Claims
- 1. A process for making discrete, closed-cell, alkenyl aromatic polymer foam packing bodies, comprising:
- a) heating an alkenyl aromatic polymer material comprising greater than 50 percent by weight alkenyl aromatic monomeric units to form a melt polymer material;
- b) forming a foamable gel by incorporating into the melt polymer material at an elevated pressure a blowing agent having about 20 weight percent or more based upon the total weight of the blowing agent of a first blowing agent selected from the group consisting of carbon dioxide, ethane, and a mixture of the foregoing;
- c) extruding the formable gel through a die to a region of reduced pressure to form an alkenyl aromatic polymer foam strand;
- d) pelletizing the foam strand to form a plurality of the discrete foam bodies; and
- e) further expanding the foam bodies by exposing them one or more times to heated air or steam.
- 2. The process of claim 1, wherein the bodies are allowed to age in air for pre-selected periods of time after pelletizing and between subsequent expansions.
- 3. The process of claim 1, wherein the blowing agent has a second blowing agent comprising a C.sub.3 -C.sub.6 hydrocarbon.
- 4. The process of claim 1, wherein the blowing agent has a second blowing agent comprising water.
- 5. The process of claim 1, wherein the alkenyl aromatic polymer material comprises greater than 70 percent by weight alkenyl aromatic monomeric units.
- 6. The process of claim 1, wherein the foam bodies have an open-cell content less than 5 percent.
- 7. The process of claim 1, wherein the foam bodies have a density of less than 16 kilograms per cubic meter.
- 8. The process of claim 1, wherein an alkenyl aromatic polymer material has a glass transition temperature of about 110.degree. C. or less.
- 9. The process of claim 1, wherein the first blowing agent comprises about 50 percent or more based upon the total weight of the blowing agent.
- 10. The process of claim 1, wherein the blowing agent is composed entirely of the first blowing agent.
- 11. The process of claim 1, wherein the blowing agent is composed entirely of carbon dioxide and water.
- 12. The process of claim 8, wherein the alkenyl aromatic material further comprises a plasticizer or an alkenyl aromatic copolymer having a glass transition temperature of about 100.degree. C. or less.
- 13. A process for making discrete, closed-cell, alkenyl aromatic polymer foam packing bodies, comprising:
- a) heating an alkenyl aromatic polymer material comprising greater than 50 percent by weight alkenyl aromatic monomeric units to form a melt polymer material;
- b) forming a foamable gel by incorporating into the melt polymer material at an elevated pressure a blowing agent having about 20 weight percent or more based upon the total weight of the blowing agent of a first blowing agent selected from the group consisting of carbon dioxide, ethane, and a mixture of the foregoing;
- c) extruding the foamable gel through a die to form an essentially continuous strand of the foamable gel;
- d) pelletizing the foamable gel strand to form a plurality of discrete gel strands;
- e) allowing the plurality of the discrete gel strands to expand in a region of reduced pressure to form a plurality of the discrete foam bodies; and
- f) further expanding the foam bodies by exposing them one or more times to heated air or steam.
- 14. The process of claim 13, wherein the bodies are allowed to age in air for pre-selected periods of time after pelletizing and between subsequent expansions.
- 15. The process of claim 13, wherein the blowing agent has a second blowing agent comprising a C.sub.3 -C.sub.6 hydrocarbon.
- 16. The process of claim 13, wherein the blowing agent has a second blowing agent comprising water.
- 17. The process of claim 13, wherein the alkenyl aromatic polymer material comprises greater than 70 percent by weight alkenyl aromatic monomeric units.
- 18. The process of claim 13, wherein the foam bodies have an open-cell content less than 5 percent.
- 19. The proces of claim 13, wherein the foam bodies have a density of less than 16 kilograms per cubic meter.
- 20. The process of claim 13, wherein an alkenyl aromatic polymer material has a glass transition temperature of about 110.degree. C. or less.
- 21. The process of claim 13, wherein the first blowing agent comprises about 50 percent or more based upon the total weight of the blowing agent.
- 22. The process of claim 13, wherein the blowing agent is composed entirely of the first blowing agent.
- 23. The process of claim 13, wherein the blowing agent is composed entirely of carbon dioxide and water.
- 24. The process of claim 20, wherein the alkenyl aromatic material further comprises a plasticizer or an alkenyl aromatic copolymer having a glass transition temperature of about 100.degree. C. or less.
- 25. A process for making an article formed of discrete, closed-cell, alkenyl aromatic polymer foam packing bodies, comprising:
- a) heating an alkenyl aromatic polymer material comprising greater than 50 percent by weight alkenyl aromatic monomeric units to form a melt polymer material;
- b) forming a foamable gel by incorporating into the melt polymer material at an elevated pressure a blowing agent having about 20 weight percent or more based upon the total weight of the blowing agent of a first blowing agent selected from the group consisting of carbon dioxide, ethane, and a mixture of the foregoing;
- c) extruding the foamable gel through a die to a region of reduced pressure to form an alkenyl aromatic polymer foam strand;
- d) pelletizing the foam strand to form a plurality of the discrete foam bodies;
- e) further expanding the foam bodies by exposing them one or more times to heated air or steam; and
- f) molding and coalescing the foam bodies to form an article.
- 26. The process of claim 25, wherein the bodies are allowed to age in air for preselected periods of time after pelletizing and between subsequent expansions prior to molding and coalescing to form the article.
- 27. A process for making discrete, closed-cell, alkenyl aromatic polymer foam strands, comprising:
- a) heating an alkenyl aromatic polymer material comprising greater than 50 percent by weight alkenyl aromatic monomeric units to form a melt polymer material;
- b) forming a foamable gel by incorporating into the melt polymer material at an elevated pressure a blowing agent having about 20 weight percent or more based upon the total weight of the blowing agent of a first blowing agent selected from the group consisting of carbon dioxide, ethane, and a mixture of the foregoing;
- c) extruding the foamable gel through a die to a region of reduced pressure to form an essentially continuous foam strand;
- d) further expanding the continuous foam strand by exposing it to heated air or steam; and
- e) intermittently severing the continuous foam strand to form a plurality of discrete foam strands.
- 28. A process for making discrete, closed-cell, alkenyl aromatic polymer foam strands, comprising:
- a) heating an alkenyl aromatic polymer material comprising greater than 50 percent by weight alkenyl aromatic monomeric units to form a melt polymer material;
- b) forming a foamable gel by incorporating into the melt polymer material at an elevated pressure a blowing agent having about 20 weight percent or more based upon the total weight of the blowing agent of a first blowing agent selected from the group consisting of carbon dioxide, ethane, and a mixture of the foregoing;
- c) extruding the foamable gel through a die to a region of reduced pressure to form an essentially continuous foam strand;
- d) intermittently severing the continuous foam strand to form a plurality of discrete foam strands; and
- e) further expanding the discrete foam strands by exposing them one or more times to heated air or steam.
- 29. The process of claim 27, wherein the foam strands are allowed to age in air for a preselected period of time after severing and prior to further expansion of the foam strands.
Parent Case Info
This application is a continuation-in-part of Ser. No. 07/965,917 filed Oct. 23, 1992, now abandoned, which is incorporated herein by reference.
US Referenced Citations (17)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
965917 |
Oct 1992 |
|