Process for growing a film epitaxially upon a MgO surface

Abstract

A process and structure wherein optical quality perovskites, such as BaTiO.sub.3 or SrTiO.sub.3, are grown upon a single crystal MgO substrate involves the epitaxial build up of alternating planes of TiO.sub.2 and metal oxide wherein the first plane grown upon the MgO substrate is a plane of TiO.sub.2. The layering sequence involved in the film build up reduces problems which would otherwise result from the interfacial electrostatics at the first atomic layers, and these oxides can be stabilized as commensurate thin films at a unit cell thickness or grown with high crystal quality to thicknesses of 0.5-0.7 .mu.m for optical device applications.

Description

BACKGROUND OF THE INVENTION

This invention relates generally to the preparation of structures for use in semiconductor and/or optical wave guide applications and relates, more particularly, to the growth of an epitaxial film upon a MgO surface.

Oxides in a class of oxides known as perovskites are known to exhibit technologically-significant properties, such as ferroelectricity, piezoelectricity, superconductivity and nonlinear electro-optic behavior, and for this reason, are grown upon substrates for the purpose of incorporating these properties within electronic devices. Of these electronic devices, optical guided wave (OGW) devices constructed with perovskites are relatively demanding from the standpoint of optical clarity and necessarily require long range structural coherence. Heretofore, the optical clarity and structural coherence of a perovskite film grown upon MgO has been limited due, at least in part, to the inability to grow a perovskite upon MgO wherein the grown perovskite is of a single orientation. It would be desirable to provide a process for growing perovskite of single-orientation upon MgO and thus enhance the quality of the resulting structure for OGW applications.

Accordingly, an object of the present invention is to provide a new and improved process for growing a perovskite of single orientation on MgO and a structure formed with the process.

Another object of the present invention is to provide such a process which is well-suited for coating a MgO surface with a single layer of TiO.sub.2, which layer provides a plane of a perovskite crystal.

SUMMARY OF THE INVENTION

This invention resides in a process for coating a body having a MgO surface with an epitaxial film wherein the film includes crystalline constituents of a perovskite and a structure formed by the process.

The process includes the steps of growing, by molecular beam epitaxy (MBE) techniques, a single plane of TiO.sub.2 upon the MgO surface so that the TiO.sub.2 of the single layer is disposed at ordered sites across the MgO surface. In a further embodiment of the method, the step of growing a single plane of TiO.sub.2 is followed by the step of growing, by MBE techniques, a single layer of metal oxide upon the TiO.sub.2 layer. The metal oxide grown in this step is one oxide of a group of oxides consisting of BaO, SrO, CaO and MgO.

In a still further embodiment of the process, the growth of the single plane of metal oxide is followed by the sequential steps of growing an epitaxial plane of TiO.sub.2 directly upon the previously-grown plane of metal oxide and growing an epitaxial plane of metal oxide directly upon the previously-grown plane of TiO.sub.2.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of a body upon which an epitaxial perovskite can be grown in accordance with the method of the present invention.

FIG. 2 is an exploded perspective view of a structure within which a film of perovskite is grown upon a layer of MgO and illustrating schematically the successive layers of constituents comprising the structure.

FIG. 3 is a schematic perspective view of ultra high vacuum equipment with which steps of the present invention may be performed.

FIG. 4 is a SEM micrograph image of a cross section of a BaTiO.sub.3 film of 0.6 .mu.m thickness epitaxially grown upon MgO(001).

FIG. 5 is a cube model representing the lattice orientation at the interface of a structure wherein an MgO surface is covered with BaO.

FIG. 6a is a photograph providing RHEED data for a clean MgO surface wherein the data is obtained along a �100! zone axis.

FIG. 6b is a photograph providing RHEED data for a single layer coverage of BaO on (001)MgO wherein the data is obtained along a �100! zone axis.

FIG. 7a is a photograph (like that of FIG. 6a) providing RHEED data for a clean MgO surface wherein the data is obtained along a �100! zone axis.

FIG. 7b is a photograph providing RHEED data for one monolayer coverage of TiO.sub.2 on MgO(001) wherein the data is obtained along the �100! zone axis.

FIG. 8a is a plan view of a ball model of a clean MgO surface.

FIG. 8b is a plan view of a ball model of a one monolayer coverage of TiO.sub.2 on MgO(001).

FIG. 9 is a table providing in-plane and out-of-plane structure data and index of refraction data for SrTiO.sub.3 and BaTiO.sub.3 thin films on MgO.

FIG. 10 is a graph providing data relating to wavelength dependence of optical loss in thin film SrTiO.sub.3 on MgO.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

Turning now to the drawings in greater detail, there is shown in FIG. 1 a body or wafer 20 having a surface 22 defined by substrate layer of magnesium oxide, i.e. the (001) face, upon which a perovskite of single-orientation can be grown. In the interests of the present invention, the surface layer of MgO can be provided by the outer layer of a body comprised entirely of MgO or the outer layer of a series of layers formed upon a base substrate comprised, for example, of silicon. In either instance, however, the crystalline structure of the MgO layer is clean, ordered and atomically smooth to promote the subsequent epitaxial growth thereupon of constituents of a perovskite crystal.

The crystalline lattice structure of perovskite is a simple cubic structure and includes a plane of TiO.sub.2 and a plane of metal oxide. For example, the crystalline lattice structure of the perovskite BaTiO.sub.3 includes a plane of TiO.sub.2 and a plane of BaO. Similarly, the bulk crystalline structure of the perovskite SrTiO.sub.3 includes a plane of TiO.sub.2 and a plane of SrO. As will be apparent herein, the process of the invention involves the initial formation of a plane of TiO.sub.2 upon the MgO surface and the subsequent formation of additional planes of metal oxide and TiO.sub.2 upon the initial plane of TiO.sub.2 so that the subsequently-formed planes alternate with one another.

With reference to FIG. 2, there is illustrated a structure, indicated 24, upon which alternating planes 26 and 28 of TiO.sub.2 and metal oxide, respectively, are formed upon the MgO surface 22. Each plane 26 or 28 is formed upon the MgO surface 22 by molecular beam epitaxy (MBE) techniques and with MBE equipment. Briefly, the MBE equipment with which the process described herein can be carried out includes an ultra high vacuum (UHV) growth/characterization facility, a fragment of which is indicated 30 in FIG. 3. The facility 30 includes a container 32 having an inner chamber within which the body 20 is positioned so that its surface 22 faces downwardly, and a plurality of canisters 34, 36 and 38 are provided within the base of the container 32 for providing a vapor source of metal desired to be added to the substrate surface during the formation of the structure 24. In this connection, each canister 34, 36 and 38 is adapted to hold a crucible containing a desired metal, and in this case, the canisters hold metal constituents of the perovskite, e.g., BaTiO.sub.3, SrTiO.sub.3, CaTiO.sub.3 or MgTiO.sub.3, desired to be formed upon the MgO surface 24.

An opening is provided in the top of each canister, and a shutter is associated with the canister opening for movement between a closed condition at which the interior of the canister is closed and thereby isolated from the MgO surface 22 and a closed condition at which the contents of the container 32, i.e., the metal vapor, is exposed to the MgO surface 22. In addition, an oxygen source 40 is connected to the chamber so that by opening and closing a valve associated with the source 40, oxygen can be delivered to or shut off from the chamber. The opening and closing of each canister shutter and the oxygen source valve is accurately controlled by a computer controller (not shown).

Before the desired layers, or planes, are grown upon the MgO surface 22, the MgO surface is rendered atomically smooth. To this end, the MgO surface 22 can be treated with a polishing compound which is commercially available as a cleaner under the trade designation Syton. The body 20 is then placed within the UHV facility 30, and the temperature of the body 20 is raised to about 1000.degree. C. At this elevated temperature, unwanted contaminants, such as water and dirt, are driven from the surface 22 and Mg ions which may be under strain at the surface 22 are permitted to shift to a more stable, or relieved, position. While maintaining suitable control over the operation of the MBE facility 30, MgO is grown onto the surface 22 to restore crystalline perfection at the MgO surface as MgO is deposited within so as to fill voids or similar defects which may exist across the surface 22. By growing an additional thickness of about 1000 .ANG. of Mg onto the surface 22, the desired cleanliness and smoothness of the surface 22 is obtained.

In preparation of the growth of TiO.sub.2 onto the MgO surface 22, the pressure in the UVH chamber is lowered to between about 2-5.times.10.sup.-7 torr. The desired layer of TiO.sub.2 is then built upon the MgO surface 22 by conventional MBE techniques while the chamber pressure is maintained between about 2-5.times.10.sup.-7 torr. For example, Ti metal vapor could initially be deposited upon the MgO surface 22 and then oxygen from the source 40 could be released over the surface so that the desired layer of TiO.sub.2 is formed at the surface 22. Alternatively, the surface 22 could be simultaneously exposed to Ti vapor and oxygen, in controlled amounts, so that TiO.sub.2 forms and then accumulates on the surface 22.

During either of the aforementioned deposition processes involving the TiO.sub.2 layer, careful control of the MBE operation is maintained to ensure that no more than one layer, i.e., one plane, of TiO.sub.2 is deposited upon the surface 22. The bulk form of the compound TiO.sub.2, as characterized by the ordered surface structure formed in this step, has a nonequilibrium structure and is not found in nature, and there exists a tendency for the formed TiO.sub.2 to accumulate into clusters if the surface 22 is exposed to a greater amount of TiO.sub.2 than is needed to comprise a single plane of TiO.sub.2. Of course, if such clusters develop, the TiO.sub.2 layer looses its order, and the ability to grow ordered layers upon the TiO.sub.2 layer is destroyed. Thus, careful control must be maintained over the deposition of Ti vapor and the release of oxygen from the source 40 so that a single layer, and only a single layer, of TiO.sub.2 accumulates at ordered sites upon the MgO surface 22.

Following the development of the desired layer of TiO.sub.2 upon the MgO surface 22, a layer of metal oxide which comprises the other plane of the desired perovskite is formed upon the TiO.sub.2 layer. If, for example, the desired perovskite is BaTiO.sub.3, then the vapor released in the facility chamber is Ba, and if the desired perovskite is SrTiO.sub.3, then the vapor released into the chamber facility is Sr.

Conventional MBE techniques are used to grow the desired oxide, e.g., BaO or SrO, layer upon the formed TiO.sub.2 layer. For example, the metal vapor, e.g., Ba or Sr, may be initially deposited upon the TiO.sub.2 surface, and then the oxygen may be subsequently released into the chamber so that the metal oxide forms upon the TiO.sub.2 surface. Alternatively, the TiO.sub.2 layer could be simultaneously exposed to metal vapor and oxygen so that the metal oxide accumulates on the TiO.sub.2 layer. In either event, careful control should be maintained over the deposition operation here so that no more than one plane of the desired metal oxide is developed at this stage upon the TiO.sub.2 layer and so that the pattern of metal oxide deposited upon the TiO.sub.3 layer is ordered.

Upon formation of the desired plane of metal oxide, a second plane of TiO.sub.2 is grown upon the metal oxide plane in accordance with the aforedescribed techniques used to grow TiO.sub.2 onto the MgO surface. Then, upon formation of the desired second plane of TiO.sub.2, a second plane of the metal oxide, e.g., BaO or SrO, is grown upon the second plane of TiO.sub.2.

Thereafter, layers of TiO.sub.2 and metal oxide are formed in an alternating fashion until at least about twenty-five cell units of the desired perovskite are grown upon the MgO surface. Dislocations which may develop within the formed layers nucleate so as to provide internal strain relief within the first twenty-five cell units so that lattice strain does not appear at the surface of the layup of planes. Thus, the surface defined by the twenty-fifth cell unit is ordered and free of strain.

Once the strain-free surface of perovskite is formed, steps can then be taken to grow addition layers of the perovskite upon the build up of cell units. In this connection, subsequent growth of the perovskite upon its strain-free bulk form is homoepitaxial, rather than heteroepitaxial so that the characteristics of the interface between adjacent layers of TiO.sub.2 and metal oxide are not likely to present problems during growth. Thus, the perovskite can be built upon itself after the initial twenty-five cell units of perovskite are formed. To this end, the perovskite is grown layer-by-layer upon the strain-free surface by conventional MBE techniques to that each layer of perovskite is one cell unit high. For example, the strain free surface may be initially be exposed to Ti and metal, e.g., Ba or Sr, vapors and then to oxygen so that the perovskites forms upon the strain-free surface. Alternatively, the strain-free surface can be exposed simultaneously to the Ti and metal vapors and oxygen so that the perovskite forms and then settles upon the strain-free surface. In either instance, careful control of the MgO process is maintained so that the build up of successive layers of the perovskite is effected epitaxially.

The clarity of the resulting perovskite is realized, at least in part, by the aforedescribed build up of alternating layers of TiO.sub.2 and metal oxide on the MgO surface in that this build up minimizes undersirable effects which could otherwise result from interfacial electrostatics developed between MgO and the superposed layers subsequently grown thereon. To appreciate the interfacial electrostatics issue, the structure of the perovskite oxides can be considered. The distinguishing characteristic of the perovskite oxide class is recognized as a closest-packing of large cations and oxygen anions arranged as stacked sheets normal to a �111! direction. The octahedral interstices that form as a result of this sheet-stacking sequence are in turn filled with higher valence, smaller cations. The resulting structures are cubic with low index stable crystal faces. The naturally occuring crystal truncations are {001} and are then, for example with BaTiO.sub.3, either BaO planes or TiO.sub.2 planes, as mentioned earlier. The ion sizes and charges in these planes are distinctly different, and the initiation of a heteroepitaxial growth sequence for such a structure on another insulating oxide must take this into account.

With reference to the micrograph image of FIG. 4, there is shown a fracture cross section of a representative BaTiO.sub.3 film on (100)MgO. The FIG. 4 material was grown by using source-shuttering MBE techniques in ultra high vacuum. The film is adherent, single phase and optically clear. The epitaxy is cube-on-cube and uniquely results from the aforedescribed layering sequence that begins at the TiO.sub.2 -plane of the perovskite structure. The layering sequence is a requirement for single-orientation, epitaxial growth of a perovskite on MgO.

For a heteroepitaxial transition between insulating oxides, the interface electrostatics (ion-ion near neighbor interactions) of the first layers critically determine whether a commensurate structure can develop. For example, in going from MgO to BaTiO.sub.3 on the (001) face of MgO, if the transition is initiated at a barium oxide plane, the structure at the interface cannot develop commensurately with the MgO surface. The basic incompatibility results from the large ion-size difference between barium and magnesium. In particular, it is impossible to avoid near-neighbor ion configurations where cation-cation or anion-anion repulsive interactions occur in large numbers. This naturally leads to interfacial energy and an inherent instability. In each study made up until now which has been directed to interfacial equilibrium and surface segregation phenomena for the alkaline earth oxides, the clear result emerged that no single layer of BaO on MgO existed that was energically stable. We have found that the energetic stability is of paramount importance to the growth of single-orientation perovskites on MgO.

For purposes of comparison, barium metal and oxygen was deposited onto a MgO surface at a substrate temperature of 500.degree. C. to form BaO at a 1/2 monolayer coverage based on the MgO surface. This monolayer coverage is equivalent to one monolayer of BaO in BaTiO.sub.3. The high interfacial energies that would result from commensurate BaO epitaxy on MgO should drive some mechanism for lowering the interfacial energy. In this regard, there is shown in FIG. 5 a cube model of the interface and associated reflection high-energy electron diffraction (RHEED) patterns from clean and 1/2 monolayer BaO-covered (100)MgO surfaces. The implication of surface segregation theories is that island-like nucleation of incommensurate BaO-type structures should develop, and it is believed that this does occur. The cube model shown in FIG. 5 shows an idealization of parallel and 45.degree.-rotated morphologies of an (100) interface between MgO and BaO, and FIGS. 6a and 6b show diffraction patterns as experimental confirmation of their existence. The RHEED pattern shown in FIG. 6a results from an MgO surface prepared in the MBE system by growing 100 nm of MgO homoepitaxially on (001)MgO. The 0,0 and allowed 0,2 surface rods are seen. In FIG. 6b, surface diffraction at the same zone axis is illustrated but is modified by a single-layer-coverage BaO deposition. It can be seen in FIG. 6b that incommensurate crystallite orientations have formed and give rise to diffraction at what would be the 0,2 rod position for cube-on-cube BaO and at the 1,1 rod of 45.degree.-rotated BaO as well. Moreover, in addition to the rod spacing indicating the microstructural characteristics of the interface, the diffraction intensity is modulated along the reciprocal lattice BaO rods in a Bragg-like manner, i.e., 3-dimensional diffraction occurs that is indicative of "islanding" or surface roughening. These multi-orientation, 3-dimensional island structures defeat any attempt at growing optical-quality, thick perovskite films.

With reference again to the structure construction of the present invention, there are provided in FIGS. 7a and 7b photographs of RHEED data which illustrate the dramatically different result that can be obtained by moving up one plane from the MgO layer (whose ball model is depicted in FIG. 8a) in the BaTiO.sub.3 unit cell to the TiO.sub.2 plane (whose ball model is depicted in FIG. 8b) and initiating the growth sequence at that point. A commensurate, atomically flat layer of TiO.sub.2 can form in which every other cation row is vacant over the underlying Mg.sup.2+ sites. This TiO.sub.2 surface satisfies the electrostatic requirements for anion-cation near-neighbor pairs at the interface and is a low-energy, stable truncation of the MgO surface. The missing row of cations in this layer provides the energetically favorable sites for subsequent barium ion attachment to the crystal surface. As the perovskite growth is continued with alternating barium and titanium deposition cycles, BaTiO.sub.3 grows layer-by-layer and strain relief can occur by nucleation of simple edge dislocations maintaining the single orientation cube-on-cube epitaxy. The BaTiO.sub.3 lattice parameter relaxes to its strain-free, bulk value within ten unit cells from the original interface. The transition from heteropitaxy to homoepitaxy of the perovskite is completed with the desired single-orientation material and its advantageous long-range structural coherence. With the transition from heteroepitaxy to homoepitaxy accomplished in the manner described above, growth rates on the order of 1 .mu.m/hr can be attained at temperatures as low as 500.degree. C. by codeposition of barium and titanium or strontium and titanium with oxygen arrival rates equivalent to pressures of 10.sup.-7 torr. Structural and optical characteristics of the resulting thin films are provided in table form in FIG. 9.

The MBE process described above for the stabilization of the interface between a perovskite oxide and the alkaline earth oxide MgO provides an opportunity heretofore unavailable to exploit the electro-optic properties of thin-film epitaxial ferroelectrics in waveguide applications. In support of this contentions, there is provided in FIG. 10 a plot of the waveguide dependence for optical loss in thin film SrTiO.sub.3 on an MgO surface. Such a film is of high optical clarity and can be directly compared with the performance of LiNbO.sub.3, the most commonly applied material in EO devices. It is believed that this is the first demonstration of such optical clarity of SrTiO.sub.3 and BaTiO.sub.3 grown in thin film form. The crystal quality that is obtained by the methods described above does not result from incremental improvements upon known information, but rather, is attained by directly addressing the fundamental requirements of interfacial energy minimization between perovskite and alkaline earth oxides.

It will be understood that numerous modifications and substitutions can be had to the aforedescribed embodiments without departing from the spirit of the invention. For example, although the aforedescribed process describes a build up of a relatively thick film of perovskite upon a MgO surface, a usable product which could, for example, permit the intrinsic properties of MgO to be studied may include only a single layer of TiO.sub.2 overlying a MgO surface. Thus, in accordance with the broader aspects of the present invention, an embodiment of the process could terminate upon the formation of a single plane of TiO.sub.2 upon a MgO surface. Accordingly, the aforedescribed embodiments are intended for the purpose of illustration and not as limitation.

Claims

1. A process for coating a body with an epitaxial film wherein the body has a surface of MgO, the process comprising the steps of:

growing, by molecular beam epitaxy techniques (MBE) techniques, a single commensurate plane consisting of TiO.sub.2 upon the MgO surface so that the TiO.sub.2 of the single plane directly contacts and is commensurate with the MgO surface.

2. The process as defined in claim 1 wherein the MBE techniques involve a controlling of the exposure of the MgO surface to Ti vapor and oxygen so that no more than a single plane of TiO.sub.2 is formed directly upon the MgO surface.

3. The process as defined in claim 1 wherein the step of growing a single plane of TiO.sub.2 upon the MgO surface is followed by the step of:

growing, by MBE techniques, a single commensurate plane consisting of metal oxide upon the TiO.sub.2 plane wherein the metal oxide is one oxide of an oxide group consisting of BaO, SrO, CaO and MgO.

4. The process as defined in claim 3 wherein the step of growing a single commensurate plane of metal oxide is followed by the steps of:

growing a single commensurate plane consisting of TiO.sub.2 upon the grown plane of the one metal oxide, and then

growing a single commensurate plane consisting of the one metal oxide upon the grown plane of TiO.sub.2.

5. The process as defined in claim 4 wherein the steps of growing a single plane of TiO.sub.2 upon the grown plane of the one metal oxide and growing a single plane of the one metal oxide upon the grown layer of TiO.sub.2 are repeated until the total number of single planes of metal oxide is at least twenty-five.

6. The process as defined in claim 1 wherein the MgO surface is atomically smooth and clean, and the MBE techniques used to grow the single layer of TiO.sub.2 upon the MgO surface during the step of growing is carried out while the environment about the MgO surface is maintained between about 2-5.times.10.sup.-7 torr.

7. A process for growing a crystalline film of perovskite constituents upon a MgO surface wherein the crystalline film to be grown includes a plane consisting of TiO.sub.2 and a plane consisting of metal oxide wherein the metal of the metal oxide is the metal which combines with Ti and oxygen to form the perovskite, the process comprising the steps of:

growing, by molecular beam epitaxy (MBE) techniques, an epitaxial layer directly upon the MgO surface wherein the epitaxial layer is comprised of a single commensurate plane consisting of TiO.sub.2 and wherein the TiO.sub.2 of the single plane directly contacts and is commensurate with the MgO surface.

8. The process as defined in claim 7 wherein the epitaxial layer is a first layer and the step of growing is followed by the step of:

growing, by MBE techniques, a second epitaxial layer upon the first epitaxial layer wherein the second epitaxial layer is comprised of a single commensurate plane consisting of the metal oxide.

9. The process as defined in claim 8 wherein the step of growing the second epitaxial layer of metal oxide is followed by the sequential steps of:

a) growing a single epitaxial and commensurate plane consisting of TiO.sub.2 directly upon the previously-grown plane of the metal oxide, and

b) growing a single epitaxial and commensurate plane consisting of the metal oxide directly upon the previously-grown plane of TiO.sub.2.

10. The process as defined in claim 9 wherein steps a) and b) are repeated, inclusively, until no lattice strain within the layup of planes appears at the surface of the layup.

11. The process as defined in claim 9 wherein steps a) and b) are repeated, inclusively, until the total number of metal oxide planes is at least twenty-five.

12. The process as defined in claim 11 wherein the twenty-fifth plane of metal oxide is followed by the steps of:

growing, by MBE techniques, layers of the perovskite upon the grown layup of planes wherein the perovskite layers are grown in a layer-by-layer fashion.

13. A process for growing a perovskite film onto a MgO surface wherein the crystalline form of the desired perovskite includes a single plane consisting of TiO.sub.2 and a single plane consisting of metal oxide, the process including the steps of

epitaxially growing upon the MgO surface a first commensurate plane consisting of TiO.sub.2 wherein the TiO.sub.2 of the first plane directly contacts and is commensurate with the MgO surface;

epitaxially growing a commensurate plane consisting of metal oxide upon the plane of TiO.sub.2 wherein the metal oxide of the metal oxide plane directly contacts and is commensurate with the TiO.sub.2 of the first plane; and repeating in sequence

the steps of growing a commensurate plane consisting of TiO.sub.2 upon the grown plane of metal oxide and growing a commensurate plane consisting of metal oxide upon the grown plane of TiO.sub.2 so that the grown planes provide layers of the perovskite in bulk form.

14. The process as defined in claim 13 wherein the steps of growing a plane consisting of TiO.sub.2 and growing a plane consisting of metal oxide are repeated in sequence until lattice strains do not appear at the surface of the layup of planes, and subsequently

growing the perovskite upon the surface of the layup of planes in a layer-by-layer fashion.