Process for producing polyolefin thermoplastic elastomer composition

Abstract

A process for producing a polyolefin thermoplastic elastomer composition having superior rubbery elasticity, mechanical properties, etc. and also having improved processing fluidity, workability, etc. is provided, which process comprises blending(A) 40 to 80% by weight of an ethylene-propylene copolymer rubber and/or an ethylene-propylene-diene terpolymer, as a soft segment component,(B) 60 to 20% by weight of a crystalline ethylene-propylene block copolymer having an ethylene content of at least 5% by weight and a melt flow index of 0.5 to 30 g/10 minutes or a crystalline ethylene-propylene random copolymer having an ethylene content of at least 1.5% by weight and a melt flow index of 0.5 to 30 g/10 minutes, each as a hard segment, and based upon 100 parts by weight of the total of (A) and (B),(C) 0.3 to 5 parts by weight of an organosilane,(D) 0.1 to 3 parts by weight of an organic radical-generator,(E) 0 to 5 parts by weight of white carbon, and(F) 0 to 100 parts by weight of an extender oil, followed by subjecting the resulting blend to dynamic partial crosslinking.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a process for producing a polyolefin thermoplastic elastomer composition. More particularly it relates to a process for producing a partially crosslinked polyolefin thermoplastic elastomer composition suitable to extrusion molding or injection molding for thick products.

2. Description of the Related Art

In the case of subjecting conventional rubbers to injection molding, there have been problems that since the process requires steps of blending additives into a rubber, kneading the resulting blend, filling into a mold and vulcanizing, a particular molding machine is required, the cycle time becomes longer and the steps are troublesome. In the case of the extrusion molding, too, similar problems have been raised. Thus, as a stock, a composition substituted for rubbers, which is moldable even without vulcanization and yet provided with rubbery properties has been researched. Among stocks having such properties, soft plastics such as soft vinyl chloride resin, ethylene-vinyl acetate resin, low density polyethylene, etc. are superior in the aspect of both moldability and softness, but on the other hand are inferior in the aspect of heat resistance, mechanical strengths, repellent elasticity, etc.; hence these plastics have been restricted in the use applications.

Thus, in recent years, as materials having intermediate properties between those of vulcanized rubbers and those of soft plastics, compositions comprising an olefin copolymer rubber and an olefin plastic have been noted among thermoplastic elastomers. Namely, research has been made around polypropylene and ethylene-propylene copolymer rubber, for example, a composition obtained by melt-kneading a polyolefin resin with an ethylene-propylene copolymer rubber, disclosed in Japanese patent application laid-open No. Sho 49-53938/1974, a composition having an improved impact strength, obtained by blending an olefin copolymer rubber with an olefin plastic at two stages, disclosed in Japanese patent application laid-open No. Sho 60-71652/1985, etc.

Among these compositions, olefin thermoplastic elastomers having the rubbery part therein partially crosslinked at the time of melt-kneading are so superior in the heat resistance and rubbery elasticity that development thereof has been advanced as a most promising composition. Partially crosslinked olefin thermoplastic elastomers have generally been produced by mechanically melt-kneading an olefin rubber such as ethylene-propylene copolymer rubber or ethylene-propylene-non-conjugated diene terpolymer rubber with polypropylene usually by means of Bambury mixer, kneader, etc. and at the same time adding a crosslinking agent such as organic peroxide, etc. to effect partial crosslinking. As such a process for obtaining thermoplastic elastomers, for example, the following have been proposed: a process of partially crosslinking the rubbery part at melt-kneading (Japanese patent publication No. Sho 53-34210/1977); a process of crosslinking the same by using an organic peroxide, (Japanese patent application laid-open No. Sho 57-172944/1982); a process of partially crosslinking the same by using divinylbenzene as a crosslinking auxiliary (Japanese patent application laid-open No. Sho 57-135846/1982), a process of completely vulcanizing the same with sulfur (Japanese patent application laid-open No. Sho 52-13541/1977); a process of using an organosilane (Japanese patent application laid-open No. Sho 57-23651/1982); etc.

However, compositions obtained by merely melt-kneading an olefin copolymer rubber and an olefin plastic are inferior in the heat resistance and mechanical strength and also inferior in the practical utility. Further, the process accompanied with crosslinking is superior in obtaining a product having a heat resistance, a rubbery elasticity and a mechanical strength, but inferior in the processing fluidity, resulting in an inferior appearance of the resulting molded product. Further, in the case of using an organosilane as a crosslinking auxiliary, a process of post-crosslinking by immersing in hot water in the presence of a catalyst such as dibutyltin dilaurate is required; hence there occurs a new problem of inferior processability.

SUMMARY OF THE INVENTION

The object of the present invention is to provide a process for producing a polyolefin thermoplastic elastomer composition having overcome the drawbacks of conventional melt-kneaded compositions of an olefin copolymer rubber and an olefin plastic, and having superior rubbery elasticity, mechanical properties, etc., and also having improved processing fluidity, processability, etc.

The present inventors have made extensive research in order to achieve the above object, and as a result, have found that when the components (A) to (F) described below are fed directly to a twin-screw extruder and dynamically partially crosslinked, a polyolefin thermoplastic elastomer having improved heat-resistance, mechanical strength, rubbery elasticity and processing fluidity is obtained, and have attained the present invention.

The present invention resides in:

a process for producing a polyolefin thermoplastic elastomer composition, which comprises blending

(A) 40 to 80% by weight of an ethylene-propylene copolymer rubber and/or an ethylene-propylene-diene terpolymer, as a soft segment component,

(B) 60 to 20% by weight of a crystalline ethylene-propylene block copolymer having an ethylene content of at least 5% by weight and a melt flow index of 0.5 to 30 g/10 minutes or a crystalline ethylene-propylene random copolymer having an ethylene content of at least 1.5% by weight and a melt flow index of 0.5 to 30 g/10 minutes, each as a hard segment, and based upon 100 parts by weight of the total of (A) and (B),

(C) 0.3 to 5 parts by weight of an organosilane,

(D) 0.1 to 3.0 parts by weight of an organic radical-generator exhibiting a half-life period of one minute at a temperature of 170.degree. C. or higher,

(E) 0 to 5 parts by weight of white carbon, and

(F) 0 to 100 parts by weight of an extender oil, followed by subjecting the resulting blend to dynamic partial crosslinking.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The main portion of the composition of the present invention is composed of a hard segment and a soft segment, and among these segments, the component constituting the soft segment is preferable to be an ethylene-propylene copolymer rubber (hereinafter referred to as EPM) having a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 10 to 100 and a propylene content of 20 to 50% by weight, or an ethylene-propylene-diene terpolymer (hereinafter referred to as EPDM) having a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 10 to 110, using as the third component diene to be copolymerized, any one of ethylidene, norbornene and 1,4-hexadiene, and having a iodine value (degree of unsaturation) of preferably 16 or less.

The component constituting the hard segment in the composition of the present invention is preferred to be a crystalline ethylene-propylene block copolymer having an ethylene content of at least 5% by weight and a melt flow index of 0.5 to 30 g/10 minutes. This copolymer is a crystalline ethylene-propylene block copolymer obtained by copolymerizing ethylene with propylene at two stages. In the first stage copolymerization, an ethylene-propylene copolymer (hereinafter referred to as polymer 1) having an ethylene content of 0 to 5% by weight is formed so as to occupy 20 to 95% by weight, preferably 50 to 95% by weight of the total quantity polymerized, and in the second stage copolymerization, an ethylene-propylene copolymer (hereinafter referred to as polymer 2) having an ethylene content of 50 to 85% by weight is formed so as to occupy 80 to 5% by weight, preferably 50 to 5% by weight of the total quantity polymerized. As a result, a crystalline ethylene-propylene block copolymer (hereinafter referred to as polymer 3) is obtained. In the case where the polymer 3 as the ultimate composition is used as the hard segment, the higher the proportion ratio of polymer 2 is, the more the quantity of the soft segment used as the component (A) can be reduced.

Further, as another hard segment, a crystalline ethylene-propylene random copolymer having an ethylene content of at least 1.5% by weight and a melt flow index of 0.5 to 30 g/10 minutes can be preferably used, too. This polymer is a crystalline ethylene-propylene random copolymer obtained by copolymerizing ethylene with propylene at one stage. In addition, propylene homopolymer is inferior in the compatibility with EPM or EPDM to reduce rubbery elasticity.

The organosilane compound (C) in the present invention refers to a silane expressed by the formula RR'SiX.sub.2 wherein R represents an organic group including vinyl group, chloro group, amino group, mercapto group, glycidoxy group, methacryloxy group, etc., X represents a hydrolyzable organic group such as methoxy group, ethoxy group, etc., R' represents R or X and the respective Rs (in the case of two Rs) and the respective Xs may be different from each other. Examples of the silane are vinyltrimethoxysilane, vinyltriethoxysilane, 3-aminopropyltriethoxysilane, n-(2-aminoethyl)-3-aminopropyltrimethoxysilane, 3-glycydoxypropyltrimethoxysilane, 3-chloropropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane, etc. Among these, 3-methacryloxypropyltrimethoxysilane is preferably used. The quantity of the organosilane compound blended is 0.3 to 5 parts by weight, preferably 1 to 3 parts by weight based upon 100 parts by weight of (A)+(B). If it is less than 0.3 part by weight, the improving effect is small, while if it exceeds 5 parts by weight, the processing fluidity lowers.

As the organic radical-generator used in the present invention, those having a half-life period of one minute at a temperature of 170.degree. C. or higher are preferred. For example, di-t-butylperoxydiisopropylbenzene, 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane, dicumyl peroxide, etc. are mentioned. The quantity of the organic radical-generator blended is 0.1 to 3 parts by weight, preferably 0.5 to 2 parts by weight based upon 100 parts by weight of (A)+(B). If it is less than 0.1 part by weight, the improving effect is small, while if it exceeds 3 parts by weight, the effect is saturated, and disadvantageous economically.

In the present invention, the crystalline ethylene-propylene block copolymer or the crystalline ethylene-propylene random copolymer, each used as the hard segment may be in a pellet form, but preferably in a powder form in the aspect of dispersibility.

It is desirable to blend white carbon into the composition of the present invention. Since X of the organosilane compound RR'SiX.sub.2 used in the present invention is a hydrolyzable organic radical, a crosslinking reaction is liable to proceed with lapse of time due to moisture in air, etc., but when white carbon is added, it is possible to inhibit the crosslinking reaction with lapse of time, and it is also possible to stabilize the quality of the composition. Further, since the organosilane compound is a liquid, when it is mixed with the powder of the crystalline ethylene-propylene copolymers as the hard segment component, the mixture becomes so viscous that the quantity of the mixture fed to the extruder at the time of granulation varies to make the quality of the composition unstable, whereas, addition of white carbon overcomes such a defect. The quantity of white carbon blended is 0 to 5 parts by weight, preferably 0.3 to 2 parts by weight based upon the total 100 parts by weight of (A)+(B). Even if it exceeds 5 parts by weight, the effect is saturated, and the case is economically undesirable.

Further, an extender oil may be included in the composition of the present invention. This extender oil may be any of paraffin, naphthene and aromatic ones, and a paraffinic processing oil is most preferable in the aspects of hue, odor, etc. The quantity of the extender oil blended is 0 to 100 parts by weight, preferably 0 to 50 parts by weight based upon the total 100 parts by weight of (A)+(B). It may be added over 100 parts by weight, but the strength tends to lower.

In the present invention, the above components (A) to (F) are preliminarily mixed by means of Henschel mixer, tumbler mixer, etc. followed by dynamic partial crosslinking. This dynamic partial crosslinking refers to a process of extruding the mixture of the above (A) to (F) by means of a multi-screw extruder(twin- or three-screw) or milling by means of mill rolls to impart a shearing force of a definite value or more.

As to the shearing force at the time of using a multi-screw extruder, a specific energy W which corresponds to the shearing force and defined according to the following equation, may be in the range of 0.08 to 0.8, preferably 0.1 to 0.6: ##EQU1## wherein W: specific energy (Kw Hr/Kg) I: loaded current (A)

I.sub.O : loaded current at the time of empty-driven screw (A) E: voltage (V) .phi.: power factor Q: extruded quantity (Kg/hr)

Further, the parameters of the crosslinking conditions i.e. the quantity of the organosilane compound, the quantity of the organic radical-generator, the crosslinking temperature and the crosslinking time, are adjusted so as not to attain complete crosslinking. Whether or not a partial crosslinking to a desired extent has occurred in the composition can be judged, for example, by measuring the insolubles of partially crosslinked composition in xylene after reflux for 6 hours. The quantity of the insolubles in xylene that is a gel fraction is preferred to be 20 to 70%, preferably 30 to 60% and also to be larger by 10% or more, particularly 20% or more, than the quantity of uncrosslinked composition. Concretely, in the dynamic partial crosslinking using a twin-screw extruder, it is possible to achieve the object under the conditions of a temperature of 190.degree. to 270.degree. C., preferably 200.degree. to 250.degree. C. and a retention time of 20 to 180 seconds, preferably 50 to 120 seconds. In addition, in the case where a single-screw extruder by which a definite shearing force is not obtained is used, only a product having an inferior dispersibility of the soft segment and the hard segment and also having inferior physical properties is obtained.

The dynamically partially crosslinked composition can be processed or reprocessed by means of conventional processing machines for extrusion molding, injection molding, compression molding, etc.

In the above manner, it is possible to obtain a polyolefin thermoplastic elastomer superior in heat resistance, mechanical strength, rubbery elasticity and processing fluidity.

The thus obtained elastomer is melt-extruded and cut into a suitable form or pelletized in the case of using a multi-screw extruder. A manner of cutting the meltextrudate under water and a manner of mist-cutting the melt-extrudate while injecting water are preferred. Further, it is also possible to employ a hot-cutting manner.

The present invention will be described in more detail by way of Examples and Comparative examples, but it should not be construed to be limited thereto. The evaluation methods employed in Examples and Comparative examples were carried out according to the following methods:

1) MFR: Melt Flow Rate according to JIS K 7210,

______________________________________ temperature: 230.degree. C.load: 2.16 or 10 kgfunit: g/10 min.______________________________________

2) 100% elongation set

______________________________________ Tester: Tensilon UTM-1 typeTest piece: JIS K 7113 No. 1 test pieceLength between chacks: 115 mmLength between bench marks: 50 mmTensile rate: 200 mm/min.______________________________________

When the distance between the bench marks reached 100 mm, the test piece was kept for 10 minutes, followed by opening the chucks, allowing the test piece to stand still, measuring the length between the chucks and calculating the resulting elongation set according to JIS K 6301 (unit %).

3) Stress and elongation at tensile breaking point:

______________________________________ Tester: Strograph W 1 typeTest piece: JIS K 7113 test piece No. 1, according to JIS K 7113Length between the chucks: 115 mmLength between bench marks: 50 mmTensile rate: 50 mm/min. (unit: stress kgf/cm.sup.2, elongation %)______________________________________

4) Stress at 100% elongation:

Calculated from stress at 100% elongation at the time of measurement of 100% elongation set (unit: kgf/cm.sub.2)

5) Flexural elastic modulus:

Tester: Tensilon STM-T-100 type, according to JIS K 7203 (unit: kgf/cm.sup.2)

6) Weather resistance:

Tester: Sunshinesuperlonglife weatherometer

Condition: Rain at 63.degree. C., no rain at 83.degree. C.

Evaluated from crack occurrence time (hr).

7) Heat aging characteristics:

Tester: Gear-type aging tester

Condition: 150.degree. C. and 160.degree. C.

Evaluated from crack occurrence time (hr).

8) Immersion in hot water:

The above-mentioned physical properties after immersion in boiling water for 48 hours were evaluated.

9) Gel fraction:

This is expressed by the percentage (%) of the weight of a residue obtained by placing a sample in a metal gauze of 500 meshes, followed by reflux in xylene for 6 hours, to the weight of the sample before the test.

EXAMPLE 1

To (A) an ethylene-propylene-ethylidenenorbornene terpolymer having a Mooney viscosity (ML.sub.1+4 100.degree. C.) of 88, an ethylene content of 74% by weight and a iodine value of 15, as a soft segment component (2.5 Kg) and (B) a crystalline ethylene-propylene block copolymer having an ethylene content of 7.5% by weight and an MFR (230.degree. C., load 2.16 kgf) of 0.60, as a hard segment component (2.5 Kg), (the total weight of (A) and (B) being 5 Kg), were added (C) 3-methacryloxypropyltrimethoxysilane as an organosilane compound (100 g), (D) 2,5-di-(t-butylperoxy)hexane as an organic radical-generator (75 g), (E) white carbon (mainly SiO.sub.2) (100 g), and Irganox 1010 (Tradename of Ciba Geigy Co., Ltd.) (5 g), BHT (5 g) and calcium stearate (5 g) each as a processing stabilizer, followed by mixing these materials with blending for 2 minutes by means of Henschel mixer or for 15 minutes by means of a tumbler mixer, melt-extruding the resulting mixture by means of a twin-screw extruder (PCM-45 manufactured by Ikegai Tekko Co., Ltd.) at 200.degree. C., pelletizing by means of a mist cutter (PHR 100 manufactured by Ikegai Tekko Co., Ltd.), measuring the melt flow rate (MFR) of the resulting pellets, thereafter injection-molding a test piece for evaluating the physical properties, by means of an injection-molding machine (IS-100 manufactured by Toshiba Kikai Co., Ltd.) under conditions of an injection temperature of 250.degree. C. and a mold temperature of 50.degree. C., and measuring the above-mentioned items 2) to 7). Table 1 shows the polymers of the soft segment component used, Table 2 shows the polymers of the hard segment component, Table 3 shows other components, and Table 4 shows the quantities of these components blended.

EXAMPLES 2-4 AND COMPARATIVE EXAMPLES 1-5

Example 1 was repeated except that the kinds and blended quantities of these components were varied to those shown in Table 4, to carry out pelletization, injection-molding of test pieces and evaluation thereof. The results are shown in Tables 5, 6 and 7.

COMPARATIVE EXAMPLE 6

Example 1 was repeated except that the twin-screw extruder is replaced by a single screw extruder. The results are shown in Table 6.

TABLE 1__________________________________________________________________________ Mooney viscosity Ethylene Amount of thirdKind Type of polymer Trade name Name of maker ML.sub.1+4 100.degree. C. content (wt. %) component (iodine__________________________________________________________________________ value)A.sub.1 Ethylene-propylene- EP57P Japan Synthetic 24 75 -- diene terpolymer Rubber Co., Ltd. rubberA.sub.2 Ethylene-propylene EP02P Japan Synthetic 88 74 15 copolymer rubber Rubber Co., Ltd.__________________________________________________________________________ TABLE 2__________________________________________________________________________ Polymer composition (ethylene content wt. %) Total ethylene First step Second step MFR loadKind Type of polymer amount ethylene amount ethylene amount 2.16 Kgf__________________________________________________________________________B.sub.1 Crystalline ethylene- 7.5 -- 59 0.60 propylene block copolymerB.sub.2 Crystalline ethylene- 11.0 -- 58 2.6 propylene block copolymerB.sub.3 Crystalline ethylene- 3.6 -- -- 2.0 propylene random copolymerB.sub.4 Crystalline ethylene- 15.5 1.5 79 2.3 propylene block copolymerB.sub.5 Propylene homopolymer -- -- -- 0.80__________________________________________________________________________ TABLE 3__________________________________________________________________________Kind General name Chemical name Trade name Name of maker__________________________________________________________________________C.sub.1 Organosilane 3-Methacryloxypropyl- Sila Ace S710 Chisso Corp. compound trimethoxysilaneC.sub.2 Organosilane Vinyltriethoxysilane Sila Ace S220 Chisso Corp. compoundC.sub.3 Organosilane N-(2-aminoethyl)-3- Sila Ace S320 Chisso Corp. compound aminopropyltrimethoxy- silaneC.sub.4 Organosilane 3-Glycidoxypropyltri- Sila Ace S510 Chisso Corp. compound methoxysilaneD Organic radical- 2,5-Dimethyl-2,5-di- Perhexa 25B Nihon Yushi Co. generator (t-butylperoxy)hexaneE White carbon Silicon dioxide AEROSIL200 Nihon Aerosil Co.F Extender oil (Processing oil) Diana process Idemitsu Kosan Co. PW-380__________________________________________________________________________ TABLE 4__________________________________________________________________________ Organic Soft segment Hard Segment Organosilane compound radical-Example or Blended Blended Blended generator White carbon Extender oilComp. ex. Kind amount wt. % Kind amount wt. % Kind amount wt. % D wt. % E wt. % F wt.__________________________________________________________________________ %Ex. 1 A.sub.1 50 B.sub.1 50 C.sub.1 2.0 1.5 2.0 --Ex. 2 A.sub.1 50 B.sub.1 50 C.sub.1 2.0 1.5 -- --Ex. 3 A.sub.1 50 B.sub.2 50 C.sub.1 2.0 1.5 2.0 --Ex. 4 A.sub.1 50 B.sub.2 50 C.sub.1 2.0 1.5 -- --Ex. 5 A.sub.1 50 B.sub.1 50 C.sub.2 2.0 1.5 2.0 --Ex. 6 A.sub.1 50 B.sub.1 50 C.sub.3 2.0 1.5 2.0 --Ex. 7 A.sub.1 50 B.sub.1 50 C.sub.4 2.0 1.5 2.0 --Ex. 8 A.sub.1 50 B.sub.1 50 C.sub.1 0.5 1.5 2.0 --Ex. 9 A.sub.1 50 B.sub.3 50 C.sub.1 2.0 1.5 2.0 --Ex. 10 A.sub.1 50 B.sub.4 50 C.sub.1 2.0 1.5 2.0 --Ex. 11 A.sub.1 50 B.sub.1 50 C.sub.1 2.0 0.3 2.0 --Ex. 12 A.sub.1 50 B.sub.1 50 C.sub.1 2.0 1.0 2.0 --Ex. 13 A.sub.1 50 B.sub.1 50 C.sub.1 2.0 1.5 2.0 25Ex. 14 A.sub.1 50 B.sub.1 50 C.sub.1 2.0 1.5 2.0 45Ex. 15 A.sub.1 60 B.sub.1 40 C.sub.1 2.0 1.5 2.0 --Ex. 16 A.sub.1 80 B.sub.1 20 C.sub.1 2.0 1.5 2.0 --Comp. A.sub.1 50 B.sub.1 50 -- -- -- -- --Ex. 1Comp. A.sub.1 50 B.sub.1 50 -- -- 1.5 -- --Ex. 2Comp. A.sub.2 50 B.sub.2 50 -- -- -- -- --Ex. 3Comp. A.sub.2 50 B.sub.2 50 -- -- 1.5 -- --Ex. 4Comp. A.sub.1 50 B.sub. 5 50 C.sub.1 2.0 1.5 2.0 --Ex. 5__________________________________________________________________________ Note: The sum of soft segment and hard segment is 100 wt. % TABLE 5__________________________________________________________________________ Stress at Elongation Stress at FlexuralExample or MFR g/10 min. 100% Elonga- tensile break- at tensile 100% Elonga- modulusComp. ex. load 10 Kgf tion set % ing point Kgf/cm.sup.2 breaking point % tion Kgf/cm.sup.2 Kgf/cm.sup.2__________________________________________________________________________Ex. 1 18 42 180< 450< 94 2240Ex. 2 17 45 150< 450< 85 2120Ex. 3 5.4 37 103 340 76 1480Ex. 4 4.8 34 115 360 75 1220Ex. 5 149 41 127 335 87 2330Ex. 6 98 43 148 390 90 2540Ex. 7 350 40 106 275 84 2340Ex. 8 258 46 105 140 78 3240Ex. 9 34 44 146< 450< 77 2030Ex. 10 4.2 42 180< 450< 90 2360Ex. 11 0.24 45 144< 450< 109 2380Ex. 12 2.1 42 176< 450< 96 2350Ex. 13 30 20 112 330 65 1300Ex. 14 462 13 53 190 44 580Ex. 15 2.1 32 162 390 -- 1360Ex. 16 0.1> 10 55 220 -- 220Comp. 5.1 48 146 360 133 3340ex. 1Comp. 274 broken 86 149 broken 2560ex. 2Comp. 31 49 112 490 112 2990ex. 3Comp. 254 41 69 520 63 1530ex. 4Comp. 76 51 185< 450< 99 3190ex. 5__________________________________________________________________________ TABLE 6__________________________________________________________________________ Stress at Elonga- StressGranulation conditions MFR tensile tion at at Flexural Extruded Specific g/10 min. 100% e- breaking tensile elonga- elasticExample or Name of Extrusion amount energy Gel frac- load longation point breaking tion modulusComp. ex. extruder temp. .degree.C. Kg/hr Kw .multidot. hr/Kg tion % 10 Kgf set % Kgf/cm.sup.2 point % Kg/cm.sup.2 Kgf/cm.sup.2__________________________________________________________________________Ex. 1 Ikegai 200 27 0.24 59 18 42 180< 450< 94 2240 PCM-45Comp. Ikegai 200 26 0.25 18 254 41 69 520 63 1530ex. 4 PCM-45Comp. Toshiba 230 27 0.07 19 17 broken 195 90 broken 3100ex. 6 SE-65 type__________________________________________________________________________ Ikegai PCM45: twinscrew extender Toshiba SE65 type: singlescrew extruder TABLE 7__________________________________________________________________________ Example or Comparative example Deterioration time (hr) Comparative ComparativeItem Example 1 example 2 Example 3 example 4__________________________________________________________________________Weather 63.degree. C., rain 300 280 420 280resistance 83.degree. C., no rain 130 120 220 120Heat aging 150.degree. C. 9 8 11 8characteristics 160.degree. C. 3 2 5 0.5__________________________________________________________________________

As seen from Table 6, in the case of Comparative example 6 where the same blend as in Example 1 was melt-extruded by means of a single-screw extruder, the specific energy and the gel fraction is so lower than those in Example 1 that the rubbery properties (100% elongation set) are deficient.

EXAMPLES 15 AND 16

The components excluding the extender oil among those in Table 4 were blended in the same manner as in Example 1, followed by melt-extruding the resulting blend by means of a twin-screw extruder (PCM-45 manufactured by Ikegai Tekko Co., Ltd.) at 200.degree. C., while injecting an extender oil in a definite quantity through an injection port by means of a pump to obtain pellets of compositions of Examples 15 and 16. Injection molding of test pieces and their evaluations were carried out in the same manner as in Example 1.

As seen from Examples 1-4 and Comparative examples 1-4, the composition of the present invention has been improved in the elongation set and flexural elasticity as compared with simple blend product or product crosslinked with organic peroxide.

As seen from Examples, 1, 9 and 10 and Comparative example 5, when a crystalline ethylene-propylene block copolymer or a crystalline ethylene-propylene random copolymer is used as the hard segment, the elongation set and flexural elasticity are improved.

As seen from Examples 1, 15 and 16, when the quantities of the hard segment and the soft segment blended are in the definite ranges, it is possible to achieve the effectiveness of the present invention.

As seen from Examples 1, 3, 5, 6 and 7 and Comparative examples 1 to 4, the effect of improving the physical properties due to the organosilane compound is evident, and in particular, the improvement effect of 3-methacryloxypropyltrimethoxysilane is notable.

From Examples 1 and 8, the effect of the quantity of the organosilane compound blended is evident, and from Examples 1, 11 and 12, the effect of the quantity of the organic peroxide blended is evident.

As seen from comparison of Examples 13, 14 and 1, the improvement effects of the fluidity in the processing, elongation set and flexural elasticity due to the blending of the processing oil is notable.

With a material obtained by immersing the test piece of Example 1 in hot water for 48 hours and a material obtained by immersing the test piece of Example 2 in hot water for 48 hours, change in the crosslinking due to water with lapse of time was observed. The results are shown in Table 8. The former case is referred to Example 1', and the latter case, Example 2'.

As seen from the results of Table 8, change in MFR is less when white carbon is used. Further, the product obtained by using white carbon formed no blocks due to coagulation processed easily.

TABLE 8__________________________________________________________________________ MFR 100% Stress at tensile Elongation at Stress at 100% FlexuralExample or g/10 min. elongation breaking point tensile breaking elongation elastic modulusCompar. ex. load 10 Kgf set % Kgf/cm.sup.2 point % Kgf/cm.sup.2 Kgf/cm.sup.2__________________________________________________________________________Example 1 18 42 180< 450< 94 2240Example 1' 6.2 35 167 275 106 2610Example 2 17 45 150< 450< 85 2120Example 2' 0.22 38 171 300 102 2440__________________________________________________________________________ Note: The molded products of Example 1' and Example 2' are samples obtained by subjecting the molded products of Example 1 and Example 2 to immersion in hot water, respectively.

With regard to Comparative examples 1 and 2 and Example 1, test pieces of 10 mm.times.5 mm.times.1 mm were prepared by means of an injection molding machine, followed by measuring the loss tangents (tan .delta.) thereof within a temperature region of -150.degree. to +165.degree. C. by means of a dynamic viscoelasticity-measuring apparatus (DMA 983 type manufactured by Dupont Co., Ltd., resonant frequency mode, temperature-raising rate 5.degree. C./min.). The following peaks were observed: a peak based on the .gamma.-transition of polyethylene (a large portion of ethylene part of ethylene-propylene block copolymer or ethylene-propylene (diene) copolymer) in the vicinity of -100.degree. C., a peak based on the glass transition of ethylene-propylene (diene) copolymer in the vicinity of -20.degree. C. and a peak based on glass transition of polypropylene in the vicinity of room temperature. When Comparative examples 1 and 2 and Example 1 are compared, it was observed that the peak intensities in the vicinity of - 20.degree. C. increase in the order of 0.087 (Comparative example 1), 0.118 (Comparative example 2) and 0.127 (Example 1), and to the contrary the peak intensities in the vicinity of room temperature decrease in this order. In the cases of Comparative example 3 and Example 3, too, the same tendency was observed.

In view of the above facts, it is evident that the composition according to the present invention has been more improved in the elastomeric properties due to the crosslinking.

According to the present invention, it is possible to provide a polyolefin thermoplastic elastomer composition having superior rubbery elasticity and mechanical properties, superior processing fluidity e.g. for injection molding, extrusion molding, etc. of thick products, and superior workability.

Claims

1. A process for producing a polyolefin thermoplastic elastomer composition, comprising the steps of:

forming a blend of

(a) 50 to 80% by weight of an ethylene-propylene copolymer rubber and/or an ethylene-propylene-diene terpolymer as a soft segment component,

(b) 50 to 20% by weight of a crystalline ethylene-propylene block copolymer having an ethylene content of at least 5% by weight and a melt flow index of 0.5 to 30 g/10 minutes and/or a crystalline ethylene-propylene random copolymer having an ethylene content of at least 1.5% by weight and a melt flow index of 0.5 to 30 g/10 minutes as a hard segment, and based upon 100 parts by weight of the total of (a) and (b),

(c) 0.3 to 5 parts by weight of an organosilane,

(d) 0.1 to 3 parts by weight of an organic radical-generator exhibiting a half-life period for one minute at a temperature of 170.degree. C. or higher,

(e) 0 to 100 parts by weight of an extender oil to obtain a resulting blend, and

(f) up to five parts by weight of white carbon;

followed by subjecting the resulting blend to dynamic partial crosslinking carried out by using a twin-screw extruder under the conditions of a temperature of 190.degree. C. to 270.degree. C. and a retention time of 20 to 180 seconds in said extruder so that the residue in xylene after reflux for 6 hours is in the range of 20 to 70% by weight in the resultant partially crosslinked composition, a specific energy W of 0.08 to 0.8, expressed by the formula

W=.sqroot.3.multidot.(I-I.sub.O).multidot.E.multidot..phi./1000.multidot.Q

wherein W=specific energy (KwHr/Kg), I=loaded current (A), I.sub.O =loaded current at the time of empty-driven screw (A), E=voltage (V), .phi.=power factor and Q=extruded quantity (Kg/hr).

2. A process for producing a polyolefin thermoplastic elastomer composition comprising the steps of:

forming a blend of

(a) 50 to 80% by weight of an ethylene-propylene copolymer rubber and/or an ethylene-propylene-diene terpolymer, as a soft segment component,

(b) 50 to 20% by weight of a crystalline ethylene-propylene block copolymer obtained by copolymerizing ethylene with propylene at two stages, in the first stage of which an ethylene-propylene copolymer having an ethylene content of 0 to 5% by weight is formed so as to occupy 20 to 95% by weight of the total quantity polymerized, and in the second stage of which an ethylene-polyethylene copolymer having an ethylene content of 50 to 85% by weight is formed so as to occupy 80 to 5% by weight of the total quantity polymerized, said crystalline ethylene-propylene block copolymer having an ethylene content of at least 5% by weight and a melt flow index of 0.5 to 30 g/10 minutes and/or a crystalline ethylene-propylene random copolymer having an ethylene content of at least 1.5% by weight and a melt flow index of 0.5 to 30 g/10 minutes as a hard segment, and based upon 100 parts by weight of the total of (a) and (b),

(c) 0.3 to 5 parts by weight of an organosilane,

(d) 0.1 to 3 parts by weight of an organic radical-generator exhibiting a half-life period for one minute at a temperature of 170.degree. C. or higher,

(e) 0 to 100 parts by weight of an extender oil to obtain a resulting blend, and

(f) up to five parts by weight of white carbon;

followed by subjecting the resulting blend to dynamic partial crosslinking carried out by using a twin-screw extruder so as to give a specific energy W, of 0.08 to 0.8, expressed by the following formula:

W=.sqroot.3.multidot.(I-I.sub.O).multidot.E.multidot..phi./1000.multidot.Q

wherein W=specific energy (KwHr/Kg),

I=loaded current (A)

I.sub.O =loaded current at the time of empty-driven screw (A)

E=voltage (V)

.phi.=power factor

Q=extruded quantity (Kg/hr).

3. A process for producing a polyolefin thermoplastic elastomer composition comprising the steps of:

forming a blend of

(a) 50 to 80 percent by weight of an ethylene-propylene copolymer rubber and/or an ethylene-propylene-diene terpolymer, as a soft segment component,

(b) 50 to 20% by weight of a crystalline ethylene-propylene block copolymer having an ethylene content of at least 5% by weight in a melt flow index of 0.5 to 30 g/10 minutes and/or a crystalline ethylene-propylene random copolymer having an ethylene content of at least 1.5 percent by weight in a melt flow index of 0.5 to 30 g/10 minutes as a hard segment, and based upon 100 parts by weight of the total of (a) and (b),

(c) 0.3 to 5 parts by weight of an organosilane,

(d) 0.1 to three parts by weight of an organic radical-generator exhibiting a half-life, for one minute at a temperature of 170.degree. C. or higher,

(e) 0 to 100 parts by weight of an extender oil, and (f) up to five parts by weight of white carbon;

followed by subjecting the resulting blend to dynamic partial cross-linking carried out by means of a twin-screw extruder so as to give a specific energy W, of 0.08 to 0.8, expressed by the following formula:

W=.sqroot.3.multidot.(I-I.sub.O).multidot.E.multidot..phi./1000.multidot.Q

wherein W=specific energy (KwHr/Kg),

I=loaded current (A)

I.sub.O =loaded current at the time of empty-driven screw (A)

E=voltage (V)

.phi.=power factor

Q=extruded quantity (Kg/hr).

4. A process for producing a polyolefin thermoplastic elastomer composition according to claim 3, wherein said organosilane is expressed by the formula RR'SiX.sub.2, wherein R represents vinyl group, chloro group, amino group, mercapto group, glycidoxy group or methacryloxy group, X represents methoxy or ethoxy group, and R' represents R or X.

5. A process for producing a polyolefin thermoplastic elastomer composition according to claim 4, wherein said organosilane is at least one compound selected from vinyltrimethoxysilane, vinyltriethoxysilane, 3-aminopropyltriethoxysilane, n-(2-aminoethyl)-3-aminopropyltrimethoxysilane, 3-glycydoxypropyltrimethoxysilane, 3-chloropropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, and, 3-mercaptopropyltrimethoxysilane.

6. A process for producing a polyolefin thermoplastic elastomer composition according to claim 3, wherein said organic radical-generator is at least one compound selected from di-t-butylperoxydiisopropylbenzene, 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane and dicumyl peroxide.

7. A process for producing a polyolefin thermoplastic elastomer composition according to claim 3, wherein said soft segment component is an ethylene-propylene copolymer rubber having a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 10 to 100 and a propylene content of 20 to 50% by weight, or an ethylene-propylene-diene terpolymer having a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 10 to 110, using as the third component diene to be copolymerized, any one of ethylidene, norbornene and 1,4-hexadiene, and having a iodine value (degree of unsaturation) of preferably 16 or less.

8. A process for producing a polyolefin thermoplastic elastomer according to claim 3, wherein said extender oil is at least one compound selected from paraffin, naphthene or aromatic compounds.