Claims
- 1. A two-part fiber finish composition, particularly for application to polyethylene terephthalate yarn prepared by a process involving spinning and drawing steps, said yarn to be made into tire cord using a single-dip treatment, said two-part finish composition consisting of:
- (a) a first finish composition consisting essentially of a polyalkylene glycol compound which is a mixed polyoxyethylated-polyoxypropylated monether prepared in accordance with the equation: ##STR9## where R is an alkyl group having 1 to 8 carbon atoms, x and y are the number of moles of propylene oxide and ethylene oxide, respectively, and wherein ethylene oxide comprises 40 to 60 percent by weight of the combined total of ethylene oxide and propylene oxide and x + y has a value to produce a molecular weight of from 500 to 850, said first finish composition being applied to the yarn prior to drawing said yarn; and
- (b) a second finish composition consisting essentially of an aqueous solution of about 70 to 95 parts by weight of said mixed polyoxyethylated-polyoxypropylated monoether, about 5 to 30 parts by weight of a silane having the structural formula: ##STR10## wherein n = 2 to 5, and a sufficient amount of a watersoluble alkaline catalyst to adjust the pH of the finish composition to 8 - 10, said second finish composition being applied as an overfinish to the yarn after drawing said yarn.
- 2. The two-part fiber finish composition of claim 1 wherein the silane is gamma-glycidoxypropyltrimethoxysilane.
- 3. The two-part fiber finish composition of claim 1 wherein the alkaline catalyst is selected from the group consisting of sodium hydroxide, potassium hydroxide and triethanolamine, and a sufficient amount of said alkaline catalyst is present in said second finish composition to adjust to pH to 8.0 - 8.5.
- 4. The two-part fiber finish composition of claim 3 wherein the alkaline catalyst is sodium hydroxide.
- 5. The two-part fiber finish composition of claim 3 wherein the alkaline catalyst is potassium hydroxide.
- 6. The two-part fiber finish composition of claim 3 wherein the alkaline catalyst is triethanolamine.
CROSS-REFERENCES TO RELATED APPLICATIONS
This is a division, of application Ser. No. 617,547, filed Sept. 29, 1975, now U.S. Pat. No. 4,054,634.
This application is related to our U.S. application Ser. No. 589,974, filed June 24, 1975, now abandoned.