Claims
- 1. A process for reclaiming waste plastics having an urethane paint film or an amino resin paint film on a base resin, comprising the steps of subjecting the paint film to hydrolysis treatment to decompose the paint film into low molecular weight hydrolysis products, kneading the plastics and resulting hydrolysis products to disperse the hydrolysis products in the base resin and recovering a reclaimed waste plastics product suitable for molding.
- 2. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted by immersing the waste plastics having the paint film in a treating liquid and heating the plastics to a temperature not more than a melting point of the plastics.
- 3. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted by immersing the waste plastics having the paint film in a treating liquid and heating the plastics above a melting point of the plastics.
- 4. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted by heating the waste plastics having the paint film to a temperature not more than a melting point of the plastics in the presence of vapor of a treating liquid.
- 5. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted by heating the waste plastics having the paint film to a temperatures above a melting point of the plastics in the presence of vapor of a treating liquid.
- 6. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted by melting and kneading the waste plastics having the paint film at a temperature above a melting point of the plastics, while a treating liquid is added to the plastics.
- 7. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein there is employed in the hydrolysis treatment a treating liquid comprising water, alcohol or a mixture thereof.
- 8. The process for reclaiming waste plastics having the paint film according to claim 7, wherein the treating liquid includes a catalyst selected from the group consisting of acids, alkalies, metallic salts, organic salts and activated clay.
- 9. The process for reclaiming the waste plastics having the paint film according to claim 8, wherein the treating liquid includes an acid or an alkali in an amount of from 0.1 to 10% by weight.
- 10. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted under applied pressure.
- 11. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein the hydrolysis treatment is conducted under ambient pressure.
- 12. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein said base resin is a thermoplastic resin selected from the group consisting of polypropylene, elastomer modified polypropylene, polyethylene, ABS resin, AS resin, polyacetal resin, polyphenylene oxide and mixtures thereof.
- 13. The process for reclaiming the waste plastics having the paint film according to claim 1, wherein said amino resin paint film is one selected from the group consisting of polyester-melamine paint films and acrylic-melamine paint films.
- 14. The process for reclaiming the waste plastics having the paint film according to claim 7, wherein said acid is one selected from the group consisting of hydrochloric acid, sulfuric acid, phosphoric acid, acetic acid, oxalic acid and tartaric acid; and said alkali is one selected from the group consisting of sodium hydroxide, potassium hydroxide and sodium alcoholates.
- 15. The process for reclaiming the waste plastics having the paint film according to claim 2, wherein said treating liquid is water.
- 16. The process for reclaiming the waste plastics having the paint film according to claim 2, wherein said treating liquid is alcohol.
- 17. The process for reclaiming the waste plastics having the paint film according to claim 16, wherein said alcohol is one selected from the group consisting of methanol, ethanol, propanol, ethylene glycol, methyl cellosolve and ethyl cellosolve.
- 18. A process for reclaiming waste plastics having a paint film comprising the steps of: pulverizing a plastic molding comprising a base resin having a paint film thereon,
- hydrolyzing the paint film on the resulting pulverized material by immersing the pulverized material in a treating liquid, and
- kneading the resulting pulverized material subjected to the hydrolysis to disperse the products of the hydrolysis in the base resin.
- 19. A process for reclaiming waste plastics having an urethane paint film or an amino resin paint film on a base resin, comprising the steps of subjecting the paint film to hydrolysis treatment and then kneading the plastics having thereon the paint film subjected to the hydrolysis treatment to disperse the paint film subjected to the hydrolysis treatment finely and uniformly in the base resin so that the resulting dispersed paint film has a particle size of about several micrometers, and recovering a reclaimed waste plastics products suitable for molding.
Priority Claims (5)
Number |
Date |
Country |
Kind |
3-192431 |
Jul 1991 |
JPX |
|
3-357843 |
Dec 1991 |
JPX |
|
3-357844 |
Dec 1991 |
JPX |
|
4-048000 |
Feb 1992 |
JPX |
|
4-105536 |
Mar 1992 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 07/982,738, filed as PCT/JP92/00847, Jul. 3, 1992, now abandoned.
US Referenced Citations (4)
Foreign Referenced Citations (7)
Number |
Date |
Country |
430199A2 |
Jun 1991 |
EPX |
4033862 |
Apr 1992 |
DEX |
4105285 |
Aug 1992 |
DEX |
51-52478 |
May 1976 |
JPX |
53-25677 |
Mar 1978 |
JPX |
54-70377 |
Jun 1979 |
JPX |
55-140528 |
Nov 1980 |
JPX |
Non-Patent Literature Citations (2)
Entry |
Plastverarbeiter, vol. 42, No. 7, Jul. 1991, Speyer/Rhein. |
Technology for Automobile, vol. 46, No. 1, 1992 (pp. 39-46). |
Continuations (1)
|
Number |
Date |
Country |
Parent |
982738 |
Apr 1993 |
|