Patent Application
20220128904
This non-provisional application claims priority under 35 U.S.C. § 119(a) on Patent Application No. 2020-179277 filed in Japan on Oct. 27, 2020, the entire contents of which are hereby incorporated by reference.
This invention relates to a positive resist composition and a pattern forming process.
To comply with the arrival of 5G communications and the enlargement of their application to artificial intelligence, LSIs are designed toward higher integration density, higher operating speed, and lower power consumption. To meet such demand, the effort to reduce the pattern rule is in rapid progress. As the advanced miniaturization technology, manufacturing of microelectronic devices at the 10 and 7-nm nodes by the immersion ArF lithography has been implemented in a mass scale. Also, the mass manufacture of 5-nm node devices by extreme ultraviolet (EUV) lithography of wavelength 13.5 nm started. The marketing of smartphones having such devices mounted thereon was announced.
The exposure system for mask manufacturing made a transition from the laser beam exposure system to the EB exposure system to increase the accuracy of line width. Since a further size reduction becomes possible by increasing the accelerating voltage of the electron gun in the EB exposure system, the accelerating voltage increased from 10 kV to 30 kV and reached 50 kV in the current mainstream system, with a voltage of 100 kV being under investigation.
As the accelerating voltage increases, a lowering of sensitivity of resist film becomes of concern. As the accelerating voltage increases, the influence of forward scattering in a resist film becomes so reduced that the contrast of electron image writing energy is improved to ameliorate resolution and dimensional control whereas electrons can pass straightforward through the resist film so that the resist film becomes less sensitive. Since the exposure tool used in the EB lithography is designed for exposure by direct continuous writing, a lowering of sensitivity of resist film leads to an undesirably reduced throughput. To meet the need for higher sensitivity, chemically amplified resist compositions are contemplated.
As the feature size reduces, image blurs due to acid diffusion become a problem. To insure resolution for fine patterns with a size of 45 nm et seq., not only an improvement in dissolution contrast is important as previously reported, but control of acid diffusion is also important as reported in Non-Patent Document 1. Since chemically amplified resist compositions are designed such that sensitivity and contrast are enhanced by acid diffusion, an attempt to minimize acid diffusion by reducing the temperature and/or time of post-exposure bake (PEB) fails, resulting in drastic reductions of sensitivity and contrast.
A triangular tradeoff relationship among sensitivity, resolution, and edge roughness (LER, LWR) has been pointed out. Specifically, a resolution improvement requires to suppress acid diffusion whereas a short acid diffusion distance leads to a loss of sensitivity.
With the aim for high sensitivity, an attempt has been made to introduce halogen into a base polymer. When iodine which is highly absorptive to EUV is introduced into a polymer, a fairly high sensitivity is expectable. The attempt, however, increases the risk of generating development defects because heavy atoms like iodine have a very low alkaline solubility.
Since resist film swells in alkaline developer, there can occur pattern collapse, an increase of edge roughness, and a degradation of CDU. A resist material comprising polymethacrylate substituted with an acid labile group exhibits a high dissolution contrast, but undergoes a significant swell. On the other hand, a resist material comprising polyhydroxystyrene substituted with an acid labile group undergoes a slight swell, but exhibits a low dissolution contrast and hence, a low resolution. As compared with the resist material based on acid labile group-substituted polyhydroxystyrene, a resist material comprising polymethacrylate having an acid labile group-substituted phenol pendant has a high alkaline dissolution rate in the exposed region and undergoes slight swell, which lead to improved LWR and CDU. See Patent Document 1. There still exists the demand for further improvements in LWR and CDU.
An object of the present invention is to provide a positive resist composition which exhibits a higher sensitivity and resolution than the prior art positive resist compositions, reduced edge roughness and size variation, and forms a pattern of good profile after exposure, and a patterning process using the resist composition.
Making extensive investigations in search for a positive resist material capable of meeting the current requirements including high resolution, low edge roughness, and reduced size variation, the inventors have found that the acid diffusion distance must be minimized before the object can be attained, that this gives rise to problems including a lowering of sensitivity, a lowering of dissolution contrast, and a lowering of resolution of two-dimensional patterns such as hole patterns resulting from enlargement of the swollen region, that when a polymer having a fluorinated phenol whose hydroxy group is substituted with an acid labile group, as a pendant, is used as the base polymer, the acid diffusion distance can be minimized while enhancing the dissolution contrast. Better results are obtained particularly when the relevant polymer is used as the base in a chemically amplified positive resist material. A positive resist material comprising the relevant polymer has a high sensitivity, a significantly increased contrast of alkaline dissolution rate before and after exposure, a high acid diffusion suppressing effect, and a high resolution, and forms a pattern of good profile with improved edge roughness and size variation after exposure. The resist material is thus best suited as a micropatterning material for the fabrication of VLSIs and photomasks.
In one aspect, the invention provides a positive resist composition comprising a base polymer comprising repeat units having the formula (a).
Herein RA is hydrogen or methyl, X1 is each independently a single bond, phenylene group, naphthylene group, or a C1-C16 divalent linking group containing an ester bond, ether bond or lactone ring, R1 is an acid labile group, R2 is a C1-C4 alkyl group, m is an integer of 1 to 4, n is an integer of 0 to 3, and 1<m+n<4.
In a preferred embodiment, the acid labile group has the formula (a1).
Herein R3 is a C1-C6 aliphatic hydrocarbyl group which may contain a heteroatom or a phenyl group, k is an integer of 0 to 4, and the broken line designates a valence bond.
In a preferred embodiment, the base polymer further comprises repeat units (b1) having a carboxy group whose hydrogen is substituted by an acid labile group, and/or repeat units (b2) having a phenolic hydroxy group whose hydrogen is substituted by an acid labile group, exclusive of the repeat units having formula (a).
Typically, the repeat unit (b1) is represented by the formula (b1), and the repeat unit (b2) is represented by the formula (b2).
Herein RA is each independently hydrogen or methyl. Y1 is a single bond, phenylene group, naphthylene group, or a C1-C16 divalent linking group containing at least one moiety selected from an ether bond, ester bond and lactone ring. Y2 is a single bond, ester bond or amide bond. Y3 is a single bond, ether bond or ester bond. R11 and R12 are each independently an acid labile group. R13 is fluorine, trifluoromethyl, cyano or a C1-C6 saturated hydrocarbyl group. R14 is a single bond or a C1-C6 alkanediyl group in which some carbon may be replaced by an ether bond or ester bond. The subscript “a” is 1 or 2, “b” is an integer of 0 to 4, and 1≤a+b≤5.
The base polymer may further comprise repeat units having an adhesive group which is selected from among hydroxy group, carboxy group, lactone ring, carbonate group, thiocarbonate group, carbonyl group, cyclic acetal group, ether bond, ester bond, sulfonate bond, cyano group, amide bond, —O—C(═O)—S—, and —O—C(═O)—NH—.
In a preferred embodiment, the base polymer further comprises repeat units having the formula (d1), (d2) or (d3).
Herein RA is each independently hydrogen or methyl. Z1 is a single bond, C1-C6 aliphatic hydrocarbyl group, phenylene group, naphthylene group, or a C7-C18 group obtained by combining the foregoing, or —O—Z11—, —C(═O)—O—Z11—, or —C(═O)—NH—Z11—, wherein Z11 is an aliphatic hydrocarbylene group, phenylene group, naphthylene group, or a C7-C18 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond or hydroxy moiety. Z2 is a single bond or ester bond. Z3 is a single bond, —Z31—C(═O)—O—, —Z31—O—, or —Z31—O—C(═O)—, wherein Z31 is a C1-C12 aliphatic hydrocarbylene group, phenylene group or a C7-C18 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond, bromine or iodine. Z4 is a methylene group, 2,2,2-trifluoro-1,1-ethanediyl group or carbonyl group. Z5 is a single bond, methylene, ethylene, phenylene, fluorinated phenylene, trifluoromethyl-substituted phenylene, —O—Z51—, —C(═O)—O—Z51—, or —C(═O)—NH—Z51—, wherein Z51 is a C1-C6 aliphatic hydrocarbylene group, phenylene group, fluorinated phenylene group, or trifluoromethyl-substituted phenylene group, which may contain a carbonyl moiety, ester bond, ether bond, hydroxy moiety, or halogen. R21 to R28 are each independently halogen, or a C1-C20 hydrocarbyl group which may contain a heteroatom, a pair of R23 and R24, or R26 and R27 may bond together to form a ring with the sulfur atom to which they are attached. M− is a non-nucleophilic counter ion.
The resist composition may further comprise an acid generator, organic solvent, quencher, and/or surfactant.
In another aspect, the invention provides a pattern forming process comprising the steps of applying the positive resist composition defined above to form a resist film on a substrate, exposing the resist film to high-energy radiation, and developing the exposed resist film in a developer.
Typically, the high-energy radiation is i-line, KrF excimer laser, ArF excimer laser, EB, or EUV of wavelength 3 to 15 nm.
Since the decomposition efficiency of an acid generator is enhanced, the positive resist composition has a satisfactory effect of suppressing acid diffusion, exhibits a high sensitivity and high resolution, and forms a pattern of satisfactory profile, edge roughness and size variation after exposure. Because of these advantages, the positive resist composition is useful in commercial application and best suited as a micropatterning material for the microfabrication of VLSIs and photomasks by lithography processes using excimer laser, EB or EUV. The positive resist composition may be used not only in the lithography for forming semiconductor circuits, but also in the formation of mask circuit patterns, micromachines, and thin-film magnetic head circuits.
The singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. “Optional” or “optionally” means that the subsequently described event or circumstances may or may not occur, and that description includes instances where the event or circumstance occurs and instances where it does not. The notation (Cn-Cm) means a group containing from n to m carbon atoms per group. The terms “group” and “moiety” are interchangeable. In chemical formulae, the broken line denotes a valence bond; Me stands for methyl, Ac for acetyl, and Ph for phenyl.
The abbreviations have the following meaning.
EB: electron beam
EUV: extreme ultraviolet
GPC: gel permeation chromatography
Mw: weight average molecular weight
Mw/Mn: molecular weight dispersity
PAG: photoacid generator
PEB: post-exposure bake
LWR: line width roughness
CDU: critical dimension uniformity
The invention provides a positive resist composition comprising a base polymer comprising repeat units having a pendant in the form of a fluorinated phenol group whose hydroxy group is substituted with an acid labile group. The fluorinated phenol group whose hydroxy group is substituted with an acid labile group ensures to form a resist film having a high alkaline dissolution contrast after acid-aided deprotection and minimal swell and thus enables to form a resist pattern with minimal edge roughness and size variation.
Typically the repeat units have the formula (a). It is noted that the repeat units having formula (a) are sometimes simply referred to as repeat units (a).
In formula (a), RA is hydrogen or methyl. X1 is each independently a single bond, phenylene group, naphthylene group, or a C1-C16 divalent linking group containing an ester bond, ether bond or lactone ring. R1 is an acid labile group. R2 is a C1-C4 alkyl group. The subscript m is an integer of 1 to 4, n is an integer of 0 to 3, and 1≤m+n≤4.
The divalent linking group represented by X1 is not particularly limited as long as it contains an ester bond, ether bond or lactone ring. Of divalent groups obtained by combining at least one C1-C16 hydrocarbylene group with at least one moiety selected from an ester bond, ether bond and lactone ring, those groups of 1 to 16 carbon atoms are preferred. The C1-C16 hydrocarbylene group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C1-C16 alkanediyl groups such as methanediyl, ethane-1,1-diyl, ethane-1,2-diyl, propane-1,3-diyl, butane-1,4-diyl, pentane-1,5-diyl, hexane-1,6-diyl, heptane-1,7-diyl, octane-1,8-diyl, nonane-1,9-diyl, decane-1,10-diyl, undecane-1,11-diyl, dodecane-1,12-diyl, tridecane-1,13-diyl, tetradecane-1,14-diyl, pentadecane-1,15-diyl, and hexadecane-1,16-diyl; C3-C16 cyclic saturated hydrocarbylene groups such as cyclopentanediyl, cyclohexanediyl, norbornanediyl, and adamantanediyl; C6-C16 arylene groups such as phenylene, methylphenylene, ethylphenylene, n-butylphenylene, isopropylphenylene, n-butylphenylene, isobutylphenylene, sec-butylphenylene, tert-butylphenylene, naphthylene, methylnaphthylene, ethylnaphthylene, n-propylnaphthylene, isopropylnaphthylene, n-butylnaphthylene, isobutylnaphthylene, sec-butylnaphthylene, and tert-butylnaphthylene; and combinations thereof.
Examples of the monomer from which repeat units (a) are derived are shown below, but not limited thereto. Herein RA is as defined above and R1 will be described later.
In formula (a), R1 is an acid labile group. Although the acid labile group may be selected from a variety of such groups, it is preferably a group having any one of the formulae (AL-1) to (AL-3) shown later, more preferably a cyclic tertiary hydrocarbyl group having the following formula (a1).
In formula (a1), R3 is a C1-C6 aliphatic hydrocarbyl group which may contain a heteroatom or a phenyl group, and k is an integer of 0 to 4.
The C1-C6 aliphatic hydrocarbyl group R3 may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C1-C6 alkyl groups such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, neopentyl, and n-hexyl; cyclic saturated hydrocarbyl groups such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl; alkenyl groups such as vinyl, 1-propenyl, 2-propenyl, butenyl and hexenyl; cyclic saturated aliphatic hydrocarbyl groups such as cyclohexenyl; and alkynyl groups such as ethynyl and butynyl. R3 is preferably methyl, ethyl, isopropyl, tert-butyl, cyclopentyl, cyclohexyl, vinyl or ethynyl.
Examples of the cyclic tertiary hydrocarbyl group having formula (a1) are shown below, but not limited thereto.
In formula (a), R2 is a C1-C4 alkyl group. Exemplary of the alkyl group are methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, and tert-butyl.
In formula (a), m is an integer of 1 to 4, n is an integer of 0 to 3, and the sum m+n is from 1 to 4.
In one preferred embodiment, repeat units (b1) having a carboxy group whose hydrogen is substituted by an acid labile group, and/or repeat units (b2) having a phenolic hydroxy group whose hydrogen is substituted by an acid labile group, exclusive of the repeat units having formula (a), are incorporated in the base polymer for further enhancing dissolution contrast.
Typically, the repeat unit (b1) is represented by the formula (b1), and the repeat unit (b2) is represented by the formula (b2).
In formulae (b1) and (b2), RA is each independently hydrogen or methyl. Y1 is a single bond, phenylene group, naphthylene group, or a C1-C12 divalent linking group containing at least one moiety selected from an ether bond, ester bond and lactone ring. Y2 is a single bond, ester bond or amide bond. Y3 is a single bond, ether bond or ester bond. R11 and R12 are each independently an acid labile group. R13 is fluorine, trifluoromethyl, cyano or a C1-C6 saturated hydrocarbyl group. R14 is a single bond or a C1-C6 alkanediyl group in which some carbon may be replaced by an ether bond or ester bond. The subscript “a” is 1 or 2, b is an integer of 0 to 4, and the sum a+b is from 1 to 5.
Examples of the monomer from which repeat units (b1) are derived are shown below, but not limited thereto. Herein RA and R11 are as defined above.
Examples of the monomer from which repeat units (b2) are derived are shown below, but not limited thereto. Herein RA and R12 are as defined above.
The acid labile groups represented by R1, R11 and R12 may be selected from a variety of such groups, for example, those groups having the following formulae (AL-1) to (AL-3).
In formulae (AL-1), c is an integer of 0 to 6. RL1 is a C4-C20, preferably C4-C15 tertiary hydrocarbyl group, a trihydrocarbylsilyl group in which each hydrocarbyl moiety is a C1-C6 saturated hydrocarbyl moiety, a C4-C20 saturated hydrocarbyl group containing a carbonyl moiety, ether bond or ester bond, or a group having formula (AL-3). As used herein, the “tertiary hydrocarbyl group” refers to a group obtained from a hydrocarbon by removing hydrogen from tertiary carbon therein.
The tertiary hydrocarbyl group RL1 may be saturated or unsaturated and branched or cyclic. Examples thereof include tert-butyl, tert-pentyl, 1,1-diethylpropyl, 1-ethylcyclopentyl, 1-butylcyclopentyl, 1-ethylcyclohexyl, 1-butylcyclohexyl, 1-ethyl-2-cyclopentenyl, 1-ethyl-2-cyclohexenyl, and 2-methyl-2-adamantyl. Suitable trihydrocarbylsilyl groups include trimethylsilyl, triethylsilyl, and dimethyl-tert-butylsilyl.
The saturated hydrocarbyl group containing a carbonyl moiety, ether bond or ester bond may be straight, branched or cyclic, preferably cyclic, and examples thereof include 3-oxocyclohexyl, 4-methyl-2-oxooxan-4-yl, 5-methyl-2-oxooxolan-5-yl, 2-tetrahydropyranyl, and 2-tetrahydrofuranyl.
Examples of the acid labile group having formula (AL-1) include tert-butoxycarbonyl, tert-butoxycarbonylmethyl, tert-pentyloxycarbonyl, tert-pentyloxycarbonylmethyl, 1,1-diethylpropyloxycarbonyl, 1,1-diethylpropyloxycarbonylmethyl, 1-ethylcyclopentyloxycarbonyl, 1-ethylcyclopentyloxycarbonylmethyl, 1-ethyl-2-cyclopentenyloxycarbonyl, 1-ethyl-2-cyclopentenyloxycarbonylmethyl, 1-ethoxyethoxycarbonylmethyl, 2-tetrahydropyranyloxycarbonylmethyl, and 2-tetrahydrofuranyloxycarbonylmethyl.
Other examples of the acid labile group having formula (AL-1) include groups having the formulae (AL-1)-1 to (AL-1)-10.
In formulae (AL-1)-1 to (AL-1)-10, c is as defined above. RL8 is each independently a C1-C10 saturated hydrocarbyl group or C6-C20 aryl group. RL9 is hydrogen or a C1-C10 saturated hydrocarbyl group. RL10 is a C2-C10 saturated hydrocarbyl group or C6-C20 aryl group. The saturated hydrocarbyl group may be straight, branched or cyclic.
In formula (AL-2), RL2 and RL3 are each independently hydrogen or a C1-C18, preferably C1-C10 saturated hydrocarbyl group. The saturated hydrocarbyl group may be straight, branched or cyclic and examples thereof include methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, cyclopentyl, cyclohexyl, 2-ethylhexyl and n-octyl.
In formula (AL-2), RL4 is a C1-C18, preferably C1-C10 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic and typical examples thereof include C1-C18 saturated hydrocarbyl groups, in which some hydrogen may be substituted by hydroxy, alkoxy, oxo, amino or alkylamino. Examples of the substituted saturated hydrocarbyl group are shown below.
A pair of RL2 and RL3, RL2 and RL4, or RL3 and RL4 may bond together to form a ring with the carbon atom or carbon and oxygen atoms to which they are attached. RL2 and RL3, RL2 and RL4, and RL3 and RL4 taken together to form a ring are each independently a C1-C18, preferably C1-C10 alkanediyl group. The ring thus formed is preferably of 3 to 10, more preferably 4 to 10 carbon atoms.
Of the acid labile groups having formula (AL-2), suitable straight or branched groups include those having formulae (AL-2)-1 to (AL-2)-69, but are not limited thereto.
Of the acid labile groups having formula (AL-2), suitable cyclic groups include tetrahydrofuran-2-yl, 2-methyltetrahydrofuran-2-yl, tetrahydropyran-2-yl, and 2-methyltetrahydropyran-2-yl.
Also included are acid labile groups having the following formulae (AL-2a) and (AL-2b). The base polymer may be crosslinked within the molecule or between molecules with these acid labile groups.
In formulae (AL-2a) and (AL-2b), RL11 and RL12 are each independently hydrogen or a C1-C8 saturated hydrocarbyl group which may be straight, branched or cyclic. Also, RL11 and RL12 may bond together to form a ring with the carbon atom to which they are attached, and in this case, RL11 and RL12 are each independently a C1-C8 alkanediyl group. RL13 is each independently a C1-C10 saturated hydrocarbylene group which may be straight, branched or cyclic. The subscripts d and e are each independently an integer of 0 to 10, preferably 0 to 5, and f is an integer of 1 to 7, preferably 1 to 3.
In formulae (AL-2a) and (AL-2b), LA is a (f+1)-valent C1-C50 aliphatic saturated hydrocarbon group, (f+1)-valent C3-C50 alicyclic saturated hydrocarbon group, (f+1)-valent C6-C50 aromatic hydrocarbon group or (f+1)-valent C3-C50 heterocyclic group. In these groups, some carbon may be replaced by a heteroatom-containing moiety, or some carbon-bonded hydrogen may be substituted by a hydroxy, carboxy, acyl moiety or fluorine. LA is preferably a C1-C20 saturated hydrocarbon group such as saturated hydrocarbylene, trivalent saturated hydrocarbon or tetravalent saturated hydrocarbon group, or C6-C30 arylene group. The saturated hydrocarbon group may be straight, branched or cyclic. LB is —C(═O)—O—, —NH—C(═O)—O— or —NH—C(═O)—NH—.
Examples of the crosslinking acetal groups having formulae (AL-2a) and (AL-2b) include groups having the formulae (AL-2)-70 to (AL-2)-77.
In formula (AL-3), RL5, RL6 and RL7 are each independently a C1-C20 hydrocarbyl group which may contain a heteroatom such as oxygen, sulfur, nitrogen or fluorine. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C1-C20 alkyl groups, C3-C20 cyclic saturated hydrocarbyl groups, C2-C20 alkenyl groups, C3-C20 cyclic unsaturated hydrocarbyl groups, and C6-C10 aryl groups. A pair of RL5 and RL6, RL5 and RL7, or RL6 and RL7 may bond together to form a C3-C20 aliphatic ring with the carbon atom to which they are attached.
Examples of the group having formula (AL-3) include tert-butyl, 1,1-diethylpropyl, 1-ethylnorbornyl, 1-methylcyclopentyl, 1-ethylcyclopentyl, 1-isopropylcyclopentyl, 1-methylcyclohexyl, 2-(2-methyl)adamantyl, 2-(2-ethyl)adamantyl, and tert-pentyl.
Examples of the group having formula (AL-3) also include groups having the formulae (AL-3)-1 to (AL-3)-19.
In formulae (AL-3)-1 to (AL-3)-19, RL14 is each independently a C1-C8 saturated hydrocarbyl group or C6-C20 aryl group. RL15 and RL17 are each independently hydrogen or a C1-C20 saturated hydrocarbyl group. RL16 is a C6-C20 aryl group. The saturated hydrocarbyl group may be straight, branched or cyclic. Typical of the aryl group is phenyl. RF is fluorine or trifluoromethyl, and g is an integer of 1 to 5.
Other examples of the group having formula (AL-3) include groups having the formulae (AL-3)-20 and (AL-3)-21. The base polymer may be crosslinked within the molecule or between molecules with these acid labile groups.
In formulae (AL-3)-20 and (AL-3)-21, RL14 is as defined above. RL18 is a C1-C20 (h+1)-valent saturated hydrocarbylene group or C6-C20 (h+1)-valent arylene group, which may contain a heteroatom such as oxygen, sulfur or nitrogen. The saturated hydrocarbylene group may be straight, branched or cyclic. The subscript h is an integer of 1 to 3.
Examples of the monomer from which repeat units containing an acid labile group of formula (AL-3) are derived include (meth)acrylates having an exo-form structure represented by the formula (AL-3)-22.
In formula (AL-3)-22, RA is as defined above. RLc1 is a C1-C8 saturated hydrocarbyl group or an optionally substituted C6-C20 aryl group; the saturated hydrocarbyl group may be straight, branched or cyclic. RLc2 to RLc11 are each independently hydrogen or a C1-C15 hydrocarbyl group which may contain a heteroatom; oxygen is a typical heteroatom. Suitable hydrocarbyl groups include C1-C15 alkyl groups and C6-C15 aryl groups. Alternatively, a pair of RLc2 and RLc3, RLc4 and RLc6, RLc4 and RLc7, RLc5 and RLc7, RLc5 and RLc11, RLc6 and RLc10, RLc8 and RLc9, or RLc9 and RLc10, taken together, may form a ring with the carbon atom to which they are attached, and in this event, the ring-forming group is a C1-C15 hydrocarbylene group which may contain a heteroatom. Also, a pair of RLc2 and RLc11, RLc8 and RLc11, or RLc4 and RLc6 which are attached to vicinal carbon atoms may bond together directly to form a double bond. The formula also represents an enantiomer.
Examples of the monomer having formula (AL-3)-22 are described in U.S. Pat. No. 6,448,420 (JP-A 2000-327633). Illustrative non-limiting examples of suitable monomers are given below. RA is as defined above.
Examples of the monomer from which the repeat units having an acid labile group of formula (AL-3) are derived include (meth)acrylates having a furandiyl, tetrahydrofurandiyl or oxanorbornanediyl group as represented by the following formula (AL-3)-23.
In formula (AL-3)-23, RA is as defined above. RLc12 and RLc13 are each independently a C1-C10 hydrocarbyl group, or RLc12 and RLc13, taken together, may form an aliphatic ring with the carbon atom to which they are attached. RLc14 is furandiyl, tetrahydrofurandiyl or oxanorbornanediyl. RLc15 is hydrogen or a C1-C10 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be straight, branched or cyclic, and is typically a C1-C10 saturated hydrocarbyl group.
Examples of the monomer having formula (AL-3)-23 are shown below, but not limited thereto. Herein RA is as defined above.
The base polymer may further include repeat units (c) having an adhesive group. The adhesive group is selected from hydroxy, carboxy, lactone ring, carbonate, thiocarbonate, carbonyl, cyclic acetal, ether bond, ester bond, sulfonic ester bond, cyano, amide bond, —O—C(═O)—S— and —O—C(═O)—NH—.
Examples of the monomer from which repeat units (c) are derived are given below, but not limited thereto. Herein RA is as defined above.
The base polymer may further include repeat units (d) of at least one type selected from repeat units having the following formulae (d1), (d2) and (d3). These units are simply referred to as repeat units (d1), (d2) and (d3), which may be used alone or in combination of two or more types.
In formulae (d1) to (d3), RA is each independently hydrogen or methyl. Z1 is a single bond, or a C1-C6 aliphatic hydrocarbylene group, phenylene group, naphthylene group, or a C7-C18 group obtained by combining the foregoing, or —O—Z11—, —C(═O)—O—Z11— or —C(═O)—NH—Z11—, wherein Z11 is a C1-C6 aliphatic hydrocarbylene group, phenylene group, naphthylene group, or a C7-C18 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond or hydroxy moiety. Z2 is a single bond or ester bond. Z3 is a single bond, —Z31—C(═O)—O—, —Z31—O—, or wherein Z31 is a C1-C12 aliphatic hydrocarbylene group, phenylene group or a C7-C18 group obtained by combining the foregoing, which may contain a carbonyl moiety, ester bond, ether bond, bromine or iodine. Z4 is methylene, 2,2,2-trifluoro-1,1-ethanediyl or carbonyl. Z5 is a single bond, methylene, ethylene, phenylene, fluorinated phenylene, trifluoromethyl-substituted phenylene group, —O—Z51—, —C(═O)—O—Z— or —C(═O)—NH—Z51—, wherein Z51 is a C1-C6 aliphatic hydrocarbylene group, phenylene group, fluorinated phenylene group, or trifluoromethyl-substituted phenylene group, which may contain a carbonyl moiety, ester bond, ether bond, hydroxy moiety or halogen.
In formulae (d1) to (d3), R21 to R28 are each independently halogen or a C1-C20 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be straight, branched or cyclic. Examples thereof are as will be exemplified later for R101 to R105 in formulae (1-1) and (1-2).
Also, a pair of R23 and R24, or R26 and R27 may bond together to form a ring with the sulfur atom to which they are attached. Examples of the ring are as will be exemplified later for the ring that R101 and R102 in formula (1-1), taken together, form with the sulfur atom to which they are attached.
In formula (d1), M− is a non-nucleophilic counter ion. Examples of the non-nucleophilic counter ion include halide ions such as chloride and bromide ions; fluoroalkylsulfonate ions such as triflate, 1,1,1-trifluoroethanesulfonate, and nonafluorobutanesulfonate; arylsulfonate ions such as tosylate, benzenesulfonate, 4-fluorobenzenesulfonate, and 1,2,3,4,5-pentafluorobenzenesulfonate; alkylsulfonate ions such as mesylate and butanesulfonate; imide ions such as bis(trifluoromethylsulfonyl)imide, bis(perfluoroethylsulfonyl)imide and bis(perfluorobutylsulfonyl)imide; methide ions such as tris(trifluoromethylsulfonyl)methide and tris(perfluoroethylsulfonyl)methide.
Also included are sulfonate ions having fluorine substituted at α-position as represented by the formula (d1-1) and sulfonate ions having fluorine substituted at α-position and trifluoromethyl at β-position as represented by the formula (d1-2).
In formula (d1-1), R31 is hydrogen, or a C1-C20 hydrocarbyl group which may contain an ether bond, ester bond, carbonyl moiety, lactone ring, or fluorine atom. The hydrocarbyl group may be straight, branched or cyclic and examples thereof are as will be exemplified later for the hydrocarbyl group R111 in formula (1A′).
In formula (d1-2), R32 is hydrogen, or a C1-C30 hydrocarbyl group or C2-C30 hydrocarbylcarbonyl group which may contain an ether bond, ester bond, carbonyl moiety or lactone ring. The hydrocarbyl group and hydrocarbyl moiety in the hydrocarbylcarbonyl group may be saturated or unsaturated and straight, branched or cyclic and examples thereof are as will be exemplified later for the hydrocarbyl group R111 in formula (1A′).
Examples of the cation in the monomer from which repeat unit (d1) is derived are shown below, but not limited thereto. RA is as defined above.
Examples of the anion in the monomer from which repeat unit (d2) is derived are shown below, but not limited thereto. RA is as defined above.
Examples of the anion in the monomer from which repeat unit (d3) is derived are shown below, but not limited thereto. RA is as defined above.
Repeat units (d1) to (d3) function as an acid generator. The attachment of an acid generator to the polymer main chain is effective in restraining acid diffusion, thereby preventing a reduction of resolution due to blur by acid diffusion. Also edge roughness and size variation are improved since the acid generator is uniformly distributed. Where a base polymer containing repeat units (d1) to (d3), known as polymer-bound acid generator, is used, an acid generator of addition type to be described later may be omitted.
The base polymer may further comprise repeat units (e) containing iodine, but not amino. Examples of the monomer from which repeat units (e) are derived are shown below, but not limited thereto. RA is as defined above.
Besides the above-described repeat units, the base polymer may further include repeat units (f) which are derived from such monomers as styrene, acenaphthylene, indene, coumarin, and coumarone.
In the base polymer comprising repeat units (a), (b1), (b2), (c), (d1), (d2), (d3), (e) and (f), a fraction of these units is: preferably 0<a<1.0, 0≤b1≤0.9, 0≤b2≤0.9, 0≤b1+b2≤0.9, 0≤c≤0.9, 0≤d1≤0.5, 0≤d2≤0.5, 0≤d3≤0.5, 0≤d1+d2+d3≤0.5, 0≤e≤0.5, and 0≤f≤0.5;
more preferably 0.01≤a≤0.8, 0≤b1≤0.8, 0≤b2≤0.8, 0≤b1+b2≤0.8, 0≤c≤0.8, 0≤d1≤0.4, 0≤d2≤0.4, 0≤d3≤0.4, 0≤d1+d2+d3≤0.4, 0≤e≤0.4, and 0≤f≤0.4; and even more preferably 0.01≤a≤0.7, 0≤b1≤0.7, 0≤b2≤0.7, 0≤b1+b2≤0.7, 0≤c≤0.7, 0≤d1≤0.3, 0≤d2≤0.3, 0≤d3≤0.3, 0≤d1+d2+d3≤0.3, 0≤e≤0.3, and 0≤f≤0.3. Notably, a+b1+b2+c+d1+d2+d3+e+f=1.0.
The base polymer may be synthesized by any desired methods, for example, by dissolving suitable monomers selected from the monomers corresponding to the foregoing repeat units in an organic solvent, adding a radical polymerization initiator thereto, and heating for polymerization. Examples of the organic solvent which can be used for polymerization include toluene, benzene, tetrahydrofuran (THF), diethyl ether, and dioxane. Examples of the polymerization initiator used herein include 2,2′-azobisisobutyronitrile (AIBN), 2,2′-azobis(2,4-dimethylvaleronitrile), dimethyl 2,2-azobis(2-methylpropionate), benzoyl peroxide, and lauroyl peroxide. Preferably the reaction temperature is 50 to 80° C., and the reaction time is 2 to 100 hours, more preferably 5 to 20 hours.
In the case of a monomer having a hydroxy group, the hydroxy group may be replaced by an acetal group susceptible to deprotection with acid, typically ethoxyethoxy, prior to polymerization, and the polymerization be followed by deprotection with weak acid and water. Alternatively, the hydroxy group may be replaced by an acetyl, formyl, pivaloyl or similar group prior to polymerization, and the polymerization be followed by alkaline hydrolysis.
When hydroxystyrene or hydroxyvinylnaphthalene is copolymerized, an alternative method is possible. Specifically, acetoxystyrene or acetoxyvinylnaphthalene is used instead of hydroxystyrene or hydroxyvinylnaphthalene, and after polymerization, the acetoxy group is deprotected by alkaline hydrolysis, for thereby converting the polymer product to hydroxystyrene or hydroxyvinylnaphthalene. For alkaline hydrolysis, a base such as aqueous ammonia or triethylamine may be used. Preferably the reaction temperature is −20° C. to 100° C., more preferably 0° C. to 60° C., and the reaction time is 0.2 to 100 hours, more preferably 0.5 to 20 hours.
The base polymer should preferably have a weight average molecular weight (Mw) in the range of 1,000 to 500,000, and more preferably 2,000 to 30,000, as measured by GPC versus polystyrene standards using tetrahydrofuran (THF) solvent. With too low a Mw, the resist composition may become less heat resistant. A polymer with too high a Mw may lose alkaline solubility and give rise to a footing phenomenon after pattern formation.
If a base polymer has a wide molecular weight distribution or dispersity (Mw/Mn), which indicates the presence of lower and higher molecular weight polymer fractions, there is a possibility that foreign matter is left on the pattern or the pattern profile is degraded. The influences of Mw and Mw/Mn become stronger as the pattern rule becomes finer. Therefore, the base polymer should preferably have a narrow dispersity (Mw/Mn) of 1.0 to 2.0, especially 1.0 to 1.5, in order to provide a resist composition suitable for micropatterning to a small feature size.
The base polymer may be a blend of two or more polymers which differ in compositional ratio, Mw or Mw/Mn. A blend of a polymer containing repeat units (a) and a polymer containing repeat units (b1) and/or (b2), but not repeat units (a) is also acceptable.
The resist composition may comprise an acid generator capable of generating a strong acid (referred to as acid generator of addition type, hereinafter). As used herein, the term “strong acid” refers to a compound having a sufficient acidity to induce deprotection reaction of an acid labile group on the base polymer.
The acid generator is typically a compound (PAG) capable of generating an acid upon exposure to actinic ray or radiation. Although the PAG used herein may be any compound capable of generating an acid upon exposure to high-energy radiation, those compounds capable of generating sulfonic acid, imide acid (imidic acid) or methide acid are preferred. Suitable PAGs include sulfonium salts, iodonium salts, sulfonyldiazomethane, N-sulfonyloxyimide, and oxime-O-sulfonate acid generators. Exemplary PAGs are described in JP-A 2008-111103, paragraphs [0122]-[0142] (U.S. Pat. No. 7,537,880).
As the PAG used herein, sulfonium salts having the formula (1-1) and iodonium salts having the formula (1-2) are also preferred.
In formulae (1-1) and (1-2), R101 to R105 are each independently halogen or a C1-C20 hydrocarbyl group which may contain a heteroatom. Suitable halogen atoms include fluorine, chlorine, bromine and iodine.
The C1-C20 hydrocarbyl groups represented by R101 to R105 may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C1-C20 alkyl groups such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, n-hexyl, n-octyl, n-nonyl, n-decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, heptadecyl, octadecyl, nonadecyl and icosyl; C3-C20 saturated cyclic hydrocarbyl groups such as cyclopropyl, cyclopentyl, cyclohexyl, cyclopropylmethyl, 4-methylcyclohexyl, cyclohexylmethyl, norbornyl, and adamantyl; C2-C20 alkenyl groups such as vinyl, propenyl, butenyl, and hexenyl; C2-C20 alkynyl groups such as ethynyl, propynyl and butynyl; C3-C20 unsaturated alicyclic hydrocarbyl groups such as cyclohexenyl and norbornenyl; C6-C20 aryl groups such as phenyl, methylphenyl, ethylphenyl, n-propylphenyl, isopropylphenyl, n-butylphenyl, isobutylphenyl, sec-butylphenyl, tert-butylphenyl, naphthyl, methylnaphthyl, ethylnaphthyl, n-propylnaphthyl, isopropylnaphthyl, n-butylnaphthyl, isobutylnaphthyl, sec-butylnaphthyl, and tert-butylnaphthyl; C7-C20 aralkyl groups such as benzyl and phenethyl; and combinations thereof. In the foregoing groups, some or all of the hydrogen atoms may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, or some carbon may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy moiety, fluorine, chlorine, bromine, iodine, cyano moiety, nitro moiety, carbonyl moiety, ether bond, ester bond, sulfonic ester bond, carbonate moiety, lactone ring, sultone ring, carboxylic anhydride or haloalkyl moiety.
Also, R101 and R102 may bond together to form a ring with the sulfur atom to which they are attached. Preferred examples of the ring are shown by the following structure.
Herein the broken line designates a point of attachment to R103.
Examples of the cation in the sulfonium salt having formula (1-1) are shown below, but not limited thereto.
Examples of the cation in the iodonium salt having formula (1-2) are shown below, but not limited thereto.
In formulae (1-1) and (1-2), Xa− is an anion selected from the following formulae (1A) to (1D).
In formula (1A), Rfa is fluorine or a C1-C40 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic, and examples thereof are as will be exemplified for the hydrocarbyl group R111 in formula (1A′).
Of the anions of formula (1A), a structure having formula (1A′) is preferred.
In formula (1A′), RHF is hydrogen or trifluoromethyl, preferably trifluoromethyl.
R111 is a C1-C38 hydrocarbyl group which may contain a heteroatom. Suitable heteroatoms include oxygen, nitrogen, sulfur and halogen, with oxygen being preferred.
Of the hydrocarbyl groups, those of 6 to 30 carbon atoms are preferred because a high resolution is available in fine pattern formation. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Suitable hydrocarbyl groups include C1-C38 alkyl groups such as methyl, ethyl, n-propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, pentyl, neopentyl, hexyl, heptyl, 2-ethylhexyl, nonyl, undecyl, tridecyl, pentadecyl, heptadecyl, icosanyl; C3-C38 cyclic saturated hydrocarbyl groups such as cyclopentyl, cyclohexyl, 1-adamantyl, 2-adamantyl, 1-adamantylmethyl, norbornyl, norbornylmethyl, tricyclodecanyl, tetracyclododecanyl, tetracyclododecanylmethyl, dicyclohexylmethyl; C2-C38 unsaturated aliphatic hydrocarbyl groups such as allyl and 3-cyclohexenyl; C6-C38 aryl groups such as phenyl, 1-naphthyl, 2-naphthyl; C7-C38 aralkyl groups such as benzyl and diphenylmethyl; and combinations thereof.
In these groups, some or all of the hydrogen atoms may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, or some carbon may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy, fluorine, chlorine, bromine, iodine, cyano, nitro, carbonyl, ether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride or haloalkyl moiety. Examples of the heteroatom-containing hydrocarbyl group include tetrahydrofuryl, methoxymethyl, ethoxymethyl, methylthiomethyl, acetamidomethyl, trifluoroethyl, (2-methoxyethoxy)methyl, acetoxymethyl, 2-carboxy-1-cyclohexyl, 2-oxopropyl, 4-oxo-1-adamantyl, and 3-oxocyclohexyl.
With respect to the synthesis of the sulfonium salt having an anion of formula (1A′), reference is made to JP-A 2007-145797, JP-A 2008-106045, JP-A 2009-007327, and JP-A 2009-258695. Also useful are the sulfonium salts described in JP-A 2010-215608, JP-A 2012-041320, JP-A 2012-106986, and JP-A 2012-153644.
Examples of the anion having formula (1A) are as exemplified for the anion having formula (1A) in JP-A 2018-197853 (US 20180335696).
In formula (1), Rfb1 and Rfb2 are each independently fluorine or a C1-C40 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Suitable hydrocarbyl groups are as exemplified above for R111 in formula (1A′). Preferably Rfb1 and Rfb2 each are fluorine or a C1-C4 straight fluorinated alkyl group. A pair of Rfb1 and Rfb2 may bond together to form a ring with the linkage (—CF2—SO2—N—SO2—CF2—) to which they are attached, and the ring-forming pair is preferably a fluorinated ethylene or fluorinated propylene group.
In formula (1C), Rfc1, Rfc2 and Rfc3 are each independently fluorine or a C1-C40 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Suitable hydrocarbyl groups are as exemplified above for R111 in formula (1A′). Preferably Rfc1, Rfc2 and Rfc3 each are fluorine or a C1-C4 straight fluorinated alkyl group. A pair of Rfc1 and Rfc2 may bond together to form a ring with the linkage (—CF2—SO2—C—SO2—CF2—) to which they are attached, and the ring-forming pair is preferably a fluorinated ethylene or fluorinated propylene group.
In formula (1D), Rfd is a C1-C40 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Suitable hydrocarbyl groups are as exemplified above for R111.
With respect to the synthesis of the sulfonium salt having an anion of formula (1D), reference is made to JP-A 2010-215608 and JP-A 2014-133723.
Examples of the anion having formula (1D) are as exemplified for the anion having formula (1D) in JP-A 2018-197853 (US 20180335696).
The compound having the anion of formula (1D) has a sufficient acid strength to cleave acid labile groups in the base polymer because it is free of fluorine at α-position of sulfo group, but has two trifluoromethyl groups at β-position. Thus the compound is a useful PAG.
Compounds having the formula (2) are also useful as the PAG.
In formula (2), R201 and R202 are each independently halogen or a C1-C30 hydrocarbyl group which may contain a heteroatom. R203 is a C1-C30 hydrocarbylene group which may contain a heteroatom. Any two of R201, R202 and R203 may bond together to form a ring with the sulfur atom to which they are attached. Exemplary rings are the same as described above for the ring that R101 and R102 in formula (1-1), taken together, form with the sulfur atom to which they are attached.
The hydrocarbyl groups R201 and R202 may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C1-C30 alkyl groups such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, tert-pentyl, n-hexyl, n-octyl, 2-ethylhexyl, n-nonyl, and n-decyl; C3-C30 cyclic saturated hydrocarbyl groups such as cyclopentyl, cyclohexyl, cyclopentylmethyl, cyclopentylethyl, cyclopentylbutyl, cyclohexylmethyl, cyclohexylethyl, cyclohexylbutyl, norbornyl, oxanorbornyl, tricyclo[5.2.1.02,6]decanyl, and adamantyl; C6-C30 aryl groups such as phenyl, methylphenyl, ethylphenyl, n-propylphenyl, isopropylphenyl, n-butylphenyl, isobutylphenyl, sec-butylphenyl, tert-butylphenyl, naphthyl, methylnaphthyl, ethylnaphthyl, n-propylnaphthyl, isopropylnaphthyl, n-butylnaphthyl, isobutylnaphthyl, sec-butylnaphthyl, tert-butylnaphthyl, and anthracenyl; and combinations thereof. In these groups, some or all of the hydrogen atoms may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, or some carbon may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy, fluorine, chlorine, bromine, iodine, cyano, nitro, carbonyl, ether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride or haloalkyl moiety.
The hydrocarbylene group R203 may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include C1-C30 alkanediyl groups such as methanediyl, ethane-1,1-diyl, ethane-1,2-diyl, propane-1,3-diyl, butane-1,4-diyl, pentane-1,5-diyl, hexane-1,6-diyl, heptane-1,7-diyl, octane-1,8-diyl, nonane-1,9-diyl, decane-1,10-diyl, undecane-1,11-diyl, dodecane-1,12-diyl, tridecane-1,13-diyl, tetradecane-1,14-diyl, pentadecane-1,15-diyl, hexadecane-1,16-diyl, and heptadecane-1,17-diyl; C3-C30 cyclic saturated hydrocarbylene groups such as cyclopentanediyl, cyclohexanediyl, norbornanediyl and adamantanediyl; C6-C30 arylene groups such as phenylene, methylphenylene, ethylphenylene, n-propylphenylene, isopropylphenylene, n-butylphenylene, isobutylphenylene, sec-butylphenylene, tert-butylphenylene, naphthylene, methylnaphthylene, ethylnaphthylene, n-propylnaphthylene, isopropylnaphthylene, n-butylnaphthylene, isobutylnaphthylene, and tert-butylnaphthylene; and combinations thereof. In these groups, some or all of the hydrogen atoms may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, or some carbon may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy, fluorine, chlorine, bromine, iodine, cyano, nitro, carbonyl, ether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride or haloalkyl moiety. Of the heteroatoms, oxygen is preferred.
In formula (2), Lc is a single bond, ether bond or a C1-C20 hydrocarbylene group which may contain a heteroatom. The hydrocarbylene group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof are as exemplified above for R203.
In formula (2), XA, XB, XC and XD are each independently hydrogen, fluorine or trifluoromethyl, with the proviso that at least one of XA, XB, XC and XD is fluorine or trifluoromethyl.
In formula (2), d is an integer of 0 to 3.
Of the PAGs having formula (2), those having formula (2′) are preferred.
In formula (2′), Lc is as defined above. RHF is hydrogen or trifluoromethyl, preferably trifluoromethyl. R301, R302 and R303 are each independently hydrogen or a C1-C20 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof are as exemplified above for R111 in formula (1A′). The subscripts x and y are each independently an integer of 0 to 5, and z is an integer of 0 to 4.
Examples of the PAG having formula (2) are as exemplified for the PAG having formula (2) in JP-A 2017-026980.
Of the foregoing PAGs, those having an anion of formula (1A′) or (1D) are especially preferred because of reduced acid diffusion and high solubility in the solvent. Also those having formula (2′) are especially preferred because of extremely reduced acid diffusion.
Also a sulfonium or iodonium salt having an anion containing an iodized or brominated aromatic ring may be used as the PAG. Suitable are sulfonium and iodonium salts having the formulae (3-1) and (3-2).
In formulae (3-1) and (3-2), p is an integer of 1 to 3, q is an integer of 1 to 5, and r is an integer of 0 to 3, and 1≤q+r≤5. Preferably, q is 1, 2 or 3, more preferably 2 or 3, and r is 0, 1 or 2.
In formulae (3-1) and (3-2), XB1 is iodine or bromine, and may be the same or different when p and/or q is 2 or more.
L1 is a single bond, ether bond, ester bond, or a C1-C6 saturated hydrocarbylene group which may contain an ether bond or ester bond. The saturated hydrocarbylene group may be straight, branched or cyclic.
L2 is a single bond or a C1-C20 divalent linking group when p is 1, and a C1-C20 (p+1)-valent linking group which may contain oxygen, sulfur or nitrogen when p is 2 or 3.
R401 is a hydroxy group, carboxy group, fluorine, chlorine, bromine, amino group, or a C1-C20 hydrocarbyl, C1-C20 hydrocarbyloxy, C2-C20 hydrocarbylcarbonyl, C2-C20 hydrocarbyloxycarbonyl, C2-C20 hydrocarbylcarbonyloxy or C1-C20 hydrocarbylsulfonyloxy group, which may contain fluorine, chlorine, bromine, hydroxy, amino or ether bond, or —N(R401A)(R401B), —N(R401C)—C(═O)—R401D or —N(R401C)—C(═O)—O—R401D. R401A and R401B are each independently hydrogen or a C1-C6 saturated hydrocarbyl group. R401C is hydrogen or a C1-C6 saturated hydrocarbyl group which may contain halogen, hydroxy, C1-C6 saturated hydrocarbyloxy, C2-C6 saturated hydrocarbylcarbonyl or C2-C6 saturated hydrocarbylcarbonyloxy moiety. R401D is a C1-C16 aliphatic hydrocarbyl group, C6-C12 aryl group or C7-C15 aralkyl group, which may contain halogen, hydroxy, C1-C6 saturated hydrocarbyloxy, C2-C6 saturated hydrocarbylcarbonyl or C2-C6 saturated hydrocarbylcarbonyloxy moiety. The hydrocarbyl, hydrocarbyloxy, hydrocarbylcarbonyl, hydrocarbyloxycarbonyl, hydrocarbylcarbonyloxy, and hydrocarbylsulfonyloxy groups may be straight, branched or cyclic. Groups R401 may be the same or different when p and/or r is 2 or more.
Of these, R401 is preferably hydroxy, —N(R401C)—C(═O)—R401D, —N(R401C)—C(═O)—O—R401D fluorine, chlorine, bromine, methyl or methoxy.
In formulae (3-1) and (3-2), Rf1 to Rf4 are each independently hydrogen, fluorine or trifluoromethyl, at least one of Rf1 to Rf4 is fluorine or trifluoromethyl. Rf1 and Rf2, taken together, may form a carbonyl group. Preferably, both Rf3 and Rf4 are fluorine.
R402 to R406 are each independently halogen or a C1-C20 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include those exemplified above for the hydrocarbyl groups R101 to R105 in formulae (1-1) and (1-2). In these groups, some or all of the hydrogen atoms may be substituted by hydroxy, carboxy, halogen, cyano, nitro, mercapto, sultone, sulfone, or sulfonium salt-containing moieties, and any constituent —CH2— may be replaced by an ether bond, ester bond, carbonyl moiety, amide bond, carbonate moiety or sulfonic ester bond. R402 and R403 may bond together to form a ring with the sulfur atom to which they are attached. Exemplary rings are the same as described above for the ring that R101 and R102 in formula (1-1), taken together, form with the sulfur atom to which they are attached.
Examples of the cation in the sulfonium salt having formula (3-1) include those exemplified above as the cation in the sulfonium salt having formula (1-1). Examples of the cation in the iodonium salt having formula (3-2) include those exemplified above as the cation in the iodonium salt having formula (1-2).
Examples of the anion in the onium salts having formulae (3-1) and (3-2) are shown below, but not limited thereto. Herein XBI is as defined above.
When used, the acid generator of addition type is preferably added in an amount of 0.1 to 50 parts, and more preferably 1 to 40 parts by weight per 100 parts by weight of the base polymer. The resist composition functions as a chemically amplified positive resist composition when the base polymer includes repeat units (d) and/or the acid generator of addition type is contained.
An organic solvent may be added to the resist composition. The organic solvent used herein is not particularly limited as long as the foregoing and other components are soluble therein. Examples of the organic solvent are described in JP-A 2008-111103, paragraphs [0144]-[0145] (U.S. Pat. No. 7,537,880). Exemplary solvents include ketones such as cyclohexanone, cyclopentanone, methyl-2-n-pentyl ketone and 2-heptanone; alcohols such as 3-methoxybutanol, 3-methyl-3-methoxybutanol, 1-methoxy-2-propanol, 1-ethoxy-2-propanol, and diacetone alcohol (DAA); ethers such as propylene glycol monomethyl ether (PGME), ethylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monoethyl ether, propylene glycol dimethyl ether, and diethylene glycol dimethyl ether; esters such as propylene glycol monomethyl ether acetate (PGMEA), propylene glycol monoethyl ether acetate, ethyl lactate, ethyl pyruvate, butyl acetate, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, tert-butyl acetate, tert-butyl propionate, and propylene glycol mono-tert-butyl ether acetate; and lactones such as γ-butyrolactone, which may be used alone or in admixture.
The organic solvent is preferably added in an amount of 100 to 10,000 parts, and more preferably 200 to 8,000 parts by weight per 100 parts by weight of the base polymer.
The positive resist composition may comprise a quencher. The quencher is typically selected from conventional basic compounds. Conventional basic compounds include primary, secondary, and tertiary aliphatic amines, mixed amines, aromatic amines, heterocyclic amines, nitrogen-containing compounds with carboxy group, nitrogen-containing compounds with sulfonyl group, nitrogen-containing compounds with hydroxy group, nitrogen-containing compounds with hydroxyphenyl group, alcoholic nitrogen-containing compounds, amide derivatives, imide derivatives, and carbamate derivatives. Also included are primary, secondary, and tertiary amine compounds, specifically amine compounds having a hydroxy group, ether bond, ester bond, lactone ring, cyano group, or sulfonic ester bond as described in JP-A 2008-111103, paragraphs [0146]-[0164], and compounds having a carbamate group as described in JP 3790649. Addition of a basic compound may be effective for further suppressing the diffusion rate of acid in the resist film or correcting the pattern profile.
Onium salts such as sulfonium salts, iodonium salts and ammonium salts of sulfonic acids which are not fluorinated at α-position as described in U.S. Pat. No. 8,795,942 (JP-A 2008-158339) and similar onium salts of carboxylic acid may also be used as the quencher. While an α-fluorinated sulfonic acid, imide acid, and methide acid are necessary to deprotect the acid labile group of carboxylic acid ester, an α-non-fluorinated sulfonic acid and a carboxylic acid are released by salt exchange with an α-non-fluorinated onium salt. An α-non-fluorinated sulfonic acid and a carboxylic acid function as a quencher because they do not induce deprotection reaction.
Examples of the quencher include a compound (onium salt of α-non-fluorinated sulfonic acid) having the formula (4) and a compound (onium salt of carboxylic acid) having the formula (5).
R501—SO3−Mq+ (4)
R502—CO2−Mq+ (5)
In formula (4), R501 is hydrogen or a C1-C40 hydrocarbyl group which may contain a heteroatom, exclusive of the hydrocarbyl group in which the hydrogen bonded to the carbon atom at α-position of the sulfone group is substituted by fluorine or fluoroalkyl moiety.
The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof include alkyl groups such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, tert-pentyl, n-pentyl, n-hexyl, n-octyl, 2-ethylhexyl, n-nonyl, n-decyl; cyclic saturated hydrocarbyl groups such as cyclopentyl, cyclohexyl, cyclopentylmethyl, cyclopentylethyl, cyclopentylbutyl, cyclohexylmethyl, cyclohexylethyl, cyclohexylbutyl, norbornyl, tricyclo[5.2.1.02,6]decanyl, adamantyl, and adamantylmethyl; alkenyl groups such as vinyl, allyl, propenyl, butenyl and hexenyl; cyclic unsaturated aliphatic hydrocarbyl groups such as cyclohexenyl; aryl groups such as phenyl, naphthyl, alkylphenyl groups (e.g., 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, 4-ethylphenyl, 4-tert-butylphenyl, 4-n-butylphenyl), dialkylphenyl groups (e.g., 2,4-dimethylphenyl and 2,4,6-triisopropylphenyl), alkylnaphthyl groups (e.g., methylnaphthyl and ethylnaphthyl), dialkylnaphthyl groups (e.g., dimethylnaphthyl and diethylnaphthyl); heteroaryl groups such as thienyl; and aralkyl groups such as benzyl, 1-phenylethyl and 2-phenylethyl.
In these groups, some hydrogen may be substituted by a moiety containing a heteroatom such as oxygen, sulfur, nitrogen or halogen, and some carbon may be replaced by a moiety containing a heteroatom such as oxygen, sulfur or nitrogen, so that the group may contain a hydroxy moiety, cyano moiety, carbonyl moiety, ether bond, ester bond, sulfonic ester bond, carbonate bond, lactone ring, sultone ring, carboxylic anhydride, or haloalkyl moiety. Suitable heteroatom-containing hydrocarbyl groups include alkoxyphenyl groups such as 4-hydroxyphenyl, 4-methoxyphenyl, 3-methoxyphenyl, 2-methoxyphenyl, 4-ethoxyphenyl, 4-tert-butoxyphenyl, 3-tert-butoxyphenyl; alkoxynaphthyl groups such as methoxynaphthyl, ethoxynaphthyl, n-propoxynaphthyl and n-butoxynaphthyl; dialkoxynaphthyl groups such as dimethoxynaphthyl and diethoxynaphthyl; and aryloxoalkyl groups, typically 2-aryl-2-oxoethyl groups such as 2-phenyl-2-oxoethyl, 2-(1-naphthyl)-2-oxoethyl and 2-(2-naphthyl)-2-oxoethyl.
In formula (5), R502 is a C1-C40 hydrocarbyl group which may contain a heteroatom. Examples of the hydrocarbyl group R502 are as exemplified above for the hydrocarbyl group R501. Also included are fluorinated alkyl groups such as trifluoromethyl, trifluoroethyl, 2,2,2-trifluoro-1-methyl-1-hydroxyethyl, 2,2,2-trifluoro-1-(trifluoromethyl)-1-hydroxyethyl, and fluorinated aryl groups such as pentafluorophenyl and 4-trifluoromethylphenyl.
In formulae (4) and (5), Mq+ is an onium cation. The onium cation is preferably selected from sulfonium, iodonium and ammonium cations, more preferably sulfonium and iodonium cations. Exemplary sulfonium cations are as exemplified above for the cation in the sulfonium salt having formula (1-1). Exemplary iodonium cations are as exemplified above for the cation in the iodonium salt having formula (1-2).
A sulfonium salt of iodized benzene ring-containing carboxylic acid having the formula (6) is also useful as the quencher.
In formula (6), R601 is hydroxy, fluorine, chlorine, bromine, amino, nitro, cyano, or a C1-C6 saturated hydrocarbyl, C1-C6 saturated hydrocarbyloxy, C2-C6 saturated hydrocarbylcarbonyloxy or C1-C4 saturated hydrocarbylsulfonyloxy group, in which some or all hydrogen may be substituted by halogen, or —N(R601A)—C(═O)—R601B or —N(R601A)—C(═O)—O—R601B. R601A is hydrogen or a C1-C6 saturated hydrocarbyl group. R601B is a C1-C6 saturated hydrocarbyl or C2-C8 unsaturated aliphatic hydrocarbyl group.
In formula (6), x′ is an integer of 1 to 5, y′ is an integer of 0 to 3, and z′ is an integer of 1 to 3. L11 is a single bond, or a C1-C20 (z′+1)-valent linking group which may contain at least one moiety selected from ether bond, carbonyl moiety, ester bond, amide bond, sultone ring, lactam ring, carbonate bond, halogen, hydroxy moiety, and carboxy moiety. The saturated hydrocarbyl, saturated hydrocarbyloxy, saturated hydrocarbylcarbonyloxy, and saturated hydrocarbylsulfonyloxy groups may be straight, branched or cyclic. Groups R601 may be the same or different when y′ and/or z′ is 2 or 3.
In formula (6), R602, R603 and R604 are each independently halogen, or a C1-C20 hydrocarbyl group which may contain a heteroatom. The hydrocarbyl group may be saturated or unsaturated and straight, branched or cyclic. Examples thereof are as exemplified above for the hydrocarbyl groups R101 to R105 in formulae (1-1) and (1-2). In these groups, some or all hydrogen may be substituted by hydroxy, carboxy, halogen, oxo, cyano, nitro, sultone, sulfone, or sulfonium salt-containing moiety, or some carbon may be replaced by an ether bond, ester bond, carbonyl moiety, amide bond, carbonate moiety or sulfonic ester bond. Also R602 and R603 may bond together to form a ring with the sulfur atom to which they are attached.
Examples of the compound having formula (6) include those described in U.S. Pat. No. 10,295,904 (JP-A 2017-219836). These compounds exert a sensitizing effect due to remarkable absorption and an acid diffusion controlling effect.
Also useful are quenchers of polymer type as described in U.S. Pat. No. 7,598,016 (JP-A 2008-239918). The polymeric quencher segregates at the resist surface and thus enhances the rectangularity of resist pattern. When a protective film is applied as is often the case in the immersion lithography, the polymeric quencher is also effective for preventing a film thickness loss of resist pattern or rounding of pattern top.
When used, the quencher is preferably added in an amount of 0 to 5 parts, more preferably 0 to 4 parts by weight per 100 parts by weight of the base polymer. The quencher may be used alone or in admixture.
With the foregoing components, other components such as a surfactant, dissolution inhibitor, water repellency improver, and acetylene alcohol may be blended in any desired combination to formulate a positive resist composition.
Exemplary surfactants are described in JP-A 2008-111103, paragraphs [0165]-[0166]. Inclusion of a surfactant may improve or control the coating characteristics of the resist composition. When used, the surfactant is preferably added in an amount of 0.0001 to parts by weight per 100 parts by weight of the base polymer. The surfactant may be used alone or in admixture.
The inclusion of a dissolution inhibitor in the positive resist composition may lead to an increased difference in dissolution rate between exposed and unexposed areas and a further improvement in resolution. The dissolution inhibitor which can be used herein is a compound having at least two phenolic hydroxy groups on the molecule, in which an average of from 0 to 100 mol % of all the hydrogen atoms on the phenolic hydroxy groups are replaced by acid labile groups or a compound having at least one carboxy group on the molecule, in which an average of 50 to 100 mol % of all the hydrogen atoms on the carboxy groups are replaced by acid labile groups, both the compounds having a molecular weight of 100 to 1,000, and preferably 150 to 800. Typical are bisphenol A, trisphenol, phenolphthalein, cresol novolac, naphthalenecarboxylic acid, adamantanecarboxylic acid, and cholic acid derivatives in which the hydrogen atom on the hydroxy or carboxy group is replaced by an acid labile group, as described in U.S. Pat. No. 7,771,914 (JP-A 2008-122932, paragraphs [0155]-[0178]).
When the positive resist composition contains a dissolution inhibitor, the dissolution inhibitor is preferably added in an amount of 0 to 50 parts, more preferably 5 to 40 parts by weight per 100 parts by weight of the base polymer. The dissolution inhibitor may be used alone or in admixture.
A water repellency improver may be added to the resist composition for improving the water repellency on surface of a resist film. The water repellency improver may be used in the topcoatless immersion lithography. Suitable water repellency improvers include polymers having a fluoroalkyl group and polymers having a specific structure with a 1,1,1,3,3,3-hexafluoro-2-propanol residue and are described in JP-A 2007-297590 and JP-A 2008-111103, for example. The water repellency improver to be added to the resist composition should be soluble in the alkaline developer and organic solvent developer. The water repellency improver of specific structure with a 1,1,1,3,3,3-hexafluoro-2-propanol residue is well soluble in the developer. A polymer having an amino group or amine salt copolymerized as repeat units may serve as the water repellent additive and is effective for preventing evaporation of acid during PEB, thus preventing any hole pattern opening failure after development. The water repellency improver may be used alone or in admixture. An appropriate amount of the water repellency improver is 0 to 20 parts, more preferably 0.5 to 10 parts by weight per 100 parts by weight of the base polymer.
Also, an acetylene alcohol may be blended in the resist composition. Suitable acetylene alcohols are described in JP-A 2008-122932, paragraphs [0179]-[0182]. An appropriate amount of the acetylene alcohol blended is 0 to 5 parts by weight per 100 parts by weight of the base polymer. The acetylene alcohols may be used alone or in admixture.
The positive resist composition is used in the fabrication of various integrated circuits. Pattern formation using the resist composition may be performed by well-known lithography processes. The process generally involves the steps of applying the resist composition onto a substrate to form a resist film thereon, exposing the resist film to high-energy radiation, and developing the exposed resist film in a developer. If necessary, any additional steps may be added.
The resist composition is first applied onto a substrate on which an integrated circuit is to be formed (e.g., Si, SiO2, SiN, SiON, TiN, WSi, BPSG, SOG, or organic antireflective coating) or a substrate on which a mask circuit is to be formed (e.g., Cr, CrO, CrON, MoSi2, or SiO2) by a suitable coating technique such as spin coating, roll coating, flow coating, dipping, spraying or doctor coating. The coating is prebaked on a hot plate at a temperature of 60 to 150° C. for 10 seconds to 30 minutes, preferably at 80 to 120° C. for 30 seconds to 20 minutes. The resulting resist film is generally 0.01 to 2 μm thick.
The resist film is then exposed to a desired pattern of high-energy radiation such as UV, deep-UV, EB, EUV of wavelength 3-15 nm, x-ray, soft x-ray, excimer laser light, γ-ray or synchrotron radiation. When UV, deep-UV, EUV, x-ray, soft x-ray, excimer laser light, γ-ray or synchrotron radiation is used as the high-energy radiation, the resist film is exposed thereto directly or through a mask having a desired pattern in a dose of preferably about 1 to 200 mJ/cm2, more preferably about 10 to 100 mJ/cm2. When EB is used as the high-energy radiation, the resist film is exposed thereto directly or through a mask having a desired pattern in a dose of preferably about 0.1 to 100 μC/cm2, more preferably about 0.5 to 50 μC/cm2. It is appreciated that the positive resist composition is suited in micropatterning using KrF excimer laser, ArF excimer laser, EB, EUV, x-ray, soft x-ray, γ-ray or synchrotron radiation, especially in micropatterning using EB or EUV.
After the exposure, the resist film may be baked (PEB) on a hotplate or in an oven at 60 to 150° C. for 10 seconds to 30 minutes, preferably at 80 to 120° C. for 30 seconds to 20 minutes.
After the exposure or PEB, the resist film is developed in a developer in the form of an aqueous base solution for 3 seconds to 3 minutes, preferably 5 seconds to 2 minutes by conventional techniques such as dip, puddle and spray techniques. A typical developer is a 0.1 to 10 wt %, preferably 2 to 5 wt % aqueous solution of tetramethylammonium hydroxide (TMAH), tetraethylammonium hydroxide (TEAH), tetrapropylammonium hydroxide (TPAH), or tetrabutylammonium hydroxide (TBAH). The resist film in the exposed area is dissolved in the developer whereas the resist film in the unexposed area is not dissolved. In this way, the desired positive pattern is formed on the substrate.
In an alternative embodiment, a negative pattern may be formed via organic solvent development using the positive resist composition. The developer used herein is preferably selected from among 2-octanone, 2-nonanone, 2-heptanone, 3-heptanone, 4-heptanone, 2-hexanone, 3-hexanone, diisobutyl ketone, methylcyclohexanone, acetophenone, methylacetophenone, propyl acetate, butyl acetate, isobutyl acetate, pentyl acetate, butenyl acetate, isopentyl acetate, propyl formate, butyl formate, isobutyl formate, pentyl formate, isopentyl formate, methyl valerate, methyl pentenoate, methyl crotonate, ethyl crotonate, methyl propionate, ethyl propionate, ethyl 3-ethoxypropionate, methyl lactate, ethyl lactate, propyl lactate, butyl lactate, isobutyl lactate, pentyl lactate, isopentyl lactate, methyl 2-hydroxyisobutyrate, ethyl 2-hydroxyisobutyrate, methyl benzoate, ethyl benzoate, phenyl acetate, benzyl acetate, methyl phenylacetate, benzyl formate, phenylethyl formate, methyl 3-phenylpropionate, benzyl propionate, ethyl phenylacetate, and 2-phenylethyl acetate, and mixtures thereof.
At the end of development, the resist film is rinsed. As the rinsing liquid, a solvent which is miscible with the developer and does not dissolve the resist film is preferred. Suitable solvents include alcohols of 3 to 10 carbon atoms, ether compounds of 8 to 12 carbon atoms, alkanes, alkenes, and alkynes of 6 to 12 carbon atoms, and aromatic solvents. Specifically, suitable alcohols of 3 to 10 carbon atoms include n-propyl alcohol, isopropyl alcohol, 1-butyl alcohol, 2-butyl alcohol, isobutyl alcohol, t-butyl alcohol, 1-pentanol, 2-pentanol, 3-pentanol, t-pentyl alcohol, neopentyl alcohol, 2-methyl-1-butanol, 3-methyl-1-butanol, 3-methyl-3-pentanol, cyclopentanol, 1-hexanol, 2-hexanol, 3-hexanol, 2,3-dimethyl-2-butanol, 3,3-dimethyl-1-butanol, 3,3-dimethyl-2-butanol, 2-ethyl-1-butanol, 2-methyl-1-pentanol, 2-methyl-2-pentanol, 2-methyl-3-pentanol, 3-methyl-1-pentanol, 3-methyl-2-pentanol, 3-methyl-3-pentanol, 4-methyl-1-pentanol, 4-methyl-2-pentanol, 4-methyl-3-pentanol, cyclohexanol, and 1-octanol. Suitable ether compounds of 8 to 12 carbon atoms include di-n-butyl ether, diisobutyl ether, di-s-butyl ether, di-n-pentyl ether, diisopentyl ether, di-s-pentyl ether, di-t-pentyl ether, and di-n-hexyl ether. Suitable alkanes of 6 to 12 carbon atoms include hexane, heptane, octane, nonane, decane, undecane, dodecane, methylcyclopentane, dimethylcyclopentane, cyclohexane, methylcyclohexane, dimethylcyclohexane, cycloheptane, cyclooctane, and cyclononane. Suitable alkenes of 6 to 12 carbon atoms include hexene, heptene, octene, cyclohexene, methylcyclohexene, dimethylcyclohexene, cycloheptene, and cyclooctene. Suitable alkynes of 6 to 12 carbon atoms include hexyne, heptyne, and octyne. Suitable aromatic solvents include toluene, xylene, ethylbenzene, isopropylbenzene, t-butylbenzene and mesitylene. The solvents may be used alone or in admixture.
Rinsing is effective for minimizing the risks of resist pattern collapse and defect formation. However, rinsing is not essential. If rinsing is omitted, the amount of solvent used may be reduced.
A hole or trench pattern after development may be shrunk by the thermal flow, RELACS® or DSA process. A hole pattern is shrunk by coating a shrink agent thereto, and baking such that the shrink agent may undergo crosslinking at the resist surface as a result of the acid catalyst diffusing from the resist layer during bake, and the shrink agent may attach to the sidewall of the hole pattern. The bake is preferably at a temperature of 70 to 180° C., more preferably 80 to 170° C., for a time of 10 to 300 seconds. The extra shrink agent is stripped and the hole pattern is shrunk.
Examples of the invention are given below by way of illustration and not by way of limitation. The abbreviation “pbw” is parts by weight.
Synthesis of Polymers
Monomers M-1 to M-7 and PAG Monomers PM-1 to PM-3 used in the synthesis of polymers have the structure shown below. The Mw of polymers is measured by GPC versus polystyrene standards using tetrahydrofuran (THF) solvent.
Synthesis of Polymer P-1
A 2-L flask was charged with 14.6 g of Monomer M-1, 6.0 g of 4-hydroxystyrene, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of azobisisobutyronitrile (AIBN) as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of isopropyl alcohol (IPA) for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-1. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-2
A 2-L flask was charged with 13.9 g of Monomer M-2, 4.2 g of 4-hydroxystyrene, 10.9 g of PAG Monomer PM-1, and 40 g of THE solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-2. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-3
A 2-L flask was charged with 9.7 g of Monomer M-2, 3.0 g of 4-(1-methylcyclohexyloxy)styrene, 4.2 g of 3-hydroxystyrene, 11.8 g of PAG Monomer PM-3, and 40 g of THE solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-3. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-4
A 2-L flask was charged with 3.3 g of Monomer M-2, 6.4 g of 1-methylcyclopentyl methacrylate, 4.2 g of 4-hydroxystyrene, 11.0 g of PAG Monomer PM-2, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-4. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-5
A 2-L flask was charged with 3.8 g of Monomer M-3, 6.4 g of 1-ethylcyclopentyl methacrylate, 4.2 g of 4-hydroxystyrene, 11.0 g of PAG Monomer PM-2, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-5. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-6
A 2-L flask was charged with 3.2 g of Monomer M-4, 6.4 g of 1-methylcyclopentyl methacrylate, 4.2 g of 3-hydroxystyrene, 11.0 g of PAG Monomer PM-2, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-6. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-7
A 2-L flask was charged with 3.6 g of Monomer M-5, 6.4 g of 1-methylcyclopentyl methacrylate, 4.2 g of 3-hydroxystyrene, 11.0 g of PAG Monomer PM-2, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-7. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-8
A 2-L flask was charged with 3.6 g of Monomer M-6, 6.4 g of 1-methylcyclopentyl methacrylate, 4.2 g of 3-hydroxystyrene, 11.0 g of PAG Monomer PM-2, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-8. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Polymer P-9
A 2-L flask was charged with 3.3 g of Monomer M-7, 6.4 g of 1-methylcyclopentyl methacrylate, 4.2 g of 3-hydroxystyrene, 11.0 g of PAG Monomer PM-2, and 40 g of THF solvent. The reactor was cooled at −70° C. in a nitrogen atmosphere, after which vacuum pumping and nitrogen blow were repeated three times. The reactor was warmed up to room temperature, whereupon 1.2 g of AIBN as polymerization initiator was added. The reactor was heated at 60° C. and held at the temperature for 15 hours for reaction. The reaction solution was poured into 1 L of IPA for precipitation. The resulting white solid was collected by filtration and dried in vacuum at 60° C., obtaining Polymer P-9. The polymer was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Comparative Polymer cP-1
Comparative Polymer cP-1 was synthesized by the same procedure as in Synthesis Example 1 aside from using 1-methylcyclopentyl methacrylate instead of Monomer M-1. Comparative Polymer cP-1 was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Comparative Polymer cP-2
Comparative Polymer cP-2 was synthesized by the same procedure as in Synthesis Example 1 aside from using 4-(1-methylcyclohexyloxy)styrene instead of Monomer M-1. Comparative Polymer cP-2 was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Synthesis of Comparative Polymer cP-3
Comparative Polymer cP-3 was synthesized by the same procedure as in Synthesis Example 1 aside from using 4-(1-methylcyclohexyloxy)phenyl methacrylate instead of Monomer M-1. Comparative Polymer cP-3 was analyzed for composition by 13C- and 1H-NMR spectroscopy and for Mw and Mw/Mn by GPC.
Positive resist compositions were prepared by dissolving the selected components in a solvent in accordance with the recipe shown in Table 1, and filtering through a filter having a pore size of 0.2 μm. The solvent contained 50 ppm of surfactant PolyFox PF-636 (Omnova Solutions Inc.).
The components in Table 1 are as identified below.
PGMEA (propylene glycol monomethyl ether acetate)
DAA (diacetone alcohol)
Each of the positive resist compositions in Table 1 was spin coated on a silicon substrate having a 20-nm coating of silicon-containing spin-on hard mask SHB-A940 (Shin-Etsu Chemical Co., Ltd., silicon content 43 wt %) and prebaked on a hotplate at 105° C. for 60 seconds to form a resist film of 50 nm thick. Using an EUV scanner NXE3400 (ASML, NA 0.33, σ 0.9/0.6, quadrupole illumination), the resist film was exposed to EUV through a mask bearing a hole pattern having a pitch of 46 nm+20% bias. The resist film was baked (PEB) on a hotplate at the temperature shown in Table 1 for 60 seconds and developed in a 2.38 wt % TMAH aqueous solution for 30 seconds to form a hole pattern having a size of 23 nm.
The resist pattern was observed under CD-SEM (CG-6000, Hitachi High-Technologies Corp.). The exposure dose that provides a hole pattern of 23 nm size is reported as sensitivity. The size of 50 holes was measured, from which a 3-fold value (3σ) of standard deviation (σ) was computed and reported as size variation or CDU.
The resist composition is shown in Table 1 together with the sensitivity and CDU of EUV lithography.
It is demonstrated in Table 1 that positive resist compositions comprising a base polymer having a pendant in the form of a fluorinated phenol group whose hydroxy group is substituted with an acid labile group offer a high sensitivity and improved CDU.
Japanese Patent Application No. 2020-179277 is incorporated herein by reference.
Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-179277 | Oct 2020 | JP | national |