Claims
- 1. A method of preparing substantially dry water swellable polyelectrolyte fibers which comprises
- 1. preparing a solution comprising
- I. a solvent selected from the groups consisting of water, lower alcohols and mixtures thereof,
- Ii. about 5 to about 60% by weight based on (I) of a crosslinkable carboxylic copolymer which contains in the copolymer
- A. about 25 to about 98% by weight based on the total weight of the copolymer of units derived from an alkali metal salt of an olefinically unsaturated monosulfonic or monocarboxylic acid;
- B. about 2 to about 50% by weight of units derived from an olefinically unsaturated monocarboxylic acid; and
- C. about 0.1 to about 5.0% by weight of units derived from an N-substituted acrylamide or methacrylamide wherein the substituent group is a hydroxy methylene or an alkoxymethylene group having 1-8 carbons,
- 2. extruding said solution into a bath comprising lower alkyl ketones or chlorinated hydrocarbons to form an extruded fiber,
- 3. separating the extruded fiber from said bath, and
- 4. heating said fibers to a temperature greater than about 30.degree. C. to crosslink said polyelectrolyte.
- 2. The polyelectrolyte fiber produced by the method of claim 1.
- 3. A method as set forth in claim 1 wherein the crosslinkable carboxylic copolymer contains 90 weight percent of units derived from sodium acrylate, 9 weight percent of units derived from acrylic acid and 1.0 weight percent of units derived from N-methylolacrylamide.
- 4. A method as set forth in claim 1 wherein the crosslinkable carboxylic copolymer contains 79 weight percent of units derived from sodium styrene sulfonate, 20 weight percent of units derived from acrylic acid and 1.0 weight percent of units derived from N-methylolacrylamide.
- 5. A method as set forth in claim 1 wherein the crosslinkable carboxylic copolymer contains 90 weight percent of units derived from sodium acrylate, 9 weight percent of units derived from acrylic acid and 1.0 weight percent of units derived from N-isobutoxymethylacrylamide.
- 6. A method as set forth in claim 1 wherein the crosslinkable carboxylic copolymer contains 79.7 weight percent of units derived from sodium acrylate, 20 weight percent of units derived from acrylic acid, and 0.3 weight percent of units derived from N-methylolacrylamide
- 7. The polyelectrolyte fiber produced by the method of claim 3.
- 8. The polyelectrolyte fiber produced by the method of claim 4.
- 9. The polyelectrolyte fiber produced by the method of claim 5.
- 10. The polyelectrolyte fiber produced by the method of claim 6.
Parent Case Info
CROSS-REFERENCE TO RELATED APPLICATION
This is a divisional, of application Ser. No. 494,439, filed Aug. 5, 1974.