. UV-Vis spectra of the T-series thin films on quartz were obtained using a Perkin Elmer Lambda 20 at room temperature. Gel permeation chromatographic (GPC) analysis was performed on Waters GPC system consisting of, Waters 2414 RI detector, Shodex columns (KF-802,803,805), Waters 717 plus auto-sampler, and Waters 515 HPLC pump. The system was calibrated using polystyrene standards. THF was used as the eluent, at a flow rate of 1.0 mL/min. TGA and DSC thermal analyses were conducted on a Perkin Elmer pyris 1 TGA and a TA Q100 with a refrigerated cooling system, respectively. Both measurements were performed under continuous flow nitrogen, at a heating rate 10° C./min. AFM (Model D15000, Nanoscope) and FESEM (JSM-6700F, JEOL) were used to analysis the surface morphology of the coated films. A prism coupler (Model 2100, Metricon) and ellipsometer (GES-5E, SOPRA) were used to measure the film thickness and refractive index of the prepared thin films at the wavelength of 633 nm: The microstructures of the T-series thin films were examined by using a high-resolution transmission electron microscope (JEM-2100F, JEOL). X-ray diffraction (XRD) was performed at a MicroMax 002 X-ray scattering instrument (PSAXS-USH-WAXS-002, Osmic) using CuKα radiation (1.5406 Å) with comparable intensity to a focused beam from a rotating anode generator at room temperature.
When the polyimide bearing acid endgroups was added into the Ti(OBu)4 solution, the chelating phenomenon between carboxylic acid and butoxy groups would occur simultaneously due to the reactive acid groups for coordinating with titanium atoms. So the behavior of the hybrids according to the molar ratio of [Ti]/[COOH] was interesting and necessary to be examined. If a stoichiometric molar ratio of [Ti]/[COOH]=1 was chosen, the gelation would be formed simultaneously after the polyimide was added. A definite molar ratio of [Ti]/[COOH], the threshold value>3, would allow one to obtain not a gel but a transparent solution. The value of this threshold was valid for many parameters, such as the alkyl chain of Ti(OR′)4, the acid value and molecular weight of polyimide, the solid content, and temperature . . . etc. The new increase of the molar ratio of [Ti]/[COOH] could give rise to a more stable solution. These results revealed that the bridging bidentate mode of titanium, the main coordination mode for tridimensional gel, could be inhibited with increasing the loading ratio of Ti(OBu)4.
In the present invention, the larger value ([Ti]/[COOH]>8) than the threshold was chosen to obtain the stable solution and further sol-gel process was executed to form the homogeneous hybrid thin films. During the sol-gel process, the meta-stable solution could be well controlled by appropriate experimental conditions, [H+]=0.1 mole/Kg and [H2O]/[Ti]=2. Although the undesired gelation would still occur with the storage time increased, the time before gelation was enough to spin-on the thin films. The molar ratio of [H2O]/[Ti] could be also decreased to get the more stable and the longer gel time. But the degree of hydrolysis-condensation of Ti(OBu)4 is too less to convert completely to titania. If 6FDA-6FpDA-Aniline (without acid endgroups) were in place of 6FDA-6FpDA-4ABA, the mixtures would have no crosslinking points and be very stable no matter what any molar ratio of [Ti]/[COOH]. However, the formed films would occur serious phase separation due to the absence of the interaction force between titania and polyimide. The phenomenon would be examined by morphologic analyses and discussed later. To conclude, these results showed that the polyimides have been already coordinated with titanium through carboxylic acid groups and play a major role for gelation.
ah = film thickness,
bRq is the root mean square roughness,
cn = refractive index.
a) shows the height and phase AFM images of TP50 thin film. The surface roughness of the hybrid films analyzed by AFM is listed in Table 1. For TP50 thin film, the appearances of topographic and phase image show high homogeneously dispersion of titania. As shown in Table 1, the surface roughness of the hybrid films is 5.122 nm, 1.607 nm, 0.364 nm, 0.214 nm, and 0.309 nm for TP30, TP50, TP70, TP90, and TP100, respectively. It suggests the homogeneous hybrid films are obtained. Here, two compared methods were examined to address the morphologic changes resulted from the interaction force of polyimide and titanium. In the first method, except that no acid catalyst and water were added, the same procedure as TP50 was followed (sample TW50). In the second method, the same preparation as TP50 was followed, except that 6FDA-6FpDA-Aniline was used in place of 6FDA-6FpDA-4ABA (sample TA50). Further characterizations of these specimens were achieved by AFM measurements (
The cross-sectional HRTEM images of TP50 and TP70 thin films are shown in
According to the present invention, high refractive index polyimide titania hybrid optical thin films were successfully prepared from the soluble polyimde with carboxylic acid end group with titanium butoxide by controlling the organic/inorganic mole ratio, water/acid content, and mixed solvent system. The nanocrystalline titania domain in the polyimide matrice could be as high as 90 wt % and thus the refractive index of 1.943 was achieved. The hybrid films also possessed excellent thermal properties and highly optical transparency in the visible region. Therefore, the prepared polyimide-titania hybrid thin films could have the potential applications for optoelectronic devices.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims.