The invention relates to a process for producing a multilayer coating from a filler, a base coat and a clear coat layer, which process may in particular be used for coating vehicle bodies and vehicle body parts.
Multilayer coatings made up, for example, of a filler, a base coat and a clear coat layer are typical coating structures in vehicle coating. Similar coating structures, for example based on a primer and a transparent or pigmented top coat layer are also known from other fields of industrial coating.
EP 1050551, for example, accordingly describes aqueous two-component polyurethane systems with improved adhesion and corrosion resistance, which are very suitable for direct coating of metallic substrates, for example vehicle bodies. The aqueous two-component PU system contains an aqueous OH-functional resin dispersion, a polyisocyanate with free isocyanate groups and an epoxy-functional silane component.
EP 1484349 furthermore describes coating compositions for coating plastics, in particular plastics interior parts or plastics exterior attachments for vehicles, the plastics parts comprising a silver plating layer. A base coat coating composition is disclosed which contains an OH-functional acrylate resin, an organically modified polydimethylsiloxane, an epoxy-functional silane and a polyisocyanate curing agent. A clear coat coating composition is furthermore disclosed which contains an OH-functional acrylate resin, an acrylate resin with tertiary amino groups, a polyisocyanate cross-linking agent and a compound with epoxy groups and with hydrolyzable silane groups. The coating materials are applied onto the plastics substrate in the sequence: base coat, silver plating layer and clear coat. A primer is preferably applied directly onto the plastics substrate before application of the base coat layer.
It is likewise known from WO 02/051899 to use a two-component coating composition containing a polyisocyanate component, an isocyanate-reactive component and a compound with an epoxy group and an alkoxysilane group for pipe coating.
Environmentally friendly water-based coating materials are increasingly being used in vehicle coating. In particular, water-based products are increasingly being used for the color-imparting and/or special effect-imparting base coat materials, which have a relatively high solvent content. When water-borne base coat materials, for example, are used, it is of course essential to guarantee the necessary technological properties of the overall coating structure, such as for example good humidity resistance as well as satisfactory optical properties and drying characteristics. In particular, when water-borne base coat materials are used in the above-stated multilayer structure comprising base coat and clear coat, there is a lack of satisfactory initial wet adhesion between the individual layers after humidity strain, i.e. between base coat and clear coat layer and between a prior coating, for example a filler layer, and the base coat layer. Cohesion within the water-borne base coat layer itself is also unsatisfactory.
It has not hitherto been possible to provide a satisfactory solution to these adhesion problems which does not simultaneously substantially impair other important coating properties, such as the drying characteristics, stability and optical properties of the resultant coatings.
The object of the present invention was thus to provide a process for the multilayer coating of substrates using water-borne base coat materials, which yields a coating structure with very good humidity resistance and adhesion properties, e.g. satisfactory wet and dry interlayer adhesion, in particular with very good initial wet adhesion between a filler layer and the base coat layer and between the base coat and clear coat layer. Cohesive failure within the water-borne base coat layer itself should also not occur. Other important technical coating properties, such as for example the drying characteristics, the optical properties of the resultant coatings, the stability of the compositions and good application properties of the coating composition should not be impaired as a consequence.
The invention accordingly relates to a process for the multilayer coating of substrates, in particular vehicle bodies and vehicle body parts, comprising the following steps:
1. Applying a filler layer of a filler coating composition onto an optionally precoated substrate,
2. Applying a base coat layer of a water-based base coat coating composition containing color-imparting and/or special effect-imparting pigments onto the filler layer
3. Applying a clear coat layer of a transparent clear coat coating composition onto the base coat layer and
4. Curing the clear coat layer, optionally together with the filler layer and/or the base coat layer,
wherein the filler coating composition and the transparent clear coat coating composition being organic solvent-based coating compositions comprising:
X denoting the residues
with m being 1-4, or 3,4- epoxycyclohexyl,
R1, R2, R3 mutually independently meaning identical or different organic residues with 1 to 30 carbon atoms per molecule, providing that at least one of the residues is an alkoxy group with 1 to 4 carbon atoms and
n is 2, 3 or 4, preferably 2 or 3.
It has surprisingly been found that, by using the specific epoxy-functional silane compounds C) in the filler and clear coat coating composition to be used in the process according to the invention, a multilayer structure of a filler, a water-borne base coat and a clear coat, is obtained which exhibits excellent adhesion properties, i.e. excellent wet adhesion and excellent high pressure cleaning resistance as well. In particular the multilayer structure has excellent interlayer adhesion between the filler layer and the water-borne base coat layer and between the water-borne base coat layer and the clear coat layer, without consequently impairing other important technical coating properties such as application properties, drying and optical properties. It has surprisingly also proved possible to improve cohesion within the water-borne base coat layer, in particular after exposure to severe conditions, for example in the moist heat test.
The invention will be explained in greater detail below.
It will be appreciated that certain features of the invention which are, for clarity, described above and below in the context of separate embodiments may also be provided in combination in a single embodiment. Conversely, various features of the invention that are, for brevity, described in the context of a single embodiment may also be provided separately or in any sub-combination. In addition, references in the singular may also include the plural (for example, “a” and “an” may refer to one, or one or more) unless the context specifically states otherwise.
The use of numerical values in the various ranges specified in this application, unless expressly indicated otherwise, are stated as approximations as though the minimum and maximum values within the stated ranges were both preceded by the word “about”. Thus, slight variations above and below the stated ranges can be used to achieve substantially the same results as values within the ranges. Moreover, in the disclosure of these ranges, a continuous range is intended, covering every value between the minimum and maximum values, including the minimum and maximum end points of the range.
The term (meth)acrylic as used here and hereinafter should be taken to mean methacrylic and/or acrylic.
Unless stated otherwise, all molecular weights (both number and weight average molecular weight) referred to herein are determined by GPC (gel permeation chromatographie) using polystyrene as the standard and tetrahydrofurane as the liquid phase.
Water-based coating compositions are coating compositions, wherein water is used as solvent or thinner when preparing and/or applying the coating composition. Usually, water-based coating compositions contain for example 30 to 90% by weight of water, based on the total amount of the coating composition and optionally, up to 20% by weight, preferably, below 15% by weight of organic solvents, based on the total amount of the coating composition.
Accordingly organic solvent-based coating compositions are coating compositions, wherein organic solvents are used as solvents or thinner when preparing and/or applying the coating composition. Usually, solvent-based coating compositions contain for example 20 to 90% by weight of organic solvents, based on the total amount of the coating composition.
The filler coating composition and the transparent clear coat coating composition used in the process according to the invention will first of all be explained in greater detail.
The filler coating composition and the clear coat coating composition comprise each a “two-component” coating composition, i.e. the components which are reactive towards one another, namely the component comprising active hydrogen (A) and the polyisocyanate component (B), must be stored separately from one another prior to application in order to avoid a premature reaction. Generally binder component A) and polyisocyanate component B) may only be mixed together shortly before application. The term “shortly before application” is well-known to a person skilled in the art. The time period within which the ready-to-use coating composition may be prepared prior to the actual use/application depends, e.g., on the pot life of the coating composition.
In principle, the coating compositions can still be adjusted to spray viscosity with organic solvents prior to application. All the further components which are required for producing a usable coating composition, such as for example pigments, fillers, organic solvents and additives, may in each case be present in one of the two components or in both components of the two-component system.
Also, the epoxy-functional silane compounds C) may be present in one of the two components or in both components. Most preferred the epoxy-functional silane compounds C) are present in the polyisocyanate component B).
The filler coating composition to be used in the process of the present invention preferably comprises 30 to 70% by weight solids of the at least one binder with functional groups containing active hydrogen (component A1) and 20 to 50% by weight solids of the at least one curing agent with free isocyanate groups (component B1), relative to the total amount of the filler coating composition.
The clear coat coating composition to be used in the process of the present invention preferably comprises 30 to 70% by weight solids of the at least one binder with functional groups containing active hydrogen (component A2) and 20 to 50% by weight solids of the at least one curing agent with free isocyanate groups (component B2), relative to the total amount of the clear coating composition.
The terms component A1 and B1 as used here and hereinafter should be taken to mean component A and component B of the filler coating composition.
The terms component A2 and B2 as used here and hereinafter should be taken to mean component A and component B of the clear coat coating composition.
The epoxy-functional silane compounds C) are preferably used in the filler and clear coat coating composition in concentrations of 0.2 to 5.0% by weight solids, in particular of 0.25 to 3.0% by weight solids and most preferred in the filler coating composition of 0.35 to 1.5% by weight solids, and in the clear coat coating composition of 2.0 to 3.0% by weight solids, relative to the sum of the solids content of component A) and component B). If component C) is used in quantities of greater than 5.0% by weight solids in the clear coat coating composition this leads to inferior viscosity and color stability of the multilayer coating.). If component C) is used in quantities of greater than 5.0% by weight solids in the filler coating composition this increases the risk of blistering during humidity/temperature strain and of cracking. If component C) is used in quantities of less than 0.2% by weight solids the described positive effects can not be achieved.
In addition to components A1), B1) and C) the filler coating composition may contain usual components to be used in filler coating compositions, such as pigments, fillers, additives and organic solvents. The pigments, fillers, additives and organic solvents are used in usual quantities known to a skilled person.
In addition to components A2), B2) and C) the clear coating composition may contain usual components to be used in clear coating compositions, such as transparent pigments, additives and organic solvents. The transparent pigments, additives and organic solvents are used in usual quantities known to a skilled person.
Component A1) of the filler coating composition and Component A2) of the clear coating composition comprise binders with functional groups containing active hydrogen. The binders may be oligomeric and/or polymeric compounds with a number average molecular weight (Mn) of, e.g., 500 to 200,000 g/mole, preferably of 1100 to 100,000 g/mole. The functional groups with active hydrogen in particular comprise hydroxyl groups, primary and/or secondary amino groups. Binders with hydroxyl groups are preferably used.
The binders with hydroxyl groups are for example the polyurethanes, (meth)acrylic copolymers, polyesters and polyethers, known from polyurethane chemistry to the skilled person, which are used in the formulation of organic solvent based coating compositions. They may each be used individually or in combination with one another.
Preferably hydroxyl-functional (meth)acrylic copolymers are used as component A).
Examples of (meth)acrylic copolymers include all (meth)acrylic copolymers which are suited for solvent-based coating compositions and known to a skilled person. For example, they can be those with a number average molecular weight Mn of 1000-20000 g/mol, preferably, of 1100-15000, an acid value of 0-60 mg KOH/g, preferably, of 0-35 mg KOH/g and a hydroxyl value of 20-400 mg KOH/g, preferably, of 20-250 mg KOH/g and most preferred of 40-180 mg KOH/g. The (meth)acrylic copolymers can also have been prepared in the presence of different binders, e.g., in the presence of oligomeric or polymeric polyester and/or polyurethane resins.
The preparation of the (meth)acrylic copolymers takes place by usual preparation techniques, e.g., by radical polymerization in the organic phase, in which monomers, solvents and polymerization catalyst are charged into a conventional polymerization reactor.
The (meth)acrylic copolymers thus formed have, for example, a glass transition temperature (Tg) of at least 30° C. and preferably of 40-80° C. But they may also have a glass transition temperature (Tg) of 0° C. and below, for example of −15 to 0° C.
All glass transition temperatures disclosed herein are determined by DSC (differential scanning calorimetry).
Typically useful polymerization catalysts are azo type catalysts such as azo-bis-isobutyronitrile, 1,1′-azo-bis(cyanocylohexane), acetates such as t-butyl peracetate, peroxides such as di-t-butyl peroxide, benzoates such as t-butyl perbenzoate, octoates such as t-butyl peroctoate and the like.
Typical solvents that can be used are ketones such as methyl amyl ketone, methyl isobutyl ketone, methyl ethyl ketone, aromatic hydrocarbons such as toluene, xylene, alkylene carbonates such as propylene carbonate, n-methyl pyrrolidone, ethers, ester, such as butyl acetate, and mixtures of any of the above.
Free-radically polymerizable, olefinically unsaturated monomers, which may be used are monomers which, in addition to at least one olefinic double bond, also contain further functional groups and monomers which, apart from at least one olefinic double bond, contain no further functional groups. Further functional groups may be, for example, urea, hydroxyl, carboxyl, sulfonic acid, silane, amine, amide, acetoacetate or epoxy groups. It would be clear that only those functional groups can be combined in the poly(meth)acrylate copolymer which do not tend to self-crosslink.
Olefinically unsaturated monomers with hydroxyl groups can be used to introduce hydroxyl groups into the (meth)acrylic copolymers. Suitable hydroxy-functional unsaturated monomers are, for example, hydroxyalkyl esters of alpha, beta-olefinically unsaturated monocarboxylic acids with primary or secondary hydroxyl groups. These may, for example, comprise the hydroxyalkyl esters of acrylic acid, methacrylic acid, crotonic acid and/or isocrotonic acid. The hydroxyalkyl esters of (meth)acrylic acid are preferred. The hydroxyalkyl residues may contain, for example, 2-10 C atoms, preferably, 2-6 C atoms. Examples of suitable hydroxyalkyl esters of alpha, beta-olefinically unsaturated monocarboxylic acids with primary hydroxyl groups are hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate, hydroxybutyl (meth)acrylate, hydroxyamyl (meth)acrylate, hydroxyhexyl (meth)acrylate. Examples of suitable hydroxyalkyl esters with secondary hydroxyl groups are 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate and 3-hydroxybutyl (meth)acrylate. Further olefinically unsaturated monomers or adducts with hydroxyl groups may, of course, also be used.
Carboxyl functional olefinically unsaturated monomers are used to introduce carboxyl groups into the (meth)acrylic copolymers. Examples of suitable olefinically unsaturated carboxylic acids include acrylic acid, methacrylic acid, crotonic acid and isocrotonic acid, itaconic acid, maleic acid, fumaric acid and the halfesters of the difunctional acids. Acrylic and methacrylic acid are preferred.
Examples of other additional suitable unsaturated monomers, which contain apart from an olefinic double bond further functional groups are dimethylaminoethyl (meth)acrylate, acetoacetoxyethyl (meth)acrylate, (meth)acrylamide, alkoxy methyl (meth)acrylamides, vinyl silane, methacryloxyethyl trialkoxysilanes, acrylamido 2-methyl propane, vinyl imidazole.
Unsaturated monomers which, apart from at least one olefinic double bond, contain no further functional groups are, for example, aliphatic esters of olefinically unsaturated carboxylic acids, vinyl ester and/or vinylaromatic hydrocarbons.
Examples of suitable aliphatic esters of olefinically unsaturated carboxylic acids include, in particular, esters of alpha, beta-olefinically unsaturated monocarboxylic acids with aliphatic alcohols. Examples of suitable olefinically unsaturated carboxylic acids are acrylic acid, methacrylic acid, crotonic acid and isocrotonic acid. The alcohols are, in particular, aliphatic monohydric branched or unbranched alcohols having 1-20 carbon atoms in the molecule. Examples of (meth)acrylates with aliphatic alcohols are methyl acrylate, ethyl acrylate, isopropyl acrylate, tert.-butyl acrylate, n-butyl acrylate, isobutyl acrylate, 2-ethylhexyl acrylate, lauryl acrylate, stearyl acrylate and the corresponding methacrylates.
Examples of suitable vinyl esters are vinyl acetate, vinyl propionate and vinyl esters of saturated monocarboxylic acids branched in the alpha position, e.g., vinyl esters of saturated alpha,alpha'-dialkylalkane monocarboxylic acids and vinyl esters of saturated alpha-alkylalkane monocarboxylic acids having in each case 5-13 carbon atoms, preferably, 9-11 carbon atoms in the molecule.
Examples of vinylaromatic hydrocarbons preferably are those having 8-12 carbon atoms in the molecule. Examples of such monomers are styrene, alpha-methylstyrene, chlorostyrenes, vinyltoluenes, 2,5-dimethylstyrene, p-methoxystyrene and tertiary-butylstyrene.
The hydroxyl-functional binder component A), i.e. the binder component A1 of the filler coating composition and the binder component A2 of the clear coat coating composition suitably comprises about 10 to 100% by weight solids, preferably 30 to 80 by weight solids, based on the weight solids of the binder of at least one hydroxyl-functional (meth)acrylate copolymer as described above. Preferred (meth)acrylate copolymer comprise:
Examples of alkyl-substituted cycloaliphatic acrylate or methacrylates can include, among others, trimethylcyclohexyl methacrylate, t-butyl cyclohexyl methacrylate, isobornyl methacrylate, or combinations thereof.
Preferred alkyl-substituted aromatic vinyl monomers are alkyl-substituted styrene monomers, such as t-butyl styrene. Blends of the above-mentioned comonomers, for example, t-butylstryrene with such monomers as isobornyl-, t-butylcyclohexyl-, or trimethylcyclohexyl(meth)acrylate are also suitable.
Suitable hydroxyl functional (meth)acrylic copolymers are preferably composed of polymerized monomers of styrene, a methacrylate which is either methyl methacrylate, isobornyl methacrylate, cyclohexyl methacrylate or a mixture of these monomers, a second methacrylate monomer which is either n-butyl methacrylate, isobutyl methacrylate or ethyl hexyl methacrylate or a mixture of these monomers and a hydroxy alkyl (meth)acrylate or acrylate that has 1-8 carbon atoms in the alkyl group such as hydroxy ethyl methacrylate, hydroxy propyl methacrylate, hydroxy butyl methacrylate, hydroxy ethyl acrylate, hydroxy propyl acrylate, hydroxy butyl acrylate and the like.
One further preferred (meth)acrylic copolymer contains the following constituents: styrene, methyl methacrylate, isobutyl methacrylate and hydroxy ethyl methacrylate.
Another preferred acrylic polymer contains the following constituents: styrene, isobornyl methacrylate, ethyl hexyl methacrylate, hydroxy ethyl methacrylate and hydroxy propyl methacrylate.
Another preferred acrylic contains styrene, methyl methacrylate, isobornyl methacrylate, ethyl hexyl methacrylate, isobutyl methacrylate, and hydroxy ethyl methacrylate. Compatible blends of two of the above (meth)acrylic copolymers can also be used.
Optionally, the (meth)acrylic copolymer can contain about 0.5-2% by weight of acrylamide or methacrylamide such as n-tertiary butyl acrylamide or methacrylamide.
Examples of hydroxyl-functional polyester resins which can be used as binder component A) include all polyester resins which are suited for solvent-based coating compositions, for example, hydroxyl-functional polyesters with a number average molecular weight of 500-10,000 g/mol, preferably, of 1100-8000 g/mol, an acid value of 10-150 mg KOH/g, preferably, of 15-50 mg KOH/g and a hydroxyl value of 40-400 mg KOH/g, preferably, of 50-200 g/mol. The polyesters may be saturated or unsaturated and they may optionally be modified with fatty acids. The polyesters are produced using known processes with elimination of water from polycarboxylic acids and polyalcohols.
Also, usual hydroxy-functional polyurethane resins can be used.
The preferred hydroxyl-functional (meth)acrylate copolymers may be used in combination with other hydroxyl-functional resins. The (meth)acrylate resins may advantageously be used in combination with at least one hydroxyl-functional polyester oligomer. Preferred polyester oligomers having a weight average molecular weight (Mw) not exceeding 3,000, preferably of 200-2,000, and a polydispersity of less than 1.7.
Useful oligomers include caprolactone oligomers containing terminal hydroxyl groups which may be prepared by initiating the polymerization of caprolactone with a cyclic polyol, particularly a cycloaliphatic polyol, in the presence of a tin catalysts via conventional solution polymerization techniques. Such caprolactone oligomers are well known and described at length in Anderson et al. U.S. Pat. No. 5,354,797.
Other useful oligomers include alkylene oxide polyester oligomers containing terminal hydroxyl groups which may be made by reacting stoichiometric amounts of a cycloaliphatic monomeric anhydride with a linear or branched polyol in solution at elevated temperatures in the presence of a tin catalyst using standard techniques and then capping the acid oligomers so formed with monofunctional epoxies, particularly alkylene oxide.
Cycloaliphatic anhydride monomers such as hexahydrophthalic anhydride and methyl hexahydrophthalic anhydride are typically employed in the alkylene oxide oligomers above. Aliphatic or aromatic anhydrides, such as succinic anhydride or phthalic anhydride may also be used in conjunction with the anhydrides described above. Typically useful linear or branched polyols include, hexanediol, 1,4-cyclohexane dimethanol, trimethylol propane, and pentaerythritol. Useful monofunctional epoxies include alkylene oxides of 2 to 12 carbon atoms. Ethylene, propylene and butylene oxides are preferred although ethylene oxide is most preferred. Other epoxies, such as. Cardura CE5 or Cardura CE10 glycidyl ether may be used in conjunction with the monofunctional epoxies described above. Particularly preferred alkylene oxide oligomers are formed from methyl hexahydrophthalic anhydride; either 1,4-cyclohexanedimethanol, trimethylol propane, or pentaerythritol; and ethylene oxide reacted in stoichiometric amounts.
Furthermore suitable oligomeric polyesters can be prepared using a monoepoxyester and preferably a monoepoxyester of a branched polycarboxylic acid such as a tertiary fatty acid like Cardura® CE10 (versatic acid CE10) or Cardura® CE5 (pivalic acid CE5). Those oligomeric polyesters can be synthesized by various routes, but preferably by employing a ring-opening polycondensation reaction in which a multi-functional polyol (preferably two to four-functional) or a blend of those polyols, so that the average functionality is at least two, are reacted with an anhydride and/or acid anhydride and further with a sufficient amount of a monoepoxyester to convert the acid groups into hydroxyl groups.
Suitable polyols for the above-mentioned synthesis are glycerine, trimethylolpropane, pentaerythritol, neopentyl glycol, ethyleneglycol, and the like. Suitable anhydrides for the above-mentioned synthesis include succinic anhydride, maleic anhydride, phthalic anhydride, hexahydrophthalic anhydride, methylhexahydrophthalic anhydride, and the like.
Suitable acid-anhydrides for the above-mentioned synthesis are trimellitic anhydride, hydrogenated trimellitic anhydride, the Diels-Alder adduct of maleic anhydride with sorbic acid, the hydrogenated Diels-Alder adduct of maleic anhydride and sorbic acid, and the like.
Suitable monoepoxyesters which can be used for the above-mentioned synthesis are the epoxyesters of benzoic acid, acetic acid, privalic acid (Cardura CE5), versatic acid (Cardura CE10), isobutyric acid (Cardura CE4).
Compatible blends of any of the aforementioned oligomers can be used as well.
In particular those combinations of hydroxyl-functional (meth)acrylate copolymers and hydroxyl-functional polyester oligomers can be used advantageously as component A2) in the clear coat coating composition. Component A2) may comprise 10-100, preferably 30-70% by weight of the at least one (meth)acrylate copolymer and 0-90, preferably 30-70% by weight of the at least one polyester oligomer. Useful combinations of hydroxyl-functional (meth)acrylic copolymers and hydroxyl-functional polyester oligomers are disclosed, for example, in EP 801 661 and U.S. Pat. No. 6,472,493.
The filler and clear coating compositions can also contain low molecular reactive components, so-called reactive thinners, which are able to react with the cross-linking components. Examples of these are hydroxy- or amino-functional reactive thinners.
The filler and clear coating compositions to be used according to the invention contain polyisocyanates with free isocyanate groups (component B) as cross-linking agents. Examples of the polyisocyanates are any number of organic polyisocyanates with aliphatically, cycloaliphatically, araliphatically and/or aromatically bound free isocyanate groups. The polyisocyanates are liquid at room temperature or become liquid through the addition of organic solvents. At 23° C., the polyisocyanates generally have a viscosity of 1 to 3,500 mPas, preferably of 5 to 3,000 mPas.
The preferred polyisocyanates for the clear coating compositions are polyisocyanates or polyisocyanate mixtures with exclusively aliphatically and/or cycloaliphatically bound isocyanate groups with an average NCO functionality of 1.5 to 5, preferably 2 to 4.
Examples of particularly suitable polyisocyanates are what are known as “paint polyisocyanates” based on hexamethylene diisocyanate (HDI), 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI) and/or bis(isocyanatocyclohexyl)-methane and the derivatives known per se, containing biuret, allophanate, urethane and/or isocyanurate groups of these diisocyanates which, following production, are freed from surplus parent diisocyanate, preferably by distillation, with only a residue content of less than 0.5% by weight. Triisocyanates, such as, triisocyanatononan can also be used.
Sterically hindered polyisocyanates are also suitable. Examples of these are 1,1,6,6-tetramethyl-hexamethylene diisocyanate, 1,5-dibutyl-penta-methyldiisocyanate, p- or m-tetramethylxylylene diisocyanate and the appropriate hydrated homologues.
In principle, diisocyanates can be converted by the usual process to higher functional compounds, for example, by trimerization or by reaction with water or polyols, such as, for example, trimethylolpropane or glycerine. The polyisocyanates can also be used in the form of isocyanate-modified resins.
The polyisocyanate cross-linking agents can be used individually or mixed.
The polyisocyanate cross-linking agents are those commonly used in the paint industry, and are described in detail in the literature and are also obtainable commercially.
The isocyanate groups of polyisocyanate crosslinking agent B) may be partially blocked. Low molecular weight compounds containing active hydrogen for blocking NCO groups are known. Examples of these are aliphatic or cycloaliphatic alcohols, dialkylaminoalcohols, oximes, lactams, imides, hydroxyalkyl esters, esters of malonic or acetoacetic acid.
It is especially preferred that the polyisocyanate or polyisocyanate mixture B2) to be used in the clear coating composition comprises at least one low viscous polyisocyanate. The term low viscous polyisocyanates as used here and hereinafter should be taken to mean polyisocyanates having a viscosity of equal to or below 300 mPas, preferably of equal to or below 200 mPas, for example a viscosity of 10 to 300 mPas, preferably of 10 to 200 mPas. Examples of those low viscous polyisocyanates are commercially available polyisocyanates, e.g. Desmodur 3400 from Bayer. The low viscous polyisocyanates can be used alone or in combination with other polyisocyanates with higher viscosity of , for example, 300 to 3000 mPas. The use of those low viscous polyisocyanates as crosslinking agent strengthens the positive effects achieved with the present invention. It also leads to a more favourable balance between spray viscosity and content of volatile organic compounds (VOC) of the clear coat coating composition. Polyisocyanate component B2) can comprise, e.g. 20-80% by weight solids of low viscous polyisocyanates and 80-20% by weight solids of other polyisocyanates, relative to the solids content of component B2).
Although not preferred, the polyisocyanate crossliking agent B) can be used in combination with co-crosslinkers, e.g., in combination with melamine resins and/or completely blocked polyisocyanates.
According to the invention at least one epoxy-functional silane compound of Formula (I) is used as component C) in the filler as well as in the clear coating composition.
Preferred compounds of the formula (I) are those in which X is
with m being 1-4.
Compounds in which R1, R2 and R3 mutually independently mean identical or different alkoxy groups having 1-4, preferably 1, 2 or 3 carbon atoms are likewise preferred. Particularly preferred alkoxy groups are methoxy, ethoxy and isopropoxy groups.
Examples of particularly suitable epoxy-functional silane compounds of the general formula (I) are (3-glycidoxypropyl)trimethoxysilane, (3-glycidoxypropyl)triethoxysilane, (3-glycidoxypropyl)triisopropoxysilane, beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane and beta-(3,4-epoxycyclohexyl)ethyltriethoxysilane. Silanes with methoxy groups, such as for example (3-glycidoxypropyl)trimethoxysilane and beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane are particularly preferred here.
It is most preferred to use (3-glycidoxypropyl)trimethoxysilane.
Epoxy-functional silane compounds which may be used are also obtainable as commercial products, for example under the name Dynasylan Glymo from Degussa, Silquest A-187 and Silquest A-186 from GE Silicones and A-186 and A-187 from ACC Silicones.
The active hydrogen containing, in particular hydroxy-functional binder component A) and the cross-linking agents B) are used in in such quantity ratios that the equivalent ratio of hydroxyl groups of component A) to the isocyanate groups of the cross-linking agent B) is 5:1 to 1:5, for example, preferably, 3:1 to 1:3, particularly preferably, 1.5:1 to 1:1.5. If further hydroxy-functional binders and reactive thinners are used, their reactive functions should be taken into consideration when calculating the equivalent ratio.
The filler and clear coating compositions may contain in addition organic solvents and conventional coating additives. The solvents may originate from the preparation of the binders or they may be added separately. They are organic solvents typical of those used for coatings and well known to the skilled person.
The additives are the conventional additives, which may be used, in the coating sector in filler and clear coats. Examples of such additives typical for use in clear coating compositions include light protecting agents, e.g., based on benzotriazoles and HALS compounds (hindered amine light stabilizers), leveling agents based on (meth)acrylic homopolymers or silicone oils, rheology-influencing agents, such as, fine-particle silica or polymeric urea compounds, anti-foaming agents, wetting agents, curing catalysts for the cross-linking reaction, for example, organic metal salts, such as, dibutyltin dilaurate, zinc naphthenate and compounds containing tertiary amino groups such as triethylamine for the hydroxyl/isocyanate reaction.
Examples of such additives typical for use in filler coating compositions include levelling agents based on (meth)acrylic homopolymers or silicone oils, anticratering agents, antifoaming agents, wetting agents, curing catalysts as disclosed above, dispersing agents, thickeners and emulsifiers.
The filler coating compositions also contain conventional organic and/or inorganic color-imparting pigments and/or extenders as are known to the person skilled in the art for the production of coating compositions, in particular for the production of filler compositions in the vehicle coating sector. Examples of pigments are titanium dioxide, micronized titanium dioxide, iron oxide pigments, carbon black, azo pigments, phthalocyanine pigments, quinacridone and pyrrolopyrrole pigments.
Examples of extenders are silicon dioxide, aluminium silicate, aluminium oxide, barium sulfate and talcum.
The filler coating compositions generally have a weight ratio of extenders and pigments to binder (solids) of preferably, 4.0:1.0 to 1.0:2.0, particularly preferably, of 3.0:1.0 to 1.5 to 1.0. Pigment volume concentration (PVC) is for example in the range of 20 to 65 for filler compositions in general and preferably in the range of 35 to 55 for sanding fillers. PVC is the ratio of volume of pigments/extenders to total volume of all non-volatile components of the composition (including pigments/extenders, binders, additives etc.)
Preferred filler coating compositions which are to be applied in step 1 of the process according to the invention comprise:
Preferred hydroxyl-functional (meth)acrylate resins are those as described already above. In particular preferred are (meth)acrylate copolymers comprising
Preferred clear coat coating compositions which are to be applied in step 3 of the process according to the invention comprise:
A2) at least one hydroxyl-functional (meth)acrylate resin, optionally in combination with at least one hydroxyl-functional oligomeric polyester,
B2) at least one polyisocyanate and
C) at least one epoxy-functional silane of the general Formula (I) as defined above.
Further preferred clear coat coating compositions which are to be applied in step 3 of the process according to the invention comprise:
A2) at least one hydroxyl-functional (meth)acrylate resin, optionally in combination with at least one hydroxyl-functional oligomeric polyester,
B2) at least one low-viscosity polyisocyanate having a viscosity of equal to or below 300 mPas, for example a viscosity of 10 to 300 mPas, and
Preferred hydroxyl-functional (meth)acrylate resins and oligomeric polyesters are those as described already above. Preferred (meth)acrylate copolymers comprise:
Preferably the clear coat coating compositions are substantially free of polyether polyols.
It has been found that, by using the epoxy-functional silane compounds C) in the filler coating composition as well as in the clear coat coating composition of the multilayer structure, it is possible to achieve both greatly improved humidity resistance and adhesion properties, i.e. greatly improved interlayer adhesion between the individual layers and very good cohesion within the water-borne base coat layer, e.g. after humidity/temperature strain. It is assumed here that epoxy-functional silane C) diffuses into the water-borne base coat layer across the boundary layer between clear coat and base coat and across the boundary layer between filler coat and base coat thus contributes to a distinct improvement in interlayer adhesion between the filler layer and the water-borne base coat layer and between the clear coat layer and the water-borne base coat layer. The water-borne base coat layer exhibits very good cohesion, even when applied in relatively thick films of for example 25 μm, as are required for the application of solid water-based base coat coating compositions.
It is especially preferred that component C) is part of the polyisocyanate cross-linking agent. Hence, a further advantage of the present invention is that in both the filler and the clear coat coating composition the same polyisocyanate cross-linking agent containing component C) can be used.
The individual steps of the process according to the invention are explained in greater detail below.
In the multilayer coating process according to the invention, in step 1 a filler layer of the organic solvent-based filler coating composition is applied onto an optionally precoated substrate. Suitable substrates are metal and plastics substrates, in particular the substrates known in the automotive industry, such as for example iron, zinc, aluminium, magnesium, stainless steel or the alloys thereof, together with polyurethanes, polycarbonates or polyolefins.
In the case of vehicle body or vehicle body part coating, the filler coating compositions are applied, preferably by means of spraying, onto the substrates. The substrates, in particular the vehicle bodies or parts thereof may already be precoated in conventional manner before application of the filler coating composition. The prior coating may comprise a coating of a primer coating composition, for example, a wash primer as is conventionally used in vehicle coating. The filler coating compositions may also perform the function of a filler-primer or priming filler. The filler coating compositions are applied usually in a resulting dry film thickness of 25 to 400 μm, for example, in a resulting dry film thickness of 80 to 250 μm in case of sanding fillers (before sanding).
The filler coating composition may also be applied onto an intact existing or original coating, for example, onto electrodeposited primers.
In the multilayer coating process according to the invention, in step 2 a base coat layer of a water-based base coat coating composition is applied onto the filler layer.
The filler layer may be cured or dried or flashed off before application of the water-borne base coat coating composition. In case of sanding fillers the filler layer is, for example, dried or cured at room temperature, e.g. overnight, or dried or cured at temperatures of e.g. 40-60° C.
The water-based base coat coating composition to be applied in step 2) comprises effect or solid-colour base coat coating compositions as are conventionally used in vehicle coating.
The water-based base coat compositions contain the conventional constituents of a water-based pigmented base coat coating composition: color-imparting and/or special effect-imparting pigments, one or more binders, water and optionally at least one of the following constituents: crosslinking agents, fillers, conventional coating additives and organic solvents.
Examples of binders are conventional film-forming, water-dilutable binders familiar to the person skilled in the art, such as water-dilutable polyester resins, water-dilutable (meth)acrylic copolymer resins or water-dilutable polyester/(meth)acrylic copolymer hybrids and water-dilutable polyurethane resins or polyurethane/(meth)acrylic copolymer hybrids. These may be reactive or non-functional resins.
The water-based base coat coating compositions may be physically drying or chemically crosslinking. Accordingly, the water-based coating compositions may contain crosslinking agents, such as, for example, free polyisocyanates. Selection of the optionally used crosslinking agents depends on the type of crosslinkable groups in the binders and is familiar to the person skilled in the art. Physically drying water-based coating compositions are preferred.
Preferably the water-based base coating compositions comprise water-dilutable polyurethane resins, optionally in combination with other water-dilutable resins, e.g. water-dilutable (meth)acrylic copolymers, and with dispersants. Examples of water-dilutable polyurethane resins are those, for example, with a number average molecular weight Mn of 500 to 500 000 g/mol, preferably, of 1100 to 300 000 g/mol, most preferably, of 5000 to 300 000 g/mol, an acid value of 10 to 100 mg KOH/g, preferably of 20 to 80 mg KOH/g. Appropriate polyurethane resins which may be used are, for example, prepared by reacting compounds which are reactive with respect to isocyanate groups and polyisocyanates having at least 2 free isocyanate groups per molecule. The thus obtained polyurethane resins can still be subjected to chain extension to increase the molecular weight. For example, NCO-functional polyurethane prepolymers can be reacted with compounds, which are reactive with respect to isocyanate groups. Compounds, which are reactive with respect to isocyanate groups, are in particular compounds with hydroxyl and/or secondary and/or primary amino groups. OH-functional polyurethane prepolymers can be chain extended for example with polyisocyanates.
Preferably the water-based base coating compositions comprise at least one water-reducible polyurethane/polyurea resin based on polycarbonate and/or polyester polyols. Most preferred the water-based base coating compositions comprise the at least one water-reducible polyurethane/polyurea resin based on polycarbonate and/or polyester polyols in combination with at least one aqueous (meth)acrylic latex. Preferably the aqueous (meth)acrylic latex is prepared by multistage emulsion polymerization in the aqueous phase, comprising the steps:
Useful water-reducible polyurethane/polyurea resins based on polycarbonate polyols and on mixtures of polycarbonate and polyester polyols are described, for example in EP 427 979 and EP 669 352. Useful aqueous (meth)acrylic lattices are described, for example in WO 2006/118974.
The polyurethane/polyurea resins and aqueous (meth)acrylic lattices can be used in combination with pigment dispersants, in particular pigment dispersions based on graft copolymers. The graft copolymers have weight average molecular weights of about 5,000-100,000 and a polymeric backbone and macromonomer side chains attached to the backbone, wherein the polymeric backbone is hydrophobic in comparison to the side chains and contains polymerized ethylenically unsaturated hydrophobic monomers and the side chains are hydrophilic macromonomers attached to the backbone at a single terminal point and contain polymerized ethylenically unsaturated monomers and 2-100% by weight, based on the weight of the graft copolymer, of polymerized ethylenically unsaturated acid containing monomers and have a weight average molecular weight of about 1,000-30,000. Those pigment dispersions are described, for example in U.S. Pat. No. 5,231,131.
The water-based base coat coating compositions contain conventional coating pigments, for example, special effect pigments (effect-imparting pigments) and/or color-imparting pigments selected from among white, colored and black pigments.
Special effect pigments impart to a coating a special effect, e.g. a color flop and/or lightness flop dependent on the angle of observation. Examples of those pigments are conventional effect pigments such as metal pigments. Example of metal pigments are those made from aluminum, copper or other metals, interference pigments such as, for example, metal oxide coated metal pigments, for example, iron oxide coated aluminum, coated mica such as, for example, titanium dioxide coated mica, pigments which produce a graphite effect, iron oxide in flake form, liquid crystal pigments, coated aluminum oxide pigments, coated silicon dioxide pigments. Examples of white, colored and black pigments are the conventional inorganic or organic pigments known to the person skilled in the art, such as, for example, titanium dioxide, iron oxide pigments, carbon black, azo pigments, phthalocyanine pigments, quinacridone pigments, pyrrolopyrrole pigments, perylene pigments.
The water-based base coat coating compositions may contain conventional coating additives in conventional quantities, for example, of 0.1 to 5 wt. %, relative to the solids content thereof. Examples are neutralizing agents, antifoaming agents, wetting agents, adhesion promoters, catalysts, levelling agents, anticratering agents, thickeners, rheology control agents, e.g. layered silicates and light stabilizers.
Once the water-borne base coat coating composition has been applied and optionally dried or cured, the clear coat coating composition is applied in step 3 of the process of the present invention. The clear coat coating composition may here be applied onto the base coat layer either after drying or curing or after briefly flashing off, for example, at room temperature.
The resultant coatings may be cured at room temperature or be forced at higher temperatures, for example of up to 80° C., preferably at 40 to 60° C. They may, however, also be cured at higher temperatures of for example 80-160° C. Curing temperatures are determined by the field of use as well as the by the type of crosslinker. The coating compositions are applied by conventional processs, preferably by means of spray application.
The process according to the invention can be used in automotive and industrial coating, however particularly advantageously in vehicle repair coating. Curing temperatures from 20° C. to 80° C., for example, particularly from 40° C. to 60° C. are used in vehicle repair coating. The coating compositions can also be used advantageously for coating large vehicles and transportation vehicles, such as, trucks, busses and railroad cars, where typically curing temperatures of up to 80° C. or higher than 80° C. are used. Furthermore, the coating compositions can be used for coating any industrial goods other than motor vehicles.
The invention will be explained in more detail on the basis of the examples below. All parts and percentages are on a weight basis unless otherwise indicated.
LE2004, a commercial sanding primer surfacer (from DuPont Refinish), based on a hydroxyl-functional (meth)acrylic copolymer, has been used as base component (hydroxyl component) for the primer.
Desmodur® 3390, a HDI-trimer based polyisocyanate from Bayer has been used as activator (cross-linking agent). The activator has been modified with 6% by weight solids of an epoxy-functional silane of formula (I) (Dynasylan® Glymo from Degussa), relative to the total amount of activator, which corresponds to 2.8% by weight solids of the epoxy-functional silane, relative to the sum of the solids content of the hydroxyl-functional (meth)acrylic copolymer and the polyisocyanate. The non-modified activator, which does not contain the epoxy-functional silane, has been used for comparison (Comp. Activator 1). The activators were formulated with the ingredients shown in Table 1. The amount of the solvents was adjusted in order to keep the solids (70%) constant.
The primer LE2004 (base component) was activated with activator 1 and the comparative activator 1 (7:1 volume ratio base component:activator) to form primer 1 (PR 1) according to the invention and comparative primer 1 (comp. PR 1).
Clear coat 3800, a commercial clear coat from DuPont Refinish, based on a combination of (meth)acrylic polyols and hydroxy-terminated polyester oligomers, has been used as clear coat base component.
Activator 1 as described in Table 1 was used to activate the clear coat 3800 (base component) (3:1 volume ratio base component:activator) to form clear coat 1 according to the invention (CC1). The weight solids of the epoxy-functional silane, relative to the sum of the solids content of the clear coat base component and the activator amounts to 3% in this case. Comparative activator 1 described in Table 1 was used to activate the clear coat 3800 (base component) (3:1 volume ratio base component:activator) to form comparative clear coat 1 without epoxy-functional silane (comp. CC 1).
Primer 1 and comparative primer 1 have been applied on a substrate, pre-coated with an electro-coat coating composition, in a resulting dry film thickness of 80 μm (before sanding) and baked for 30 minutes at 60° C.
A commercial black water-based base coats (Cromax Pro® Jet Black/086 from DuPont; dry film thickness 10 μm -BC 1) has been applied onto the primers. Clear coat 1 and comparative clear coat 1 were applied respectively over the panels with the black base coats on primer 1 and comparative primer 1 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multi-layer coating are shown in Table 2.
Primer compositions have been prepared as in Example 1 (primer 1 and comparative primer 1).
Clear coat 8600, a commercial clear coat from DuPont Refinish, based on a combination of (meth)acrylic polyols and hydroxy-terminated polyester oligomers, has been used as clear coat base component.
Activator 1 as described in Table 1 was used to activate the clear coat 8600 (base component) (3:1 volume ratio base component:activator) to form clear coat 2 according to the invention (CC2). The weight solids of the epoxy-functional silane, relative to the sum of the solid contents of the clear coat base component and the activator amounts to 3% in this case. Comparative activator 1 described in Table 1 was used to activate the clear coat 8600 (base component) (3:1 volume ratio base component:activator) to form comparative clear coat 2 (comp. CC 2).
Primers 1 and comparative primer 1 are applied on a substrate, pre-coated with an electro-coat coating composition, in a resulting dry film thickness of 80 μm (before sanding) and baked for 30 minutes at 60° C.
A commercial silver metallic water-based base coat (Cromax Pro Silbersee/LY7W from DuPont Refinish; dry film thickness 10 μm-BC 2) has been applied onto the primers. Clear coat 2 and comparative clear coat 2 were applied respectively over the panels with the silver metallic base coats on primer 1 and comparative primer 1 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multi-layer coatings are shown in Table 3.
A commercial red water-based base coat (Cromax Pro® Rouge Vif/075 from DuPont Refinish; dry film thickness of 21 μm-BC 3) is applied onto the primers.
Clear coats 2 and comparative clear coat 2 were applied respectively over the panels with the red base coats on primer 1 and comparative primer 1 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multicoating compositions are shown in Table 4.
Primer coating compositions have been prepared as in Example 1 with the only difference that a polyisocyanate mixture of Desmodur® 3400, a HDI-uretdione based polyisocyanate from Bayer and Desmodur® 3390, a polyisocyanate from Bayer has been used as activator (cross-linking agent).
The activators were formulated with the ingredients shown in Table 5. The amount of the solvents was adjusted in order to keep the solids (70% by weight) constant.
The primer LE2004 (base component) was activated with activators 2 and 3 and the comparative activator 2 (7:1 volume ratio base component:activator) to form primers 2 and 3 (PR 2, PR 3) according to the invention and comparative primer 2 (comp. PR 2).
The clear coat 8600 (base component) was activated with activators 2 and 3 and the comparative activator 2 (3:1 volume ratio base component:activator) to form clear coats 3 and 4 (CC 3, CC 4) according to the invention and comparative clear coat 3 (comp. CC 3).
The primers 2 and 3 and comparative primer 2 are applied on a substrate, pre-coated with an electro-coat coating composition, in a resulting dry film thickness of 80 μm (before sanding) and baked for 30 minutes at 60° C.
A commercial silver metallic water-based base coat (Cromax Pro Silbersee/LY7W from DuPont Refinish; dry film thickness 10 μm-BC 2) is applied onto the primers. Clear coats 2 and 3 and comparative clear coat 3 were applied respectively over the panels with the silver metallic base coats on the primer 2 and 3 and comparative primer 2 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multicoating compositions are shown in Table 6.
A commercial red water-based base coat (Cromax Pro® Rouge Vif/075 from DuPont Refinish; dry film thickness of 21 μm-BC 3) is applied onto the primers.
Clear coats 2 and 3 and comparative clear coat 3 were applied respectively over the panels with the red pearl base coats on the primer 2 and 3 and comparative primer 2 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multi-layer coatings are shown in Table 7.
Primer coating compositions have been prepared as in Example 1 with the only difference that a polyisocyanate mixture of Desmodur® 3400, a HDI-uretdione based polyisocyanate from Bayer and Desmodur® 3390, a polyisocyanate from Bayer has been used as activator (cross-linking agent).
The activators were formulated with the ingredients shown in Table 8. The amount of the solvents was adjusted in order to keep the solids (70% by weight) constant.
The primer LE2004 (base component) was activated with activators 4 and the comparative activator 3 (7:1 volume ratio base component:activator) to form primer 4 (PR 4) according to the invention and comparative primer 3 (comp. PR 3).
Clear coat 8035, a commercial clear coat from DuPont, based on a combination of (meth)acrylic polyols and hydroxy-terminated polyester oligomers, has been used as clear coat base component.
Activator 4 described in Table 8 was used to activate the clear coat 8035 (base component) (3:1 volume ratio base component:activator) to form clear coat 5 (CC 5) according to the invention. The weight solids of the epoxy-functional silane, relative to the sum of the solid contents of the clear coat base component and the activator amounts to 2% in this case. Comparative activator 3 described in Table 8 was used to activate the clear coat 8035 (base component) (3:1 volume ratio base component:activator) to form comparative clear coat 4 (comp. CC 4).
Primer 4 and comparative primer 3 are applied on a precoated substrate in a resulting dry film thickness of 80 μm (before sanding) and baked for 30 minutes at 60° C.
A commercial grey pearl water-based base coats (Cromax Pro Delfingrau/LX7Z from DuPont Refinish; dry film thickness 10 μm-BC 4) is applied onto the primers.
Clear coats 5 and comparative clear coat 4 were applied respectively over the panels with the pearl metallic base coats on the primer 4 and comparative primer 3 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multicoating compositions are shown in Table 9.
VOC Nonstop filler, a commercial sanding primer from DuPont Refinish, has been used as primer base component.
The activators were formulated with the ingredients shown in Table 10. The amount of the solvents was adjusted in order to keep the solids (70% by weight) constant.
Activator 5 described in Table 10 was used to activate the VOC Nonstop filler (base component) (5:1 volume ratio base component:activator) to form primer 5 (PR 5) according to the invention. Comparative activator 3 described in Table 10 was used to activate the VOC Nonstop filler (base component) (5:1 volume ratio base component:activator) to form comparative primer 4 (comp. PR 4).
Activator 5 described in Table 10 was used to activate the 8600 clear coat (base component) (3:1 volume ratio base component:activator) to form clear coat 6 (CC 6) according to the invention. The weight solids of the epoxy-functional silane, relative to the sum of the solid contents of the clear coat base component and the activator amounts to 1.5% in this case. Comparative activator 3 described in Table 1 was used to activate the 8600 clear coat (base component) (3:1 volume ratio base component:activator) to form comparative clear coat 5 (comp. CC5).
Primer 5 and comparative primer 4 are applied on a precoated substrate in a resulting dry film thickness of 80 μm (before sanding) and baked for 30 minutes at 60° C.
A commercial silver metallic water-based base coat (Cromax Pro Silbersee/LY7W from DuPont Refinish; dry film thickness 10 μm-BC 2) is applied onto the primers. Clear coats 6 and comparative clear coat 5 were applied respectively over the panels with the silver metallic base coats on primer 5 and comparative primer 4 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multicoating compositions are shown in Table 11.
A commercial grey pearl water-based base coats (Cromax Pro Delfingrau/LX7Z from DuPont Refinish; dry film thickness 10 μm-BC 4) is applied onto the primers. Clear coats 6 and comparative clear coat 5 were applied respectively over the panels with the pearl metallic base coats on the primer 5 and comparative primer 4 in a resulting dry film thickness of 50 μm and baked for 30 minutes at 60° C. Properties of these multicoating compositions are shown in Table 12.
The results clearly show that the multilayer coating prepared according to the invention has improved adhesion properties as can be seen on the basis of the high pressure cleaning resistance (HPC) and of the wet adhesion after humidity cabinet.
In particular important is a rush recovering after strain in humidity cabinet. An improved recovering has been observed still after 4 hours and even after 30 minutes.
Test methods
All multilayer systems were prepared in the same way. Metal panels coated with electro-deposit primer (10×30 cm) were used for all tests. A commercial 2K primer has been applied on the panels, baked for 30 minutes at 60° C. and sanded. A commercial 1K waterborne basecoat has been applied on top of the primer. For solid colors the dry film thickness varied between 20-25 μm. For metallic colors and pearls the dry film thickness varied respectively between 10-15 μm and 15-20 μm. The basecoat was flashed till flat before applying the clear coat. Commercial 2K clear coats were applied over the basecoat and baked 30 minutes at 60° C. The dry film thickness of the clear coats varied between 45-60 μm. All coated panels were aged one week prior to testing.
The test has been performed on an Erichsen VDA 508 apparatus according to a test method, which is conform customer's specifications (Reference:Méthode d'essai du group PSA, no. D241312).
500 g of gravel is projected with a pressure of 1.5 bar under an angle of 45° on the coated panel. This is repeated. A scotch tape is placed over the chipped area and rubbed with a rubber eraser to ensure good contact. In the next step the tape is pulled away from the tester to remove any loose film particles.
The chipping performance is rated from 0 (total failure) till 10 (no failure) according the density and size of the chips, which are described by photographic representations.
This test is performed according to a test method, which is based on Volvo specifications (STD 423-0015).
Before testing high pressing cleaning resistance, which reflects adhesion, an initial paint damage is made on the test panel by scribing two 0.5 mm scribe lines using a scribing tool with a flat shaving steel. The scribed lines are made down to the substrate, at right angles to each other to create a cross.
Water with a temperature of 50° C. is sprayed with a pressure of 150 bar on the damaged panel (φ=4 cm) during 30 seconds. The distance between the gun and the panel amounts to 15 cm.
When the test is completed, the panel is wiped dry and the extension of the paint damage is rated. The % of paint remaining expresses the high pressure cleaning resistance. The numbers in the tables refer to % of removed paint (0% is the best).
This test method is based on ASTM D2247-92 and ASTM D3359-92A.
Dry and wet adhesion are evaluated with the cross-cut tape test. A grid hatch is made with a manual cross cut tester, where the lines are 1 mm apart.
The panels are brushed lightly to remove any detached flakes or ribbons of coating.
A scotch tape is placed over the grid and smoothed into place by a finger. To ensure good contact with the film the tape is rubbed with a rubber eraser. Within 60 to 120 seconds of application, the tape is removed by seizing the free end and pulling it off rapidly back upon itself at as close to an angle of 45 degrees as possible. The dry adhesion is rated a first time from 0 (total failure) till 10 (no failure) according the amount of damage, which is described by photographic representations.
Again pressure-sensitive tape is placed over the same intersection, smoothed into place by a finger and rubbed with a rubber eraser to ensure good contact. Within 60 to 120 seconds of application, the tape is removed by seizing the free end and pulling it off rapidly in opposite direction at as close to an angle of 0 degrees as possible. The dry adhesion is rated a second time from 0 (total failure) till 10 (no failure) according the amount of damage, which is described by photographic representations.
For the evaluation of wet adhesion the same method is used but here the panels are placed for one week in an enclosed chamber, containing heated, saturated mixture of water and water vapour (40° C.), prior to testing. The panels are allowed to recover 30 minutes, 4 hours and 24 hours before they are rated in the same way as above. The type of failure has also been evaluated (number in brackets in the wet adhesion line):
1:substrate/paint failure
2:primer/topcoat failure
3: basecoat/clear coat failure
4: primer/primer failure
5: primer cohesion failure
6:basecoat cohesion failure
This application claims priority from U.S. Provisional Application Ser. No. 61/008,521 (filed Dec. 20, 2007), the disclosure of which is incorporated by reference herein for all purposes as if fully set forth.
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/US08/87558 | 12/19/2008 | WO | 00 | 6/16/2010 |
Number | Date | Country | |
---|---|---|---|
61008521 | Dec 2007 | US |