Patent Application
20190300650
The invention relates to resin pellets, resin pellet manufacturing methods, and methods for manufacturing molded articles using the resin pellets.
Polyamide 66 (which is also referred to as “nylon 66” or “PA 66”) is light in weight and has high self-lubricity, for example. Thus, polyamide 66 is used in a wide range of applications. Examples of the applications include sliding members, such as gears of speed reducers for electric power steering systems and resin bearing cages. In response to recent demands for smaller size and higher power automobile parts, resin members used for such parts are required to have high mechanical strength and high stiffness. To meet such requirements, carbodiimide is added to polyamide so as to increase resin stiffness and toughness.
Japanese Patent Application Publication No. 2014-209032 (JP 2014-209032 A), for example, discloses a resin pellet provided by a process involving melting and blending polyamide 66, a copper heat stabilizer, polycarbodiimide, and an impact modifier (e.g., EPDM rubber onto which maleic anhydride is grafted) in a two-shaft kneader, extruding the resulting blend, and solidifying the extruded blend.
Unfortunately, simply melting and blending polyamide and polycarbodiimide so as to manufacture resin pellets may substantially complete an increase in molecular weight of polyamide induced by the action of polycarbodiimide in the course of manufacture of the resin pellets. In this case, molding heat generated during manufacture of molded articles using the resin pellets tends to promote resin decomposition (or thermal decomposition), leading to large variations in molecular weights and properties of the resulting molded articles.
An excessive increase in molecular weight of resin pellets yet to be molded forces a manufacturer to mold high melt viscosity resins. This disadvantageously makes it difficult to mold the resins with stability.
An object of the invention is to provide a resin pellet, a resin pellet manufacturing method, and a method for manufacturing a molded article using the resin pellet that enable stable mass-production of molded articles having high molecular weights and reduction of property variations among the molded articles.
A resin pellet according to an aspect of the invention includes a polyamide resin and a carbodiimide group. The percentage of the carbodiimide group to the resin pellet is 0.03% to 0.33% by mass. The resin pellet according to the aspect of the invention is provided by, for example, a resin pellet manufacturing method including adding a carbodiimide bond-containing compound to a molten polyamide resin so as to cause an unreacted carbodiimide group to remain.
The foregoing and further features and advantages of the invention will become apparent from the following description of example embodiments with reference to the accompanying drawings, wherein like numerals are used to represent like elements and wherein:
Embodiments of the invention will be described below in detail. A resin pellet according to an embodiment of the invention contains a polyamide resin and a carbodiimide group. Examples of the polyamide resin include aliphatic polyamides (such as PA 6, PA 66, PA 46, PA 12, PA 612, PA 610, PA 11, and PA 410), and aromatic polyamides (such as PA 6T, PA 9T, PA 10T, and PA MXD6). The polyamide resin is preferably aliphatic polyamide and more preferably polyamide 66 (PA 66). Any one of these polyamides may be used alone, or a combination of any two or more of these polyamides may be used. The polyamide resin has a number average molecular weight Mn of 15,000 to 25,000, for example. A base resin in the resin pellet may contain, in addition to the polyamide resin, a thermoplastic elastomer (such as an acid-denatured ethylene elastomer, EGMA, EPDM, or a polyamide elastomer), for example. Mixing a thermoplastic elastomer increases shock resistance of the resulting resin pellet.
The carbodiimide group is a functional group represented by the following formula: (—N═C═N—). The percentage of the carbodiimide group(s) to the resin pellet according to this embodiment of the invention is preferably 0.03% to 0.33% by mass, and more preferably 0.06% to 0.25% by mass. The amount of carbodiimide group(s) contained in the resin pellet may be determined using Lambert-Beer's law in accordance with the procedure illustrated in
The following description discusses the details of how the amount of carbodiimide group(s) contained in the resin pellet is determined. First, as illustrated in
Following the thickness adjustment, the thin-piece sample is placed on a KBr plate 105 and thus set on a base 106 of an infrared (IR) spectrophotometer as illustrated in
As illustrated in
The molar absorption coefficient c determined, the absorbance A known, and the sample thickness L known are substituted into the following equation: C═A/εL. Thus, the amount of carbodiimide group(s) (—N═C═N—) contained in the resin pellet is determined. Because a carbodiimide group is not the only element contained in a carbodiimide group-containing compound, the amount of carbodiimide group(s) is estimated from the chemical structure and amount of a carbodiimide group-containing compound. The resin pellet according to this embodiment of the invention has a number average molecular weight Mn of 25,000 to 40,000. The number average molecular weight Mn of the resin pellet is calculated by gel permeation chromatography (GPC) or solution viscosity method, for example.
The carbodiimide group(s) remain(s) in the resin pellet according to this embodiment of the invention. Thus, during injection molding of the resin pellet, the molding temperature thereof is utilized, so that the action of unreacted carbodiimide group(s) promotes the reaction of a terminal carboxyl group (—COOH) and/or an amino group (—NH2) of the polyamide resin with the carbodiimide group(s), and promotes the reaction between the terminal carboxyl group (—COOH) and terminal amino group (—NH2) of the polyamide resin. This enables a plurality of polyamide resin polymer chains made in advance by polymerization or a plurality of polyamide resin polymer chains connected to each other by the action of the carbodiimide group(s) during manufacturing of the resin pellet (which will be described below) to be further bound to each other in a chain-like manner. Consequently, the resin to be molded into a molded article will have a higher molecular weight.
The resin pellet according to this embodiment of the invention may contain a lubricant. The lubricant is not limited to any particular type of lubricant. Examples of the lubricant include the following known lubricants: metallic soaps, such as a metallic stearate; synthetic hydrocarbons, such as paraffin wax and synthetic polyethylene wax; fatty acids, such as a stearic acid; higher alcohols, such as a stearyl alcohol; higher aliphatic amides, such as a stearic acid amide and an oleic acid amide; esters, such as a higher fatty acid ester of an alcohol; and a silicone compound. Of these lubricants, higher aliphatic amides and a silicone compound are preferable lubricants to be used.
In this embodiment, any of the above known lubricants may be used. In particular, heat resistance conditions for the lubricant to be used are preferably such that the lubricant heated by TG-DTA at 10° C./min in a nitrogen atmosphere is reduced in weight by 10% at a temperature of 340° C. or above. Suppose that the lubricants meeting these heat resistance conditions have definite melting points. In this case, the lubricant having a melting point of 200° C. or above is preferably used. The resin pellet according to this embodiment of the invention may contain filler(s). Examples of the filler(s) include: short fiber fillers, such as glass fiber, carbon fiber, aramid fiber, cellulose fiber, poly(p-phenylenebenzobisoxazole) (PBO) fiber, polyarylate (PAR) fiber, and polytetrafluoroethylene (PTFE) fiber; plate-like fillers, such as glass flake; and micro reinforcing fillers, such as carbon nanotube and carbon nanofiber. One or more of these fillers may be contained in the resin pellet. Of these fillers, a short fiber filler is preferably used. Glass fiber is more preferably used as the filler. Organic fiber, such as aramid fiber, PBO fiber, PAR fiber, or PTFE fiber, is most preferably used as the filler.
A method for manufacturing the resin pellet will be described below.
The body 28 includes a main feeder 110, a side feeder 111, a cylinder 33, a screw 34, and a nozzle 35. The side feeder 111 is disposed between the main feeder 110 and the nozzle 35. In other words, the side feeder 111 is disposed downstream of the main feeder 110. The body 28 is not limited to any particular configuration. The body 28 may be, for example, a known kneader, such as a two-shaft (or multi-shaft) extruder or single-shaft extruder.
The main feeder 110 includes a tank 29, a scale 38, and a slot 32. The side feeder 111 includes a tank 112, a scale 113, and a slot 114. An agitator 37 is disposed upstream of the tank 29. Raw materials mixed in the agitator 37 are passed through the tank 29 and the scale 38 located downstream thereof and are then fed into the slot 32 of the main feeder 110.
The first step in preparing the resin pellets 26 is to supply a polyamide resin 39 and an optional additive to the cylinder 33 from the main feeder 110 serving as a shared feeder. The polyamide resin 39 and the optional additive may be separately fed into the tank 29 and then supplied to the cylinder 33, or may be mixed in the agitator 37 and then supplied to the cylinder 33. Mixing the polyamide resin 39 and the optional additive in the agitator 37 involves dry blending and master batching.
Any of the polyamide resins described above may be used as the polyamide resin 39. The percentage of the polyamide resin 39 to the total amount of raw materials used in the preparation of the resin pellets 26 is, for example, 45% to 90% by mass. A lubricant is preferably used as the optional additive. Some lubricants produce an “intermolecular sliding effect”, leading to a reduction in viscosity of raw materials of the resin pellets 26 during kneading. This enables kneading at a relatively low temperature. Thus, using such a lubricant as the optional additive controls the rate of reaction (or chain reaction) of the polyamide resin 39 during kneading of the polyamide resin 39, a filler 40, and a carbodiimide bond-containing compound 41 (which will hereinafter be simply referred to as “carbodiimide 41”).
When a lubricant such as one of those described above is used, the percentage of the lubricant to the total amount of raw materials used in the preparation of the resin pellets 26 is, for example, 0.01% to 1% by mass. The polyamide resin 39 and the optional additive supplied to the cylinder 33 are kneaded by rotation of the screw 34. The polyamide resin 39 and the optional additive are kneaded, with the temperature of the cylinder 33 at 275° C. to 325° C. and the rotational speed of the screw 34 at 100 rpm to 500 rpm, for example.
The next step is to simultaneously supply the filler 40 and the carbodiimide 41 to the cylinder 33 from the side feeder 111 serving as a shared feeder. It is basically difficult to knead a high-molecular-weight polyamide resin with a filler. The method according to this embodiment, however, allows a resin to be kneaded in a low viscosity state, thus enabling the resin to mix with a filler.
Examples of the filler 40 to be used include those previously described.
When glass fiber, for example, is used as the filler 40, the glass fiber preferably has a diameter of 6 μm to 15 μm, and more preferably has a diameter of 6 μm to 8 μm. Using the glass fiber having a diameter falling within these ranges comparatively increases the area of contact between the glass fiber and the polyamide resin in each resin pellet 26. This favorably increases the mechanical strength and stiffness of the resulting molded article formed by molding the resin pellets 26.
The percentage of the glass fiber to the total amount of raw materials used in the preparation of the resin pellets 26 is, for example, 10% to 50% by mass.
When organic fiber is used as the filler 40, the diameter of the organic fiber is not limited to any particular diameter. The organic fiber has a diameter of 9 μm to 15 μm, for example. The percentage of the organic fiber to the total amount of raw materials used in the preparation of the resin pellets 26 is, for example, 5% to 25% by mass. Using the organic fiber within this range prevents aggregation so as to knead the raw resin with the organic fiber uniformly, while cutting down the amount of relatively expensive organic fiber. This effectively increases the wear resistance of the resin. The carbodiimide 41 to be used may be any compound that contains a carbodiimide group (—N═C═N—). The carbodiimide 41 may be monocarbodiimide containing a single carbodiimide group, or polycarbodiimide containing a plurality of carbodiimide groups. Any type of carbodiimide, such as aliphatic carbodiimide, aromatic carbodiimide or modified carbodiimide, may be used as the carbodiimide 41. Of these carbodiimides, aromatic carbodiimide is preferably used as the carbodiimide 41. One specific example of such carbodiimide commercially available is “Stabaxol P-100” manufactured by LANXESS. When the carbodiimide 41 is aromatic carbodiimide, its aromatic ring and adjacent functional group produce a steric hindrance effect, thus controlling the rate of reaction (or chain reaction) of the polyamide resin 39 during kneading of the polyamide resin 39, the filler 40, and the carbodiimide 41. This facilitates control operations for allowing the percentage of residual carbodiimide group(s) to each resin pellet 26 to be 0.03% to 0.33% by mass. The control operations include, for example, controlling the temperature of the cylinder 33, the time during which kneading is to be performed, and the pressure during kneading.
Suppose that the carbodiimide 41 is aliphatic carbodiimide and has no aromatic ring. The carbodiimide 41 in this case makes it difficult to achieve the above-mentioned steric hindrance effect produced by an aromatic ring and an adjacent functional group. The carbodiimide 41 in this case, however, achieves a similar effect when the carbodiimide 41 contains a lubricant. This is because, in such a case, the lubricant produces an intermolecular sliding effect as previously mentioned. In other words, when aliphatic carbodiimide is used as the carbodiimide 41, a lubricant such as one of those described above is preferably used in combination therewith. When aliphatic carbodiimide is used as the carbodiimide 41, employing a first technique described below favorably enables the percentage of residual carbodiimide group(s) to each resin pellet 26 to be 0.03% to 0.33% by mass. The first technique described below is provided by way of example only, and any other technique may be used.
The first technique includes step (1) involving disposing the side feeder 111 close to the nozzle 35. This reduces the time allowed for the reaction of the polyamide resin 39 induced by the action of the carbodiimide group(s). Thus, the reaction (or chain reaction) of the polyamide resin 39 is controlled.
The first technique further includes step (2) involving reducing the temperature set for the barrel of the kneading machine 27. Melting the polyamide resin 39 in the vicinity of the main feeder 110 at a temperature equal to or higher than the melting point of the polyamide resin 39 would enable the molten polyamide resin 39 to flow if the temperature set for a region downstream of the main feeder 110 is low. Thus, reducing the temperature set for the barrel controls the reaction (or chain reaction) of the polyamide resin 39.
The first technique further includes step (3) involving reducing the number of revolutions set for the kneading machine 27. Reducing the number of revolutions decreases shearing heat applied to the resin, thus controlling the reaction (or chain reaction) of the polyamide resin 39.
The first technique further includes step (4) involving providing the kneading machine 27 with the screw and kneading disks having a low-shearing configuration. This means that, for example, the ratio of kneading disks to the screw (i.e., the number of kneading disks) may be reduced, or kneading disks small in width may be used. Consequently, the effect of kneading is lessened, thus controlling the reaction (or chain reaction) of the polyamide resin 39.
The number average molecular weight Mn of the carbodiimide 41 is preferably relatively high. The number average molecular weight Mn of the carbodiimide 41 is 3,000 to 25,000, for example. The percentage of the carbodiimide 41 to the total amount of raw materials used in the preparation of the resin pellets 26 is, for example, 0.5% to 4% by mass. Using the carbodiimide 41 within this range favorably provides a final molded article whose number average molecular weight Mn is 30,000 or more. Because the carbodiimide 41 is not excessive in amount, this embodiment of the invention reduces the risk of, for example, an increase in resin pressure (or viscosity) during kneading, heat generation during kneading, thermal decomposition of the polyamide resin 39 and the carbodiimide 41 associated with the heat generation, and a reduction in strength of adhesion of the filler 40 to the resin caused by convergence degradation associated with the heat generation.
When the carbodiimide 41 is powder, the carbodiimide 41 may be supplied independently through the side feeder 111, or may be mixed with a polyamide resin and then supplied through the side feeder 111. Mixing the carbodiimide 41 with the polyamide resin involves dry blending and master batching. The filler 40 and the carbodiimide 41 are added to a kneaded mixture of the polyamide resin 39 and the optional additive being conveyed through the cylinder 33, so that the polyamide resin 39, the optional additive, the filler 40, and the carbodiimide 41 are subjected to further kneading so as to provide a kneaded mixture of these substances. The time between the supply of the carbodiimide 41 and the ejection of the kneaded mixture from the nozzle 35 (which will hereinafter be referred to as a “kneading time for the carbodiimide 41”) ranges from one second to one minute, for example. Accordingly, the distance between the side feeder 111 and the nozzle 35 may be set in accordance with the kneading time for the carbodiimide 41. As illustrated in
Following the supply of the carbodiimide 41, the kneaded mixture is ejected in the form of a strand from the nozzle 35, solidified by being cooled in the cooling water tank 30, and then pelletized by the pelletizer 31. Carrying out these steps provides the resin pellets 26 each containing the polyamide resin 39, with the filler 40 dispersed therein. Each resin pellet 26 thus provided contains 0.03% to 0.33% of unreacted carbodiimide group(s) (i.e., residual carbodiimide) by mass. The term “unreacted carbodiimide group(s)” refers to carbodiimide group(s) that has/have not reacted during the kneading process previously described. Feeding the carbodiimide 41 from the side feeder 111 allows the unreacted carbodiimide group(s) to remain in each resin pellet 26. In this case, the carbodiimide 41 is allowed to favorably remain in each resin pellet 26 by, for example, appropriately selecting the type of carbodiimide to be used as the carbodiimide 41, adjusting the number average molecular weight Mn of the carbodiimide 41, and deciding whether the carbodiimide 41 should contain a lubricant. The types of carbodiimide to be used as the carbodiimide 41 include aromatic carbodiimide and aliphatic carbodiimide.
The number average molecular weight Mn of each resin pellet 26 provided is, for example, 25,000 to 40,000. The above-described manufacturing procedure involves supplying the carbodiimide 41 to the cylinder 33 from the side feeder 111. This limits the time allowed for the reaction of the polyamide resin 39 induced by the action of the carbodiimide group(s). If the carbodiimide 41 is supplied from the main feeder 110, the reaction of the polyamide resin 39 proceeds while the resin being kneaded is conveyed substantially from end to end of the cylinder 33. This embodiment, however, shortens the distance allowed for the reaction of the polyamide resin 39 so that the reaction of the polyamide resin 39 occurs only between the side feeder 111 and the nozzle 35, thus limiting the time allowed for the reaction of the polyamide resin 39. Consequently, this embodiment easily causes the unreacted carbodiimide group(s) to remain in each resin pellet 26 provided.
The above procedure involves supplying the carbodiimide 41 in the course of kneading of the polyamide resin 39 and the filler 40. This reduces the occurrence of disadvantageous conditions, such as excessive torque, heat generation, and strand tearing in the body 28, and unfavorable resinous attachments to the body 28, more effectively than when the polyamide resin 39, the filler 40, and the carbodiimide 41 are simultaneously supplied to the cylinder 33 so as to start kneading or when the polyamide resin 39 and the carbodiimide 41 are simultaneously supplied to the cylinder 33 from the main feeder 110 (i.e., the preceding one of the feeders) so as to start kneading. Consequently, this embodiment enables stable production of the resin pellets 26.
Although the above description has been predicated on the assumption that the carbodiimide 41 is supplied from the side feeder 111, the carbodiimide 41 may alternatively be supplied from the main feeder 110. In such a case, using a second technique described below favorably enables the percentage of residual carbodiimide group(s) to each resin pellet 26 to be 0.03% to 0.33% by mass. The second technique described below is provided by way of example only, and any other technique may be used.
The second technique includes step (1) involving performing at least one of steps (2) to (4) of the first technique employed in using aliphatic carbodiimide as the carbodiimide 41.
The second technique further includes step (2) involving disposing a highly sterically hindering functional group, such as an isopropyl group, on the periphery of the carbodiimide group(s) when aromatic carbodiimide is used as the carbodiimide 41.
Using the second technique controls the rate of reaction of the carbodiimide 41 (i.e., the ease of reaction between the carbodiimide group(s) and polyamide). Suppose that a lubricant is used in one of the steps. In this case, the lubricant heated by TG-DTA at 10° C./min in a nitrogen atmosphere is reduced in weight by 10% at a temperature of 340° C. or above, thus achieving an effect described below. Specifically, the temperature of the cylinder 33 is set in the range of, for example, 275° C. to 325° C. during kneading of the resin in the cylinder 33. Setting the temperature of the cylinder 33 at a high temperature in this range (i.e., at a temperature of 300° C. or above) enables a reduction in viscosity by addition of the lubricant so as to produce the effect of improving kneadability and moldability, although black spots are likely to occur in the resin. The occurrence of such black spots is caused by decomposition, gasification, and carbonization of the lubricant that are induced by a heat history during kneading of the resin, for example. Such black spots may hinder the growth of necking of the resin and cause breaking of the resin to proceed from the black spots, resulting in a reduction in mechanical strength (e.g., tensile elongation at break) of the resin. One conceivable solution to the occurrence of black spots is to utilize, for example, image analysis so as to mechanically remove (or screen out) resin pellets having black spots, and another conceivable solution is to screen out, before shipment, molded articles having black spots. Unfortunately, either of these solutions leads to an increase in cost or a reduction in yield.
To solve such problems, this embodiment of the invention involves the use of a lubricant that meets the heat resistance conditions previously mentioned. This would reduce or eliminate the occurrence of black spots if the resin is kneaded at a temperature as high as 300° C. or above. Such an advantage reduces breaking of the resin that proceeds from the black spots. Thus, with an increase in molecular weight of the resin, the mechanical strength of the resin is maintained at a favorable level. Because what is needed for this solution is to simply select the type of lubricant to be used, the step of screening out resin pellets, for example, is unnecessary, resulting in no increase in cost or no reduction in yield.
The resin pellets thus provided are usable for any type of structural member (or molded article) whose constituents include a polyamide resin. Examples of such structural members include various resin gears, various bearing cages, and various housings. Specific examples of such structural members include a worm wheel, a worm housing and a sensor housing for a power steering system, a resin-wound guide bearing for a sliding door, and a housing for an electric oil pump. The usage of the resin pellets according to this embodiment of the invention is not limited to these specific examples.
An exemplary molded article formed from the resin pellets according to this embodiment of the invention will be described below with reference to the accompanying drawings.
The gear 20 thus described is usable not only as a worm wheel for a power steering system but also as any of various other gears, such as a bevel gear and a helical gear. The manufacture of the gear 20 involves, for example, preparing a mold (not illustrated), melting the resin pellets 26 provided by following the procedure illustrated in
In the course of manufacture of the resin pellets 26 illustrated in
This embodiment intentionally causes the percentage of residual unreacted carbodiimide group(s) to each resin pellet 26, provided by following the procedure illustrated in
In this embodiment, the step of kneading raw materials of the resin pellets 26 and the step of molding the resin pellets 26 are regarded as a series of heating steps. Throughout the series of heating steps, the chain reaction of the polyamide resin 39 is allowed to proceed to an appropriate level so as to increase the molecular weight of the polyamide resin 39 to an unprecedented level. This keeps the chain reaction of the polyamide resin 39 from proceeding excessively just in the step of kneading raw materials of the resin pellets 26, and thus prevents the reaction of the polyamide resin 39 from becoming so excessive that the polyamide resin 39 is decomposed in the subsequent step of molding the resin pellets 26.
The chain reaction of the polyamide resin 39 in the resin pellets 26 yet to be molded is still in progress, and the molecular weight of the resin pellets 26 yet to be molded is lower than the molecular weight of the final molded article (e.g., the resulting gear 20). The number average molecular weight Mn of the gear 20 is, for example, 30,000 or more, while the number average molecular weight Mn of the resin pellets 26 is, for example, 25,000 to 40,000. The polyamide resin 39 in the resin pellets 26 yet to be molded is relatively low in viscosity. This facilitates molding and thus makes it unnecessary to excessively raise the molding temperature. Consequently, thermal decomposition of the resin is controlled so as to reduce molecular weight variations and property variations among the molded articles (or gears 20).
The resin pellets 26 are moldable in a relatively low viscosity state. This would allow the resin to be favorably filled into the mold if an injection molding machine, for example, has a small gate diameter. In the step of kneading raw materials of the resin pellets 26, the filler 40 is naturally favorably dispersible throughout the polyamide resin 39 whose molecular weight is not high (or whose viscosity is low) before the carbodiimide 41 is fed. Organic fiber, in particular, is soft and thus unlikely to break, making it generally difficult to knead a high viscosity, high molecular weight molten resin with organic fiber. Kneading a high molecular weight molten resin with organic fiber requires, for example, increasing the number of revolutions of a kneading machine and/or increasing the temperature set for a barrel, thus reducing the viscosity of the resin so as to effect a reduction in kneading torque. Such a technique causes resin decomposition to proceed owing to heat generation, leading to a reduction in molecular weight. This makes it difficult to take advantage of properties of a high molecular weight resin, such as high wear resistance. In other words, uniformly mixing organic fiber, which is unlikely to damage an associated component and contributes to an increase in wear resistance of a resin, by the technique known in the art makes it difficult to increase the molecular weight of a resin. Giving higher priority to increasing the molecular weight of a resin makes it difficult to uniformly mix organic fiber. The method according to this embodiment, however, makes it possible to knead a resin in a low viscosity state. This enables an increase in molecular weight of the resin while uniformly dispersing organic fiber in the resin. When organic fiber is used, carbodiimide group(s) react(s) not only with a polyamide resin but also with the organic fiber. In an example where aramid fiber, for example, is used, carbodiimide group(s) react(s) with an amido group in the aramid fiber. Thus, using organic fiber in the method according to this embodiment achieves the effect of increasing the strength of adhesion between the polyamide resin and the organic fiber. Consequently, the wear resistance of the resulting molded article is higher than when no organic fiber is added.
As described thus far, this embodiment provides the gear 20 having high mechanical strength and wear resistance. More specifically, the embodiment of the invention provides mechanical strength, stiffness, and dimensional stability required for the gear 20. The number average molecular weight Mn of the resin is 30,000 or more, resulting in high resistance to crack extension. The high resistance to crack extension would reduce the speed of crack extension if the filler 40 triggers crack-inducing resin wear and/or flaking. Consequently, this embodiment reduces the wear volume of the teeth 24 and thus achieves wear resistance required for the teeth 24.
These advantages serve to prevent an increase in variation in the inter-core distance between the gear 20 and an associated component. Suppose that the gear 20 is used as a worm wheel for a speed reducer of a power steering system. In this case, rattling sounds will not be produced because a variation in the inter-core distance between the worm wheel and a worm does not increase, and in addition, durability and life of the worm wheel will increase. Worm wheels, in particular, may be expected to be further reduced in size and increasingly used in higher power applications in the future. This will increase loads to an unprecedented level and will result in application of large torques to the worm wheels. Worm wheels having poor wear resistance will have reduced durability and life due to application of such large torques. When the gear 20 according to this embodiment is used as a worm wheel, the worm wheel has high wear resistance as described above and is thus adequately adaptable to future applications where the worm wheel needs to be smaller in size and is intended for higher power use. The gear 20 manufactured using the resin pellets 26 containing organic fiber has increased wear resistance and is unlikely to damage an associated component. Organic fiber is lower in Mohs hardness than glass fiber. Thus, if sliding of the gear 20 causes organic fiber to be exposed at the surface of the gear 20, the gear 20 would be prevented from wearing away the surface of an associated component. When the gear 20 is used as a worm wheel, for example, a component associated with the gear 20 is a worm. Suppose that sliding contact between the gear 20 and an associated component causes organic fiber to come off the gear 20. In this case, the organic fiber that has come off the gear 20 will not wear away the gear 20. Accordingly, the resin pellets 26 containing organic fiber are favorably used in manufacturing a molded article (e.g., a sliding member) that is particularly required to have a low probability of damaging an associated component and have high wear resistance. Using the organic fiber-containing resin pellets 26 in manufacturing the gear 20 to be used as a worm wheel prevents wearing away of a metal worm that is a component associated with the gear 20. This makes it unnecessary to perform, for example, induction heat treatment for increasing the hardness of the worm, so that an increase in manufacturing cost is prevented. Using the organic fiber-containing resin pellets 26 in manufacturing a resin-wound guide bearing (or roller) for a sliding door prevents peeling off of a coating on a vehicle body that is a component associated with the guide bearing (or roller). This makes it unnecessary to attach an additional component, such as a guide rail, to the sliding door, so that an increase in manufacturing cost is prevented as in the case of using the organic fiber-containing resin pellets 26 in manufacturing the gear 20 to be used as a worm wheel. Suppose that a molded article to be manufactured is a container (e.g., a housing such as one previously described) that will not come into contact with any particular component and is required to have high mechanical strength and stiffness rather than high wear resistance. In such a case, the resin pellets 26 containing glass fiber may be used. In other words, an appropriate selection may be made between using the resin pellets 26 containing organic fiber and using the resin pellets 26 containing glass fiber in accordance with the usage of a molded article to be manufactured and characteristics required for the molded article.
Although the embodiment of the invention has been described thus far, the invention may be practiced in other embodiments.
In one example, the body 28 of the kneading machine 27 may include two side feeders as illustrated in
The filler 40 may be supplied to the cylinder 33 from the main feeder 110 together with the polyamide resin 39. In such a case, the position from which the filler 40 is to be supplied is upstream of the position from which the carbodiimide 41 is to be supplied. Thus, the filler 40 is supplied before an increase in molecular weight induced by the action of carbodiimide group(s) starts, i.e., when the viscosity of the resin is lower. This further enhances dispersion of the filler 40. Suppose that the filler 40 is organic fiber. In this case, if the filler 40 is supplied in an initial stage of kneading, the organic fiber would keep its shape, because the organic fiber is soft and unlikely to break. The molded article manufactured by the method according to the embodiment of the invention may contain no filler. Various other design modifications may be made within the scope of the claims.
The invention will be further described below in relation to Examples 1 to 8, Comparative Example 1, and Reference Examples 1 and 2. The invention is not limited to the examples described below.
In accordance with the data given in Table 1 below, raw materials were supplied to the kneading machine 27 arranged as illustrated in
Commercial Product 1
Polyamide 66 manufactured by Asahi Kasei Corp. (e.g., non-reinforced grade “Leona 1502S”) was molded into a test sample. Neither glass fiber nor carbodiimide was added.
Commercial Product 2
Polyamide 66 manufactured by BASF (e.g., “A5H”) was molded into a test sample. Neither glass fiber nor carbodiimide was added.
Commercial Product 3
Polyamide 66 manufactured by DuPont (e.g., “Zytel® E51HSB NC010”) was molded into a test sample. Neither glass fiber nor carbodiimide was added.
Evaluation Test
(1) Amount of Residual Carbodiimide
The amount of residual carbodiimide contained in the resin pellets provided by Examples 1 to 8 and Reference Example 2 was measured by following the procedure illustrated in
Table 1 suggests that when no lubricant is contained, using aromatic carbodiimide as in Examples 1 to 8 enables the percentage of residual carbodiimide group(s) to each resin pellet to be 0.03% to 0.33% by mass. Using aliphatic carbodiimide as in Reference Example 2 causes almost all of carbodiimide groups to be consumed at the time when resin pellets are prepared, so that the percentage of residual carbodiimide to each resin pellet is 0.01% by mass.
The comparison between Example 2 and Example 5 reveals that the amount of residual carbodiimide group(s) when a carbodiimide compound is added from the side feeder is larger than the amount of residual carbodiimide group(s) when a carbodiimide compound is added from the main feeder, assuming that the amount of carbodiimide compound added in both cases is the same.
(2) Number Average Molecular Weight Mn
For each test sample, the number average molecular weight Mn was measured by gel permeation chromatography (GPC). The results of the measurement are given in Table 1 and
(3) Time-Varying Changes in Number Average Molecular Weight Mn
(4) Tensile Elongation at Break and Tensile Strength
For Examples 1 to 8 and Reference Example 2, tensile elongation at break and tensile strength were measured in conformity with JIS K 7161. The results of the measurement are given in Table 1 and
Table 1 reveals that adding a carbodiimide compound from the main feeder as in Examples 1 to 3 achieves high tensile elongation at break, particularly when the amount of residual carbodiimide is 0.03% by mass as in Example 2. Table 1 further reveals that adding a carbodiimide compound from the side feeder as in Examples 4 to 7 achieves high tensile elongation at break, particularly when the amount of residual carbodiimide is 0.15% by mass as in Example 6.
Referring to Reference Examples 3 to 8, the following description discusses how the frequency of occurrence of black spots in the resin and the tensile elongation at break of the resin change depending on heat resistance conditions for lubricants. Specifically, polyamide 66 manufactured by Asahi Kasei Corp. under the product name “Leona 1702” was kneaded with each lubricant described in Table 2, with the temperature of the cylinder set at 300° C. during kneading. Thus, resin pellets were prepared. The resin pellets prepared were then molded into test samples.
(1) Tensile Elongation at Break
For Reference Examples 3 to 8, tensile elongation at break was measured in conformity with JIS K 7161. The results of the measurement are given in Table 2.
(2) Frequency of Occurrence of Black Spots
After the test of tensile elongation at break just mentioned, we made observations to determine whether a black spot occurred at each broken surface. The number of samples n for each reference example was five. We estimated the frequency of occurrence of black spots by giving two points to each sample with a black spot having a size of 100 mm or more, giving one point to each sample with a black spot having a size of less than 100 mm, and giving zero point to each sample with no black spot. The sum of points given to the five samples for each reference example was determined to be the measurement result for each reference example. The sum of points given to the five samples for each reference example is 10 points at the maximum.
As illustrated in
Referring to Examples 9 and 10 and Comparative Examples 2 to 5, the following description discusses how the molecular weight and wear resistance of the molded article increase by the combined use of a carbodiimide compound and organic fiber (e.g., aramid fiber). In accordance with the data given in Table 3 below, raw materials were supplied to the kneading machine 27 arranged as illustrated in
Evaluation Test
(1) Amount of Residual Carbodiimide
The amount of residual carbodiimide in the resin pellets provided by Examples 9 and 10 was measured by following the procedure illustrated in
(2) Number Average Molecular Weight Mn
For each test sample, the number average molecular weight Mn was measured by gel permeation chromatography (GPC). The results of the measurement are given as relative ratios in
(3) Frictional Wear Test (for Wear Resistance)
Suzuki frictional wear test was conducted to measure the amount of reduction in height of each test sample. The amount of height reduction measured is determined to be a wear volume and expressed in mm. The results of the test are given in
(4) Evaluation
The number average molecular weight of raw resin used for each of Comparative Examples 3 and 5 was higher than the number average molecular weight of raw resin used for each of Examples 9 and 10 and Comparative Examples 2 and 4. In spite of this,
| Number | Date | Country | Kind |
|---|---|---|---|
| 2015-229676 | Nov 2015 | JP | national |
| 2016-077494 | Apr 2016 | JP | national |
| 2016-187529 | Sep 2016 | JP | national |
This is a Divisional of application Ser. No. 15/355,502 filed Nov. 18, 2016, which claims priority to Japanese Patent Applications No. 2015-229676 filed on Nov. 25, 2015, No. 2016-077494 filed on Apr. 7, 2016 and No. 2016-187529 filed on Sep. 26, 2016. The entire disclosures of the prior applications are hereby incorporated by reference herein their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15355502 | Nov 2016 | US |
| Child | 16446915 | US |