This application claims priority to Chinese Application No(s). 200710196399.5 filed 28Nov. 2007 and Japanese Application No. 2007-331300, filed 25 Dec. 2007, the entire contents of each of which are hereby incorporated by reference.
1. Field of the Invention
The present invention relates to a protective film forming method and, more specifically, to a method for forming a thin protective film on a surface of a protection target.
2. Description of the Related Art
Recently, in order to implement size-reduction and large capacity, there has been a rapid advancement in increasing the recording density of magnetic disk devices. Accordingly, it is required to decrease distance between a magnetic head slider and a magnetic disk, i.e., to decrease floating amount of the magnetic head slider further with respect to the magnetic disk.
In the meantime, a decrease in the floating amount of the magnetic head slider with respect to the magnetic disk may increase a chance for the magnetic head slider to be in contact or to be collided with a magnetic head face that is being rotated at a high speed. Thus, it is necessary to form a protective film on a floating face of the magnetic head slider. Further, it is necessary for the protective film to have a high sliding characteristic (low friction characteristic) and abrasion resistance since it may come in contact with the magnetic disk face. Furthermore, for increasing the recording density, it is necessary to form a thickness of the protective film to be extremely thin in order to narrow the distance between a magnetic head element part and the magnetic disk. Moreover, the magnetic head element part comprises a magnetic recording element and a magnetoresistive element working as a reproducing element. Each of those elements is formed with a magnetic material that is easily corroded, so that the protective film is also required to have a function of preventing corrosion of the magnetic materials.
Now, a magnetic head slider protective film forming method employed conventionally will be described by referring to
Then, the magnetic head slider manufactured through the above-described steps is required to pass various kinds of corrosion tests so that the quality thereof can be maintained. Typical examples of the corrosion tests are an acid dipping test depicted in Patent Document 1 and a hot-and-humid test depicted in Patent Document 2.
However, when thickness of the protective film formed through the above-described steps, i.e., the protective film constituted with a double-layered film, is tried to be made thinner, it is difficult for such protective film to pass the corrosion tests mentioned above with the film thickness of less than 2 nm, for example. Therefore, the protective film of the above-described structure cannot be made thinner because of its corrosion resistance, so that it is not possible to achieve high recording density. Inversely, when the film of such protective film is thinned, the corrosion resistance is deteriorated. This results in deteriorating the quality of the magnetic head slider.
Further, as shown in
It is therefore an object of the present invention to improve the foregoing inconveniences and, in particular, to provide a high-quality protection target by forming a protective film that is thin and excellent in corrosion resistance.
Thus, a protective film forming method for forming a protective film at least on a part a surface of a protection target according to one aspect of the present invention employs a structure which comprises: a base film forming step for forming a base film on the surface of the protection target; and a DLC film forming step for forming a diamond-like carbon film on the base film, wherein the base film forming step forms the base film on the surface of the protection target for a plurality of times by repeating a process of depositing the base film in a prescribed thickness and eliminating a part of or a whole part of the base film.
Further, the present invention employs such a structure that the protective film forming method comprises, before the DLC film forming step, an insulating layer forming step for forming an insulating layer on a surface of the base film on which the diamond-like carbon film is to be formed.
Further, the protective film forming method employs such a structure that the base film forming step comprises: a first base film forming step for forming a first base film by depositing a base film in a prescribed thickness on the surface of the protection target and eliminating a part of or a whole part of the base film thereafter; and a second base film forming step for forming a second base film by depositing a base film further on the first base film and eliminating a part of the base film.
Specifically, the first base film forming step deposits a base film in a film thickness of 1 nm or more, and eliminates a part of the base film thereafter in such a manner that the base film comes to have less than 1 nm film thickness. Further, the second base film forming step deposits a base film in a film thickness of 1 nm or more, and eliminates a part of the base film thereafter in such a manner that the base film comes to have less than 1 nm film thickness.
With the present invention, first, the base film in a prescribed film thickness that can be materialized as a continuous film is deposited directly on the surface of the protection target. Thereafter, a part of or a whole part of the deposited base film is eliminated along the film-thickness direction so as to reduce the thickness of the film thereby to form the first base film. Then, a base film in thickness that is sufficient to be materialized as a continuous film is deposited thereon, and a part of the deposited base film is eliminated along the film-thickness direction so as to reduce the thickness of the film thereby to form the second base film. Note here that a base film formed by the above-described method which deposits a base film in a prescribed thickness and eliminates it thereafter may be deposited on the above-described base films further. Thereafter, the diamond-like carbon film is formed on the top layer. Thereby, the protective film can be formed. With this, it is possible to form the protective film that is thin but has suppressed film defect.
It is possible for the insulating characteristic of the film itself to be deteriorated, since the film thickness is made thinner. However, the insulating characteristic can be secured by forming the insulating layer on the surface of the base film on which the diamond-like carbon film is to be formed. With this, the protective film with an excellent corrosion resistance can be formed. Therefore, it is possible to improve the quality of the protection target on which the protective film is formed. Furthermore, it is possible to secure the electric characteristic by suppressing the AC noise and the like of the protection target.
Further, the protective film forming method employs such a structure that the base film forming step forms the base film by using one of silicon, silicon oxide, silicon nitride, and silicon carbide. Furthermore, the method employs such a structure that the base film forming step deposits the base film by sputtering, particularly by an ion beam sputtering method or a magnetron sputtering method.
Further, the protective film forming method employs such a structure that elimination of the base film performed in the base film forming step is executed by an oblique incident ion beam etching method which irradiates an ion beam by tilting it with respect to a film-thickness direction of the base film. Furthermore, the protective film forming method comprises, before the base film forming step, a surface cleaning step for cleaning the surface of the protection target, and the surface cleaning step is executed by performing an oblique incident ion beam etching method which irradiates an ion beam by tilting it with respect to a film-thickness direction of the base film. With this, the energy applied by the ion beam to the surface form which the base film is eliminated or the surface to be cleaned, i.e., the protection target itself, can be suppressed. Thus, damages that may be imposed upon the protection target can be lightened. By cleaning the surface, a natural oxide film on the surface of the protection target can be eliminated, so that the adhesion property of the base film formed thereon can be improved.
The protective film forming method employs such a structure that the base film forming step and/or the surface cleaning step is executed by the oblique incident ion beam etching method using a gas containing argon. Further, the insulating layer forming step forms the insulating layer by insulating the surface of the base layer on which the diamond-like carbon film is to be formed, by applying a plasma treatment. Note here that the insulating layer forming step performs the plasma treatment by using a mixed gas of argon and nitrogen or oxygen. Furthermore, the plasma treatment performed in the insulating layer forming step is executed by an electron cyclotron resonance plasma method or an oblique incident ion beam etching method. Moreover, the DLC film forming step forms the diamond-like carbon film by a Filtered Cathodic Vacuum Arc (FCVA) method.
Further, a protection target manufacturing method as another aspect of the present invention manufactures the protection target by forming the protective film at least on a part of the surface of the protection target by using the protective film forming method described above. The protection target manufacturing method is a magnetic head slider manufacturing method, for example, which forms a protective film on a floating face of the magnetic had slider as a protection target by using the above-described protective film forming method.
Further, another aspect of the present invention is a protection target that has the protective film formed thereon by the protective film forming method described above. The protection target has the protective film at least on a part of its surface. The protective film includes: a base film formed by repeating a process of depositing the base film in a prescribed thickness on the surface of the protection target and eliminating a part of or a whole part of the base film; and a diamond-like carbon film formed on the base film. Further, the protective film has an insulating layer obtained by insulating a surface of the base film on which the diamond-like carbon film is to be formed. The protection target is a magnetic head slider, for example.
Still another aspect of the present invention is a head gimbal assembly comprising the magnetic head slider, for example. Further, it can be applied to a hard disk drive that comprises the head gimbal assembly.
By employing the present invention for the protective film of the magnetic head slider to be loaded on the hard disk drive, the film thickness of the protective film can be formed extremely thin so as to narrow the distance between the magnetic head element part and the magnetic disk. This makes it possible to improve the corrosion resistance. Therefore, it is possible to achieve high recording density of the hard disk drive and to improve the reliability at the same time.
The present invention is structured and functions in the manner described above. With this, the protective film that is extremely thin and has a suppressed film defect can be formed. Therefore, the present invention can provide such an excellent effect that it is possible to form the protective film with an excellent corrosion resistance and to improve the quality of the protection target on which the protection film is formed, which has not been achieved conventionally.
A protective film forming method according to the present invention has a distinctive feature in its process for forming a base film that is a part of a protective film. Specifically, it is distinctive in respect that each layer, when forming a double-layered base film, is deposited once in a thickness to be thicker than a target thickness, and it is eliminated to a desired thickness thereafter. Further, it is also distinctive to provide an insulating layer between the base layer and a diamond-like carbon film, when forming the diamond-like carbon film on the base layer.
Hereinafter, the protective film forming method will be described in a concretive manner in a form of embodiments. The embodiments will be described by referring to a case of using a magnetic head slider as a target on which a protective film is formed. However, protection targets are not limited only to the magnetic head sliders. The protective film forming method of the present invention can be applied also when forming protective films on any kinds of articles such as other electronic components. Further, it is noted that all the articles (protection targets) that have the protective films formed by the method of the present invention are to be included within a scope of the present invention.
First Embodiment
A first embodiment of the present invention will be described by referring to
The protection target in this embodiment is a magnetic head slider 1 shown in
In the magnetic head slider 1 shown in
(Outline of Magnetic Head Slider Manufacturing Method)
First, the outline of the method for manufacturing the magnetic had slider 1 will be described by referring to
Subsequently, the wafer 30 on which the magnetic head parts 11 shown in
Subsequently, the surface of the bar block 31, which is to be a floating face S of the magnetic head slider 1, is polished by a lapping device (a lapping step (step S3 of
Then, the protective film 2 described above is formed on the lapped surface of the bar block 31, which is the floating face S of the magnetic head slider 1 (step S4 of
Thereafter, the bar block 31 is cut out into the individual magnetic head sliders 1 by a slider cutting device (step S5 of
(Protective Film Forming Method)
Next, the method for forming the protective film shown as step S4 of
With the irradiated ion beam, a natural oxide film on the surface 13 of the bar block 31 can be eliminated, thereby making it possible to strengthen the adhesion property of the base film (protective film) that is formed on the surface 13 later. Further, it is also possible to adjust the length of the recording element and reproducing element with the irradiated ion beam. Particularly, irradiated is not a vertical ion beam but a tilted ion beam with respect to the surface 13 of the bar block 31. Therefore, it is possible to suppress an energy applied to the bar block 31 by the ion beam. That is, it is more preferable to irradiate the ion beam by having it tilted from the vertical direction by a prescribed angle than irradiating it vertically to the surface 13 of the bar block 31. As a result, damages to the bar bock 31 to be the magnetic head sliders 1 generated by cleaning can be lightened, which results in suppressing deterioration of the quality thereof.
The gas used for the ion beam etching performed in the above-described surface cleaning step is not limited to the one having the component mentioned above. Further, the cleaning method is not limited to using the ion beam etching, but may employ any kinds of methods. However, it is desirable to employ a method that performs cleaning by irradiating a relatively low energy to the surface 13 of the bar block 31.
Subsequently, a base film having silicon as a main component, which is a part of the protective film 2, is formed on the cleaned surface 13 of the bar block 31 (a base film forming step). In the embodiment, in particular, two layers of base films are formed. For the material of the base films, silicon, silicon oxide, silicon nitride, or silicon carbide is used, for example. The base film forming step will be described in details hereinafter.
First, a first base film is formed on the surface 13 of the bar block 31 as in
Thereafter, a part of or whole part of the base film 21 deposited in a thickness of 1 nm or more is eliminated to be in a thinner thickness (for example, less than 1 nm) as shown in
Thereby, with the irradiated ion beam, it becomes possible to form an extremely thin first base film 21 by eliminating a part of the base film 21 that is once deposited relatively thicker.
In the above-described elimination processing, irradiated is not the vertical ion beam with respect to the surface 13 of the bar block 31 but the ion beam that is tilted with respect to the direction of the film thickness, as in the case of the cleaning step described above. Thus, it is possible to suppress the energy applied by the ion beam to the bar block 31 itself. As a result, damages that may be imposed upon the bar block 31, i.e., on the magnetic head sliders 1, can be lightened, thereby making it possible to suppress deterioration of the quality thereof.
At the time of eliminating the base film, it is etched to a prescribed thickness, while measuring the film thickness through a measurement method by ESCA that is disclosed in Patent Document 3, which measures composition and linkage state of the chemical elements on a substance surface. For example, when found by the ESCA measurement that amount of silicon has reached a specific value or less, it is judged that a desired amount of base film has been removed. Upon this, the elimination processing is stopped.
Subsequently, as shown in
Thereafter, a part of the base film 22 deposited in a thickness of 1 nm or more is eliminated to be in a thinner thickness (for example, less than 1 nm) as shown in
Thereby, with the irradiated ion beam, it becomes possible to form an extremely thin second base film 22 by eliminating a part of the base film 22 that is once deposited relatively thicker. This method makes it possible to form a protective film that is extremely thin and has fewer defects.
In the elimination processing performed at the time of forming the second base film 22, irradiated is the ion beam that is tilted with respect to the direction of the film thickness, as in the case of forming the first base film 21 described above. Thus, it is possible to suppress the energy applied by the ion beam to the bar block 31 itself. As a result, damages that may be imposed upon the bar block 31, i.e., on the magnetic head sliders 1, can be lightened, thereby making it possible to suppress deterioration of the quality thereof. Further, as described above, at the time of eliminating the base film, the film thickness thereof is adjusted to a desired thickness, while measuring the film thickness through a measurement method by ESCA that is disclosed in Patent Document 3, which measures composition and linkage state of the chemical elements on a substance surface.
Subsequently, processing for forming an insulating layer on the second base film 22 is performed (an insulating layer forming step (step S16 of
As described above, by forming the insulating film 22a, it is possible to secure the insulating characteristic of the protective film 2. Thus, the corrosion resistance can be improved. Further, the protective film 2 keeps the characteristic of silicon or carbon as it is, so that a head noise component called an AC noise is to remain especially in a TMR head. The AC noise is peculiar to TMR, which is induced by a local short-circuit of a sensor part. In order to shut off the short-circuit, it is desirable to use an insulating composition. Thus, it is desirable to nitride or oxide Si as described above, in order to secure the insulating characteristic without specifically changing the composition by a great amount. Therefore, as described above, it becomes possible to improve the corrosion resistance and also to lighten the AC noise and the like so as to secure an electric characteristic through insulating the surface of the base film 22 that has silicon as the main component.
Further, through providing the insulating characteristic, it becomes possible to control an internal stress of the film, which is important for thinning the film. That is, while the base film having silicon as the main component is used for improving the adhesion property of the carbon film, it also provides the effect of achieving stress control at the same time. Specifically, with a deposited layer having a sharp internal stress, the adhesion property is overwhelmed by the internal stress, thereby causing exfoliation. Thus, it is necessary to change the internal stress successively. Through providing the insulating characteristic as described above, it becomes possible to control the internal stress gradually.
Subsequently, a diamond-like carbon film 23 is formed on the above-described base films 22 and 23, i.e., on the insulating film 22a formed on the surface of the second base film 22, as shown in
In the manner described above, the protective film 2 is formed with the first base film 21, the second base film 22 and 22a with the insulated surface, and the DLC film 23. The protective film 2 is formed as a low-defect continuous film by repeatedly depositing and eliminating the first base film 21 and the second base film 22. Further, the surface of the second base film 22 is insulated by applying a plasma treatment. With the structure described above, it is possible to secure the electric characteristic by reducing the AC noise and the like, while improving the corrosion resistance of the magnetic head slider 1 that is protected by the protective film 2.
(Corrosion Resistance Experiment)
Next, there were manufactured the magnetic head sliders (samples) on which respective protective films 2 were formed under various conditions (processing steps), and corrosion tests of each sample were conducted. The results thereof will be described by referring to
First, all the samples 1-16 were the magnetic head sliders 1 in a same structure, and the manufacturing steps of the magnetic head sliders 1 were almost the same. However, methods for forming the respective protective films 2, i.e., the processing steps thereof, were different from each other as shown in
The processing steps for forming the protective film are as follows.
For the oblique incident IBE method used in the steps (1), (3), and (5) described above, the ion energy was set as 150 V, and the tilt angle was set as 65 degrees for not damaging the bar blocks. As an experiment, the angle of the ion beam with respect to the surface 13 of the bar block was set as 0 degree, i.e., set to be vertical. With that angle, obtained was a clearly bad result. Further, in the nitriding treatment by the oblique incident IBE method used in the step (6), the ion energy was set as 50 V, and the tilt angles was set as 65 degrees to suppress the energy to be low in order to restrain the surface elimination effect to be about 0.2 nm.
The magnetic head slider samples 1-16 having the various protective films, i.e., the above-described protective films, were formed by combining each of the above-described steps (1)-(8) and by changing the film-thicknesses of the base films and the DLC film. The magnetic head sliders according to the present invention described above are the samples 6-11 and 13-16. That is, those samples were obtained by forming two layers of the base films, insulating the surface, and forming the DLC film further. In the meantime, the samples 1 and 2 were obtained by forming the protective films by a conventional method that is shown mainly in
The acid dipping test as the corrosion test conducted on each sample was executed through dipping the bar blocks with the protective film in an oxalic acid solution (0.25 N) for four minutes and counting the number of corroded sliders. The number of corroded slider was divided by the number of dipped sliders to show the corrosion rate in percentages. An optical microscope of 1500 magnifications was used to observe the sliders to judge whether or not the sliders were corroded. Further, two bars were used to have a hundred (50×2=100) sliders as the sample base number. For the hot-and-humid test, the bars were kept in an atmosphere at 85 degrees Celsius and with 85% RH for a hundred hours. Then, QST measurement was conducted before and after to find what percentages of sliders with 5% or more of MRR change rate were generated. Further, for the head noise to be measured, noise components to be overlapped with a main waveform were swept successively as “0” Oe→“+300” Oe “0” Oe→“31 300” Oe, and noise peaks of 1.2% or higher were counted when “+300” Oe and “−300” Oe were applied. Then, the number of sliders that had one-hundred fifty or more noise peaks of 1.2% or higher in a single slider was counted, and values obtained by dividing that number by the whole number of measured sliders were shown in percentages.
As shown in
As has been described above, the protective film 2 according to the embodiment is constituted with two layers of base films (first base film 21 and second base film 22) formed by once depositing a film relatively thicker, and eliminating a part thereof. Thereby, a low-defect continuous film can be obtained. Therefore, the corrosion resistance can be improved. Further, by insulating the surface of the second base film 22 with a plasma treatment, it is also possible to secure the electric characteristic by lightening the AC noise and the like, while improving the corrosion resistance further. As a result, it becomes possible to improve the quality and reliability of the protection targets such as the magnetic head sliders that are protected by the protective film 2.
As a result of the ESCA measurement, the peak position of Nls was in 397.5-398 eV, and the peak position of Si2p was in 101.5-102 eV. It is known according to Patent Document 3 that Si2p is 101.6 eV when Nls is 397.5 eV. Thus, it is considered a proof that a nitride film is fabricated on the surface of the second base film 22 through the above-described steps.
Second Embodiment
Next, a second embodiment of the present invention will be described by referring to
Further,
Through constituting the head gimbal assembly 50 having the magnetic head slider 1 disclosed in the first embodiment and also constituting the hard disk drive 100 in the manner described above, it becomes possible to increase the storage capacity of the hard disk drive 100 and to improve the reliability.
The protective film forming method according to the present invention can be utilized when forming a protective film on the surfaces of electronic components and the like, such as the magnetic head sliders. Therefore, the protective film forming method according to the present invention has an industrial applicability.
Number | Date | Country | Kind |
---|---|---|---|
2007 1 0196399 | Nov 2007 | CN | national |
2007-331300 | Dec 2007 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
5609948 | David et al. | Mar 1997 | A |
5841608 | Kasamatsu et al. | Nov 1998 | A |
6246538 | Kasamatsu et al. | Jun 2001 | B1 |
6490136 | Ito et al. | Dec 2002 | B1 |
6985315 | Yokohata et al. | Jan 2006 | B2 |
6995948 | Nakayama | Feb 2006 | B2 |
7269889 | Ueda et al. | Sep 2007 | B2 |
8035929 | Kawakita et al. | Oct 2011 | B2 |
20070163103 | Kagami et al. | Jul 2007 | A1 |
Number | Date | Country |
---|---|---|
1691138 | Nov 2005 | CN |
62-140225 | Jun 1987 | JP |
2001-343227 | Dec 2001 | JP |
2003-109339 | Apr 2003 | JP |
2003-208703 | Jul 2003 | JP |
2005-259346 | Sep 2005 | JP |
2005-302185 | Oct 2005 | JP |
2006-107673 | Apr 2006 | JP |
2007-026506 | Feb 2007 | JP |
Number | Date | Country | |
---|---|---|---|
20090135521 A1 | May 2009 | US |