Process of making U.V. cured polyurethanes using diazonium salt promoters

Information

  • Patent Grant
  • 4544466
  • Patent Number
    4,544,466
  • Date Filed
    Tuesday, December 6, 1983
    41 years ago
  • Date Issued
    Tuesday, October 1, 1985
    39 years ago
Abstract
A process for the rapid curing of polyurethanes comprising the steps of (a) mixing together a diisocyanate compound, a diol, a polyol, and a diazonium salt and thereafter (b) exposing the resulting mixture to ultraviolet light in the wavelength range of about 2000 to about 4000 Angstroms for a period of about 0.1 second to about 20 minutes at a temperature in the range of about 0.degree. F. to about 180.degree. F.
Description

This invention relates to a process for the rapid curing of polyurethane compounds in the presence of ultraviolet light sensitive diazonium salt compounds.
The reaction of diisocyanates, diols, and polyols to form polyurethane compounds is well known. Furthermore, the addition of such promoters as tin salts and tertiary amines to the urethane reaction mixture is also known. The disadvantage of using these reaction promoters, though, is that they promote almost instantaneous curing of the urethane which is not always desirable. Instead, it may be more desirable to add the reaction promoter with urethane curing achieved later on.
Therefore, it is an object of this invention to provide a rapid, efficient process for the curing of polyurethane compounds yet which does not take place almost immediately when a promoter is added to the urethane reaction mixture.
Other aspects, objects, and advantages of the present invention are apparent from the specification and claims.
In accordance with the present invention, I have discovered that in a process wherein hydroxy-containing hydrocarbons and diisocyanates are reacted to form urethane polymers, an improvement is made in the curing process by the addition of ultraviolet light activated diazonium salts to the reaction mixture. In this manner, curing is not achieved until the reaction mixture is exposed to ultraviolet light sufficient to affect activation of the diazonium salt compound. This contrasts sharply with the situation wherein undesired instantaneous curing is achieved with the addition of certain tin salts and tertiary amines to the reaction mixture.
Briefly, the process of my invention comprises the steps of (a) mixing together a diisocyanate compound, a diol, a polyol, and a diazonium salt compound and then thereafter (b) exposing the resulting mixture to ultraviolet light.
The diisocyanate compounds useful in the present invention are those represented by the formula OCN--R--NCO wherein R is a C.sub.4 to C.sub.12 alkylene, arylene, alkarylene, or aralkylene radical.
Exemplary of such diisocyanate compounds include 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, polymethylene polyphenyl isocyanate, hexamethylene diisocyanate, 4,4'-methylene bis(cyclohexyl isocyanate) and mixtures thereof. Presently preferred are 4,4'-methylene bis(cyclohexyl isocyanate), and mixtures of 2,4- and 2,6-toluene diisocyanate.
Any suitable diol may be used in the present invention such as 1,4-butane diol, polypropylene glycol, and hydroxy-terminated polyesters and mixtures thereof.
Additionally, any suitable polyol may be used in the present invention as well. Exemplary of such polyols are trimethylolpropane, pentaerythritol, glycerol, 1,4,6-hexanetriol, polyether polyols such as those derived from 1,2,6-hexanetriol and propylene oxide and mixtures thereof.
The diazonium salts useful in the present invention are those represented by the formula: ##STR1## wherein R.sup.1 represents an electron withdrawing group (preferably either F, Cl, Br, I, or NO.sub.2), M is an element selected from the group consisting of B, P, As, Sb, Bi, and Sn, n is 4, 5, or 6, and x is 1, 2, or 3.
Examples of such diazonium salts are:
p-chlorobenzenediazonium tetrafluoroborate
p-chlorobenzenediazonium hexafluorophosphate
p-bromobenzenediazonium hexafluorophosphate
p-fluorobenzenediazonium hexafluorophosphate
p-iodoenzenediazonium hexafluoroarsenate
p-nitrobenzenediazonium hexafluoroarsenate
p-nitrobenzenediazonium tetrafluoroborate
p-nitrobenzenediazonium hexafluoroarsenate
2,4-dichlorobenzenediazonium tetrafluoroborate
2,4-dibromobenzenediazonium hexafluoroarsenate
2,4-dichlorobenzenediazonium hexafluorophosphate
2,4-dichlorobenzenediazonium pentafluorostannate
2,4-dichlorobenzenediazonium hexafluorobismate
2,4,6-trichlorobenzenediazonium tetrafluoroborate
2,4,6-trichlorobenzenediazonium hexafluorophosphate
2,4,6-trichlorobenzenediazonium hexafluoroarsenate
2,4,6-trichlorobenzenediazonium hexafluoroantimonate
2,4-dinitrobenzenediazonium pentafluorostannate
2,6-dichlorobenzenediazonium hexafluoroborate
and mixtures thereof.
The synthesis of diazonium salts is well known in the art. Generally, it involves the reaction of a primary aromatic amine, NaNO.sub.2, and a mineral acid at a temperature usually in the range of about 0.degree. C. to about 25.degree. C.
In the present invention, the amount of diazonium fluoro compound employed is generally about 0.5 to about 5 weight percent based on the total weight of the isocyanate/diol/polyol/diazonium salt mixture.
Generally, the same approximate number of equivalents of diisocyanate should be employed as the total hydroxy equivalent amount of the diol and polyol.
After thorough mixing of the above ingredients, the above mixture is exposed to ultraviolet light, generally in the wavelength of about 2000 to about 4000 Angstroms to effect curing of the polyurethanes. Such light is available from sunlight and from many different commercial lamps including mercury vapor lamps, UV fluorescent lamps, and the like.
Conditions of exposure to ultraviolet light under which the desired product is obtained are generally exposure of about 0.1 second to about 20 minutes at a temperature in the range of about 0.degree. F. to about 180.degree. F., preferably about 1 minute to 5 minutes at a temperature in the range of about 75.degree. F. to about 140.degree. F.
The cured compounds of this invention are useful as resins in both the paint and ink industries.
The following examples further illustrate the present invention.





EXAMPLE I
This example describes the general procedure used to synthesize the diazonium compounds disclosed herein.
p-Chlorobenzenediazonium tetrafluoroborate was prepared as follows: To an 800 milliliter beaker was added 60 milliliters of concentrated hydrochloric acid and 60 milliliters of water followed by 12.75 grams (0.1 mole) of p-chloroaniline. The mixture was then cooled in a wet-ice bath and diazotized with 14 grams (0.2 mole) sodium nitrite dissolved in 24 milliliters of water. This solution was then filtered and the filtrate added slowly with a high rate of stirring to 34 grams (0.3 mole) of sodium tetrafluoroborate dissolved in 60 milliliters of water. The resultant mixture was stirred for an additional 5 minutes and then filtered. The residue was washed with 100 milliliters of distilled water which dissolved away about 50 percent of the product. The remaining material was dried for 4 hours at ambient room temperature and stored in a vacuum desiccator until used.
Additional similar diazonium compounds were prepared in the same manner. These compounds are listed in Table I.
TABLE I______________________________________Preparation of Aromatic Diazonium Fluoro CompoundsBasic IngredientsCom- Fluoro-pound Amine Salt Product______________________________________1 p-Chloroaniline NaBF.sub.4 p-Chlorobenzenediazonium tetrafluoroborate2 p-Chloroaniline NaPF.sub.6 p-Chlorobenzenediazonium hexafluorophosphate3 p-Nitroaniline NaAsF.sub.6 p-Nitrobenzenediazonium hexafluoroarsenate4 p-Nitroaniline NaBF.sub.4 p-Nitrobenzenediazonium tetrafluoroborate5 p-Nitroaniline NaPF.sub.6 p-Nitrobenzenediazonium hexafluorophosphate6 2,4-Dichloro- NaBF.sub.4 2,4-Dichlorobenzene- aniline diazonium tetrafluoroborate7 2,4-Dichloro- NaPF.sub.6 2,4-Dichlorobenzene- aniline diazonium hexafluorophosphate8 2,4,6-Trichloro- NaBF.sub.4 2,4,6-Trichlorobenzene- aniline diazonium tetrafluoroborate9 2,4,6-Trichloro- NaPF.sub.6 2,4,6-Trichlorobenzene- aniline diazonium hexafluorophosphate10 2,4,6-Trichloro- NaAsF.sub.6 2,4,6-Trichlorobenzene- aniline diazonium hexafluoroarsenate______________________________________
EXAMPLE II
This example describes a qualitative determination of the sensitivity of substituted benzenediazonium polyfluoro compounds in a typical isocyanate/polyol reaction and illustrates that unlike other catalysts the diazonium compounds do not catalyze the isocyanate/polyol reactions unless subjected to ultraviolet light.
A mixture of 13.1 grams (0.1 equivalent) of Hylene W 4,4'-methylene bis(cyclohexyl isocyanate), 3.60 grams (0.08 equivalent) of 1,4-butenediol and 1.02 grams (0.02 equivalent) of trimethylolpropane were mixed and placed in a test tube to which was then added 0.35 gram of a catalyst assumed to be dibutyltindilaurate. This catalyst was prepared in-situ from 0.17 gram (0.0006 mole) dibutyltin dichloride, 0.13 grams (0.0006 mole) of p-chlorobenzenediazonium tetrafluoroborate, and 0.11 gram (0.0006 mole) of lauric acid. The isocyanate/polyol/catalyst mixture cured to a hard foamy material within 10 minutes of mixing.
The procedure was repeated except the catalyst in-situ mixture was replaced with only 0.17 gram (0.0006 mole) dibutyltin dichloride. Again the isocyanate/polyol/catalyst mixture cured to a hard foamy material in 10 minutes.
Again the procedure was repeated except the catalyst consisted of only 0.13 gram (0.0006 mole) p-chlorobenzenediazonium tetrafluoroborate. The isocyanate/polyol/catalyst mixture did not cure at ambient room temperature in over 3 hours. The mixture was then irradiated with a 4 inch 100 Watt/inch Hanovia ultraviolet light whereupon some curing took place. Heating to about 150.degree. F. (66.degree. C.) and irradiating for 6 minutes resulted in about one-half the solution being cured. The cured material had a dark cherry red color.
These results which are summarized in Table II show the p-chlorobenzenediazonium tetrafluoroborate useful as a catalyst that is activated upon exposure to ultraviolet light.
TABLE II______________________________________Effect of Catalyst on a Isocyanate/Polyol Reaction13.1 g (0.1 eq.) 4,4'-methylene bis(cyclohexyl isocyanate) 3.6 g (0.08 eq.) 1,4-butanediol 1.02 g (0.02 eq.) trimethylolpropaneRunNo. Catalyst Results______________________________________1 0.35 g In-Situ dibutyltin dilaurate 1. Cures to hard (0.17 g dibutyltin dichloride foamy material in 0.11 g lauric acid 10 minutes. 0.13 g p-chlorobenzenediazonium tetrafluoroborate)2 0.17 g dibutyltin dichloride 2. Cured to hard foamy material in 10 minutes.3 0.13 g p-chlorobenzenediazonium 3. Does not cure in tetrafluoroborate 3 hours. Partial cure after U.V. exposure.______________________________________
EXAMPLE III
This example describes the procedure used to evaluate the diazonium fluoro compounds as catalysts for the isocyanate/polyol curing reaction.
The isocyanate, polyols and catalyst were mixed and placed in a quartz test tube. The contents were then exposed to ultraviolet light (4 inch 100 watt/inch Hanovia lamp) for the various times. The temperature of the liquid rose to about 150.degree. F. (66.degree. C.) due to the heat from the lamp. After 1 minute exposure time, the solution was cooled, transferred into a Soxhlet extractor through which refluxing acetone passed for about 8 hours. The remaining solid material was filtered, dried and weighed to determine the amount of polymerization that had occurred. This value was reported as % Polymerization. The process was repeated at 3, 5 and 10 minute exposure times.
These results are listed in Table III and indicate the best catalysts are those based on hexafluoro phosphorous (Runs 2, 5, 7 and 9) followed by those based on hexafluoro arsenic (Runs 3 and 10) followed by those based on tetrafluoro boron (Runs 6, 1, 4 and 8).
TABLE III______________________________________Effect of Diazonium FluoroCompounds on Isocyanate/Polyol Polymerization (Curing)Formulation: 13.1 grams (0.1 eq.) Isocyanate.sup.a 3.6 grams (0.08 eq.) 1,4-Butanediol 1.02 grams (0.02 eq.) Trimethylolpropane 0.18 gram Diazonium Catalyst % Polymerization at Various U.V. Exposure Times.sup.b 1 3 5 10No. Diazonium Catalyst min. min. min. min.______________________________________1 p-Chlorobenzenediazonium 0 1.7 36.1 36.8 tetrafluoroborate2 p-Chlorobenzenediazonium 2.6 12.2 75.5 72.8 hexafluorophosphate3 p-Nitrobenzenediazonium -- 57.7 66.0 65.6 hexafluoroarsenate4 p-Nitrobenzenediazonium 1.0 36.3 44.1 31.2 tetrafluoroborate5 p-Nitrobenzenediazonium 1.1 60.9 68.6 64.6 hexafluorophosphate6 2,4-Dichlorobenzenediazonium 0.5 17.7 39.2 58.6 tetrafluoroborate7 2,4-Dichlorobenzenediazonium 1.4 71.1 64.9 66.3 hexafluorophosphate8 2,4,6-Trichlorobenzenediazonium 0.3 2.9 26.1 39.3 tetrafluoroborate9 2,4,6-Trichlorobenzenediazonium 1.3 52.2 59.0 65.4 hexafluorophosphate10 2,4,6-Trichlorobenzenediazonium 2.5 81.5 72.6 71.1 hexafluoroarsenate11 Control-No Catalyst 0.1 0.1 29.5 29.2______________________________________ .sup.a Hylene W, 4,4methylene bis(cyclohexyl isocyanate). .sup.b 4 in. 100 watt/inch Hanovia U.V. lamp, exposure temp. 150.degree. F. (66.degree. C.).
Reasonable variations and modifications which will be apparent to those skilled in the art can be made in this invention without departing from the spirit and scope thereof.
Claims
  • 1. In a process for the production of polyurethane compounds by the polymerization reaction of a diisocyanate compound of the formula OCN--R--NCO wherein R is a C.sub.4 to C.sub.20 alkylene, arylene, alkarylene or aralkylene radical with at least one diol and at least one polyol, the improvement which comprises admixing with said diisocyanate compound and said diol and polyol as a catalyst for said polymerization reaction at least one diazonium salt compound of the formula ##STR2## wherein R' is any electron withdrawing group, M is one selected from the group consisting of B, P, As, Sb, Bi and Sn, n is 4, 5 or 6, and x is 1, 2 or 3; and thereafter subjecting the resulting reaction mass to ultraviolet light in the wavelength range of about 2000 to about 4000 Angstroms for a period of about 0.1 to 20 minutes at a temperature in the range of about 0.degree. F. to about 180.degree. F.
  • 2. A process according to claim 1 wherein said diisocyanate is 4,4'-methylene bis(cyclohexyl isocyanate).
  • 3. A process according to claim 1 wherein said diol is 1,4-butanediol.
  • 4. A process according to claim 1 wherein said polyol is trimethylopropane.
  • 5. A process according to claim 4 wherein R.sup.1 is at least one selected from the group consisting of F, Cl, Br, I and NO.sub.2.
  • 6. A process according to claim 1 wherein said diazonium salt compound is employed in an amount in the range of about 0.5 to about 5 weight percent based on the total weight of the mixture of isocyanate, diol, polyol and diazonium salt.
US Referenced Citations (15)
Number Name Date Kind
2739889 Neugebauer et al. Mar 1956
3235382 Neugebauer et al. Feb 1966
3457071 Notley et al. Jul 1969
3552961 Notley et al. Jan 1971
3711390 Feinberg Jan 1973
3711391 Feinberg Jan 1973
3954584 Miyata et al. May 1976
4092172 Higuchi May 1978
4186017 Palmer Jan 1980
4272603 Chenevert Jun 1981
4289838 Rowe et al. Sep 1981
4337307 Neubauer Jun 1982
4343885 Reardon Aug 1982
4483759 Szycher et al. Nov 1984
4506003 Ruckert et al. Mar 1985
Foreign Referenced Citations (1)
Number Date Country
975456 Feb 1961 GBX
Non-Patent Literature Citations (2)
Entry
Kosar, J., "Light-Sensitive Systems", J. Wiley & Sons, 1965, pp. 194-197.
Noller, C. R., "Textbook of Organic Chemistry", 2nd Ed., W. B. Saunders Co., 1958, p. 341.