Patent Application
20120107641
1. Technical Field
The present disclosure relates to a process for joining a metal part and a ceramic part, especially to a process for joining a stainless steel part and a silicon carbide ceramic part, and a composite article made by the process.
2. Description of the Related Art
It is desirable to join stainless steel parts and silicon carbide ceramic parts. A typical process for joining stainless steel and silicon carbide ceramic is by positioning physically separate nickel foil or molybdenum foil as intermediate layer between stainless steel and silicon carbide ceramic. The foil retains its separate nature through manufacturing in the final product and do not chemically interact with the stainless steel or silicon carbide ceramic. Furthermore, in case of using physically separate nickel foil, due to great difference between the coefficients of heat expansion of the silicon carbide ceramic and the nickel foil, the ceramic/nickel interface has a large thermal stress, thus, the bond between the stainless steel and the silicon carbide ceramic via nickel foil is not as stable as desired. In case of using physically separate molybdenum foil, due to having a relatively low reaction activity, it is difficult for silicon carbide ceramic and molybdenum foil to inter-diffuse into each other, enhancing the difficulty of bonding.
Therefore, there is room for improvement within the art.
Many aspects of the embodiments can be better understood with reference to the following drawings. The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the exemplary process for joining stainless steel part and silicon carbide ceramic part, and composite article made by the process. Moreover, in the drawings like reference numerals designate corresponding parts throughout the several views. Wherever possible, the same reference numbers are used throughout the drawings to refer to the same or like elements of an embodiment.
Referring to
A silicon carbide (SiC) ceramic part 20, a molybdenum (Mo) foil 40, a nickel (Ni) foil 50 and a stainless steel (SUS) part 30 are provided. The Mo foil 40 and the Ni foil 50 are used as a joining medium between the SiC part 20 and the SUS part 30. The Mo foil 40 and the Ni foil 50 each has a thickness of about 0.2 mm-0.5 mm, preferably of about 0.2 mm-0.3 mm.
The SiC ceramic part 20, the SUS part 30, the Mo foil 40 and the Ni foil 50 are pretreated. The pretreatment may include the step of polishing the surfaces of the SiC ceramic part 20, the SUS part 30, the Mo foil 40 and the Ni foil 50 by sandpaper to produce smooth surfaces. Then, the SiC ceramic part 20, the SUS part 30, the Mo foil 40 and the Ni foil 50 are cleaned with an organic solution (e.g., alcohol or acetone) in an ultrasonic cleaner, to remove grease from their surfaces. Then, the SiC ceramic part 20, the SUS part 30, the Mo foil 40 and the Ni foil 50 are rinsed with water and dried.
A nickel coating 60 is directly deposited on a surface 201 of the SiC ceramic part 20. The nickel coating 60 may be formed by physical vapor deposition, such as sputtering. Alternatively, the nickel coating 60 can be formed by electroless plating. The thickness of the nickel coating 60 may be about 2 μm-6 μm, preferably 3 μm-4 μm.
A clamping mold 70 is used to hold the SiC ceramic part 20, the SUS part 30, the Mo foil 40 and the Ni foil 50. The clamping mold 70 includes a pressing member 72, a corresponding supporting member 74 and a receiving part 76. The receiving part 76 defines a cavity 762 for receiving the SiC ceramic part 20, the SUS part 30, the Mo foil 40 and the Ni foil 50. The pressing member 72 and the supporting member 74 extend towards the cavity 762 from opposing directions and can be moved relative to the cavity 762 by a driving system such as hydraulic pressure system. The SiC ceramic part 20, the Mo foil 40, the Ni foil 50 and the SUS part 30 are placed into the cavity 762 and clamped by the pressing member 72 and the supporting member 74. The Mo foil 40 and the Ni foil 50 are inserted between the SiC ceramic part 20 and the SUS part 30. The Mo foil 40 abuts against the nickel coating 60 formed on the SiC ceramic part 20, the Ni foil 50 abuts against the SUS part 30. The pressing member 72 and the supporting member 74 from two opposite sides, bring the surfaces of the parts to be joined into tight contact, for compressing the SiC ceramic part 20, the Mo foil 40, the Ni foil 50 and the SUS part 30. The clamping mold 70 may be made of graphite.
An hot press sintering device 100 including a chamber 101 is provided. The clamping mold 70 is placed into the chamber 101. The chamber 101 is evacuated to an internal pressure of about 2×10−3 Pa-8×10−3 Pa. Argon (Ar) as a protective gas is fed into the chamber 101 to create a pressure of about 0.2 MPa-0.5 MPa. Then, the chamber 101 is heated at a rate of about 20 degrees Celsius per minute (° C./min)-40° C./min. When the temperature of the chamber 101 reaches to about 300° C., the pressing member 72 and the supporting member 74 begin to press toward each other at about 10 MPa to press the parts clamped therebetween. The chamber 101 is heated at a rate of about 60° C./min-120° C./min as the clamping pressure applied by the members 72,74 steadily increases, until the temperature of the chamber 101 reaches to about 850° C.-1100° C., and the clamping pressure reaches to about 100 MPa. The pressure and temperature are maintained in their respective peak ranges for about 15 min-35 min, so that the Mo foil 40, the Ni foil 50 and the nickel coating 60 will chemically interact with each other, and the Mo foil 40 chemically interacts with the nickel coating 60 and the SiC ceramic part 20, and the Ni foil 50 chemically interacts with the SUS part 30. Accordingly, the SiC ceramic part 20 and the SUS part 30 are connected by the Mo foil 40, the Ni foil 50 and the nickel coating 60 to form a composite article 10. The composite article 10 is removed after the chamber 101 is cooled.
Referring to
The composite article 10 manufactured by the present process includes the SiC ceramic part 20, the SUS part 30 and a multi-layered connecting layer 80 connecting the SiC ceramic part 20 to the SUS part 30. The connecting layer 80 is formed by depositing the nickel coating 60 on the SiC ceramic part 20 and placing the Mo foil 40 and the Ni foil 50 between the SiC ceramic part 20 and the SUS part 30, and then heating and pressing the SiC ceramic part 20 and the SUS part 30 as previously described. The various layers of the connecting layer 80 result from differing chemical interaction between the SUS part 30, nickel coating 60, Mo foil 40, Ni foil 50, and SiC ceramic part 20. In particular, the connecting layer 80 includes:
a) a first transition layer 81: The first transition layer 81 is adjacent to the SiC ceramic part 30. The first transition layer 81 results from chemical interaction of the SiC ceramic part 20, nickel coating 60, and the Mo foil 40. The first transition layer 81 mainly includes compounds comprising Ni element and Si element (such as NiSi), and Ni with Mo solid solutions. The nickel coating 60 completely reacts with the SiC ceramic part 20 and the Mo foil 40 during the bonding processing;
b) a Mo layer 82: The Mo layer 82 is adjacent to the first transition layer 81. The Mo layer 80 results from portions of the Mo foil 40 that do not react with either the SiC ceramic part 20 or the Ni foil 50;
c) a second transition layer 83: The second transition layer 83 is located between the Mo layer 82 and the Ni layer 84. The second transition layer 83 mainly includes Mo with Ni solid solutions, and intermetallic compounds comprising Mo and Ni. The compounds and solutions result from chemical reactions between adjacent portions of the Mo foil 40 and Ni foil 50;
d) an Ni layer 84: The Ni layer 84 results from portions of the Ni foil 50 that do not react with either the Mo foil 40 or the SUS part 30; and
e) a third transition layer 85: The third transition layer 85 is located between the Ni layer 84 and the SUS part 30 and connects together the Ni layer 84 and the SUS part 30. The third transition layer 85 mainly includes intermetallic compounds comprising Ni and Fe, and Ni with Fe solid solutions. The compounds and solutions result from chemical reactions between adjacent portions of the Ni foil 50 and the SUS part 30.
The thermal expansion rate of the connecting layer 80 gradually changes from a value close to that of the SiC ceramic part 20 (in the area of 81) to a value close to that of SUS part 30 (in the area of 85). This results in a composite article 10 well suited to temperature changes due to the gradual, rather than abrupt, changes in its internal thermal expansion rates.
Furthermore, the connecting layer 80 of the composite article 10 has no crack or aperture, and has a smooth surface. The composite article 10 has a shear strength in a range from about 50 MPa to about 80 MPa, and a tension strength in a range from about 60 MPa to about 100 MPa.
It is to be understood that even though numerous characteristics and advantages of the present embodiments have been set forth in the foregoing description, together with details of assemblies and functions of various embodiments, the disclosure is illustrative only, and changes may be made in detail, especially in matters of shape, size, and arrangement of parts within the principles of the present invention to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201010525043.3 | Oct 2010 | CN | national |
This application is related to co-pending U.S. Patent Applications (Attorney Docket No. US35129), entitled “PROCESS FOR JOINING STAINLESS STEEL PART AND ZIRCONIA CERAMIC PART AND COMPOSITE ARTICLES MADE BY SAME”. Such applications have the same assignee as the present application. The above-identified applications are incorporated herein by reference.