The present disclosure is directed to a seal bar, a seal bar apparatus, and a process for sealing a flexible fitment between two flexible films.
Known are flexible pouches with rigid pour spouts for storage and delivery of flowable materials, often referred to as “pour-pouches.” Many conventional pour-pouches utilize a rigid pour spout, with the base of the spout having winglets. Each winglet is a structure that is perpendicular to the base, each winglet extends radially away (in opposing directions) from the annular base of the spout. Winglets are used to increase the surface area of the annular base in order to promote adhesion between the spout and flexible packaging film.
Winglets, however, are problematic because they require a specialized heat seal bar to effectively seal the winglet to flexible film packaging. The specialized heat seal bar requires a unique shape that mates with the shape of the spout base and winglet. In addition, the heat seal process requires precise and mated alignment between the spout and the films to ensure the spout is in parallel alignment with the film orientation.
As such, the production of flexible pouches is replete with inefficiency due to (1) the expense of specialized heat seal equipment, (2) the production down-time for precise seal bar-winglet alignment, (3) the production down-time required for precise spout-film alignment, (4) the failure rate (leaks) due to misalignment, and (5) the quality control steps required at each stage of pour-pouch production.
The art recognizes the need for alternative equipment and processes in the production of pour-pouches. The art further recognizes the need for improved pour spouts that avoid the production drawbacks of spouts having winglets.
The present disclosure provides a seal bar, a seal bar apparatus and a process for sealing a fitment to a pour-pouch. The present fitment reduces the amount of materials used to produce the fitment itself and also simplifies the pour-pouch production process.
The present disclosure provides a seal bar. In an embodiment, the seal bar comprises a base member having a flat front surface and a flat recessed surface a distance (d) behind the front surface. The front surface defines an x-axis, X. The flat recessed surface has a first endpoint (A1), wherein an axis that is perpendicular to the flat recessed surface at the first endpoint (A1) defines a first y-axis (Y1). The seal bar has a concave surface extending the distance (d) between the first endpoint (A1) and a point (B1) on the flat front surface. The concave surface defines a quadrant arc segment of an ellipse between the first endpoint (A1) and the point (B1).
The present disclosure provides a seal bar apparatus. In an embodiment, the seal bar apparatus includes a first seal bar and a second seal bar. Each seal bar is the same, and has the structure and geometry of the seal bar disclosed above. The first seal bar and the second seal bar oppose each other. The flat front surface of the first seal bar faces the flat front surface of the second seal bar.
The present disclosure provides a process. In an embodiment, the process includes (A) providing the seal bar apparatus disclosed above. The process includes (B) providing a fitment with a base. The base comprises an ethylene/α-olefin multi-block copolymer. The process includes (C) placing the base between two opposing multilayer films. Each multilayer film has a respective seal layer comprising an olefin-based polymer. The placing step forms a film/base/film sandwich. The process includes (D) positioning the film/base/film sandwich between the opposing first seal bar and the second seal bar of the seal bar apparatus. The process includes (E) sealing the base to each multilayer film with the opposing heated seal bars.
An advantage of the present disclosure is a seal bar, or a pair of seal bars, for improved single stage heat sealing a fitment to flexible films.
An advantage of the present disclosure is a pair of seal bars embodying a unique elliptical arc geometry.
An advantage of the present disclosure is a pour-pouch production process that requires less time (greater efficiency) and fewer failures (higher productivity) compared to pour-pouch production processes utilizing spouts with winglets.
An advantage of the present disclosure is a flexible fitment with resiliency to spring back to an open position after full collapse during heat seal, the fitment made from ethylene/α-olefin multi-block copolymer that is compatible with seal layer polyolefins.
All references to the Periodic Table of the Elements herein shall refer to the Periodic Table of the Elements, published and copyrighted by CRC Press, Inc., 2003. Also, any references to a Group or Groups shall be to the Groups or Groups reflected in this Periodic Table of the Elements using the IUPAC system for numbering groups. Unless stated to the contrary, implicit from the context, or customary in the art, all parts and percents are based on weight. For purposes of United States patent practice, the contents of any patent, patent application, or publication referenced herein are hereby incorporated by reference in their entirety (or the equivalent US version thereof is so incorporated by reference), especially with respect to the disclosure of synthetic techniques, definitions (to the extent not inconsistent with any definitions provided herein) and general knowledge in the art.
The numerical ranges disclosed herein include all values from, and including, the lower value and the upper value. For ranges containing explicit values (e.g., 1 or 2, or 3 to 5, or 6, or 7) any subrange between any two explicit values is included (e.g., 1 to 2; 2 to 6; 5 to 7; 3 to 7; 5 to 6; etc.).
Unless stated to the contrary, implicit from the context, or customary in the art, all parts and percents are based on weight, and all test methods are current as of the filing date of this disclosure.
The term “composition,” as used herein, refers to a mixture of materials which comprise the composition, as well as reaction products and decomposition products formed from the materials of the composition.
The terms “comprising,” “including,” “having,” and their derivatives, are not intended to exclude the presence of any additional component, step or procedure, whether or not the same is specifically disclosed. In order to avoid any doubt, all compositions claimed through use of the term “comprising” may include any additional additive, adjuvant, or compound, whether polymeric or otherwise, unless stated to the contrary. In contrast, the term, “consisting essentially of” excludes from the scope of any succeeding recitation any other component, step or procedure, excepting those that are not essential to operability. The term “consisting of” excludes any component, step or procedure not specifically delineated or listed.
Density is measured in accordance with ASTM D 792 with values reported in grams per cubic centimeter, g/cc.
Elastic recovery is measured as follows. Stress-strain behavior in uniaxial tension is measured using an Instron™ universal testing machine at 300% min−1 deformation rate at 21° C. The 300% elastic recovery is determined from a loading followed by unloading cycle to 300% strain, using ASTM D 1708 microtensile specimens. Percent recovery for all experiments is calculated after the unloading cycle using the strain at which the load returned to the base line. The percent recovery is defined as:
% Recovery=100*(Ef−Es)/Ef
where Ef is the strain taken for cyclic loading and Es is the strain where the load returns to the baseline after the unloading cycle.
An “ethylene-based polymer,” as used herein is a polymer that contains more than 50 mole percent polymerized ethylene monomer (based on the total amount of polymerizable monomers) and, optionally, may contain at least one comonomer.
Melt flow rate (MFR) is measured in accordance with ASTM D 1238, Condition 280° C./2.16 kg (g/10 minutes).
Melt index (MI) is measured in accordance with ASTM D 1238, Condition 190° C./2.16 kg (g/10 minutes).
Shore A hardness is measured in accordance with ASTM D 2240.
Tm or “melting point” as used herein (also referred to as a melting peak in reference to the shape of the plotted DSC curve) is typically measured by the DSC (Differential Scanning calorimetry) technique for measuring the melting points or peaks of polyolefins as described in U.S. Pat. No. 5,783,638. It should be noted that many blends comprising two or more polyolefins will have more than one melting point or peak, many individual polyolefins will comprise only one melting point or peak.
An “olefin-based polymer,” as used herein is a polymer that contains more than 50 mole percent polymerized olefin monomer (based on total amount of polymerizable monomers), and optionally, may contain at least one comonomer. Nonlimiting examples of olefin-based polymer include ethylene-based polymer and propylene-based polymer.
A “polymer” is a compound prepared by polymerizing monomers, whether of the same or a different type, that in polymerized form provide the multiple and/or repeating “units” or “mer units” that make up a polymer. The generic term polymer thus embraces the term homopolymer, usually employed to refer to polymers prepared from only one type of monomer, and the term copolymer, usually employed to refer to polymers prepared from at least two types of monomers. It also embraces all forms of copolymer, e.g., random, block, etc. The terms “ethylene/α-olefin polymer” and “propylene/α-olefin polymer” are indicative of copolymer as described above prepared from polymerizing ethylene or propylene respectively and one or more additional, polymerizable α-olefin monomer. It is noted that although a polymer is often referred to as being “made of” one or more specified monomers, “based on” a specified monomer or monomer type, “containing” a specified monomer content, or the like, in this context the term “monomer” is understood to be referring to the polymerized remnant of the specified monomer and not to the unpolymerized species. In general, polymers herein are referred to has being based on “units” that are the polymerized form of a corresponding monomer.
A “propylene-based polymer” is a polymer that contains more than 50 mole percent polymerized propylene monomer (based on the total amount of polymerizable monomers) and, optionally, may contain at least one comonomer.
The present disclosure provides a seal bar. The seal bar includes a base member having a flat front surface, a flat recessed surface, and a concave surface extending between the flat front surface and the flat recessed surface. The flat recessed surface is located a distance (d) behind the flat front surface. The flat front surface defines an x-axis, X. The recessed surface has a first endpoint (A1). An axis that is perpendicular to the flat recessed surface at the first endpoint (A1) defines a first y-axis (Y1). The concave surface extends the distance (d) between a point (B1) on the flat front surface and the first endpoint (A1) on the flat recessed surface. The concave surface defines a quadrant arc segment of an ellipse between the first endpoint (A1) and the point (B1).
1. Seal Bar
Referring to the drawings, and initially to
In an embodiment, heat sealing includes radio frequency sealing, ultrasonic welding, and combinations thereof.
It is understood that seal bar 210 has the same components as the seal bar 10, with the description of seal bar 10 applying equally to seal bar 210. The reference numerals for the seal bar 210 are the same as the reference numerals for the components of the seal bar 10, with the understanding that the components for the seal bar 210 will begin with the numeral “2.” For example, seal bar 210 is a second seal bar with the same structure and geometry as seal bar 10, seal bar 210 disposed in mirror image relation with respect to seal bar 10. The seal bar 210 has the same structure as seal bar 10 and the first digit “2” in the reference numeral for seal bar “210” designating the “second” seal bar 210.
The seal bar 10 includes a base member 12 having a flat front surface 14 and a flat recessed surface 16. For clarity, the first seal bar has a base member 12 having a flat front surface 14. Correspondingly, the second seal bar 210 has a base member 212 with a flat front surface 214. The flat recessed surface 16 is located a distance (d) behind the flat front surface. The flat recessed surface 16 has opposing endpoints, depicted as a first endpoint (A1) and a second endpoint (A2) as shown in
In an embodiment, the distance between (A1) and (A2) is from 14.0 mm, or 15.0 mm, or 16.0 mm, or 16.4 mm, or 16.8 mm to 17.2 mm, or 18.0 mm, or 19.0 mm or 20.0 mm.
In an embodiment, the seal bars are tailored to the fitment and to the films used to make the flexible container. The distances of Length, LA1+Length LA2 is sufficient to allow closure of seal bars with the collapsed fitment and films inside and also provide contact pressure at the concave surfaces of the seal bar to the fitment and films.
The seal bar end proximate to the first endpoint (A1) will hereafter be referred to as the first seal bar end. The seal bar end proximate to the second endpoint (A2) will hereafter be referred to as the second seal bar end.
The flat front surface 14 defines an x-axis, X, as shown in
At the first end of the seal bar 10,
Similarly, at the second end of the seal bar 10,
The unique geometry of the present seal bar is depicted with the front elevation view of the seal bars 10, 210 as the reference, as shown in
An “ellipse,” as used herein, is a plane curve such that the sum of the distances of each point in its periphery from two fixed points, the foci, are equal. The ellipse has a center which is the midpoint of the line segment linking the two foci. The ellipse has a major axis (the longest diameter through the center). The minor axis is the shortest line through the center. The ellipse center is the intersection of the major axis and the minor axis. A “circle” is a specific form of ellipse, where the two focal points are in the same place (at the circle's center). The term “ellipse,” as used herein, excludes the circle.
The concave surface 18 defines a quadrant arc segment of ellipse E1.
wherein
the center of the ellipse E1 is point (C1), the intersection of the x-axis and the first y-axis, (Y1);
x1 is the ellipse semi-major axis;
y1 is the ellipse semi-minor axis having the length (d); and
R1 is the ratio of the semi-major axis (x1) divided by the semi-minor axis (y1) and R1 is from 0.6 to 3.0.
In an embodiment, Equation (1) includes:
distance d from 0.3 mm, or 0.4 mm, or 0.5 mm, or 0.6 mm, or 0.7 mm, or 0.8 mm, or 0.9 mm, or 1.0 mm to 1.2 mm, or 1.5 mm, or 1.7 mm, or 1.9 mm, or 2.0 mm;
x1 from 0.1 mm, or 0.5 mm, 0.8 mm, or 1.0 mm, or 1.5 mm, 1.6 mm, or 2.0 mm, or 3.0 mm, or 4.0 mm, or 5.0 mm, or 6.0 mm to 7.0 mm, or 8.0 mm, or 9.0 mm, or 10.0 mm, or 11.0 mm, or 12.0 mm; and
R1 from 0.6, or 0.8, or 1.0, or 1.05, or 1.09 to 1.8, or 1.9, or 2.0, or 2.5 or 3.0. In a further embodiment, R1 is from greater than 1.0, or 1.1, or 1.2, or 1.3, or 1.5 to 2.0, or 2.5 or 3.0.
In an embodiment, distance d is the same as the thickness t, the wall thickness of the fitment base.
The concave surface 18 is the quadrant arc segment of the elliptical quadrant sector defined by first endpoint (A1) on the flat recessed surface, point (B1) on the flat front surface, and point (C1), the origin of ellipse E1. The concave surface 18 is the quadrant arc segment of ellipse E1 between first endpoint A1 and point B1.
In an embodiment, the distance between (B1) and (C1) is from 0.1 mm, or 0.5 mm, or 0.8 mm, or 1.0 mm, or 1.5 mm, or 1.6 mm, or 2.0 mm, or 3.0 mm, or 4.0 mm, or 5.0 mm, or 6.0 mm to 7.0 mm, or 8.0 mm, or 9.0 mm, or 10.0 mm, or 11.0 mm, or 12.0 mm. In a further embodiment, the distance between (B1) and (C1) is the same as the value for x1.
On the second side of the seal bar 10, the concave surface 118 defines a quadrant arc segment of a second ellipse, ellipse E2.
wherein
the center of the second ellipse E2 is point (C2), the intersection of the x-axis and the second y-axis, (Y2);
x2 is the ellipse semi-major axis;
y2 is the ellipse semi-minor axis having the length (d); and
R2 is the ratio of the semi-major axis (x2) divided by the semi-minor axis (y2), and R2 is from 0.6 to 3.0.
In an embodiment, Equation (2) includes:
distance d from 0.3 mm, or 0.4 mm, or 0.5 mm, or 0.6 mm, or 0.7 mm, or 0.8 mm, or 0.9 mm, or 1.0 mm to 1.2 mm, or 1.5 mm, or 1.7 mm, or 1.9 mm, or 2.0 mm;
x2 from 0.1 mm, or 0.5 mm, or 0.8 mm, or 1.0 mm, or 1.5 mm, or 1.6 mm, or 2.0 mm, or 3.0 mm, or 4.0 mm, or 5.0 mm, or 6.0 mm to 7.0 mm, or 8.0 mm, or 9.0 mm, or 10.0 mm, or 11.0 mm, or 12.0 mm; and
R2 is from 0.6, or 0.8, or 1.0, or 1.05, or 1.09 to 1.8, or 1.9, or 2.0, or 2.5, or 3.0. In a further embodiment, R2 is from greater than 1.0, or 1.1, or 1.2, or 1.3, or 1.5 to 2.0, or 2.5 or 3.0.
The concave surface 118 is the quadrant arc segment of the elliptical quadrant sector defined by point (A2) on the flat recessed surface, point (B2) on the flat front surface, and point (C2), the origin of second ellipse E2. The concave surface 118 is the quadrant arc segment of the second ellipse E2 between the second endpoint A2 and the point B2.
In an embodiment, the distance between (B2) and (C2) is from is from 0.1 mm, or 0.5 mm, 0.8 mm, or 1.0 mm, or 1.5 mm, 1.6 mm, or 2.0 mm, or 3.0 mm, or 4.0 mm, or 5.0 mm, or 6.0 mm to 7.0 mm, or 8.0 mm, or 9.0 mm, or 10.0 mm, or 11.0 mm, or 12.0 mm. In a further embodiment, the distance between (B1) and (C1) is the same as the value for x2.
2. Seal Bar Apparatus
The seal bar apparatus 300 includes the first seal bar 10 and the second seal bar 210. The first seal bar 10 and the second seal bar 210 have the same, or substantially the same structure, geometry, and construction as previously disclosed. The first seal bar 10 and the second seal bar 210 oppose each other such that the flat front surface 14 of the first seal bar 10 faces the flat front surface 214 of the second seal bar 210 as shown in
In an embodiment, the distance between (A1) and (A2) is from 14.0 mm, or 15.0 mm, or 16.0 mm, or 16.4 mm, or 16.8 mm to 17.2 mm, or 18.0 mm, or 19.0 mm, or 20.0 mm.
In an embodiment, the distance between (B1) and (B2) is from 18.0 mm, or greater than 18.0 mm, or 18.5 mm, or 18.9 m to 19.0 mm, or 19.5 mm, or 20.0 mm. In a further embodiment, the distance between (B1) and (B2) is 1.12 times the distance between (A1) and (A2) for any of the distances disclosed in the immediately preceding paragraph.
In an embodiment, the distance between (C1) and (C2) is from 17.0 mm, or 17.5 mm, or 17.9 mm to 18.0 mm.
3. Process
The present disclosure provides a process. In an embodiment, the process includes (A) providing the seal bar apparatus 300 with the first seal bar 10 and the second seal bar 210. The process includes (B) providing a fitment with a base, the base comprising an ethylene/α-olefin multi-block copolymer. The process includes (C) placing the base between two opposing multilayer films, each multilayer film having a respective seal layer comprising an olefin-based polymer and forming a film/base/film sandwich. The process includes (D) positioning the film/base/film sandwich between the opposing first seal bar and the second seal bar of seal bar assembly. The process includes (E) sealing the base to each multilayer film with opposing heated seal bars.
4. Fitment
A fitment 410 has a base 412 and a top 414 as shown in
In an embodiment, the fitment is a tube member. A “tube member” is an elongated hollow cylinder for transporting a flowable material.
In an embodiment, the base is only composed of, or is otherwise formed solely from, the blend of ethylene/α-olefin multi-block copolymer and high density polyethylene.
In an embodiment the entire fitment 410 (the base 412 and the top 414) is only composed of, or is otherwise solely formed from, the polymeric blend of ethylene/α-olefin multi-block copolymer and the high density polyethylene.
In an embodiment, the base has a wall 415, as shown in
The base 412 (and optionally the entire fitment 410) is formed from the polymeric blend of ethylene/α-olefin multi-block copolymer and high density polyethylene. The term “ethylene/α-olefin multi-block copolymer” includes ethylene and one or more copolymerizable α-olefin comonomer in polymerized form, characterized by multiple blocks or segments of two or more polymerized monomer units differing in chemical or physical properties. The term “ethylene/α-olefin multi-block copolymer” includes block copolymer with two blocks (di-block) and more than two blocks (multi-block). The terms “interpolymer” and “copolymer” are used interchangeably herein. When referring to amounts of “ethylene” or “comonomer” in the copolymer, it is understood that this means polymerized units thereof. In some embodiments, the ethylene/α-olefin multi-block copolymer can be represented by the following formula:
(AB)n
Where n is at least 1, preferably an integer greater than 1, such as 2, 3, 4, 5, 10, 15, 20, 30, 40, 50, 60, 70, 80, 90, 100, or higher, “A” represents a hard block or segment and “B” represents a soft block or segment. Preferably, As and Bs are linked, or covalently bonded, in a substantially linear fashion, or in a linear manner, as opposed to a substantially branched or substantially star-shaped fashion. In other embodiments, A blocks and B blocks are randomly distributed along the polymer chain. In other words, the block copolymers usually do not have a structure as follows:
AAA-AA-BBB-BB
In still other embodiments, the block copolymers do not usually have a third type of block, which comprises different comonomer(s). In yet other embodiments, each of block A and block B has monomers or comonomers substantially randomly distributed within the block. In other words, neither block A nor block B comprises two or more sub-segments (or sub-blocks) of distinct composition, such as a tip segment, which has a substantially different composition than the rest of the block.
Preferably, ethylene comprises the majority mole fraction of the whole block copolymer, i.e., ethylene comprises at least 50 mole percent of the whole polymer. More preferably ethylene comprises at least 60 mole percent, at least 70 mole percent, or at least 80 mole percent, with the substantial remainder of the whole polymer comprising at least one other comonomer that is preferably an α-olefin having 3 or more carbon atoms. In some embodiments, the ethylene/α-olefin multi-block copolymer may comprise 50 mol % to 90 mol % ethylene, or 60 mol % to 85 mol %, or 65 mol % to 80 mol %. For many ethylene/octene multi-block copolymers, the composition comprises an ethylene content greater than 80 mole percent of the whole polymer and an octene content of from 10 to 15, or from 15 to 20 mole percent of the whole polymer.
The ethylene/α-olefin multi-block copolymer includes various amounts of “hard” segments and “soft” segments. “Hard” segments are blocks of polymerized units in which ethylene is present in an amount greater than 90 weight percent, or 95 weight percent, or greater than 95 weight percent, or greater than 98 weight percent based on the weight of the polymer, up to 100 weight percent. In other words, the comonomer content (content of monomers other than ethylene) in the hard segments is less than 10 weight percent, or 5 weight percent, or less than 5 weight percent, or less than 2 weight percent based on the weight of the polymer, and can be as low as zero. In some embodiments, the hard segments include all, or substantially all, units derived from ethylene. “Soft” segments are blocks of polymerized units in which the comonomer content (content of monomers other than ethylene) is greater than 5 weight percent, or greater than 8 weight percent, greater than 10 weight percent, or greater than 15 weight percent based on the weight of the polymer. In some embodiments, the comonomer content in the soft segments can be greater than 20 weight percent, greater than 25 weight percent, greater than 30 weight percent, greater than 35 weight percent, greater than 40 weight percent, greater than 45 weight percent, greater than 50 weight percent, or greater than 60 weight percent and can be up to 100 weight percent.
The soft segments can be present in an ethylene/α-olefin multi-block copolymer from 1 weight percent to 99 weight percent of the total weight of the ethylene/α-olefin multi-block copolymer, or from 5 weight percent to 95 weight percent, from 10 weight percent to 90 weight percent, from 15 weight percent to 85 weight percent, from 20 weight percent to 80 weight percent, from 25 weight percent to 75 weight percent, from 30 weight percent to 70 weight percent, from 35 weight percent to 65 weight percent, from 40 weight percent to 60 weight percent, or from 45 weight percent to 55 weight percent of the total weight of the ethylene/α-olefin multi-block copolymer. Conversely, the hard segments can be present in similar ranges. The soft segment weight percentage and the hard segment weight percentage can be calculated based on data obtained from DSC or NMR. Such methods and calculations are disclosed in, for example, U.S. Pat. No. 7,608,668, entitled “Ethylene/α-Olefin Block Interpolymers,” filed on Mar. 15, 2006, in the name of Colin L. P. Shan, Lonnie Hazlitt, et al. and assigned to Dow Global Technologies Inc., the disclosure of which is incorporated by reference herein in its entirety. In particular, hard segment and soft segment weight percentages and comonomer content may be determined as described in Column 57 to Column 63 of U.S. Pat. No. 7,608,668.
The ethylene/α-olefin multi-block copolymer is a polymer comprising two or more chemically distinct regions or segments (referred to as “blocks”) preferably joined (or covalently bonded) in a linear manner, that is, a polymer comprising chemically differentiated units which are joined end-to-end with respect to polymerized ethylenic functionality, rather than in pendent or grafted fashion. In an embodiment, the blocks differ in the amount or type of incorporated comonomer, density, amount of crystallinity, crystallite size attributable to a polymer of such composition, type or degree of tacticity (isotactic or syndiotactic), regio-regularity or regio-irregularity, amount of branching (including long chain branching or hyper-branching), homogeneity or any other chemical or physical property. Compared to block interpolymers of the prior art, including interpolymers produced by sequential monomer addition, fluxional catalysts, or anionic polymerization techniques, the present ethylene/α-olefin multi-block copolymer is characterized by unique distributions of both polymer polydispersity (PDI or Mw/Mn or MWD), polydisperse block length distribution, and/or polydisperse block number distribution, due, in an embodiment, to the effect of the shuttling agent(s) in combination with multiple catalysts used in their preparation.
In an embodiment, the ethylene/α-olefin multi-block copolymer is produced in a continuous process and possesses a polydispersity index (Mw/Mn) from 1.7 to 3.5, or from 1.8 to 3, or from 1.8 to 2.5, or from 1.8 to 2.2. When produced in a batch or semi-batch process, the ethylene/α-olefin multi-block copolymer possesses Mw/Mn from 1.0 to 3.5, or from 1.3 to 3, or from 1.4 to 2.5, or from 1.4 to 2.
In addition, the ethylene/α-olefin multi-block copolymer possesses a PDI (or Mw/Mn) fitting a Schultz-Flory distribution rather than a Poisson distribution. The present ethylene/α-olefin multi-block copolymer has both a polydisperse block distribution as well as a polydisperse distribution of block sizes. This results in the formation of polymer products having improved and distinguishable physical properties. The theoretical benefits of a polydisperse block distribution have been previously modeled and discussed in Potemkin, Physical Review E (1998) 57 (6), pp. 6902-6912, and Dobrynin, J. Chem. Phys. (1997) 107 (21), pp 9234-9238.
In an embodiment, the present ethylene/α-olefin multi-block copolymer possesses a most probable distribution of block lengths.
In a further embodiment, the ethylene/α-olefin multi-block copolymer of the present disclosure, especially those made in a continuous, solution polymerization reactor, possess a most probable distribution of block lengths. In one embodiment of this disclosure, the ethylene multi-block interpolymers are defined as having:
(A) Mw/Mn from about 1.7 to about 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, where in the numerical values of Tm and d correspond to the relationship:
Tm>−2002.9+4538.5(d)−2422.2(d)2, or
(B) Mw/Mn from about 1.7 to about 3.5, and is characterized by a heat of fusion, ΔH in J/g, and a delta quantity, ΔT, in degrees Celsius defined as the temperature difference between the tallest DSC peak and the tallest Crystallization Analysis Fractionation (“CRYSTAF”) peak, wherein the numerical values of ΔT and ΔH have the following relationships:
ΔT>−0.1299(ΔH)+62.81 for ΔH greater than zero and up to 130 J/g
ΔT≥48° C. for ΔH greater than 130 J/g
wherein the CRYSTAF peak is determined using at least 5 percent of the cumulative polymer, and if less than 5 percent of the polymer has an identifiable CRYSTAF peak, then the CRYSTAF temperature is 30° C.; or
(C) elastic recovery, Re, in percent at 300 percent strain and 1 cycle measured with a compression-molded film of the ethylene/α-olefin interpolymer, and has a density, d, in grams/cubic centimeter, wherein the numerical values of Re and d satisfy the following relationship when ethylene/α-olefin interpolymer is substantially free of crosslinked phase:
Re>1481−1629(d); or
(D) has a molecular weight fraction which elutes between 40° C. and 130° C. when fractionated using TREF, characterized in that the fraction has a molar comonomer content of at least 5 percent higher than that of a comparable random ethylene interpolymer fraction eluting between the same temperatures, wherein said comparable random ethylene interpolymer has the same comonomer(s) and has a melt index, density and molar comonomer content (based on the whole polymer) within 10 percent of that of the ethylene/α-olefin interpolymer; or
(E) has a storage modulus at 25° C., G′(25° C.), and a storage modulus at 100° C., G′(100° C.), wherein the ratio of G′(25° C.) to G′(100° C.) is in the range of about 1:1 to about 9:1.
The ethylene/α-olefin multi-block copolymer may also have:
(F) molecular fraction which elutes between 40° C. and 130° C. when fractionated using TREF, characterized in that the fraction has a block index of at least 0.5 and up to about 1 and a molecular weight distribution, Mw/Mn, greater than about 1.3; or
(G) average block index greater than zero and up to about 1.0 and a molecular weight distribution, Mw/Mn greater than about 1.3.
Suitable monomers for use in preparing the present ethylene/α-olefin multi-block copolymer include ethylene and one or more addition polymerizable monomers other than ethylene. Examples of suitable comonomers include straight-chain or branched α-olefins of 3 to 30, or 3 to 20, or 4 to 8 carbon atoms, such as propylene, 1-butene, 1-pentene, 3-methyl-1-butene, 1-hexene, 4-methyl-1-pentene, 3-methyl-1-pentene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene and 1-eicosene; cyclo-olefins of 3 to 30, or 3 to 20, carbon atoms, such as cyclopentene, cycloheptene, norbornene, 5-methyl-2-norbornene, tetracyclododecene, and 2-methyl-1,4,5,8-dimethano-1,2,3,4,4a,5,8,8a-octahydronaphthalene; di- and polyolefins, such as butadiene, isoprene, 4-methyl-1,3-pentadiene, 1,3-pentadiene, 1,4-pentadiene, 1,5-hexadiene, 1,4-hexadiene, 1,3-hexadiene, 1,3-octadiene, 1,4-octadiene, 1,5-octadiene, 1,6-octadiene, 1,7-octadiene, ethylidenenorbornene, vinyl norbornene, dicyclopentadiene, 7-methyl-1,6-octadiene, 4-ethylidene-8-methyl-1,7-nonadiene, and 5,9-dimethyl-1,4,8-decatriene; and 3-phenylpropene, 4-phenylpropene, 1,2-difluoroethylene, tetrafluoroethylene, and 3,3,3-trifluoro-1-propene.
In an embodiment, the ethylene/α-olefin multi-block copolymer is void of styrene (i.e., is styrene-free).
The ethylene/α-olefin multi-block copolymer can be produced via a chain shuttling process such as described in U.S. Pat. No. 7,858,706, which is herein incorporated by reference. In particular, suitable chain shuttling agents and related information are listed in Col. 16, line 39 through Col. 19, line 44. Suitable catalysts are described in Col. 19, line 45 through Col. 46, line 19 and suitable co-catalysts in Col. 46, line 20 through Col. 51 line 28. The process is described throughout the document, but particularly in Col. Col 51, line 29 through Col. 54, line 56. The process is also described, for example, in the following: U.S. Pat. No. 7,608,668; U.S. Pat. No. 7,893,166; and U.S. Pat. No. 7,947,793.
In an embodiment, the ethylene/α-olefin multi-block copolymer has hard segments and soft segments, is styrene-free, consists of only (i) ethylene and (ii) a C4-C8 α-olefin comonomer, and is defined as having:
a Mw/Mn from 1.7 to 3.5, at least one melting point, Tm, in degrees Celsius, and a density, d, in grams/cubic centimeter, where in the numerical values of Tm and d correspond to the relationship:
Tm<−2002.9+4538.5(d)−2422.2(d)2,
In an embodiment, the ethylene/α-olefin multi-block copolymer is an ethylene/octene multi-block copolymer (consisting only of ethylene and octene comonomer) and has one, some, any combination of, or all the properties (i)-(ix) below:
(i) a melt temperature (Tm) from 80° C., or 85° C., or 90° C. to 95, or 99° C., or 100° C., or 105° C. to 110° C., or 115° C., or 120° C., or 125° C.;
(ii) a density from 0.86 g/cc, or 0.87 g/cc, or 0.88 g/cc to 0.89 g/cc;
(iii) 50-85 wt % soft segment and 40-15 wt % hard segment;
(iv) from 10 mol %, or 13 mol %, or 14 mol %, or 15 mol % to 16 mol %, or 17 mol %, or 18 mol %, or 19 mol %, or 20 mol % octene in the soft segment;
(v) from 0.5 mol %, or 1.0 mol %, or 2.0 mol %, or 3.0 mol % to 4.0 mol %, or 5 mol %, or 6 mol %, or 7 mol %, or 9 mol % octene in the hard segment;
(vi) a melt index (MI) from 1 g/10 min, or 2 g/10 min, or 5 g/10 min, or 7 g/10 min to 10 g/10 min, or 15 g/10 min to 20 g/10 min;
(vii) a Shore A hardness from 65, or 70, or 71, or 72 to 73, or 74, or 75, or 77, or 79, of 80;
(viii) an elastic recovery (Re) from 50%, or 60% to 70%, or 80%, or 90%, at 300% 300% min·1 deformation rate at 21° C. as measured in accordance with ASTM D 1708.
(ix) a polydisperse distribution of blocks and a polydisperse distribution of block sizes.
In an embodiment, the ethylene/α-olefin multi-block copolymer is an ethylene/octene multi-block copolymer.
The present ethylene/α-olefin multi-block copolymer may comprise two or more embodiments disclosed herein.
In an embodiment, the ethylene/octene multi-block copolymer is sold under the Tradename INFUSE™ is available from The Dow Chemical Company, Midland, Mich., USA. In a further embodiment, the ethylene/octene multi-block copolymer is INFUSE™ 9817.
In an embodiment, the ethylene/octene multi-block copolymer is INFUSE™ 9500.
In an embodiment, the ethylene/octene multi-block copolymer is INFUSE™ 9507.
5. High Density Polyethylene
The base 412 (and optionally the entire fitment 410) is composed of a polymeric blend of the ethylene/α-olefin multi-block copolymer and a high density polyethylene. A “high density polyethylene” (or “HDPE”) is an ethylene homopolymer or an ethylene/α-olefin copolymer with at least one C3-C10 α-olefin comonomer, and has a density from greater than 0.940 g/cc, or 0.945 g/cc, or 0.950 g/cc, or 0.955 g/cc to 0.960 g/cc, or 0.965 g/cc, or 0.970 g/cc, or 0.975 g/cc, or 0.980 g/cc. Nonlimiting examples of suitable comonomers include propylene, 1-butene, 1 pentene, 4-methyl-1-pentene, 1-hexene, and 1-octene. The HDPE includes at least 50 percent by weight units derived from ethylene, i.e., polymerized ethylene, or at least 70 percent by weight, or at least 80 percent by weight, or at least 85 percent by weight, or at least 90 weight percent, or at least 95 percent by weight ethylene in polymerized form. The HDPE can be a monomodal copolymer or a multimodal copolymer. A “monomodal ethylene copolymer” is an ethylene/C4-C10 α-olefin copolymer that has one distinct peak in a gel permeation chromatography (GPC) showing the molecular weight distribution. A “multimodal ethylene copolymer” is an ethylene/C4-C10 α-olefin copolymer that has at least two distinct peaks in a GPC showing the molecular weight distribution. Multimodal includes copolymer having two peaks (bimodal) as well as copolymer having more than two peaks.
In an embodiment, the HDPE has one, some, or all of the following properties: and has one, some, any combination of, or all the properties (i)-(iv) below:
(i) a density from 0.945 g/cc, or 0.950 g/cc, or 0.955 g/cc, or 0.960 g/cc to 0.965 g/cc, or 0.970 g/cc, or 0.975 g/cc, or 0.980 g/cc; and/or
(ii) a melt index (MI) from 0.5 g/10 min, or 1.0 g/10 min, or 1.5 g/10 min, or 2.0 g/10 min to 2.5 g/10 min, or 3.0 g/10 min, or 5.0 g/10 min, or 10.0 g/10 min, or 15.0 g/10 min, or 20.0 g/10 min, or 25.0 g/10 min, or 30.0 g/10 min, or 35.0 g/10 min; and/or
(iii) a melt temperature (Tm) from 125° C., or 128° C., or 130° C. to 132° C., or 135° C., or 137° C.; and/or
(iv) a bimodal molecular weight distribution.
In an embodiment, the HDPE has a density from 0.955 g/cc, or 0.957 g/cc, or 0.959 g/cc to 0.960 g/cc, or 0.963 g/cc, or 0.965 g/cc and has a melt index from 1.0 g/10 min, or 1.5 g/10 min, or 2.0 g/10 min to 2.5 g/10 min, or 3.0 g/10 min.
Nonlimiting examples of suitable, commercially available HDPE include, but are not limited to, Dow High Density Polyethylene resins sold under the trade names CONTINUUM™ and UNIVAL™.
HDPE is distinct from each of the following types of ethylene-based polymer: linear low density polyethylene (LLDPE), metallocene-LLDPE (m-LLDPE), ultra low density polyethylene (ULDPE), very low density polyethylene (VLDPE), multi-component ethylene-based copolymer (EPE), ethylene/α-olefin multi-block copolymer, ethylene plastomers/elastomers, and low density (LDPE), as each polymer is defined in co-pending application U.S. Ser. No. 15/275,842 filed on Sep. 26, 2016, incorporated by reference herein in its entirety.
The base 412 and/or the entire fitment 410 is composed of the ethylene/α-olefin multi-block copolymer/HDPE polymeric blend. The polymeric blend of ethylene/α-olefin multi-block copolymer and HDPE includes from 60 wt %, or 65 wt %, or 70 wt %, or 75 wt % to 80 wt %, or 85 wt %, or 90 wt % of the ethylene/α-olefin multi-block copolymer and a reciprocal amount of HDPE or from 40 wt %, or 35 wt %, or 30 wt %, or 25 wt % to 20 wt %, or 15 wt %, or 10 wt % HDPE.
In an embodiment, the entire fitment is composed of only the ethylene/α-olefin multi-block copolymer and HDPE polymeric blend which includes from 70 wt %, or 73 wt %, or 75 wt % to 78 wt %, or 80 wt %, or 83 wt %, or 85 wt %, or 87 wt %, or 90 wt % of the ethylene/α-olefin multi-block copolymer and a reciprocal amount of HDPE or from 30 wt %, or 27 wt %, or 25 wt % to 22 wt %, or 20 wt %, or 17 wt %, or 15 wt %, or 13 wt %, or 10 wt % of the HDPE.
6. Multilayer Films
The process includes placing the base 412 between two opposing multilayer films 416, 418 to form a film/base/film sandwich 419, as shown in
The fitment base 412 is placed between two opposing multilayer films and subsequently sealed thereto. Each multilayer film 416, 418 has a respective seal layer containing an olefin-based polymer.
In an embodiment, each multilayer film 416, 418 is made from a flexible film having at least one, or at least two, or at least three layers. The flexible film is resilient, flexible, deformable, and pliable. The structure and composition for each flexible film 416, 418 may be the same or may be different. For example, each multilayer film 416, 418 can be made from a separate web, each web having a unique structure and/or unique composition, finish, or print. Alternatively, each multilayer film 416, 418 can be the same structure and the same composition.
The flexible multilayer film is composed of a polymeric material. Nonlimiting examples of suitable polymeric material include olefin-based polymer; propylene-based polymer; ethylene-based polymer; polyamide (such as nylon), ethylene-acrylic acid or ethylene-methacrylic acid and their ionomers with zinc, sodium, lithium, potassium, or magnesium salts; ethylene vinyl acetate (EVA) copolymers; and blends thereof. The flexible multilayer film can be either printable or compatible to receive a pressure sensitive label or other type of label for displaying of indicia on the flexible container 442.
In an embodiment, a flexible multilayer film is provided and includes at least three layers: (i) an outermost layer, (ii) one or more core layers, and (iii) an innermost seal layer. The outermost layer (i) and the innermost seal layer (iii) are surface layers with the one or more core layers (ii) sandwiched between the surface layers. The outermost layer may include (a-i) a HDPE, (b-ii) a propylene-based polymer, or combinations of (a-i) and (b-ii), alone, or with other olefin-based polymers such as LDPE. Nonlimiting examples of suitable propylene-based polymers include propylene homopolymer, random propylene/α-olefin copolymer (majority amount propylene with less than 10 weight percent ethylene comonomer), and propylene impact copolymer (heterophasic propylene/ethylene copolymer rubber phase dispersed in a matrix phase).
With the one or more core layers (ii), the number of total layers in the present multilayer film (416, 418) can be from three layers (one core layer), or four layers (two core layers), or five layers (three core layers, or six layers (four core layers), or seven layers (five core layers) to eight layers (six core layers), or nine layers (seven core layers), or ten layers (eight core layers), or eleven layers (nine core layers), or more.
Each multilayer film 416, 418 has a thickness from 75 microns, or 100 microns, or 125 microns, or 150 microns to 200 microns, or 250 microns or 300 microns or 350 microns, or 400 microns.
In an embodiment, each multilayer film 416, 418 a flexible multilayer film having the same structure and the same composition.
The flexible multilayer film 416, 418 may be (i) a coextruded multilayer structure or (ii) a laminate, or (iii) a combination of (i) and (ii). In an embodiment, the flexible multilayer film has at least three layers: a seal layer, an outer layer, and a tie layer between. The tie layer adjoins the seal layer to the outer layer. The flexible multilayer film may include one or more optional inner layers disposed between the seal layer and the outer layer.
In an embodiment, the flexible multilayer film is a coextruded film having at least two, or three, or four, or five, or six, or seven to eight, or nine, or 10, or 11, or more layers. Some methods, for example, used to construct films are by cast co-extrusion or blown co-extrusion methods, adhesive lamination, extrusion lamination, thermal lamination, and coatings such as vapor deposition. Combinations of these methods are also possible. Film layers can comprise, in addition to the polymeric materials, additives such as stabilizers, slip additives, antiblocking additives, process aids, clarifiers, nucleators, pigments or colorants, fillers and reinforcing agents, and the like as commonly used in the packaging industry. It is particularly useful to choose additives and polymeric materials that have suitable organoleptic and/or optical properties.
In an embodiment, the outermost layer includes a HDPE. In a further embodiment, the HDPE is a substantially linear multi-component ethylene-based copolymer (EPE) such as ELITE′″ resin provided by The Dow Chemical Company.
In an embodiment, each core layer includes one or more linear or substantially linear ethylene-based polymers or block copolymers having a density from 0.908 g/cc, or 0.912 g/cc, or 0.92 g/cc, or 0.921 g/cc to 0.925 g/cc, or less than 0.93 g/cc. In an embodiment, each of the one or more core layers includes one or more ethylene/C3-C8 α-olefin copolymers selected from linear low density polyethylene (LLDPE), ultralow density polyethylene (ULDPE), very low density polyethylene (VLDPE), EPE, olefin block copolymer (OBC), plastomers/elastomers, and single-site catalyzed linear low density polyethylenes (m-LLDPE).
In an embodiment, the seal layer includes one or more ethylene-based polymers having a density from 0.86 g/cc, or 0.87 g/cc, or 0.875 g/cc, or 0.88 g/cc, or 0.89 g/cc to 0.90 g/cc, or 0.902 g/cc, or 0.91 g/cc, or 0.92 g/cc. In a further embodiment, the seal layer includes one or more ethylene/C3-C8 α-olefin copolymers selected from EPE, plastomers/elastomers, or m-LLDPE.
In an embodiment, the flexible multilayer film is a coextruded film, the seal layer is composed of an ethylene-based polymer, such as a linear or a substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin monomer such as 1-butene, 1-hexene or 1-octene, having a Tm from 55° C. to 115° C. and a density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3 and the outer layer is composed of a polyamide having a Tm from 170° C. to 270° C.
In an embodiment, the flexible multilayer film is a coextruded and/or laminated film having at least five layers, the coextruded film having a seal layer composed of an ethylene-based polymer, such as a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin comonomer such as 1-butene, 1-hexene or 1-octene, the ethylene-based polymer having a Tm from 55° C. to 115° C. and a density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3 and an outermost layer composed of a material selected from HDPE, EPE, LLDPE, OPET (biaxially oriented polyethylene terephthalate), OPP (oriented polypropylene), BOPP (biaxially oriented polypropylene), polyamide, and combinations thereof.
In an embodiment, the flexible multilayer film is a coextruded and/or laminated film having at least seven layers. The seal layer is composed of an ethylene-based polymer, such as a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin comonomer such as 1-butene, 1-hexene or 1-octene, the ethylene-based polymer having a Tm from 55° C. to 115° C. and density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3. The outer layer is composed of a material selected from HDPE, EPE, LLDPE, OPET, OPP, BOPP, polyamide, and combinations thereof.
In an embodiment, the flexible multilayer film is a coextruded (or laminated) film of three or more layers where all layers consist of ethylene-based polymers. In a further embodiment, the flexible multilayer film is a coextruded (or laminated) film of three or more layers where each layer consists of ethylene-based polymers and (1) the seal layer is composed of a linear or substantially linear ethylene-based polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin comonomer such as 1-butene, 1-hexene or 1-octene, the ethylene-based polymer having a Tm from 55° C. to 115° C. and density from 0.865 to 0.925 g/cm3, or from 0.875 to 0.910 g/cm3, or from 0.888 to 0.900 g/cm3 and (2) the outer layer includes one or more ethylene-based polymers selected from HDPE, EPE, LLDPE or m-LLDPE and (3) each of the one or more core layers includes one or more ethylene/C3-C8 α-olefin copolymers selected from low density polyethylene (LDPE), linear low density polyethylene (LLDPE), ultralow density polyethylene (ULDPE), very low density polyethylene (VLDPE), EPE, olefin block copolymer (OBC), plastomers/elastomers, and single-site catalyzed linear low density polyethylenes (m-LLDPE).
In an embodiment, the flexible multilayer film is a coextruded and/or laminated five layer, or a coextruded (or laminated) seven layer film having at least one layer containing OPET or OPP.
In an embodiment, the flexible multilayer film is a coextruded (or laminated) five layer, or a coextruded (or laminated) seven layer film having at least one layer containing polyamide.
In an embodiment, the flexible multilayer film is a seven-layer coextruded (or laminated) film with a seal layer composed of an ethylene-based polymer, or a linear or substantially linear polymer, or a single-site catalyzed linear or substantially linear polymer of ethylene and an alpha-olefin monomer such as 1-butene, 1-hexene or 1-octene, having a Tm from 90° C. to 106° C. The outer layer is a polyamide having a Tm from 170° C. to 270° C. The film has an inner layer (first inner layer) composed of a second ethylene-based polymer, different than the ethylene-based polymer in the seal layer. The film has an inner layer (second inner layer) composed of a polyamide the same or different to the polyamide in the outer layer. The seven layer film has a thickness from 100 micrometers to 250 micrometers.
7. Sealing
The present process includes positioning the film/base/film sandwich between the opposing seal bars 10, 210 as shown in
The sealing step includes adjoining, or otherwise welding, each multilayer film 416, 418 to respective upper portion 413a and a lower portion 413b of the base 412 as shown in
In an embodiment, the process includes:
(i) selecting, for the base 412, an ethylene/α-olefin multi-block copolymer having a melt temperature, Tm1, from 115° C. to 125° C.;
(ii) selecting, for the seal layers, an olefin-based polymer having a melt temperature, Tm2, such that Tm2 is from 10° C. to 40° C. less than Tm1.
In an embodiment, Tm2 is from 10° C., or 15° C., or 20° C. to 25° C., or 30° C., or 35° C., or 40° C. less than Tm1.
In an embodiment, each seal layer is formed from an ethylene-based polymer with a Tm2 from 10° C. to 40° C. less than the Tm1 of the ethylene/α-olefin multi-block copolymer in the base 12. The flat seal bars 20, 22 are heated to a temperature greater than or equal to the melt temperature (Tm2) of the seal layer ethylene-based polymer and less than or equal to the melt temperature, Tm1 (or to at least the softening temperature of the ethylene/α-olefin multi-block copolymer), of the base 412. The compression force and heat imparted by the opposing flat bars flat seal bars 10, 210 simultaneously (i) flatten, or otherwise deform, the base 412; (ii) compress the seal layer of each multilayer film 416, 418 against the outer surface of the base 412; (iii) form a seal joint 424 and a seal joint 426 on opposing ends of the flattened base 412; (iv) melt the ethylene-based polymer in the seal layers, (v) soften and/or melt at least some of the ethylene/α-olefin multi-block copolymer present in the base 412, (vi), form a flowable caulk 428 composed of (a) the ethylene/α-olefin multi-block copolymer from the base, (b) the ethylene-based polymer from the seal layers, or (c) a combination of (a) and (b); and (vii) weld upper portion/lower portion 413a, 413b to respective seal layers of films 416, 418.
In an embodiment, the sealing step entails one, some or all of the following seal conditions:
(i) a temperature from 160° C., or 170° C. to 180° C., or 190° C., or 200° C.;
(ii) a pressure (or seal force) from 1 MegaPascals (MPa) to 2 MPa;
(iii) application of (i) and/or (ii) for a duration (seal time or dwell time) from 0.1 seconds, or 0.5 seconds, or 0.75 seconds, or 1.0 second, or 2.0 seconds, or 3.0 seconds, or 4.0 seconds, or 5.0 seconds to 6.0 seconds, or 7.0 seconds, or 0.75 seconds, or 8.0 seconds, or 9.0 seconds or 10 seconds.
The compression force fully collapses the base 412 upon itself, so that opposing flattened sides of the base contact each other, closing the base 412, and giving the base 412 a linear configuration F as shown in
In an embodiment, the compression force and the heating of the closed seal bars 10, 210 forces the flowable caulk 428 to move, or otherwise flow, from the outer surface of the base 412 and into the seal joint 424 and into the seal joint 426. The caulk 428 flows into, and fills (wholly or partially), seal joint 424 and seal joint 426 as shown in
The process includes opening the closed seal bars 10, 210, thereby removing the compression force and removing the heat from the base 412. When the closed seal bars 10, 210 are opened, the elasticity provided by the ethylene/α-olefin multi-block copolymer in the base 412 enables the base 412 to recoil, or otherwise spring back, from the linear, compressed configuration F and return to an open position as shown in
In an embodiment, the post-flattened base 412 can have either a circular or an elliptical cross-section G as shown in
The opening of the closed seal bars forms a welded construction 430 as shown in
The sealing step applies a compressive and pinching force for sufficient duration to enable the caulk 428 to set and solidify, thereby firmly bonding the multilayer films 416, 418 to the base 412 at the seal joints 424, 426. The solidified caulk 428 forms in situ winglets 436, 438 (
In an embodiment, the process includes forming the winglet 436 and/or the winglet 438 having a length H (
8. Flexible Container
The process includes forming a flexible container. The opposing multilayer films 416, 418 are superimposed on each other and form a common peripheral edge 440 as shown in
The heat and stress of flat bar sealing of fitment to film to make containers is limited. A fitment composed of low elasticity polyolefin (e.g., LDPE, HDPE) crushes, cracks, breaks, and is unusable. A fitment composed of a polyolefin elastomer (e.g., ENGAGE or VERSIFY elastomers) can exhibit deformation, yet does not recover adequately or welds shut. A fitment composed of a crosslinked elastomer (e.g., TPV) may fully recover but does not seal adequately and does not form a hermetic seal. Applicant surprisingly discovered that a fitment composed of the present polymeric blend of ethylene/α-olefin multi-block copolymer and HDPE recovers (recoils), will not seal to itself, and will seal the fitment to the film of the container using heat seal bars.
Nonlimiting examples for seal bar parameters fulfilling Equation (1) and Equation (2) based on fitment wall thickness, t, and values for seal bars 10, 210 are provided as scenarios A, B, and C shown in Table 1 below.
By way of example, and not limitation, examples of the present disclosure are provided.
1. Seal Bars
A seal bar apparatus is used to produce flexible pouches by heat sealing fitments to multilayer films. The seal bar apparatus has opposing seal bars with the structure of seal bars 10, 210 as shown in
Flexible multilayer films with structures shown in Table 3 below are used in the present examples.
2. Multilayer Films
3. Fitments
Nine comparative samples (CS) and four inventive examples (IE) of fitments are prepared. The dimensions for each fitment are identical, with only the material varying across the fitments. The CS fitments are composed of 100 wt % INFUSE 9817. The inventive fitments are composed of 70 wt % INFUSE 9817 and 30 wt % DMDC-1250 NT 7 HDPE. Each fitment has a base wall with a thickness (thickness t) of 0.8 mm and a base inside diameter of 12.5 mm. The base has an outside diameter of 14.1 mm as presented in Table 2 above.
The material and composition for fitments are shown in Table 4 below.
4. Processing Conditions
Each fitment is placed between two opposing films of Film 1 (from Table 3), with seal layers facing each other to form a film/base/film sandwich as shown in
Each film/base/film sandwich is subjected to a heat sealing procedure using a seal bar apparatus as depicted by seal bar apparatus 300 (with opposing seal bars 10, 210). The heat seal conditions are provided in Table 5 below.
The heat sealing procedure produces flexible containers that are stand-up pouches (SUPs) as shown in
5. Leak Test
The Lippke test evaluates additional seal integrity for the SUPs. The Lippke test perforates the flexible container with a needle and air pressurized to 150 mbar according to the conditions as described in Table 6 below. After 60 seconds, the pressure gap is registered. If the flexible container has no failure, the pressure will remain the same. The flexible container sample is submerged into a water tank so that air bubbles can be observed coming out of fissure or failure where it exists. The Lippke test determines whether the failure comes from the triple sealing point or from different sources such as poor fitment-closure junction.
Leak test for the flexible containers is performed under the following parameters.
The flexible container is subjected to an internal pressure of 150 mbar. The test entails waiting 10 seconds for settling. The pressure drop is measured for 60 seconds. The flexible container is then submerged in water and the spout/cap junction is observed to monitor whether bubble formation occurs. Higher values for pressure drop indicate a higher leak in the package.
Applicant discovered that the unique structure and geometry of the present seal bars 10, 210 alone, or in combination with fitment composed of the ethylene/α-olefin multi-block copolymer/HDPE blend forms hermetic film-to-fitment seals and hermetic film-to-film seals with little-to-no deformation of the fitment top. The present process yields improved fitment-to-cap sealing as evidenced by the lower pressure drop for IE 1-4 compared to higher pressure drop for CS 1-9. The elliptical curvature of the concave surfaces for the present seal bars provides sufficient winglet formation for hermetic seals to be made while also providing greater recoil and recovery of the fitment, enabling the fitment to revert back to a circular cross-sectional shape post-heat sealing, i.e., with low distortion of the fitment due to sealing.
It is specifically intended that the present disclosure not be limited to the embodiments and illustrations contained herein, but include modified forms of those embodiments including portions of the embodiments and combinations of elements of different embodiments as come within the scope of the following claims.
Number | Name | Date | Kind |
---|---|---|---|
4555293 | French | Nov 1985 | A |
5087235 | Lafleur | Feb 1992 | A |
5203819 | Gleason | Apr 1993 | A |
5324233 | Owensby | Jun 1994 | A |
5417035 | English | May 1995 | A |
5437595 | Smith | Aug 1995 | A |
5484375 | Owensby et al. | Jan 1996 | A |
5505040 | Janssen et al. | Apr 1996 | A |
5561966 | English | Oct 1996 | A |
5783638 | Lai et al. | Jul 1998 | A |
5976300 | Buchanan | Nov 1999 | A |
6729109 | Knoerzer et al. | May 2004 | B2 |
7608668 | LiPiShan et al. | Oct 2009 | B2 |
7736288 | Mizuo et al. | Jun 2010 | B2 |
7858706 | Arriola et al. | Dec 2010 | B2 |
7908826 | Reaves et al. | Mar 2011 | B2 |
7864829 | Vess | Jun 2011 | B2 |
8075189 | Berman | Dec 2011 | B2 |
8362396 | Vess | Jan 2013 | B2 |
8672182 | Bonet | Mar 2014 | B2 |
8734015 | Futase | May 2014 | B2 |
8950618 | Degutis et al. | Feb 2015 | B2 |
9132944 | Schick | Sep 2015 | B2 |
20040161174 | Bartel et al. | Aug 2004 | A1 |
20090196537 | Aikawa et al. | Aug 2009 | A1 |
20100119783 | Futase | May 2010 | A1 |
20110062192 | Gruber | Mar 2011 | A1 |
20110110613 | Futase | May 2011 | A1 |
20120005993 | Doll | Jan 2012 | A1 |
20130315508 | Futase | Nov 2013 | A1 |
20140217119 | Futase | Aug 2014 | A1 |
20150175323 | Barron | Jun 2015 | A1 |
20170120552 | Franca | May 2017 | A1 |
20170121083 | Hishihuma | May 2017 | A1 |
Number | Date | Country |
---|---|---|
46847 | Mar 1986 | AU |
2012212402 | Jun 2016 | AU |
2239006 | Mar 2006 | CA |
103016890 | Apr 2013 | CN |
203318776 | Dec 2013 | CN |
203997078 | Dec 2014 | CN |
29522009 | Jun 1999 | DE |
102009042983 | Mar 2011 | DE |
820854 | May 2001 | EP |
2366531 | Sep 2015 | EP |
H071587 | Jan 1995 | JP |
H11124144 | May 1999 | JP |
2001018954 | Jan 2001 | JP |
2005298038 | Oct 2005 | JP |
2007159804 | Jun 2007 | JP |
4392198 | Dec 2009 | JP |
2010095272 | Apr 2010 | JP |
4466154 | May 2010 | JP |
4712085 | Jun 2011 | JP |
2011240932 | Dec 2011 | JP |
5360573 | Dec 2013 | JP |
5459639 | Apr 2014 | JP |
5227450 | Jul 2014 | JP |
2015071455 | Apr 2015 | JP |
2007067029 | Jun 2007 | WO |
2009087454 | Jul 2009 | WO |
2010058052 | May 2010 | WO |
Entry |
---|
Potemkin, Physical Review E (1998) 57(6) pp. 6902-6912. |
Dobrynin, J. Chem. Phys. (1997), 107(21), pp. 9234-9238. |
Number | Date | Country | |
---|---|---|---|
20180086528 A1 | Mar 2018 | US |