Patent Grant
11603613
This application is the U.S. national phase entry under 35 U.S.C. § 371 of International Application No. PCT/FR2016/050082, filed on Jan. 15, 2016, which claims priority to French Patent Application No. 1550348, filed on Jan. 16, 2015, the entireties of which are herein incorporated by reference.
The present disclosure relates to non-woven sheets and to laminated assemblies including such sheets.
The present disclosure relates more particularly to non-woven sheets and to laminated assemblies suitable for use in the field of hygiene, in particular for fabricating diapers elastic ears.
In the present disclosure, the term “non-woven” covers any non-woven fabric coming within the definition commonly accepted by the person skilled in the art, typically textiles made of fibers and/or filaments that are tangled together and held together in order to form a sheet.
On production lines for laminated assemblies, and as shown in
Because of this tension F, the sheet is subjected to a reduction in its width. This phenomenon, known as “neckdown” or as “shrinkage”, is shown diagrammatically in
In production lines, another solution consists in unwinding non-woven sheets without any tension, e.g. by transporting them on a conveyor belt. In order to form a laminated assembly, those sheets are then assembled without tension to an elastic film. Nevertheless, when the laminated assembly is subsequently unwound, the non-woven sheets making it up are subjected to the neckdown phenomenon, giving rise to deformation in the laminated assembly, thereby preventing it from being guided properly on downstream production lines.
One of the objects of the present invention is to provide a method of processing a sheet and a sheet as processed in this way, making it possible to remedy the above-mentioned drawbacks of the prior art.
More particularly, one of the objects of the invention is to make it possible to control the width of a non-woven sheet while such a sheet is being unwound under tension on a production line.
This object is achieved with a non-woven sheet extending in a longitudinal direction and a lateral direction orthogonal to the longitudinal direction, said sheet comprising:
whereby the elongation of the reinforced zone under the effect of a given force exerted in the longitudinal direction is strictly less than the elongation of the non-reinforced zone under the effect of the same force.
The term “bonding” when used of the fibers and/or filaments should be understood herein to mean any bonding that increases their cohesion. More particularly, such bonding may comprise locally increasing the volumetric density of the sheet (particularly but not exclusively locally increasing the density of fibers and/or filaments), obtained by any mechanical bonding (e.g. by compression) and/or thermal bonding and/or chemical bonding of the fibers and/or filaments, or indeed by a combination of several such types of bonding. For example, the bonding may be welding.
Consequently, the stiffness of the sheet is greater in each zone of reinforcement than in the non-reinforced zones.
When the sheet is subjected to longitudinal tension, its elongation in the longitudinal direction is limited compared with a non-reinforced prior art sheet when subjected to the same longitudinal tension, thereby also limiting the deformation that is induced in the lateral direction.
In the present disclosure, the elongation of a zone of the sheet is expressed as a percentage relative to its initial length.
A sheet of the invention may for example be constituted by a non-woven fabric obtained using dry-laid (dry process), wet-laid (wet process), or spun-laid technology (melt spinning/extrusion process), and consolidated by mechanical, thermal, chemical, and/or adhesive bonding.
In an example, the sheet is constituted by a consolidated carded type non-woven sheet, in particular a non-woven sheet of the Spunlace type, i.e. it is consolidated by hydro-entanglement.
The reinforcing pattern is generally constituted by repeating a unit pattern in the longitudinal direction of the sheet.
In an example, the geometric shapes constituting the reinforcing pattern are discrete elements, which may for example be circles, crosses, lozenges, oblong shapes, etc.
The term “discrete” is used of elements that are discontinuous or indeed isolated, so as to be distinct from one another. These elements may thus be defined by a closed outline.
The term “plurality of geometric shapes” is used to mean at least two discrete elements of respective outlines of the at least two discrete elements that may be identical, similar, or different.
Some shapes may be solid. Others may be constituted by a closed-loop curve that presents, over its entire extent, an inner margin and an outer margin.
In an example, the geometric shapes of the reinforcing pattern in each zone of reinforcement are arranged in such a manner that any straight line extending in the lateral direction of the sheet intersects at least one of said shapes. The reinforcement of the sheet is thus continuous over its entire length. Localized manifestations of the neckdown phenomenon are thus avoided.
In another example, the geometric shapes of the reinforcing pattern of each zone of reinforcement are arranged in such a manner that any straight line that is inclined relative to the lateral direction by an angle lying strictly in the range 0 to 90°, more particularly strictly in the range 0 to 45°, still more particularly inclined at an angle of about 24°, intersects at least one of said shapes of said zone.
The zone of reinforcement is generally defined by a left limit straight line DG and a right limit straight line DD, said parallel limit lines extending in the longitudinal direction of the sheet. The weld pattern is contained entirely between these two lines and each line is tangential to at least one shape of the reinforcing pattern.
In an example, the bonding percentage in the zone of reinforcement is greater than 10%, or more precisely greater than 15%, or indeed greater than 25%.
In an example, the bonding percentage in the zone of reinforcement is less than 90%, or more particularly less than 70%.
In the present disclosure, the bonding percentage in the zone of reinforcement is equal to the percentage of the area of said segment covered by the geometric shapes of the reinforcing pattern. It is generally measured on a segment of the zone of reinforcement having a width equal to the width of said zone and a length equal to an integer number of reinforcing unit patterns.
By way of example, this integer number may be selected so that the length of the segment is greater than the width of the reinforcing zone.
First and second adjacent zones of reinforcement are generally separated by an intermediate strip without reinforcement, extending in the longitudinal direction, and preferably presenting a width that is equal to at least 10% of the smaller of the widths of the two reinforcing zones.
In an example, the width of each zone of reinforcement represents at most 80% of the width of the sheet, preferably at most 60% of the width of the sheet.
For each reinforcing zone, it is possible to define a useful portion that is defined by a left limit margin BG and by a right limit margin BD.
The limit margin on one side of the useful portion is defined as follows:
It includes the “end” points of the reinforcing pattern, in other words the points that are furthest towards the outside on said side (in the lateral direction), with this applying for each coordinate along an axis extending in the longitudinal direction of the sheet.
Where appropriate, the limit margin also includes straight line segments extending in the lateral direction and interconnecting its portions constituted by the above-defined end points.
Each limit margin may thus be a straight line, a curved line, or a combination of one or more straight and/or curved line segments.
It is possible to measure the bonding percentage over the useful portion of the zone of reinforcement along a segment of said useful portion extending over a length that is equal to the length of the unit pattern. It is equal to the percentage of the surface area of said segment that is covered by the geometric shapes of the reinforcing pattern.
The bonding percentage over the useful portion of the zone of reinforcement may for example be greater than 15%, or more precisely greater than 20%, or indeed greater than 35%.
Generally, the bonding percentage over the useful portion of the zone of reinforcement is less than 90%, more particularly less than 75%.
In an example, the elongation of the reinforced zone under the effect of a traction force of 5 Newtons (N) exerted in the longitudinal direction is less than the elongation of the non-reinforced zone under the effect of the same force.
The elongation of the zone of reinforcement under the effect of said given force exerted in the longitudinal direction may for example be at least 5% less than, and more particularly at least 15% less than, or indeed more particularly at least 50% less than the elongation of the non-reinforced zone under the effect of the same force. For example, if the non-reinforced zone presents an elongation of 17% when subjected to a traction force of 5 Newtons, then the elongation of the zone of reinforcement is less than or equal to 12%.
In an example, the sheet further comprises at least one activated zone extending over a width that is less than the width of the sheet, and in which the non-woven fabric is activated.
A non-woven sheet generally presents little capacity for elongation compared with the capacity for elongation of an elastic film. When such a sheet is to be laminated on an elastic film in order to form a laminated assembly, it is sometimes necessary to apply prior processing locally or to its entire surface for the purpose of reducing the cohesion of its structure, so that once it has bonded to the elastic film the resulting laminated assembly can be stretched easily (with a lesser force, e.g. 10 N).
Activation consists in subjecting the non-woven fabric to stretching. It acts locally and in non-reversible manner to increase the capacity of the non-woven fabric to lengthen. Typically, activation is performed in the lateral direction of the sheet.
The activated non-woven fabric, in cross-section view, generally presents a wavy shape in its activated zone so long as it is not subjected to any external tension.
The present disclosure also provides a laminated assembly comprising at least one first sheet as defined above together with at least one elastic film connected to said first sheet.
In an example, the laminated assembly comprises at least a second non-woven sheet, the at least one elastic film being interposed between the first and second sheets.
In an example, the first sheet comprises at least one first zone of reinforcement, and the second sheet is a sheet of the above-defined type, having at least one second zone of reinforcement.
By way of example, the first and second zones of reinforcement may overlap over at least one overlap zone of predetermined width.
In an example, the projections of the respective reinforcing patterns of the first and second zones of reinforcement coincide over at least one zone of the laminated assembly.
Consideration is given herein to the projections of the reinforcing patterns onto a plane orthogonal to the thickness of the laminated assembly (in other words a plane orthogonal to the stacking direction of the layers of the laminated assembly).
In another example, the reinforcing pattern of the first zone of reinforcement and the reinforcing pattern of the second zone of reinforcement are different.
In another example, the projection of the respective reinforcing patterns of the first and second zones of reinforcement in the Z direction are arranged in such a manner that any straight line extending in the lateral direction of the sheet intersects the projections of the geometric shapes of the reinforcing patterns of the first and second zones of reinforcement. In particular, the projection of the respective reinforcing patterns of the first and second zones of reinforcement in the Z direction are arranged in such a manner that any straight line inclined relative to the lateral direction at an angle lying strictly between 0 and 90°, more particularly lying strictly between 0 and 45°, still more particularly inclined at an angle of about 24°, intersects the projection of the geometric shapes of the reinforcing patterns of the first and second zones of reinforcement.
Each zone of reinforcement of each sheet may be offset in the lateral direction relative to an elastic portion of the laminated assembly.
The term “elastic portion” of the laminated assembly is used to mean a portion of the laminated assembly including the elastic film and adapted to be stretched under the effect of a stretching force exerted in the lateral direction and adapted to return substantially to its initial shapes and dimensions after said stretching force has been released. By way of example, it may be a portion that conserves residual deformation or remanence after elongation and release (also known as “permanent set” or “SET” for short) of less than 20%, more particularly less than 15%, in certain circumstances less than 5% of its initial dimension (before elongation) for an elongation of 100% of its initial dimension, at ambient temperature (23° C.).
In another example, at least one first zone of reinforcement of the first sheet and at least one second zone of reinforcement of the second sheet overlap over at least one overlap zone of predetermined width, and one of the first zone of reinforcement of the first sheet and the second zone of reinforcement of the second sheet extends beyond said overlap zone towards an elastic portion of the laminated assembly in its lateral direction.
The present disclosure also provides a method of processing a non-woven sheet, said sheet extending in a longitudinal direction and in a lateral direction orthogonal to the longitudinal direction, the method comprising at least one reinforcing step during which, over at least one zone of reinforcement of the sheet extending over the entire length of the sheet as measured in the longitudinal direction and over a width that is strictly less than the width of the sheet as measured in its lateral direction, fibers and/or filaments constituting the sheet are bonded together using a reinforcing pattern comprising a plurality of geometric shapes in such a manner that the elongation of the reinforced zone under the effect of a given force exerted in the longitudinal direction is less than the elongation of a non-reinforced zone of the sheet under the effect of the same force.
During the reinforcing step, the cohesion of the fibers and/or filaments of the sheet is increased. More particularly, the volumetric density of the sheet is increased locally (particularly but not exclusively the density of fibers and/or filaments is increased locally), by mechanical bonding (e.g. by compressing the sheet), and/or thermal bonding (by heating the sheet), and/or chemical bonding of the fibers and/or filaments, or indeed by a combination of a plurality of such types of bonding. By way of example, the fibers and/or filaments may be locally welded.
By way of example, the reinforcement step may be performed by hot calendering.
In variants, it may also be performed by laser, by ultrasound, by embossing (cold calendering), or indeed by a combination of at least two such technologies.
In an example, the method further comprises an activation step in which the non-woven fabric is stretched in order to activate it over at least one activated zone of the sheet.
In an example, the method further comprises, prior to the reinforcement step, a step of adjusting the width of the sheet.
Several embodiments are described in the present disclosure. Nevertheless, unless specified to the contrary, characteristics described with reference to any one embodiment may be applied to any other embodiment.
The invention can be well understood and its advantages appear better on reading the following detailed description of several embodiments shown as non-limiting examples. The description refers to the accompanying drawings, in which:
The sheet 10 is defined relative to a longitudinal direction X1 in which its length L is measured, and a lateral direction Y1 that is orthogonal to X1, in which its width l is measured. These two longer dimensions of the sheet are shown in plan view of
By way of example, the sheet 10 is made as a Spunlace type non-woven fabric, constituted by a plurality of fibers consolidated by hydro-entanglement, and commonly used in the field of hygiene for its softness and its natural capacity for deformation.
Because of its high capacity for deformation, Spunlace non-woven fabric is particularly subject to the above-described neckdown phenomenon. When tension is applied thereto in a given direction, it undergoes considerable deformation in the orthogonal direction. Consequently, on a production line where it is subjected to considerable longitudinal tension, a Spunlace non-woven sheet shrinks significantly in its width direction.
In accordance with the invention, the sheet 10 is locally reinforced in order to avoid the neckdown phenomenon.
As shown in
The reinforced zones 20a, 20b, 20c, and 20d are bordered by non-reinforced zones 40.
Because of the bonding provided locally between the fibers, the sheet 10 is stiffened in the zones of reinforcement 20a, 20b, 20c, and 20d. Because of this stiffening, the lengthening of a reinforced zone of the sheet under the effect of a given force exerted in the longitudinal direction X1 is less than the lengthening of a non-reinforced zone, for the same force.
Consequently, when the sheet is subjected to longitudinal tension, its deformation induced in the lateral direction is limited compared with a non-reinforced sheet.
In order to measure the elongation of one zone of reinforcement or of one non-reinforced zone, it is possible by way of example to use the following methods:
The non-woven sheet is prepared in a normal atmosphere, as defined by the standard ASTDM 5170, at a temperature 23° C.±2° C. and at relative humidity of 50%±5%.
The equipment used is a dynamometer complying with the standard EN 10002, in particular a Synergie 200H, available from the supplier NTS Systems Corp. USA, together with utilization software TESTWORKS 4.04 B.
A cutter or scissors is/are used for preparing a sample having a width of 10 millimeters (mm) in the cross direction (CD) of the sheet and a length of 150 mm in the machine direction (MD) of the sheet, in a zone of reinforcement or in a non-reinforced zone.
The sample is placed between the jaws of the dynamometer.
The following parameters are selected:
The sample is stretched in its width direction (corresponding to the longitudinal direction of the sheet) until it breaks, by moving the jaws vertically.
A curve is then obtained by plotting stretching force as a function of percentage elongation. It is thus possible to define the percentage elongation at 5 N, which corresponds to the elongation to which the sheet is subjected when being unwound on the production line.
The value of 5 N is not limiting, and in other measurement methods it might be different, e.g. equal to 10 N.
The sheet thus presents a plane of symmetry P parallel to its longitudinal direction X1.
The number, the width, and the locations of the zones of reinforcement of a sheet of the invention may nevertheless vary as a function of needs and of the subsequent use intended for the sheet. Thus, a sheet may have a single zone of reinforcement or a number of zones of reinforcement that is other than four. Furthermore, although such symmetrical configurations provide advantages, in particular of enabling two identical elastic lugs to be fabricated simultaneously from a laminate using such a sheet by cutting along the plane of symmetry P, the zone(s) of reinforcement of a sheet are not necessarily in the side margins of the sheet nor are they necessarily centered relative to the sheet. Furthermore, they need not necessarily be arranged symmetrically. The widths of the zones of reinforcement in a given sheet may also be adjusted depending on circumstances.
Nevertheless, and as shown in
In the example shown, the non-woven sheet 10 also has an activated zone 30a, 30b in each non-reinforced zone 40 situated between two adjacent zones of reinforcement 20a, 20b, 20c, where an activated zone 30a, 30b is in the form of a continuous strip of width l3 in which the fibers of the non-woven fabric have been activated.
Preferably, the width l3 of an activated zone is greater than the width l1 of the zone of reinforcement. More particularly, the width l3 of an activated zone is 1.5 times greater than the width l1 of the zone of reinforcement.
For reasons of concision, only one zone of reinforcement 20a of the sheet 10 is described in detail below. All of the elements described with reference to that zone of reinforcement 20a are nevertheless applicable to the other zones of reinforcement 20b, 20c of the sheet 10.
As shown in
Preferably, the width l1 of the zone of reinforcement 20a (in other words the distance measured in the lateral direction Y1 between the lines DG and DD) represents no more than 80% of the width l of the sheet 10, preferably no more than 60% of the width l of the sheet 10.
In the example, in register with the reinforcing pattern 22, the fibers of the sheet 10 are compressed and welded together, possibly involving as much as complete melting of the material from which they are made, the fibers as such disappearing and being replaced by a zone of film, thereby locally increasing the density of the sheet. By way of example, such reinforcement may be obtained by hot calendering, as described in greater detail below.
The thickness e1 of the sheet 10 in the zone of reinforcement 20a is less than the thickness e of the sheet in the non-reinforced zones 40, as can be seen in
The reinforcing pattern 22 contained in the zone 20a is typically constituted by regularly repeating a unit pattern 26 of length lm in the longitudinal direction X1.
The reinforcing unit pattern 26 of the zone 20a is shown in greater detail in
In this example, it is made up of a combination of discrete solid geometric shapes, specifically crosses and lozenges.
The bonding percentage in the zone of reinforcement 20a, in other words the bonding percentage over a segment of the zone of reinforcement corresponding to the unit pattern 26, is preferably greater than 10% and less than 90%, or more precisely lies in the range 25% to 70%.
A useful portion 28 of the zone of reinforcement 20a is also defined, being defined by a left limit margin BG and a right limit margin BD. In the example of
The left and right limit margins BG and BD of the useful portion 28 are shown in
The left margin BG includes the end points of the reinforcing pattern 22 that are the furthest to the left (in the lateral direction Y1), and this applies for each coordinate taken along an axis extending in the longitudinal direction X1. These end points are represented by a continuous bold line in
The right margin BD comprises the end points of the reinforcing pattern 22 that are the furthest to the right (in the lateral direction Y1), with this applying to each coordinate taken along an axis extending in the longitudinal direction X1. These end points are represented by a continuous bold line on the right in
The bonding percentage over a useful portion 28 of the zone of reinforcement 20a, as measured over a segment having a length Lm (the unit pattern in this example) is preferably greater than 15%, and more particularly greater than 20% and less than 90%.
As is well known to the person skilled in the art, the fibers and/or filaments of a non-woven fabric are held together as a result of consolidation performed over the entire extent of tangled fibers and/or filaments during fabrication of the non-woven fabric, which consolidation may be thermal (calendering, ultrasound, etc.), mechanical (hydro-entanglement, needling, etc.), chemical, or adhesive.
Consolidation provides a certain amount of cohesion for the fibers and/or filaments, enabling them to be manipulated and transported, and in particular to be wound in the form of a roll and to be unwound. Under certain circumstances, consolidation may be performed at a plurality of points that are distributed in substantially uniform manner over the entire width of the non-woven sheet. For example, calendered carded non-woven fabric typically presents thermal consolidation points.
The consolidation points form a pattern that is different from the reinforcing pattern. For simplification purposes, these consolidation points of the non-woven fabric are not shown in the figures.
It should be understood that the consolidation points are clearly to be distinguished from the above-described reinforcing pattern. Consolidation serves to give the sheet a certain amount of initial cohesion over its entire area in order to form a non-woven fabric, whereas the reinforcement provided by the present invention serves to increase locally the initial cohesion that results from that consolidation. The consolidation points of the non-woven fabric are therefore not taken into account when calculating the above-mentioned bonding percentage of the reinforcement.
In an example, the geometric shapes 24 of the reinforcing pattern 22 are arranged in such a manner that any line extending in the lateral direction Y1 of the sheet 10, such as the line D1 in
Still more preferably, the geometric shapes 24 of the reinforcing pattern 22 are arranged in such a manner that any line that slopes relative to the lateral direction Y1 at an angle Ω lying strictly between 0 to 90°, such as the line D2 in
The above-described reinforcing pattern 22 is nevertheless not limiting, and it is possible for the geometric patterns 24 and the way they are arranged to vary.
In particular, the geometric shapes 24 constituting the reinforcing pattern 22 need not be solid. Thus, in a variant, each shape 24 may be constituted by a closed-loop curve that presents over its entire extent an inside margin and an outside margin.
This applies to the reinforcing pattern 22A shown in
Selecting this type of pattern serves to limit the energy needed for creating it, while conserving satisfactory performance. Furthermore, the surface remains soft to the touch.
In another example, the reinforcing pattern 22 may also have limit margins BG and BD extending in directions that are substantially inclined relative to the longitudinal direction X1, e.g. deviating from that direction in alternation to the left and then to the right, so as to form a zigzag or a sinewave. Such an arrangement can be obtained using calendering rollers pivoting from left to right or from right to left while making a unit reinforcing pattern.
A reinforcing sheet 10 of the above-described type can be used in the fabrication of laminated assemblies, and in particular trilaminates comprising two non-woven sheets and at least one elastic film interposed between said sheets.
A first embodiment of such a laminated assembly 100 is shown in
The laminated assembly 100 is formed by superposing, in the direction Z:
The non-woven sheets 110, 110′ of the laminated assembly and the elastic films 150, 152 interposed between said sheets are connected together by adhesive 160, 160′.
The activated zones 130a and 130b of the first sheet 110 give it a certain capacity for elongation, locally.
The second sheet, made of a non-woven fabric that is more elastic than the fabric constituting the first sheet 110, is not activated.
Nevertheless, in a variant embodiment, both sheets could be made of non-woven fabric of the same kind.
In the example, the adhesive 160, 160′ is applied in solid strips 161 and 161′ between the elastic films and on their lateral margins, whereby the elastic films are securely fastened to the sheets 110 and 110′, in straight lines or beads 162 and 162′ in register with the activated zones 130a and 130b of the first sheet 110. In a variant, the elastic film may have adhesive applied over its entire width in continuous manner, possibly selecting a thickness for the adhesive that is smaller in certain zones (in particular in the center).
In the example shown, the elastic films 150 and 152 may be stretched between the beads of adhesive 162 and 162′, thereby providing the laminated assembly 100 with elasticity.
The zones E situated in register with the central zones of the elastic films 150 and 152 covered in the beads of adhesive 162 and 162′ thus constitute portions of the laminated assembly 100 that are said to be “elastic”.
In another embodiment, it is possible to envisage that the elastic film is applied directly on the non-woven sheets, thereby obtaining a laminate that does not have any adhesive (or fastener agent), e.g. by applying the sheets onto the elastic film at the outlet from an extruder.
By way of example, and as shown in
In the example of
In other embodiments, a first zone of reinforcement of the first sheet and a second zone of reinforcement of the second sheet may overlap, in other words they may be positioned in register with each other in the Z direction.
Under such circumstances, the reinforcing pattern in the two superposed zones may be identical or different.
Furthermore, the two zones of reinforcement may optionally have the same width, and the two zones may overlap over their entire width or over a portion only of their width.
Thus, by way of example,
In this embodiment, the first and second zones of reinforcement 120a and 120′ extend over the entire length of the sheet measured in the longitudinal direction and over a width that is strictly less than the width of the sheet measured in the lateral direction.
In this example, it can be seen that the projection in the Z direction of the respective reinforcing patterns 122A and 122B of the first and second zones of reinforcement 120a and 120′ are arranged in such a manner that any straight line extending in the lateral direction Y1 of the sheet intersects the projection of the geometric shapes of the reinforcing patterns of the first and second zones of reinforcement. In particular, the projection of the respective reinforcing patterns 122A and 122B of the first and second zones of reinforcement 120a and 120′ in the Z direction are arranged in such a manner that any line that is inclined relative to the lateral direction at an angle lying strictly between 0 and 90°, and still more particularly lying strictly between 0 and 45°, and more particularly inclined at an angle of about 24°, intersects the projection of the geometric shapes of the reinforcing patterns of the first and second zones of reinforcement.
In a particular arrangement, the zones of reinforcement may have reinforcing patterns that are identical or partially identical, and the projections of the respective reinforcing patterns of the first and second zones of reinforcement in the stacking direction may coincide over at least a predetermined width of the laminated assembly.
The general structure of the laminated assembly, in particular concerning the arrangement of lines and strips of adhesive, is substantially identical to that of
In this example, a first zone of reinforcement 220a forming part of the first sheet overlaps a second zone of reinforcement 220a′ forming part of the second sheet 210′ over an overlap zone referenced ZC in
The opposite side of the laminated assembly is arranged symmetrically, so it is not described in greater detail below.
In the particular example shown, the zones of reinforcement 220a and 220a′ have the same width and they overlap over this entire width referenced lc (width of the overlap zone).
In a particular provision, the reinforcing patterns of the first and second zones of reinforcement are identical.
Thus, by way of example,
In an example, the projections onto a plane orthogonal to the Z direction of the thickness of the laminated assembly 200, the reinforcing patterns 222A, 222A′ of the first and second zones of reinforcement 220a, 220a′, coincide over the overlap zone ZC, as shown in
In another example shown in
In yet another example, shown in
As shown in
In the example, the portion of the second zone of reinforcement 220a′ projecting beyond the overlap zone is referenced ZR. This portion faces a non-reinforced zone of the first sheet 210. It is arranged in the lateral direction Y1 between the overlap zone ZC and the elastic film 250.
It has been found that such provisions make it possible to limit the concentrations of stresses in the laminated assembly, and to increase its ability to withstand rupture.
It should be observed that the example of
Furthermore, the zone of reinforcement that extends beyond the overlap zone ZC towards the elastic portion E of the laminated assembly could equally well be the first zone of reinforcement 220a of the first sheet 210.
From upstream to downstream in the travel direction of the sheet for processing (from left to right in the figure) the installation 900 comprises:
In an example, the method of processing the sheet comprises the following steps:
Once it has been unwound, the sheet 10 is activated locally by the activation module 74. In the example, this module 74 has two activation rollers R1 and R2 each having a stack of parallel disks. Since the disks of each roller mesh with the disks of the adjacent roller, the zones of the sheet 10 passing between the disks of the rollers R1 and R2 are stretched in the lateral direction Y1, thereby forming the activated zones 30a and 30b. In these locations, the fibers of the sheet 10 are broken.
The sheet 10 is then deformed more generally by the stretcher module 76 which generally comprises a plurality of rollers (not shown) having the purpose of stretching the sheet locally. The sheet is stretched therein until it reaches a width lmax greater than the useful width l desired for the laminated assembly that is fabricated downstream in the production line 82.
In the width management module 78, which comprises means for measuring the width of the sheet and means for adjusting this width to a desired value, e.g. by stretching, the width of the sheet 10 is adjusted to the useful width l that it is to conserve throughout the production line 82.
It is then reinforced, immediately downstream from the width management module 78 in order to avoid any variation in its width.
By way of example, the reinforcement is performed by hot calendering.
Under such circumstances, the reinforcement module 80 comprises two heated calendering rollers R3 and R4 that form reinforcing rollers, with at least one of them including rings on its outside surface (four rings in this example) carrying portions in relief reproducing a unit reinforcing pattern. When the sheet 10 passes between the reinforcing rollers, in its longitudinal direction, portions in relief press against the fibers that deform and become welded together under the effect of heat, thereby forming the zones of reinforcement 20a, 20b, 20c, 20d.
In variant embodiments and by way of example, the reinforcement could be made by: laser; ultrasound; embossing; or indeed a combination of two or more of these technologies.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1550348 | Jan 2015 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2016/050082 | 1/15/2016 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2016/113516 | 7/21/2016 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5569528 | Van der Loo et al. | Oct 1996 | A |
| 5620779 | Levy | Apr 1997 | A |
| 8148598 | Tsang | Apr 2012 | B2 |
| Number | Date | Country |
|---|---|---|
| 1218170 | Nov 2004 | EP |
| 2401147 | Jun 2015 | EP |
| S52-124983 | Oct 1977 | JP |
| S61-201064 | Sep 1986 | JP |
| 2003-507585 | Feb 2003 | JP |
| 2013-520578 | Jun 2013 | JP |
| 2100498 | Dec 1997 | RU |
| 2673772 | Nov 2018 | RU |
| 0100915 | Jan 2001 | WO |
| 03008192 | Jan 2003 | WO |
| Entry |
|---|
| International Search Report and English language translation issued in International App. No. PCT/FR2016/050082 dated May 2, 2016 (8 pages). |
| Office Action issued in Japanese Patent Application No. 2017-537431, dated Oct. 1, 2019 (8 pages). |
| Number | Date | Country | |
|---|---|---|---|
| 20170362756 A1 | Dec 2017 | US |