Patent Application
20210375623
The present disclosure relates to a manufacturing process for selective area growth (SAG) nanowire growth, and in particular to a manufacturing process for a SAG nanowire growth with a planarization process of a buffer layer, which reduces defects during the SAG nanowire growth.
Nanowires show great promise for applications in quantum computing. Unfortunately, it is difficult to manufacture high quality nanowires. Conventional processes for manufacturing nanowires include selective-area-growth (SAG) wherein nanowires are selectively grown directly on a substrate through a patterned mask. To function properly, nanowires must be a conducting semiconductor material. The substrate on which the nanowires are grown is desired to be an insulating material. To meet this condition, there is often a large difference in the crystal lattice constant of the substrate and the nanowires to be grown via SAG. This crystal lattice mismatch causes crystalline defects in the nanowires during growth such as dislocations and stacking faults. The crystalline defects can penetrate the nanowires and in turn decrease the performance of the resulting nanowires.
In addition, surface smoothness of the nanowires, which enables electrons to move consistently and uniformly within the nanowires, is critical to the quality and functionality of the nanowires. Accordingly, there is a need for manufacturing nanowires with reduced crystalline defects without sacrificing the surface smoothness of the nanowires.
The present disclosure relates to a method for manufacturing a nanowire structure. According to an exemplary process, a substrate is firstly provided. An intact buffer region is formed over the substrate, and a sacrificial top portion of the intact buffer region is eliminated to provide a buffer layer with a planarized top surface. Herein, the planarized top surface has a vertical roughness below 10 Å. Next, a patterned mask is formed over the planarized top surface of the buffer layer. The patterned mask includes an opening through which a portion of the planarized top surface of the buffer layer is exposed. A nanowire is then formed over the exposed portion of the planarized top surface of the buffer layer through the opening of the patterned mask. The buffer layer is configured to have a lattice constant between a lattice constant of the substrate and a lattice constant of the nanowire, so as to provide a transition between the lattice constant of the substrate and the lattice constant of the nanowire.
In one embodiment of the exemplary process, the planarized top surface of the buffer layer has the vertical roughness below 5 Å.
In one embodiment of the exemplary process, the sacrificial top portion of the intact buffer region is eliminated by a chemical and mechanical polishing (CMP) technique, which includes one or more of chemical etching, oxidizing, surfactant solutions, and mechanical polishing.
In one embodiment of the exemplary process, the sacrificial top portion of the intact buffer region is eliminated by a chemical and mechanical polishing (CMP) technique, which utilizes one or more chemicals including hydrochloric acid, hydrogen peroxide, ammonium dodecyl sulfate and silica nanoparticles.
In one embodiment of the exemplary process, the eliminated sacrificial top portion of the intact buffer region has a thickness between 1 nm and 1000 nm.
In one embodiment of the exemplary process, the lattice constant of the buffer layer gradually varies from the planarized top surface of the buffer layer on the nanowire to a bottom surface of the buffer layer on the substrate.
In one embodiment of the exemplary process, the buffer layer includes a number of discrete layers, each of which is formed of a different material.
In one embodiment of the exemplary process, the substrate is formed of one of indium phosphide, gallium antimonide, and gallium arsenide. The buffer layer includes one or more layers each formed of one or more of indium aluminum arsenide, indium gallium arsenide, and aluminum gallium arsenide antimonide. The nanowire is formed of one of indium arsenide, indium antimonide, and indium arsenide antimonide.
In one embodiment of the exemplary process, the patterned mask is formed of one of silicon dioxide, silicon nitride, aluminum oxide, and diamond.
According to another embodiment, the exemplary process further includes providing a superconductor layer on the nanowire.
In one embodiment of the exemplary process, forming the patterned mask starts with forming a mask layer over the planarized top surface of the buffer layer. Next, a lithography mask with an opening is applied over the mask layer. A portion of the mask layer is eliminated aligning the opening of the lithography mask to form the patterned mask. As such, the opening of the patterned mask is a same size of the opening of the lithography mask, and the portion of the planarized top surface of the buffer layer is exposed. At last, the lithography mask is removed to expose the patterned mask.
In one embodiment of the exemplary process, the intact buffer region is formed by molecular-beam epitaxy (MBE), chemical beam epitaxy (CBE), chemical vapor deposition (CVD), or metal organic chemical vapor deposition (MOCVD).
In one embodiment of the exemplary process, the nanowire is formed by MBE, CBE, or CVD.
The present disclosure also relates to an exemplary nanowire structure, which includes a substrate, a buffer layer, a patterned mask, and a nanowire. The buffer layer with a planarized top surface resides over the substrate. The planarized top surface of the buffer layer has a vertical roughness below 10 Å. The patterned mask with an opening resides over the planarized top surface of the buffer layer, such that a portion of the planarized top surface of the buffer layer is exposed through the opening of the patterned mask. The nanowire resides over the exposed portion of the planarized top surface of the buffer layer through the opening of the patterned mask. Herein, the buffer layer is configured to have a lattice constant between a lattice constant of the substrate and a lattice constant of the nanowire, so as to provide a transition between the lattice constant of the substrate and the lattice constant of the nanowire.
In one embodiment of the nanowire structure, the planarized top surface of the buffer layer has the vertical roughness below 5 Å.
In one embodiment of the nanowire structure, the lattice constant of the buffer layer gradually varies from the planarized top surface of the buffer layer on the nanowire to a bottom surface of the buffer layer on the substrate.
In one embodiment of the nanowire structure, the buffer layer includes a number of discrete layers, each of which is formed of a different material.
In one embodiment of the nanowire structure, the lattice constant of the buffer layer at least partially transitions between the lattice constant of the substrate and the lattice constant of the nanowire.
In one embodiment of the nanowire structure, the lattice constant of a buffer layer completely transitions between the lattice constant of the substrate and the lattice constant of the nanowire.
In one embodiment of the nanowire structure, the substrate is formed of one of indium phosphide, gallium antimonide, and gallium arsenide. The buffer layer includes one or more layers each formed of one or more of indium aluminum arsenide, indium gallium arsenide, and aluminum gallium arsenide antimonide. The nanowire is formed of one of indium arsenide, indium antimonide, and indium arsenide antimonide.
Those skilled in the art will appreciate the scope of the present disclosure and realize additional aspects thereof after reading the following detailed description of the preferred embodiments in association with the accompanying drawing figures.
The accompanying drawing figures incorporated in and forming a part of this specification illustrate several aspects of the disclosure, and together with the description serve to explain the principles of the disclosure.
It will be understood that for clear illustrations,
The embodiments set forth below represent the necessary information to enable those skilled in the art to practice the embodiments and illustrate the best mode of practicing the embodiments. Upon reading the following description in light of the accompanying drawing figures, those skilled in the art will understand the concepts of the disclosure and will recognize applications of these concepts not particularly addressed herein. It should be understood that these concepts and applications fall within the scope of the disclosure and the accompanying claims.
It will be understood that, although the terms first, second, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another. For example, a first element could be termed a second element, and, similarly, a second element could be termed a first element, without departing from the scope of the present disclosure. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.
It will be understood that when an element such as a layer, region, or substrate is referred to as being “on” or extending “onto” another element, it can be directly on or extend directly onto the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or extending “directly onto” another element, there are no intervening elements present. Likewise, it will be understood that when an element such as a layer, region, or substrate is referred to as being “over” or extending “over” another element, it can be directly over or extend directly over the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly over” or extending “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.
Relative terms such as “below” or “above” or “upper” or “lower” or “horizontal” or “vertical” may be used herein to describe a relationship of one element, layer, or region to another element, layer, or region as illustrated in the Figures. It will be understood that these terms and those discussed above are intended to encompass different orientations of the device in addition to the orientation depicted in the Figures.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes,” and/or “including” when used herein specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms used herein should be interpreted as having a meaning that is consistent with their meaning in the context of this specification and the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein
The substrate 12 may be formed of an insulator, such as silicon (Si), indium phosphide (InP), gallium phosphide (GaP), gallium antimonide (GaSb), or gallium arsenide (GaAs). The substrate 12 may have a thickness between 50 μm and 1000 μm. The patterned mask 16 may be formed of a dielectric material such as silicon dioxide (SiO2), silicon nitride (SiN), aluminum oxide (Al2O3), diamond, or the like. The nanowire 18 is an elongate member that has a nano-scale width and a length-to-width ratio of at least 10, or at least 20 (length of the nanowire 18, having a direction perpendicular to the cross section view, is not shown), and is grown selectively on the buffer layer 14 through the patterned mask 16. A non-limiting example of the nanowire 18 has an average width (WA) in the range of 10 to 1000 nm, optionally 50 to 100 nm or 75 to 125 nm. The length of the nanowire 18 may be of the order of micrometers, e.g. at least 1 μm, or at least 10 μm. In addition, a thickness (TN) of the nanowire 18 may be between 20 nm and 300 nm. The nanowire 18 may be formed of a conductive semiconductor such as indium arsenide (InAs), indium antimonide (InSb), or indium arsenide antimonide (InAsSb). The superconductor 20 may be formed of aluminum (Al), lead (Pb), niobium indium (NbIn), tin (Sn), or vanadium (V), with a thickness between 3 nm and 30 nm.
Since conducting semiconductors and insulators generally have very different lattice constants, a high lattice mismatch may occur between the nanowire 18 and the substrate 12 when the nanowire 18 is provided directly on the substrate 12. As a result, the nanowire 18 may not function properly. To solve this problem, the buffer layer 14 is provided between the substrate 12 and the nanowire 18. The buffer layer 14 may have a lattice constant between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18, so as to provide a transition between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18 over a thickness of the buffer layer 14. The buffer layer 14 may provide a partial transition between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18 or a complete transition between the lattice constant of the substrate 12 and the lattice constant of the nanowire 18.
In one embodiment, the lattice constant of the buffer layer 14 may gradually vary from the top surface of the buffer layer 14 on the nanowire 18 to a bottom surface of the buffer layer 14 on the substrate 12. To achieve a graded lattice constant, the buffer layer 14 may include multiple discrete layers (not shown), each of which may be formed of a different material with a same or different thickness. Herein and hereafter, the “different material” is referred to a material including different ingredients, or a material including same ingredients with different concentrations. For instance, indium aluminum arsenide (InAlAs) and indium aluminum antimonide (InAlSb) are different materials, and In0.52Al0.48As and In0.89Al0.11As are also different materials. Due to the different material, each layer of the buffer layer 14 may have a different lattice constant, so as to form the graded lattice constant in the buffer layer 14. In some applications, the lattice constant of the buffer layer 14 may gradually decrease from the top surface of the buffer layer 14 on the nanowire 18 to the bottom surface of the buffer layer 14 on the substrate 12. In various embodiments, the buffer layer 14 may include one or more layers of InAlAs, InAlSb, indium gallium arsenide (InGaAs), indium gallium phosphide (InGaP), indium aluminum arsenide antimonide (InAlAsSb), indium gallium aluminum antimonide (InGaAlSb), aluminum gallium arsenide antimonide (AlGaAsSb), and indium gallium arsenide antimonide (InGaAsSb), with possible ingredient concentrations for each of these materials. The buffer layer 14 is desired to be electrically insulating.
The buffer layer 14 provides a better lattice match for the nanowire 18 than the substrate 12. Accordingly, defects such as misfit dislocations, slip planes, and stacking faults can be reduced or eliminated. Further, other desirable properties, such as electrical confinement and insulation, can be maintained by selecting the appropriate material for the buffer layer 14. The buffer layer 14 may have a thickness between 100 nm and 50000 nm. The buffer layer 14 is not limited in its thickness, and thus can provide a much larger transition in lattice constant while maintaining other desirable characteristics of the substrate 12 such as electrical insulation. The present disclosure contemplates any and all permutations and combinations of the above mentioned materials and thicknesses for the substrate 12, the buffer layer 14, the patterned mask 16, the nanowire 18, and the superconductor 20.
In one exemplary embodiment, the substrate 12 is In P, and has a thickness of 350 μm. The buffer layer 14 includes several layers, including a first layer of In0.52Al0.48As having a thickness of 100 nm on the substrate 12, a second layer of In0.53Ga0.47As having a thickness of 2.5 nm on the first layer, a third layer of In0.52Al0.48As having a thickness of 2.5 nm on the second layer, a fourth layer on the third layer, the fourth layer transitioning from In0.52Al0.48As to In0.89Al0.11As over a thickness of 1000 nm, for example, as 20 discrete layers having a thickness of 50 nm, a fifth layer of InAl0.20As having a thickness of 33 nm on the fourth layer, a sixth layer of InAl0.20As having a thickness of 25 nm on the fifth layer, a seventh layer of InGa0.20As having a thickness of 20 nm on the sixth layer, and an eighth layer of InGa0.30As having a thickness of 17 nm on the seventh layer. The nanowire 18 is InAs on the eighth layer of the buffer layer 14. The various layers of the buffer layer 14 provide a transition in lattice constant between the substrate 12 and the nanowire 18. Notably, the particular configuration of the buffer layer 14, including the number of layers, the thickness of each layer, and the material composition of each layer are merely exemplary and are not intended to limit the scope of the present disclosure in any way.
In another exemplary embodiment, the substrate 12 is GaSb and has a thickness of 350 μm. The buffer layer 14 includes a first layer of GaSb having a thickness of 500 nm, a second layer of Al0.8Ga0.2As0.07Sb0.93 having a thickness of 50 nm on the first layer, and a third layer of InGaAs having a thickness of 2 monolayers (ML) on the second layer. The nanowire 18 is InAs having a thickness of 150 nm. Those skilled in the art will appreciate that GaSb has a lattice constant that is relatively close to that of InAs. However, other properties (e.g., electrical confinement and isolation) of GaSb may not be ideal as a platform for the nanowire 18. The buffer layer 14 may thus primarily be provided in this embodiment to provide one or more other desirable properties (e.g., electrical confinement and isolation), rather than for lattice matching.
In quantum computing, the nanowires are utilized to host and transmit quantum states emerging from the electrons in the structure, which are desired to move consistently and uniformly. Therefore, each surface of the nanowire 18 is desired to be smooth to decrease scattering of the electrons. Since the nanowire 18 is formed over the top surface of the buffer layer 14 (more details described below), the top surface of the buffer layer 14 is required to be a planarized surface. The “planarized surface” as referred to herein is a surface with a vertical roughness below 10 Å, or desirably below 5 Å.
Initially, the substrate 12 is provided as depicted in
To eliminate the uneven top surface of the intact buffer region 14R, a planarization process is introduced. The planarization process, which may be implemented by a chemical and mechanical polishing (CMP) technique, eliminates a sacrificial top portion 14S (with the uneven top surface) of the intact buffer region 14R to provide the buffer layer 14 with the planarized top surface (step 104) as depicted in
With reference to
A mask layer 16M is firstly provided over the planarized top surface of the buffer layer 14 (step 106), as illustrated in
After the patterned mask 16 is formed, the nanowire 18 is grown over the top surface of the buffer layer 14 through the opening 22 of the patterned mask 16 (step 114), as illustrated in
Those skilled in the art will recognize improvements and modifications to the preferred embodiments of the present disclosure. All such improvements and modifications are considered within the scope of the concepts disclosed herein and the claims that follow.