Process For Making Low and Specified Hardenability Structural Steel

Abstract
The invention refers to metallurgy, in particular to making low (LH) and specified (SH) hardenability steels in electric arc, induction furnaces or oxygen converters. A metallurgical unit is loaded with metal charge consisting of iron carbon alloy, scrap with a specified content of manganese, silicon, chrome, nickel and copper, providing for the final content of each of them of not more than 0.1 weight %, graphite, slag-forming components, refining of the melt with respect of carbon content prior to heat tapping in a ladle of ladle furnace is done in an electric arc or induction furnace until the carbon content conforms to the corresponding upper tolerance limit or lower than that in the converter followed by carburization in the ladle, slag composition adjustment during the refining and pure rimming periods is done by flushing a portion of slag and recurrent addition of slag-forming materials to the remaining portion of the slag to make sure the content of each of the permanent admixtures in the melt during tapping is not more than 0.1 weight %, then the melt is deoxidized in the ladle or ladle furnace with aluminum (1.0-2.5 kg/t), titanium and vanadium. The invention makes it possible to obtain better mechanical properties and stable hardenability characterized by the ideal diameter (DI):DI of a billet from 6 to 15 mm has a deviation of not more than 2 mm;DI of a billet from 16 to 50 mm has a deviation of not more than 5 mm;DI of a billet from 51 to 100 mm has a deviation of not more than 10 mm;DI of a billet over 100 mm has a deviation of less than 50 mm and better mechanical properties.
Description

The invention refers to metallurgy, in particular to making low (LH) and specified (SH) hardenability steels in electric arc, induction furnaces or oxygen converters.


First developed in Russia, low (LH) and specified (SH) hardenability structural steels have acquired industrial application and are specifically designed for parts hardened using the through-surface hardening process.


The basic feature of LH steels is that their hardenability is substantially lower then that of carbon structural steels. Thus, if the typical carbon steel 45 (SAE 1045) hardenability estimated by the ideal diameter (DI) lies within the 20-38 mm range, in the 1st generation typical low hardenability steel 58 (55 LH steel) per GOST 1050-88 (C-0.55-0.63%; Mn<0.2%; Si=0.1-0.3%; Cr, Ni, Cu<0.15% each) DI=10-16 mm, i.e. it has a narrower range.


SH steels differ from LH steels by higher values of DI—over 16 mm, while maintaining a narrower hardenability range.


Hardening of parts made from LH and SH steels using the through-surface hardening process results in formation of a high-strength surface layer with the depth of 0.1 to 0.2 of the effective section diameter (thickness) with a martensite structure with HRC˜60 (σb=2000-2800 MPa) hardness, while the more ductile core has HRC 30-40 (σb1000-1500 MPa) hardness.


A significant feature of LH and SH steels is their lower tendency to the growth of hardenability itself and the size of the actual austenite grain when heated for through-surface hardening. Practical implementation of this property is substantially affected by smelting techniques, particularly deoxidation of the steel being smelted.


The subject of this proposal is a process for smelting of LH and SH steels in industrial melting Units: electric arc, induction furnaces, or converters.


The closest method to the one proposed is the “Process for production of low hardenability structural steel in an open-hearth furnace” (RU 2164536) that includes loading of the charge in the form of steel scrap, iron carbon alloy, graphite, heating and melting of the charge, handling and flushing of slag during rimming and beginning of refining of the furnace bath with respect to composition and temperature, preliminary deoxidation of metal in the furnace and basic deoxidation in the ladle with aluminum and titanium during tapping of the melt.


The process makes it possible to produce higher grade 2nd generation LH steels featuring a still narrower and more stable hardenability range (DI=10-14 and 11-15 mm depending on the permanent admixture content), particularly fine and stable austenite grain per GOST 5639 (ASTM) #10-11 when heated in a furnace, or #10-12 with induction heating.


The disadvantage of this process lies in a rather high steel hardenability level which does not allow through-surface hardening to be used for parts with the effective section diameter (thickness) of less than 15 (12) mm, rather high deviation in the hardened layer depth in finished products, along with occasional violation of the optimum—0.1-0.2 of the diameter (thickness). The process does not provide for smelting of SH steels.


This invention is aimed at:


development of a process tor production of the 3rd generation LH steel with a finer “superfine” grain #11-14 per GOST 5639 (ASTM), lower hardenability level of DI<10 mm, substantially lower and stable deviation in hardenability—not more than 2.0 mm in the 6 mm<DI<15 mm (DI=6-8, 8-10, 11-13, 14-15 mm) range and higher mechanical properties;


development of a process for process for production of the 3rd generation SH steel with a finer “super fine” grain #11-14 per GOST 5639 (ASTM) substantially lower and stable deviation in hardenability—not more than 5.0 mm in the 16 mm<DI<50 mm range, not more than 10 MM in the 51 mm<DI<100 mm range and higher mechanical properties.


The technical result shown is achieved owing to the fact that the electric arc, indention furnace or converter is charged with iron carbon alloy, scrap with a specified content of manganese, silicon, chrome, nickel, copper, with the final content of each of them not exceeding 0.1 mass percent for LH steels, and 0.3 mass percent for SH steels, graphite, slag-forming components, melting of the charge to an extent when carbon content is not less than 1.0 weight % or 1.5 weight % in the converter, heating the furnace bath up to the temperature of beginning of refining, refining of the liquid melt with respect to carbon content prior to teeming of the heat in a ladle or ladle-furnace is done in an electric arc or induction furnace until the carbon content reaches the allowed upper limit; in the converter it should be lower than that, followed by carburization in the ladle; slag content is adjusted during pure rimming and finishing by flushing some of the initial slag and with and periodic addition of slag-forming materials to the remaining slag to make sure the indicated permanent admixtures during tapping do not exceed 0.1 weight % for LH steels and 0.3 weight % for SH steels. After that, the molten metal is deoxidized in the ladle or ladle furnace with aluminum (1.0-2.5 kg/t), titanium and vanadium, with 0.3-0.5 of the entire aluminum amount is put on the ladle bottom and the rest—on the stream until at least 0.3 of the ladle or ladle furnace volume is filled, and titanium and vanadium are added after aluminum to make sure the aluminum content in the finished metal is 0.03-0.1 weight %, titanium content is 0-0.4 weight % vanadium—0.4 weight %. During smelting, after rimming and prior to heat tapping aluminum powder or calcium borate is added. In order to ensure the required hardenability level manganese, siliceous and other materials are added in strictly weighted quantities that help to maintain the required hardenability characterized by the ideal diameter DI in steel from 6 to 15 mm with the deviation of not more than 2 mm, from 16 to 50 mm with the deviation of not more 5 mm, from 51 to 100 mm with the deviation of not more than 10 mm.


The essence of invention is as follows.


The patent applicant proposes smelting of LH and SH steels from the charge in the form of iron carbon alloy and scrap with calculated proportions of Mn, Si, Cr, Ni, Cu, with tapping of not more than 0.1 in the ladle. Similarly to the known process, the components containing the above-mentioned permanent admixtures are not added in the furnace (converter) during smelting.


The specific feature of the proposed process is the deoxidation process which basically determines the solution of the task in hand. The proposed partial deoxidation the furnace with aluminum is not done since prior to tapping aluminum reacts with nitrogen to form a coarse fraction of coagulated (aggregated) nitride (Al N) which is difficult to grind during subsequent technological operations.


Deoxidation is performed 3 steps:


deoxidation of slag with aluminum powder or calcium borate in the furnace prior to metal tapping;


deoxidation of steel is implemented during furnace and converter tapping directly in the ladle using aluminum, titanium, vanadium and nitrogen;


titanium, vanadium are added only after 100% addition of aluminum with at least 0.3 of the ladle volume filled, providing for the presence in the finished metal of specified amounts of: 0.3-1.2% carbon, 0.03-0.1 aluminum, 0-0.4% titanium, 0-0.4% vanadium, 0-0.15% nitrogen, with carbon (carburizing agent)—in the form of cast iron or graphite to ensure specified chemical composition. After a 100% filling of the ladle with metal, aluminum slag in the form of aluminum powder or calcium borate is added.


Less expensive components, such as manganese and siliceous substances, as well us chrome, nickel are added in calculated amounts of 0-1.8%, tungsten—0-1.5%, molybdenum—0-0.5%m boron—0-0.007%, individually or in groups, in strictly weighed amounts, taking into account the residual contents of permanent admixtures, prior to tapping of the furnace and providing for the specified hardenability level, characterized by the LH steel ideal diameter (DI) from 6 to 15 mm with the deviation of not more than 2 mm. SH steel DI from 16 to 50 mm with the deviation of not more 5 mm, SH steel DI from 51 to 100 mm with the deviation of not more than 10 mm, SH steel DI over 100 mm with the deviation of not more than 50 mm, are added to the steel to ensure the required hardenability, after which the steel-teeming ladle is subjected to soaking, stirring, lancing with nitrogen (argon) and teeming.







EXAMPLES OF PROCESS IMPLEMENTATION
Example #1

A 2.5 t electric arc furnace was charged with 1.5 t steel scrap, 0.85 t conversion pig iron, 0.1St limestone, 0.03 t bauxite and 0.02 t crushed electrodes. Carbon content on melting was 1.05%, metal temperature-13 1540° C. Duration of the steel pure rimming was 1 hour 20 minutes, bath temperature—1640° C. carbon drop rate—0.3%/hr at continuous renewal of slag, with aluminum powder or calcium borate added to it after rimming and prior to tapping.


During tapping, 0.5 kg/t of aluminum was supplied to the ladle bottom, and the rest of it (1.0 kg/t)—onto the stream, until not more than 0.3 of the ladle volume was filled, after which 5 kg of 70% ferrotitanium was supplied onto the chute (stream), and, as a result, without adding any other alloying agents and after holding, stirring with bars, lancing with nitrogen and teeming, the following LH steel composition was obtained, weight %: C—0.58; Mn—0.08; Si—0.03, Cr—0.05; Ni—0.14; Cu—16; S—0.03; P—0.021; Ti—0.16; Al-130.05, rem.—iron.


The steel was used to make 8 mm thick flat springs. After TSH, a cryptocrystalline martensite structure of a superfine actual austenite grain #12-13 as per standard scale was obtained in the hardened layer that was 1.4 MM deep (0.175 of the thickness, DI=7 mm).


Example #2

A 500 kg induction furnace was charged with 240 kg steel scrap, 250 kg conversion pig iron, the rest of the components being similar to those described above for the electric arc furnace in proportion to capacity. The smelting process, deoxidation with aluminum in the ladle, modifications with titanium were as per Example #1, alter which ferromanganese and ferrosilicon were added to the ladle for the finished metal to contain 0.15-0.2% Mn and 0.15-0.2% Si.


LH steel with the following composition was obtained, weight %: C—0.81; Mn—0.29; Si—0.19; Cr—0.04; Ni—0.04; Cu—0.06; S—0.030; P—0.021; Ti—0.18; Al—0.05, Fe—rem. Steel was used to make 0.3 mm dia bearing rollers.


After TSH, a cryptocrystalline martensite structure of a superfine actual austenite grain #12 as per standard scale was obtained in the hardened layer that was 3.0 MM deep (0.10 of the diameter, DI=15 mm).


Example #3

A converter was charged with 25% steel scrap and 75% liquid iron, and then lanced with oxygen in the amount of 2-3 m3/min-t, along with applying basic slag consisting of 50-70 kg/t of lime and 1-3 kg/t of fluorspar to obtain 1.5-2% carbon content. After removing high-manganese slag, lancing continued with addition of basic slag: 10-15 kg/t of lime and 1-3 kg/t of fluorspar. Lancing with oxygen is terminated when the weight fraction of each of permanent admixtures Mn, Si, Ni, Cr is at least 0.1% (excluding chrome the content of which prior to the furnace tapping turned out to be 0.23%), carbon content corresponds to the upper limit of 0.67% and bath temperature is 1630-1660° c.


The heat was tapped into a steel-teeming ladle, deoxidation with aluminum taking place in the ladle, modification with titanium is similar to that described in Example#1, after which ferromanganese and ferrosilicon were added to the ladle for the finished metal to contain 0.25-0.30% Mn and 0.15-0.2% Si, taking into account the exact content of all admixtures, including higher content of chrome to ensure an ideal diameter of 18-22 mm in the finished SH steel.


SH steel with the following composition was obtained, weight %: C—0.64; Mn—0.27; Si—0.2, Cr—0.23; Ni—0.04; Cu—0.03; S—0.030; P—0.022; Ti—0.11; Al—0.05, rem.-13 iron. Steel was used to make cylinder-shaped Parts—40 mm dia shafts.


After TSH, a fine-needled martensite structure of an austenite grain #11 as per standard scale was obtained in the hardened layer that was 4.0 MM deep (-.10 of the thickness, DI=20 mm).

Claims
  • 1. Process for smelting low (LH) and specified (SH) hardenability structural steel, with a distinction that an electric arc or induction furnace or converter is charged with iron carbon alley, scrap with a specified content of manganese, silicon, chrome, nickel and copper, providing for the final content of each of them of not more than 0.1 weight % for LH steels, and not more than 0.3 weight % for SH steels, that, when melted, contains not less than 1.0 weight % of carbon in an electric arc and induction furnace or 1.5 weight % carbon in a converter, heating of the bath to the temperature of beginning of refining, refining of the melt with respect to carbon content prior to heat tapping in the ladle or ladle furnace is done in an electric arc or induction furnace until the carbon content conforms to the corresponding upper tolerance limit or lower than that in the converter, followed by carburization in the ladle, slag composition adjustment during the refining and pure rimming periods is done by flushing a portion of slag from the furnace, converter and recurrent addition of slag-forming materials to the remaining portion of the slag to make sure the content of each of the permanent admixtures in the melt during tapping is not more than 0.1 weight % for LH steels and not more than 0.3 weight % for SH steels, then the each is deoxidized in the ladle or ladle furnace with aluminum (1.0-2.5 kg/t), titanium and vanadium, with 0.3-0.5 of the entire amount added to the ladle or ladle furnace bottom and the remaining amount—onto the stream until not less than 0.3 of the ladle or ladle-furnace volume is filled, whereas titanium, vanadium and nitrogen are added after aluminum, making sure the ready metal contains 0.3-1.2 weight % carbon, 0.03-0.10 weight % aluminum, 0-0.4 weight % titanium, 0-0.4 weight % vanadium, 0 to 0.15 weight % nitrogen.
  • 2. Process as per Item 1, with a distinction that aluminum powder or calcium borate is added to the actual slag during working of the heat after rimming and prior to tapping.
  • 3. Process as per Item 1, with a distinction that aluminum powder of calcium borate is added to the slag after 100% filling of the ladle or ladle furnace.
  • 4. Process as per Item 1, with a distinction that to ensure the required hardenability level manganese, silicone, chrome, nickel (0-1.8 weight % of each), molybdenum (0-0.5 weight %), tungsten (0-1.5 weight %), boron (0-0.007 weight %) are added to the ladle or ladle furnace individually or in groups in strictly weighed amounts that take into account residual content of permanent admixtures prior to furnace tapping and provide for the required hardenability level characterized by the LH steel ideal diameter (DI) from 6 to 15 mm with the deviation of not more than 2 mm, SH steel DI from 16 to 50 mm with the deviation of not more 5 mm, SH steel DI from 51 to 100 mm with the deviation of not more than 10 mm, SH steel DI over 100 mm with the deviation of not more than 50 mm.
  • 5. Process as per Item 1, with a distinction that the melt is lanced in the ladle or ladle-furnace with argon or nitrogen.
Priority Claims (1)
Number Date Country Kind
2010143501 Oct 2010 RU national
PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/RU2010/000817 12/31/2010 WO 00 4/25/2013