This application is a national phase of International Application No. PCT/US2006/000738 filed Jan. 10, 2006 and published in the English language, and claims priority to BR PI0500848-4 filed Jan. 10, 2005.
This invention relates generally to a retroreflective film and, more particularly, to a retroreflective film that can be used in an article (e.g., a license plate) having a substrate with an embossed, stamped, pressed, or otherwise irregular surface profile.
A retroreflective film can be used in many articles, such as license plates, highway signs, safety signs, and other retroreflecting items. In many of these applications, it is important that the film be not only reflective, but capable of accommodating a stamped, embossed, pressed or otherwise irregular substrate surface. For example, a license plate typically comprises a relatively flat substrate (e.g., an aluminum plate) that is stamped, embossed, pressed, or otherwise cold-work deformed to provide raised areas corresponding to alphanumerical characters and/or other indicia. When a retroreflective film is used in a license plate, it is laminated to the substrate when it is still flat (e.g., prior to stamping, embossing or pressing) whereby the retroreflective film must be able to accommodate the cold-work deforming step.
The present invention provides a retroreflective film that can accommodate a cold-work deformation step (e.g., a stamping, embossing, or pressing step) when adhered to a substrate. As such, the film can be incorporated into a retroreflective article (e.g. a license plate) wherein a substrate is cold-worked to form raised areas corresponding to alphanumeric characters and/or other indica. The retroreflective film incorporates a prismatic layer thereby allowing a wider range of design flexibility when devising a particular retroreflective product and/or thereby providing high retroreflective capabilities.
The present invention also provides a retroreflective article (e.g., a license plate) wherein the substrate has a visible light transmission of less than 30% and/or wherein a layer of the retroreflective film has a visible light transmission of less than 30%. For example, the substrate can comprise an aluminum plate which is essentially opaque. Additionally or alternatively, the film can include a reflective layer (e.g., a metallized layer) in back of its prismatic layer which has a low visible light transmission. In either case, the loss of light through the rear of the article is prevented thereby helping to maximize retroreflectivity.
These and other features of the invention are fully described and particularly pointed out in the claims. The following description and drawings set forth in detail a certain illustrative embodiment of the invention which is indicative of but one of the various ways in which the principles of the invention may be employed.
Referring now to the drawings, and initially to
The front surface (i.e., the surface facing the observer) of the flat background-forming area 12 is retroreflective to enhance the visibility of the license plate 10. Paint 16 (and/or another covering) can be applied to the raised indicia-forming areas 14 to render them non-reflective. The background and the indicia (e.g., the paint 16) can be the same color, but in most cases will be different colors to increase the notice-ability of the indicia.
As is best seen by referring additionally to
The raised areas 24 and 34 can be simultaneously formed to thereby form the indicia-forming areas 14 in the license plate 10. For example, the substrate 20 (without raised areas 24) and the retroreflective film 30 (without raised areas 34) can be complied so that the front surface of the substrate 20 is adhered to the rear surface of the retroreflective film 30. The substrate/film compilation 20/30 can then be stamped, embossed, pressed or otherwise cold-work deformed to produce the raised areas 24/34.
The substrate 20 should be made of a material, and should have a thickness and/or tensile strength, to accommodate the desired deformation (i.e., indicia-forming) method. For example, the substrate 20 can be made of a metal or a plastic, with a soft metal (e.g., aluminum, copper, silver, gold) with good drawing properties often being preferable. The substrate 20 can have a thickness in the range of 0.05 mm to 5 mm if it is metal. The substrate 20 can be made of an essentially opaque material, that is neither transparent nor translucent, and/or a material that has a visible light transmission of less than 30%, less than 25%, less than 20%, and/or less than 10%. In the illustrated embodiment, the substrate 20 can be a thin (e.g., 2 mm or less) aluminum plate which is essentially completely opaque.
According to the present invention, the retroreflective film 30 is constructed to accommodate the forming of its raised areas 34 (e.g., the indicia-forming areas). Specifically, the film 30 should be capable of withstanding the desired deformation method (i.e., stamping, embossing, pressing). To this end, the retroreflective film 30 has an elongation of at least 20%, preferably at least 40%, and more preferably at least 50%, at least 60%, and/or at least 70%. In fact, the retroreflective film 30 of the present invention can be designed to have an elongation in excess of 100%. Elongation refers to the extent that the film can be stretched in one or more dimensions without breaking and its “elongation” is the point of this breakage.
The construction of the retroreflective film 30 is shown in more detail in
The cover layer 40 is constructed to protect the integrity of the other layers (and particularly the prismatic layer 42) against weather, abrasion, peeling, high temperature, and/or rain acidity. In the illustrated embodiment, the paint 16 is applied to the cover layer 40 whereby this compatibility should be taken into consideration when selecting the cover layer 40 and/or the paint 16. The cover layer 40 can made from a thermoplastic resin and/or a thermoplastic polymer, such as vinyl or polyurethane. If the cover layer 40 is, for example, calendar vinyl, it can have a thickness of greater than 150 μm (about 6 mil), greater than 180 μm (about 7 mil), greater than 200 μm (about 8 mil), greater than 230 μm (about 9 mil), greater than 250 μm (about 10 mil), or at least 300 μm (about 12 mil). If the cover layer 40 is, for example, cast vinyl, it can have a thickness as low as 30 μm (about 1.2 mil). A cover coating (not shown) can be placed over the cover layer 40 for protection or other purposes. The cover layer 40 can incorporate a color pigment to result in a transparent color (e.g., yellow, red, blue, green, brown, orange, etc.).
The prismatic layer 42 has a plurality of retroreflective elements 60 embossed, casted, molded, or otherwise formed thereon. As is best seen by referring briefly to
The prismatic layer 42 can incorporate a color pigment resulting in a transparent color. This incorporation can be in addition to, or as an alternative to, the cover layer 40 including a color pigment. If both the layer 40 and the layer 42 incorporate a color pigment, it will usually be the same color, however, the use of two different pigments is certainly possible.
Typically, the prismatic layer 42 is formed from a sheet material having first and second flat surfaces. The retroreflective elements 60 are formed by embossing, casting, or molding in the first surface of the sheet material and the elements 60 extend into the sheet material a certain depth. Thus, the prismatic layer 42 is made of a material which is compatible with the element-forming method (e.g., embossing, casting, molding) and which is transparent/translucent (and preferably highly transparent). Suitable materials include, for example, acrylic or polycarbonate. A is best seen by referring briefly to
The sublayer 64 of the prismatic layer 42 can have a thickness tsublayer of less than 55 μm (about 2.17 mils), less than 50 μm (about 1.97 mils), less than 45 μm (about 1.77 mils), less than 40 μm (about 1.57 mils), less than 35 μm (about 1.37 mils), less than 30 μm (about 1.18 mils), and/or less than 25 μm (about 0.97 mils). The retroreflective elements 60 can have a height helements of greater than 35 μm (about 1.4 mils), greater than 75 μm (about 3 mils), greater than 100 μm (about 4 mils), greater than 150 μm (about 6 mils), greater than 200 μm (about 8 mils), and/or greater than 250 μm (about 10 mils). If the retroreflective elements 60 have a height helements of less than 115 μm (about 4.5 mils), the best elongation features may be obtained by the thickness tsublayer being between 50 μm (about 2 mils) and 25 μm (about 1 mil). If the retroreflective elements 60 have a height helements of greater than 115 μm (about 4.5 mils), the best elongation features may be obtained by the thickness tsublayer being less than 25 μm (about 1 mil).
As is best seen by referring briefly to
The reflective layer 44 can comprise a layer of reflective metal (e.g., silver, aluminum, gold, copper) vapor-deposited or otherwise applied over the exposed surfaces of the cube corner elements 60. The layer 44 can alternatively comprise a binder layer in which flakes of reflective metal are embedded. If the metal has a grayish color, and the cover layer 40 and the prismatic layer 42 are clear (e.g., white), the film 30 will sometimes be referred to as “gray.”
The thickness of the reflective layer 44 will usually be significantly smaller than the prismatic layer 42 (although is it somewhat exaggerated in the drawing for the purposes of illustration). For example, the layer 44 can have a thickness in the range of 0.02 μm (about 0.0008 mils) to 0.125 μm (about 0.005 mils). The reflective layer 44 can be essentially opaque (i.e., neither transparent nor translucent) and/or it can have a visible light transmission of less than 30%, less than 25%, less than 20%, and/or less than 10%.
The adhesive layer 46 can comprise an acrylic-based adhesive or an emulsion-based adhesive. The adhesive can be heat-activated, solvent-activated, or pressure-sensitive (which is often preferred). The adhesive can be permanent (i.e., attached medium cannot be removed without noticeable damage) and/or removeable (but will usually be permanent in a license plate situation). In any event, the layer 46 serves the functional purpose of adhering the film 30 to the substrate 20. However, other substrate-adhering techniques are possible with, and contemplated by, the present invention. For example, the substrate 20 could include an adhesive layer on its front surface for film-adhering purposes, or an adhesive could be applied at the location whereat the substrate-film adhering step is performed. Moreover, non-adhesive techniques, such as heat bonding or mechanical attaching, could be used to adhere the film 30 to the substrate 20. In these instances, the film 30 would not have to include the adhesive layer 46 (although another space-filling medium may sometimes be necessary).
The release liner 48 can comprise a carrier web (e.g., paper or polyester) coated with a release agent (e.g., polyethylene or silicone). The function of the release liner 48 is to cover the adhesive layer 46 until the substrate-film adhering step is performed during the assembly of the article 10 and/or to act as a carrier layer during formation of the adhesive layer 46. In either event, if the film 30 does not include an adhesive layer 46, it probably need not include the release liner 48. Additionally, if the adhesive layer 46 is such that pre-assembly protection and/or a carrying medium is not necessary, the release liner 48 could be omitted from the film's construction. In any event, if film 30 does include the release liner 48, it will typically be removed prior to the film's incorporation into the retroreflective article 10.
The retroreflective article 10 and/or the retroreflective film 30 according to the present invention can achieve high retroreflectivity (measured in, for example, in units of candela per lux-meters squared −cd/lux-m2) when compared to films having a micro-lens (and/or beaded) layer instead of a prismatic layer. Specifically, for example, at an observation angle of 0.1° and an entrance angle of −4°, retroreflectivity in the range of 250 cd/lux-m2 can be obtained; at an observation and at an entrance angle of 30° retroreflectivity in the range of 180 cd/lux-m2 can be obtained. At an observation angle of 0.2°, and entrance angles at −4° and 30°, retroreflectivity in the range of 200 cd/lux-m2 and 150 cd/lux-m2, respectively can be obtained. At an observation angle of 0.5°, and entrance angles at −4° and 30°, retroreflectivity in the range of 95 cd/lux-m2 and 65 cd/lux-m2, respectively can be obtained. As is shown schematically in
One may now appreciate that the present invention provides a retroreflective film 30 that can accommodate a cold-work deformation step when adhered to a substrate 20. As such, the film 30 is especially amendable to license plate production. That being said, the retroreflective film 30 of the present invention can be used with other sized/shaped substrates to make, for example, signs (e.g., traffic, warning, regulation, address, service, general identification), safety devices (e.g., conex, lane dividers, lane markers, channel funnels) and other items. In fact, the retroreflective film 30 may also find application in substrate-less situations, especially if the relevant surface (e.g., the road, the wall, the track, the vehicle part, etc) has an irregular profile.
Although the invention has been shown and described with respect to a certain preferred embodiment, it is obvious that equivalent and obvious alterations and modifications will occur to others skilled in the art upon the reading and understanding of this specification. The present invention includes all such alterations and modifications and is limited only by the scope of the following claims.
Number | Date | Country | Kind |
---|---|---|---|
0500848 | Jan 2005 | BR | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/US2006/000738 | 1/10/2006 | WO | 00 | 6/19/2007 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2006/076320 | 7/20/2006 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
2587325 | Husted | Feb 1952 | A |
3973342 | Gubela | Aug 1976 | A |
4983436 | Bailey et al. | Jan 1991 | A |
5227194 | De La Sierra E. | Jul 1993 | A |
5812316 | Ochi et al. | Sep 1998 | A |
6083607 | Mimura et al. | Jul 2000 | A |
6470610 | Northey | Oct 2002 | B1 |
6531212 | Owusu et al. | Mar 2003 | B2 |
Number | Date | Country |
---|---|---|
20316349 | Dec 2003 | DE |
2002090516 | Mar 2002 | JP |
85004448 | Oct 2006 | MU |
9526281 | Oct 1995 | WO |
Entry |
---|
PCT/US2006/000738; PCT International Search Report mailed Jun. 28, 2006. |
Translation of MU 85004448. |
Number | Date | Country | |
---|---|---|---|
20080092418 A1 | Apr 2008 | US |