Patent Application
20230097791
The present disclosure relates to a resistive switching memory device and, more particularly, a resistive switching memory (RRAM) that can achieve a voluntary rectification characteristic, a voluntary limit current characteristic, and a multi-level implementation by including amorphous metal oxide-based dual active layers made of the same material.
As high-density integration of volatile memories comes close to a limit, a nonvolatile memory rises as a next generation memory.
A nonvolatile memory includes a phase change RAM (PRAM), a nano-floating gate memory (NFGM), a resistive RAM (ReRAM), a polymer RAM (PoRAM), a magnetic RAM (MRAM), molecule electronics, etc., and a RRAM (resistive RAM) of these devices is spotlighted as a next generation nonvolatile memory because of an easy manufacturing process, a high switching speed, and excellent durability in comparison to other devices.
According to the technical development trend of the RRAM (Resistive RAM), a technology of achieving a cross point array using an RRAM is being developed as a strategy for further increasing integration of the RRAM.
The cross point array using an RRAM in the early stage had some problems. First, there is influence (cross-talk) between adjacent cells when a cross point array using an RRAM is formed, thereby forming a sneak path and generating backflow of a current (sneak current), so there was a problem that data errors are generated. Further, there was a problem that it is required to suppress a current that is irreversibly generated when an RRAM is driven.
In order to solve these problems, an external selection device and an external compliance current application device were applied to the existing cross point array using an RRAM, but it was impossible to use a simple metal-insulator-metal (MIM) structure, which is an advantage of the RRAM, and there was a limitation in integration.
Second, a compliance current that controls conductivity is necessarily required to drive an RRAM. A current was limited in existing RRAMs using an external diode, a transistor, etc., but it was accompanied by a limitation in integration of the memory. Further, the added external diode, transistor, etc. could not follow the processing speed of an RRAM active layer, so there was a problem that the driving speed of the memory is limited.
As another technical trend, a method of manufacturing an RRAM itself into a single device having functions not requiring help of an external diode, a transistor, etc. was proposed, and a structure including active layers made of different substances in dual layers was developed. However, it was difficult to uniformly control the number and size of polycrystalline grain boundaries, so electrical non-uniformity and instability of a device turned out as insuperable problems.
Similarly, an RRAM using a phase change needs a heat transmit layer, so there was a difficulty in performing a complicated process.
It was attempted to solve these problems by disclosing a resistance memory device including a lower electrode formed on a substrate, a variable resistive layer disposed on the lower electrode, and an upper electrode formed on the variable resistive layer, in which the variable resistive layer is composed of two or more oxide films, and a method of manufacturing the resistance memory device in Korean Patent No. 10-1401221 (titled, “Resistance memory device comprising crystalline oxidation film and method of fabricating the same”). However, since a crystalline oxidation film is included, it is difficult to control the number and size of grain boundaries and accordingly there is a limitation of electrical non-uniformity and instability of the device.
Accordingly, there is a need for a technology that can achieve a multi-level implementation as a single device to keep the advantages of an RRAM and increase integration and that can solve the problem of a sneak current that is generated when forming an array and the problem that it is required to control a compliance current.
Patent Literature 1: Korean Patent No. 10-1401221
An objective of the present disclosure for solving the problems described above is to provide a resistive switching memory device (RRAM) that can achieve a multi-level implementation as a single device.
Another objective of the present disclosure is to provide a resistive switching memory device (RRAM) that solves the problem of a sneak current that is generated between adjacent cells when a cross point array is formed, and solves the problem that it is required to control a compliance current, as a single device.
Another objective of the present disclosure is to provide a resistive switching memory device that solves the problem of controlling grain boundaries that is generated when an active layer is formed into a crystalline dual layer, and solves the corresponding problem of electrical non-uniformity and instability of a device.
The objectives to implement in the present disclosure are not limited to the technical problems described above and other objects that are not stated herein will be clearly understood by those skilled in the art from the following specifications.
In order to achieve the objectives, a resistive switching memory device that is an embodiment of the present disclosure includes: a lower electrode; an amorphous metal oxide-based first active layer positioned on the lower electrode; an amorphous metal oxide-based second active layer positioned on the first active layer; and an upper electrode positioned on the second active layer, wherein the first active layer and the second active layer are made of the same substance and are different in electrical characteristic,
In an embodiment of the present disclosure, the amorphous metal oxide-based first active layer may include crystalline metal oxide nanoparticles.
In an embodiment of the present disclosure, the amorphous metal oxide-based second active layer may include crystalline metal oxide nanoparticles.
In an embodiment of the present disclosure, the first active layer and the second active layer may be different in set driving voltage.
In an embodiment of the present disclosure, the first active layer and the second active layer may be the same in reset driving voltage.
In an embodiment of the present disclosure, the first active layer or the second active layer may show a voluntary rectification characteristic.
In an embodiment of the present disclosure, the first active layer and the second active layer may include one or more selected from a group composed of CuO, CuzO, Al2O3, Nb2O5, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, Co3O4, Fe2O3, Ag2O3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
The resistive switching memory device that is an embodiment of the present disclosure may show: (a) a first resistance state in which a first positive voltage is applied between the upper electrode and the lower electrode, so the first active layer is set into a low-resistance state; (b) a second resistance state in which a second positive voltage is applied between the upper electrode and the lower electrode, so the first active layer and the second active layer are set into a low-resistance state; and (c) a third resistance state in which a third positive voltage is applied between the upper electrode and the lower electrode, so the first active layer and the second active layer are reset into a high-resistance state.
In order to achieve the objectives, a method of manufacturing a resistive switching memory device that is another embodiment of the present disclosure includes: (i) forming an amorphous metal oxide-based first active layer on a lower electrode by electrochemical deposition; (ii) forming an amorphous metal oxide-based second active layer on the first active layer by electrochemical deposition; and (iii) forming an upper electrode on the second active layer, in which the first active layer and the second active layer are made of the same substance but process conditions of the electrochemical deposition are different.
In an embodiment of the present disclosure, the amorphous metal oxide-based first active layer may include crystalline metal oxide nanoparticles.
In an embodiment of the present disclosure, the amorphous metal oxide-based second active layer may include crystalline metal oxide nanoparticles.
In an embodiment of the present disclosure, the metal oxides of the step (i) and the step (ii) may include one or more selected from a group composed of CuO, Cu2O, Al2O3, Nb2O5, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, CosO4, Fe2O3, AgzO3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
In order to achieve the objectives, a resistive switching memory device array that is another embodiment of the present disclosure includes: a first electrode extending in a first direction; a second electrode extending in a second direction crossing the first electrode; and an amorphous metal oxide-based first active layer and an amorphous metal oxide-based second active layer sequentially formed between the first electrode and the second electrode, in which the first active layer and the second active layer are made of the same substance but are different in electrical characteristic.
In an embodiment of the present disclosure, the amorphous metal oxide-based first active layer may include crystalline metal oxide nanoparticles.
In an embodiment of the present disclosure, the amorphous metal oxide-based second active layer may include crystalline metal oxide nanoparticles.
In an embodiment of the present disclosure, the first active layer and the second active layer may include one or more selected from a group composed of CuO, Cu2O, Al2O3, Nb2O5, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, Co3O4, Fe2O3, Ag2O3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
Hereinafter, the present disclosure is described with reference to the accompanying drawings. However, the present disclosure may be modified in various different ways and is not limited to the embodiments described herein. Further, in the accompanying drawings, components irrelevant to the description will be omitted in order to obviously describe the present disclosure, and similar reference numerals will be used to describe similar components throughout the specification.
Throughout the specification, when an element is referred to as being “connected to (coupled to, combined with, in contact with)” another element, it may be “directly connected” to the other element and may also be “indirectly connected” to the other element with another element intervening therebetween. Further, unless explicitly described otherwise, “comprising” any components will be understood to imply the inclusion of other components rather than the exclusion of any other components.
Terms used in the present invention are used only in order to describe specific exemplary embodiments rather than limiting the present disclosure. Singular forms are intended to include plural forms unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” or “have” used in this specification specify the presence of stated features, numerals, steps, operations, components, parts, or a combination thereof, but do not preclude the presence or addition of one or more other features, numerals, steps, operations, components, parts, or a combination thereof.
Hereinafter, embodiments of the present disclosure are described in detail with reference to the accompanying drawings.
Referring to
The first active layer 200 and the second active layer 300 are characterized by being made of the same substance but having different electrical characteristics.
In an embodiment of the present disclosure, the upper electrode 400 and the lower electrode 100 are provided to apply a voltage to the first active layer 200 and the second active layer 300 and are made of metal or an oxide having electrical conductivity. In detail, the electrodes may include conductive oxides such as ITO(InSnO), IZO(InZnO), and AZO(AlZnO) or metals such as Ir, Pt, Ru, Au, Ag, Mo, Al, W, and Cu.
In an embodiment of the present disclosure, the first active layer 200 may be positioned on the lower electrode 100.
The first active layer 200 may include a metal oxide that can be used to form a thin film by electrochemical deposition. In detail, all metal oxides produced by bonding of hydroxyl ions and metal ions by electrochemical deposition correspond to the metal oxide described above.
For example, the metal oxide described above may include one or more selected from a group composed of CuO, Cu2O, Al2O3, Nb2OS, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, CosO4, Fe2O3, AgzO3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
The first active layer 200 is characterized by being amorphous. In detail, the first active layer 200 may be a type in which crystalline metal oxide nanoparticles are distributed in a matrix that is an amorphous metal oxide.
When a matrix itself is crystalline, it has a forming voltage, but when a matrix is an amorphous, it shows a forming-free behavior, so there is an advantage. However, when a matrix is an amorphous, there is a problem of low electrical conductivity, which is possible to resolved by distributing crystalline metal oxide nanoparticles having high electrical conductivity in an amorphous matrix.
In detail, when a voltage is applied to an RRAM device, the RRAM device changes into a low resistance state (LRS) from a high resistance state (HRS), and the forming voltage means a voltage that is required to form a conductive path for progressing this process.
In this case, in a crystalline structure in which grains and grain boundaries are clearly discriminated, the grain boundary density is not uniform in the path in which a conductive path is formed and it is difficult to form a shortest conductive path.
Accordingly, when all of first active layers 200 are crystalline, a memory device has irregular forming driving and high forming voltage when the memory device is driven.
On the contrary, when they are amorphous, the structure is dense and grain boundaries are very small, so the grain boundary density of a path where a conductive path is formed is relatively uniform. Accordingly, it is stable in formation of a conductive path and has a forming-free driving characteristic.
Next, crystalline metal oxide nanoparticles distributed in the amorphous matrix serve to form a channel when a voltage is applied. In particular, nano-level crystalline particles do not generate a grain boundary problem, which is defect that a bulk crystalline structure has, and solves the problem of low electrical conductivity of an amorphous matrix because the electrical conductivity thereof is high.
In this case, it is possible to adjust the electrical conductivity of an active layer by adjusting the size and density of crystalline metal oxide nanoparticles distributed in the amorphous matrix.
For the mechanism described above, the amorphous first active layer 200 proposed in the present disclosure has an advantage that it is possible to drive a memory device with a stable electrical characteristic and a low voltage, and satisfies a condition under which it is possible to form a plurality of active layers made of the same substance and being different in electrical characteristic.
Next, in an embodiment of the present disclosure, the second active layer 300 may be positioned on the first active layer 200.
The second active layer 300 may include a metal oxide that can be used to form a thin film by electrochemical deposition. In detail, all metal oxides produced by bonding of hydroxyl ions and metal ions by electrochemical deposition correspond to the metal oxide described above.
For example, the metal oxide described above may include one or more selected from a group composed of CuO, Cu2O, Al2O3, Nb2OS, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, CosO4, Fe2O3, AgzO3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
The second active layer 300 is characterized by being amorphous. In detail, the second active layer 300 may be a type in which crystalline metal oxide nano particles are distributed in a matrix that is an amorphous metal oxide.
Similar to the first active layer 200, when all of second active layers 300 are crystalline, the density of grain boundaries in the active layers is not uniform, so when a memory device is driven, irregular forming driving and a high forming voltage are caused. Accordingly, they are based on an amorphous matrix showing a forming-free behavior, which is for solving the problem of low electrical conductivity of an amorphous matrix using crystalline metal oxide nanoparticles distributed in a matrix.
For the mechanism described above, the amorphous second active layer 300 proposed in the present disclosure has an advantage that it is possible to drive a memory device with a stable electrical characteristic and a low voltage, and satisfies a condition under which it is possible to form a plurality of active layers made of the same substance and being different in electrical characteristic.
Next, in an embodiment of the present disclosure, the first active layer 200 and the second active layer 300 are characterized by being made of the same substance but having different electrical characteristics.
In order to achieve the effects of the present disclosure, a single memory device should have a voluntary compliance current characteristic, a voluntary current rectification characteristic, and a voluntary multi-level storage characteristic. In order to secure these characteristics, electrical characteristics should be different between dual active layers, there should be no forming step between layers, and a driving voltage forming mechanism and a filament forming mechanism should be the same, so the single memory device should have a compatible characteristic.
As for factors other than the forming voltage described above, as proposed in the present disclosure, when the active layers described above are made of the same metal oxide, the properties of the metal oxides are the same, so the driving voltage mechanisms are the same and the filament forming mechanisms are the same. Accordingly, the active layers have a compatible characteristic.
However, an electrical characteristic may be different even if the same substance is used when different voltage conditions is used for forming an active layer by electrochemical deposition.
In detail, since the degree of reduction-oxidation for production and growth of a crystal depends on a voltage that is applied in an electrochemical deposition process, the aspect of crystal growth changes, as in Experiment example 1.
Accordingly, the size and density of crystalline metal oxide nanoparticles distributed in an amorphous matrix change, the ratio of the amorphous matrix and the crystalline metal oxide nanoparticles changes, and the electrical characteristic of a thin film changes due to a difference of vacancy density of metal constituting an active layer.
As a result, the single element that is a purpose of the present disclosure satisfies the condition for securing a voluntary compliance current characteristic, a voluntary current rectification characteristic, and a voluntary multi-level storage characteristic.
For this reason, the electrical conductivity is different and a charge carrier density is different between the first active layer 200 and the second active layer 300, so a set driving voltage is different. However, since the substances are the same, a reset driving voltage is the same or has a similar range.
Further, the first active layer 200 or the second active layer 300 can show a voluntary rectification characteristic, depending on the arrangement and the voltage that is applied. Referring to (b) of
The rectification characteristic prevents backflow of a current in a single polarity-driven resistive switching memory device, so it is possible to solve the problem of cross-talk that is generated between adjacent cells when a cross point array is formed.
As a result, the resistive switching memory device (RRAM) of the present disclosure solves the problem that is generated when a cross point array is formed even without help of an external device, so there is an advantage that it is possible to achieve high-integration memory and an accurate data program is possible without an error because there is no cell intervention.
Next, the driving characteristic of the resistive switching memory device of the present disclosure is described.
A set driving voltage difference of the first active layer 200 and the second active layer 300 may cause: (a) a first resistance state in which a first positive voltage is applied between the upper electrode 400 and the lower electrode 100, so the first active layer 200 is set into a low-resistance state; (b) a second resistance state in which a second positive voltage is applied between the upper electrode 400 and the lower electrode 100, so the first active layer 200 and the second active layer 300 are set into a low-resistance state; and (c) a third resistance state in which a third positive voltage is applied between the upper electrode 400 and the lower electrode 100, so the first active layer 200 and the second active layer 300 are reset into a high-resistance state. Accordingly, it is possible to achieve a multi-level using a single device, so it is possible to greatly improve the storage capacity of a memory device while maintaining high integration and high-speed driving characteristics.
In an embodiment of the present disclosure, the active layers may be formed as two or more layers by the mechanism described above.
In detail, it is possible to form a plurality of set voltage values by forming a plurality of layers and varying the voltages at which each layers are formed, and accordingly, the resistive switching memory device that is the present disclosure can show a first resistance state to a third resistance state or more that are achieved by dual active layers. As a result, it is possible to achieve a high-capacity memory using a single device.
Hereafter, a method of manufacturing the resistive switching memory device described above is described with reference to drawings. In the following description, the configuration repeated in the resistive switching memory device described above should be construed in the same manner and repeated description is omitted.
Referring to
The first active layer 200 and the second active layer 300 are characterized in that they are made of the same substance but the process condition of the electrochemical deposition is different.
The amorphous metal oxide-based first active layer 200 and the amorphous metal oxide-based first active layer 200 may include amorphous metal oxide nanoparticles in an amorphous matrix.
In an embodiment of the present disclosure, the forming of a first active layer 200 in step (i) includes forming the first active layer 200 on the lower electrode 100 by electrochemical deposition.
The electrochemical deposition, in detail, includes: immersing the lower electrode 100 into a solution including a metal oxide and a metal surfactant; and applying a voltage to form the first active layer 200.
The metal oxide in step (i) is a metal oxide that can be used for the electrochemical deposition proposed in the present disclosure, and all metal oxides that are produced by bonding of hydroxyl ions and metal ions may correspond to the metal oxide.
For example, the metal oxide described above may include one or more selected from a group composed of CuO, Cu2O, Al2O3, Nb2OS, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, CosO4, Fe2O3, AgzO3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
The surfactant in step (i) is a substance that can induce electrochemical growth, and may include at least one or more metals of Sb, Ni, Cr, Pb, Co, or Mn, but is not limited thereto.
In an embodiment of the present disclosure, the forming of a second active layer 300 in step (ii) includes forming the second active layer 300 on the first active layer 200 by electrochemical deposition.
The electrochemical deposition, in detail, includes: immersing the lower electrode 100 into a solution including a metal oxide and a metal surfactant; and applying a voltage to form the second active layer 300.
The metal oxide in step (ii) is a metal oxide that can be used for the electrochemical deposition proposed in the present disclosure, and all metal oxides that are produced by bonding of hydroxyl ions and metal ions may correspond to the metal oxide.
For example, the metal oxide described above may include one or more selected from a group composed of CuO, Cu2O, Al2O3, Nb2O5, NiO, MgO, TiO2, ZrO2, Nb:SrTiO3, Cr:SrTiO3, Cr:SrZrO3, ZnO, Co3O4, Fe2O3, Ag2O3, Bi2O3, Sb2O3, PbO2, RuO2, MnO2, Cr2O3, and a combination thereof.
The surfactant in step (ii) is a substance that can induce electrochemical growth, and may include at least one or more metals of Sb, Ni, Cr, Pb, Co, or Mn, but is not limited thereto.
In an embodiment of the present disclosure, the electrochemical deposition in step (i) may be performed under the condition that a voltage of 0.37V is applied, and in this case, the first active layer 200 has the lowest conductivity of thin films having a structure in which crystalline nanoparticles are bonded to an amorphous matrix. The electrochemical deposition in step (ii) may be performed under the condition that a voltage of 0.50V is applied, and in this case, the second active layer 300 has the highest conductivity of thin films having a structure in which crystalline nanoparticles are bonded to an amorphous matrix.
In detail, in the electrochemical deposition, variation of the application voltage affects supply of metal and OH (hydroxyl ion), thereby affecting the ratio of the amorphous matrix and the crystalline nanoparticles of an active layer. In general, when an applied voltage increases, the quantity of metal increases, so conductivity increases.
Accordingly, it is possible to form thin films with different electrical characteristics using the same metal oxide by electrochemical deposition with different application voltages.
Hereafter, a resistive switching memory device array including the resistive switching memory device is described with reference to drawings. In the following description, the configuration repeated in the resistive switching memory device described above should be construed in the same manner and repeated description is omitted.
Referring to
In this case, the first active layer 200 and the second active layer 300 may be made of the same substance but different in electrical characteristic.
The amorphous metal oxide-based first active layer 200 and the amorphous metal oxide-based second active layer 300 may include amorphous metal oxide nanoparticles in an amorphous matrix.
In an embodiment of the present disclosure, the amorphous metal oxide is formed between the first electrode and the second electrode, thereby forming a cross point array. As described above, since the resistive switching memory device of the present disclosure has multi-level implementation and storage, a voluntary rectification characteristic, and a voluntary limit current formation characteristic even without an external device, it is possible to form a high-integration cross point array. As a result, it is possible to provide a resistive switching memory device array that has high capacity and can be driven at a high speed.
Experiment of a Cu2O Crystal Characteristic and an Electrical Characteristic According to an Application Voltage in Electrochemical Deposition
This experiment example is described with reference to
In
This experiment is an experiment of measuring crystallinity and current density of an active layer formed while a voltage was changed from Vi to Vvi when forming the active layer using Cu2O as a metal oxide by electrochemical deposition.
According to (a) of
Referring to the regions, when an applied voltage is Vi˜Viii (ED@Vx) or less, Cu2O(C—Cu2O) having crystallinity grows and crystallinity gets dense with an increase of a voltage. It is shown that crystalline Cu2O nanoparticles simultaneously grow in an amorphous Cu2O matrix at ED@Viii˜Vvi with reference to ED@Viii that is a breakpoint such that as the voltage increases, the Cu2O nanoparticles get dense and the density increases.
According to (b) of
Accordingly, as proposed by the method of manufacturing a resistive switching memory device that is the present disclosure, it was found that it is possible to change an electrical characteristic even in active layers that were deposited using the same substance by changing a voltage condition.
Further, in order to form an amorphous active layer in which crystalline nanoparticles are distributed on an amorphous active layer using Cu2O to achieve the effects of the present disclosure, it can be seen that it is required to adjust a voltage condition within the range of ED@Viii˜Vvi(−0.37V to −0.52V), and particularly, it is preferable to configure Viii and Vvi, which are most greatly different, as the first active layer and the second active layer in order to clearly discriminate a multi-level.
Experiment of Analyzing Electrical Characteristic of Crystalline/Amorphous Active Layers Under Different Voltage Conditions
This experiment example is described with reference to
In
Referring to (a) of
Referring to (b) of
That is, ED@Vi˜Vii showed that the resistance is higher as the electrochemical growth voltage is higher, and ED@Viii˜Vvi showed that the resistance is lower as the electrochemical growth voltage is higher. Accordingly, they show opposite tendencies.
Experiment of Measuring Current Characteristic Over Time During Electrochemical Growth
This experiment example is described with reference to
In
According to
According to (a) of
According to (b) of
Experiment of Checking Crystallinity of Thin Film Under Different Voltage Condition for Electrochemical Growth
This experiment example is described with reference to
According to (a) of
According to (b) of
Experiment of Measuring Resistance Variation of Resistive Switching Memory Device
This experiment example is described with reference to
Referring to
Referring to (a) and (b) of
According to (c) to (f) of
Further, it can be seen that since the higher the thin film deposition voltage, the higher the charge carrier concentration and the electrical conductivity in ED@Viii˜Vvi, a small amount of energy is required for set driving, so it is driven in a low voltage region.
Experiment of Measuring LRS and HRS Behavior of Amorphous Thin Films Under Different Voltage Condition for Electrochemical Growth
This experiment example is described with reference to
In this experiment, resistance values of an LRS and HRS according to electrode sizes from 25 μm2 and 40000 μm2 were measured in order to specify a resistance variation type of ED@Viii˜Vvi thin films. In this case, if a resistance value is affected by an electrode size, it is an interface resistance variation type, and if not so, it is a filament resistance variation type.
According to
Experiment of Checking Multi-Level Characteristic, Voluntary Rectification Characteristic, and Voluntary Limit Current Characteristic of Resistive Switching Memory Device
This experiment example is described with reference to
In this experiment, a stacked active layer was configured by selecting an ED@Viii thin film and an ED@Vvi thin film. In detail, an ED@Viii thin film was stacked on an ITO substrate and then an ED@Vvi thin film was sequentially stacked. Thereafter, a Pt upper electrode was deposited.
The two thin films both have the same structural characteristic, forming-free characteristic, and filament resistance variation characteristic on the basis of an amorphous grid, but they are different in set driving voltage due to a difference of an electrical characteristic.
According to (a) of
According to (b) of
That is, in
Experiment of Measuring Resistance of 4×4 Cross Array
This experiment example is described with reference to
In
In this experiment, a 4×4 crossbar array was configured, an LRS or HRS state was stored individually for sixteen devices, and then a resistance value of each of the devices was measured using a line electrode of the array in order to check whether a dual active resistive switching memory device device can be individually driven and can transmit accurate data in the level of an array.
In
According to (a) of
According to (b) of
According to the result, since the dual active layer resistive switching memory device device of the present disclosure has a voluntary compliance current limit function and a voluntary current rectification function, so the device can transmit accurate information without help of an external device even in the level of an array.
The present disclosure having the above configuration has an effect that since active layers are formed in dual amorphous layers made of the same material, it is possible to resolve the problem of adjustment of grain boundaries and non-uniformity and instability of a device due to the problem, whereby it is possible to produce a resistive switching memory device that has a controllable stable electrical characteristic and a large area.
Further, according to the configuration, since a forming voltage is not formed between active layers and the driving voltages and the filament mechanisms are the same, it is possible to provide a voluntary compliance current limit and voluntary current rectification characteristics through a single device without help of external device.
As a result, it is possible to implement a memory, which is driven with only an active layer characteristic without help of external device, as a nonvolatile super high-speed memory, integration of the memory is greatly improved, and the problem of cross talk is solved without help of an external device when an array is formed, whereby it is possible to implement a memory that provides accurate information without an error in data.
Further, since different electrical characteristics are implemented by applying different voltage conditions when depositing the dual active layers by electrochemical deposition, a resistive switching memory device that can be driven at a multi-level is provided. As a result, it is possible to considerably increase the capacity of a memory while maintaining high integration and super high driving characteristics.
The effects of the present invention are not limited thereto and it should be understood that the effects include all effects that can be inferred from the configuration of the present disclosure described in the following specification or claims.
The above description is provided as an exemplary embodiment of the present disclosure and it should be understood that the present disclosure may be easily modified in other various ways without changing the spirit or the necessary features of the present disclosure by those skilled in the art. Therefore, the embodiments described above are only examples and should not be construed as being limitative in all respects. For example, the components described as single parts may be divided and the components described as separate parts may be integrated.
The scope of the present disclosure is defined by the following claims, and all of changes and modifications obtained from the meaning and range of claims and equivalent concepts should be construed as being included in the scope of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2021-0128776 | Sep 2021 | KR | national |