Resin Composition

Abstract
The present application relates to a composition, a battery module and a battery pack. According to one example of the present application, it is possible to provide a battery module and a battery pack which have improved heat dissipation properties, adhesive force, adhesion reliability and processability as well as excellent power to volume.
Description
TECHNICAL FIELD
Cross-Reference to Related Applications

This application claims the benefit of priority based on Korean Patent Application No. 10-2018-0035750 filed on Mar. 28, 2018, and Korean Patent Application No. 10-2019-0029276 filed on Mar. 14, 2019, the disclosures of which are incorporated herein by reference in their entirety.


Technical Field

The present application relates to a resin composition. Specifically, the present application relates to a resin composition, a battery module comprising a cured product of the resin composition, a battery pack, and an automobile.


BACKGROUND ART

A secondary battery includes a nickel cadmium battery, a nickel hydride battery, a nickel zinc battery, or a lithium secondary battery, and the like, where a typical example thereof is a lithium secondary battery.


The lithium secondary battery mainly uses lithium oxides and carbon materials as positive electrode and negative electrode active materials, respectively. The lithium secondary battery includes an electrode assembly in which a positive plate and a negative plate coated with a positive electrode active material and a negative electrode active material, respectively, are disposed with a separator interposed therebetween, and an exterior material in which the electrode assembly is sealed and housed together with an electrolyte, which can be classified as a can type secondary battery and a pouch type secondary battery depending on the kind of the exterior material. Such a single secondary battery can be referred to as a battery cell.


In the case of medium and large devices such as automobiles or power storage systems, in order to capacity and power, a battery module in which a large number of battery cells are electrically connected to each other may be used or a battery pack in which a plurality of such battery modules are connected may be used.


In order to construct the battery module or the battery pack, various fastening parts, cooling equipment, and the like are required, where such fastening parts or cooling equipment, and the like cause an increase in the manufacturing cost of the battery module or the battery pack, and increase volume and weigh. This causes a problem that the power of the battery module or the battery pack is also lowered relative to the increased volume and weight.


In addition, when the battery pack is used in an automobile or the like, it is exposed to external shocks such as vibration, and therefore, excellent durability needs to be secured.


DISCLOSURE
Technical Problem

It is one object of the present application to provide a resin composition capable of solving the above-mentioned problems.


It is another object of the present application to provide a resin composition having excellent processability as well as heat dissipation, adhesive force and adhesion reliability, when used in a battery module or a battery pack.


It is another object of the present application to provide a battery module and a battery pack.


The above and other objects of the present application can be all solved by the present application, which is described in detail below.


Technical Solution

In one example related to the present application, the present application relates to a composition used for a battery module or a battery pack. Specifically, the composition of the present application may be a composition which is used to fix one or more battery cells in a module case by being injected into the case of the battery module and contacting the battery cells present in the battery module, as described below.


In the present application, a urethane-based composition may be used as the composition. Specifically, in the present application, a two-component urethane-based composition may be used. The two-component urethane means polyurethane formed by mixing an isocyanate-based compound and a polyol-based compound, which is distinguished from one-component polyurethane having urethane groups in a single composition.


In the case of the two-component polyurethane, a main material comprising a polyol and the like and a curing agent comprising an isocyanate and the like may react at room temperature and be cured. That is, the composition of the present application may be a room temperature curing type. In the present application, the term “room temperature” is a state without particularly warming or cooling, which may mean any temperature within the range of about 10° C. to 30° C., such as a temperature of about 15° C. or higher, 18° C. or higher, 20° C. or higher, or about 23° C. or higher and about 27° C. or lower. The curing reaction may be assisted by a catalyst such as, for example, dibutyltin dilaurate (DBTDL). Accordingly, the two-component urethane-based composition may comprise a physical mixture of a main component (polyol) and a curing agent component (isocyanate), and/or may comprise a reactant (cured product) of the main component and the curing agent component.


The two-component urethane-based composition of the present application may comprise a main composition part (or main part) containing at least a polyol resin and a curing agent composition part (or curing agent part) containing at least a polyisocyanate. Accordingly, the cured product of the resin composition may comprise both the polyol-derived unit and the polyisocyanate-derived unit. At this time, the polyol-derived unit may be a unit which is formed by urethane-reacting the polyol with the polyisocyanate, and the polyisocyanate-derived unit may be a unit which is formed by urethane-reacting the polyisocyanate with the polyol.


The composition may also comprise a filler. For example, in order to ensure thixotropy as required in the process and/or to ensure heat dissipation (thermal conductivity) within the battery module or the battery pack, the composition of the present application may comprise an excess of fillers, as described below. The details will be described in detail in the following related description.


The polyol resin and isocyanate components contained in the urethane-based composition may have a glass transition temperature (Tg) of less than 0° C. after curing. In the present application, the term “glass transition temperature after curing” may be a glass transition temperature measured for a cured product that a conversion rate based on the NCO peak around 2250 cm−1 is 80% or more, which is determined by a FT-IR analysis on the basis of the curing state at room temperature and 30 to 70% relative humidity for 24 hours.


When the glass transition temperature range is satisfied, brittle characteristics can be secured in a relatively short time even at a low temperature where the battery module or the battery pack can be used, thereby ensuring impact resistance and vibration resistance characteristics. On the other hand, if the above range is not satisfied, the tacky property of the cured product may be excessively high or the thermal stability may be lowered. In one example, the lower limit of the glass transition temperature of the urethane-based composition after curing may be about −70° C. or higher, −60° C. or higher, −50° C. or higher, −40° C. or higher, or about −30° C. or higher, and the upper limit may be about −5° C. or lower, −10° C. or lower, −15° C. or lower, or about −20° C. or lower.


In one example, an ester-based polyol resin may be used as the polyol resin contained in the main composition part. When the ester-based polyol is used, it is advantageous in securing excellent adhesion and adhesion reliability in the battery module after curing the resin composition.


In one example, as the ester-based polyol, for example, a carboxylic acid-based polyol or a caprolactone-based polyol may be used.


The carboxylic acid-based polyol can be formed by reacting components comprising a carboxylic acid and a polyol (e.g., diol or triol), and the caprolactone-based polyol can be formed by reacting components comprising a caprolactone and a polyol (e.g., diol or triol). At this time, the carboxylic acid may be a dicarboxylic acid.


In one example, the polyol may be a polyol represented by the following formula 1 or 2.




embedded image


In Formulas 1 and 2, X is a carboxylic acid-derived unit, and Y is a polyol-derived unit. The polyol-derived unit may be, for example, a triol unit or a diol unit. In addition, n and m may be any number.


In Formula above, the carboxylic acid-derived unit is a unit formed by reacting a carboxylic acid with a polyol, and the polyol-derived unit is a unit formed by reacting a polyol with a carboxylic acid or caprolactone.


That is, when the hydroxyl group of the polyol and the carboxyl group of the carboxylic acid are reacted, the water (HO2) molecule is eliminated by condensation reaction to form an ester bond, where after the carboxylic acid forms an ester bond by the condensation reaction, X in Formula 1 above means a moiety excluding the ester bond portion. In addition, after the polyol forms an ester bond by the condensation reaction, Y is a moiety excluding the ester bond. The ester bond is represented in Formula 1.


In addition, after the polyol forms an ester bond with caprolactone, Y in Formula 2 also represents a moiety excluding the ester bond. The ester bond is represented in Formula 2.


On the other hand, when the polyol-derived unit of Y in Formulas above is a unit derived from a polyol having three or more hydroxyl groups such as a triol unit, a branched structure may be realized in the Y part in the formula structure.


In Formula 1 above, the kind of the carboxylic acid-derived unit of X is not particularly limited, but in order to secure desired physical properties, it may be any one unit selected from the group consisting of a phthalic acid unit, an isophthalic acid unit, a terephthalic acid unit, a trimellitic acid unit, a tetrahydrophthalic acid unit, a hexahydrophthalic acid unit, a tetrachlorophthalic acid unit, an oxalic acid unit, an adipic acid unit, an azelaic acid unit, a sebacic acid unit, a succinic acid unit, a malic acid unit, a glutaric acid unit, a malonic acid unit, a pimelic acid unit, a suberic acid unit, a 2,2-dimethylsuccinic acid unit, a 3,3-dimethylglutaric acid unit, a 2,2-dimethylglutaric acid unit, a maleic acid unit, a fumaric acid unit, an itaconic acid unit and a fatty acid unit. From the viewpoint of a low glass transition temperature in the above-described range, an aliphatic carboxylic acid-derived unit may be preferable to an aromatic carboxylic acid-derived unit.


On the other hand, in Formulas 1 and 2, the kind of the polyol-derived unit of Y is not particularly limited, but in order to secure desired physical properties, it may be one or more selected from the group consisting of an ethylene glycol unit, a diethylene glycol unit, a propylene glycol unit, a 1,2-butylene glycol unit, a 2,3-butylene glycol unit, a 1,3-propanediol unit, a 1,3-butanediol unit, a 1,4-butanediol unit, a 1,6-hexanediol unit, a neopentyl glycol unit, a 1,2-ethylhexyldiol unit, a 1,5-pentanediol unit, a 1,9-nonanediol unit, a 1,10-decanediol unit, a 1,3-cyclohexanedimethanol unit, a 1,4-cyclohexanedimethanol unit, a glycerin unit and a trimethylolpropane unit.


On the other hand, in Formula 1 above, n is any number, and the range may be selected in consideration of the desired physical properties of the resin composition or a resin layer, which is the cured product thereof. For example, n may be about 2 to 10 or 2 to 5.


Also, in Formula 2 above, m is any number, and the range may be selected in consideration of the desired physical properties of the resin composition or a resin layer, which is the cured product thereof. For example, m is about 1 to 10 or 1 to 5.


If n and m in Formulas 1 and 2 are outside the above ranges, the crystallizability expression of the polyol becomes stronger, which may adversely affect the injection processability of the composition.


The molecular weight of the polyol may be adjusted in consideration of low-viscosity characteristics, durability or adhesion, and the like, as described below, which may be within a range of, for example, about 300 to 2,000. Unless otherwise specified, in this specification, the “molecular weight” may be a weight average molecular weight (Mw) measured using GPC (gel permeation chromatograph). If it is out of the above range, the reliability of the resin layer after curing may be poor and problems related to volatile components may occur.


In the present application, the polyisocyanate may mean a compound containing two or more isocyanate groups.


In the present application, the kind of the polyisocyanate contained in the curing agent composition part is not particularly limited, but in order to secure desired physical properties, a non-aromatic isocyanate compound containing no aromatic group can be used. That is, it may be advantageous to use an aliphatic or alicyclic series. When an aromatic polyisocyanate is used, the reaction rate may be too fast and the glass transition temperature of the cured product may be increased, so that it may be difficult to ensure the processability and physical properties suitable for the use of the composition of the present application.


For example, an aliphatic or aliphatic cyclic polyisocyanate or a modified product thereof may be used. Specifically, an aliphatic polyisocyanate such as hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, norbornane diisocyanate methyl, ethylene diisocyanate, propylene diisocyanate or tetramethylene diisocyanate; an aliphatic cyclic polyisocyanate such as transcyclohexane-1,4-diisocyanate, isophorone diisocyanate, bis(isocyanatomethyl)cyclohexane diisocyanate or dicyclohexylmethane diisocyanate; or one or more carbodiimide-modified polyisocyanates or isocyanurate-modified polyisocyanates of the foregoing; and the like may be used. Also, a mixture of two or more of the above-listed compounds may be used.


The ratio of the polyol-derived resin component to the polyisocyanate-derived resin component in the resin composition is not particularly limited, which can be appropriately adjusted so that the urethane reaction between them can be performed.


As described above, an excess of fillers may be included in the composition, for securing heat dissipation (thermal conductivity) or thixotropy as required in the process, where if an excess of fillers is used, the viscosity of the composition increases, so that the processability at the time of injecting the composition into the case of the battery module may be deteriorated. Therefore, it requires low-viscosity properties sufficient to not interfere with the processability, while comprising an excess of fillers. In addition, when merely showing a low viscosity, it is also difficult to ensure the processability, so that it may be necessary that appropriate thixotropy is required, excellent adhesive force is exhibited when cured and the curing itself proceeds at room temperature. Then, the ester-based polyol is advantageous for securing the adhesion after curing, but is highly crystalline, so that there is a high possibility of becoming a wax state at room temperature and there is a disadvantage in securing proper injection processability due to viscosity increase. Even if it is used by lowering the viscosity through melting, the viscosity increase by crystallization in the injection or application process of the composition, which can be continued after mixing with fillers, occurs due to crystallizability occurring naturally in the storage process, and as a result, the processability may be lowered. In view of this point, the ester-based polyol used in the present application can satisfy the following characteristics.


In the present application, the ester-based polyol may be an amorphous or sufficiently low crystalline polyol. Here, the “amorphous” means a case where the crystallization temperature (Tc) and the melting temperature (Tm) are not observed in a DSC (differential scanning calorimetry) analysis. At this time, the DSC analysis can be performed at a rate of 10° C./minute within a range of −80° C. to 60° C., and for example, a method can be performed, in which the temperature is raised from 25° C. to 50° C. at the above rate, and then the temperature is reduced to −70° C. and raised to 50° C. again. Here, the “sufficiently low crystalline” means a case where the melting point or melting temperature (Tm) observed in the DSC analysis is less than 15° C., which is about 10° C. or lower, 5° C. or lower, 0° C. or lower, −5° C. or lower, −10° C. or lower, or −20° C. or lower or so. At this time, the lower limit of the melting point is not particularly limited, but for example, the melting point may be about −80° C. or higher, about −75° C. or higher, or about −70° C. or higher. When the polyol is crystalline or has high (room temperature) crystallizability, such as not satisfying the melting point range, the viscosity difference depending on the temperature easily increases, so that in the process of mixing the filler and the resin, the dispersion degree of the filler and the viscosity of the final mixture may be adversely affected, the processability is lowered, and as a result, it may become difficult to satisfy the cold resistance, the heat resistance and the water resistance required in the adhesive composition for a battery module.



FIG. 1 is a graph showing the results of DSC analysis of several polyols as an example for determining the amorphous characteristic or the sufficiently low crystallizability characteristic of the ester-based polyol. According to the present application, Sample #1 can be determined to be amorphous and Samples #2 and #3 can be determined to be sufficiently low crystalline. On the other hand, in the case of Sample #4 having a melting temperature (Tm) of 33.52° C., it can be said that the crystallizability is high.


Furthermore, in the present application, an additive may be used in order to secure the use of the resin composition and the function required according to the use thereof. For example, the resin composition may comprise a predetermined filler in consideration of thermal conductivity, insulating property, heat resistance (TGA analysis), and the like of the resin layer. The form or method in which the filler is contained in the resin composition is not particularly limited. For example, the filler may be used to form a urethane-based composition in a state that it is contained in the main composition part and/or the curing agent composition part in advance. Alternatively, in the process of mixing the main composition part and the curing agent composition part, the separately prepared filler may also be used by a method that it is mixed together.


In one example, the filler included in the composition may be at least a thermally conductive filler. In the present application, the term thermally conductive filler may mean a material having a thermal conductivity of about 1 W/mK or more, about 5 W/mK or more, about 10 W/mK or more, or about 15 W/mK or more. Specifically, the thermal conductivity of the thermally conductive filler may be about 400 W/mK or less, about 350 W/mK or less, or about 300 W/mK or less. The kind of the usable thermally conductive filler is not particularly limited, but it may be a ceramic filler when insulating property and the like are considered together. For example, ceramic particles such as alumina, AlN (aluminum nitride), BN (boron nitride), silicon nitride, SiC or BeO may be used. The shape or ratio of the filler is not particularly limited, which may be suitably adjusted in consideration of the viscosity of the urethane-based composition, the possibility of settling in the cured resin layer of the composition, the desired heat resistance or thermal conductivity, an insulating property, a filling effect or dispersibility, and the like. Generally, the larger the size of the filler, the higher the viscosity of the composition comprising the same and the higher the possibility that the filler precipitates in the resin layer. Furthermore, the smaller the size, the thermal resistance tends to be increased. Therefore, the filler having an appropriate type and size may be selected in consideration of the above points, and two or more fillers may also be used, if necessary. Considering the filling amount, it is advantageous to use a spherical filler, but considering network formation or conductivity, a filler in a form such as needle-like morphology or flattened morphology may also be used. The thermal conductivity of the filler can be measured according to known methods, wherein the thermal conductivity of the filler can be measured by a method of melting the filler and then making a specimen.


In one example, the composition may comprise a thermally conductive filler having an average particle diameter in a range of 0.001 μm to 80 μm. In another example, the average particle diameter of the filler may be 0.01 μm or more, 0.1 μm or more, 0.5 μm or more, 1 μm or more, 2 μm or more, 3 μm or more, 4 μm or more, 5 μm or more, or about 6 μm or more. In another example, the average particle diameter of the filler may be about 75 μm or less, about 70 μm or less, about 65 μm or less, about 60 μm or less, about 55 μm or less, about 50 μm or less, about 45 μm or less, about 40 μm or less, about 35 μm or less, about 30 μm or less, about 25 μm or less, about 20 μm or less, about 15 μm or less, about 10 μm or less, or about 5 μm or less. The average particle diameter can be measured using a PSA (particle size analysis) apparatus. In one example, when ranking from 1 to 100 for particles by size, the average particle diameter may mean D (50), which is the particle size of the 50th order.


In order to obtain excellent heat dissipation performance, it can be considered that a high content of the thermally conductive filler is used. For example, the filler may be used in an amount of about 50 to 2,000 parts by weight, relative to 100 parts by weight of the total resin components, that is, the sum of the ester-based polyol resin and polyisocyanate contents. In another example, the filler content may be used in excess of the total resin component. Specifically, the filler may be used in an amount of about 100 parts by weight or more, about 150 parts by weight or more, about 200 parts by weight or more, about 250 parts by weight or more, about 300 parts by weight or more, about 350 parts by weight or more, about 400 parts by weight or more, about 500 parts by weight or more, about 550 parts by weight or more, about 600 parts by weight or more, or about 650 parts by weight or more, relative to 100 parts by weight of the sum of the ester-based polyol resin and polyisocyanate contents. In one example, when the filler is used in the above range, it may be distributed in the same amount in the main composition part and the curing agent composition part.


As described above, when the thermally conductive filler is used in a high content, the viscosity of the main composition part or the curing agent composition part, containing the filler, or the composition comprising them may increase. As described above, when the viscosity of the resin composition is too high, the injection processability is poor, whereby the physical properties required for the resin layer may not be sufficiently realized throughout the resin layer. In view of this point, it is preferable to use a low-viscosity component which may be liquid or have sufficient flow as the resin component.


In one example, each of the ester-based polyol resin and polyisocyanate components may have a viscosity of 10,000 cP or less. Specifically, the resin component may have a viscosity of 8,000 cP or less, 6,000 cP or less, 4,000 cP or less, 2,000 cP or 1,000 CP or less. Preferably, the upper limit of the viscosity may be 900 cP or less, 800 cP or less, 700 cP or less, 600 cP or less, 500 cP or less, or 400 cP or less. Although not particularly limited, the lower limit of viscosity of each resin component may be 50 cP or more, or 100 cP or more. If the viscosity is too low, the processability may be good, but as the molecular weight of the raw material is low, the possibility of volatilization may increase, and heat resistance/cold resistance, flame retardance and adhesive force may be deteriorated, where such disadvantages can be prevented by satisfying the lower limit range. The viscosity can be measured at room temperature, for example, using a Brookfield LV type viscometer.


In addition to the above, various kinds of fillers can be used. For example, the use of a carbon (-based) filler such as graphite may be considered in order to secure insulation properties of the cured resin layer of the resin composition. Alternatively, a filler such as, for example, fumed silica, clay or calcium carbonate can be used. The form or content ratio of the filler is not particularly limited, which may be selected in consideration of the viscosity of the resin composition, the possibility of settling in the resin layer, the thixotropy, the insulating property, the filling effect or the dispersibility.


The composition may further comprise a viscosity controlling agent, such as a thixotropic agent, a diluent, a dispersant, a surface treatment agent or a coupling agent, for adjusting viscosity, if necessary, for example, for raising or lowering viscosity or for controlling viscosity depending on shear force.


The thixotropic agent controls the viscosity of the resin composition depending on the shear force, whereby the process of manufacturing the battery module can be effectively performed. As the usable thixotropic agent, fumed silica and the like can be exemplified.


The diluent or dispersant is usually used for lowering the viscosity of the resin composition, and any of various kinds known in the art can be used without limitation as long as it can exhibit the above action.


The surface treatment agent is for surface treatment of the filler introduced into the resin layer, and any of various kinds known in the art can be used without limitation as long as it can exhibit the above action.


The coupling agent may be used, for example, to improve the dispersibility of the thermally conductive filler such as alumina, and any of various kinds known in the art may be used without limitation as long as it can exhibit the above action.


In addition, the resin composition may further comprise a flame retardant or a flame retardant auxiliary agent. In this case, a known flame retardant may be used without any particular limitation, and for example, a flame retardant in the form of a solid phase or a liquid flame retardant may be applied. The flame retardant includes, for example, organic flame retardants such as melamine cyanurate and inorganic flame retardants such as magnesium hydroxide. When the amount of the filler filled in the resin layer is large, a liquid type flame retardant material (TEP, triethyl phosphate, or TCPP, tris(1,3-chloro-2-propyl)phosphate, etc.) may also be used. In addition, a silane coupling agent capable of acting as a flame retardant synergist may also be added.


The composition may comprise the above-described constitutions, and may be a solvent type composition, a water-based composition or a solventless type composition, but considering the convenience of the manufacturing process, which is described below, the solventless type may be suitable.


The composition of the present application may have physical properties suitable for the use as described below after curing. Among physical properties mentioned in this specification, when the measured temperature influences the physical properties, the physical properties may be physical properties measured at room temperature, unless otherwise specified. Furthermore, the expression “after curing” in connection with physical properties can be used in the same meaning as described above in relation to the glass transition temperature.


In one example, the resin composition may have predetermined adhesive force (S1) at room temperature after curing. Specifically, the resin layer may have adhesive force of about 150 gf/10 mm or more, 200 gf/10 mm or more, 250 gf/10 mm or more, 300 gf/10 mm or more, 350 gf/10 mm or more, or 400 gf/10 mm or more. When the adhesive force satisfies the above range, appropriate impact resistance and vibration resistance can be ensured. The upper limit of the resin layer adhesive force is not particularly limited, which may be about 1,000 gf/10 mm or less, 900 gf/10 mm or less, 800 gf/10 mm or less, 700 gf/10 mm or less, 600 gf/10 mm or less, or 500 gf/10 mm or less or so. When the adhesive force is too high, there is a risk that the pouch portion to which the cured composition is attached will tear. Specifically, in the case where a shock occurs in which the shape of the battery module is deformed due to an accident while driving the vehicle, when the battery cell is attached too strongly through the cured resin layer, dangerous materials inside the battery can be exposed or explode, while the pouch is torn. The adhesive force can be measured with respect to the aluminum pouch according to the method disclosed in the following examples.


In another example, the adhesive force of the resin composition after curing can be maintained at a considerable level even under high-temperature/high-humidity, as described in the following examples. Specifically, in the present application, the % ratio [(S2/S1)×100] of the adhesive force (S2) measured by the same method after a high-temperature/high-humidity acceleration test performed under predetermined conditions relative to the adhesive force (S1) measured at room temperature may be 70% or more, or 80% or more. In one example, the high-temperature/high-humidity acceleration test can be measured after storing the same specimen as the specimen used for measuring the room temperature adhesive force for 10 days under conditions of a temperature of 40 to 100° C. and humidity of 75% RH or more. When the adhesive force and the relationship are satisfied, excellent adhesion durability can be maintained even if the use environment of the battery module changes.


In one example, the resin composition can have excellent heat resistance after curing. In this regard, the composition of the present application may have a 5% weight loss temperature of 120° C. or higher at the time of a thermogravimetric analysis (TGA) measured for the cured product of only the resin components in a state of comprising no filler. In addition, the composition of the present application may have an 800° C. balance of 70 wt % or more at the time of a thermogravimetric analysis (TGA) measured for the cured product of the resin composition in a state of comprising the filler. In another example, the 800° C. balance may be about 75 wt % or more, about 80 wt % or more, about 85 wt % or more, or about 90 wt % or more. In another example, the 800° C. balance may be about 99 wt % or less. At this time, the thermogravimetric analysis (TGA) can be measured within a range of 25 to 800° C. at a temperature raising rate of 20° C./minute under a nitrogen (N2) atmosphere of 60 cm3/minute. The heat resistance characteristics related to the thermogravimetric analysis (TGA) can be secured by controlling the kind of the resin and/or the filler or the content thereof.


In one example, the resin composition may have excellent electrical insulation after curing. In the battery module structure as described below, when the resin layer exhibits predetermined electrical insulation, the performance of the battery module can be maintained and stability can be ensured. For example, the cured product of the resin composition may have a dielectric breakdown voltage of about 10 kV/mm or more, 15 kV/mm or more, or 20 kV/mm or more, as measured according to ASTM D149. The higher the value of the dielectric breakdown voltage is, the resin layer shows more excellent insulation, and thus it is not particularly limited, but may be about 50 kV/mm or less, 45 kV/mm or less, 40 kV/mm or less, 35 kV/mm or less, or 30 kV/mm or less in consideration of composition of the resin layer or the like. The dielectric breakdown voltage in the above range can be secured, for example, by adjusting the contents of the filler and the resin component described above.


In another example of the present application, the present application relates to a battery module. The module comprises a module case and a battery cell. The battery cell may be housed in the module case. One or more battery cells may be present in the module case, and a plurality of battery cells may be housed in the module case. The number of battery cells housed in the module case is adjusted depending on applications and the like, which is not particularly limited. The battery cells housed in the module case may be electrically connected to each other.


The module case may comprise at least sidewalls and a bottom plate which form an internal space in which the battery cell can be housed. Also, the module case may further comprise a top plate for sealing the internal space. The sidewalls, the bottom plate, and the top plate are integrally formed with each other, or the sidewalls, the bottom plate, and/or the top plate as separated from each other are assembled, so that the module case can be formed. The shape and size of such a module case are not particularly limited and may be appropriately selected depending on applications, or the type and number of the battery cell housed in the internal space, and the like.


Here, since there are at least two plates constituting the module case, the term top plate and bottom plate are terms having relative concepts used to distinguish them. That is, it does not mean that in the actual use state, the top plate necessarily exists at the upper portion and the bottom plate necessarily exists at the lower portion.



FIG. 2 is a view showing an exemplary module case (10), which is an example of a box-shaped case (10) comprising one bottom plate (10a) and four sidewalls (10b). The module case (10) may further comprise a top plate (10c) sealing the internal space.



FIG. 3 is a schematic view of the module case (10) of FIG. 2, as observed from above, in which the battery cells (20) are housed.


A hole may be formed in the bottom plate, the sidewalls, and/or the top plate of the module case. When a resin layer is formed by an injection process, the hole may be an injection hole used for injecting a material for forming the resin layer, that is, the resin composition, as described below. The shape, number and position of the hole can be adjusted in consideration of the injection efficiency of the material for forming the resin layer. In one example, the hole may be formed at least on the bottom plate and/or the top plate.


In one example, the hole may be formed at about ¼ to ¾ point or about ⅜ to ⅞ point, or approximately the middle, of the total length of the sidewalls, the bottom plate, or the top plate. By injecting the resin composition through the injection hole formed at this point, the resin layer can be injected so as to have a wide contact area. As shown in FIG. 4, the ¼, ¾, ⅜ or ⅞ point is, for example, a ratio of the distance (A) to the hole forming position relative to the total length (L) measured based on any one end face (E) of the bottom plate or the like. The end (E) at which the length (L) and the distance (A) are formed may be any end (E) as long as the length (L) and the distance (A) are measured from the same end (E). In FIG. 4, the injection hole (50a) is in a form of being located at the approximately middle part of the bottom plate (10a).


The size and shape of the injection hole are not particularly limited, and can be adjusted in consideration of the injection efficiency of a resin layer material to be described below. For example, the hole may have a circular shape, an elliptical shape, a polygonal shape such as triangle or square, or an amorphous shape. The number and spacing of the injection hole are not particularly limited and can be adjusted so that the resin layer can have a wide contact area with the bottom plate or the like, as described above.


An observation hole (for example, 50b in FIG. 4) may be formed at the end of the top plate and the bottom plate, and the like where the injection hole is formed. For example, when the material of the resin layer is injected through the injection hole, such an observation hole may be formed for observing whether the injected material is injected well to the end of the sidewalls, the bottom plate, or the top plate. The position, shape, size, and number of the observation hole are not particularly limited as long as they are formed so that it can be confirmed whether the injected material is properly injected.


The module case may be a thermally conductive case. The term thermally conductive case means a case in which the thermal conductivity of the entire case is 10 W/mk or more, or at least a portion having the thermal conductivity as above is included. For example, at least one of the sidewalls, the bottom plate and the top plate as described above may have the thermal conductivity described above. In another example, at least one of the sidewalls, the bottom plate, and the top plate may comprise a portion having the thermal conductivity. For example, as described below, the battery module of the present application may comprise a first filler-containing cured resin layer in contact with the top plate and the battery cell, and a second filler-containing cured resin layer in contact with the bottom plate and the battery cell, where at least the second filler-containing cured resin layer may be a thermally conductive resin layer, whereby it can be said that at least the bottom plate may have thermal conductivity or may comprise a thermally conductive portion.


Here, the thermal conductivity of the thermally conductive top plate, bottom plate, sidewall or the thermally conductive portion may be 20 W/mk or more, 30 W/mk or more, 40 W/mk or more, 50 W/mk or more, 60 W/mk or more, 70 W/mk or more, 80 W/mk or more, 90 W/mk or more, 100 W/mk or more, 110 W/mk or more, 120 W/mk or more, 130 W/mk or more, 140 W/mk or more, 150 W/mk or more, 160 W/mk or more, 170 W/mk or more, 180 W/mk or more, 190 W/mk or more, or about 195 W/mk or more. The higher the value of the thermal conductivity is, the more advantageous it is from the viewpoint of the heat dissipation property of the module, and the like, and the upper limit is not particularly limited. In one example, the thermal conductivity may be about 1,000 W/mk or less, 900 W/mk or less, 800 W/mk or less, 700 W/mk or less, 600 W/mk or less, 500 W/mk or less, 400 W/mk or less, 300 W/mk or less, or 250 W/mk or less, but is not limited thereto. The kind of materials exhibiting the thermal conductivity as above is not particularly limited, and for example, includes metal materials such as aluminum, gold, pure silver, tungsten, copper, nickel, or platinum. The module case may be comprised entirely of the thermally conductive material as above, or at least a part of the module case may be a portion comprised of the thermally conductive material. Accordingly, the module case may have the above-mentioned range of thermal conductivity, or comprise at least one portion having the aforementioned thermal conductivity.


In the module case, the portion having a thermal conductivity in the above range may be a portion in contact with the resin layer and/or the insulating layer as described below. In addition, the portion having the thermal conductivity may be a portion in contact with a cooling medium such as cooling water. When it has such a structure, heat generated from the battery cell can be effectively discharged to the outside.


Also, the type of the battery cell housed in the module case is not particularly limited, and a variety of known battery cells may be applied. In one example, the battery cell may be a pouch type. Referring to FIG. 5, the pouch type battery cell (100) may typically comprise an electrode assembly, an electrolyte, and a pouch exterior material.



FIG. 5 is an exploded perspective view schematically showing the configuration of an exemplary pouch type cell, and FIG. 6 is a combined perspective view of the configuration of FIG. 5.


The electrode assembly (110) included in the pouch type cell (100) may be in a form in which at least one positive plate and at least one negative plate are disposed with each separator interposed therebetween. The electrode assembly (110) may be a wound type in which one positive plate and one negative plate are wound together with the separator, or a stacked type in which a plurality of positive plates and a plurality of negative plates are laminated alternately with each separator interposed therebetween.


The pouch exterior material (120) may be configured in a form equipped with, for example, an outer insulating layer, a metal layer, and an inner adhesive layer. Such an exterior material (120) protects inner elements such as the electrode assembly (110) and the electrolyte, to complement the electrochemical properties by the electrode assembly (110) and the electrolyte, and to consider heat dissipation or the like. Such a metal thin film may be interposed between insulating layers formed of an insulating material in order to ensure electrical insulation with elements such as the electrode assembly (110) and the electrolyte, or other elements outside the battery (100). In addition, the pouch may further comprise, for example, a polymer resin layer (base material) such as PET.


In one example, the exterior material (120) may comprise an upper pouch (121) and a lower pouch (122), where in at least one of the upper pouch (121) and the lower pouch (122), a concave internal space (I) can be formed. The electrode assembly (110) can be housed in the internal space (I) of this pouch. A sealing portion (S) is provided on each outer peripheral surface of the upper pouch (121) and the lower pouch (122) and these sealing portions (S) are bonded to each other so that the internal space accommodating the electrode assembly (110) can be sealed.


Each electrode plate of the electrode assembly (110) is provided with an electrode tab, and one or more electrode tabs may be connected to an electrode lead. The electrode lead may be interposed between the sealing portions (S) of the upper pouch (121) and the lower pouch (122) and exposed to the outside of the exterior material (120) to function as an electrode terminal of the secondary battery (100).


The shape of the pouch type cell as described above is only one example, and the battery cell applied in the present application is not limited to the above-described kind. In the present application, various shapes of known pouch type cells or other types of cells can be all applied as battery cells.


The battery module of the present application may further comprise a resin layer. Specifically, the battery module of the present application may comprise a cured resin layer in which the filler-containing composition is cured. The cured resin layer may be formed from the urethane-based composition as described above.


The battery module may comprise, as the resin layer, a first filler-containing cured resin layer in contact with the top plate and the battery cell, and a second filler-containing cured resin layer in contact with the bottom plate and the battery cell. One or more of the first and second filler-containing cured resin layers may comprise a cured product of the urethane-based composition as described above, thereby having the predetermined adhesive force, cold resistance, heat resistance, and insulation as described above. In addition, the first and second filler-containing cured resin layers may have the following characteristics.


In one example, the resin layer may be a thermally conductive resin layer. In this case, the thermal conductivity of the thermally conductive resin layer may be about 1.5 W/mK or more, about 2 W/mK or more, 2.5 W/mK or more, 3 W/mK or more, 3.5 W/mK or more, or 4 W/mK or more. The thermal conductivity may be 50 W/mK or less, 45 W/mK or less, 40 W/mK or less, 35 W/mK or less, 30 W/mK or less, 25 W/mK or less, 20 W/mK or less, 15 W/mK or less, 10 W/mK or less, 5 W/mK or less, 4.5 W/mK or less, or about 4.0 W/mK or less. When the resin layer is a thermally conductive resin layer as above, the bottom plate, the top plate and/or the sidewall, and the like to which the resin layer is attached may be a portion having the above-described thermal conductivity of 10 W/mK or more. At this time, the module case portion representing the thermal conductivity may be a part in contact with a cooling medium, for example, cooling water or the like. The thermal conductivity of the resin layer is measured using known hot disk equipment, which is, for example, a value measured according to ASTM D5470 standard or ISO 22007-2 standard. The thermal conductivity of such a resin layer may be secured, for example, by appropriately adjusting the filler contained in the resin layer and the content thereof, as described above.


In one example, in the battery module, the resin layer or the battery module, to which the resin layer is applied, may have a thermal resistance of 5 K/W or less, 4.5 K/W or less, 4 K/W or less, 3.5 K/W or less, 3 K/W or less, or about 2.8 K/W. When the resin layer or the battery module, to which the resin layer is applied, is adjusted in order to exhibit the thermal resistance in the above range, excellent cooling efficiency or heat dissipation efficiency can be secured. The measurement of the thermal resistance can be performed by attaching a temperature sensor according to the cell position on the module while driving the battery module and calculating it based on the temperature measured from the sensor. The method of measuring the thermal resistance is not particularly limited, and for example, the thermal resistance can be measured according to ASTM D5470 standard or ISO 22007-2 standard.


In one example, the resin layer may be a resin layer formed to maintain durability even in a predetermined thermal shock test. The thermal shock test may be performed in a manner known in the art. For example, when one cycle is composed of holding the battery module at a low temperature of −40° C. for 30 minutes, and then again holding it for 30 minutes after increasing the temperature to 80° C., it may be a resin layer that cannot be peeled off or cracked from the module case or the battery cell of the battery module after the thermal shock test that the cycle is repeated 100 times. For example, when the battery module is applied to a product, such as an automobile, requiring a long guarantee period (for example, about 15 years or more in the case of the automobile), performance may be required in the same level as above for ensuring durability.


In one example, the resin layer may be a flame retardant resin layer. In the present application, the term flame retardant resin layer may mean a resin layer showing a V-0 rating in UL 94 V Test (vertical burning test). This can secure stability against fires and other accidents that may occur in the battery module.


In one example, the resin layer may have a specific gravity of 5 or less. In another example, the specific gravity may be 4.5 or less, 4 or less, 3.5 or less, or 3 or less. The resin layer showing the specific gravity in this range is advantageous for manufacturing a lightweight battery module. The lower the value of the specific gravity is, the more advantageous the lightening of the module is, and thus the lower limit is not particularly limited. For example, the specific gravity can be about 1.5 or more, or 2 or more. The components added to the resin layer can be adjusted so that the resin layer exhibits the specific gravity in the above range. For example, when the fillers are added, a method of applying fillers capable of securing a desired thermal conductivity even at a low specific gravity, if possible, that is, fillers having a low specific gravity or surface-treated fillers, and the like may be used.


In one example, it is preferable that the resin layer does not contain volatile substances, if possible. For example, the resin layer may have a ratio of non-volatile components of 90 wt % or more, 95 wt % or more, or 98 wt % or more. Here, the non-volatile components and the ratio thereof can be specified in the following manner. That is, the non-volatile component can be defined as the remaining portion after the resin layer is maintained at 100° C. for about 1 hour. Thus, the ratio of the non-volatile component can be measured based on the initial weight of the resin layer and the ratio after the resin layer is maintained at 100° C. for about 1 hour.


In one example, it may be advantageous that the resin layer has a low shrinkage ratio during the process of curing or after curing. This can prevent the occurrence of peeling or voids that may occur during the manufacture or use process of the module. The shrinkage ratio can be appropriately adjusted within a range capable of exhibiting the above-mentioned effect, and can be, for example, less than 5%, less than 3% or less than about 1%. The lower the value of the shrinkage ratio is, the more advantageous the shrinkage ratio is, and thus the lower limit is not particularly limited.


In one example, the resin layer may have a low coefficient of thermal expansion (CTE) to prevent the occurrence of peeling or voids, and the like that may occur during the manufacture or use process of the module. The coefficient of thermal expansion can be, for example, less than 300 ppm/K, less than 250 ppm/K, less than 200 ppm/K, less than 150 ppm/K or less than about 100 ppm/K. The lower the value of the coefficient of thermal expansion is, the more advantageous the coefficient is, and thus the lower limit is not particularly limited. The method of measuring the coefficient of thermal expansion is not particularly limited. For example, it is measured using a TMA (thermo mechanical analyzer) under an expansion mode and a 0.05 N load in a range of −40 to 125° C. at a condition of 5° C./min, where the coefficient of thermal expansion can be measured in a manner that confirms the length change rate within the designated temperature section based on the modified length.


In one example, in order to impart good durability or impact resistance to the battery module, the resin layer may have an appropriate level of tensile strength. For example, the resin layer may be configured to have a young's modulus of about 1.0 MPa or more. The young's modulus may be, for example, a slope value when is measured in the tensile mode at a low temperature (about −40° C.), room temperature (about 25° C.) and a high temperature (about 80° C.) for each point within the range of −40 to 80° C. The higher the temperature, the lower the young's modulus is measured. For example, the resin layer of the present application may have a young's modulus of 1.0 Mpa or more, more specifically, in the range of 10 to 500 Mpa. When the young's modulus is less than the above range, the function of fixing a large weight cell is not good, and when it is too large, brittle characteristics are strong, so that cracks may occur in an impact situation such as a vehicle collision.


In one example, it may be advantageous that the resin layer exhibits an appropriate hardness. For example, if the hardness of the resin layer is too high, the reliability may be adversely affected because the resin layer has a brittle characteristic. When this point is considered, by controlling the hardness of the resin layer, the impact resistance and the vibration resistance can be secured, and the durability of the product can be ensured. The resin layer may have, for example, a hardness in Shore A type of less than 100, 99 or less, 98 or less, 95 or less, or 93 or less, or a hardness in Shore D type of less than about 80, about 70 or less, about 65 or less, or about 60 or less. The lower limit of the hardness is not particularly limited. For example, the hardness in Shore A type may be 60 or more, or the hardness in Shore 00 type may be 5 or more, or about 10 or more or so. The hardness in the above range can be ensured by controlling the content of the filler and the like. The Shore hardness can be measured according to a known method using a hardness meter for each type, such as, for example, a shore A hardness meter. A known method is ASTM D2240 or the like.


By forming the cured resin layer satisfying the characteristics in the battery module as described above, a battery module having excellent durability against external impact or vibration can be provided.


In the battery module of the present application, at least one of the sidewall, the bottom plate and the top plate in contact with the resin layer may be the above-described thermally conductive sidewall, bottom plate or top plate. On the other hand, in this specification, the term contact may also mean a case where, for example, the top plate, the bottom plate and/or the sidewall or the battery cell is in direct contact with the resin layer, or another element, for example, an insulating layer or the like exists therebetween. In addition, the resin layer in contact with the thermally conductive sidewall, bottom plate or top plate may be in thermal contact with the target. At this time, the thermal contact may mean a state that the resin layer is in direct contact with the bottom plate or the like, or other elements, for example, an insulating layer or the like as described below, between the resin layer and the bottom plate or the like are present, but the other element does not interfere with heat transfer from the battery cell to the resin layer, and from the resin layer to the bottom plate or the like. Here, the phrase “does not interfere with heat transfer” means the case that even when other elements (e.g., an insulating layer or a guiding portion as described below) exists between the resin layer and the bottom plate or the like, the total thermal conductivity of the other elements and the resin layer is about 1.5 W/mK or more, about 2 W/mK or more, 2.5 W/mK or more, 3 W/mK or more, 3.5 W/mK or more, or 4 W/mk or more, or the total thermal conductivity of the resin layer and the bottom plate or the like in contact therewith is included in the range even when the other elements are present. The thermal conductivity of the thermal contact may be 50 W/mk or less, 45 W/mk or less, 40 W/mk or less, 35 W/mk or less, 30 W/mk or less, 25 W/mk or less, 20 W/mk or less, 15 W/mk or less, 10 W/mk or less, 5 W/mk or less, 4.5 W/mk or less, or about 4.0 W/mk or less. This thermal contact can be achieved by controlling the thermal conductivity and/or the thickness of the other element when the other element is present.


The thermally conductive resin layer may be in thermal contact with the bottom plate or the like and may also be in thermal contact with the battery cell. By adopting such a structure, various fastening parts or cooling equipment of the module, and the like, which was previously required in the construction of a general battery module or a battery pack as an assembly of such modules, is greatly reduced, and simultaneously it is possible to implement a module in which heat dissipation characteristics are ensured and more battery cells are housed per unit volume. Accordingly, the present application can provide a battery module having high power while being more compact and lighter.



FIG. 7 is an exemplary cross-sectional diagram of the battery module. In FIG. 6, the module may be in a form which comprises a case (10) including sidewalls (10b) and a bottom plate (10a); a plurality of battery cells (20) housed inside the case and a resin layer (30) in contact with both the battery cell (20) and the case (10). FIG. 7 is a diagram of the resin layer (30) existing on the side of the bottom plate (10a), but the battery module of the present application may also comprise a resin layer located on the side of the top plate in the same form as FIG. 7.


In the above structure, the bottom plate or the like in contact with the resin layer (30) may be the thermally conductive bottom plate or the like as described above.


The contact area between the resin layer and the bottom plate or the like may be about 70% or more, about 75% or more, about 80% or more, about 85% or more, about 90% or more, or about 95% or more, relative to the total area of the bottom plate or the like. The upper limit of the contact area is not particularly limited, and may be, for example, 100% or less, or less than about 100%.


When the top plate or the bottom plate is thermally conductive and the cured resin layer in contact therewith is also thermally conductive, the thermally conductive portion or the thermally conductive bottom plate or the like may be a portion in contact with a cooling medium such as cooling water. That is, as schematically shown in FIG. 7, the heat (H) can be easily discharged to the bottom plate or the like by the above structure, and heat release can be easily performed even in more simplified structures by contacting this bottom plate or the like with the cooling medium (CW).


The first and second cured resin layers may each have a thickness in a range of, for example, about 100 μm to 5 mm or in a range of about 200 μm to 5 mm. In the structure of the present application, the thickness of the resin layer may be set to an appropriate thickness in consideration of the desired heat dissipation characteristics or durability. The thickness may be the thickness of the thinnest portion of the resin layer, the thickness of the thickest portion, or the average thickness.


As shown in FIG. 7, a guiding portion (10d) which can guide the housed battery cell (20) may also be present on at least one surface of the inside of the module case (10), for example, a surface (10a) in contact with the resin layer (30). At this time, the shape of the guiding portion (10d) is not particularly limited, and an appropriate shape can be employed in consideration of the shape of the battery cell to be applied. The guiding portion (10d) may be integrally formed with the bottom plate or the like, or may be attached separately thereto. The guiding portion (10d) may be formed using a thermally conductive material, for example, a metallic material such as aluminum, gold, pure silver, tungsten, copper, nickel, or platinum in consideration of the above-described thermal contact. In addition, although not shown in the drawings, an interleaf or an adhesive layer may also be present between the housed battery cells (20). Here, the interleaf can act as a buffer upon charging and discharging the battery cell.


In one example, the battery module may further comprise an insulating layer between the module case and the battery cell or between the resin layer and the module case. FIG. 8 illustratively shows a case where the insulating layer (40) is formed between the guiding portion (10d) formed on the bottom plate (10a) of the case and the resin layer (30). By adding an insulating layer, it is possible to prevent problems such as an electrical short phenomenon or a fire due to a contact between the cell and the case by an impact that may occur during use. The insulating layer may be formed using an insulating sheet having high insulation and thermal conductivity, or may be formed by applying or injecting a material exhibiting insulating properties. For example, in a method for manufacturing a battery module as described below, a process of forming an insulating layer may be performed before the injection of the resin composition. A so-called TIM (thermal interface material) or the like may be applied in forming the insulating layer. Alternatively, the insulating layer may be formed of an adhesive material, and for example, the insulating layer may also be formed using a resin layer having little or no filler such as thermally conductive fillers. As the resin component which can be used for forming the insulating layer, an acrylic resin, PVC (poly(vinyl chloride)), an olefin resin such as PE (polyethylene), an epoxy resin, silicone or a rubber component such as an EPDM (ethylene propylene diene monomer) rubber, and the like can be exemplified, without being limited thereto. The insulating layer may have an insulation breakdown voltage, as measured according to ASTM D149, of about 5 kV/mm or more, about 10 kV/mm or more, about 15 kV/mm or more, 20 kV/mm or more, 25 kV/mm or more, or 30 kV/mm or more. The higher the value of the dielectric breakdown voltage is, the better the insulation shows, and thus it is not particularly limited. For example, the dielectric breakdown voltage of the insulating layer may be about 100 kV/mm or less, 90 kV/mm or less, 80 kV/mm or less, 70 kV/mm or less, or 60 kV/mm or less. The thickness of the insulating layer can be set to an appropriate range in consideration of the insulating property and the thermal conductivity of the insulating layer, and the like, and for example, may be about 5 μm or more, 10 μm or more, 20 μm or more, 30 μm or more, 40 μm or more, 50 μm or more, 60 μm or more, 70 μm or more, 80 μm or more, or 90 μm or more or so. In addition, the upper limit of the thickness is not particularly limited and may be, for example, about 1 mm or less, about 200 μm or less, 190 μm or less, 180 μm or less, 170 μm or less, 160 μm or less, or 150 μm or less.


In another example of the present application, the present application relates to a method for manufacturing a battery module, for example, the above-mentioned battery module.


The manufacturing method of the present application may comprise steps of injecting a resin composition into the above-described module case; housing a battery cell in the module case, and curing the resin composition to form the resin layer.


The order of the step of injecting the resin composition into the module case and the step of housing the battery cell in the module case is not particularly limited. For example, the resin composition may be first injected into the module case, followed by housing the battery cell in that state, or the battery cell may be first housed inside the module case, followed by injecting the resin composition therein.


As the resin composition, the above-mentioned resin composition can be used.


The method of injecting the resin composition into the module case is not particularly limited, and a known method can be applied. For example, a resin composition may be injected by pouring the resin composition into an opening of a module case, or a method of injecting a resin composition by the above-described injection hole formed on a module case, a method of applying a resin composition to both a battery cell and a battery module, and the like may be applied. For proper fixing, the injection process may also be performed while constantly vibrating the battery module or the battery cell.


The manner, in which the battery cell is housed in the module case into which the resin composition is injected or in the module case before the composition is injected, is not particularly limited.


The housing of the battery cells can be performed by arranging the battery cells at suitable positions in the module case in consideration of the desired arrangement and the like. In addition, when the cartridge structure is present, the step can be performed by placing the battery cells at proper positions of the cartridge structure, or inserting the cartridge structure, in which the battery cells are located, into the module case.


After the battery cells are housed therein, adhesion between the battery cells or adhesion between the battery cells and the module case can be achieved by curing the injected resin composition. The manner of curing the resin composition is not particularly limited. In one example, when the composition is used, the resin composition can be cured by a method of holding the resin composition at room temperature for a predetermined time. The curing may also be accelerated by applying heat for a certain period of time at such a level as not to impair the thermal stability of the cell. For example, by applying heat at a temperature of less than 60° C., more specifically, in a range of about 30° C. to 50° C., before curing or during the curing process, or before housing the battery cell or during the housing process, the takt time can be reduced and the processability can be improved. The cured product capable of achieving adhesion between battery cells or achieving adhesion between the battery cell and the module case may have a conversion rate of at least 80% or more, as described above.


In another example of the present application, the present application relates to a battery pack, for example, a battery pack comprising two or more battery modules as described above. In the battery pack, the battery modules may be electrically connected to each other. A method of electrically connecting two or more battery modules to constitute a battery pack is not particularly limited, and all known methods can be applied thereto.


The present application also relates to a device comprising the battery module or the battery pack. An example of such a device may include, but is not limited to, automobiles such as electric vehicles, and may be devices for all applications requiring secondary batteries as power. In addition, a method of constructing the automobile using the battery module or the battery pack is not particularly limited, and a general method known in the related art can be applied.


Advantageous Effects

The present application has the effect of the invention which provides a composition capable of effectively securing battery cells in a module case and improving heat dissipation and manufacturing processability of a battery module. In addition, according to the present application, there are provided a battery module and a battery pack each having a resin layer with excellent cold resistance, heat resistance, insulation and adhesion reliability. Accordingly, it is possible to provide a battery module and a battery pack which have improved heat dissipation properties and durability as well as excellent power to volume.





BRIEF DESCRIPTION OF DRAWINGS


FIG. 1 shows an example of determining an amorphous characteristic or a sufficiently low crystallizability of an ester-based polyol according to one example of the present application.



FIG. 2 shows an exemplary module case, which can be applied in the present application.



FIG. 3 schematically shows a form in which battery cells are housed in a module case.



FIG. 4 schematically shows an exemplary bottom plate where injection holes and observation holes are formed.



FIGS. 5 and 6 schematically show an exemplary battery pouch which can be used as a battery cell.



FIGS. 7 and 8 schematically show the structure of an exemplary battery module.





The respective reference numerals and symbols described in connection with the drawings are as follows.

    • 10: module case
    • 10a: bottom plate
    • 10b: sidewall
    • 10c: top plate
    • 10d: guiding portion
    • 20: battery cell
    • 30: resin layer
    • 50a: injection hole
    • 50b: observation hole
    • 40: insulating layer
    • 100: pouch type cell
    • 110: electrode assembly
    • 120: exterior material
    • 121: upper pouch
    • 122: lower pouch
    • S: sealing portion


BEST MODE

Hereinafter, the battery module of the present application will be described with reference to Examples and Comparative Examples. However, the scope of the present application is not limited by the scope given below.


Evaluation Methods


1. Amorphous Characteristic Based on Tm (Melting Point)


The Tm for the polyol resin used in Examples and Comparative Examples was measured through a DSC analysis using Q2000 (TA instruments), while changing the temperature in the order of 25° C.->50° C.->−70° C.->50° C. at a temperature elevation rate of 10° C./min.


2. Adhesive Force (S1) (Unit: Gf/10 mm)


The aluminum pouch used to manufacture the battery cell was cut to a width of about 10 mm. The resin composition each used in Examples and Comparative Examples was loaded on a glass plate, and the cut aluminum pouch was loaded thereon so that the resin composition was in contact with the PET (poly(ethylene terephthalate)) side of the pouch and then the resin composition was cured under the conditions of 25° C. and 50% RH for 24 hours. Subsequently, while the aluminum pouch was peeled off at a peeling angle of 180° and a peeling speed of 300 mm/min with a tensile tester (texture analyzer), the adhesive force was measured.


3. Adhesion Reliability


A specimen of the cured resin composition was produced in the same manner as in the above adhesive force measurement and stored under conditions of 85° C. and 85% RH for 10 days. Thereafter, the adhesive force (S2) was measured in the same manner as in Item 2 above.


4. Tg (Glass Transition Temperature)


The mixture of the same resins (without any filler) as used in Examples and Comparative Examples was cured at room temperature for 24 hours, and the Tg of the cured product was measured by a DSC analysis, while changing the temperature from −75° C. to 50° C. at a temperature elevation rate of 10° C./min.


EXAMPLES AND COMPARATIVE EXAMPLES
Example 1

Preparation of Two-Component Urethane-Based Composition


Polyol: A resin (having a viscosity of about 280 cP as measured with a Brookfield LV type viscometer) comprising, as the caprolactone-based polyol represented by Formula 2 above, a polyol having a number of repeating units (m in Formula 2) of about 1 to 3 or so and containing 1,4-butanediol as the polyol-derived unit (Y in Formula 2) was used in a predetermined amount in the main composition.


Isocyanate: A mixture (having a viscosity of 170 cP as measured with a Brookfield LV type viscometer) of HDI (hexamethylene diisocyanate) and a HDI trimer was used in the curing agent composition. At this time, the used amount of the isocyanate compound was adjusted so that the NCO index was about 100.


Filler: Alumina was used. The content thereof was adjusted in a ratio of 1,000 parts by weight relative to 100 parts by weight of the sum of the polyol and isocyanate contents, and the alumina was divided and formulated in the same amount into the main composition part and the curing agent composition part.


Catalyst: Dibutyltin dilaurate (DBTDL) was used in a predetermined amount.


Physical Property Measurement Results


The glass transition temperature (Tg) of the prepared composition measured in the above-mentioned manner was less than 0° C. Then, the melting point (Tm) measured in the above-mentioned manner was 11° C. Also, the adhesive force (S1) was 449 gf/10 mm, and the ratio (S2/S1) between the adhesive force was 70% or more. From this, it can be seen that the composition of Example 1 can provide proper processability at the time of injection into the battery module even when containing an excessive amount of filler, and has excellent adhesion and adhesion reliability after curing.


Example 2

Preparation of Two-Component Urethane-Based Composition


A composition was prepared as in Example 1, except that neopentyl glycol was changed and used at the time of forming the Y unit of the polyol formula 2 (the viscosity of the prepared polyol was about 300 cP when measured with a Brookfield LV type viscometer).


Physical Property Measurement Results


The glass transition temperature (Tg) of the prepared composition measured in the above-mentioned manner was less than 0° C. and the used polyol had weak crystallizability, so that the crystallization temperature (Tc) and the melting temperature (Tm) were not measured on the DSC. Also, the adhesive force (S1) was 467 gf/10 mm, and the ratio (S2/S1) between the adhesive force was 70% or more. From this, it can be seen that the composition of Example 2 can provide proper processability at the time of injection into the battery module even when containing an excessive amount of filler, and has excellent adhesion and adhesion reliability after curing.


Comparative Example 1

Preparation of Two-Component Urethane-Based Composition


A composition was prepared in the same manner as in Example 1, except that PPG (hydroxyl group: 360 mg KOH/g) of an ether-based polyol was used as the resin used in the main composition part.


Physical Property Measurement Results


The glass transition temperature (Tg) of the prepared composition measured in the above-mentioned manner was less than 0° C. and the melting point was observed to be less than 15° C. Then, the adhesive force (S1) was 116 gf/10 mm, and the ratio (S2/S1) between the adhesive force was 70% or more. From this, it can be seen that the composition of Comparative Example 1, which does not have the ester-based polyol in the constitutions of the present application, cannot provide sufficient adhesive force necessary for bonding the battery cell to the case in the battery module.


Comparative Example 2

Preparation of Two-Component Urethane-Based Composition


A composition was prepared in the same manner as in Example 1, except that methylene diphenyl diisocyanate (MDI) of the aromatic diisocyanate was used in the curing agent composition part.


Physical Property Measurement Results


The glass transition temperature (Tg) of the prepared composition measured in the above-mentioned manner exceeded 0° C. and the melting point (Tm) was 15° C. or lower. Also, the adhesive force (S1) was 666 gf/10 mm, and the ratio (S2/S1) between the adhesive force was 70% or more. From this, it can be seen that the composition of Comparative Example 2 using an aromatic isocyanate as a curing component has poor injection processability and poor storage stability due to a high curing rate, and since the cured product has a high glass transition temperature, it is not suitable as a material for a battery module which requires impact resistance or vibration resistance, and the like.


Comparative Example 3

Preparation of Two-Component Urethane-Based Composition


A composition was prepared in the same manner as in Example 1, except that the repeating unit m of Formula 2 was 11 in the main composition part.


Physical Property Measurement Results


The glass transition temperature (Tg) of the prepared composition measured in the above-mentioned manner was 0° C. or lower and the melting point (Tm) exceeded 20° C. Also, the adhesive force (S1) was 467 gf/10 mm, and the ratio (S2/S1) between the adhesive force was 70% or more. From this, it can be concluded that the composition of Comparative Example 4 using a polyol having no sufficiently low crystallizability, which is required in the present application, has poor injection processability for a composition used as an adhesive in a battery module due to crystallizability at room temperature.

Claims
  • 1. A urethane-based composition comprising a main composition part comprising an ester-based polyol resin; a curing agent composition part comprising a polyisocyanate; and a filler, wherein the ester-based polyol resin is an amorphous polyol, in which a crystallization temperature (Tc) and a melting temperature (Tm) are not observed in a DSC (differential scanning calorimetry) analysis, or has a melting temperature (Tm) of less than 15° C.
  • 2. The urethane-based composition according to claim 1, wherein a mixture of the ester-based polyol resin and polyisocyanate has a glass transition temperature (Tg) of less than 0° C. after curing.
  • 3. The urethane-based composition according to claim 1, wherein each of the ester-based polyol resin and the polyisocyanate has a viscosity of less than 10,000 cP.
  • 4. The urethane-based composition according to claim 2, wherein each of the ester-based polyol resin and the polyisocyanate has a viscosity of 2,000 cP or less.
  • 5. The urethane-based composition according to claim 1, wherein the ester-based polyol resin is represented by the following formula 1 or 2:
  • 6. The urethane-based composition according to claim 5, wherein the carboxylic acid-derived unit X is one or more units selected from the group consisting of a phthalic acid unit, an isophthalic acid unit, a terephthalic acid unit, a trimellitic acid unit, a tetrahydrophthalic acid unit, a hexahydrophthalic acid unit, a tetrachlorophthalic acid unit, an oxalic acid unit, an adipic acid unit, an azelaic acid unit, a sebacic acid unit, a succinic acid unit, a malic acid unit, a glutaric acid unit, a malonic acid unit, a pimelic acid unit, a suberic acid unit, a 2,2-dimethylsuccinic acid unit, a 3,3-dimethylglutaric acid unit, a 2,2-dimethylglutaric acid unit, a maleic acid unit, a fumaric acid unit, an itaconic acid unit and a fatty acid unit.
  • 7. The urethane-based composition according to claim 5, wherein the polyol-derived unit Y is any one or two or more units selected from the group consisting of an ethylene glycol unit, a propylene glycol unit, a 1,2-butylene glycol unit, a 2,3-butylene glycol unit, a 1,3-propanediol unit, a 1,3-butanediol unit, a 1,4-butanediol unit, a 1,6-hexanediol unit, a neopentyl glycol unit, a 1,2-ethylhexyldiol unit, a 1,5-pentanediol unit, a 1,9-nonanediol unit, a 1,10-decanediol unit, a 1,3-cyclohexanedimethanol unit, a 1,4-cyclohexanedimethanol unit, a glycerin unit and a trimethylolpropane unit.
  • 8. The urethane-based composition according to claim 1, wherein the polyisocyanate is a non-aromatic polyisocyanate.
  • 9. The urethane-based composition according to claim 8, wherein the non-aromatic polyisocyanate is an alicyclic polyisocyanate, a carbodiimide-modified alicyclic polyisocyanate, or an isocyanurate-modified alicyclic polyisocyanate.
  • 10. The urethane-based composition according to claim 1, wherein the filler comprises alumina, AlN (aluminum nitride), BN (boron nitride), silicon nitride, SiC, or BeO.
  • 11. The urethane-based composition according to claim 1, wherein the filler is contained in an amount of 50 to 2,000 parts by weight relative to 100 parts by weight of the sum of the ester-based polyol resin and polyisocyanate contents.
  • 12. The urethane-based composition according to claim 10, wherein the filler is contained in an amount of 100 to 2,000 parts by weight relative to 100 parts by weight of the sum of the ester-based polyol resin and polyisocyanate contents.
  • 13. The urethane-based composition according to claim 1, which has adhesive force (S1) measured at room temperature after curing of 150 gf/10 mm or more.
  • 14. The urethane-based composition according to claim 13, which has a ratio of the adhesive force (S2) measured after curing and storage under the conditions of 40 to 100° C. and 75% relative humidity for 10 days to the adhesive force (S1) of 70% or more.
  • 15. A battery module comprising a module case having a top plate, a bottom plate and sidewalls, wherein an inner space is formed by the top plate, the bottom plate, and the sidewalls; a plurality of battery cells existing in the inner space of the module case; anda resin layer formed by curing the urethane-based composition according to claim 1 and in contact with the plurality of battery cells.
  • 16. A battery pack comprising one or more battery modules according to claim 15.
  • 17. An automobile comprising the battery module according to claim 15.
  • 18. A method of manufacturing a battery module, comprising injecting the urethane-based composition according to claim 1 into a module case; housing a battery cell in the module case, and curing the urethane-based composition to form the resin layer.
  • 19. The method of manufacturing battery module according to claim 18, wherein the curing of the urethane-based composition is performed by holding the resin composition at room temperature or heating at a temperature in a range of about 30° C. to 50° C. for a predetermined time.
Priority Claims (2)
Number Date Country Kind
10-2018-0035750 Mar 2018 KR national
10-2019-0029276 Mar 2019 KR national
PCT Information
Filing Document Filing Date Country Kind
PCT/KR2019/003149 3/19/2019 WO 00