Patent Application
20080018022
a-10c illustrate three embodiments of shot marks in the UHMWPE panels of the invention.
The ram extrusion process employed by the subject invention upstream from the die is substantially that described in U.S. Pat. Nos. 3,887,319, 3,883,631, and 4,145,175, herein incorporated by reference.
The present invention pertains to the ram extrusion of panels of high width and aspect ratio, as described hereinafter. The term “panel” refers to a substantially flat extrusion. Typically, the sharp corners of the nominally rectangular cross-section may be rounded, and indeed, the entire edge portions may be circular, elliptical, etc. A purely rectangular cross-section with sharp corners is generally not desirable due to stress points in the die at such corners. The principle utility of the subject invention is to produce large width sheets of constant thickness, this constant thickness extending to a position at or proximate the edge. Thus, by the definition of “panel” as used herein is meant a generally flat sheet of less than ±0.050 inch (±1.27 mm) thickness variation over a central portion of the panel which includes at least about 80% of the overall panel width, preferably at least 90% of the panel width, and most preferably 95% or more of the overall panel width. Thus, it would not depart from the spirit of the invention to produce a sheet having a “dumbbell” or other cross-section, with edge portions significantly thicker or thinner than the majority of the panel. These portions can easily be removed, preferably by the manufacturer but also by the end user, by conventional sawing or slicing steps.
Because of its large width and of its asymmetry due to the high width to thickness aspect ratio, the production of wide panels from a substantially rectangular die, i.e. a die with substantially parallel surfaces across its width, is very problematic, and many attempts to do so have failed. Unlike many smaller products which are ram extruded at exit temperatures above the crystalline melt temperature, panels of large width, upon initiation of crystallization, will distort in unpredictable ways due to the volume contraction which occurs during crystallization as well as internal stresses which are created. However, allowing full solidification prior to exit from the die is generally not practiced due to loss of contact with the die walls. If the die walls are progressively narrowed toward the exit, contact can be maintained, but the buildup of pressure can at times be so high as to separate the die halves, or even to rupture the die or its support.
The UHMWPE panels of the present invention are partially crystalline as a result of exiting the slit die of the ram extrusion apparatus at a temperature below the crystalline melt temperature. While for thin gauge panels, i.e., those having thicknesses of 1.5-2 cm or less, the entire panel temperature (e.g., throughout its thickness) may be less than the crystalline melt temperature, for thicker panels especially, the interior of the panel may be at a higher temperature. Thus, it is not necessary that the entire panel be at such a low temperature, provided that the surface of the panel, and preferably the panel interior to a depth of about 3 mm, is below the crystalline melt temperature. To further reduce the interior temperature of thick panels, the rate of extrusion can be slowed, thus spending more time in the cooling zone; the cooling zone may be extended; or the temperature of the cooling fluid can be lowered. These methods may be employed singly or in any combination.
Applicants have surprisingly discovered a means of providing a solidified product without loss of die contact, while minimizing any pressure excursions. The process employs a back pressure device, and is the subject of a copending application entitled “Process For Ram Extrusion Of UHMWPE Sheet Products”, filed on even date herewith. However, despite the use of a back pressure device, Applicants have found that it is very difficult to keep the process running in a stable manner, i.e. defined as producing a flat, commercially acceptable product with a small reject rate.
Applicants believe that the non-robust nature of such processes is due to the same factors which destroy product uniformity of amorphous panels during cooling and crystallization, but in this case the irregularities are exhibited within the die as opposed to outside the die. Applicants have surprisingly discovered that a robust process can be provided if a plurality of three or more cooling zones are located proximate the exit face of the die distributed in the width direction, on both the top and bottom die halves, or in a monolithic die, above and below the die slit. The plurality of cooling zones are preferably arranged symmetrically on either the top half, the bottom half, or both, about a centerline of the die. Most preferably 5-10 cooling zones or more are utilized on both the top and bottom, greater numbers being advantageous with increasing panel width. Thus far, for sheets of approximately 1 m to 1.2 in width, 5 to 7 zones of substantially equal size, as shown in
A plurality of cooling zones are independently controlled. Each cooling zone is preferably independently controlled, although in a given installation it may be found that two or more zones may be controlled together. Experience has shown, however, that independent control is highly desirable and in most cases necessary. Each cooling zone preferably has its own inlet and outlet, although outlets may be shared in parallel with adjacent zones in suitable designs. Series connection of all zones will not work. The zones are fed cooling fluid, which may be gas or liquid, but is highly preferred to be liquid, due to the high heat removal demands. Cooling liquid may be water, although glycols or other heat transfer fluids may be used. Water is preferable, and a closed system with cooling means which assures uniform water temperature is desirable. The temperature in a given zone is measured by a suitable measuring means, preferably by a thermocouple positioned in the die proximate the zone, and the flow and or temperature of coolant is regulated by conventional process controls. Preferably, proportional valving rather than on/off valving is employed, and temperature regulation is preferably adjusted by varying the rate of coolant flow rather than adjusting the coolant temperature. Temperature may also be adjusted by providing sufficient cooling to provide a lower than desired temperature, and then elevating the temperature to the desired temperature by electrical heating. This is not preferred. Temperature in each cooling zone is preferably regulated between ±3° F. (1.7° C.) of the set point, more preferably ±1° F. (0.6° C.).
The temperatures of the individual zones are adjusted to provide a flat product. In one machine embodiment, the cooling zones positioned across one of the die halves will be at the same temperature for the majority of the machine operation, and the cooling zones in the lower die half will be at a uniform temperature relative to each other, but at a temperature different from the temperature of the upper die half cooling zones. Depending in part upon the length of the cooling zone in the machine direction, the temperature of the individual zones may range from 80° F. (27° C.) to 200° F. (93° C.), preferably from 90° F. (32° C.) to 180° F. (82° C.). The bottom cooling zones are in general maintained at a lower temperature than those on the top, i.e. different by about 1° F. to 25° F. (0.6° C. to 14° C.), in general about 3° F. to 15° F. (1.7° C. to 8.3° C.). It has been surprisingly discovered that the lower temperatures produce sheets with shot marks of relatively low height. The multiple transverse cooling zones can also be used with dies designed to extrude narrower panels, for example of 0.4 m width.
The machine operator, observing the panels exiting the machine, will adjust the cooling zone temperature individually if warpage or surface imperfections are noted. For example, if the panel warps or curls in an upward direction on the far right side, the top and bottom zones corresponding to the position of the warpage will be adjusted by making the top zone colder or the bottom zone warmer, or both. In general, it is desirable to have the temperature of a given zone as close as possible to adjoining zones to minimize uneven cooling. In like fashion, if the entire sheet bows uniformly, i.e. “curls”, then the temperature differential between the top and bottom zones is adjusted to remove the bow. Only minimal training of the operator is required to maintain stable operation.
The process can also be easily implemented as an automatic process in hardware and/or software, for example, by scanning the panel transversely at one or more positions along its length by means of an optical comparator or the like, or feel gauges, etc., which detect warpage or bowing, and make corrections automatically. It should be noted that due to the nature of the problems associated with ram extrusion of high aspect ratio panels, numerous factors will cause instability, for example, fluctuations in coolant temperature, raw material batch changes, etc, and even the opening of a door to the operating environment. Further information regarding the cooling zones will be presented in the Examples.
The panels of the subject invention should be flat, i.e. free from warp and bowing, and also of uniform thickness, preferably ±0.030 inch (0.76 mm). The cross-section is thus substantially rectangular. However, the sides of the panels are generally rounded at least at the corners, since such rounding lowers the pressure in the die and also eliminates sharp die corners, which would then be points of stress which could crack at the high pressures involved. By “substantially rectangular” is meant a generally flat sheet when viewed from the end, with perpendicular, curved, or radiused sides, and parallel or substantially parallel main surfaces. Likewise, a rectangular die slit is one which has two faces having a length equal to the width of the panel to be produced, whose faces are flat and parallel to each other under extrusion pressure, the faces connected by sides which are preferably rounded or radiused. It is the flatness of the panels, and of the die faces which produce a substantially flat panel, which satisfy the definition of “substantially rectangular” herein.
It has been found, however, that if a die of substantially rectangular geometry when not under operating pressure is employed as a die in the extrusion of large width panels, the resulting panels do not have uniform thickness, have numerous surface irregularities, and in general produce a commercially inferior and generally unacceptable product. For most applications, such products have to be surface machined or skived to produce a flat surface. This process is wasteful of expensive polymer and adds further process steps, which further increases cost.
It has been found that it is advantageous to utilize a die which is manufactured with a shape which is other than substantially rectangular, in particular a shape in which the edge region of the top and bottom surfaces of the die slit are not flat and parallel to each other, in conjunction with a support structure which, like the die, distorts under stress, the die and support structure coacting such that distortion of the non-rectangular die under operating pressure transforms the die opening into an opening such that a flat product is produced. In a further embodiment, the die and support structure are merged into one, by employing massive die top and bottom halves. Such a massive die is not preferred, due to its cost.
The preferred die geometry is one in which the most central portion of the die is of lesser height than edge regions of the die. When the die expands against the support structure, the edge regions of the die will distort the least, while the central area, and the support structure above and below the central area, will distort more, bringing the faces of the die to a substantially parallel geometry. For the purposes of this invention, a die will have substantially parallel geometry if, during operation, a panel which has thickness variations over its width of less than 0.050 inch (1.27 mm) is produced. Applicants have discovered that a high quality panel of large width may be produced by employing a die which preferably has a dual taper, and one in which the die is cooled proximate the exit such that the panel exits the die at a temperature below the crystalline melt temperature.
The dual tapers of a preferred embodiment of the subject invention die may be divided conceptually into a vertical taper and a transverse taper. The vertical taper is a narrowing of the die proximate its inlet end as viewed from the side, i.e. a narrowing in a vertical direction. The transverse taper is a narrowing of the height of the die slit in a direction transverse to the machine direction, i.e. across the width of the continuously produced panel stock.
The vertical taper is more clearly shown by reference to
If T is the height at the edge of the die exit slit, the height at other portions of the die may be roughly established by Te and Tm where Te is the height at a distance De from the cavity edge, where De is 9 inches (22.5 cm) or less, and Tm is the height of the cavity at a distance Dm from the cavity edge where Dm>9 inches (22.5 cm). The values of Te and Tm for dies of nominally 1.2 m width is then given by
Te=T
1−0.00275 De and
Tm=T
1−[0.00275 De−(0.00175(Dm−De))]
The constants 0.00275 and 0.00175 are related to the thickness of the die (not the cavity height), the thickness of any supporting structures, the width of the die, etc. Due to the complex nature of the process and the intricacies of the die, etc. per se, for example the cooling passages, die length, die transition zone, etc.; for dies of appreciably different dimensions, different constants and different limiting values of De and Dm must be determined. Resort may be had to techniques such as finite element analysis, for example, software for which is readily available. However, it may be more expedient to machine the die by trial and error, with the material removal being conservative, such that the final shape is approached by successive refinements without having to begin the machining process again.
The difference T1−T2 may be determined empirically by production of a die having a small and preferably inadequate value of T1−T2, performing a trial ram extrusion, and measuring the differences in thickness of the panel produced in a direction transverse to the machine direction. If significant differences in thickness or surface irregularities are noted, the die can then be machined to produce a greater height variance in the slit. It should be noted that the most advantageous shape of the die surface 60 is not necessarily circular, but may indeed be parabolic, hyperbolic, ellipsoidal, etc., and may in fact, as later discussed, be multiply tapered.
It has been found through a great deal of effort, that the shape of the die slit and the value of T2−T1 is dependent on several factors which together define the requisite geometry. By the latter term is meant a die slit shape which, in conjunction with the operating parameters of the machine, e.g. resin type, temperature, internal pressure, length (machine direction) of die, width (transverse) of die, preferably produce a panel product with a thickness variation across the width of the panel of less than 0.050 inch (1.27 mm), more preferably less than 0.030 inch (0.76 mm), and most preferably less than 0.020 inch (0.51 mm). Since these values are total thickness variation, the surface height fluctuations are generally ± half these values, i.e. preferably ±0.010 inch (0.25 mm) or less.
The parameters which are most important in determining the transverse slit taper are: the internal pressure; the width of the panel; and the deflection of the support structure restraining means preferably used. As the width of the panel increases, the force exerted on the two mold halves, at any given pressure, increases also. This pressure will tend to force the mold halves apart, and in prior machines, has literally done so. The die halves of the preferred embodiment of the subject invention machines are about 11-12 cm in thickness. If these die halves were unsupported on their exterior, they would bend so much in producing a 1 cm thick panel 1.2 m wide that they would buckle and break. It would be possible, of course, to make the die halves of much thicker material. However, stainless steel is expensive, and even were the die halves 25 cm thick, bending would still be severe. A preferred material for the dies is T420 stainless steel, preferably polished and coated with a wear resistant and preferably lubricious coating. Conversion coatings, and preferably metal coatings, such as hard chrome or nickel may be used. Advantageously, diamond-like carbon (DLC) coatings such as supplied by Diamonex Products, Allentown, Pa. as Diamonexo DLC or amorphous diamond coatings such as are disclosed in U.S. Pat. No. 6,103,305, herein incorporated by reference, are used. Such diamond coatings are well known for their low coefficients of friction. Peripheral die components can be made of hardened steel, for example PHS 4140 prehardened steel.
The degree of distortion of the die along the direction transverse to the machine direction is dependent upon the width of the panel being produced. The greater the panel width, the greater the internal die surface area and the greater the force exerted on the die halves. Moreover, transverse to the machine direction, the distortion may be viewed as a force moment distant from the securing devices uniting the die halves. For example, in a two piece die secured on its flanks by a series of bolts or similar devices, distortion will be greater the further from the securing devices. Thus, the die will distort somewhat more in the middle than at the edges. Moreover, the force on the securing bolts will receive a much greater contribution from the central area of the die than from the edges of the die.
To decrease the distortion of the die, a “window frame” support structure is preferably used with the dies of the present invention. The “window frame” consists of massive supports above and below the dies, these supports having a high modulus. Preferably, the supports are made of carbon steel, for example Viscount® —44 steel. The supports are shown in
Thus, for relatively “narrow” panels of 0.6 to 1 m, by using supports of exceptionally heavy section, for example 1 m in thickness, or by reverse beveling the supports to counter distortion, the die slit may have minimal transverse taper or even no taper. However, such massive supports are generally undesirable, as they not only increase machine cost, but engender a severe weight penalty as well, thus requiring a stronger and hence more massive base, i.e. floor, to support the weight.
In a further embodiment, the slit die is machined to have a straight, non-tapered main section, or even one with a reverse taper, i.e. with greater height in the middle than at the edges, but is used with contoured window frame supports, as shown in
Thus, with respect to the die geometry, the shape of the slit is such so as to provide substantially planar top and bottom surfaces of the product panel when under load, i.e. at the high operating pressure of the ram extrusion process. This achievement is accomplished by providing a contoured mold which distorts to the desired shape under load; a non-contoured mold with a contoured and distortable window frame, or a non-contoured mold with a massive and substantially non-distortable window frame. For a die of ca. 1.2 m width and ca. 1 cm exit slit height, the supports above and below the die will have to be about 0.75 m thick for the latter embodiment. Preferred dies also have the vertical taper previously described.
The rams used in producing the panels of the subject invention are stepped rams, as illustrated in
The die contains at least one heated and one cooled section relative to the machine direction. One heated section is proximate the portion of the die where the ram enters the die, although it may also be advantageous to establish a cooling zone between the ram entry point or cavity 45 of
A plurality of such heating zones is shown in the perspective drawing of a slit die in
The cooling section is preferably located proximate the exit of the die, and consists of a plurality of cooling passages 33, each having an inlet and an outlet. Other arrangements of cooling zones, for example a plurality of inlets bored parallel to the machine direction and communicating with one or more common outlets bored transversely to the machine direction are also possible. The arrangement itself is not critical. However, whatever the arrangement, the cooling zones must allow for temperature variation to be established as desired transverse to the die slit, for example to maintain the central area of the slit at a higher or lower temperature than the edge regions, or intermediate zones.
It is highly beneficial to the operation of the present ram extrusion process to minimize the build-up of pressure within the die. Good temperature control is a necessary requirement for producing a consistent product, but increasing temperature does not have a great effect in lowering operating pressure since UHMWPE is gel-like and rubbery, rather than a viscous fluid. It has been discovered that addition of small amounts of long chain fatty acids and fatty acid salts such as stearic acid, palmitic acid, linolenic acid, and their salts, particularly their calcium and zinc salts, aid in lowering internal pressure, presumably by lowering friction of the gel particles with the die walls. Other lubricants such as montan esters, amides, polyethylene waxes, silicone oils, and the like are also suitable. Such lubricants are generally used in amounts of from 0.1 to 3% by weight, more preferably 0.2 to 2% by weight, most preferably 0.5 to 1.5% by weight. It is important, however, to minimize the amount of lubricant to avoid loss of mechanical properties. Thus it is preferable that 1.5% or less be employed.
It has also been surprisingly discovered that minimizing oxygen content of the resin powder during the process greatly lowers operating pressure. Typically in ram extrusion, resin powder is pneumatically directed to a supply hopper above the ram extrusion machine by air. It has been found that if an oxygen-free gas is injected into the hopper, preferably at or near the bottom, to sweep or “sparge” air out of the hopper, that the pressure in the die is lowered by 150 to 200 lb/in2, a very surprising amount. This reduction in pressure may result in lowering the force exerted against the die halves by as much as 1.5×104 lbs pressure in a 1 m×0.5 m die. Any oxygen-free or oxygen-depleted gas may be used, including helium, argon, carbon dioxide, nitrogen, or the like.
The UHMWPEs employed in the process are conventional powdery resins, as supplied by Ticona, Braskem, and DSM, for example. Preferred number average molecular weight ranges are between 2·106 Da and 10·106 Da, more preferably between 4·106 Da and 8·106 Da. Although the preferred UHMWPE used in the present invention is homopolymeric or substantially homopolymeric, i.e. with only a low content of copolymerizable comonomers, the compositions may, as also indicated elsewhere herein, include conventional processing aids or property-modifying additives. Examples of the latter groups of components include, but are not limited to, components such as thermal stabilizers; UV stabilizers; nucleating and clarifying agents; dyes and pigments; electrically conducting materials such as metal powders, carbon powders, graphite and the like; fillers, for example non-reinforcing fillers having BET surface areas <50 m2/g and reinforcing fillers such as fumed silica having surface areas ≧50 m2/g; lamellar reinforcements such as mica, expanded shale, and the like; fibrous reinforcement in the form of chopped or otherwise attenuated fibers, for example glass fibers, ceramic fibers, aramid fibers, metal fibers, carbon fibers, thermoset and thermoplastic fibers such as those of polyimide, polyetherimide, polysulfone, polyethersulfone, polyether ketone (PEK) and its variants (PEKK, PEEK, etc.); tougheners such as particulate elastomers; other thermoplastics, such as non-UHMW PE; plasticizers, etc. The amounts of such additives is generally small.
Having described in detail individual components of the present invention, a preferred embodiment is a ram extrusion process employing a slit die having a width greater than 0.6 m and preferably having an aspect ratio of width to height greater than 10:1, more preferably greater than 20:1, and yet more preferably greater than 40:1, the die having a top portion and a bottom portion, each of the top and bottom portions containing a plurality of three and preferably at least five cooling zones positioned across the width of the die, the temperature of a plurality of zones in each set of zones being independently adjustable. The length of the cooling zone in the machine direction and the temperature of the zones are such that a UHMWPE panel exiting the die has cooled below its crystalline melt temperature and is at least partially crystalline.
In another preferred embodiment, a two piece die, the exit of which is not the shape of the desired cross-section of a ram extruded product when not under pressure, is contained within support structure of high strength and modulus which bears against the die halves and restrains their distortion outwards at the operating pressure of the ram extrusion process. However, under pressure, distortion which cannot be completely restrained by the support structure distorts the die and support structure in such a way that the die exit assumes a shape which allows the ram extrusion of panels of at least 0.6 m width and preferably of at least the aspect ratios previously described, the panel having variations in thickness of less than 0.050 inch (1.27 mm), preferably less than 0.030 inch (0.76 mm), and more preferably less than 0.015 inch (0.38 mm). The die has at least one cooling zone in each die half, proximate the die exit, such that the UHMWPE panel exiting the die is at a temperature below the crystalline melt temperature, preferably below 137° C., more preferably below 250° F. (121° C.), more preferably below 120° C., yet more preferably below 110° C., still more preferably in the range of 40 to 100° C., and most preferably between 75° C. and 85° C.
In a yet more preferred embodiment, the die of the foregoing embodiment has a small vertical taper or “narrowing” from the height of the die where the ram enters, to a somewhat uniform and narrower height along the machine direction towards the die exit. Also, in this preferred embodiment, the shape of the die transverse to the machine direction is such that the height of the die slit is less at the center of the slit than at the edges of the slit, and the support structure consists of heavy steel slabs machined to have substantially flat faces which bear against the respective die halves. The steel slabs are tensioned by a plurality of threaded connectors, most preferably by multi-jackbolt tensioners such as those available from Superbolt, Inc. Carnegie, Pa., and described in U.S. Pat. Nos. 6,263,764; 6,112,396; 6,381,827; 6,199,453; 5,083,889; and 4,846,614.
In a yet more preferred embodiment, the die of the foregoing embodiment is employed, and is also provided with a plurality of at least three cooling zones in each die half, as previously described. The temperatures of the various cooling zones are set to provide stable extrusion of the panel product, and are individually adjusted when necessary to counter process variations which produce warp, bow, surface irregularities, and thickness variations, these adjustments preferably being made during operation of the machine.
The product produced by the inventive process is a novel product whose manufacture was not possible prior to the present invention. As indicated previously, due to the difficulties of ram extrusion, it had been impossible to ram extrude constant thickness panels of large width and high aspect ratio, i.e. thin panels. Thus, to produce thin panels, thick, compression molded panels were skived to produce thin sheets. However, these sheets have irregular surfaces, both in terms of thickness variation as well as appearance.
Panels produced by the subject invention process are characterized by a smooth, glossy, and uniform surface. The smoothness can be assessed easily by touch, and the gloss of the surface assessed visually, or by optical inspection techniques such as the standard ASTM D2457-03 and D523-89 test methods, preferably at a 60° angle. Using this test methodology, employing a BYK Gardner Color Guide Glass Meter supplied by BYK Gardner U.S.A., Columbia, Md. and a 60° test angle, average gloss measurements preferably range from 35 upwards, with most panels in the range of 35 to 45. This is in contrast to skived panels which, although also smooth, have significantly lower gloss, averaging about 24 using the same test methodology.
The uniform surface has a 3σ thickness variation of less than ±0.050 inch (±1.25 mm), more preferably within ±0.030 inch (±0.76 mm), and yet more preferably within ±0.020 inch (±0.50 mm). While the surface is smooth and glossy, it can further be distinguished from skived panels by the presence of shot marks substantially perpendicular to the length of the sheet (in the machine direction) and substantially parallel to each other. These shot marks are believed to be caused by the stationary dwell between ram extrusion cycles, and the profile and height of the shot marks can be measured by standard profilometry techniques. The shot marks have a maximum height (top to bottom) of only several microns, i.e. less than 70 μm, more preferably less than 25 μm, and importantly, do not interfere with known uses of thin panel stock. Products have been produced over extended trials with shot marks measuring about 5-10 μm in height. The shot marks may easily be seen by observing the panel at an oblique angle.
a-10c illustrates several shot mark patterns. In
However, the flow of UHMWPE is generally retarded somewhat at the edges of the die, and may experience less retardation at the die center. The retardation at the two edges may not be the same either. The result is that the shot marks are typically somewhat “wavy” or “undulating” across the panel surfaces (shot marks are on both front and back surfaces) as shown at 102 in
Thus, the present invention also pertains to an UHMWPE panel having a width greater than 0.6 m, and characterized by generally parallel shot marks on both top and bottom surfaces. For panels whose length direction corresponds to the machine direction, these shot marks are transverse to the machine direction of the panel. The surface of the panels are smooth and glossy, and have a thickness tolerance as previously described. Preferred panels are from 4 mm to 10 cm in thickness, more preferably less than 2 cm thick. Preferred panels have a global flatness variation of less than 0.150 inch (3.8 mm; 3σ) with a tolerance of ±0.030 inch (0.8 mm; 3σ), and preferably a global flatness variation of less than 0.100 inch (2.5 mm) with a tolerance of less than ±0.024 inch (0.6 mm; 3σ). The sideways bow (curvature) of the panels, without trimming, is preferably within approximately the same values as the global flatness. It should be noted that these sideways bow tolerances for the panel as extruded, are superior than that which can ordinarily be obtained by conventional sawing of the edge. Thus, it is preferred that the subject invention panels retain their edges “as produced”, and are not sawn.
Having generally described this invention, a further understanding can be obtained by reference to certain specific examples which are provided herein for purposes of illustration only and are not intended to be limiting unless otherwise specified.
A ram extrusion machine is provided having a stainless steel die composed of two halves, substantially as described herein, as illustrated, for example, by
The die is contained within a support structure consisting of two flat surfaced carbon steel billets measuring 68 in. (1.7 m) by 15 in. (0.38 m) by 22.5 in. (0.58 m), which are tensioned by 5 multi-jackbolt tensioners having a bolt diameter of 2 in. (5 cm). The steel billets are positioned over the die about one inch from the exit end and extending from that point toward the ram entry end of the die, as illustrated in
UHMWPE resin powder 6540 from Braskem, Sao Paulo, Brazil, having a melt temperature of 133° C., an average particle size (D50) of 190 μm, and an average molecular weight of 8×106 g/mol is introduced pneumatically into a hopper above the UHMWPE entry ports in the top die half. A flow of nitrogen is introduced into the hopper near the bottom to remove air from the resin powder. The ram is drawn back and resin powder is allowed to fill the die cavity below the hopper. The ram then enters the die and compresses the resin powder and pushes it into the vertically tapered portion of the die, this resin in turn pushing the previous portion of resin powder, which has now been heated to a gel, towards the die exit. The ram dwells at this position for approximately 1 second, and then the cycle is repeated. At the beginning of each cycle, once the die is full, 0.5 inch (12.5 mm) of length of an UHMWPE panel of 0.375 inch (9.5 mm) thickness and width of 4 feet (1.22 m) exits the die. The panel is partially restrained in movement by a cloth covered back pressure device which facilitates continued contact of the cool (250° F.) panel with the walls of the die. The back pressure device is constructed so as to allow for variations in back pressure across the width of the panel. The panel is taken up on a flat conveyor, and the operator adjusts the cooling zone temperatures to remove warp and bow from the panel. The top and bottom cooling zone temperatures at stable, flat panel production, are [42° C., 56° C., 60° C., 49° C., 43° C.] and [42° C., 49° C., 53° C., 44° C., 41° C.] respectively. The panel exits the die at a temperature below 100° C., much lower than the crystalline melt temperature. The flat panels produced are cut to length, and have a glossy flat surface with a thickness variation of less than 0.030 inch. Mold “shot marks” of a length equivalent to each ram stroke's production can be seen if observed carefully at a high angle of incidence, but are virtually invisible when viewed head on. The panel has slightly rounded edges which are uniform from panel to panel, and is of commercial quality.
The same machine and process are used as in Example 1, but the die has in addition to the vertical taper, non-parallel exit faces having dual side tapers and a curvilinear top section, as described in
A commercial press molding operation is employed, employing a large, thick section coffin-like mold. UHWMPE resin powder is introduced into the mold cavity and a close fitting top inserted into the mold. The mold and three other molds of similar size are loaded into a stack, placed under a pressure of 1000 lb/in2, (6.9 MPa) and heated to above the crystalline melt temperature, held at this temperature for 90 minutes, and then slowly allowed to cool. Thick plaques are obtained from which 0.375 inch (0.95 cm) thick panels can be produced by skiving in a separate step. Prior to skiving, the production rate is 75 lbs/hour (33.5 Kg/hr). Following skiving, a long anneal time at elevated temperature is required to reduce end curl and edge curl and internal stresses.
While embodiments of the invention have been illustrated and described, it is not intended that these embodiments illustrate and describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention.