Rare earth optical temperature sensor

Information

  • Patent Grant
  • 6746149
  • Patent Number
    6,746,149
  • Date Filed
    Tuesday, June 1, 1999
    25 years ago
  • Date Issued
    Tuesday, June 8, 2004
    20 years ago
Abstract
A rare earth optical temperature sensor is disclosed for measuring high temperatures. Optical temperature sensors exist that channel emissions from a sensor to a detector using a light pipe. The invention uses a rare earth emitter to transform the sensed thermal energy into a narrow band width optical signal that travels to a detector using a light pipe. An optical bandpass filter at the detector removes any noise signal outside of the band width of the signal from the emitter.
Description




The invention described herein was made by employees of the United States Government and may be manufactured and used by or for the Government for Government purposes without the payment of any royalties thereon or therefor.




BACKGROUND OF THE INVENTION




The present invention relates to temperature sensors and in particular to high temperature optical temperature sensors.




Selective emitters are devices for converting thermal energy into narrow band radiation or energy. Most solid state materials have nearly a constant spectral emittance (gray body). The spectral emittance of a rare earth is characterized by several emission bands in the visible and near infrared region resulting from electronic transitions from the lowest excited states. Materials containing rare earths (e.g., ytterbium (Yb), erbium (Er), thulium (Tm), dysprosium (D


Y


), and holmium (Ho)) can emit in narrow wavelength bands in the visible and near infrared region of the spectrum.




Selective emitters have been used in thermophotovoltaic energy conversion systems such as those described in U.S. Pat. Nos. 4,584,426 and 5,080,724.




Many existing temperature sensors are unsuitable and/or uneconomical for use in high temperature (greater than 2,000° K) harsh environments. For example, metal thermocouples suffer from high thermal conductivity (e.g., 1 W/cmK) that conducts heat away from the measurement site, causing errors in the measurement. Other sensors may require sophisticated electronics or other techniques to eliminate errors from the measurements.




SUMMARY OF THE INVENTION




An optical temperature sensor includes an emitter having a selective energy emission band. The emitter emits energy within the emission band in response to the emitter temperature. The sensor also includes a light pipe having a first and a second end. The first end communicates with the emitter. Also included is an optical bandpass filter communicating with the second end. The filter has a pass band corresponding to the emission band. Also included is a detector communicating with the filter. The detector detects the emitted energy as a measure of the temperature.











BRIEF DESCRIPTION OF THE DRAWING




The drawing is a schematic diagram of a sensor according to the invention.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




Referring to the drawing, an optical temperature sensor


10


includes a selective emitter


12


, a light pipe


14


, an optical bandpass filter


16


and a detector


18


. The emitter


12


may be, for example, a section of a circular cylinder friction fit into a cavity in the end of the light pipe


14


and have an approximate longitudinal thickness of 0.1 mm and a diameter in the approximate range of 0.1 to 1 mm. The selective emitter may also be deposited on the end of the light pump by a conventional film deposition technique such as evaporation, sputtering, or plasma spraying.




The emitter


12


may be composed, for example, of a rare earth oxide, a rare earth alumunum garnet, or a rare earth doped host material. The emitter


12


has a selective energy emission band, i.e., the emitter emits energy within the emission band in response to the temperature of the emitter


12


. The host material of the emitter


12


may be, for example, yttrium aluminum garnet (YAG, Y


3


Al


5


O


12


) or yttrium oxide (Y


2


O


3


). Different rare earth dopants provide different selective emission bands. For example, Yb provides a band about λ=1 μm, Er: λ=1.5 μm, Tm: λ=1.7 μm, Ho: λ=2.0 μm, and D


Y


: λ=2.7 μm.




The radiation emitted by the emitter


12


is coupled into the light pipe


14


. The light pipe


14


may be, for example, a circular cylindrical optical fiber having an approximate diameter in the range of 0.1 to 1.0 mm. The light pipe


14


acts as a waveguide for the radiation emitted by the emitter


12


. The light pipe


14


may be composed, for example, of sapphire, yttrium oxide or quartz. The filter


16


is a conventional optical bandpass filter. The filter


16


passes radiation in the emission band of the emitter


12


. Radiation in the light pipe


14


within the emission band of the emitter


12


is passed by the filter


16


to the detector


18


. Typically, the detector


18


will be an optical sensor sensitive to a relatively broad band of radiation (e.g., near infrared, infrared) which will include the emission band of the emitter


12


. The detector


18


may be, for example, composed of silicon, lead sulfide (PbS) or indium antimonide (InSb).




The temperature converter


20


receives a signal from the detector


18


indicative of the radiation emitted by the emitter


12


and converts this signal to a more useable form, e.g., a displayed temperature, a digitized temperature, a temperature control signal or an alarm.




The radiation in the emittance bands of the rare earths is strongly dependent on the temperature (e.g., greater than T


4


). The radiation emitted by a rare earth in an emission band is as follows:







q
x

=


15

π
4








ε
b



σ
sb



T
4






u
l


u
n






u
3



e
u

-
1









u









where






u
n


=




hc
0



λ
u


kT







and






u
l


=


hc
0



λ
l


kT








σ
sb

=

Stefan


-


Boltzmann





constant






λ
u

=

short





wavelength





end





of





selective





emitter





emission





band






λ
l

=

long





wavelength





end





of





selective





emitter





emission





band





h
=

Planck





constant






c
0

=

speed





of





light





in





a





vacuum





k
=

Boltzmann





constant





T
=

temperature





in





degrees





Kelvin






ε
b

=

emittance





of





emission





band





of





selective





emitter











If the radiation then travels through the light pipe


14


and the filter


16


(which passes wavelengths between λ


l


and λ


u


), the radiation at the detector


18


will be:








q




d




=T




f




T




s




q




E










T


f


=transmission of filter








T


s


=transmission of light pipe






The radiation q


E


leaving the emitter


12


is a sensitive function of the temperature T of the emitter


12


. Therefore, excellent temperature resolution is possible with the sensor


10


. In addition, the host materials YAG and yttrium oxide, or a rare earth oxide, or a rare earth aluminum garnet, can be used in high temperature (greater than 2,000° K) environments, thus providing a sensitive temperature sensor that can operate in high temperatures and harsh environments.




The most expensive component in the sensor


10


is the detector


18


. As a result, the lowest cost sensor


10


will use a detector of silicon. In this case, a Yb selective emitter may be chosen because such an emitter has an emission band centered at about λ=1 μm and silicon responds only for λ less than 1.1 μm (near infrared). The emitter


12


may then be, for example, ytterbium doped YAG or yttrium oxide.




Using a light pipe


14


of sapphire, the sensor


10


has, for example, a conductivity of about 0.01 W/cmK. This is much lower than that of a metal thermocouple (e.g., 1 W/cmK) and produces much less error in the measurement due to conduction of heat away from the measurement site.




Ytterbium, which has the shortest wave length emission band of the rare earths, requires the highest temperature to produce significant radiation. Therefore, if lower temperature operation is required, other rare earths with longer wavelength emission bands may be required. In this case, another detector instead of silicon would likely be chosen.




In operation, the emitter


12


is placed in contact with a sample whose temperature is desired. The emitter


12


assumes the temperature of the sample and emits a corresponding amount of radiation within the selective emission band of emitter


12


. The radiation travels along the light pipe


14


and through the filter


16


and is detected by the detector


18


. The detector


18


provides a signal that corresponds to the temperature of the sample. This signal is converted by the temperature converter


20


into an actual temperature. This conversion can be, for example, a look-up table or a model of the physical relationships.




Temperature error with the sensor


10


will result from stray radiation within the wavelength range transmitted by the filter


16


. This error will be small since, for example, sapphire is transparent out to a wavelength of almost 5 μm. Therefore, most of the radiation with a wavelength less than 5 μm that strikes the sapphire will pass through the fiber and will not reach the detector. Also, the radiation from the emitter


12


will be much larger than any stray radiation within the selective energy emission band. The selective emitter/filter combination has the effect of substantially improving the signal to noise ratio in the sensor.




The upper temperature limit for the sensor is determined by the melting point of the emitter material and the light pipe material. For YAG, the melting point is 2,200° K; and for the rare earth oxides the melting points are greater than 2200° K. Sapphire has a melting point of 2,345° K. If a higher operating temperature is desired, then yttrium oxide with a melting point of 2,683° K can be used for both the light pipe and emitter host material.




The lower temperature limit for the sensor is determined by the minimum power that the detector


18


can measure. If Yb is the rare earth used in the sensor, then λ


u


is approximately 0.9 μm and λ


l


is approximately 1.1 μm. Assuming ε


b


is 0.5 and T


f


T


s


is 0.1, then T greater than 625° K will yield q


d


greater than 1×10


−7


W/cm


2


. A silicon detector at room temperature of 0.01 cm


2


area will respond to this value of q


d


. Therefore, if Yb is used as the rare earth in the selective emitter then a temperature as low as 625° K is detectable.




It should be evident that this disclosure is by way of example and that various changes may be made by adding, modifying or eliminating details without departing from the fair scope of the teaching contained in this disclosure. The invention is therefore not limited to particular details of this disclosure except to the extent that the following claims are necessarily so limited.



Claims
  • 1. An optical temperature sensor, said sensor comprising:an emitter having a selective energy emission band, said emitter converting thermal energy to energy within said emission band in response to a temperature of said emitter, and wherein said emitter contains a rare earth element; a light pipe having a first end and a second end, said first end communicating with said emitter; an optical bandpass filter communicating with said second end, said filter having a pass band within said emission band; and a detector communicating with said filter, said detector detecting said emitted energy as a measure of said temperature.
  • 2. An optical temperature sensor, said sensor comprising:an emitter having a selective energy emission band, said emitter converting thermal energy to energy within said emission band in response to a temperature of said emitter, and wherein said emitter is composed of a rare earth aluminum garnet; a light pipe having a first end and a second end, said first end communicating with said emitter; an optical bandpass filter communicating with said second end, said filter having a pass band within said emission band; and a detector communicating with said filter, said detector detecting said emitted energy as a measure of said temperature.
  • 3. An optical temperature sensor, said sensor comprising:an emitter having a selective energy emission band, said emitter converting thermal energy to energy within said emission band in response to a temperature of said emitter, and wherein said emitter is composed of a rare earth oxide; a light pipe having a first end and a second end, said first end communicating with said emitter; an optical bandpass filter communicating with said second end, said filter having a pass band within said emission band; and a detector communicating with said filter, said detector detecting said emitted energy as a measure of said temperature.
  • 4. An optical temperature sensor according to claim 3, wherein said rare earth oxide is ytterbium oxide.
  • 5. An optical temperature sensor, said sensor comprising:an emitter having a selective energy emission band, said emitter converting thermal energy to energy within said emission band in response to a temperature of said emitter, and wherein said emitter is a high temperature host material which is doped with a rare earth element; a light pipe having a first end and a second end, said first end communicating with said emitter; an optical bandpass filter communicating with said second end, said filter having a pass band within said emission band; and a detector communicating with said filter, said detector detecting said emitted energy as a measure of said temperature.
  • 6. An optical temperature sensor according to claim 5, wherein said emitter is composed of yttrium oxide doped with ytterbium.
  • 7. An optical temperature sensor according to claim 5, wherein said host material is yttrium aluminum garnet which is doped with a rare earth element.
  • 8. An optical temperature sensor according to claim 7, wherein said dopant is ytterbium.
US Referenced Citations (23)
Number Name Date Kind
4313344 Brogardh et al. Feb 1982 A
4448547 Wickersheim May 1984 A
4523315 Stone Jun 1985 A
4576486 Dils Mar 1986 A
4584426 Nelson Apr 1986 A
4625389 Readhead Dec 1986 A
4764104 Nelson Aug 1988 A
4794619 Tregay Dec 1988 A
4826426 Nelson May 1989 A
5035513 Fehrenbach et al. Jul 1991 A
5080724 Chubb Jan 1992 A
5290103 Fevrier et al. Mar 1994 A
5299869 Wissinger Apr 1994 A
5352040 Mihalczo et al. Oct 1994 A
5447786 Rose et al. Sep 1995 A
5579427 Rusanov et al. Nov 1996 A
5601661 Milstein et al. Feb 1997 A
5780370 Chen et al. Jul 1998 A
5846684 Paz-Pujalt et al. Dec 1998 A
5879473 Sarraf Mar 1999 A
5885484 Allison et al. Mar 1999 A
6013199 McFarland et al. Jan 2000 A
6045259 Djeu Apr 2000 A