Rigid extrusion profiles of chlorinated polyvinyl chloride polymer blends having improved surface properties and method of manufacture

Abstract

Blends of chlorinated polyvinyl chloride and chlorinated polyethylene and methods for preparing extruded profiles such as a window spacer, a glazing bead, a window lineal, and a track for lighting, having smooth surface characteristics are disclosed. The blends comprise 100 weight parts CPVC containing from 62% to 72% chlorine, preferably 65% to 71% chlorine and from 10 to 30 weight parts, preferably 15 to 25 parts of chlorinated polyethylene containing from 25 to 45% chlorine and extruding the blend. The preferred embodiments of the invention are further defined by a particular combination for the chlorine content of CPVC, the real weight average molecular weight of CPE (M.sub.w) and polydispersity (M.sub.w /M.sub.n), defined as the ratio of the weight average to number average molecular weight, and extrusion shear rate.

Description

FIELD OF THE INVENTION

This invention pertains to blends of post-chlorinated polyvinyl chloride (CPVC) and chlorinated polyethylene (CPE), and methods for making extruded rigid profiles from the blends and exhibiting smooth satin surface appearance.

BACKGROUND OF THE INVENTION

Combinations of polyvinyl chloride and chlorinated polyethylene are established in the art, for example, flexible wire and cable cladding. Blends of PVC and chlorinated polyethylene are recognized as contributing both impact modifying characteristics as well as ease of melt processing. Chlorinated polyethylene is not particularly efficient when utilized as the sole impact modifier with PVC, hence an amount needed to boost notched Izod Impact strength to at least about 10 lb.-ft./inch notch will lead to appreciable loss in rigidity, measured as tensile of flexural modulus.

There have been suggested graft copolymers of chlorinated polyethylene and PVC. Ludwig Beer, in 1962 suggested in U.S. Pat. No. 3,268,623 that improvements in properties could be obtained by dissolving CPE in vinyl chloride monomer and suspension polymerizing to yield an improved combination compared to mechanical blending of the two resins.

In U.S. Pat. No. 4,481,333 Fleisher et al. disclosed the combination of PVC, CPE, and fluoropolymer. There it was taught that if prior to combining with PVC, fluoropolymer and CPE are first combined, a 10-fold lesser quantity of fluoropolymer (PTFE) provided the same magnitude of reduction in extruder torque compared to a ternary mixture.

Hankey disclosed in Canadian Patent No. 636,534 that on the addition of 19 weight parts of CPE "per 100 weight parts of PVC" (phr), room temperature notched Izod impact strength improved to 24 ft.-lb./inch notch. Hankey showed that at this level of CPE, the flexural modulus of PVC was lowered from 400,000 psi to 270,000 psi, while in a combination 5 parts of CPE, 5 parts of a rubbery diene type polymeric impact modifier and 90 parts of PVC, room temperature notched Izod impact was comparable but rigidity was not sacrificed to the same degree. The samples demonstrated were milled and compression molded, with no teaching to extrusion characteristics.

Frey and Klug disclosed in U.S. Pat. No. 3,940,456 that extruded PVC blends with chlorinated high pressure polyethylene may, in certain instances, exhibit coarseness, i.e., rough extrusion characteristics. They proposed to solve this problem by employing a CPE which had been chlorinated in the presence of a finely-divided silicic acid and siloxane oil. The CPE described was of high molecular weight characterized by a specific viscosity and methylcyclohexane swell. The swell number indicated the "through" chlorination, i.e., the degree to which all chains were chlorinated.

Klug and Frey disclosed in U.S. Pat. No. 4,280,940 the combination of PVC and two CPE's to provide improved transparency for weatherable blends. They noted that the incorporation of CPE with methylcyclohexane (MCH) swell of more than 10% lead to reduced transparency. Klug and Frey also noted that the combination of CPE and PVC with K value 70 is difficult and can lead to rough extrudate. They proposed a combination of PVC (K=55-65) and two CPE's, one having a low MCH swell, and both containing 37-42% chlorine.

With respect to CPVC/CPE blends, Jennings and Kliner of the B. F. Goodrich Co. disclosed in U.S. Pat. No 3,299,182 the combination of impact improvement and processing enhancement of CPVC with small amounts of homogeneously chlorinated low pressure, high density polyethylene at usage levels of from 2 to 10 phr. Processing aids, plasticizers and impact modifiers were preferably avoided. The examples illustrated a variety of chlorinated polyethylene base polymers combined at 5 parts per 100 parts CPVC (phr), the CPVC having a density of 1.57 g/cc, corresponding to a chlorine content of about 66%. CPE and CPVC were precipitated from cements, dried, milled and pressed for determination of heat distortion temperature (HDT) and IZOD impact strength. The CPE chlorine content from 30-40% was preferred and impact strength was maximized using most types of base polyethylene having about 35% chlorine content. Exceptions to this trend occurred with a copolymer of ethylene and butene having a relatively high melt index. The preferred Zeigler type polyethylenes chlorinated to about 30-32% always gave higher impact strength than those with higher chlorine content. It was noted that extrusion speed and appearance of the extrudate was best at 7 phr CPE, while at 10 phr and higher, chemical resistance and HDT were detrimentally altered.

Dreyfuss and Tucker also of the BFGoodrich Company disclosed in U.S. Pat. No. 3,453,347 that enhanced melt flow rate and processing stability of CPVC/CPE blends can be obtained by the addition of 0.25 to 2.5 phr of rubbery amorphous polyalkylene mono-epoxide. One aspect of the '347 patent was to obtain a combination of HDT and impact resistance with from 5 to 10 phr CPE. A small effective amount, on the order of 1 to 2 phr of the amorphous rubbery epoxide imparted higher melt flow rates. The working examples were prepared by milling and compression molding, while melt flow rate was measured by a small extrusion rheometer. The best melt flow rate/HDT/impact strength balance was observed at CPE use levels of 7.75 phr.

Buning, et al have taught in U.S. Pat. No. 3,459,692 that due to the higher crystallinity of stereo-regular CPVC and the tendency of a cooling melt to re-crystallize, molded articles from a blend of CPE and stereo-regular CPVC are more brittle than blends with atactic CPVC. They found that milled, pressed sheets of a blend of CPE and CPVC, where the CPVC was derived from 55 to 85% syndiotactic PVC were shown to exhibit toughness, no re-crystallization tendency and had higher corresponding Vicat softening temperatures than with the atactic CPVC blend.

More recently, G. Wear in U.S. Pat. No. 4,213,891 disclosed the use of a combination of high and low molecular weight chlorinated polyethylene with CPVC for calendared sheets having improved thermoforming characteristics. Another object of Wear was the use of PVC/acrylate based impact modifier for compounds with reduced smoke emission. CPVC having 66% chlorine was combined with 15 phr CPE (36% Cl and m.w. greater than 1,000,000) and 7.5 phr CPE (22% Cl and mw less than 100,000). The blend was fluxed on a Banbury/mill then fed into a calendar stack to produce a uniform 0.010-0.017 inch sheet.

There have been found no detailed published reports systematically studying the extrusion characteristics of CPVC/CPE blends in which CPE is present above 10 phr. Blends of PVC and CPE exhibit more consistent melt characteristics than blends of post-chlorinated PVC and CPE. Although at low levels of 1 to 5 phr, CPE imparts improved impact strength and processibility under low shear extrusion, the behavior of extrudates containing more than 10 phr CPE under higher shear conditions is different. The differences with PVC can not be extrapolated to CPVC blends. Good processibility suggests lower viscosity, torque and work input, hence processing stability, however this does take account of the variations in extrusion quality observed over varied conditions, varying chlorination level or molecular weight of CPE and CPVC.

Compared to PVC, chlorinated PVC exhibits higher density, higher Tg, improved resistance to solvent and chemical attack, requires higher extrusion temperature with greater susceptibility to degradation, higher melt viscosity and brittleness, these properties vary with different chlorine content of CPVC. The heat distortion temperature for homo-PVC is about 75.degree. C. whereas it is 80.degree. C. to 180.degree. C. for chlorinated PVC, and is proportionate with chlorine content. Likewise, Vicat softening point for PVC is at least about 30.degree. C. lower for chlorinated PVC. As the temperature of processing increases with CPVC chlorine content, blend morphology with CPE varies.

As illustrated below relatively 63-65% chlorine content CPVC is observed to behave differently with CPE than CPVC with relatively high chlorine content due in part to changing morphology with temperature. Whereas homo-PVC has a characteristic viscosity range for given molecular weight, its structure is uniform, made up of repeating units having the following structure: ##STR1## whereas chlorinated PVC is a combination of three structures, one of which corresponds to the repeating unit of PVC (I), and two other repeating unit types: ##STR2## The proportion of structures I, II and III for CPVC varies with chlorine content, the higher the chlorine content the higher proportion of structures II and III and the lesser proportion of structure I. Correlation between chlorine content and proportion of structures I, II and III in non post-chlorinated and chlorinated PVC is set forth in Table A below:

TABLE A______________________________________ % Chlorine Structure Content (I) (II) (III)______________________________________PVC 56.6 100 0 0CPVC 57.5 97.2 2.8 0" 61.2 81.1 17.5 1.4" 63.2 71.1 26.8 2.1" 69.5 31.1 49.9 19.0" 72.6 5.5 60.5 34.0______________________________________

On the basis of Table A, chlorinated PVC with a chlorine content of about 61% contains about 80% of structure I that corresponds to non post-chlorinated PVC, about 17% of structure II, and about 1% of structure III whereas at 72% chlorine content, chlorinated PVC contains about 5% of structure I, more than 60% of structure II, and more than 35% of structure III. Thus, there is no simple extrapolation of properties obtained in blends of PVC and CPE to blends of CPVC and CPE.

DIFFERENTIAL SCANNING CALORIMETRY

In the following table CPVC, tin stabilizer and chlorinated low molecular weight polyethylene was evaluated using differential scanning calorimetry method to confirm that two distinct phases exist for this blend:

______________________________________Sample phr CPE Tg CPE .degree.C. Tg CPVC .degree.C.______________________________________CPE (35% Cl.) neat -12.9 --*CPVC 68.5% CL -- -- 143.0" 10 -16.5 132.9" 15 -18.6 132.8" 20 -18.7 132.7" 25 -16.9 132.5______________________________________ *no tin stabilizer present

By way of this method it is evident that with 68.5% chlorine CPVC a non-miscible two-phase blend exists with no shift in the glass transition temperature of either polymer beyond the plasticization effect of the tin stabilizer present.

Scanning electron microscopic observation of cross sections of extruded blends also confirms that at a discrete dispersed CPE domain exists and has a domain size of one micron and smaller. There are significant differences in extrudability observed across blends of CPVC/CPE with Varying molecular weights and chlorine levels of each. The varying quality of extrudate is unexplained by any general theory. It has also been observed that a specific blend may extrude well within a certain range of shear rate, for instance, 100-500 sec.sup.-1 yet when one increases the output rate, the extrusion undergoes melt fracture, giving a rough surface appearance.

The prior art recognizes that chlorinated polyethylene can be combined with CPVC in small amounts less that 10 phr to obtain processing improvements. The art also teaches the combination of PVC and lower amounts of chlorinated polyethylene with a core/shell impact modifier to obtain impact strength with less loss in HDT.

The prior art recognizes the maximum impact strength improvement for CPVC with CPE containing 30-32% chlorine, and that good appearance and extrusion speed are obtained when the CPE is present at about 7 phr.

It has been observed that as the chlorine content of CPVC is increased, the extrusion processing window for combination with CPE changes considerably. The incidence of rough extrusion occurs with increasing frequency using a variety of differently chlorinated polyethylenes of varying molecular weight as one increases the chlorine content of CPVC.

While it would be desirable to utilize CPVC containing at least 65% by weight chlorine for its high HDT, the limited processing window with CPE presents a problem in obtaining smooth extrudates under Varied processing shear conditions. The inclusion of conventional core/shell impact modifier with CPE, as suggested by Hankey for PVC, did not achieve an improvement in surface smoothness. Also, it was been observed that the appearance of extruded profiles from CPVC containing conventional core/shell impact modifier alone exhibits less desirable gloss and tactile characteristics.

Among the published art, there has been little disclosure of the use of CPE with CPVC for rigid profile extrusion of appearance articles such as window spacers, gaskets, glazing beads, window lineals, track lights, and the like. The designs used in commercial applications often require intricate cross-section shapes for profiles and the localized shear forces at the interface of the die and extrudate may vary widely as with the part geometry. Such rigid profiles having varied geometry formed in extruders under relatively high shear rates, exhibit more sensitivity towards melt fracture loss of shape and/or waviness.

It would thus be desirable to obtain the smooth extrudate surface and tactile characteristics under with high extrusion output rates. It would also be desirable to achieve high output rates for extruded profiles having any intricate cross-sectional shape while also maintaining dimensional stability and low percent die swell.

In a systematic study of immiscible but mechanically compatible CPVC/CPE blends, extrusions were obtained under varying processing conditions. With the use of rheological equations for Newtonian fluids, the apparent viscosity of non-Newtonian rod shaped extrudate was used with quantified output to calculate the instantaneous shear rate of the extrudate independent of shape. The surface characteristics under each condition were visually rated and compared. The general equations used for a rod-shaped die, are:

S.sub.D =9.8.times.10.sup.-3 Q/p r.sup.3 and P=2.9.times.10.sup.-5 S.sub.D VL/r wherein: S.sub.D =shear rate, s.sup.-1 Q=flow rate, lb./hr. p=melt density, g/cc r=radius, in inches P=pressure, psi L=land length, in inches and V=viscosity in poise.

In studies with a small extruder equipped with a 0.046 inch rod die, under varying conditions, there were found particular combinations of CPVC and CPE types extruded under particular conditions that exhibited excellent appearance characteristics and low die swell.

SUMMARY OF THE INVENTION

An object of the present invention is to provide specified blends for rigid profile extrusion of appearance parts such as window spacers, glazing beads, window lineals, and track lights, having smooth surface characteristics. The object is achieved by a method of extruding blends in a specified range of shear rate generally from about 100 sec.sup.-1 to about 4,000 sec.sup.-1, the blends comprising 100 weight parts of CPVC having an I.V. of the precursor PVC of from about 0.4 to about 1.6, preferably 0.5 to 1.2 and most preferably from 0.7 to 1.0, and a CPVC chlorine content of from 62% to 72%, preferably greater than 65% up to 71%, in combination with from about 10 phr to about 30 phr of a single chlorinated polyethylene.

Another object of the invention is defined by a method of preparing an extruded profile from a blend comprising 100 weight parts CPVC containing from 62% to 72%, preferably greater than 65% up to 71% chlorine and 10 to 30 weight parts chlorinated polyethylene containing from 25% to 45% chlorine and extruding the blend in a specified range of shear rate depending on the specific CPVC and CPE present. The preferred embodiments of the invention are further defined by the particular combination wherein the chlorine content of CPVC, the real weight average molecular weight of CPE (M.sub.w) and polydispersity (M.sub.w /M.sub.n), defined as the ratio of the weight average to number average molecular weight, and shear range are as follows for embodiments (a) through (m):

______________________________________ CPE M.sub.wCPVC Cl level .times. 10.sup.3 CPE M.sub.w /M.sub.n shear range (S.sup.-1)______________________________________(a) 62%-64% 90-130 4-8 100-600(b) 62%-64% 150-200 3-8 100-500(c) 64.1%-66% 90-130 4-8 100-4,000(d) 64.1%-66% 170-220.sup.1 6-9 100-500(e) 64.1%-66% 170-210.sup.2 8-11 100-550(f) 66.1%-69% 90-130 4-8 100-4,000(g) 66.1%-69% 150-200 3-8 100-1,300(h) 66.1%-69% 290-330 8-14 100-650(i) 66.1%-69% 170-220.sup.1 6-11 100-1,800(j) 69.1%-72% 90-130 4-8 100-3,500(j) 69.1%-72% 150-200 3-8 100-1,000(k) 69.1%-72% 290-330 8-14 100-500(l) 69.1%-72% 170-220.sup.1 6-9 100-3,500(m) 69.1%-72% 170-210 8-11 100-2,300______________________________________ .sup.1 38%-44% chlorine content .sup.2 33-37% chlorine content More preferred embodiments are specified by the following: ______________________________________ CPE M.sub.wCPVC Cl level .times. 10.sup.3 CPE M.sub.w /M.sub.n shear range (S.sup.-1)______________________________________(a) 62%-64% 90-130 4-8 300-600(b) 62%-64% 150-200 3-8 400-500(c) 64.1%-66% 90-130 4-8 350-4,000(d) 64.1%-66% 170-220.sup.1 6-9 400-500(e) 64.1%-66% 170-210.sup.2 8-11 350-550(f) 66.1%-69% 90-130 4-8 400-4,000(g) 66.1%-69% 150-200 3-8 400-1,300(h) 66.1%-69% 290-330 8-14 500-650(i) 66.1%-69% 170-220.sup.1 6-11 400-1,800(j) 69.1%-72% 90-130 4-8 350-3,500(j) 69.1%-72% 150-200 3-8 300-1,000(k) 69.1%-72% 290-330 8-14 350-500(l) 69.1%-72% 170-220.sup.1 6-9 500-3,500(m) 69.1%-72% 170-210 8-11 400-2,300______________________________________ .sup.1 38%-44% chlorine content .sup.2 33-37% chlorine content Still more preferred embodiment of (a) contains a chlorinated polyethylene having a real average molecular weight of from 115,000 to 125,000 and a polydispersity of from 5-7. The more preferred embodiment of (b) contains a chlorinated polyethylene having a real average molecular weight of from 175,000 to 195,000 and a polydispersity of from 5-6. The more preferred embodiment of (c) contains a chlorinated polyethylene having a real average molecular weight of from 115,000 to 125,000 and a polydispersity of from 5-7. The more preferred embodiment of (d) contains a chlorinated polyethylene having a real average molecular weight of from 190,000 to 205,000 and a polydispersity of 6-9.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a photomicrograph at 15.times. magnification of a section of a 0.046 in. extruded rod which is representative of a very smooth surface appearance.

FIG. 2 is a photomicrograph at 15.times. magnification of a section of a 0.046 in. extruded rod which is representative a smooth surface appearance.

FIG. 3 is a photomicrograph at 15.times. magnification of a section of a 0.046 in. extruded rod which is representative of a semi-smooth surface appearance.

FIG. 4 is a photomicrograph at 15.times. magnification of a section of a 0.046 in. extruded rod which is representative a slightly rough surface appearance.

FIG. 5 is a photomicrograph at 15.times. magnification of a section of a 0.046 in. extruded rod which is representative a rough surface appearance.

FIG. 6 is a photomicrograph at 15.times. magnification of a section of a 0.046 in. extruded rod which is representative a very rough surface appearance.

DETAILED DESCRIPTION

The rigid thermoplastic CPVC/CPE compounds specified herewith are defined as compositions having a modulus of elasticity, either in flexure or in tension, greater than 700 Mpa (100,000 psi), and preferably greater than 1,400 MPa at 23.degree. C. and 50% relative humidity when tested in accordance with ASTM Method D747, Test for Stiffness of Plastics by Means of a Cantilever Beam, ASTM Methods D790, Test for Flexural Properties of Plastics and Electrical Insulating Materials, ASTM Method D638, Test for Tensile Properties of Plastics, or ASTM Methods D882, Test for Tensile Properties of Thin Plastic Sheeting. As a semi-rigid extrudate, the compounds herein may exhibit a modulus of from 70 to 700 MPa (10,000 to 100,000 PSI). Rigid versions are most preferred.

The articles of manufacture are extruded profiles in any shape comprising CPVC as the major component and chlorinated polyethylene as the second component. There can be included preferably in minor amounts less than the weight of CPVC present, one or more other halopolymers selected from the group consisting of homopolymers and copolymers of: polyvinyl chloride, polyvinyl fluoride, polyvinylidene chloride, and polyvinylidene fluoride. These halopolymers enumerated above are commercially available from sources listed in Chemical Week Buyers' Guide, October-1990, Vol. 147 No. 18, New York. In addition, other halopolymer materials are described in detail in the following U.S. Patents: polyvinylidene fluoride--U.S. Pat. No. 4,585,701; polyvinyl chloride--U.S. Pat. No. 5,036,121; chlorinated polyethylene--U.S. Pat. No. 3,299,182 and U.S. Pat. No. 4,749,751; and polyvinylidene chloride--U.S. Pat. No. 4,362,834.

Post-chlorinated PVC is available commercially worldwide from a variety of sources including Atochem S.A., The B. F. Goodrich Co., Nippon Carbide Industries, Co., Ltd., and Tokuyama Sekisui Industry Co., Ltd.

Post-chlorinated PVC for use herein is preferably prepared by the post-chlorination of suspension polymerized PVC. Suspension polymerization techniques are well established in the art and set forth in the Encyclopedia of PVC, pp. 76-85 published by Marcel Decker, Inc. (1976) and need not be discussed in great detail here.

Chlorinated polyvinyl chloride is obtained by chlorinating homopolymers or copolymers containing less than 50% by weight of one or more copolymerizable comonomers. Suitable comonomers for vinyl chloride include acrylic and methacrylic acids; esters of acrylic and methacrylic acid, wherein the ester portion has from 1 to 12 carbon atoms, for example methyl-, ethyl-, butyl-, ethylhexyl acrylates and the like; methyl-, ethyl- , butyl methacrylates and the like; hydroxyalkyl esters of acrylic and methacrylic acid, for example hydroxymethyl acrylate, hydroxyethyl acrylate, hydroxyethyl methacrylate and the like; glycidyl esters of acrylic and methacrylic acid, for example glycidyl acrylate, glycidyl methacrylate and the like; alpha, beta-unsaturated dicarboxylic acids and their anhydrides, for example maleic acid, fumaric acid, itaconic acid and acid anhydrides of these, and the like; acrylamide and methacrylamide; acrylonitrile and methacrylonitrile; maleimides, for example, N-cyclohexyl maleimide; olefin, for example ethylene, propylene, isobutylene, hexene, and the like; vinylidene halide, for example, vinylidene chloride; vinyl ester, for example vinyl acetate; vinyl ether, for example methyl vinyl ether, allyl glycidyl ether, n-butyl vinyl ether and the like; crosslinking monomers, for example diallyl phthalate, ethylene glycol dimethacrylate, methylene bis-acrylamide, tracrylyl triazine, divinyl ether, allyl silanes and the like; and including mixtures of any of the above comonomers. Comonomers as well as crosslinking comonomers are preferably absent. That is, preferred are homopolymers and uncrosslinked CPVC polymers.

The molecular weight as measured by I.V., of precursor polyvinyl chloride for the post-chlorinated polymer will range from about 0.4 to about 1.6, preferably 0.5 to 1.2 and most preferredly from about 0.7 to 1.0 I.V.. The inherent viscosity is a representative measure of the molecular weight of a polymer and is obtained in accordance with ASTM procedure No. D-1243-66. The choice of molecular weight is made by considering the shape and intricacy of the profile, the processing conditions and the physical property balance desired. If the molecular weight is too low, there may be insufficient melt strength and dimensional stability of the hot extrudate will suffer, and if the molecular weight is too high, the compound may not be processible under the desired conditions. Excellent results are obtained under a variety of conditions and cross-sectional shapes using an I.V. of the PVC precursor of about 0.85 to 0.95.

Chlorination of PVC can be carried out in any conventional manner as known to the art and to the literature to obtain a chlorinated base polymer having higher than 57 percent by weight chlorine up to about 74 percent by weight based upon the total weight of the polymer, however, in the practice of the invention, the use of a major amount of CPVC having a chlorine content of greater than 65% and up to 74% is preferred, and more preferably from 67% to about 71% chlorine.

The preferred method of post-chlorination is by the aqueous suspension chlorination method. There are considerations relative to this method wherein the preferred mode of chlorination employs a relatively concentrated aqueous suspension of the precursor PVC. The most preferred method results in a CPVC resin having a density which does not deviate more than about 20 percent from the mean density, and a surface area which does not deviate more than 30 percent from the mean surface area is more desirable. A concentration of about 15 to about 35 weight percent of solids in the suspension is preferred. Generally a concentration of the suspension higher than the specified range results in less uniform chlorinated product, while concentrations below 15 percent yield uniform product, but are not as economical. By "aqueous suspension" of PVC base polymer we refer to a slurry-like mixture of base polymer macrogranules suspended in water. This process is particularly directed to a batch process.

It is desired that oxygen be removed from the aqueous suspension before chlorination is initiated. This may be effected in any convenient manner, and assisted with agitation. Heating as may be required is preferably done after Cl.sub.2 is sparged into suspension from a liquid Cl.sub.2 cylinder until the pressure in the reactor reaches about 25 psig, at which point the suspension is saturated with Cl.sub.2. It is preferred that this pressure be somewhat higher, that is in the range from about 35 psig to about 100 psig, to get the optimum results, though a pressure as low as 10 psig and higher than 100 psig may be employed. The amount of Cl.sub.2 charged to the reactor is determined by weight loss in the Cl.sub.2 cylinder. The reactor is preferably brought up to a "soak" temperature in the range from about 60.degree. C. to about 75.degree. C. at which soak temperature the suspension is maintained under agitation for a soak period in the range from about 1 minute to about 45 minutes. Excessive pressure adversely affects the porosity of the macrogranules to the detriment of the stability of the chlorinated product.

It is desirable to complete the chlorination reaction under photo-illumination, preferably with ultraviolet light, or the desired conversion of base polymer to chlorinated base polymer product does not occur. Chlorination proceeds at a rate which depends upon the pressure and temperature within the reactor, higher rates being favored at higher temperature and pressure. It is most preferred to adjust the soak temperature, the mass of resin, and the level of photo-illumination so that the temperature is "ramped" by the heat of reaction until it levels off at a finishing temperature of about 100.degree. C. After chlorination has proceeded to the desired degree, the suspension is preferably not cooled but dumped to be centrifuged and the chlorinated polymer freed from the aqueous phase, after which Hcl is removed from the product, preferably by neutralizing with an aqueous solution of an alkali metal hydroxide. The product is then washed with water to free the chlorinated polymer of residual alkali, and dried, all in a conventional manner, except that the temperatures at which the operations are carried out may be in the range from about 60.degree. C. to about 100.degree. C., which are higher than conventionally used.

Chlorinated polyethylene used herein has a specific gravity of from about 1.13 to 1.4, preferably about 1.16, a residual crystallinity of from about 0 to about 25%, preferably 0 to 10%, and a chlorine content from about 25% to about 45%, preferably 35% to 44%. The chlorination can be either homogeneous or heterogenous, preferably to a small extent. Surface appearance of extrudates depended on CPE molecular weight and polydispersity as measured by gel permeation chromatography and on the extrusion conditions used as illustrated below. Chlorination methods for CPE include aqueous suspension, solution, or gas phase methods, with the preferred method by way of suspension chlorination. CPE is commercially available from Dow Chemical Inc. The amount of CPE present ranges from about 10 to about 30 phr, preferably from about 12 to about to 25 phr, still more preferred are levels from 15 to 25 phr. The particular combination of CPVC and CPE within the scope of the present invention will be described below.

The core/shell type impact modifiers can be present but are preferably absent. These include acrylonitrile butadiene styrene terpolymers (ABS), methacrylate, acrylonitrile, butadiene, styrene (MABS) polymers and methacrylate butadiene styrene polymer (MBS). Other impact modifiers are disclosed in Plastics compounding, November/December, 1983: "Update: Impact Modifiers for Rigid PVC," by Mary C. McMurrer. Various commercial MBS grades include Paraloid.RTM. KM-653, BTA-733 from Rohm and Haas, or Kanegafuchi Inc. B-56 and B-22; Commercial polyacrylate impact modifiers include KM.RTM.-323B, and KM.RTM.-330, from Rohm and Haas, Inc.; ABS grades are commercially available from GE Plastics, Inc, for example, Blendex.RTM. 336.

Thermal stabilizers are employed in the compounds herein and can be selected from various organic compounds, for example dibutyltin-S-S'-bi-(isooctylmercaptoacetate), dibutyl tin dilaurate, di-butyltin di-2-ethylhexyl thioglycolate dimethyl tin di-isooctyl-thioglycolate, and the like. Tin compounds are generally used at from 1 to 5 phr, preferably about 2.0 to 4.0 phr. Secondary stabilizers may be included for example a metal salt of phosphoric acid, polyols, or epoxidized oils. Specific examples of salts include water-soluble, alkali metal phosphate salts, disodium hydrogen phosphate, orthophosphates such as mono-,di-, and tri-orthophosphates of said alkali metals, alkali metal polyphosphates, -tetrapolyphosphates and -metaphosphates and the like. The most preferred secondary stabilizer is disodium hydrogen phosphate (DSP) and is used by treating the CPVC resin. Polyols such as sugar alcohols, and epoxides such as epoxidized soya oil can be used. Typical levels of secondary stabilizers can range from about 0.1 wt. parts to about 7.0 wt. parts per 100 wt. parts halopolymer (phr). In addition, commercially available antioxidants are used such as phenolics, BHT, BHA, various hindered phenols and various inhibitors like substituted benzophenones.

Other auxiliary components are contemplated. Antistats may be used and are commercially available under the Glycolube.RTM. trademark of Lonza Corp. Exemplary lubricants are the various hydrocarbons, such as paraffins, paraffin oils, low molecular weight polyethylene, oxidized polyethylenes, fatty acids and their salts such as stearic acid and calcium stearate, fatty alcohols such as cetyl, stearyl, or octadecyl alcohol; metal soaps such as calcium or zinc salts of oleic acid; fatty amides of organic acids such as stearamide, ethylene-bis-stearamide; preferred fatty esters and partial esters such as butyl stearate, polyol esters such as glycerol monostearate, hexaglycerol distearate; and fatty ester waxes such as stearyl esters. The most preferred lubricant is oxidized polyethylene. Henkel Co. produces a variety of preferred fatty ester formulations under the Loxiol.RTM. mark. Combinations of internal and external lubricants may also be used. Lubrication of the halopolymer compounds of the present invention is a complex art. Since several lubricants can be combined in countless variations, the total amount of lubricant may vary generally from about 2 to 10 phr, preferably from 2 to about 6 phr. Optimization of particular individual lubricant formulations is beyond the scope of the present invention, and can be achieved as one skilled in the art prefers.

Adjustment of melt viscosity can be achieved as well as increasing melt strength by optionally employing commercial acrylic process aids such as those from Rohm and Haas under the Paraloid.RTM. Trademark, for example Paraloid.RTM. K-120ND, K-120N, K-175.

Exemplary fillers are optional and include clay, wollastonite, mica, barytes, calcium carbonate and silica including precipitated silicas, silica gels, metallic silicates, pyrogenic or fumed silicas and the like. These have the general formulae: SiO.sub.2, M.sub.n (SiO.sub.3).sub.x. The values of n and x can vary with the oxidation state of the metal associated with the SiO.sub.3 ion. The values n and x are usually integers from about 1 to about 4.

Preferred pigments are the various titanium dioxides (TiO.sub.2) and carbon blacks which are commercially available. Preferred TiO.sub.2 types are coated or uncoated, rutile titanium dioxide powder. An exemplary commercial grade is Ti-Pure.RTM. R-100 from E. I. DuPont De Nemours and Co. Inc. (DuPont). If used, pigments such as TiO.sub.2 are present in an amount ranging from 1 to 25 phr, more typically 3 to 15 phr, and most typically from 3 to about 8 phr. Optional coloring pigments can be used.

The method of compounding is straightforward as any high intensity method to uniformly mix and fuse the components into a homogeneous compound such as with a Banbury/mill, followed by sheeting, slitting or extrusion into pellets, or cubes. The differences in process handling of CPVC compared with polyvinyl chloride-based compounds relate mainly to the temperature and viscosity differences and care must be taken to avoid too much work and shear burning. In the preparation of compounds, the components can be combined and mixed with a Banbury and milled on a heated roll mill. The fused compound can be extruded and chopped into cubes. Alternatively, the components can be combined in a compounding twin screw extruder. The compounds are extruded into final form at conventional stock temperatures from about 175.degree. C. to about 235.degree. C. and preferably from about 200.degree. C. to about 225.degree. C. The extruder characteristics applicable to melt processing of the compounds of the present invention include:

Head pressure rating of at least 7500 psi (51.7 Mpa). Extruder drive/gearbox capable of generating high torque at low rpm. Vacuum venting to remove volatile components, moisture and entrapped air. A barrel L/D of at least 16/1 for twin screw; generally at least 20/1 for single screw. Temperature controllers able to control within 5.degree. F. or preferably +/-2.degree. F. Accurately controllable powder metering screw for powder compounds.

A ramped barrel temperature profile is advisable with a zone nearest the hopper set at 180.degree. C. and the zone nearest the die at about 195.degree. C. for 0.75 inch diameter screw. There can be used calibrating blocks at the exit end to assist in proper dimension sizing as the hot profile is cooled. Air streams can be used to improve heat loss, and for more close tolerances, vacuum water sizing devices can be used. The extent to which one chooses to employ calibrator blocks and air or water sizing will depend on dimension tolerances for the particular profile shape, the intended output volume of any one profile article and the number of different profiles made with a particular production set. These considerations are beyond the scope of the disclosure.

EXAMPLES

In the examples below, compounds were prepared as listed below. The components were combined in a Banbury/mill and extruded in a Brabender extruder equipped with a 0.046 inch rod die. The extrusion conditions were controlled by varying the rpm from 5 to 50 rpm. The actual shear rates were calculated for each example using quantitative extrusion volume output rates. For each rpm series the calculated shear rates were grouped as follows:

______________________________________SCREW (S.sup.-1)RPM SHEAR RANGE______________________________________ 5 400-50010 800-100015 1000-130020 1200-180025 1500-220030 1700-330040 2200-330050 2700-4100______________________________________

The compounds used in the examples contained one of the following CPVC resins.

______________________________________ ResinResin Chlorine Resin Wt.No. Content, % I.V. Amount______________________________________1 63.1 0.92 1002 65.2 0.92 1003 68.3 0.92 1004 70.3 0.92 100______________________________________

The examples contained either of the following components:

______________________________________ Real %Number Type Wt. PHR AVE. MW.sup.2 M.sub.w /M.sub.n chlorine______________________________________A CPE 20 120,000 5.7 36B CPE 20 188,000 6.6 36C CPE 20 317,000 11.6 36D CPE 20 197,000 7.4 42E CPE 20 192,000 9.5 35F.sup.x CPE 20 180,000 -- 25G.sup.x CPE 20 180,000 -- 40H Acrylic 20 -- -- --I MBS 20 -- -- --______________________________________ X estimated .sup.2 Real weight average and number average molecular weight were measured by Waters 150CV gel permeation chromatograph equipped with refractometer detector and a capillary viscometer. Approximately 0.03 mg of samples were dissolved in 10 ml trichlorobenzene stabilized with 250 ppm BHT. The samples were filtered through Gelman Acrodisc CR PTFE 0.45 .mu.m filter. The samples were heated to 130.degree. C. and allowed to stand at least 90 minutes before measurement under the following conditions: column set: PLgel 10 .mu.m, 1 guard column+3 mixed bed columns+a 100 .ANG. column. Mobile phase: Trichlorobenzene Flow rate: 1.0 ml/minute Temperature: 135.degree. C. sample size: 200 .mu.l @ ca. 0.3% Intensities: 64.times.8

The following formulation was used in evaluating extrudates:

______________________________________Component Amount______________________________________CPVC 100Component (A-J) 20tin thioglyocolate 2.25Oxidized polyethylene 1.5Glycerol ester 1.0Antioxidant 0.25TiO.sub.2 5.0Carbon black 0.25______________________________________

The Brabender extruder barrel zones were maintained at the following temperatures (.degree.C.):

______________________________________Zone 1 Zone 2 Zone 3 Die______________________________________180 185 190 195______________________________________

Percent die swell measurements were taken by comparing the actual diameter of the extrudate after cooling and the die diameter. The following results were reported as (extrudate dia.-die dia.)/die dia..times.100.

______________________________________% DIE SWELL RPMEXAMPLE 5 10 15 20 25 30 40 50______________________________________1-A 41 35 30 39 43 46 48 501-B 39 41 41 43 46 46 43 431-C 57 48 48 48 52 50 52 501-D 61 54 50 55 74 57 54 Fail*1-E 52 48 50 55 40 57 59 Fail*1-F 50 43 46 44 96 49 50 501-G 70 59 54 55 97 59 61 Fail*1-H 33 33 33 33 77 39 39 391-I 35 37 37 33 99 37 35 33______________________________________ *too irregular to measure Lumpy flow Example 1-A exhibits a desirable reduced level of swell. ______________________________________% DIE SWELL RPMEXAMPLE 5 10 15 20 25 30 40 50______________________________________2-A 33 33 33 37 39 41 48 502-B 39 39 39 41 43 46 58 482-C 43 43 48 50 57 57 57 592-D 52 52 54 57 62 61 65 652-E 46 46 48 50 54 59 61 612-F 37 35 37 39 41 46 48 502-G 54 52 52 57 57 61 63 652-H 33 37 43 50 54 59 61 592-I 33 35 43 48 54 52 52 503-A 28 28 28 30 33 35 37 413-B 37 35 35 37 41 43 46 483-C 46 50 48 50 50 52 57 593-D 50 57 54 54 54 57 59 633-E 41 41 41 41 46 48 54 573-F 28 30 30 30 35 37 41 463-G 48 52 50 52 52 54 61 673-H 43 67 80 87 91 91 96 933-I 57 61 63 65 67 70 67 634-A 43 37 26 26 26 24 26 304-B 33 30 28 30 30 33 41 434-C 41 41 39 37 39 39 41 464-D 48 48 43 41 41 43 46 504-E 50 50 46 46 41 37 41 434-F 28 24 24 26 26 28 30 354-G 46 41 37 39 39 39 43 464-H 65 76 78 78 80 83 89 894-I 59 57 54 57 59 65 65 70______________________________________

It can be seen from the above die swell measurements taken at the indicated RPM, among resin series 1 through 4, that the degree of die swell varies widely as between CPE resins of different chlorine content as well as molecular weight. However it is observed that die swell is comparatively less among the examples exhibiting the best surface smoothness.

The following actual shear rates were calculated:

__________________________________________________________________________SHEAR RATE, SEC -1RPMEX. 5 10 15 20 25 30 40 50__________________________________________________________________________1-A 409 754 1084 1373 1685 2034 2647 32371-B 396 718 1072 1406 1735 1982 2694 32781-C 405 768 1114 1390 1719 2017 2577 31691-D 466 791 1254 1574 1983 2357 2964 3379*1-E 440 779 1105 1407 1668 1983 2552 31611-F 367 626 994 1243 1478 1679 2230 29551-G 386 719 1004 1327 1621 1940 2640 3288*1-H 388 782 1112 1542 1844 2267 2877 37091-I 364 739 1088 1420 1785 2092 2754 33592-A 382 727 1007 1320 1642 1976 2558 32042-B 386 691 1010 1365 1650 1987 2710 32552-C 399 723 1095 1477 1780 2085 2658! 3271!2-D 452 784 1227 1598 1987 2355 3106 3709!2-E 417 786 1165 1482 1813 2126 2661 23142-F 349 625 937 1173 1436 1673 2225 27842-G 414 766 1153 1480 1786 2062 2665! 3346!2-H 468 774 1188 1605 1943 2404 3173 40472-I 381 726 1093 1539 1905 2294 2937 36473-A 486 772 1129 1421 1792 2060 2654 32113-B 450 807 1158 1430 1728 2048 2287 432943-C 539 867 1266 1569 1840 2175 2711 34783-D 487 994 1428 1739 2144 2497 3008 37173-E 487 878 1202 1510 1823 2103 2638 33423-F 354 676 977 1219 1531 1735 2196 25983-G 476 896 1248 1590 1901 2192 2788 34963-H 443 767 1220 1673 2097 2451 3231 39713-I 391 795 1174 1570 1901 2270 2889 34804-A 409 573 855 1433 1713 2019 2690 33214-B 440 826 1208 1533 1867 2173 2819 34244-C 513 966 1357 1769 2149 2463 2991 36834-D 535 914 1365 1818 2260 2687 3338 41174-E 482 958 1299 1626 1906 2184 2821 34804-F 389 738 967 1234 1499 1762 2236 27194-G 519 1000 1349 1677 1930 2228 2884 35114-H 453@ 910* 1297' 1652' 2083' 2427' 3233' 4120'4-I 374 747 1078 1348 1654 2004 2697 3293__________________________________________________________________________ @ Slightly Lumpy * Lumpy ' Very Lumpy ! Fail Slightly Spiral

BRABENDER TORQUE

The equilibrium torque for the above series of compounds was evaluated in a Haake Rheomix Model No. 600 under the following conditions:

______________________________________Mixing Bowl Temp .degree.C. 210RPM 35Sample Weight 65 gms.______________________________________

3 minute load and heat soak at 10 rpm before testing.

The following table lists the torque reading under controlled conditions and each compound can be compared. The general trends show that torque is directly proportional to CPVC chlorine content and the average molecular weight of the impact modifier. The MBS impact modifier exhibited the highest torque while CPE-A exhibited the lowest torque.

______________________________________BRABENDER TORQUE (m-g)ADDITIVE CPVC TYPETYPE 1 2 3 4______________________________________A 1230 1500 1540 1690B 1530 1800 2000 2030C 1570 1780 2080 2070D 1480 1650 1980 1920E 1420 1600 1820 1910F 1640 1700 2000 1970G 1620 1690 2000 2070H 1590 1880 2220 2500I 2000 2220 2680 2920______________________________________

SURFACE APPEARANCE

Series 1-4 with additives A-I were extruded with the aforementioned single screw extruder equipped with a 0.046 in. circular die. Each example was compared to an established appearance criteria using six categories and illustrated in FIGS. 1-4 for the standards. The figures show photomicrographs made at 15.times. magnification of rods which were representative of each appearance classification category. The categories are as follows:

SMOOTH RODS 1. Very smooth/silky feeling rods with no texture visible. 2. Smooth feeling rods with a slight texture visible. 3. Smooth feeling rods with some texture visible ROUGH RODS 1. Some texture can be felt and seen. 2. Rough to the touch and lots of visible texture. 3. Very rough to the touch and extremely coarse texture seen. In a preferrd embodiment, CPVC resin is used which has been pre-treated with a phosphate salt. The following compounds illustrate the significant improvement with the use of this type of resin for improving the processing stability. ______________________________________Component Example A Example B______________________________________Untreated CPVC 100 (parts) --DSP treated CPVC -- 100Tin stabilizer 2.25 2.25Chlorinated PE 20 20lubricant 2.5 2.5TiO.sub.2 5 5Antioxidant 0.25 0.25Brabender stability (minutes) 6.5 13.7Torque (m-g) 2100 1800Temperature (.degree.C.) 222 225______________________________________

Table A below represents the extrusion appearance ratings of the compound containing CPVC with a chlorine content of 63.1; Table B illustrates the appearance of extrudate from compounds made with a 65.2% chlorine level; Table C illustrates the appearance of extrudate from compounds made with 68.3% chlorine level, and table D illustrates the appearance of extrudates from compounds made with 70.3% chlorine CPVC. The preferred embodiments are made with a CPVC containing from 67 to 72% chlorine, with the most preferred CPVC contains from 67% to 70% chlorine. The most preferred chlorinated polyethylene contains from 35% to 37% chlorine and has a real weight average molecular weight of from 90,000 to 130,000, more preferably 115,000 to 125,000 and most preferably about 120,000, with a polydispersity of from 5 to 7 as in CPE number A above.

TABLE A__________________________________________________________________________5 rpm 10 rpm 15 rpm 20 rpm 25 rpm 30 rpm 40 rpm 50 rpm__________________________________________________________________________1-A semi sl. sl. semi sl. sl. sl. sl. smooth rough rough smooth rough rough rough rough lumpy lumpy lumpy1-B very very very very very very very very rough rough rough rough rough rough rough rough1-C rough very very very very very very very rough rough rough rough rough rough rough lumpy1-D semi sl. rough rough rough rough rough very smooth rough rough lumpy1-E very very very very very very very very rough rough rough rough rough rough rough rough lumpy lumpy1-F rough very very very very very very very rough rough rough rough rough rough rough lumpy1-G rough sl. very very very very very very lumpy rough rough rough rough rough rough rough lumpy wavy1-H smooth smooth smooth smooth smooth smooth smooth smooth1-I smooth very very smooth smooth smooth very smooth rough rough smooth lumpy lumpy__________________________________________________________________________ TABLE B__________________________________________________________________________5 rpm 10 rpm 15 rpm 20 rpm 25 rpm 30 rpm 40 rpm 50 rpm__________________________________________________________________________2-A smooth smooth smooth smooth smooth smooth smooth smooth2-B very very very rough rough rough rough rough rough rough rough2-C very very very very very very very rough rough rough rough rough rough rough rough wavy wavy2-D very sl. rough rough rough rough sl. sl. smooth rough rough rough wavy2-E smooth rough very very very rough rough rough rough rough rough2-F semi very very very very very rough rough smooth rough rough rough rough rough2-G smooth sl. rough very very very rough rough rough rough rough rough wavy wavy2-H very very very very very smooth semi sl. smooth smooth smooth smooth smooth smooth rough2-I very very very very very very very very smooth smooth smooth smooth smooth smooth smooth smooth__________________________________________________________________________ TABLE C__________________________________________________________________________5 rpm 10 rpm 15 rpm 20 rpm 25 rpm 30 rpm 40 rpm 50 rpm__________________________________________________________________________3-A very very very very very very very very smooth smooth smooth smooth smooth smooth smooth smooth3-B semi smooth semi sl. sl. sl. rough sl. smooth smooth rough rough rough rough3-C smooth rough rough very very very rough rough rough rough rough3-D very smooth semi semi sl. sl. sl. sl. smooth smooth smooth rough rough rough rough3-E smooth smooth sl. sl. sl. rough rough rough rough rough rough3-F very very very very very very very very smooth rough rough rough rough rough rough rough3-G smooth semi semi sl. sl. sl. sl. sl. rough smooth smooth rough rough rough rough lumpy3-H semi sl. rough very very very very very smooth rough rough rough rough rough rough lumpy lumpy lumpy lumpy lumpy3-I very very very very very very sl. rough sl. rough smooth smooth smooth smooth smooth smooth lumpy lumpy__________________________________________________________________________ TABLE D__________________________________________________________________________5 rpm 10 rpm 15 rpm 20 rpm 25 rpm 30 rpm 40 rpm 50 rpm__________________________________________________________________________4-A semi- smooth very very very very very very smooth smooth smooth smooth smooth smooth smooth4-B smooth semi- sl. rough rough rough rough very smooth rough rough4-C semi- rough very very very very very very smooth rough rough rough rough rough rough4-D smooth smooth smooth smooth smooth smooth semi sl. smooth rough4-E smooth smooth smooth smooth smooth semi rough rough smooth4-F very smooth rough very very very very very smooth rough rough rough rough rough4-G smooth sl. sl. rough rough rough rough rough rough rough4-H very rough very very very very very very smooth lumpy rough rough rough rough rough rough lumpy lumpy lumpy lumpy lumpy lumpy4-I smooth very very very very very very very smooth smooth smooth smooth smooth smooth smooth__________________________________________________________________________

Claims

1. An extruded profile having smooth surface appearance made from a chlorinated polyvinyl chloride blend, said blend comprising 100 weight parts of chlorinated polyvinyl chloride containing from 62% to 72% chlorine and 10 to 30 weight parts chlorinated polyethylene and a stabilizer comprising a metal salt of phosphoric acid, the blend comprising any one of the following:

(a) chlorinated polyvinyl chloride containing 62% to 64% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 90,000 to 130,000 and a polydispersity of from 4 to 8, said blend (a) extruded in a shear range of from 100 S.sup.-1 to 600 S.sup.-1 ;

(b) chlorinated polyvinyl chloride containing 64.1% to 66% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 90,000 to 130,000 and a polydispersity of from 4 to 8 said blend (b) extruded in a shear range of from 350 S.sup.-1 to 4,000 S.sup.-1 ;

(c) said chlorinated polyvinyl chloride containing 64.1% to 66% chlorine, said chlorinated polyethylene having a chlorine content of from 38% to 44% chlorine, a real weight average molecular weight of from 170,000 to 220,00 and a polydispersity of from 4 to 8, said blend (c) extruded in a shear range of from 400 S.sup.-1 to 500 S.sup.-1 ;

(d) said chlorinated polyvinyl chloride containing 66.1% to 69% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 90,000 to 130,00 and a polydispersity of from 4-8, said blend (e) extruded in a shear range of from 300 S.sup.-1 to 600 S.sup.-1 ;

(e) said chlorinated polyvinyl chloride containing 66.1% to 69% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 150,000 to 200,000 and a polydispersity of from 3-8, said blend (f) extruded in a shear range of from 400 S.sup.-1 to 1,300 S.sup.-1 ;

(f) said chlorinated polyvinyl chloride containing 66.1% to 69% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 290,000 to 330,000 and a polydispersity of from 8-14, said blend (g) extruded in a shear range of from 500 S.sup.-1 to 650 S.sup.-1 ;

(g) said chlorinated polyvinyl chloride containing from 69.1% to 72% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 90,000 to 130,000 and a polydispersity of from 4-8, said blend (h) extruded in a shear range of from 350 S.sup.-1 to 3,500 S.sup.-1 ;

(h) said chlorinated polyvinyl chloride containing from 69.1 to 72% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 150,000 to 200,000 and a polydispersity of from 3-8, said blend (i) extruded in a shear range of from 300 S.sup.-1 to 1,000 S.sup.-1 ; or

(i) said chlorinated polyvinyl chloride containing from 69.1% to 72% chlorine, said chlorinated polyethylene having a real weight average molecular weight of from 290,000 to 330,000 and a polydispersity of from 8-14, said blend (i) extruded in a shear range of from 350 S.sup.-1 to 500 S.sup.-1.

2. The extruded profile of claim 1 made from the blend (a) wherein said chlorinated polyethylene has a real weight average molecular weight of from 115,000 to 125,000 a polydispersity of from 5-7 and a chlorine content of from 32% to 38%.

3. The extruded profile of claim 1 made from the blend (b) wherein said chlorinated polyethylene has a polydispersity of from 5-6 and a chlorine content of from 32% to 38%.

4. The extruded profile of claim 1 made from the blend (f) wherein said chlorinated polyethylene has a real weight average molecular weight of from 310,000 to 325,000 a polydispersity of from 10-13 and a chlorine content of from 32% to 38%.

5. The extruded profile of claim 1 wherein chlorinated polyethylene is present at from 15 to 25 weight parts per 100 weight parts of chlorinated polyvinyl chloride.

6. The extruded profile of claim 1 in the shape of a window spacer, a glazing bead, a window lineal, and a track for lighting.

7. A method of making an extruded profile having good surface appearance comprising extruding a composition according to claim 1.

8. An extruded profile having a smooth surface appearance made from a chlorinated polyvinyl chloride blend, said blend comprising 100 weight parts of a chlorinated polyvinyl chloride containing from 69.1% to 72% chlorine and 10 to 30 weight parts chlorinated polyethylene, said chlorinated polyethylene having a real weight average molecular weight of of from 170,000 to 220,000 and a polydispersity of from 7-9 said blend extruded in a shear range of from 500 S.sup.-1 to 3,500 S.sup.-1.

9. A method of making an extruded profile having good surface appearance comprising extruding a composition in the shear range of from 100 to 3,500 reciprocal seconds, said composition comprising 100 weight parts of chlorinated polyvinyl chloride containing from 69.1% to 72% chlorine and from 10 to 30 weight parts of chlorinated polyethylene, said chlorinated polyethylene having a real weight average molecular weight of from 170,000 to 220,000 and a polydispersity of from 7-9.