Claims
- 1. A process for preparing a rubber article containing a polymeric reinforcement which consists essentially of the steps of: (1) plasma treating the polymeric reinforcement in a manner whereby reactive groups containing Zerewitinoff active hydrogen atoms are bonded to the surface thereof; (2) incorporating the polymeric reinforcement having Zerewitinoff active hydrogen atoms bonded to the surface thereof into an uncured rubber composition, wherein said rubber composition has pendant blocked isocyanate groups bound thereto; and (3) curing the uncured rubber with sulfur into a desired shape for the rubber article at an elevated temperature sufficient to deblock the isocyanate groups bonded to the uncured rubber allowing for the isocyanate groups to react with the Zerewitinoff active hydrogen atoms bonded to the surface of the polymeric reinforcement, wherein said elevated temperature is a temperature which is within the range of about 140.degree. C. to about 250.degree. C.
- 2. A process as specified in claim 1 wherein the pendant blocked isocyanate groups are covalently bonded to the backbone of the rubber and are present in moieties have the structural formula: ##STR13## wherein A represents an alkylene group, an arylene group or an alkarylene group and wherein X represents a blocking agent.
- 3. A process as specified in claim 2 wherein the pendant blocked isocyanate groups are present in moieties having the structural formula: ##STR14## wherein X represents the blocking agent.
- 4. A process as specified in claim 2 wherein the pendant blocked isocyanate groups are present in moieties having the structural formula: ##STR15## and wherein said moieties are distributed throughout the polymer chains of the rubber in a random manner.
- 5. A process as specified in claim 2 wherein the polymeric reinforcement is in the form of a tire cord.
- 6. A process as specified in claim 5 wherein the tire cord is a polyester tire cord.
- 7. A process as specified in claim 5 wherein the tire cord is a nylon tire cord.
- 8. A process as specified in claim 2 wherein the polymeric reinforcement is a polymeric fabric.
- 9. A process as specified in claim 2 wherein the reactive groups containing Zerewitinoff active hydrogen atoms are selected from the group consisting of carboxyl groups, hydroxyl groups, amines, hydroperoxides, and mercaptans.
- 10. A process as specified in claim 2 wherein the reactive groups bonded to the polymeric reinforcement are hydroxyl groups.
- 11. A process as specified in claim 1 wherein the rubber article is a tire.
- 12. A process as specified in claim 1 wherein the rubber article is a hose.
- 13. A process as specified in claim 1 wherein the rubber article is a belt.
- 14. A process as specified in claim 1 wherein the rubber containing blocked isocyanate groups is comprised of repeat units which are derived from at least one conjugated diene monomer and tetrahydro-N- 1-methyl-1- 3-(1-methylethenyl)phenyl!ethyl!-2-oxo-1-H-pyrrolo-1-carboxamide monomer.
- 15. A process as specified in claim 1 wherein the pendant blocked isocyanate groups bound to the rubber composition occur in repeat units which have the structural formula: ##STR16## wherein X represents a blocking agent selected from the group consisting of alcohols, cyclic amides, ketoximes, phenols, and secondary amines.
- 16. A process as specified in claim 15 wherein the blocking agent is selected from the group consisting of caprolactam and 2-pyrrolidinone.
- 17. A process as specified in claim 16 wherein the rubber having pendant blocked isocyanate groups bound thereto has from about 0.005 to about 0.1 moles of blocked isocyanate groups per hundred grams of total weight.
- 18. A process as specified in claim 17 wherein the molar ratio of Zerewitinoff active hydrogen containing groups in the polymeric reinforcement to blocked isocyanate groups in the rubber composition is within the range of about 0.6:1 to about 2:1.
- 19. A process as specified in claim 15 wherein the blocking agent is selected from the group consisting of a cyclic amide.
- 20. A process as specified in claim 4 wherein the elevated temperature is a temperature which is within the range of about 160.degree. C. to about 220.degree. C.
Parent Case Info
This is a continuation-in-part application of U.S. patent application Ser. No. 7/956,221, filed on Oct. 5, 1992 abandoned.