Patent Application
20090081842
This invention generally relates to thin film electronic components and devices, such as thin film transistors, environmental barrier layers, capacitors, insulators, and bus lines, where a plurality of the layers are made by an atmospheric atomic layer deposition process. In particular, the present invention relates to a process for making semiconductor material layers, dielectric material layers, conducting electrode material layers and protective layers for thin film transistors, which can be used in electronic devices, particularly in displays.
Deposition of materials is a key step in fabrication of thin film electronic devices, including semiconductor devices and supporting electronic components such as resistors and capacitors, insulators, protective layers, bus lines, and other conductive structures. Traditional thin film electronic materials deposition is conducted using expensive vacuum deposition methods including evaporation, CVD, and sputtering. There is substantial interest in utilizing processes for deposition that do not involve the expense associated with vacuum processing. In typical vacuum processing, a large metal chamber and sophisticated vacuum pumping systems are required in order to provide the necessary environment. These items increase the capital cost of systems and preclude the easy use of continuous web based systems.
The cost of deposition equipment for electronic device manufacture, in terms of both the initial expenditure, cycle time, and floor space, continues to be a large incentive driving manufacturing productivity improvements. Traditionally, semiconductor manufacturers seeking to improve process cycle time arrange equipment to minimize travel distance of material between process steps. Unfortunately, this approach often results in tools of different size being placed next to each other at the expense of efficient use of fab space. In contrast, placement of groups of like equipment together results in the highest possible tool packing density; however material flow and cycle time are often compromised.
Adoption of a common tool set for deposition of a variety of electronic materials presents several opportunities for improving the design of a production facility. A common equipment base offers a high tool packing density simply because deposition modules of the same size fit together and minimize the amount of space wasted. Being able to change the material deposited through a particular equipment module allows enormous flexibility in process flow, even enabling multiple products from a single production facility. Many other cost benefits also follow from the need to maintain fewer types of equipment.
There is a also interest in depositing electronic materials on plastic or flexible substrates, particularly because these supports would be more mechanically robust, lighter weight, and potentially lead to cheaper manufacturing by allowing roll-to-roll processing. A useful example of a flexible substrate is polyethylene terephthalate. Such plastics, however, limit device processing to below 200° C.
Thin film transistors (TFTs) are representative of the electronic and manufacturing issues for most thin-film components. Thin film transistors (TFTs) are widely used as switching elements in electronics, for example, in active-matrix liquid-crystal displays, smart cards, and a variety of other electronic devices and components thereof. The thin film transistor (TFT) is an example of a field effect transistor (FET). The best-known example of an FET is the MOSFET (Metal-Oxide-Semiconductor-FET), today's conventional switching element for high-speed applications. For applications in which a transistor needs to be applied to a substrate, a thin film transistor is typically used. Critical to fabricating the thin film transistor is the deposition of materials, including a semiconductor or channel material, gate dielectric, conducting electrodes, and a protective material, onto the substrate. Presently, most thin film devices are made using vacuum deposited amorphous silicon as the channel material.
Amorphous silicon as a semiconductor for use in TFTs still has its drawbacks. The deposition of amorphous silicon, during the manufacture of transistors, requires relatively difficult or complicated processes such as plasma enhanced chemical vapor deposition and high temperatures (typically about 360° C.) to achieve the electrical characteristics sufficient for display applications. Such high processing temperatures disallow deposition on substrates made of certain plastics that might otherwise be desirable for use in applications such as flexible displays.
In the past decade, various materials have received attention as a potential alternative to amorphous silicon for use in semiconductor channels of thin film transistors. Semiconductor, dielectric, conducting, and protective materials are desirable that are simpler to process, especially those that are capable of being applied to large areas by relatively simple processes. Semiconductor, dielectric, conducting, and protective materials that can be deposited at lower temperatures would open up a wider range of substrate materials, including plastics, for flexible electronic devices.
The discovery of practical inorganic semiconductors as a replacement for current silicon-based technologies has also been the subject of considerable research efforts. For example, metal oxide semiconductors are known that constitute zinc oxide, indium oxide, gallium indium zinc oxide, tin oxide, or cadmium oxide deposited with or without additional doping elements including metals such as aluminum. Such semiconductor materials, which are transparent, can have an additional advantage for certain applications, as discussed below.
A semiconductor material useful in a TFT must display several characteristics. In typical applications of a thin film transistor, the desire is for a switch that can control the flow of current through the device. As such, it is desired that when the switch is turned on a high current can flow through the device. The extent of current flow is related to the semiconductor charge carrier mobility. When the device is turned off, it is desired that the current flow be very small. This is related to the native charge carrier concentration. Furthermore, it is desired that the device be weakly or not at all influenced by visible light to avoid a light-protection layer. In order for this to be true, the semiconductor band gap must be sufficiently large (>3 eV) so that exposure to visible light does not cause an inter-band transition. Zinc oxide based materials are capable of delivering these features. Furthermore, in a real high volume web based atmospheric manufacturing scheme, it is highly desirable that the chemistries used in the process be both cheap and of low toxicity, which can be satisfied also by the use of ZnO-based materials and the majority of its precursors.
High on/off ratios result when the device in its off state has very low current flow, often referred to as current leakage. There are many applications in which low leakage is essential. In display applications, low leakage is required for the pixel select transistor. This select transistor is a switch that allows a charge to enter in and be stored in the pixel. In a perfect transistor without leakage, once the charge is stored in the pixel the transistor is switched to its off state and this charge cannot diminish by leakage through the select transistor. Too high of an off current in a transistor will cause a decay in stored charge in the pixel which results in poor display performance.
Another transistor characteristic that is relevant for useful operation is the steepness of the transistor turn on, represented by the subthreshold slope. As the gate voltage of a transistor is varied, the transistor will start in an off state, characterized by low current flow, and transition to an on state, characterized by high current flow. When the gate voltage reaches a point at which the transistor begins to turn on, there is a substantial increase in drain current with increasing gate voltage. This increase, called the subthreshold slope, is measured in volts of gate voltage per decade of drain current. This expression therefore represents the number of volts of gate voltage required to produce a 10-fold increase in drain current. Lower values of the subthreshold slope indicate faster device turn on and are desirable.
Various processes for making zinc oxide films have been disclosed, both high temperature and low temperature processes, including radio frequency magnetron sputtering or modified reactive planar magnetron sputtering.
Ohya et al. (Japanese Journal of Applied Physics, Part 1, January 2001, vol. 40, no. 1, pages 297-8) disclose a thin film transistor of ZnO fabricated by chemical solution deposition.
Transparent conducting oxides are reviewed in the August 2000 issue of the Materials Research Bulletin, Volume 25 (8) 2000, devoted to materials and properties of transparent conducting oxide compounds.
One low temperature process for deposition of such oxide semiconductors is disclosed in US 2004/0127038 to Carcia et al. This patent publication discloses a semiconductor deposition process that uses magnetron sputtering of a metal oxide (ZnO, In2O3, SnO2, CdO) or metal (Zn, In, Sn, Cd) target in an atmosphere with a controlled partial pressure of oxygen in an inert gas. This is a low temperature process that is compatible with temperature sensitive substrates and components, for example, drive circuits for displays on flexible, polymer substrates. The field effect transistors of Carcia et al. are based on a nominally undoped metal oxide semiconductor that must be deposited using physical vapor deposition or chemical vapor deposition, preferably rf (radio frequency) magnetron sputtering.
Japanese Kokai JP2004349583 discloses a method of producing a thin film transistor in which a dispersion of zinc-oxide nanoparticles is ink-jetted to form the semiconducting channel. No actual examples, however, are described relating to the preparation of the dispersion.
US 2004/0127038 discloses a method to produce high quality zinc-oxide thin film transistors using sputtering as a vacuum deposition method.
Steven K. Volkman et al., in “A novel transparent air-stable printable n-type semiconductor technology using ZnO nanoparticles,” 2004 IEEE International Electron Device meeting Technical Digest, pp. 769, 2004, disclose a method for producing thin film transistors using organically stabilized zinc-oxide nanoparticles. The disclosed process involves an exposure to a temperature of 400° C.
Although successful zinc oxide based devices have been made with sputtering techniques, it is clear that very precise control over the reactive gas composition (such as oxygen content) is required to produce good quality devices. Chemical vapor deposition (CVD) techniques, in which two reactive gasses are mixed to form the desired film material, can be useful routes to achieving high quality film growth. Atomic layer deposition (“ALD”) is yet another alternative film deposition technology that can provide improved thickness resolution and conformal capabilities, compared to its CVD predecessor. The ALD process segments the conventional thin-film deposition process of conventional CVD into single atomic-layer deposition steps.
ALD can be used as a fabrication step for forming a number of types of thin-film electronic devices, including semiconductor devices and supporting electronic components such as resistors and capacitors, insulators, bus lines, and other conductive structures. ALD is particularly suited for forming thin layers of metal oxides in the components of electronic devices. General classes of functional materials that can be deposited with ALD include conductors, dielectrics or insulators, and semiconductors.
Examples of useful semiconducting materials are compound semiconductors such as gallium arsenide, gallium nitride, cadmium sulfide, zinc oxide, and zinc sulfide.
Advantageously, ALD steps are self-terminating and can deposit precisely one atomic layer when conducted up to or beyond self-termination exposure times. An atomic layer typically ranges from about 0.1 to about 0.5 molecular monolayers, with typical dimensions on the order of no more than a few Angstroms. In ALD, deposition of an atomic layer is the outcome of a chemical reaction between a reactive molecular precursor and the substrate. In each separate ALD reaction-deposition step, the net reaction deposits the desired atomic layer and substantially eliminates “extra” atoms originally included in the molecular precursor. In its most pure form, ALD involves the adsorption and reaction of each of the precursors in the complete absence of the other precursor or precursors of the reaction. In practice in any process it is difficult to avoid some direct reaction of the different precursors leading to a small amount of chemical vapor deposition reaction. The goal of any process claiming to perform ALD is to obtain device performance and attributes commensurate with an ALD process while recognizing that a small amount of CVD reaction can be tolerated.
In ALD applications, typically two molecular precursors are introduced into the ALD reactor in separate stages. For example, a metal precursor molecule, MLx, comprises a metal element, M that is bonded to an atomic or molecular ligand, L. For example, M could be, but would not be restricted to, Al, W, Ta, Si, Zn, etc. The metal precursor reacts with the substrate when the substrate surface is prepared to react directly with the molecular precursor. For example, the substrate surface typically is prepared to include hydrogen-containing ligands, AH or the like, that are reactive with the metal precursor. Sulfur (S), oxygen (O), and Nitrogen (N) are some typical A species. The gaseous precursor molecule effectively reacts with all of the ligands on the substrate surface, resulting in deposition of a single atomic layer of the metal:
substrate-AH+MLx→substrate-AMLx-1+HL (1)
where HL is a reaction by-product. During the reaction, the initial surface ligands, AH, are consumed, and the surface becomes covered with AMLx-1 ligands, which cannot further react with metal precursor MLx. Therefore, the reaction self-terminates when all of the initial AH ligands on the surface are replaced with AMLx-1 species. The reaction stage is typically followed by an inert-gas purge stage that eliminates the excess metal precursor and the HL by-product species from the chamber prior to the separate introduction of the other precursor.
A second molecular precursor then is used to restore the surface reactivity of the substrate towards the metal precursor. This is done, for example, by removing the L ligands and re-depositing AH ligands. In this case, the second precursor typically comprises the desired (usually nonmetallic) element A (i.e., O, N, S), and hydrogen (i.e., H2O, NH3, H2S). The next reaction is as follows:
substrate-A−ML+AHY→substrate-A−M−AH+HL (2)
This converts the surface back to its AH-covered state. (Here, for the sake of simplicity, the chemical reactions are not balanced.) The desired additional element, A, is incorporated into the film and the undesired ligands, L, are eliminated as volatile by-products. Once again, the reaction consumes the reactive sites (this time, the L terminated sites) and self-terminates when the reactive sites on the substrate are entirely depleted. The second molecular precursor then is removed from the deposition chamber by flowing inert purge-gas in a second purge stage.
In summary, then, an ALD process requires alternating in sequence the flux of chemicals to the substrate. The representative ALD process, as discussed above, is a cycle having four different operational stages:
1. MLx reaction;
2. MLx purge;
3. AHy reaction; and
4. AHy purge, and then back to stage 1.
This repeated sequence of alternating surface reactions and precursor-removal that restores the substrate surface to its initial reactive state, with intervening purge operations, is a typical ALD deposition cycle. A key feature of ALD operation is the restoration of the substrate to its initial surface chemistry condition. Using this repeated set of steps, a film can be layered onto the substrate in equal metered layers that are all identical in chemical kinetics, deposition per cycle, composition, and thickness.
Self-saturating surface reactions make ALD insensitive to transport non-uniformities, which might otherwise impair surface uniformity, due either to engineering tolerances and the limitations of the flow process or related to surface topography (that is, deposition into three dimensional, high aspect ratio structures). As a general rule, a non-uniform flux of chemicals in a reactive process generally results in different completion times at different areas. However, with ALD, each of the reactions is allowed to complete on the entire substrate surface. Thus, differences in completion kinetics impose no penalty on uniformity. This is because the areas that are first to complete the reaction self-terminate the reaction; other areas are able to continue until the full treated surface undergoes the intended reaction.
Typically, an ALD process deposits about 0.1-0.2 nm of a film in a single ALD cycle (with numbered steps 1 through 4 as listed earlier). A useful and economically feasible cycle time must be achieved in order to provide a uniform film thickness in a range of from about 3 nm to 300 nm for many or most semiconductor applications, and even thicker films for other applications. Industry throughput standards dictate that substrates be processed in 2 minutes to 3 minutes, which means that ALD cycle times must be in a range from about 0.6 seconds to about 6 seconds.
An ALD process must be able to execute this sequencing efficiently and reliably for many cycles in order to allow cost-effective coating of many substrates. In an effort to minimize the time that an ALD reaction needs to reach self-termination, at any given reaction temperature, one approach has been to maximize the flux of chemicals flowing into the ALD reactor, using a so-called “pulsing” process. In the pulsed ALD process, a substrate sits in a chamber and is exposed to the above sequence of gases by allowing a first gas to enter the chamber, followed by a pumping cycle to remove that gas, followed by the introduction of a second gas to the chamber, followed by a pumping cycle to remove the second gas. This sequence can be repeated at any frequency and variations in gas type and/or concentration. The net effect is that the entire chamber experiences a variation in gas composition with time, and thus this type of ALD can be referred to as time dependent ALD. The vast majority of existing ALD processes are time dependent ALD.
In order to maximize the flux of chemicals into the ALD reactor, it is advantageous to introduce the molecular precursors into the ALD reactor with minimum dilution of inert gas and at high pressures. However, these measures work against the need to achieve short cycle times and the rapid removal of these molecular precursors from the ALD reactor. Rapid removal in turn dictates that gas residence time in the ALD reactor be minimized.
Existing ALD approaches have been compromised with the trade-off between the need to shorten reaction times and improve chemical utilization efficiency, and on the other hand, the need to minimize purge-gas residence and chemical removal times. One approach to overcome the inherent limitations of time depended ALD systems is to provide each reactant gas continuously and to move the substrate through each gas in succession. In these systems a relatively constant gas composition exists, but is located to specific areas or spaces of the processing system. Therefore, these systems will be referred to as spatially dependent ALD systems.
For example, U.S. Pat. No. 6,821,563 entitled “GAS DISTRIBUTION SYSTEM FOR CYCLICAL LAYER DEPOSITION” to Yudovsky describes a spatially dependent ALD processing system, under vacuum, having separate gas ports for precursor and purge gases, alternating with vacuum pump ports between each gas port. Each gas port directs its stream of gas vertically downward toward a substrate. The separate gas flows are separated by walls or partitions, with vacuum pumps for evacuating gas on both sides of each gas stream. A lower portion of each partition extends close to the substrate, for example, about 0.5 mm or greater from the substrate surface. In this manner, the lower portions of the partitions are separated from the substrate surface by a distance sufficient to allow the gas streams to flow around the lower portions toward the vacuum ports after the gas streams react with the substrate surface.
A rotary turntable or other transport device is provided for holding one or more substrate wafers. With this arrangement, the substrate is shuttled beneath the different gas streams, effecting ALD deposition thereby. In one embodiment, the substrate is moved in a linear path through a chamber, in which the substrate is passed back and forth a number of times.
Another approach using continuous gas flow spatially dependent ALD is shown in U.S. Pat. No. 4,413,022 entitled “METHOD FOR PERFORMING GROWTH OF COMPOUND THIN FILMS” to Suntola et al. A gas flow array is provided with alternating source gas openings, carrier gas openings, and vacuum exhaust openings. Reciprocating motion of the substrate over the array effects ALD deposition, again, without the need for pulsed operation. In the embodiment of
While processes such as those described in the '563 Yudovsky and '022 Suntola et al. patents may avoid some of the difficulties inherent to pulsed gas approaches, these processes have other drawbacks. For example, it would be very difficult to maintain a uniform vacuum at different points in an array and to maintain synchronous gas flow and vacuum at complementary pressures, thus compromising the uniformity of gas flux that is provided to the substrate surface. Neither the gas flow delivery unit of the '563 Yudovsky patent nor the gas flow array of the '022 Suntola et al. patent can be used in closer proximity to the substrate than about 0.5 mm.
U.S. Patent Publication No. 2005/0084610 to Selitser discloses an atmospheric pressure atomic layer chemical vapor deposition process. Selitser state that extraordinary increases in reaction rates are obtained by changing the operating pressure to atmospheric pressure, which will involve orders of magnitude increase in the concentration of reactants, with consequent enhancement of surface reactant rates. The embodiments of Selitser involve separate chambers for each stage of the process, although
A spatially dependent ALD process can be accomplished with other apparatus or systems described in more detail in commonly assigned U.S. application Ser. No. 11/392,007; U.S. application Ser. No. 11/392,006; U.S. application Ser. No. 11/620,740; and U.S. application Ser. No. 11/620,744, filed Jan. 08, 2007 by Levy and entitled “DEPOSITION SYSTEM AND METHOD USING A DELIVERY HEAD SEPARATED FROM A SUBSTRATE BY GAS PRESSURE.” All these identified applications hereby incorporated by reference in their entirety. These systems attempt to overcome one of the difficult aspects of a spatial ALD system, which is undesired intermixing of the continuously flowing mutually reactive gases. In particular, U.S. Ser. No. 11/392,007 employs a novel transverse flow pattern to prevent intermixing, while U.S. Ser. No. 11/620,744 and U.S. Ser. No. 11/620,740 employ a coating head partially levitated by the pressure of the reactive gases of the process to accomplish improved gas separation.
The references discussed above are mostly concerned with making a single layer by using various ALD methods. There is no recognition of the potential manufacturing benefits to having a single piece of deposition equipment to deposit most, if not all, of the active layers in a TFT device.
Sugihara et al., US 2006/0244107, disclose a method to prepare acceptor-doped ZnO-based TFTs with an adjacent barrier layer. In their method, the films are prepared by using pulsed laser deposition with a substrate temperature of 300° C. and using nitric oxide as the N-dopant for the ZnO-based semiconductor layer. Sugihara et al. do discuss TFTs where the dielectric (Al2O3), the semiconductor (ZnO) and the protective layer (Al2O3) are all deposited using the same method. However, the method disclosed in Sugihara et al. of pulsed laser deposition is a vacuum process and not well suited for high throughput. Additionally, there is no recognition in Sugihara et al. that having a common process is a manufacturing advantage; in fact they propose alternative materials for the protective layer, including resins, which could not be deposited by the pulsed laser deposition method used to deposit the semiconductor.
Thus, a need still remains to be able to make high quality TFT devices at low cost, without the need for multiple types of deposition equipment
The present invention relates to a process of making a thin film transistor comprising at least five layers including a gate layer, a dielectric layer, a channel layer, a source-drain layer, and a protective layer, wherein at least three layers are grown a by an atomic layer deposition (ALD) process that is carried out substantially at or above atmospheric pressure, wherein the temperature of the substrate during deposition is under 300° C., and wherein the ALD process comprises simultaneously directing a series of gas flows comprising, in order, at least a first reactive gaseous material, an inert purge gas, and a second reactive gaseous material through a plurality of output openings spaced apart from the substrate, and transporting the substrate in a direction relative to the plurality of output openings, such that the substrate experiences a sequence of the first, second and third gaseous materials and whereby the sequence causes a layer to be formed on the substrate by ALD.
The present invention further relates to a process of making semiconductor material layers, dielectric material layers, conducting electrode material layers, and protective layers for thin film transistors, which are deposited employing a common piece of equipment, wherein the process is carried out substantially at or above atmospheric pressure and the temperature of the substrate during deposition is under 300° C. During the process, the substrate or deposition device for the gaseous materials, or both, is capable of providing relative movement between the output face of the deposition device and the substrate while maintaining close proximity.
In a preferred embodiment, the process can be operated with continuous movement of a substrate being subjected to thin film deposition, wherein the process is capable of conveying the support on or as a web past the deposition device, preferably in an unsealed environment open to ambient at substantially atmospheric pressure.
It is an advantage of the present invention that it provides an advantageous process for atomic layer deposition of a zinc-oxide-based n-type semiconductor onto a substrate, well suited to a number of different types of substrates and deposition environments.
It is yet a further advantage of the present invention that it is adaptable for deposition on a web or other moving substrate, including deposition onto a large area substrate.
It is a further advantage of the present invention that it allows operation, in preferred embodiments, under atmospheric pressure conditions.
It is still a further advantage of the present invention that it can be employed in low temperature processes at atmospheric pressures, which process may be practiced in an unsealed environment, open to ambient atmosphere.
The invention is also directed to a transistor comprising a zinc-oxide-based semiconductor, preferably on a flexible substrate, made by the present process.
Semiconductor films made by the present method are capable of exhibiting, in the film form, excellent field-effect electron mobilities of greater than 0.1 cm2/Vs and on-off ratios of greater than 104, in which performance properties are sufficient for use in a variety of relevant technologies, including active matrix display backplanes.
A TFT structure includes, in addition to the semiconductor, conducting electrodes, commonly referred to as a source and a drain, for injecting a current into the semiconductor. The semiconductor films made by the present invention can be used in thin film transistors each comprising spaced apart first and second contact means connected to a semiconductor film. A third contact means can be spaced from said semiconductor film by an insulator, and adapted for controlling, by means of a voltage applied to the third contact means, a current between the first and second contact means through said film. The first, second, and third contact means can correspond to a drain, source, and gate electrode in a field effect transistor.
The objects, features, and advantages of the present invention will become apparent to those skilled in the art upon a reading of the following detailed description when taken in conjunction with the drawings wherein there is shown and described an illustrative embodiment of the invention.
While the specification concludes with claims particularly pointing out and distinctly claiming the subject matter of the present invention, it is believed that the invention will be better understood from the following description when taken in conjunction with the accompanying drawings, wherein:
The entire process of making the thin film transistor or electronic device of the present invention, or at least the production of the thin film semiconductor, can be carried out below a maximum support temperature of about 300° C., more preferably below 250° C., or even at temperatures around room temperature (about 25° C. to 70° C.). The temperature selection generally depends on the support and processing parameters known in the art, once one is armed with the knowledge of the present invention contained herein. These temperatures are well below traditional integrated circuit and semiconductor processing temperatures, which enables the use of any of a variety of relatively inexpensive supports, such as flexible polymeric supports. Thus, the invention enables production of relatively inexpensive circuits containing thin film transistors with significantly improved performance.
For the description that follows, the term “gas” or “gaseous material” is used in a broad sense to encompass any of a range of vaporized or gaseous elements, compounds, or materials. Other terms used herein, such as: reactant, precursor, vacuum, and inert gas, for example, all have their conventional meanings as would be well understood by those skilled in the materials deposition art. The figures provided are not drawn to scale but are intended to show overall function and the structural arrangement of some embodiments of the present invention.
The process of the present invention offers a significant departure from conventional approaches to making a thin film transistor, employing a system for delivery of gaseous materials to a substrate surface to deposit the functional layers, and that can be adaptable to deposition on larger and web-based substrates and capable of achieving a highly uniform thin-film deposition at improved throughput speeds. The process of the present invention employs a continuous spatially dependent ALD (as opposed to pulsed or time dependent ALD) gaseous material distribution for three or more of the transistor components. The process of the present invention allows operation at atmospheric or near-atmospheric pressures and is capable of operating in an unsealed or open-air environment.
In one embodiment of the present process, the gate layer, dielectric layer for the gate layer, channel layer, source drain layer, and protective layer in thin film transistors are grown by an atomic layer deposition process. In another embodiment, only (or at least) the dielectric layer, channel layer, and the protective layer are grown by the present atomic layer deposition process. In yet another embodiment, only (or at least) the gate layer, the dielectric layer, channel layer, and the protective layer are grown by the present atomic layer deposition process. In one particular embodiment, at least three of the five layers are oxide layers. In another particular embodiment, the gate layer is grown by the present atomic layer deposition process and the gate layer is zinc oxide doped with an element selected from indium, aluminum, boron, and fluorine. In yet another particular embodiment, the source-drain layer is grown by the present atomic layer deposition process and the source-drain layer is zinc oxide doped with an element selected from indium, aluminum, boron, and fluorine. In yet another embodiment of the present process, the gate layer is a metal grown by the present atomic layer deposition process, the gate layer, and the source-drain layer is a metal grown by the present said atomic layer deposition process.
As shown in Step 1, a continuous supply of gaseous materials for the system is provided for depositing a thin film of material on a substrate. The Steps in Sequence 15 are sequentially applied. In Step 2, with respect to a given area of the substrate (referred to as the channel area), a first molecular precursor or reactive gaseous material is directed to flow in a first channel over the channel area of the substrate and reacts therewith. In Step 3 relative movement of the substrate and the multi-channel flows in the system occurs, which sets the stage for Step 4, in which second channel (purge) flow with inert gas occurs over the given channel area. Then, in Step 5, relative movement of the substrate and the multi-channel flows sets the stage for Step 6, in which the given channel area is subjected to atomic layer deposition in which a second molecular precursor now (in this particular embodiment, transversely and substantially parallel to the surface of the substrate) over the given channel area of the substrate and reacts with the previous layer on the substrate to produce (theoretically) a monolayer of a desired material. A first molecular precursor is in gas form, for example, an organometallic compound such as diethylzinc or trimethyl-aluminum. In such an embodiment, the second molecular precursor is also in gaseous form and can be, for example, a non-metallic oxidizing compound. Optionally, a volatile acceptor doping compound can be supplied to the system in any way in which allows it to react to sites in the growing film. Thus, it can be delivered with the first or second molecular precursors, or with the purge gas. Preferably the volatile acceptor is delivered in common with the oxidizing molecular precursor.
In Step 7, relative movement of the substrate and the multi-channel flows then sets the stage for Step 8 in which again an inert gas is used, this time to sweep excess second molecular precursor from the given channel area from the previous Step 6. In Step 9, relative movement of the substrate and the multi-channels occurs again, which sets the stage for a repeat sequence, back to Step 2. The cycle is repeated as many times as is necessary to establish a desired film. In the present embodiment of the process, the steps are repeated with respect to a given channel area of the substrate, corresponding to the area covered by a flow channel. Meanwhile the various channels are being supplied with the necessary gaseous materials in Step 1. Simultaneous with the sequence of box 15 in
The primary purpose of the second molecular precursor is to condition the substrate surface back toward reactivity with the first molecular precursor. The second molecular precursor also provides material from the molecular gas to combine with metal at the surface, for example, in the ZnO example, forming an oxide with a freshly deposited zinc-containing precursor.
This particular embodiment does not need to use a vacuum purge to remove a molecular precursor after applying it to the substrate. Purge steps are expected by most researchers to be the most significant throughput-limiting step in ALD processes.
Assuming that, for the two reactant gases in
Because the film can be deposited one monolayer at a time it tends to be conformal and have uniform thickness.
Oxides that can be made using the process of the present invention include, but are not limited to: ZnO, Al2O3, titanium oxides, indium oxide, and tin oxide. Mixed structure oxides that can be made using the process of the present invention can include, for example, InZnO. Doped materials that can be made using the process of the present invention can include, for example, ZnO:Al, MgxZn1-xO, and LiZnO.
Metals that can be made using the process of the present invention include, but are not limited to: copper, tungsten, aluminum, nickel, ruthenium, and rhodium. It will be apparent to the skilled artisan that alloys of two, three or more metals may be deposited, compounds may be deposited with two, three, or more constituents, and such things as graded films and nano-laminates may be produced as well.
These variations are simply variants using particular embodiments of the invention in alternating cycles. There are many other variations within the spirit and scope of the invention, so the invention is limited only by the claims that follow.
For various volatile zinc-containing precursors, precursor combinations, and reactants useful in ALD thin film processes, reference is made to the Handbook of Thin Film Process Technology, Vol. 1, edited by Glocker and Shah, Institute of Physics (IOP) Publishing, Philadelphia 1995, pages B1.5:1 to B1.5:16, hereby incorporated by reference; and Handbook of Thin Film Materials, edited by Nalwa, Vol. 1, pages 103 to 159, hereby incorporated by reference, including Table V1.5.1 of the former reference.
Although oxide substrates provide groups for ALD deposition, plastic substrates can be used by suitable surface treatment.
Referring now to
In one embodiment, gas inlet ports 14 and 16 are adapted to accept first and second gases that react sequentially on the substrate surface to effect ALD deposition, and gas inlet port 18 receives a purge gas that is inert with respect to the first and second gases. Deposition device 10 is spaced a distance D from substrate 20, provided on a substrate support, as described in more detail subsequently. Reciprocating motion can be provided between substrate 20 and deposition device 10, either by movement of substrate 20, by movement of deposition device 10, or by movement of both substrate 20 and deposition device 10. In the particular embodiment shown in
The cross-sectional view of
The cross-sectional views of
As
As mentioned above, in this particular embodiment, there are no vacuum channels interspersed between the output channels 12, that is, no vacuum channels on either side of a channel delivering gaseous materials to drawn the gaseous materials around the partitions. This advantageous, compact arrangement is possible because of the innovative gas flow that is used. Unlike gas delivery arrays of earlier processes that apply substantially vertical (that is, perpendicular) gas flows against the substrate and must then draw off spent gases in the opposite vertical direction, deposition device 10 directs a gas flow (preferably substantially laminar in one embodiment) along the surface for each reactant and inert gas and handles spent gases and reaction by-products in a different manner, as described subsequently. The gas flow used in the present invention is directed along and generally parallel to the plane of the substrate surface. In other words, the flow of gases is substantially transverse to the plane of a substrate rather than perpendicular to the substrate being treated.
The cross-sectional views of
A particular deposition device 10 may use output channels 12 configured using any one of the gas flow configurations or combinations thereof, either the F1 flow of
Exhaust port 26 is not a vacuum port, in the conventional sense, but is simply provided to draw off the gaseous flow in its corresponding output channel 12, thus facilitating a uniform gas flow pattern within the channel. A negative draw, just slightly less than the opposite of the gas pressure at gas output port 24, can help to facilitate an orderly gas flow. The negative draw can, for example, operate at a pressure of between 0.9 and 1.0 atmosphere, whereas a typical vacuum is, for example, below 0.1 atmosphere. An optional baffle 58, as shown in dotted outline in
Because no gas flow around partition 22 to a vacuum exhaust is needed, output face 36 can be positioned very closely, to within about 1 mil (approximately 0.025 mm) of the substrate surface. By comparison, an earlier approach such as that described in the U.S. Pat. No. 6,821,563 to Yudovsky, cited earlier, required gas flow around the edges of channel sidewalls and was thus limited to 0.5 mm or greater distance to the substrate surface. Positioning the deposition device 10 closer to the substrate surface is preferred in the present invention. In a preferred embodiment, distance D from the surface of the substrate can be 0.4 mm or less, preferably within 0.3 mm, more preferably within 0.25 mm of the output face of the deposition device or the bottom of the guide walls that provide the flow channels.
The cross-sectional views of
In order to provide smooth flow along the length of output channel 12, gas output port 24 may be inclined at an angle away from normal, as indicated in
The plan view of
The exploded views of
It is desirable that when a large number of plates are assembled for such an embodiment, the gas flow delivered to the substrate is uniform across all of the channels delivering a particle flow (I, M, or O). This can be accomplished by proper design of the plates, such as having restrictions in some part of the flow pattern for each plate which are accurately machined to provide a reproducible pressure drop for each channel.
Although the method of stacking plates is a particularly useful way of constructing a deposition device for use in this invention, there are a number of other methods to build such structures and may be useful in alternate embodiments of deposition devices that can be used in the present process. For example, the deposition device for use in the present process may be constructed by direct machining of a metal block, or of several metal blocks adhered together. Furthermore, molding techniques involving internal mold features can be employed, as will be understood by the skilled artisan. A deposition device can also be constructed using any of a number of stereolithography techniques.
As can be seen from the example embodiment of
Because gas flow can inadvertently draw ambient gases, due to low-pressure zones that are created, it may be useful to provide additional protection barrier from an inert layer. Referring to
As was particularly described with reference to
Typically, ALD requires multiple deposition cycles, building up a controlled film depth with each cycle. Using the nomenclature for types of gaseous materials given earlier, a single cycle can, for example in a simple design, provide one application of first reactant gaseous material O and one application of second reactant gaseous material M.
The distance between output channels for O and M reactant gaseous materials determines the needed distance for reciprocating movement to complete each cycle. For the example deposition device 10 of
A deposition device 10 may have only enough output channels 12 to provide a single cycle. Alternately, deposition device 10 may have an arrangement of multiple cycles, enabling it to cover a larger deposition area or enabling its reciprocating motion over a distance that allows two or more deposition cycles in one traversal of the reciprocating motion distance.
In one embodiment, a given area of the substrate is exposed to a gas flow in a channel for less than 500 milliseconds, preferably less than 100 milliseconds. The relative movement of the substrate to a channel during oscillation is at a speed of at least 0.1 cm/sec, and the gas flow in the channels is at least 1 cm/sec.
Preferably, the temperature of the substrate during deposition is under 300° C., more preferably under 250° C.
For example, in one particular application, it was found that each O-M cycle formed a layer of one atomic diameter over about ¼ of the treated surface. Thus, four cycles, in this case, are needed to form a uniform layer of 1 atomic diameter over the treated surface. Similarly, to form a uniform layer of 10 atomic diameters in this case, then, 40 cycles would be required.
An advantage of the reciprocating motion used for a deposition device 10 used in one embodiment of the present process is that it allows deposition onto a substrate 20 whose area exceeds the area of output face 36.
In
In a preferred embodiment, ALD can be performed at or near atmospheric pressure and over a broad range of ambient and substrate temperatures, preferably at a temperature of under 300° C. Preferably, a relatively clean environment is needed to minimize the likelihood of contamination; however, full “clean room” conditions or an inert gas-filled enclosure would not be required for obtaining good performance when using preferred embodiments of the process of the present invention.
Optionally, the present process can be accomplished with other apparatus or systems described in more detail in commonly assigned U.S. application Ser. No. 11/392,007; U.S. application Ser. No. 11/392,006; U.S. application Ser. No. 11/620,744; and U.S. application Ser. No. 11/620,740. All above-identified applications incorporated by reference in their entirety.
In the embodiments in the latter three applications, a delivery device having an output face for providing gaseous materials for thin-film material deposition onto a substrate comprises elongated emissive channels in at least one group of elongated emissive channels, of the three groups of elongated emissive channels (namely, at least one group of: (i) one or more first elongated emissive channels, (i) one or more second elongated channels, and (iii) a plurality of third elongated channels) that is capable of directing a flow, respectively, of at least one of the first gaseous material, second gaseous material, and the third gaseous material substantially orthogonally with respect to the output face of the delivery device, which flow of gaseous material is capable of being provided, either directly or indirectly from each of the elongated emissive channels in the at least one group, substantially orthogonally to the surface of the substrate.
In one embodiment, apertured plates are disposed substantially in parallel to the output face, and apertures on at least one of the apertured plates form the first, second, and third elongated emissive channels. In an alternative embodiment, the apertured plates are substantially perpendicularly disposed with respect to the output face.
In one such embodiment, the deposition device comprises exhaust channels, for example, a delivery device for thin-film material deposition of a zinc-oxide-based semiconductor onto a substrate comprising: (a) a plurality of inlet ports comprising at least a first inlet port, a second inlet port, and a third inlet port capable of receiving a common supply for a first reactive gaseous material, a second reactive gaseous material, and a third (inert purge) gaseous material, respectively; (b) at least one exhaust port capable of receiving exhaust gas from thin-film material deposition and at least two elongated exhaust channels, each of the elongated exhaust channels capable of gaseous fluid communication with the at least one exhaust port; and (c) at least three pluralities of elongated output channels, (i) a first plurality of first elongated output channels, (ii) a second plurality of second elongated output channels, and (iii) a third plurality of third elongated output channels, each of the first, second, and third elongated output channels capable of gaseous fluid communication, respectively, with one of the corresponding first inlet port, second inlet port, and third inlet port; wherein each of the first, second, and third elongated output channels and each of the elongated exhaust channels extend in a length direction substantially in parallel; wherein each first elongated output channel is separated on at least one elongated side thereof from a nearest second elongated output channel by a relatively nearer elongated exhaust channel and a relatively less near third elongated output channel; and wherein each first elongated emissive channel and each second elongated emissive channel is situated between relatively nearer elongated exhaust channels and between relatively less nearer elongated emissive channels.
Further embodiments can comprise a gas diffuser associated with at least one group of the three groups of elongated emissive channels such that at least one of the first, second, and third gaseous material, respectively, is capable of passing through the gas diffuser prior to delivery from the delivery device to the substrate, during thin-film material deposition onto the substrate, and wherein the gas diffuser maintains flow isolation of the at least one of first, second, and third gaseous material downstream from each of the elongated emissive channels in the at least one group of elongated emissive channels.
In one embodiment such a gas diffuser is capable of providing a friction factor for gaseous material passing there through that is greater than 1×102, thereby providing back pressure and promoting equalization of pressure where the flow of the at least one first, second and third gaseous material exits the delivery device. In one embodiment of the invention, the gas diffuser comprises a porous material through which the at least one of the first, second, and third gaseous material passes. In a second embodiment of the invention, the gas diffuser comprises a mechanically formed assembly comprising at least two elements comprising interconnected passages, for example, in which nozzles are connected to a flow path provided by a thin space between parallel surface areas in the two elements.
In one embodiment, the one or more of the gas flows from the deposition devices provides a pressure that at least contributes to the separation of the surface of the substrate from the face of the delivery head, thereby providing a “floating head” or “air bearing” type deposition head, which can help to stabilize the gas flows and limit intermixing of the gas flows.
Although deposition only occurs in the areas of the deposition head which exhibit an alternating sequence of reactive gases, practical considerations dictate that a deposition system have sections adjacent to the deposition head to provide an area on which to load and unload a substrate into or out of the coating section, as well as to optionally provide support for portions of the substrate that extend past the deposition area as indicated in the deposition process 60 of
Since the deposition head maintains its proximity to the substrate optionally via a gas bearing effect, it is convenient that the entrance and exit sections also use a similar effect. These sections may have a distribution of gas delivery slots (or more generally, ports) that is very similar to that of the deposition section. In fact, it is possible in some circumstances that the entrance and exit slots be identical to output slots in the deposition region except that they are supplied only with a single gas.
The entrance section 200 and exit section 240 may be supplied with any gas for floatation that does not adversely impact the manufacture and performance of the thin films. In many cases, it may be desirable to use an inert gas as the flotation gas for entrance section 200 and exit section 240. Alternatively, since the substrate is likely to see air before and after deposition, there may be times when cost savings in terms of gas utilization can be achieved by using air as the floatation gas for one or both of these sections.
The entrance section 200 and exit section 240 can optionally use only a single gas supply without additional gas handling considerations. In a preferred embodiment, the non-depositing output faces of the entrance section 200 and exit section 240 have an arrangement of non-depositing output openings 252 supplying gas to the non-depositing output face of the entrance or exit section and an arrangement of gas exhaust ports 254 withdrawing gas from the surface of the non-depositing output face. The use of exhaust ports 254 allows for more robust positioning of the substrate and maintenance of an appropriate gap between the substrate and the non-depositing output face.
As indicated above, for the entrance section 200 and exit section 240 the non-depositing output face may have output openings 252 and exhaust ports 254 that may take the form of slots as envisioned for the deposition or coating sections. However, these openings may be of any convenient shape since containment or separation of gas from one type of opening to another is not required in these sections, as compared to the coating section. Examples of other types of openings would be square, pentagonal, or preferably circular openings, just to name a few.
In the case where the non-depositing output openings 252 and exhaust ports 254 are slots, the preferred arrangement of slots would be to have each exhaust port or channel 254 surrounded on each side by non-depositing output openings 252, and likewise at each non-depositing output opening 252 surrounded on each side by exhaust ports 254. In a preferred embodiment, the openings at the furthest ends of the entrance and exit sections would be non-depositing output openings. In the case where non-depositing output openings 252 and exhaust ports 254 are circular openings, these could be disposed in any manner that provides an alternation of said types of openings. One preferred arrangement would be holes on a square pattern in which each output opening 252 is surrounded by its nearest neighbors with exhaust ports 254, and likewise each exhaust port surrounded by non-depositing output opening 252.
Alternately, the entrance and exit sections could employ porous materials to deliver gases to the non-depositing output face.
The entrance, exit, and coating sections may be maintained at a specified, pre-selected temperature or temperature range, optionally with different temperature set points for each of the sections.
Any manner in which a substrate can be repeatedly exposed to the alternating sequence of gases from the coating head will cause the ALD growth of a film. A reciprocation motion has been envisioned in the prior art for such a growth. However, reciprocating motion involves a complex mechanical system to allow for substrate loading and repeated reversing of substrate direction. A less obvious but still significant problem with the reciprocating motion is that at least a portion of the substrate during it growth must be withdrawn from the deposition area between each stroke, leading to the exposure of the withdrawn regions to a possibly uncontrolled environment.
The present solution to the above problem involves designing the coating or delivery head with enough ALD cycles that a substrate need only make a single pass, or at most a single bi-directional pass, through the coating region in order to receive the required amount of deposition for a particular thin film. It can be seen that in such a configuration, the entire ALD growth at any location on the substrate can be accomplished, in one preferred embodiment, without any need to cause a reversal in direction of the substrate for deposition purposes.
Again with reference to the deposition system 60 of the embodiment of
Another advantage of the above unidirectional motion is simplification of the mechanical systems required for substrate transport. Substrate transport can be accomplished with the use of any sort of device causing linear motion, such as a linear motor driven linear stage, a rotary motor driven linear stage, a belt drive, or any other methods of introducing linear motion as known by a skilled artisan. Non-contact methods to provide movement of the substrate could also be accomplished. Such methods include viscous forces, such as directed gas streams, magnetic, and electrical forces.
Because the system does not require any change in direction of the substrate, and the gas bearing effect produces low friction, travel of the substrate through the deposition zone can also be accomplished by providing the substrate with an initial velocity and then allowing the substrate to glide by its own inertia though the deposition zone, at least to some extent. An initial velocity to the substrate could be imparted by any of the motion methods discussed above.
It is also possible that the substrate velocity be imparted by the effect of gravity. Thus, the coating, entrance, and exit sections may be inclined to allow gravity feed to accomplish part or all of the motion of the substrate. Furthermore, the degree of incline of these sections may be variable mechanically such that during the course of a deposition a stationary substrate could be accelerated by changing the incline of the coating section, entrance section, or exit section from horizontal to some level of incline.
Although a unidirectional single pass deposition system may be preferred for simplicity of substrate transport, a bi-directional system may be preferred for a deposition system with a smaller foot-print. In the case of a bi-directional system, the entrance and exit section would be of similar length to that of the unidirectional system, but the coating section would only need to be half the length, relatively speaking. Again referring to
The coating section 220, entrance section 200, and exit section 240 of the current invention are complex mechanical systems with a high number of internal passageways and depositing output face openings. Often these systems will be constructed of a large number of bonded parts. Furthermore, in order to achieve a single pass deposition, the length of the coating section and number of depositing output face slots can be quite large. For example, a single deposition cycle may require eight elongated slots: Purge—Exhaust—First Reactive Gas—Exhaust—Purge—Exhaust—Second Reactive Gas—Exhaust. If it is assumed that a single deposition cycle produces 1 Å of layer thickness, then to achieve 1000 Å of layer thickness would require 1000 of the above cycles. If we further assume that each of the elongated slots is separated from its neighbor by 0.025 inches, then the total length of the deposition zone would be 16.7 feet. Furthermore, if the entrance section and exit section need to be at some reasonable length to support the substrate, these sections could easily exceed 5 feet in length.
Creating such a large deposition region may be difficult to achieve by creating a single monolithic deposition device. The difficulty arises from several factors. First of all such long heads will be composed of thousands of parts, and a successfully constructed head will require assembling this large number of parts without significant or unacceptable defects. Furthermore, there may be significant problems in mounting and handling a very large head into the overall deposition system. Finally, if the head is damaged in operation, replacing a single large head will be very costly and time consuming.
An alternative to the single large deposition head is to construct the head of independent modules. A module can represent a full section, such as the entrance, exit, or coating section. Alternatively, a given section can be constructed from a number of modules.
In one preferred embodiment, the deposition system can comprise, for example, eight or more modules in the coating section, preferably 10 to 100 modules. Each of such modules can comprises a delivery head that is substantially separately and independently constructed, assembled, and placed in the deposition system.
To understand how the number of modules can impact the yield in constructing the coating section, consider the example of a coating section that is composed of 8000 plates. Assume that, in assembly, there is a defect rate such that in assembling every 200 plates there is a 2% chance of having a defect in the assembly. In assembling this section as modules of 200 plates each, there will be required 40 working modules, and therefore approximately 41 modules will need to be assembled to yield 40 usable modules (approximately 2% wasted work). To attempt a single construction of 8000 plates, the probability of a single construction working is 0.9840=44%. As a result, approximately 2 full coating sections will be required to yield a single working section (approximately 50% wasted work). The present modular aspect in one embodiment of the invention can significantly avoid or reduce that problem.
In a preferred embodiment, the coating, entrance, and exit sections of the present invention all operate with a gas bearing effect. As such, the separation between the substrate and the deposition device can be very small, sometimes as low as 10 microns. It is therefore very important that the depositing output faces of sections have surfaces free of discontinuities. In a modular configuration, the modules of a section, illustrated with the coating section of
There are a number of ways to achieve a suitable height positioning of the modules. The modules can individually be mounted upon a position adjusting means and upon installation of a given module, the position adjusting means can be used to adjust the height of the depositing output face to some desired position. Examples of height adjusting means are rotary micrometer positioners, piezoelectric positioners, and other means known in the art.
Often it is desired to coat a thin film consisting of a single material. There are however desirable thin films in which a complete film containing a number of layers of different materials can be useful. It is possible in the case of a modular coating section that a plurality of modules within the coating section are capable of delivering the different gases, thus not all modules produce the same coatings.
The process of the present invention is advantaged in its capability to perform deposition onto a substrate over a broad range of temperatures, including room or near-room temperature in some embodiments. The process of the present invention can operate in a vacuum environment, but is particularly well suited for operation at or near atmospheric pressure.
The production of thin film transistors and electronic devices from the ALD deposited semiconductor, dielectric, conductive and protective materials can be accomplished by conventional techniques known to the skilled artisan. In one embodiment, a substrate is provided, a film or layer of the active material as described above can be applied to the substrate, and electrical contacts made to the layer. The exact process sequence is determined by the structure of the desired transistor. Thus, in the production of a field effect transistor, for example, a gate electrode can be first deposited on a substrate, for example a vacuum or solution deposited metal or organic conductor, or an ALD deposited conductor. The gate electrode can then be insulated with a dielectric and then source and drain electrodes and a layer of the n-channel semiconductor material can be applied on top. The structure of such a transistor and hence the sequence of its production can be varied in the customary manner known to a person skilled in the art. Thus, alternatively, a gate electrode can be deposited first, followed by a gate dielectric, then the semiconductor can be applied, and finally the contacts for the source electrode and drain electrode deposited on the semiconductor layer. A third structure could have the source and drain electrodes deposited first, then the semiconductor, with dielectric and gate electrode deposited on top.
The skilled artisan will recognize other structures can be constructed and/or intermediate surface modifying layers can be interposed between the above-described components of the thin film transistor. In most embodiments, a field effect transistor comprises an insulating layer, a gate electrode, a semiconductor layer comprising a ZnO material as described herein, a source electrode, and a drain electrode, wherein the insulating layer, the gate electrode, the semiconductor layer, the source electrode, and the drain electrode are in any sequence as long as the gate electrode and the semiconductor layer contact opposite sides of the insulating layer, and the source electrode and the drain electrode both contact the semiconductor layer.
Techniques for fabricating these structures include selective deposition, sequential masking, photolithography, laser, and/or other means known to the skilled artisan.
A thin film transistor (TFT) is an active device, which is the building block for electronic circuits that switch and amplify electronic signals. Attractive TFT device characteristics include a high ratio of the on current to the off current, and a steep subthreshold slope. In the operation of such a TFT device, a voltage applied between the source and drain electrodes establishes a substantial current flow only when the control gate electrode is energized. That is, the flow of current between the source and drain electrodes is modulated or controlled by the bias voltage applied to the gate electrode. The relationship between material and device parameters of the zinc-oxide-based semiconductor TFT can be expressed by the approximate equation (see Sze in Semiconductor Devices—Physics and Technology, John Wiley & Sons (1981)):
where Id is the saturation source-drain current, C is the geometric gate capacitance, associated with the insulating layer, W and L are physical device dimensions, μ is the carrier (hole or electron) mobility in the zinc-oxide-based semiconductor, and Vg is the applied gate voltage, and Vth is the threshold voltage. Ideally, the TFT allows passage of current only when a gate voltage of appropriate polarity is applied. However, with zero gate voltage, the “off” current between source and drain will depend on the intrinsic conductivity σ of the zinc-oxide-based semiconductor,
σ=nqμ
where n is the charge carrier density and q is the charge, so that
(Isd)=σ(Wt/L)Vsd@Vg=0
wherein t is the zinc-oxide-based semiconductor layer thickness and Vsd is the voltage applied between source and drain. Therefore, for the TFT to operate as a good electronic switch, e.g. in a display, with a high on/off current ratio, the semiconductor needs to have high carrier mobility but very small intrinsic conductivity, or equivalently, a low charge carrier density. On/off ratios >104 are desirable for practical devices.
The TFT structure described herein includes a metal-oxide-based semiconductor or channel with conducting electrodes, commonly referred to as a source and a drain, for injecting a current into the semiconductor and a capacitance charge injection scheme for controlling and/or modulating the source-drain current. One particularly attractive application of metal-oxide-based semiconductor TFT's is in the drive circuits for displays on flexible, polymer substrates. Metal oxide semiconductor transistors and/or transistor arrays are useful in applications including, but not limited to, flat panel displays such as active matrix imagers, sensors, rf price labels, electronic paper systems, rf identification tags and rf inventory tags.
The present invention is preferably used for making an “enhancement-mode transistor” which means a transistor in which there is negligible off-current flow, relative to on-current flow, between a source and a drain at zero gate voltage. In other words, the transistor device is “normally off.” (In contrast, a depletion-mode transistor is “normally on” meaning that more than a substantially negligible current flows between a source and a drain at zero gate voltage. Enhancement-mode devices are typically preferred.)
Turning now to
Described in the embodiments of
Cross-sectional views of typical deposited thin film transistors are shown in
Each thin film transistor (TFT) in the embodiments of
The off current is defined as the current flowing between the source electrode 120 and the drain electrode 130 when charge has not been intentionally injected into the channel by the application of a gate voltage. This occurs for a gate-source voltage more negative, assuming an n-channel, than a certain voltage known as the threshold voltage. See Sze in Semiconductor Devices—Physics and Technology, John Wiley & Sons (1981), pages 438-443. The on current is defined as the current flowing between the source electrode 120 and the drain electrode 130 when charge carriers have been accumulated intentionally in the channel by application of an appropriate voltage to the gate electrode 144, and the channel is conducting. For an n-channel accumulation-mode TFT, this occurs at gate-source voltage more positive than the threshold voltage. It is desirable for this threshold voltage to be zero, or slightly positive, for n-channel operation. Switching between on and off is accomplished by the application and removal of an electric field from the gate electrode 144 across the gate dielectric 156 to the semiconductor-dielectric interface, effectively charging a capacitor.
The specific examples of transistor configurations described herein are for illustrative purposes and should not be considered as limiting the scope of the appended claims. For example, a further (third) specific transistor structure is shown in
Yet a fourth variation of a TFT structure is shown in
The TFT structure of
Alternatively, the contacts in the above configuration of
A support for supporting the TFT during manufacturing, testing, and/or use can include organic or inorganic materials. For example, the support may comprise inorganic glasses, ceramic foils, polymeric materials, filled polymeric materials, coated metallic foils, acrylics, epoxies, polyamides, polycarbonates, polyimides, polyketones, poly(oxy-1,4-phenyleneoxy-1,4-phenylenecarbonyl-1,4-phenylene) (sometimes referred to as poly(ether ether ketone) or PEEK), polynorbornenes, polyphenyleneoxides, poly(ethylene naphthalenedicarboxylate) (PEN), poly(ethylene terephthalate) (PET), poly(ether sulfone) (PES), poly(phenylene sulfide) (PPS), and fiber-reinforced plastics (FRP). Flexible substrates can also be thin metal foils such as stainless steel provided they are coated with an insulating layer to electrically isolate the thin film transistor. A flexible support, in some embodiments of the present invention, allows for roll processing, which may be continuous, providing economy of scale and economy of manufacturing over flat and/or rigid supports. The flexible support chosen preferably is capable of wrapping around the circumference of a cylinder of less than about 50 cm diameter, more preferably 25 cm diameter, most preferably 10 cm diameter, without distorting or breaking, using low force as by unaided hands. The preferred flexible support may be rolled upon itself. However, if flexibility is not a concern, then the substrate may be a wafer or sheet made of materials including glass and silicon. The thickness of the substrate may vary, and according to particular examples it can range from about 100 μm to about 1 cm.
In some embodiments of the invention, the support may be optional. For example, in a top construction as in
The gate electrode can be any useful conductive material. A variety of gate materials known in the art, are also suitable, including metals, degenerately doped semiconductors, conducting polymers, and printable materials such as carbon ink, silver-epoxy, or sinterable metal nanoparticle suspensions. For example, the gate electrode may comprise doped silicon, or a metal, such as aluminum, chromium, gold, silver, nickel, copper, tungsten, palladium, platinum, tantalum, and titanium. Gate electrode materials can also include transparent conductors such as indium-tin oxide (ITO), ZnO, SnO2, or In2O3. Conductive polymers also can be used, for example polyaniline, poly(3,4-ethylenedioxythiophene)/poly(styrene sulfonate) (PEDOT:PSS). In addition, alloys, combinations, and multilayers of these materials may be useful. In a preferred embodiment of the present invention the gate electrode comprises a conducting oxide or metal and is deposited by the same ALD method used to deposit the semiconducting layer.
The thickness of the gate electrode may vary, and according to particular examples it can range from about 50 to about 1000 nm. The gate electrode may be introduced into the structure by chemical vapor deposition, sputtering, evaporation and/or doping, or solution processing.
The same material can provide the gate electrode function and also provide the support function of the support. For example, doped silicon can function as the gate electrode and support the TFT.
The gate dielectric is provided in contact with the gate electrode. This gate dielectric electrically insulates the gate electrode from the balance of the TFT device. Thus, the gate dielectric comprises an electrically insulating material. The gate dielectric should have a suitable dielectric constant that can vary widely depending on the particular device and circumstance of use. For example, a dielectric constant from about 2 to 100 or even higher is known for a gate dielectric. Useful materials for the gate dielectric may comprise, for example, an inorganic electrically insulating material. The gate dielectric may comprise a plurality of layers of different materials having different dielectric constants.
Specific examples of materials useful for the gate dielectric include strontiates, tantalates, titanates, zirconates, aluminum oxides, silicon oxides, tantalum oxides, titanium oxides, silicon nitrides, barium titanate, barium strontium titanate, barium zirconate titanate, zinc selenide, and zinc sulfide. In addition, alloys, combinations, and multilayers of these examples can be used for the gate dielectric. Of these materials, aluminum oxides, silicon oxides, and zinc selenide are preferred. The gate dielectric is preferably deposited by the same ALD method used to deposit the semiconducting layer. The gate dielectric can be provided in the TFT as a separate layer, or formed on the gate such as by oxidizing the gate material to form the gate dielectric. The dielectric layer may comprise two or more layers having different dielectric constants. Such insulators are discussed in U.S. Pat. No. 5,981,970, hereby incorporated by reference and copending US Application Publication No. 2006/0214154, hereby incorporated by reference. Gate insulator materials typically exhibit a band-gap of greater than about 5 eV.
The thickness of the gate insulator layer may vary, and according to particular examples it can range from about 10 to about 300 nm. The gate dielectric layer may be introduced into the structure by techniques such as chemical vapor deposition, sputtering, atomic layer deposition, or evaporation, solution.
Source/drain terminals refer to the terminals of a TFT, between which conduction occurs under the influence of an electric field. Designers often designate a particular source/drain terminal to be a “source” or a “drain” on the basis of the voltage to be applied to that terminal when the TFT is operated in a circuit.
The source electrode and drain electrode are separated from the gate electrode by at least the gate dielectric, while the zinc-oxide-based semiconductor layer can be over or under the source electrode and drain electrode. The source and drain electrodes can be any useful conductive material. Useful materials include most of those materials described above for the gate electrode, for example, aluminum, barium, calcium, chromium, gold, silver, nickel, palladium, platinum, titanium, copper, tungsten, polyaniline, PEDOT:PSS, other conducting polymers, alloys thereof, combinations thereof, and multilayers thereof. Other illustrative materials include transparent, n-type conductors such as indium-tin oxide (ITO), ZnO, SnO2, or In2O3. Preferred electrodes are silver, gold, PEDOT:PSS, or aluminum.
The source electrode and drain electrode can be provided by any useful means such as chemical or physical vapor deposition (e.g., thermal evaporation, sputtering), evaporation, ink jet printing, or doping of the semiconductor channel layer material via diffusion or ion implantation and solution deposition. In a preferred embodiment of the present invention the source and drain electrodes comprise a conducting oxide or metal and are deposited by the same ALD method used to deposit the semiconductor layer. Patterning of these electrodes can be accomplished by known methods such as shadow masking, additive photolithography, subtractive photolithography, printing, microcontact printing, and pattern coating. The source and drain terminals may be fabricated such that they are geometrically symmetrical or non-symmetrical.
Electrical contact to the gate electrode, source, drain and substrate may be provided in any manner. For example, metal lines, traces, wires, interconnects, conductors, signal paths, and signaling mediums may be used for providing the desired electrical connections. The related terms listed above, are generally interchangeable, and appear in order from specific to general. Metal lines, generally aluminum (Al), copper (Cu), or an alloy of Al and Cu, are typical conductors that provide signal paths for coupling or interconnecting, electrical circuitry. Conductors other than metal may also be utilized.
In cases where another layer covers the electrical contact of interest, connection to the electrical contact can be made by creating a “via” that penetrates to the contact. Such vias can be made by convenient patterning operations such as lithography, etching, or laser based processes.
An illustrative n-channel operation of the transistor involves applying a positive voltage to the gate electrode, grounding the source, and applying a positive voltage to the drain. For example, a voltage of about 5 to about 40 V may be applied to the gate electrode and the drain during operation. The threshold voltage may range from about—minus 10 to about 20 V, although devices can operate with larger ranges. Electrons flow from the source, along the semiconductor thin film, and out of the transistor through the drain. The effective mobility of the electrons may vary depending upon the specific structure, but typically should be greater than 0.01 cm 2V−1s−1 for useful practical applications. Simply by removing the positive voltage applied to the gate electrode turns the transistor off when the transistor is an enhancement-mode transistor.
Electronic devices in which TFTs and other devices are useful include, for example, more complex circuits, e.g., shift registers, integrated circuits, logic circuits, smart cards, memory devices, radio-frequency identification tags, backplanes for active matrix displays, active-matrix displays (e.g. liquid crystal or OLED), solar cells, ring oscillators, and complementary circuits, such as inverter circuits, for example, in combination with other transistors made using available p-type organic semiconductor materials such as pentacene. In an active matrix display, a transistor according to the present invention can be used as part of voltage hold circuitry of a pixel of the display. In devices containing the TFTs, such TFTs are operatively connected by means known in the art.
One example of a microelectronic device is an active-matrix liquid-crystal display (AMLCD). One such device is an optoelectronic display that includes elements having electrodes and an electro-optical material disposed between the electrodes. A connection electrode of the transparent transistor may be connected to an electrode of the display element, while the switching element and the display element overlap one another at least partly. An optoelectronic display element is here understood to be a display element whose optical properties change under the influence of an electrical quantity such as current or voltage such as, for example, an element usually referred to as liquid crystal display (LCD). The presently detailed transistor has sufficient current carrying capacity for switching the display element at such a high frequency that the use of the transistor as a switching element in a liquid crystal display is possible. The display element acts in electrical terms as a capacitor that is charged or discharged by the accompanying transistor. The optoelectronic display device may include many display elements each with its own transistor, for example, arranged in a matrix. Certain active matrix pixel designs, especially those supplying a display effect that is current driven, may require several transistors and other electrical components in the pixel circuit.
One specific example of a basic AMLCD cell circuit is depicted in
All of the following thin film examples employ a flow setup as indicated in
The following flows are delivered to the ALD coating apparatus: metal (zinc) precursor flow 92 containing metal precursors diluted in nitrogen gas; oxidizer-containing flow 93 containing non-metal precursors or oxidizers diluted in nitrogen gas; nitrogen purge flow 95 composed only of the inert gas. The composition and flows of these streams are controlled as described below.
Gas bubbler 82 contains diethylzinc. Gas bubbler 83 contains trimethylaluminum. Both bubblers are kept at room temperature. Flow meters 85 and 86 deliver flows of pure nitrogen to the diethylzinc bubbler 82 and trimethylaluminum bubbler 83, respectively. The output of the bubblers now contain nitrogen gas saturated with the respective precursor solutions. These output flows are mixed with a nitrogen gas dilution flow delivered from flow meter 87 to yield the overall flow of metal precursor flow 92. In the following examples, the flows will be as follows:
Gas bubbler 84 contains pure water for the control (or ammonia in water for the inventive example) at room temperature. Flow meter 88 delivers a flow of pure nitrogen gas to gas bubbler 84, the output of which represents a stream of saturated water vapor. An airflow is controlled by flow meter 91. The water bubbler output and air streams are mixed with dilution stream from flow meter 89 to produce the overall flow of oxidizer-containing flow 93 which has a variable water composition, ammonia composition, oxygen composition, and total flow. In the following examples, the flows will be as follows:
Flow meter 94 controls the flow of pure nitrogen that is to be delivered to the coating apparatus.
Streams or Flows 92, 93, and 95 are then delivered to an atmospheric pressure coating head where they are directed out of the channels or microchamber slots as indicated in
In order to perform a deposition, the coating head is positioned over a portion of the substrate and then moved in a reciprocating fashion over the substrate, as represented by the arrow 98. The length of the reciprocation cycle was 32 mm. The rate of motion of the reciprocation cycle is 30 mm/sec.
The following characterization is used:
Transistor characterization of the devices fabricated using the present invention was performed with a Hewlett Packard HP 4156 parameter analyzer. Device testing was done in air in a dark enclosure.
The results were typically averaged from several devices. For each device, the drain current (Id) was measured as a function of source-drain voltage (Vd) for various values of gate voltage (Vg). Furthermore, for each device the drain current was measured as a function of gate voltage for various values of source-drain voltage. For most devices, Vg was swept from −10 V to 20 V with the drain voltage held at 20V.
Parameters extracted from the data include field-effect mobility (μ), threshold voltage (Vth), and the ratio of Ion/Ioff for the measured drain current. These measurements can be taken without any protective film on the semiconductor thin film, yielding substantially the same results with or without the protective film. The field-effect mobility was extracted in the saturation region, where Vd>Vg−Vth. In this region, the drain current is given by the equation (see Sze in Semiconductor Devices—Physics and Technology, John Wiley & Sons (1981)):
where, W and L are the channel width and length, respectively, and Cox is the capacitance of the dielectric layer, which is a function of dielectric thickness and dielectric constant of the material. Given this equation, the saturation field-effect mobility was extracted from a straight-line fit to the linear portion of the √Id versus Vg curve. The threshold voltage, Vth, is the x-intercept of this straight-line fit.
The log of the drain current as a function of gate voltage was plotted. Parameters extracted from the log Id plot include the Ion/Ioff ratio. The Ion/Ioff ratio is simply the ratio of the maximum to minimum drain current. For the purpose of the claimed invention, the on/off ratio is measured by the ratio of the on current, defined as the drain current at a gate voltage of 10 V in excess of the threshold voltage, to the off current, defined as the drain current at a gate voltage for which the transistor is in an off state. The measurements in the present examples were taken in excess of 10V which would result in minor changes to the measurement.
(1) Conductive ITO substrate (100 nm thick on soda lime glass, commercially available from MBC, product #255.
(2) Me3Al (commercially available from Aldrich Chemical Co.).
(3) Et2Zn (commercially available from Aldrich Chemical Co.).
(4) Ammonium Hydroxide [aqueous ammonia], (reagent grade, ˜29 weight % ammonia, commercially available from J. T. Baker Chemical Co.).
The purpose of this example was to prepare a TFT device with dielectric, semiconductor, and protection layers prepared by the ALD coating apparatus described above. This thin film transistor device (TFT) is comprised of a glass substrate, an ITO (indium tin oxide) gate electrode, a 1100 Å thick Al2O3 dielectric layer, a 200 Å thick ZnO layer, evaporated Al metal source/drain electrodes, and a 200 Å Al2O3 protection layer. The device used to prepare the Al2O3 and ZnO layers has been described in detail in
The coating head has isolated channels through which flow: (1) inert nitrogen gas; (2) a mixture of nitrogen, and water vapor; and (3) a mixture of active metal alkyl vapor (Me3Al or Et2Zn) in nitrogen. The flow rate of the active metal alkyl vapor was controlled by bubbling nitrogen through the pure liquid (Me3Al or Et2Zn) contained in an airtight bubbler by means of individual mass flow control meters. The flow of water vapor was controlled by adjusting the bubbling rate of nitrogen passed through pure water in a bubbler. The temperature of the coating head was maintained at 40° C. Adjusting the flow rates of the individual gasses to the settings shown in Table 1 below, the coating process was initiated by oscillating the coating head across the substrate for the number of cycles specified. Electrical test results for the above device (sample 1) having ITO gate electrode and ALD-coated dielectric, semiconductor and protective layers are shown below in Table 2.
The purpose of this example was to prepare a TFT device that had a transparent, conductive gate electrode of In-doped ZnO prepared by the same ALD coating system used for the dielectric and semiconductor layers. The devices had the following cross sectional composition: glass substrate/In-doped ZnO gate electrode/Al2O3 dielectric/ZnO semiconductor/Al source and drain electrodes. The In-doped ZnO gate electrode, layer 7A, was prepared as for the ZnO semiconductor layer, except that a flow of trimethylindium vapor is added to the flow of diethyl zinc at a flow rate of 40 sccm, and the layer was grown to approximately 2000 Å thick. The resistivity of the In-doped ZnO gate electrode layer was measured to be 3.3E-02 ohm*cm. An Al2O3 dielectric layer (7B) and a ZnO semiconductor layer (7C) were then coated onto the top of layer 7A using the settings specified in Table 1. Aluminum source and drain contacts were evaporated onto the top of layer 7C through a shadow mask, yielding thin film transistors with channel lengths of 50, 100 or 150 μm and a channel width of 600 μm. A photolithographic process was used to isolate devices on the substrate, producing islands of ZnO. Electrical test results for the above device (sample 2) having the In-doped ZnO gate electrode are shown below in Table 2.
The purpose of this example was to prepare a TFT device that had a transparent, conductive gate electrode of In-doped ZnO prepared by the same ALD coating system used for the dielectric, semiconductor, and protection layers. The devices had the following cross sectional composition: glass substrate/In-doped ZnO gate electrode/Al2O3 dielectric/ZnO semiconductor/Al source and drain electrodes/Al2O3 protection layer. The sample was prepared as for Example 2 and electrically tested, and subsequently the protective layer was applied using the ALD coating system and the conditions listed for the protection layer in Table 1 above. The sample was then electrically tested again. Electrical test results for the above device (sample 3) having the In-doped ZnO gate electrode are shown below in Table 2 and are compared to a those of sample 2, which was identical except that it had no protection layer.
The data in Table 2 demonstrate that the devices all function well as field effect transitors, with mobility of order 5 cm2/Vs and current on/off ratios in excess of 1×107. The data for samples 2 and 3 show in addition that the InZnO layer produced on the atmospheric pressure atomic layer deposition device in this work is sufficiently conductive so that it functions well as a gate electrode in a TFT device.
The present application is related to U.S. application Ser. No. 11/392,007, filed Mar. 29, 2006 by Levy and entitled, “PROCESS FOR ATOMIC LAYER DEPOSITION,” U.S. application Ser. No. 11/392,006, filed Mar. 29, 2006 by Levy and entitled “APPARATUS FOR ATOMIC LAYER DEPOSITION,” U.S. application Ser. No. 11/620,738, filed Jan. 8, 2007 by Levy and entitled “DELIVERY DEVICE FOR DEPOSITION,” U.S. application Ser. No. 11/620,740, filed Jan. 8, 2007 by Nelson et al. and entitled “DELIVERY DEVICE COMPRISING GAS DIFFUSER FOR THIN FILM DEPOSITION,” U.S. application Ser. No. 11/620,744, filed Jan. 8, 2007 by Levy and entitled, “DEPOSITION SYSTEM AND METHOD USING A DELIVERY HEAD SEPARATED FROM A SUBSTRATE BY GAS PRESSURE,” U.S. application Ser. No. ______ (docket 93187), filed Jan. 26, 2007 by Peter Cowdery-Corvan et al. and entitled, “PROCESS FOR ATOMIC LAYER DEPOSITION,” U.S. application Ser. No. ______ (docket 94077), filed concurrently herewith by Kerr et al. and entitled, “DEPOSITION SYSTEM FOR THIN FILM FORMATION,” U.S. application Ser. No. ______ (docket 94217), filed concurrently herewith by Kerr et al. and entitled “DELIVERY DEVICE FOR DEPOSITION,” and US. application Ser. No. ______ (docket 94079), filed concurrently herewith by Levy et al. and entitled, “SYSTEM FOR THIN FILM DEPOSITION UTILIZING COMPENSATING FORCES,” all the above identified applications incorporated by reference in their entirety.