Claims
- 1. A process for producing substantially unagglomerated particles of a carbide of silicon or a carbide-forming metal capable of forming a gaseous sub-oxide selected from the group consisting of aluminum, boron, tantlum, titanium, zirconium, hafnium, yttrium, lanthanum, chromium, niobium, molybdenum, tungsten and vanadium from a corresponding oxide, said process comprising:
- forming a uniform dispersion consisting essentially of particles having an average size of less than two microns of said oxide in a polymer having the following characteristics: (a) a molecular weight of at least 10,000 and a long chain structure of at least 200 monomer units and (b) a carbon yield of at least 30% by weight.
- said dispersion being formed by dissolving the polymer in a solvent having a lower affinity for said oxide than the polymer, introducing the oxide particles into the resulting solution, agitating the solution to disperse the particles uniformly, and then removing the solvent from the solution such that said particles are substantially unagglomerated and separated from each other by said polymer;
- carbonizing the resulting dispersion in an inert atmosphere in order to convert the polymer to carbon;
- heating the carbonized product in an inert atmosphere in the presence of a catalyst for the formation of said sub-oxide at a first temperature, which results in the formation of carbide particles or whiskers having an average particle diameter of less than two microns, then raising the temperature to a second temperature to drive the reaction to completion; and
- removing any remaining excess carbon from the resulting carbide product by oxidizing the carbon.
- 2. A process according to claim 1 wherein the solvent is removed from the solution by introducing the solution into a bath of a liquid non-solvent for the polymer, which nonsolvent is miscible with the solvent.
- 3. A process according to claim 1, wherein said polymer is selected from the group consisting of polyacrylonitrile, copolymers thereof and terpolymers thereof.
- 4. A process according to claim 3 wherein said copolymer contains up to 25% by weight of units derived from a copolymerizable monomer.
- 5. A process according to claim 3 wherein said copolymer contains up to 10% by weight of units derived from a copolymerizable monomer.
- 6. A process according to claim 3 wherein said copolymer contains about 6% by weight of units derived from a copolymerizable monomer.
- 7. A process according to claim 4 wherein the copolymerizable monomer is selected from the group consisting of methyl acrylate and methyl methacrylate.
- 8. A process according to claim 3, wherein the polymer/ oxide dispersion is cyclized by heating in air before subjecting the dispersion to the carbonizing step.
- 9. A process according to claim 2, wherein the polymer is selected from the group consisting of polyacrylonitrile, copolymers thereof and terpolymers thereof, the solvent is dimethylformamide and the non-solvent is selected from the group consisting of water and a mixture of water and dimethylformamide.
- 10. A process according to claim 1 wherein the polymer is selected from the group consisting of cellulose, cellulose derivatives, polyvinyl alcohol, copolymers containing units derived from vinyl alcohol, terpolymers containing units derived from vinyl alcohol, polyarylethers, polyacenaphthylene, and polyacetylene.
- 11. A process according to claim 1 wherein said dispersion is heated to a temperature within the range of 500-700.degree. C. in order to carbonize the polymer.
- 12. A process according to claim 1, wherein said first and second temperatures are within the range of 1400.degree. to 2000.degree. C."
- 13. A process according to claim 2 wherein a solid particulate blowing agent is incorporated into said solution before the solution is introduced into the bath and wherein the temperature of the bath is maintained above a decomposition temperature of the blowing agent so that said polymer/oxide dispersion is formed as a hollow product.
- 14. A process according to claim 1 wherein the polymer/ oxide dispersion is ground to form particles which are then packed together before the dispersion is subjected to the carbonizing and carbide-forming step.
- 15. A process according to claim 1 wherein said oxide is selected from the group consisting of the oxides of silicon, titanium, tungsten, zirconium and tantalum.
- 16. A process according to claim 1 wherein said oxide is SiO.sub.2.
- 17. A process according to claim 1 wherein said oxide is TiO.sub.2.
- 18. A process according to claim 1 wherein said oxide is WO.sub.3.
- 19. A process according to claim 1 wherein said oxide is Ta.sub.2 O.sub.5.
- 20. A process according to claim 1 wherein said oxide is ZrO.sub.2.
Priority Claims (2)
Number |
Date |
Country |
Kind |
524364 |
Dec 1986 |
CAX |
|
541167 |
Jul 1987 |
CAX |
|
Parent Case Info
This is a continuation of application Ser. No. 07/126,777. filed Nov. 30, 1987 now abandoned.
US Referenced Citations (11)
Foreign Referenced Citations (6)
Number |
Date |
Country |
2136288 |
Jul 1970 |
DEX |
52-150416 |
Jun 1976 |
JPX |
52-103408 |
Jul 1976 |
JPX |
54-125200 |
Sep 1979 |
JPX |
56-17910 |
Jan 1981 |
JPX |
2162504A |
Feb 1986 |
GBX |
Non-Patent Literature Citations (4)
Entry |
U.S. Application Ser. No. 541,188, 12/7/84 (Chemical Abstracts 102:977336). |
Oak Ridge National Laboratory-Carbothermal Synthesis of Silicon Carbide Janney, et al.-May 1985. |
Synthesis of Sinterable SiC Powders by Carbothermic Reduction of Gel-Derived Precursors and Pyrolysis of Polycarbosilane-Wei, et al.-vol. 63, No. 8 (1984). |
"ORLON" Acrylic Fiber: Chemistry and Properties-R. C. Houtz Textile Research Journal, Nov. 1950. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
126777 |
Nov 1987 |
|