Claims
- 1. A process for forming a resist mask comprising the steps of (1) coating onto a substrate a layer comprising a mixture of polyamic acid material of reduced acidity comprising a polyamic acid having the general formula ##STR7## wherein Q is C or C=O, R is a divalent aromatic or aliphatic radical having no active hydrogen, R.sub.1 is hydrogen or an alkyl group containing 1 to 3 carbon atoms, and R.sub.2 and R.sub.3 are independently selected from H, CH.sub.3, C.sub.n H.sub.2n+1 where n is a positive integer, and CF.sub.3, m is an integer from 0 to 1 and p is a positive integer, which is reacted or blended to form (a) a polyamic acid material having a level of acidity which is reduced by from about 10 to about 40 percent of the original polyamic acid and (b) a diazoquinone photosensitizer, each of (a) and (b) being present in sufficient quantity to form a photoresist composition which, after radiation exposure and development in alkaline solution, produces a resist image of fine line resolution, (2) image-wise exposing said layer to a source of radiation and then (3) developing said layer in an alkaline developer solution to remove the exposed portion of the layer whereby the exposed photoresist exhibits a reduced dissolution rate in the developer.
- 2. The process of claim 1 wherein the polyamic acid of reduced acidity is prepared by partially imidizing the polyamic acid prior to radiation exposure.
- 3. The process of claim 2 wherein the polyamic acid is partially imidized to an imidization level of from about 10 to about 30 percent.
- 4. The process of claim 1 wherein the diazoquinone photosensitizer is 2,3,4-tri[(6-diazo-5,6-dihydro-5-oxo-napthalenyl) sulfonyl-oxy]benzophenone.
- 5. The process of claim 1 wherein the diazoquinone photosensitizer is 4,8-bis[6-diazo-5,6-dihydro-5-oxo-1-naphthalenyl) sulfonyl oxy methyl] tricyclo [5.2.1.0.sup.2,6 ] decane.
- 6. The process of claim 1 wherein the diazoquinone sensitizer is incorporated in the photoresist composition at a concentration of about 5 to about 25 percent by weight.
- 7. The process of claim 1 wherein the polyamic acid has the formula ##STR8##
- 8. The process of claim 1 wherein the layer is image-wise exposed with ultraviolet light in step (2), and after exposure is baked at about 100.degree. to about 130.degree. C. and blanket exposed with ultraviolet light whereby upon development in step (3) a negative resist is produced.
- 9. A method of reducing the dissolution rate of a photoresist composition comprised of a mixture of a polyamic acid and a diazoquinone photosensitizer, which comprises reducing the acidity of a polyamic acid having the general formula ##STR9## wherein Q is C or C=O, R is a divalent aromatic or aliphatic radical having no active hydrogen, R.sub.1 is hydrogen or an alkyl group containing 1 to 3 carbon atoms, and R.sub.2 and R.sub.3 are independently selected from H, CH.sub.3, C.sub.n H.sub.2n+1 where n is a positive integer, and CF.sub.3, m is an integer from 0 to 1 and p is a positive integer, by reacting or blending said polyamic acid to form (a) a polyamic acid material having a level of acidity which is reduced by from about 10 to about 40 percent of the original polyamic acid and mixing (a) with (b) a diazoquinone photosensitizer, each of (a) and (b) being present in sufficient quantity to form a photoresist composition which, after radiation exposure and development in alkaline solution, produces a resist image of fine line resolution.
- 10. The method of claim 9 wherein the polyamic acid or reduced acidity is a partially imidized polyamic acid.
- 11. The method of claim 10 wherein the polyamic acid is partially imidized to an imidization level of from about 20 to about 40 percent.
- 12. The method of claim 9 wherein the polyamic acid of reduced acidity is a carboxylate amine salt formed by the reaction of a polyamic acid and a basic organic compound.
- 13. The method of claim 9 wherein the polyamic acid of reduced acidity is a polyamic acid wherein a portion of the free carboxylic acid groups of the polyamic acid have been neutralized by reaction with an organic base.
- 14. The method of claim 13 wherein the organic base is triethylamine.
- 15. The method of claim 9 wherein the polyamic acid of reduced acidity is selected from the group consisting of a blend of a polyamic acid with (a) an ester derivative thereof, (b) a copolymer of the polyamic acid and an ester derivative thereof and (c) mixtures thereof.
- 16. The method of claim 9 wherein the polyamic acid has the formula ##STR10##
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a division of U.S. Ser. No. 107,505, filed October 8, 1987, U.S. Pat. No. 4,880,722 which is a continuation-in-part of U.S. Ser. No. 804,869, filed December 5, 1985, abandoned.
US Referenced Citations (21)
Non-Patent Literature Citations (1)
Entry |
De Forest, W. S., "Photoresist Materials and Processes", McGraw-Hill Book Co., 1975, pp. 147-149. |
Divisions (1)
|
Number |
Date |
Country |
Parent |
107505 |
Oct 1987 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
804869 |
Dec 1985 |
|