Patent Application
20230326955
One embodiment of the present invention relates to a manufacturing method of a metal oxide. Another embodiment of the present invention relates to a transistor, a semiconductor device, and an electronic device. Another embodiment of the present invention relates to a manufacturing method of a semiconductor device. Another embodiment of the present invention relates to a semiconductor wafer and a module.
Note that in this specification and the like, a semiconductor device means any device that can function by utilizing semiconductor characteristics. A semiconductor element such as a transistor, a semiconductor circuit, an arithmetic device, and a storage device are each one embodiment of a semiconductor device. It can be sometimes said that a display device (a liquid crystal display device, a light-emitting display device, or the like), a projection device, a lighting device, an electro-optical device, a power storage device, a storage device, a semiconductor circuit, an imaging device, an electronic device, and the like include a semiconductor device.
Note that one embodiment of the present invention is not limited to the above technical field. One embodiment of the invention disclosed in this specification and the like relates to an object, a method, or a manufacturing method. One embodiment of the present invention relates to a process, a machine, manufacture, or a composition of matter.
In recent years, semiconductor devices have been developed, and LSIs, CPUs, memories, and the like are mainly used as the semiconductor devices. A CPU is an assembly of semiconductor elements which each include a chip of a semiconductor integrated circuit (including at least a transistor and a memory) processed from a semiconductor wafer and an electrode serving as a connection terminal.
A semiconductor circuit (IC chip) of an LSI, a CPU, a memory, or the like is mounted on a circuit board, for example, a printed wiring board, to be used as one of the components of a variety of electronic devices.
A technique by which a transistor is formed using a semiconductor thin film formed over a substrate having an insulating surface has been attracting attention. The transistor is used in a wide range of electronic devices such as an integrated circuit (IC) or an image display device (also simply referred to as a display device). A silicon-based semiconductor material is widely known as a semiconductor thin film applicable to the transistor and further, an oxide semiconductor has been attracting attention as another material.
It is known that a transistor using an oxide semiconductor has extremely low leak current in a non-conduction state. For example, a low-power-consumption CPU utilizing a feature of low leak current of the transistor using an oxide semiconductor is disclosed in Patent Document 1. Furthermore, for example, a storage device that can retain stored contents for a long time by utilizing a feature of low leak current of the transistor using an oxide semiconductor is disclosed in Patent Document 2.
In recent years, demand for an integrated circuit with higher density has risen with reductions in size and weight of electronic devices. Furthermore, the productivity of a semiconductor device including an integrated circuit is desired to be improved.
An object of one embodiment of the present invention is to provide a semiconductor device with a small variation in electrical characteristics of transistors. Another object of one embodiment of the present invention is to provide a semiconductor device with favorable reliability. Another object of one embodiment of the present invention is to provide a semiconductor device with favorable electrical characteristics. Another object of one embodiment of the present invention is to provide a semiconductor device with high on-state current. Another object of one embodiment of the present invention is to provide a semiconductor device that can be miniaturized or highly integrated. Another object of one embodiment of the present invention is to provide a semiconductor device with low power consumption.
Note that the description of these objects does not preclude the existence of other objects. One embodiment of the present invention does not have to achieve all these objects. Other objects are apparent from the description of the specification, the drawings, the claims, and the like, and other objects can be derived from the description of the specification, the drawings, the claims, and the like.
One embodiment of the present invention is a manufacturing method of a semiconductor device including a capacitor whose leak current is lower than or equal to 1.5×10−21 (A) per capacitance of 4.3 fF in a measurement environment at a temperature of 125° C. In the manufacturing method of a semiconductor device, a first conductor is formed; a second insulator is formed over the first conductor; a third insulator is formed over the second insulator; a second conductor is formed over the third insulator; a fourth insulator is deposited over the second conductor and the third insulator; by heat treatment, hydrogen contained in the third insulator diffuses into and is absorbed by the second insulator; the first conductor is one electrode of the capacitor; the second conductor is the other electrode of the capacitor; and each of the second insulator and the third insulator is a dielectric of the capacitor.
It is preferable that, in the above method, the second insulator be a metal oxide deposited by an ALD method and containing aluminum and the third insulator be an oxide deposited by a CVD method and containing silicon and nitrogen.
Another embodiment of the present invention is a manufacturing method of a semiconductor device including a capacitor whose leak current is lower than or equal to 1.5×10−21 (A) per capacitance of 4.3 fF in a measurement environment at a temperature of 125° C. In the manufacturing method of a semiconductor device, a first conductor is formed; a second insulator is formed over the first conductor; a third insulator is formed over the second insulator; a second conductor is formed over the third insulator; a fourth insulator is deposited over the second conductor and the third insulator; by heat treatment, hydrogen contained in the second insulator diffuses into and is absorbed by the third insulator; the first conductor is one electrode of the capacitor; the second conductor is the other electrode of the capacitor; and each of the second insulator and the third insulator is dielectric of the capacitor.
It is preferable that, in the above method, the second insulator be an oxide deposited by a CVD method and containing silicon and nitrogen and the third insulator be a metal oxide deposited by an ALD method and containing aluminum.
Another embodiment of the present invention is a manufacturing method of a semiconductor device including a capacitor whose leak current is lower than or equal to 1.5×10−21 (A) per capacitance of 4.3 fF in a measurement environment at a temperature of 125° C. In the manufacturing method of a semiconductor device, a first conductor is formed; a second insulator is formed over the first conductor; a third insulator is formed over the second insulator; microwave treatment is performed over the third insulator; a second conductor is formed over the third insulator; a fourth insulator is deposited over the second conductor and the third insulator; by heat treatment, hydrogen contained in the third insulator diffuses into and is absorbed by the second insulator; the first conductor is one electrode of the capacitor; the second conductor is the other electrode of the capacitor; and each of the second insulator and the third insulator is a dielectric of the capacitor.
It is preferable that, in the above method, the second insulator be a metal oxide deposited by an ALD method and containing aluminum and the third insulator is an oxide deposited by a CVD method and containing silicon and nitrogen.
Another embodiment of the present invention is a manufacturing method of a semiconductor device including a capacitor whose leak current is lower than or equal to 1.5×10−21 (A) per capacitance of 4.3 fF in a measurement environment at a temperature of 125° C. In the manufacturing method of a semiconductor device, a first conductor is formed; a second insulator is formed over the first conductor; microwave treatment is performed over the second insulator; a third insulator is formed over the second insulator; a second conductor is formed over the third insulator; a fourth insulator is deposited over the second conductor and the third insulator; by heat treatment, hydrogen contained in the second insulator diffuses into and is absorbed by the third insulator; the first conductor is one electrode of the capacitor; the second conductor is the other electrode of the capacitor; and each of the second insulator and the third insulator is a dielectric of the capacitor.
It is preferable that, in the above method, the second insulator be an oxide deposited by a CVD method and containing silicon and nitrogen and the third insulator be a metal oxide deposited by an ALD method and containing aluminum.
It is preferable that, in the above method, the microwave treatment be performed using a gas containing oxygen and a pressure of the microwave treatment be lower than or equal to 133 Pa.
It is preferable that, in the above methods, a temperature of the heat treatment be in the range higher than or equal to 300° C. and lower than or equal to 550° C., and time for the heat treatment is in the range longer than or equal to 2 hours and shorter than or equal to 16 hours.
According to one embodiment of the present invention, a semiconductor device with a small variation in electrical characteristics of transistors can be provided. According to another embodiment of the present invention, a semiconductor device with favorable reliability can be provided. According to another embodiment of the present invention, a semiconductor device with favorable electrical characteristics can be provided. According to another embodiment of the present invention, a semiconductor device with high on-state current can be provided. According to another embodiment of the present invention, a semiconductor device that can be miniaturized or highly integrated can be provided. According to another embodiment of the present invention, a semiconductor device with low power consumption can be provided.
Note that the description of these effects does not preclude the existence of other effects. One embodiment of the present invention does not have to have all these effects. Other effects are apparent from the description of the specification, the drawings, the claims, and the like and other effects can be derived from the description of the specification, the drawings, the claims, and the like.
Hereinafter, embodiments are described with reference to the drawings. Note that the embodiments can be implemented with many different modes, and it is readily understood by those skilled in the art that modes and details thereof can be changed in various ways without departing from the spirit and scope thereof. Thus, the present invention should not be interpreted as being limited to the description of the embodiments below.
In the drawings, the size, the layer thickness, or the region is exaggerated for clarity in some cases. Therefore, they are not limited to the illustrated scale. Note that the drawings schematically illustrate ideal examples, and embodiments of the present invention are not limited to shapes, values, and the like shown in the drawings. For example, in the actual manufacturing process, a layer, a resist mask, or the like might be unintentionally reduced in size by treatment such as etching, which might not be reflected in the drawings for easy understanding. Furthermore, in the drawings, the same reference numerals are used in common for the same portions or portions having similar functions in different drawings, and repeated description thereof is omitted in some cases. Furthermore, the same hatch pattern is used for the portions having similar functions, and the portions are not especially denoted by reference numerals in some cases.
Furthermore, especially in a top view (also referred to as a “plan view”), a perspective view, or the like, the description of some components might be omitted for easy understanding of the invention. In addition, some hidden lines and the like might not be illustrated.
The ordinal numbers such as “first” and “second” in this specification and the like are used for convenience and do not denote the order of steps or the stacking order of layers. Therefore, for example, the term “first” can be replaced with the term “second”, “third”, or the like as appropriate. In addition, the ordinal numbers in this specification and the like do not sometimes correspond to the ordinal numbers that are used to specify one embodiment of the present invention.
Moreover, in this specification and the like, terms for describing arrangement, such as “over” and “under”, are used for convenience for describing the positional relationship between components with reference to drawings. The positional relationship between components is changed as appropriate in accordance with a direction in which the components are described. Thus, without limitation to terms described in this specification, the description can be changed appropriately depending on the situation.
When this specification and the like explicitly state that X and Y are connected, for example, the case where X and Y are electrically connected, the case where X and Y are functionally connected, and the case where X and Y are directly connected are regarded as being disclosed in this specification and the like. Accordingly, without being limited to a predetermined connection relationship, for example, any other connection relationship than that shown in drawings or texts is also regarded as disclosed in the drawings or the texts. Here, X and Y each denote an object (e.g., a device, an element, a circuit, a wiring, an electrode, a terminal, a conductive film, or a layer).
In this specification and the like, a transistor is an element having at least three terminals including a gate, a drain, and a source. In addition, the transistor includes a region where a channel is formed (hereinafter also referred to as a channel formation region) between the drain (a drain terminal, a drain region, or a drain electrode) and the source (a source terminal, a source region, or a source electrode), and current can flow between the source and the drain through the channel formation region. Note that in this specification and the like, a channel formation region refers to a region through which current mainly flows.
Furthermore, functions of a source and a drain are sometimes interchanged with each other when transistors having different polarities are used or when the direction of current is changed in circuit operation, for example. Therefore, the terms “source” and “drain” can sometimes be interchanged with each other in this specification and the like.
Note that a channel length refers to, for example, a distance between a source (a source region or a source electrode) and a drain (a drain region or a drain electrode) in a region where a semiconductor (or a portion where current flows in a semiconductor when a transistor is in an on state) and a gate electrode overlap each other or a channel formation region in a top view of the transistor. Note that in one transistor, channel lengths in all regions do not necessarily have the same value. In other words, the channel length of one transistor is not fixed to one value in some cases. Thus, in this specification, the channel length is any one of the values, the maximum value, the minimum value, or the average value in a channel formation region.
A channel width refers to, for example, the length of a channel formation region in a direction perpendicular to a channel length direction in a region where a semiconductor (or a portion where current flows in a semiconductor when a transistor is in an on state) and a gate electrode overlap each other, or a channel formation region in a top view of the transistor. Note that in one transistor, channel widths in all regions do not necessarily have the same value. In other words, the channel width of one transistor is not fixed to one value in some cases. Thus, in this specification, the channel width is any one of the values, the maximum value, the minimum value, or the average value in a channel formation region.
Note that in this specification and the like, depending on the transistor structure, a channel width in a region where a channel is actually formed (hereinafter also referred to as an “effective channel width”) is sometimes different from a channel width shown in a top view of a transistor (hereinafter also referred to as an “apparent channel width”). For example, in a transistor whose gate electrode covers a side surface of a semiconductor, the effective channel width is larger than the apparent channel width, and its influence cannot be ignored in some cases. For example, in a miniaturized transistor whose gate electrode covers a side surface of a semiconductor, the proportion of a channel formation region formed in the side surface of the semiconductor is increased in some cases. In that case, the effective channel width is larger than the apparent channel width.
In such a case, estimation of an effective channel width by actual measurement is sometimes difficult. For example, estimation of an effective channel width from a design value requires assumption that the shape of a semiconductor is known. Accordingly, in the case where the shape of a semiconductor is not known exactly, it is difficult to measure the effective channel width accurately.
In this specification, the simple term “channel width” refers to an apparent channel width in some cases. Alternatively, in this specification, the simple term “channel width” refers to an effective channel width in some cases. Note that values of a channel length, a channel width, an effective channel width, an apparent channel width, and the like can be determined, for example, by analyzing a cross-sectional TEM image and the like.
Note that impurities in a semiconductor refer to, for example, elements other than the main components of a semiconductor. For example, an element with a concentration lower than 0.1 atomic % can be regarded as an impurity. When an impurity is contained, for example, the density of defect states in a semiconductor increases or the crystallinity decreases in some cases. In the case where the semiconductor is an oxide semiconductor, examples of an impurity which changes the characteristics of the semiconductor include Group 1 elements, Group 2 elements, Group 13 elements, Group 14 elements, Group 15 elements, and transition metals other than the main components of the oxide semiconductor; hydrogen, lithium, sodium, silicon, boron, phosphorus, carbon, and nitrogen are given as examples. Note that water also serves as an impurity in some cases. In addition, oxygen vacancies (also referred to as VO) are formed in an oxide semiconductor in some cases by entry of impurities, for example.
Note that in this specification and the like, silicon oxynitride is a material that contains more oxygen than nitrogen in its composition. Moreover, silicon nitride oxide is a material that contains more nitrogen than oxygen in its composition.
In this specification and the like, the term “insulator” can be replaced with an insulating film or an insulating layer. Furthermore, the term “conductor” can be replaced with a conductive film or a conductive layer. Moreover, the term “semiconductor” can be replaced with a semiconductor film or a semiconductor layer.
In this specification and the like, “parallel” indicates a state where two straight lines are placed at an angle greater than or equal to −10° and less than or equal to 10°. Accordingly, the case where the angle is greater than or equal to −5° and less than or equal to 5° is also included. Furthermore, “substantially parallel” indicates a state where two straight lines are placed at an angle greater than or equal to −30° and less than or equal to 30°. Moreover, “perpendicular” indicates a state where two straight lines are placed at an angle greater than or equal to 80° and less than or equal to 100°. Accordingly, the case where the angle is greater than or equal to 85° and less than or equal to 95° is also included. Furthermore, “substantially perpendicular” indicates a state where two straight lines are placed at an angle greater than or equal to 60° and less than or equal to 120°.
In this specification and the like, a metal oxide is an oxide of a metal in a broad sense. Metal oxides are classified into an oxide insulator, an oxide conductor (including a transparent oxide conductor), an oxide semiconductor (also simply referred to as an OS), and the like. For example, in the case where a metal oxide is used in a semiconductor layer of a transistor, the metal oxide is referred to as an oxide semiconductor in some cases. That is, an OS transistor can also be called a transistor including a metal oxide or an oxide semiconductor.
In this specification and the like, “normally off” means that drain current per micrometer of channel width flowing through a transistor is 1×10−20 A or lower at room temperature, 1×10−18 A or lower at 85° C., or 1×10−16 A or lower at 125° C. when no potential is applied to a gate or the gate is supplied with a ground potential.
In this embodiment, an example of a semiconductor device including a transistor 200 of one embodiment of the present invention and a manufacturing method thereof are described with reference to
A structure of a semiconductor device including the transistor 200 is described with reference to
The semiconductor device of one embodiment of the present invention includes an insulator 212 over a substrate (not illustrated), an insulator 214 over the insulator 212, the transistor 200 over the insulator 214, an insulator 280 over the transistor 200, an insulator 282 over the insulator 280, an insulator 283 over the insulator 282, an insulator 274 over the insulator 283, and an insulator 285 over the insulator 283 and the insulator 274. The insulator 212, the insulator 214, an insulator 216, the insulator 280, the insulator 282, the insulator 283, the insulator 285, and the insulator 274 each function as an interlayer film. In addition, the semiconductor device also includes a conductor 240 (a conductor 240a and a conductor 240b) that is electrically connected to the transistor 200 and functions as a plug. Note that an insulator 241 (an insulator 241a and an insulator 241b) is provided in contact with a side surface of the conductor 240 functioning as a plug. A conductor 246 (a conductor 246a and a conductor 246b) electrically connected to the conductor 240 and functioning as a wiring is provided over the insulator 285 and the conductor 240. The insulator 283 is in contact with part of a top surface of the insulator 214, a side surface of the insulator 216, a side surface of an insulator 222, a side surface of an insulator 275, a side surface of the insulator 280, and a side surface and a top surface of the insulator 282.
The insulator 241a is provided in contact with an inner wall of an opening formed in the insulator 280, the insulator 282, the insulator 283, and the insulator 285, and the conductor 240a is provided in contact with a side surface of the insulator 241a. The insulator 241b is provided in contact with an inner wall of an opening formed in the insulator 280, the insulator 282, the insulator 283, and the insulator 285, and the conductor 240b is provided in contact with a side surface of the insulator 241b. The insulator 241 has a structure in which a first insulator is provided in contact with the inner wall of the opening and a second insulator is provided on the inner side of the first insulator. The conductor 240 has a structure in which a first conductor is provided in contact with the side surface of the insulator 241 and a second conductor is provided on the inner side of the first conductor. Here, a top surface of the conductor 240 can be substantially level with a top surface of the insulator 285 in a region overlapping with the conductor 246.
Although the first insulator of the insulator 241 and the second insulator of the insulator 241 are stacked in the transistor 200, the present invention is not limited thereto. For example, the insulator 241 may be provided to have a single-layer structure or a stacked-layer structure of three or more layers. Although the first conductor of the conductor 240 and the second conductor of the conductor 240 are stacked in the transistor 200, the present invention is not limited thereto. For example, the conductor 240 may be provided to have a single-layer structure or a stacked-layer structure of three or more layers. In the case where a structure body has a stacked-layer structure, layers may be distinguished by ordinal numbers corresponding to the formation order.
As illustrated in
Hereinafter, the oxide 230a and the oxide 230b are collectively referred to as the oxide 230 in some cases. The conductor 242a and the conductor 242b are collectively referred to as the conductor 242 in some cases. The insulator 271a and the insulator 271b are collectively referred to as the insulator 271 in some cases.
An opening reaching the oxide 230b is provided in the insulator 280 and the insulator 275. The insulator 252, the insulator 250, the insulator 254, and the conductor 260 are placed in the opening. The conductor 260, the insulator 252, the insulator 250, and the insulator 254 are provided between the conductor 242a and the conductor 242b and between the insulator 271a and the insulator 271b in the channel length direction of the transistor 200. The insulator 254 includes a region in contact with a side surface of the conductor 260 and a region in contact with a bottom surface of the conductor 260.
The oxide 230 preferably includes the oxide 230a placed over the insulator 224 and the oxide 230b placed over the oxide 230a. Including the oxide 230a under the oxide 230b makes it possible to inhibit diffusion of impurities into the oxide 230b from components formed below the oxide 230a.
Although a structure in which two layers, the oxide 230a and the oxide 230b, are stacked as the oxide 230 in the transistor 200 is described, the present invention is not limited thereto. For example, the oxide 230 may be provided as a single layer of the oxide 230b or to have a stacked-layer structure of three or more layers, or the oxide 230a and the oxide 230b may each have a stacked-layer structure.
The conductor 260 functions as a first gate (also referred to as a top gate) electrode, and the conductor 205 functions as a second gate (also referred to as a back gate) electrode. The insulator 252, the insulator 250, and the insulator 254 function as a first gate insulator, and the insulator 222 and the insulator 224 function as a second gate insulator. Note that the gate insulator is also referred to as a gate insulating layer or a gate insulating film in some cases. The conductor 242a functions as one of a source and a drain, and the conductor 242b functions as the other of the source and the drain. At least part of a region of the oxide 230 overlapping with the conductor 260 functions as a channel formation region.
The region 230bc functioning as the channel formation region has a smaller amount of oxygen vacancies or a lower impurity concentration than the region 230ba and the region 230bb, and thus is a high-resistance region with a low carrier concentration. Accordingly, the region 230bc can be regarded as being i-type (intrinsic) or substantially i-type.
The region 230ba and the region 230bb functioning as the source region and the drain region include a large amount of oxygen vacancies and have a high concentration of an impurity such as hydrogen, nitrogen, or a metal element; thus the region 230ba and the region 230bb are each a low-resistance region with increased carrier concentration. In other words, the region 230ba and the region 230bb are each an n-type region having a higher carrier concentration and a lower resistance than the region 230bc.
The carrier concentration in the region 230bc functioning as the channel formation region is preferably lower than or equal to 1×1018 cm−3, further preferably lower than 1×1017 cm−3, still further preferably lower than 1×1016 cm−3, yet further preferably lower than 1×1013 cm−3, yet still further preferably lower than 1×1012 cm−3. Note that the lower limit of the carrier concentration in the region 230bc functioning as the channel formation region is not particularly limited and can be, for example, 1×10−9 cm−3.
Between the region 230bc and the region 230ba or the region 230bb, a region having a carrier concentration that is lower than or substantially equal to the carrier concentrations in the region 230ba and the region 230bb and higher than or substantially equal to the carrier concentration in the region 230bc may be formed. That is, the region functions as a junction region between the region 230bc and the region 230ba or the region 230bb. The hydrogen concentration in the junction region is lower than or substantially equal to the hydrogen concentrations in the region 230ba and the region 230bb and higher than or substantially equal to the hydrogen concentration in the region 230bc in some cases. The amount of oxygen vacancies in the junction region is smaller than or substantially equal to the amounts of oxygen vacancies in the region 230ba and the region 230bb and larger than or substantially equal to the amount of oxygen vacancies in the region 230bc in some cases.
Although
In the oxide 230, it is sometimes difficult to clearly detect the boundaries between the regions. The concentration of a metal element and an impurity element such as hydrogen and nitrogen, which is detected in each region, may be not only gradually changed between the regions, but also continuously changed in each region. That is, the region closer to the channel formation region preferably has a lower concentration of a metal element and an impurity element such as hydrogen and nitrogen.
In the transistor 200, a metal oxide functioning as a semiconductor (such a metal oxide is hereinafter also referred to as an oxide semiconductor) is preferably used for the oxide 230 (the oxide 230a and the oxide 230b) including the channel formation region.
The metal oxide functioning as a semiconductor preferably has a band gap of 2 eV or more, further preferably 2.5 eV or more. With the use of such a metal oxide having a large band gap, the off-state current of the transistor can be reduced.
As the oxide 230, it is preferable to use, for example, a metal oxide such as an In-M-Zn oxide containing indium, an element M, and zinc (the element M is one or more kinds selected from aluminum, gallium, yttrium, tin, copper, vanadium, beryllium, boron, titanium, iron, nickel, germanium, zirconium, molybdenum, lanthanum, cerium, neodymium, hafnium, tantalum, tungsten, magnesium, and the like). Alternatively, an In—Ga oxide, an In—Zn oxide, or an indium oxide may be used as the oxide 230.
The atomic ratio of In to the element M in the metal oxide used as the oxide 230b is preferably greater than the atomic ratio of In to the element M in the metal oxide used as the oxide 230a.
Including the oxide 230a under the oxide 230b makes it possible to inhibit diffusion of impurities and oxygen into the oxide 230b from components formed below the oxide 230a.
When the oxide 230a and the oxide 230b contain a common element (as the main component) besides oxygen, the density of defect states at an interface between the oxide 230a and the oxide 230b can be made low. Since the density of defect states at the interface between the oxide 230a and the oxide 230b can be made low, the influence of interface scattering on carrier conduction is small, and high on-state current can be obtained.
The oxide 230b preferably has crystallinity. It is particularly preferable to use a CAAC-OS (c-axis aligned crystalline oxide semiconductor) as the oxide 230b.
The CAAC-OS is a metal oxide having a dense structure with high crystallinity and a small amount of impurities or defects (e.g., oxygen vacancies (VO)). In particular, after the formation of a metal oxide, heat treatment is performed at a temperature at which the metal oxide does not become a polycrystal (e.g., 400° C. to 600° C., inclusive), whereby a CAAC-OS having a dense structure with higher crystallinity can be obtained. When the density of the CAAC-OS is increased in such a manner, diffusion of impurities or oxygen in the CAAC-OS can be further reduced.
On the other hand, it is difficult to observe a clear crystal grain boundary in the CAAC-OS; thus, it can be said that a reduction in electron mobility due to the crystal grain boundary is less likely to occur. Thus, a metal oxide including a CAAC-OS is physically stable. Therefore, the metal oxide including a CAAC-OS is resistant to heat and highly reliable.
If impurities and oxygen vacancies exist in a region of an oxide semiconductor where a channel is formed, a transistor using the oxide semiconductor might have variable electrical characteristics and poor reliability. In some cases, hydrogen in the vicinity of an oxygen vacancy forms a defect that is the oxygen vacancy into which hydrogen enters (hereinafter sometimes referred to as VOH), which generates an electron serving as a carrier. Therefore, when the region of the oxide semiconductor where a channel is formed includes oxygen vacancies, the transistor tends to have normally-on characteristics (even when no voltage is applied to the gate electrode, the channel exists and current flows through the transistor). Thus, impurities, oxygen vacancies, and VOH are preferably reduced as much as possible in the region of the oxide semiconductor where a channel is formed. In other words, it is preferable that the region of the oxide semiconductor where a channel is formed have a reduced carrier concentration and be of an i-type (intrinsic) or substantially i-type.
As a countermeasure to the above, an insulator containing oxygen that is released by heating (hereinafter, sometimes referred to as excess oxygen) is provided in the vicinity of the oxide semiconductor and heat treatment is performed, so that oxygen can be supplied from the insulator to the oxide semiconductor to reduce oxygen vacancies and VOH. However, supply of an excess amount of oxygen to the source region or the drain region might cause a decrease in the on-state current or field-effect mobility of the transistor 200. Furthermore, a variation of oxygen supplied to the source region or the drain region in the substrate plane leads to a variation in characteristics of the semiconductor device including the transistor.
Therefore, the region 230bc functioning as the channel formation region in the oxide semiconductor is preferably an i-type or substantially i-type region with reduced carrier concentration, whereas the region 230ba and the region 230bb functioning as the source region and the drain region are preferably n-type regions with high carrier concentrations. That is, it is preferable that oxygen vacancies and VOH in the region 230bc of the oxide semiconductor be reduced and the region 230ba and the region 230bb not be supplied with an excess amount of oxygen.
Thus, in this embodiment, microwave treatment is performed in an atmosphere containing oxygen in a state where the conductor 242a and the conductor 242b are provided over the oxide 230b so that oxygen vacancies and VOH in the region 230bc can be reduced. Here, the microwave treatment refers to, for example, treatment using an apparatus including a power source that generates high-density plasma with the use of a microwave. The microwave treatment is sometimes referred to as microwave-excitation treatment.
The microwave treatment in an atmosphere containing oxygen converts an oxygen gas into plasma using a high-frequency wave such as a microwave or RF and activates the oxygen plasma. At this time, the region 230bc can be irradiated with the high-frequency wave such as a microwave or RF. By the effect of the plasma, a microwave, or the like, VOH in the region 230bc can be cut; thus, hydrogen (H) can be removed from the region 230bc and an oxygen vacancy (VO) can be filled with oxygen. That is, the reaction “VOHH+VO” occurs in the region 230bc, so that the hydrogen concentration in the region 230bc can be reduced. As a result, oxygen vacancies and VOH in the region 230bc can be reduced to lower the carrier concentration.
In the case where the microwave treatment is performed in an atmosphere containing oxygen, the high-frequency wave such as the microwave or RF, the oxygen plasma, or the like is blocked by the conductor 242a and the conductor 242b and does not affect the region 230ba nor the region 230bb. In addition, the effect of the oxygen plasma can be reduced by the insulator 271 and the insulator 280 that are provided to cover the oxide 230b and the conductor 242. Hence, a reduction in VOH and supply of an excess amount of oxygen do not occur in the region 230ba or the region 230bb in the microwave treatment, preventing a decrease in carrier concentration.
Microwave treatment is preferably performed in an atmosphere containing oxygen after deposition of an insulating film to be the insulator 252 or after deposition of an insulating film to be the insulator 250. By performing the microwave treatment in an atmosphere containing oxygen through the insulator 252 or the insulator 250 in such a manner, oxygen can be efficiently supplied into the region 230bc. In addition, the insulator 252 is placed to be in contact with the side surface of the conductor 242 and the surface of the region 230bc, thereby inhibiting oxygen more than necessary from being supplied to the region 230bc and inhibiting the side surface of the conductor 242 from being oxidized. Furthermore, the side surface of the conductor 242 can be inhibited from being oxidized when an insulating film to be the insulator 250 is deposited.
The oxygen supplied into the region 230bc has any of a variety of forms such as an oxygen atom, an oxygen molecule, and an oxygen radical (an O radical, an atom or a molecule having an unpaired electron, or an ion). Note that the oxygen supplied into the region 230bc can have any one or more of the above forms, and particularly preferably is an oxygen radical. Furthermore, the film quality of the insulator 252 and the insulator 250 can be improved, leading to higher reliability of the transistor 200.
In the above manner, oxygen vacancies and VOH can be selectively removed from the region 230bc in the oxide semiconductor, whereby the region 230bc can be an i-type or substantially i-type region. Furthermore, supply of an excess amount of oxygen to the region 230ba and the region 230bb functioning as the source region and the drain region can be inhibited and the n-type conductivity can be maintained. As a result, a change in the electrical characteristics of the transistor 200 can be inhibited, and thus a variation in the electrical characteristics of the transistors 200 in the substrate plane can be inhibited.
With the above structure, a semiconductor device with a small variation in transistor characteristics can be provided. A semiconductor device with favorable reliability can also be provided. A semiconductor device with favorable electrical characteristics can be provided.
As illustrated in
The radius of curvature of the curved surface is preferably greater than 0 nm and less than the thickness of the oxide 230b in a region overlapping with the conductor 242, or less than half of the length of a region that does not have the curved surface. Specifically, the radius of curvature of the curved surface is greater than 0 nm and less than or equal to 20 nm, preferably greater than or equal to 1 nm and less than or equal to 15 nm, and further preferably greater than or equal to 2 nm and less than or equal to 10 nm. Such a shape can improve the coverage of the oxide 230b with the insulator 252, the insulator 250, the insulator 254, and the conductor 260.
The oxide 230 preferably has a stacked-layer structure of a plurality of oxide layers with different chemical compositions. Specifically, the atomic ratio of the element M to a metal element that is a main component of the metal oxide used as the oxide 230a is preferably greater than the atomic ratio of the element M to a metal element that is a main component of the metal oxide used as the oxide 230b. Moreover, the atomic ratio of the element M to In in the metal oxide used as the oxide 230a is preferably greater than the atomic ratio of the element M to In in the metal oxide used as the oxide 230b. Furthermore, the atomic ratio of In to the element Min the metal oxide used as the oxide 230b is preferably greater than the atomic ratio of In to the element M in the metal oxide used as the oxide 230a.
The oxide 230b is preferably an oxide having crystallinity, such as a CAAC-OS. An oxide having crystallinity, such as a CAAC-OS, has a dense structure with small amounts of impurities and defects (e.g., oxygen vacancies) and high crystallinity. This can inhibit oxygen extraction from the oxide 230b by the source electrode or the drain electrode. This can reduce oxygen extraction from the oxide 230b even when heat treatment is performed; thus, the transistor 200 is stable with respect to high temperatures in a manufacturing process (what is called thermal budget).
Here, the conduction band minimum gradually changes at a junction portion of the oxide 230a and the oxide 230b. In other words, the conduction band minimum at the junction portion of the oxide 230a and the oxide 230b continuously changes or is continuously connected. To achieve this, the density of defect states in a mixed layer formed at the interface between the oxide 230a and the oxide 230b is preferably made low.
Specifically, when the oxide 230a and the oxide 230b contain a common element as a main component besides oxygen, a mixed layer with a low density of defect states can be formed. For example, in the case where the oxide 230b is an In-M-Zn oxide, an In-M-Zn oxide, an M-Zn oxide, an oxide of the element M, an In—Zn oxide, indium oxide, or the like may be used as the oxide 230a.
Specifically, as the oxide 230a, a metal oxide with a composition of In:M:Zn=1:3:4 [atomic ratio] or in the neighborhood thereof, or a composition of In:M:Zn=1:1:0.5 [atomic ratio] or in the neighborhood thereof can be used. As the oxide 230b, a metal oxide with a composition of In:M:Zn=1:1:1 [atomic ratio] or in the neighborhood thereof, a composition of In:M:Zn=1:1:2 [atomic ratio] or in the neighborhood thereof, or a composition of In:M:Zn=4:2:3 [atomic ratio] or in the neighborhood thereof can be used. Note that a composition in the neighborhood includes the range of ±30% of an intended atomic ratio. Gallium is preferably used as the element M.
When the metal oxide is deposited by a sputtering method, the above atomic ratio is not limited to the atomic ratio of the deposited metal oxide and may be the atomic ratio of a sputtering target used for depositing the metal oxide.
As illustrated in
When the oxide 230a and the oxide 230b have the above structure, the density of defect states at the interface between the oxide 230a and the oxide 230b can be made low. Thus, the influence of interface scattering on carrier conduction is small, and the transistor 200 can have high on-state current and excellent frequency characteristics.
At least one of the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285 preferably functions as a barrier insulating film, which inhibits diffusion of impurities such as water and hydrogen from the substrate side or above the transistor 200 into the transistor 200. Thus, for at least one of the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285, it is preferable to use an insulating material having a function of inhibiting diffusion of impurities such as hydrogen atoms, hydrogen molecules, water molecules, nitrogen atoms, nitrogen molecules, nitrogen oxide molecules (e.g., N2O, NO, or NO2), or copper atoms (an insulating material through which the impurities are less likely to pass). Alternatively, it is preferable to use an insulating material having a function of inhibiting oxygen (e.g., at least one of oxygen atoms, oxygen molecules, and the like) from diffusing (an insulating material through which the oxygen is less likely to pass).
Note that in this specification, a barrier insulating film refers to an insulating film having a barrier property. A barrier property in this specification means a function of inhibiting diffusion of a targeted substance (also referred to as having low permeability). In addition, a barrier property in this specification means a function of capturing and fixing (also referred to as gettering) a targeted substance.
An insulator having a function of inhibiting diffusion of oxygen and impurities such as water and hydrogen is preferably used for the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285; for example, aluminum oxide, magnesium oxide, hafnium oxide, gallium oxide, indium gallium zinc oxide, silicon nitride, or silicon nitride oxide can be used. For example, silicon nitride, which has a higher hydrogen barrier property, is preferably used for the insulator 212, the insulator 275, and the insulator 283. For example, aluminum oxide or magnesium oxide, which has a function of capturing or fixing hydrogen well, is preferably used for the insulator 214, the insulator 271, the insulator 282, and the insulator 285. In this case, impurities such as water and hydrogen can be inhibited from diffusing to the transistor 200 side from the substrate side through the insulator 212 and the insulator 214. Impurities such as water and hydrogen can be inhibited from diffusing to the transistor 200 side from an interlayer insulating film and the like which are placed outside the insulator 285. Alternatively, oxygen contained in the insulator 224 and the like can be inhibited from diffusing to the substrate side through the insulator 212 and the insulator 214. Alternatively, oxygen contained in the insulator 280 and the like can be inhibited from diffusing to above the transistor 200 through the insulator 282 and the like. In this manner, it is preferable that the transistor 200 be surrounded by the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285, which have a function of inhibiting diffusion of oxygen and impurities such as water and hydrogen.
Here, an oxide having an amorphous structure is preferably used for the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285. For example, a metal oxide such as AlOx), (x is a given number greater than 0) or MgOy (y is a given number greater than 0) is preferably used. In such a metal oxide having an amorphous structure, an oxygen atom has a dangling bond and sometimes has a property of capturing or fixing hydrogen with the dangling bond. When such a metal oxide having an amorphous structure is used as the component of the transistor 200 or provided around the transistor 200, hydrogen contained in the transistor 200 or hydrogen present around the transistor 200 can be captured or fixed. In particular, hydrogen contained in the channel formation region of the transistor 200 is preferably captured or fixed. The metal oxide having an amorphous structure is used as the component of the transistor 200 or provided around the transistor 200, whereby the transistor 200 and a semiconductor device which have favorable characteristics and high reliability can be manufactured.
Although each of the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285 preferably has an amorphous structure, a region having a polycrystalline structure may be partly formed. Alternatively, each of the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285 may have a multilayer structure in which a layer having an amorphous structure and a layer having a polycrystalline structure are stacked. For example, a stacked-layer structure in which a layer having a polycrystalline structure is formed over a layer having an amorphous structure may be employed.
The insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285 can be deposited by a sputtering method, for example. Since a sputtering method does not need to use a molecule containing hydrogen as a deposition gas, the hydrogen concentrations in the insulator 212, the insulator 214, the insulator 271, the insulator 275, the insulator 282, the insulator 283, and the insulator 285 can be reduced. Note that the deposition method is not limited to a sputtering method, and a chemical vapor deposition (CVD) method, a molecular beam epitaxy (MBE) method, a pulsed laser deposition (PLD) method, an atomic layer deposition (ALD) method, or the like can be used as appropriate.
The resistivities of the insulator 212, the insulator 275, and the insulator 283 are preferably low in some cases. For example, by setting the resistivities of the insulator 212, the insulator 275, and the insulator 283 to approximately 1×1013 Ωcm, the insulator 212, the insulator 275, and the insulator 283 can sometimes reduce charge up of the conductor 205, the conductor 242, the conductor 260, or the conductor 246 in treatment using plasma or the like in the manufacturing process of a semiconductor device. The resistivities of the insulator 212, the insulator 275, and the insulator 283 are preferably higher than or equal to 1×1010 Ωcm and lower than or equal to 1×1015 Ωcm.
The insulator 216, the insulator 274, the insulator 280, and the insulator 285 each preferably have a lower permittivity than the insulator 214. When a material with a low permittivity is used for an interlayer film, parasitic capacitance generated between wirings can be reduced. For the insulator 216, the insulator 274, the insulator 280, and the insulator 285, silicon oxide, silicon oxynitride, silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, porous silicon oxide, or the like can be used as appropriate, for example.
The conductor 205 is placed to overlap with the oxide 230 and the conductor 260. Here, the conductor 205 is preferably provided to be embedded in an opening formed in the insulator 216. Part of the conductor 205 is embedded in the insulator 214 in some cases.
The conductor 205 includes the conductor 205a and the conductor 205b. The conductor 205a is provided in contact with a bottom surface and a sidewall of the opening. The conductor 205b is provided to be embedded in a recessed portion formed in the conductor 205a. Here, a top surface of the conductor 205b is substantially level with a top surface of the conductor 205a and a top surface of the insulator 216.
Here, for the conductor 205a, it is preferable to use a conductive material having a function of inhibiting diffusion of impurities such as a hydrogen atom, a hydrogen molecule, a water molecule, a nitrogen atom, a nitrogen molecule, a nitrogen oxide molecule (N2O, NO, NO2, or the like), and a copper atom. Alternatively, it is preferable to use a conductive material having a function of inhibiting diffusion of oxygen (e.g., at least one of an oxygen atom, an oxygen molecule, and the like).
When the conductor 205a is formed using a conductive material having a function of inhibiting diffusion of hydrogen, impurities such as hydrogen contained in the conductor 205b can be prevented from diffusing into the oxide 230 through the insulator 224 and the like. When the conductor 205a is formed using a conductive material having a function of inhibiting diffusion of oxygen, the conductivity of the conductor 205b can be inhibited from being lowered because of oxidation. As the conductive material having a function of inhibiting diffusion of oxygen, for example, titanium, titanium nitride, tantalum, tantalum nitride, ruthenium, or ruthenium oxide is preferably used. Thus, a single layer or stacked layers of the above conductive material can be used as the conductor 205a. For example, titanium nitride can be used for the conductor 205a.
Moreover, the conductor 205b is preferably formed using a conductive material containing tungsten, copper, or aluminum as its main component. For example, tungsten can be used for the conductor 205b.
The conductor 205 sometimes functions as a second gate electrode. In that case, by changing a potential applied to the conductor 205 not in conjunction with but independently of a potential applied to the conductor 260, the threshold voltage (Vth) of the transistor 200 can be controlled. In particular, Vth of the transistor 200 can be higher by applying a negative potential to the conductor 205, and the off-state current can be reduced. Thus, drain current at the time when a potential applied to the conductor 260 is 0 V can be lower in the case where a negative potential is applied to the conductor 205 than in the case where the negative potential is not applied to the conductor 205.
The electric resistivity of the conductor 205 is designed in consideration of the potential applied to the conductor 205, and the thickness of the conductor 205 is determined in accordance with the electric resistivity. The thickness of the insulator 216 is substantially equal to that of the conductor 205. The conductor 205 and the insulator 216 are preferably as thin as possible in the allowable range of the design of the conductor 205. When the thickness of the insulator 216 is reduced, the absolute amount of impurities such as hydrogen contained in the insulator 216 can be reduced, thereby reducing the amount of the impurities to be diffused into the oxide 230.
As illustrated in
In this specification and the like, a transistor having the S-channel structure refers to a transistor having a structure in which a channel formation region is electrically surrounded by the electric fields of a pair of gate electrodes. The S-channel structure disclosed in this specification and the like is different from a Fin-type structure and a planar structure. With the S-channel structure, resistance to a short-channel effect can be enhanced, that is, a transistor in which a short-channel effect is less likely to occur can be provided.
Furthermore, as illustrated in
Although the transistor 200 having a structure in which the conductor 205 is a stack of the conductor 205a and the conductor 205b is illustrated, the present invention is not limited thereto. For example, the conductor 205 may be provided to have a single-layer structure or a stacked-layer structure of three or more layers.
The insulator 222 and the insulator 224 function as a gate insulator.
It is preferable that the insulator 222 have a function of inhibiting diffusion of hydrogen (e.g., at least one of a hydrogen atom, a hydrogen molecule, and the like). In addition, it is preferable that the insulator 222 have a function of inhibiting diffusion of oxygen (e.g., at least one of an oxygen atom, an oxygen molecule, and the like). For example, the insulator 222 preferably has a function of inhibiting diffusion of one or both of hydrogen and oxygen more than the insulator 224.
As the insulator 222, an insulator containing an oxide of one or both of aluminum and hafnium, which is an insulating material, is preferably used. For the insulator, aluminum oxide, hafnium oxide, an oxide containing aluminum and hafnium (hafnium aluminate), or the like is preferably used. Alternatively, an oxide containing hafnium and zirconium, e.g., a hafnium-zirconium oxide is preferably used. In the case where the insulator 222 is formed using such a material, the insulator 222 functions as a layer that inhibits release of oxygen from the oxide 230 to the substrate side and diffusion of impurities such as hydrogen from the periphery of the transistor 200 into the oxide 230. Thus, providing the insulator 222 can inhibit diffusion of impurities such as hydrogen into the transistor 200 and inhibit generation of oxygen vacancies in the oxide 230. Moreover, the conductor 205 can be inhibited from reacting with oxygen contained in the insulator 224 and the oxide 230.
Alternatively, the above insulator may be added with aluminum oxide, bismuth oxide, germanium oxide, niobium oxide, silicon oxide, titanium oxide, tungsten oxide, yttrium oxide, or zirconium oxide, for example. Alternatively, the insulator may be subjected to nitriding treatment. A stack of silicon oxide, silicon oxynitride, or silicon nitride over these insulators may be used for the insulator 222.
For example, a single layer or stacked layers of an insulator(s) containing what is called a high-k material such as aluminum oxide, hafnium oxide, tantalum oxide, zirconium oxide, or hafnium-zirconium oxide may be used for the insulator 222. As miniaturization and high integration of transistors progress, a problem such as leak current may arise because of a thinner gate insulator. When a high-k material is used for an insulator functioning as the gate insulator, a gate potential at the time when the transistor operates can be reduced while the physical thickness of the gate insulator is maintained. Furthermore, a substance with a high permittivity such as lead zirconate titanate (PZT), strontium titanate (SrTiO3), or (Ba, Sr)TiO3 (BST) may be used for the insulator 222.
Silicon oxide or silicon oxynitride, for example, can be used as appropriate for the insulator 224 that is in contact with the oxide 230.
In a manufacturing process of the transistor 200, heat treatment is preferably performed with the surface of the oxide 230 exposed. For example, the heat treatment is performed preferably at a temperature higher than or equal to 100° C. and lower than or equal to 600° C., further preferably higher than or equal to 350° C. and lower than or equal to 550° C. Note that the heat treatment is performed in a nitrogen gas or inert gas atmosphere, or an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more. For example, the heat treatment is preferably performed in an oxygen atmosphere. This can supply oxygen to the oxide 230 to reduce oxygen vacancies (VO). The heat treatment may be performed under reduced pressure. Alternatively, the heat treatment may be performed in an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more in order to compensate for released oxygen, after heat treatment in a nitrogen gas or inert gas atmosphere. Alternatively, the heat treatment may be performed in a nitrogen gas or inert gas atmosphere successively after heat treatment is performed in an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more.
Note that oxygen adding treatment performed on the oxide 230 can promote a reaction in which oxygen vacancies in the oxide 230 are repaired with supplied oxygen, i.e., a reaction of “VO+O→null”. Furthermore, hydrogen remaining in the oxide 230 reacts with supplied oxygen, so that the hydrogen can be removed in a form of H2O (dehydration). This can inhibit recombination of hydrogen remaining in the oxide 230 with oxygen vacancies and formation of VOH.
Note that the insulator 222 and the insulator 224 may each have a stacked-layer structure of two or more layers. In that case, without limitation to a stacked-layer structure formed of the same material, a stacked-layer structure formed of different materials may be employed. The insulator 224 may be formed into an island shape so as to overlap with the oxide 230a. In this case, the insulator 275 is in contact with the side surface of the insulator 224 and the top surface of the insulator 222.
The conductor 242a and the conductor 242b are provided in contact with the top surface of the oxide 230b. Each of the conductor 242a and the conductor 242b functions as a source electrode or a drain electrode of the transistor 200.
For the conductor 242 (the conductor 242a and the conductor 242b), for example, a nitride containing tantalum, a nitride containing titanium, a nitride containing molybdenum, a nitride containing tungsten, a nitride containing tantalum and aluminum, a nitride containing titanium and aluminum, or the like is preferably used. In one embodiment of the present invention, a nitride containing tantalum is particularly preferable. As another example, ruthenium oxide, ruthenium nitride, an oxide containing strontium and ruthenium, or an oxide containing lanthanum and nickel may be used. These materials are preferable because they are each a conductive material that is not easily oxidized or a material that maintains the conductivity even after absorbing oxygen.
Note that hydrogen contained in the oxide 230b or the like diffuses into the conductor 242a or the conductor 242b in some cases. In particular, when a nitride containing tantalum is used for the conductor 242a and the conductor 242b, hydrogen contained in the oxide 230b or the like is likely to diffuse into the conductor 242a or the conductor 242b, and the diffused hydrogen is bonded to nitrogen contained in the conductor 242a or the conductor 242b in some cases. That is, hydrogen contained in the oxide 230b or the like is absorbed by the conductor 242a or the conductor 242b in some cases.
No curved surface is preferably formed between the side surface of the conductor 242 and a top surface of the conductor 242. When no curved surface is formed in the conductor 242, the conductor 242 can have a large cross-sectional area in the channel width direction as illustrated in
The insulator 271a is provided in contact with the top surface of the conductor 242a, and the insulator 271b is provided in contact with the top surface of the conductor 242b. The insulator 271 preferably functions as at least a barrier insulating film against oxygen. Thus, the insulator 271 preferably has a function of inhibiting diffusion of oxygen. For example, the insulator 271 preferably has a function of inhibiting diffusion of oxygen more than the insulator 280. For the insulator 271, an insulator such as aluminum oxide or magnesium oxide, for example, may be used.
The insulator 275 is provided to cover the insulator 224, the oxide 230a, the oxide 230b, the conductor 242, and the insulator 271. The insulator 275 preferably has a function of capturing and fixing hydrogen. In that case, the insulator 275 preferably includes silicon nitride, or a metal oxide having an amorphous structure, for example, an insulator such as aluminum oxide or magnesium oxide. Alternatively, for example, a stacked film of aluminum oxide and silicon nitride over the aluminum oxide may be used as the insulator 275.
When the above insulator 271 and the insulator 275 are provided, the conductor 242 can be surrounded by the insulators having a barrier property against oxygen. That is, oxygen contained in the insulator 224 and the insulator 280 can be prevented from diffusing into the conductor 242. As a result, the conductor 242 can be inhibited from being directly oxidized by oxygen contained in the insulator 224 and the insulator 280, so that an increase in resistivity and a reduction in on-state current can be inhibited.
The insulator 252 functions as part of the gate insulator. As the insulator 252, a barrier insulating film against oxygen is preferably used. As the insulator 252, an insulator that can be used as the insulator 282 described above may be used. An insulator containing an oxide of one or both of aluminum and hafnium is preferably used as the insulator 252. As the insulator, aluminum oxide, hafnium oxide, an oxide containing aluminum and hafnium (hafnium aluminate), an oxide containing hafnium and silicon (hafnium silicate), or the like can be used. In this embodiment, aluminum oxide is used for the insulator 252. In this case, the insulator 252 is an insulator containing at least oxygen and aluminum.
As illustrated in
Even when an excess amount of oxygen is contained in the insulator 280, the insulator 250 and the like, oxygen can be inhibited from being excessively supplied to the oxide 230a and the oxide 230b. Thus, the region 230ba and the region 230bb are prevented from being excessively oxidized by oxygen through the region 230bc; a reduction in on-state current or field-effect mobility of the transistor 200 can be inhibited.
As illustrated in
Furthermore, the insulator 252 needs to be provided in an opening formed in the insulator 280 and the like, together with the insulator 254, the insulator 250, and the conductor 260. The thickness of the insulator 252 is preferably thin for miniaturization of the transistor 200. The thickness of the insulator 252 is greater than or equal to 0.1 nm and less than or equal to 5.0 nm, preferably greater than or equal to 0.5 nm and less than or equal to 3.0 nm, further preferably greater than or equal to 1.0 nm and less than or equal to 3.0 nm. In that case, at least part of the insulator 252 preferably includes a region with the above-described thickness. The thickness of the insulator 252 is preferably smaller than that of the insulator 250. In that case, at least part of the insulator 252 preferably includes a region having a thickness smaller than that of the insulator 250.
To form the insulator 252 having a small thickness like the above-described thickness, an ALD method is preferably used for deposition. Examples of an ALD method include a thermal ALD method, in which a precursor and a reactant react with each other only by a thermal energy, and a PEALD (Plasma Enhanced ALD) method, in which a reactant excited by plasma is used. The use of plasma in a PEALD method is sometimes preferable because deposition at a lower temperature is possible.
An ALD method, which enables an atomic layer to be deposited one by one using self-limiting characteristics of atoms, has advantages such as deposition of an extremely thin film, deposition on a component with a high aspect ratio, deposition of a film with a small number of defects such as pinholes, deposition with excellent coverage, and low-temperature deposition. Therefore, the insulator 252 can be formed on the side surface of the opening formed in the insulator 280 and the like to have a small thickness like the above-described thickness and to have favorable coverage.
Note that some of precursors usable in an ALD method contain carbon or the like. Thus, in some cases, a film provided by an ALD method contains impurities such as carbon in a larger amount than a film provided by another deposition method. Note that impurities can be quantified by secondary ion mass spectrometry (SIMS), X-ray photoelectron spectroscopy (XPS), or auger electron spectroscopy (AES).
The insulator 250 functions as part of the gate insulator. The insulator 250 is preferably provided in contact with the top surface of the insulator 252. The insulator 250 can be formed using silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, porous silicon oxide, or the like. In particular, silicon oxide and silicon oxynitride, which have thermal stability, are preferable. In this case, the insulator 250 is an insulator containing at least oxygen and silicon.
As in the insulator 224, the concentration of impurities such as water and hydrogen in the insulator 250 is preferably reduced. The thickness of the insulator 250 is preferably greater than or equal to 1 nm and less than or equal to 20 nm, further preferably greater than or equal to 0.5 nm and less than or equal to 15.0 nm. In this case, at least part of the insulator 250 preferably includes a region with the above-described thickness.
Although
In the case where the insulator 250 has a stacked-layer structure of two layers as illustrated in
In the case where silicon oxide, silicon oxynitride, or the like is used for the insulator 250a, the insulator 250b may be formed using an insulating material that is a high-k material having a high relative permittivity. The gate insulator having a stacked-layer structure of the insulator 250a and the insulator 250b can be thermally stable and can have a high relative permittivity. Thus, a gate potential that is applied during operation of the transistor can be reduced while the physical thickness of the gate insulator is maintained. In addition, the equivalent oxide thickness (EOT) of the insulator functioning as the gate insulator can be reduced. Therefore, the withstand voltage of the insulator 250 can be increased.
The insulator 254 functions as part of a gate insulator. As the insulator 254, a barrier insulating film against hydrogen is preferably used. This can prevent diffusion of impurities such as hydrogen contained in the conductor 260 into the insulator 250 and the oxide 230b. As the insulator 254, an insulator that can be used as the insulator 283 described above may be used. For example, silicon nitride deposited by a PEALD method may be used as the insulator 254. In this case, the insulator 254 is an insulator containing at least nitrogen and silicon.
Furthermore, the insulator 254 may have a barrier property against oxygen. Thus, oxygen contained in the insulator 250 can be inhibited from diffusing into the conductor 260.
Furthermore, the insulator 254 needs to be provided in an opening formed in the insulator 280 and the like, together with the insulator 252, the insulator 250, and the conductor 260. The thickness of the insulator 254 is preferably thin for miniaturization of the transistor 200. The thickness of the insulator 254 is greater than or equal to 0.1 nm and less than or equal to 5.0 nm, preferably greater than or equal to 0.5 nm and less than or equal to 3.0 nm, further preferably greater than or equal to 1.0 nm and less than or equal to 3.0 nm. In that case, at least part of the insulator 254 preferably includes a region with the above-described thickness. The thickness of the insulator 254 is preferably smaller than that of the insulator 250. In that case, at least part of the insulator 254 preferably includes a region having a thickness smaller than that of the insulator 250.
The conductor 260 functions as the first gate electrode of the transistor 200. The conductor 260 preferably includes the conductor 260a and the conductor 260b placed over the conductor 260a. For example, the conductor 260a is preferably placed to cover the bottom surface and the side surface of the conductor 260b. Moreover, as illustrated in
For the conductor 260a, it is preferable to use a conductive material having a function of inhibiting diffusion of impurities such as a hydrogen atom, a hydrogen molecule, a water molecule, a nitrogen atom, a nitrogen molecule, a nitrogen oxide molecule, and a copper atom. Alternatively, it is preferable to use a conductive material having a function of inhibiting diffusion of oxygen (e.g., at least one of an oxygen atom, an oxygen molecule, and the like).
In addition, when the conductor 260a has a function of inhibiting diffusion of oxygen, the conductivity of the conductor 260b can be inhibited from being lowered because of oxidation due to oxygen contained in the insulator 250. As the conductive material having a function of inhibiting diffusion of oxygen, for example, titanium, titanium nitride, tantalum, tantalum nitride, ruthenium, or ruthenium oxide is preferably used.
The conductor 260 also functions as a wiring and thus is preferably formed using a conductor having high conductivity. For example, a conductive material containing tungsten, copper, or aluminum as its main component can be used for the conductor 260b. The conductor 260b may have a stacked-layer structure; for example, a stacked-layer structure of the conductive material and titanium or titanium nitride may be employed.
In the transistor 200, the conductor 260 is formed in a self-aligned manner to fill the opening formed in the insulator 280 and the like. The formation of the conductor 260 in this manner allows the conductor 260 to be placed properly in a region between the conductor 242a and the conductor 242b without positional alignment.
As illustrated in
The insulator 280 is provided over the insulator 275, and the opening is formed in a region where the insulator 250 and the conductor 260 are to be provided. In addition, the top surface of the insulator 280 may be planarized.
The insulator 280 functioning as an interlayer film preferably has a low permittivity. When a material with a low permittivity is used for an interlayer film, parasitic capacitance generated between wirings can be reduced. The insulator 280 is preferably provided using a material similar to that for the insulator 216, for example. In particular, silicon oxide and silicon oxynitride, which have thermal stability, are preferable. Materials such as silicon oxide, silicon oxynitride, and porous silicon oxide are particularly preferable because a region containing oxygen to be released by heating can be easily formed.
The concentration of impurities such as water and hydrogen in the insulator 280 is preferably reduced. Oxide containing silicon such as silicon oxide, silicon oxynitride, or the like is used as appropriate for the insulator 280, for example.
The insulator 282 preferably functions as a barrier insulating film that inhibits impurities such as water and hydrogen from diffusing into the insulator 280 from above and preferably have a function of capturing impurities such as hydrogen. The insulator 282 preferably functions as a barrier insulating film that inhibits passage of oxygen. For the insulator 282, a metal oxide having an amorphous structure, for example, an insulator such as aluminum oxide can be used. In this case, the insulator 282 is an insulator containing at least oxygen and aluminum. The insulator 282, which has a function of capturing impurities such as hydrogen, is provided in contact with the insulator 280 in a region sandwiched between the insulator 212 and the insulator 283, whereby impurities such as hydrogen contained in the insulator 280 and the like can be captured and the amount of hydrogen in the region can be constant. It is preferable to use, in particular, aluminum oxide having an amorphous structure for the insulator 282, in which case hydrogen can be captured or fixed more effectively in some cases. Accordingly, the transistor 200 and a semiconductor device which have favorable characteristics and high reliability can be manufactured.
The insulator 283 functions as a barrier insulating film that inhibits impurities such as water and hydrogen from diffusing into the insulator 280 from above. The insulator 283 is placed over the insulator 282. The insulator 283 is preferably formed using a nitride containing silicon such as silicon nitride or silicon nitride oxide. For example, silicon nitride deposited by a sputtering method may be used as the insulator 283. When the insulator 283 is deposited by a sputtering method, a high-density silicon nitride film can be formed. To obtain the insulator 283, silicon nitride deposited by a PEALD method or a CVD method may be stacked over silicon nitride deposited by a sputtering method.
For the conductor 240a and the conductor 240b, a conductive material containing tungsten, copper, or aluminum as its main component is preferably used. The conductor 240a and the conductor 240b may each have a stacked-layer structure.
In the case where the conductor 240 has a stacked-layer structure, a conductive material having a function of inhibiting passage of impurities such as water and hydrogen is preferably used for a first conductor placed in the vicinity of the insulator 285, the insulator 283, the insulator 282, the insulator 280, the insulator 275, and the insulator 271. For example, tantalum, tantalum nitride, titanium, titanium nitride, ruthenium, ruthenium oxide, or the like is preferably used. The conductive material having a function of inhibiting passage of impurities such as water and hydrogen may be used as a single layer or stacked layers. Moreover, impurities such as water and hydrogen contained in a layer above the insulator 283 can be inhibited from entering the oxide 230 through the conductor 240a and the conductor 240b.
For the insulator 241a and the insulator 241b, a barrier insulating film that can be used as the insulator 275 or the like may be used. As the insulator 241a and the insulator 241b, for example, an insulator such as silicon nitride, aluminum oxide, or silicon nitride oxide may be used. Since the insulator 241a and the insulator 241b are provided in contact with the insulator 283, the insulator 282, and the insulator 271, impurities such as water and hydrogen contained in the insulator 280 or the like can be inhibited from entering the oxide 230 through the conductor 240a and the conductor 240b. In particular, silicon nitride is suitable because of its high blocking property against hydrogen. Furthermore, oxygen contained in the insulator 280 can be prevented from being absorbed by the conductor 240a and the conductor 240b.
When the insulator 241a and the insulator 241b each have a stacked-layer structure as illustrated in
For example, aluminum oxide deposited by an ALD method may be used as the first insulator and silicon nitride deposited by a PEALD method may be used as the second insulator. With this structure, oxidation of the conductor 240 can be inhibited, and entry of hydrogen into the conductor 240 can be inhibited.
The conductor 246 (the conductor 246a and the conductor 246b) functioning as a wiring may be placed in contact with the top surface of the conductor 240a and the top surface of the conductor 240b. The conductor 246 is preferably formed using a conductive material containing tungsten, copper, or aluminum as its main component. Furthermore, the conductor may have a stacked-layer structure; for example, a stacked-layer structure of the conductive material and titanium or titanium nitride may be employed. Note that the conductor may be formed to be embedded in an opening provided in an insulator.
Component materials that can be used for the semiconductor device are described below.
As a substrate where the transistor 200 is formed, an insulator substrate, a semiconductor substrate, or a conductor substrate can be used, for example. Examples of the insulator substrate include a glass substrate, a quartz substrate, a sapphire substrate, a stabilized zirconia substrate (e.g., an yttria-stabilized zirconia substrate), and a resin substrate. Examples of the semiconductor substrate include a semiconductor substrate using silicon or germanium as a material and a compound semiconductor substrate including silicon carbide, silicon germanium, gallium arsenide, indium phosphide, zinc oxide, or gallium oxide. Another example is a semiconductor substrate having an insulator region in the semiconductor substrate described above, e.g., an SOI (Silicon On Insulator) substrate. Examples of the conductor substrate include a graphite substrate, a metal substrate, an alloy substrate, and a conductive resin substrate. Other examples include a substrate including a metal nitride and a substrate including a metal oxide. Other examples include an insulator substrate provided with a conductor or a semiconductor, a semiconductor substrate provided with a conductor or an insulator, and a conductor substrate provided with a semiconductor or an insulator. Alternatively, these substrates provided with elements may be used. Examples of the element provided for the substrate include a capacitor element, a resistor, a switching element, a light-emitting element, and a storage element.
Examples of the insulator include an insulating oxide, an insulating nitride, an insulating oxynitride, an insulating nitride oxide, an insulating metal oxide, an insulating metal oxynitride, and an insulating metal nitride oxide.
As miniaturization and high integration of transistors progress, for example, a problem such as leak current may arise because of a thinner gate insulator. When a high-k material is used for the insulator functioning as a gate insulator, the voltage during operation of the transistor can be lowered while the physical thickness of the gate insulator is maintained. In contrast, when a material with a low relative permittivity is used for the insulator functioning as an interlayer film, parasitic capacitance generated between wirings can be reduced. Thus, a material is preferably selected depending on the function of an insulator.
Examples of the insulator with a high relative permittivity include gallium oxide, hafnium oxide, zirconium oxide, an oxide containing aluminum and hafnium, an oxynitride containing aluminum and hafnium, an oxide containing silicon and hafnium, an oxynitride containing silicon and hafnium, and a nitride containing silicon and hafnium.
Examples of the insulator with a low relative permittivity include silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, porous silicon oxide, and a resin.
When a transistor using a metal oxide is surrounded by an insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen, the transistor can have stable electrical characteristics. As the insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen, a single layer or stacked layers of an insulator containing, for example, boron, carbon, nitrogen, oxygen, fluorine, magnesium, aluminum, silicon, phosphorus, chlorine, argon, gallium, germanium, yttrium, zirconium, lanthanum, neodymium, hafnium, or tantalum can be used. Specifically, as the insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen, a metal oxide such as aluminum oxide, magnesium oxide, gallium oxide, germanium oxide, yttrium oxide, zirconium oxide, lanthanum oxide, neodymium oxide, hafnium oxide, or tantalum oxide; or a metal nitride such as aluminum nitride, silicon nitride oxide, or silicon nitride can be used.
The insulator functioning as the gate insulator is preferably an insulator including a region containing oxygen to be released by heating. For example, when a structure in which silicon oxide or silicon oxynitride including a region containing oxygen to be released by heating is in contact with the oxide 230 is employed, oxygen vacancies included in the oxide 230 can be compensated for.
As a conductor, it is preferable to use a metal element selected from aluminum, chromium, copper, silver, gold, platinum, tantalum, nickel, titanium, molybdenum, tungsten, hafnium, vanadium, niobium, manganese, magnesium, zirconium, beryllium, indium, ruthenium, iridium, strontium, lanthanum, and the like; an alloy containing any of the above metal elements; an alloy containing a combination of the above metal elements; or the like. For example, it is preferable to use tantalum nitride, titanium nitride, tungsten, a nitride containing titanium and aluminum, a nitride containing tantalum and aluminum, ruthenium oxide, ruthenium nitride, an oxide containing strontium and ruthenium, an oxide containing lanthanum and nickel, or the like. In addition, tantalum nitride, titanium nitride, a nitride containing titanium and aluminum, a nitride containing tantalum and aluminum, ruthenium oxide, ruthenium nitride, an oxide containing strontium and ruthenium, and an oxide containing lanthanum and nickel are preferable because they are oxidation-resistant conductive materials or materials that retain their conductivity even after absorbing oxygen. Alternatively, a semiconductor with high electrical conductivity, typified by polycrystalline silicon containing an impurity element such as phosphorus, or silicide such as nickel silicide may be used.
A stack of a plurality of conductive layers formed of the above materials may be used. For example, a stacked-layer structure combining a material containing the above metal element and a conductive material containing oxygen may be employed. Alternatively, a stacked-layer structure combining a material containing the above metal element and a conductive material containing nitrogen may be employed. Alternatively, a stacked-layer structure combining a material containing the above metal element, a conductive material containing oxygen, and a conductive material containing nitrogen may be employed.
In the case where an oxide is used for the channel formation region of the transistor, the conductor functioning as the gate electrode preferably employs a stacked-layer structure combining a material containing the above metal element and a conductive material containing oxygen. In this case, the conductive material containing oxygen is preferably provided on the channel formation region side. When the conductive material containing oxygen is provided on the channel formation region side, oxygen released from the conductive material is easily supplied to the channel formation region.
For the conductor functioning as the gate electrode, it is preferable to use, in particular, a conductive material containing oxygen and a metal element contained in the metal oxide where the channel is formed. Alternatively, a conductive material containing the above metal element and nitrogen may be used. For example, a conductive material containing nitrogen, such as titanium nitride or tantalum nitride, may be used. Indium tin oxide, indium oxide containing tungsten oxide, indium zinc oxide containing tungsten oxide, indium oxide containing titanium oxide, indium tin oxide containing titanium oxide, indium zinc oxide, or indium tin oxide to which silicon is added may be used. Indium gallium zinc oxide containing nitrogen may be used. With the use of such a material, hydrogen contained in the metal oxide where the channel is formed can be captured in some cases. Alternatively, hydrogen entering from an external insulator or the like can be captured in some cases.
The oxide 230 is preferably formed using a metal oxide functioning as a semiconductor (an oxide semiconductor). A metal oxide that can be used as the oxide 230 of the present invention is described below.
The metal oxide preferably contains at least indium or zinc. In particular, indium and zinc are preferably contained. Furthermore, aluminum, gallium, yttrium, tin, or the like is preferably contained in addition to them. Furthermore, one kind or a plurality of kinds selected from boron, titanium, iron, nickel, germanium, zirconium, molybdenum, lanthanum, cerium, neodymium, hafnium, tantalum, tungsten, magnesium, cobalt, and the like may be contained.
Here, the case where the metal oxide is an In-M-Zn oxide containing indium, the element M, and zinc is considered. The element M is aluminum, gallium, yttrium, or tin. Examples of other elements that can be used as the element M include boron, titanium, iron, nickel, germanium, zirconium, molybdenum, lanthanum, cerium, neodymium, hafnium, tantalum, tungsten, magnesium, and cobalt. Note that a combination of two or more of the above elements may be used as the element M in some cases.
Note that in this specification and the like, a metal oxide containing nitrogen is also collectively referred to as a metal oxide in some cases. A metal oxide containing nitrogen may be referred to as a metal oxynitride.
First, the classification of crystal structures of an oxide semiconductor is described with reference to
As shown in
Note that the structures in the thick frame in
A crystal structure of a film or a substrate can be evaluated with an X-Ray Diffraction (XRD) spectrum.
In
A crystal structure of a film or a substrate can also be evaluated with a diffraction pattern observed by a nanobeam electron diffraction (NBED) method (such a pattern is also referred to as a nanobeam electron diffraction pattern).
As shown in
Oxide semiconductors might be classified in a manner different from that in
Here, the above-described CAAC-OS, nc-OS, and a-like OS are described in detail.
The CAAC-OS is an oxide semiconductor that has a plurality of crystal regions each of which has c-axis alignment in a particular direction. Note that the particular direction refers to the film thickness direction of a CAAC-OS film, the normal direction of the surface where the CAAC-OS film is formed, or the normal direction of the surface of the CAAC-OS film. The crystal region refers to a region having a periodic atomic arrangement. When an atomic arrangement is regarded as a lattice arrangement, the crystal region also refers to a region with a uniform lattice arrangement. The CAAC-OS has a region where a plurality of crystal regions are connected in the a-b plane direction, and the region has distortion in some cases. Note that the distortion refers to a portion where the direction of a lattice arrangement changes between a region with a uniform lattice arrangement and another region with a uniform lattice arrangement in a region where a plurality of crystal regions are connected. That is, the CAAC-OS is an oxide semiconductor having c-axis alignment and having no clear alignment in the a-b plane direction.
Note that each of the plurality of crystal regions is formed of one or more fine crystals (crystals each of which has a maximum diameter of less than 10 nm). In the case where the crystal region is formed of one fine crystal, the maximum diameter of the crystal region is less than 10 nm. In the case where the crystal region is formed of a large number of fine crystals, the size of the crystal region may be approximately several tens of nanometers.
In the case of an In-M-Zn oxide (the element M is one or more kinds selected from aluminum, gallium, yttrium, tin, titanium, and the like), the CAAC-OS tends to have a layered crystal structure (also referred to as a layered structure) in which a layer containing indium (In) and oxygen (hereinafter, an In layer) and a layer containing the element M, zinc (Zn), and oxygen (hereinafter, an (M, Zn) layer) are stacked. Indium and the element M can be replaced with each other. Therefore, indium may be contained in the (M, Zn) layer. In addition, the element M may be contained in the In layer. Note that Zn may be contained in the In layer. Such a layered structure is observed as a lattice image in a high-resolution TEM image, for example.
When the CAAC-OS film is subjected to structural analysis by out-of-plane XRD measurement with an XRD apparatus using θ/2θ scanning, for example, a peak indicating c-axis alignment is detected at 2θ of 31° or around 31°. Note that the position of the peak indicating c-axis alignment (the value of 2θ) may change depending on the kind, composition, or the like of the metal element contained in the CAAC-OS.
For example, a plurality of bright spots are observed in the electron diffraction pattern of the CAAC-OS film. Note that one spot and another spot are observed point-symmetrically with a spot of the incident electron beam passing through a sample (also referred to as a direct spot) as the symmetric center.
When the crystal region is observed from the particular direction, a lattice arrangement in the crystal region is basically a hexagonal lattice arrangement; however, a unit lattice is not always a regular hexagon and is a non-regular hexagon in some cases. A pentagonal lattice arrangement, a heptagonal lattice arrangement, and the like are included in the distortion in some cases. Note that a clear crystal grain boundary cannot be observed even in the vicinity of the distortion in the CAAC-OS. That is, formation of a crystal grain boundary is inhibited by the distortion of lattice arrangement. This is probably because the CAAC-OS can tolerate distortion owing to a low density of arrangement of oxygen atoms in the a-b plane direction, an interatomic bond distance changed by substitution of a metal atom, and the like.
A crystal structure in which a clear crystal grain boundary is observed is what is called polycrystal. It is highly probable that the crystal grain boundary becomes a recombination center and captures carriers and thus decreases the on-state current and field-effect mobility of a transistor, for example. Thus, the CAAC-OS in which no clear crystal grain boundary is observed is one of crystalline oxides having a crystal structure suitable for a semiconductor layer of a transistor. Note that Zn is preferably contained to form the CAAC-OS. For example, an In—Zn oxide and an In—Ga—Zn oxide are suitable because they can inhibit generation of a crystal grain boundary as compared with an In oxide.
The CAAC-OS is an oxide semiconductor with high crystallinity in which no clear crystal grain boundary is observed. Thus, in the CAAC-OS, reduction in electron mobility due to the crystal grain boundary is less likely to occur. Moreover, since the crystallinity of an oxide semiconductor might be decreased by entry of impurities, formation of defects, or the like, the CAAC-OS can be regarded as an oxide semiconductor that has small amounts of impurities and defects (e.g., oxygen vacancies). Thus, an oxide semiconductor including the CAAC-OS is physically stable. Therefore, the oxide semiconductor including the CAAC-OS is resistant to heat and highly reliable. In addition, the CAAC-OS is stable with respect to high temperatures in the manufacturing process (what is called thermal budget). Accordingly, the use of the CAAC-OS for the OS transistor can extend the degree of freedom of the manufacturing process.
[nc-OS]
In the nc-OS, a microscopic region (e.g., a region with a size greater than or equal to 1 nm and less than or equal to 10 nm, in particular, a region with a size greater than or equal to 1 nm and less than or equal to 3 nm) has a periodic atomic arrangement. In other words, the nc-OS includes a fine crystal. Note that the size of the fine crystal is, for example, greater than or equal to 1 nm and less than or equal to 10 nm, particularly greater than or equal to 1 nm and less than or equal to 3 nm; thus, the fine crystal is also referred to as a nanocrystal. Furthermore, there is no regularity of crystal orientation between different nanocrystals in the nc-OS. Thus, the orientation in the whole film is not observed. Accordingly, the nc-OS cannot be distinguished from an a-like OS or an amorphous oxide semiconductor by some analysis methods, in some cases. For example, when an nc-OS film is subjected to structural analysis using out-of-plane XRD measurement with an XRD apparatus using θ/2θ scanning, a peak indicating crystallinity is not detected. Furthermore, a diffraction pattern like a halo pattern is observed when the nc-OS film is subjected to electron diffraction (also referred to as selected-area electron diffraction) using an electron beam with a probe diameter greater than the diameter of a nanocrystal (e.g., greater than or equal to 50 nm). Meanwhile, in some cases, a plurality of spots in a ring-like region with a direct spot as the center are observed in the obtained electron diffraction pattern when the nc-OS film is subjected to electron diffraction (also referred to as nanobeam electron diffraction) using an electron beam with a probe diameter nearly equal to or less than the diameter of a nanocrystal (e.g., greater than or equal to 1 nm and less than or equal to 30 nm).
[a-Like OS]
The a-like OS is an oxide semiconductor having a structure between those of the nc-OS and the amorphous oxide semiconductor. The a-like OS includes a void or a low-density region. That is, the a-like OS has low crystallinity as compared with the nc-OS and the CAAC-OS. Moreover, the a-like OS has higher hydrogen concentration in the film than those of the nc-OS and the CAAC-OS.
Next, the above-described CAC-OS is described in detail. Note that the CAC-OS relates to the material composition.
The CAC-OS refers to one composition of a material in which elements constituting a metal oxide are unevenly distributed with a size greater than or equal to 0.5 nm and less than or equal to 10 nm, preferably greater than or equal to 1 nm and less than or equal to 3 nm, or a similar size, for example. Note that a state in which one or more metal elements are unevenly distributed and regions including the metal element(s) are mixed with a size greater than or equal to 0.5 nm and less than or equal to 10 nm, preferably greater than or equal to 1 nm and less than or equal to 3 nm, or a similar size in a metal oxide is hereinafter referred to as a mosaic pattern or a patch-like pattern.
In addition, the CAC-OS has a composition in which materials are separated into a first region and a second region to form a mosaic pattern, and the first regions are distributed in the film (this composition is hereinafter also referred to as a cloud-like composition). That is, the CAC-OS is a composite metal oxide having a composition in which the first regions and the second regions are mixed.
Here, the atomic ratios of In, Ga, and Zn to the metal elements contained in the CAC-OS in an In—Ga—Zn oxide are denoted by [In], [Ga], and [Zn], respectively. For example, the first region in the CAC-OS in the In—Ga—Zn oxide has [In] higher than [In] in the composition of the CAC-OS film. Moreover, the second region has [Ga] higher than [Ga] in the composition of the CAC-OS film. As another example, the first region has higher [In] and lower [Ga] than the second region. Moreover, the second region has higher [Ga] and lower [In] than the first region.
Specifically, the first region includes indium oxide, indium zinc oxide, or the like as its main component. The second region includes gallium oxide, gallium zinc oxide, or the like as its main component. That is, the first region can be referred to as a region containing In as its main component. The second region can be referred to as a region containing Ga as its main component.
Note that a clear boundary between the first region and the second region cannot be observed in some cases.
For example, energy dispersive X-ray spectroscopy (EDX) is used to obtain EDX mapping, and according to the EDX mapping, it is confirmed that the CAC-OS in the In—Ga—Zn oxide has a structure in which the region containing In as its main component (the first region) and the region containing Ga as its main component (the second region) are unevenly distributed and mixed.
In the case where the CAC-OS is used for a transistor, a switching function (on/off switching function) can be given to the CAC-OS owing to the complementary action of the conductivity derived from the first region and the insulating property derived from the second region. That is, the CAC-OS has a conducting function in part of the material and has an insulating function in another part of the material; as a whole, the CAC-OS has a function of a semiconductor. Separation of the conducting function and the insulating function can maximize each function. Accordingly, when the CAC-OS is used for a transistor, high on-state current (Ion), high field-effect mobility (μ), and excellent switching operation can be achieved.
An oxide semiconductor has various structures with different properties. Two or more kinds among the amorphous oxide semiconductor, the polycrystalline oxide semiconductor, the a-like OS, the CAC-OS, the nc-OS, and the CAAC-OS may be included in the oxide semiconductor of one embodiment of the present invention.
Next, the case where the above oxide semiconductor is used for a transistor is described.
When the above oxide semiconductor is used for a transistor, a transistor with high field-effect mobility can be achieved. In addition, a transistor having high reliability can be achieved.
An oxide semiconductor with a low carrier concentration is preferably used for a channel formation region of the transistor. For example, the carrier concentration in the channel formation region in an oxide semiconductor is lower than or equal to 1×1017 cm−3, preferably lower than or equal to 1×1015 cm−3, further preferably lower than or equal to 1×1013 cm−3, still further preferably lower than or equal to 1×1011 cm−3, yet further preferably lower than 1×1010 cm−3, and higher than or equal to 1×10−9 cm−3. In order to reduce the carrier concentration in an oxide semiconductor film, the impurity concentration in the oxide semiconductor film is reduced so that the density of defect states can be reduced. In this specification and the like, a state with a low impurity concentration and a low density of defect states is referred to as a highly purified intrinsic or substantially highly purified intrinsic state. Note that an oxide semiconductor with a low carrier concentration may be referred to as a highly purified intrinsic or substantially highly purified intrinsic oxide semiconductor.
A highly purified intrinsic or substantially highly purified intrinsic oxide semiconductor film has a low density of defect states and accordingly has a low density of trap states in some cases.
Electric charge trapped by the trap states in the oxide semiconductor takes a long time to disappear and might behave like fixed electric charge. Thus, a transistor whose channel formation region is formed in an oxide semiconductor with a high density of trap states has unstable electrical characteristics in some cases.
Accordingly, in order to obtain stable electrical characteristics of a transistor, reducing the impurity concentration in an oxide semiconductor is effective. In order to reduce the impurity concentration in the oxide semiconductor, it is preferable that the impurity concentration in an adjacent film be also reduced. Examples of impurities include hydrogen, nitrogen, an alkali metal, an alkaline earth metal, iron, nickel, and silicon.
Here, the influence of each impurity in the oxide semiconductor is described.
When silicon or carbon, which is one of Group 14 elements, is contained in the oxide semiconductor, defect states are formed in the oxide semiconductor. Thus, the concentration of silicon or carbon in the channel formation region in the oxide semiconductor and the concentration of silicon or carbon in the vicinity of an interface with the channel formation region in the oxide semiconductor (the concentrations obtained by secondary ion mass spectrometry (SIMS)) are each set lower than or equal to 2×1018 atoms/cm3, preferably lower than or equal to 2×1017 atoms/cm3.
When the oxide semiconductor contains an alkali metal or an alkaline earth metal, defect states are formed and carriers are generated in some cases. Thus, a transistor using an oxide semiconductor that contains an alkali metal or an alkaline earth metal is likely to have normally-on characteristics. Thus, the concentration of an alkali metal or an alkaline earth metal in the channel formation region in the oxide semiconductor, which is obtained by SIMS, is lower than or equal to 1×1018 atoms/cm3, preferably lower than or equal to 2×1016 atoms/cm3.
Furthermore, when the oxide semiconductor contains nitrogen, the oxide semiconductor easily becomes n-type by generation of electrons serving as carriers and an increase in carrier concentration. As a result, a transistor using an oxide semiconductor containing nitrogen as a semiconductor is likely to have normally-on characteristics. When nitrogen is contained in the oxide semiconductor, a trap state is sometimes formed. This might make the electrical characteristics of the transistor unstable. Therefore, the concentration of nitrogen in the channel formation region in the oxide semiconductor, which is obtained by SIMS, is set lower than 5×1019 atoms/cm3, preferably lower than or equal to 5×1018 atoms/cm3, further preferably lower than or equal to 1×1018 atoms/cm3, still further preferably lower than or equal to 5×1017 atoms/cm3.
Hydrogen contained in the oxide semiconductor reacts with oxygen bonded to a metal atom to be water, and thus forms an oxygen vacancy in some cases. Entry of hydrogen into the oxygen vacancy generates an electron serving as a carrier in some cases. Furthermore, bonding of part of hydrogen to oxygen bonded to a metal atom causes generation of an electron serving as a carrier in some cases. Thus, a transistor using an oxide semiconductor containing hydrogen is likely to have normally-on characteristics. Accordingly, hydrogen in the channel formation region in the oxide semiconductor is preferably reduced as much as possible. Specifically, the hydrogen concentration in the channel formation region in the oxide semiconductor, which is obtained by SIMS, is set lower than 1×1020 atoms/cm3, preferably lower than 5×1019 atoms/cm3, further preferably lower than 1×1019 atoms/cm3, still further preferably lower than 5×1018 atoms/cm3, yet still further preferably lower than 1×1018 atoms/cm3.
When an oxide semiconductor with sufficiently reduced impurities is used for the channel formation region of the transistor, stable electrical characteristics can be given.
A semiconductor material that can be used for the oxide 230 is not limited to the above metal oxides. A semiconductor material that has a band gap (a semiconductor material that is not a zero-gap semiconductor) may be used for the oxide 230. For example, a single element semiconductor such as silicon, a compound semiconductor such as gallium arsenide, or a layered material functioning as a semiconductor (also referred to as an atomic layer material, a two-dimensional material, or the like) is preferably used as a semiconductor material. In particular, a layered material functioning as a semiconductor is preferably used as a semiconductor material.
Here, in this specification and the like, the layered material generally refers to a group of materials having a layered crystal structure. In the layered crystal structure, layers formed by covalent bonding or ionic bonding are stacked with bonding such as the Van der Waals force, which is weaker than covalent bonding and ionic bonding. The layered material has high electrical conductivity in a monolayer, that is, high two-dimensional electrical conductivity. When a material that functions as a semiconductor and has high two-dimensional electrical conductivity is used for a channel formation region, a transistor having high on-state current can be provided.
Examples of the layered material include graphene, silicene, and chalcogenide. Chalcogenide is a compound containing chalcogen. Chalcogen is a general term of elements belonging to Group 16, which includes oxygen, sulfur, selenium, tellurium, polonium, and livermorium. Examples of chalcogenide include transition metal chalcogenide and chalcogenide of Group 13 elements.
For the oxide 230, a transition metal chalcogenide functioning as a semiconductor is preferably used, for example. Specific examples of the transition metal chalcogenide which can be used for the oxide 230 include molybdenum sulfide (typically MoS2), molybdenum selenide (typically MoSe2), molybdenum telluride (typically MoTe2), tungsten sulfide (typically WS2), tungsten selenide (typically WSe2), tungsten telluride (typically WTe2), hafnium sulfide (typically HfS2), hafnium selenide (typically HfSe2), zirconium sulfide (typically ZrS2), and zirconium selenide (typically ZrSe2).
Next, a manufacturing method of the semiconductor device that is one embodiment of the present invention and is illustrated in
Note that A of each drawing is a top view. Moreover, B of each drawing is a cross-sectional view corresponding to a portion indicated by dashed-dotted line A1-A2 in A of each drawing, and is also a cross-sectional view in the channel length direction of the transistor 200. Furthermore, C of each drawing is a cross-sectional view corresponding to a portion indicated by dashed-dotted line A3-A4 in A of each drawing, and is also a cross-sectional view in the channel width direction of the transistor 200. Furthermore, D of each drawing is a cross-sectional view of a portion indicated by dashed-dotted line A5-A6 in A of each drawing. Note that for clarity of the drawing, some components are not illustrated in the top view of A of each drawing.
Hereinafter, an insulating material for forming an insulator, a conductive material for forming a conductor, or a semiconductor material for forming a semiconductor can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like as appropriate.
Examples of the sputtering method include an RF sputtering method in which a high-frequency power source is used as a sputtering power source, a DC sputtering method in which a DC power source is used, and a pulsed DC sputtering method in which a voltage applied to an electrode is changed in a pulsed manner. An RF sputtering method is mainly used in the case where an insulating film is deposited, and a DC sputtering method is mainly used in the case where a metal conductive film is deposited. The pulsed DC sputtering method is mainly used in the case where a compound such as an oxide, a nitride, or a carbide is deposited by a reactive sputtering method.
Note that the CVD method can be classified into a plasma enhanced CVD (PECVD) method using plasma, a thermal CVD (TCVD) method using heat, a photo CVD method using light, and the like. Moreover, the CVD method can be classified into a metal CVD (MCVD) method and a metal organic CVD (MOCVD) method depending on a source gas to be used.
A high-quality film can be obtained at a relatively low temperature by a plasma enhanced CVD method. Furthermore, a thermal CVD method is a deposition method that does not use plasma and thus enables less plasma damage to an object to be processed. For example, a wiring, an electrode, an element (a transistor, a capacitor, or the like), or the like included in a semiconductor device might be charged up by receiving electric charge from plasma. In that case, accumulated electric charge might break the wiring, the electrode, the element, or the like included in the semiconductor device. In contrast, such plasma damage does not occur in the case of a thermal CVD method, which does not use plasma, and thus the yield of the semiconductor device can be increased. In addition, a thermal CVD method does not cause plasma damage during deposition, so that a film with few defects can be obtained.
As an ALD method, a thermal ALD method, in which a precursor and a reactant react with each other only by a thermal energy, a PEALD method, in which a reactant excited by plasma is used, or the like can be used.
A CVD method and an ALD method are different from a sputtering method in which particles ejected from a target or the like are deposited. Thus, a CVD method and an ALD method are deposition methods that enable favorable step coverage almost regardless of the shape of an object to be processed. In particular, an ALD method has excellent step coverage and excellent thickness uniformity and thus is suitable for covering a surface of an opening portion with a high aspect ratio, for example. On the other hand, an ALD method has a relatively low deposition rate, and thus is preferably used in combination with another deposition method with a high deposition rate, such as a CVD method, in some cases.
By a CVD method, a film with a certain composition can be deposited depending on the flow rate ratio of the source gases. For example, by a CVD method, a film in which the composition is continuously changed can be deposited by changing the flow rate ratio of the source gases during the deposition. In the case where the film is deposited while the flow rate ratio of the source gases is changed, as compared to the case where the film is deposited using a plurality of deposition chambers, the time taken for the deposition can be shortened because the time taken for transfer or pressure adjustment is omitted. Thus, the productivity of the semiconductor device can be increased in some cases.
By an ALD method, a film with a certain composition can be deposited by concurrently introducing a plurality of kinds of different precursors or controlling the cycle number of each of the plurality of kinds of different precursors.
First, a substrate (not illustrated) is prepared, and the insulator 212 is deposited over the substrate (see
In this embodiment, for the insulator 212, silicon nitride is deposited by a pulsed DC sputtering method using a silicon target in an atmosphere containing a nitrogen gas. The use of the pulsed DC sputtering method can inhibit generation of particles due to arcing on the target surface, achieving more uniform film thickness. In addition, by using the pulsed voltage, rising and falling in discharge can be made steep as compared with the case where a high-frequency voltage is used. As a result, power can be supplied to an electrode more efficiently to improve the sputtering rate and film quality.
The use of an insulator through which impurities such as water and hydrogen are less likely to pass, such as silicon nitride, can inhibit diffusion of impurities such as water and hydrogen contained in a layer below the insulator 212. When an insulator through which copper is less likely to pass, such as silicon nitride, is used for the insulator 212, even in the case where a metal that is likely to diffuse, such as copper, is used for a conductor in a layer (not illustrated) below the insulator 212, upward diffusion of the metal through the insulator 212 can be inhibited.
Next, the insulator 214 is deposited over the insulator 212 (see
In this embodiment, for the insulator 214, aluminum oxide is deposited by a pulsed DC sputtering method using an aluminum target in an atmosphere containing an oxygen gas. The use of the pulsed DC sputtering method can achieve more uniform film thickness and improve the sputtering rate and film quality. Here, RF (Radio Frequency) power may be applied to the substrate. The amount of oxygen supplied to a layer below the insulator 214 can be controlled depending on the amount of the RF power applied to the substrate. The RF power is higher than or equal to 0 W/cm2 and lower than or equal to 1.86 W/cm2. In other words, the supply amount of oxygen can be changed to be appropriate for the characteristics of the transistor, with the RF power used at the time of forming the insulator 214. Accordingly, an appropriate amount of oxygen for improving the reliability of the transistor can be supplied. The RF frequency is preferably 10 MHz or higher. The typical frequency is 13.56 MHz. The higher the RF frequency is, the less damage the substrate receives.
A metal oxide having an amorphous structure and an excellent function of capturing and fixing hydrogen, such as aluminum oxide, is preferably used for the insulator 214. In this case, the insulator 214 captures or fixes hydrogen contained in the insulator 216 and the like and prevents the hydrogen from diffusing into the oxide 230. Aluminum oxide having an amorphous structure or amorphous aluminum oxide is particularly preferably used for the insulator 214, in which case hydrogen can sometimes be captured or fixed more effectively. Accordingly, the transistor 200 and a semiconductor device which have favorable characteristics and high reliability can be manufactured.
Next, the insulator 216 is deposited over the insulator 214. The insulator 216 is preferably deposited by a sputtering method. By using a sputtering method that does not need to use a molecule containing hydrogen as a deposition gas, the hydrogen concentration in the insulator 216 can be reduced. Without limitation to a sputtering method, the insulator 216 may be deposited by a CVD method, an MBE method, a PLD method, an ALD method, or the like as appropriate.
In this embodiment, for the insulator 216, silicon oxide is deposited by a pulsed DC sputtering method using a silicon target in an atmosphere containing an oxygen gas. The use of the pulsed DC sputtering method can achieve more uniform film thickness and improve the sputtering rate and film quality.
The insulator 212, the insulator 214, and the insulator 216 are preferably successively deposited without exposure to the air. For example, a multi-chamber deposition apparatus may be used. As a result, the amounts of hydrogen in the deposited insulator 212, insulator 214, and insulator 216 can be reduced, and furthermore, entry of hydrogen into the films in intervals between deposition steps can be inhibited.
Then, an opening reaching the insulator 214 is formed in the insulator 216. Examples of the opening include a groove and a slit. A region where an opening is formed is referred to as an opening portion in some cases. The opening may be formed by wet etching; however, dry etching is preferable for microfabrication. As the insulator 214, it is preferable to select an insulator that functions as an etching stopper film used in forming the groove by etching the insulator 216. For example, in the case where silicon oxide or silicon oxynitride is used for the insulator 216 in which the groove is to be formed, silicon nitride, aluminum oxide, or hafnium oxide is preferably used for the insulator 214.
As a dry etching apparatus, a capacitively coupled plasma (CCP) etching apparatus including parallel plate electrodes can be used. The capacitively coupled plasma etching apparatus including the parallel plate electrodes may have a structure in which a high-frequency voltage is applied to one of the parallel plate electrodes. Alternatively, a structure may be employed in which different high-frequency voltages are applied to one of the parallel plate electrodes. Alternatively, a structure may be employed in which high-frequency voltages with the same frequency are applied to the parallel plate electrodes. Alternatively, a structure may be employed in which high-frequency voltages with different frequencies are applied to the parallel plate electrodes. Alternatively, a dry etching apparatus including a high-density plasma source can be used. As the dry etching apparatus including a high-density plasma source, an inductively coupled plasma (ICP) etching apparatus or the like can be used, for example.
After the formation of the opening, a conductive film to be the conductor 205a is deposited. The conductive film to be the conductor 205a desirably includes a conductor having a function of inhibiting passage of oxygen. For example, tantalum nitride, tungsten nitride, or titanium nitride can be used. Alternatively, a stacked film of the conductor having a function of inhibiting passage of oxygen and tantalum, tungsten, titanium, molybdenum, aluminum, copper, or a molybdenum-tungsten alloy can be used. The conductive film to be the conductor 205a can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like.
In this embodiment, titanium nitride is deposited as the conductive film to be the conductor 205a. When such a metal nitride is used for a layer under the conductor 205b, oxidation of the conductor 205b by the insulator 216 or the like can be inhibited. Furthermore, even when a metal that is likely to diffuse, such as copper, is used for the conductor 205b, the metal can be prevented from diffusing to the outside through the conductor 205a.
Next, a conductive film to be the conductor 205b is deposited. Tantalum, tungsten, titanium, molybdenum, aluminum, copper, a molybdenum-tungsten alloy, or the like can be used for the conductive film to be the conductor 205b. The conductive film can be deposited by a plating method, a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like. In this embodiment, tungsten is deposited for the conductive film to be the conductor 205b.
Next, by performing CMP treatment, the conductive film to be the conductor 205a and the conductive film to be the conductor 205b are partly removed to expose the insulator 216 (see
Next, the insulator 222 is deposited over the insulator 216 and the conductor 205 (see
The insulator 222 can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like. In this embodiment, as the insulator 222, hafnium oxide is deposited by an ALD method.
Subsequently, heat treatment is preferably performed. The heat treatment is performed at a temperature higher than or equal to 250° C. and lower than or equal to 650° C., preferably higher than or equal to 300° C. and lower than or equal to 500° C., further preferably higher than or equal to 320° C. and lower than or equal to 450° C. Note that the heat treatment is performed in a nitrogen gas or inert gas atmosphere, or an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more. For example, in the case where the heat treatment is performed in a mixed atmosphere of a nitrogen gas and an oxygen gas, the proportion of the oxygen gas may be approximately 20%. The heat treatment may be performed under reduced pressure. Alternatively, the heat treatment may be performed in an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more in order to compensate for released oxygen, after heat treatment is performed in a nitrogen gas or inert gas atmosphere.
The gas used in the above heat treatment is preferably highly purified. For example, the amount of moisture contained in the gas used in the above heat treatment is 1 ppb or less, preferably 0.1 ppb or less, further preferably 0.05 ppb or less. The heat treatment performed using a highly purified gas can prevent entry of moisture or the like into the insulator 222 and the like as much as possible.
In this embodiment, as the heat treatment, treatment at a temperature of 400° C. for one hour is performed with a flow rate ratio of a nitrogen gas to an oxygen gas of 4 slm:1 slm after the deposition of the insulator 222. By the heat treatment, impurities such as water and hydrogen contained in the insulator 222 can be removed, for example. In the case where an oxide containing hafnium is used for the insulator 222, the insulator 222 is partly crystallized by the heat treatment in some cases. The heat treatment can also be performed after the deposition of the insulator 224, for example.
Next, an insulating film 224A is deposited over the insulator 222 (see
Next, an oxide film 230A and an oxide film 230B are deposited in this order over the insulating film 224A (see
The oxide film 230A and the oxide film 230B can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like. An ALD method is preferably employed for the deposition of the oxide film 230A and the oxide film 230B, in which case a film with a uniform thickness can be formed even in a groove and an opening portion having a high aspect ratio. Employing a PEALD method is preferable because the oxide film 230A and the oxide film 230B can be formed at a lower temperature than that in the case of employing a thermal ALD method. In this embodiment, the oxide film 230A and the oxide film 230B are deposited by a sputtering method.
For example, in the case where the oxide film 230A and the oxide film 230B are deposited by a sputtering method, oxygen or a mixed gas of oxygen and a rare gas is used as a sputtering gas. Increasing the proportion of oxygen contained in the sputtering gas can increase the amount of excess oxygen in the oxide films to be deposited. In the case where the oxide films are deposited by a sputtering method, the above In-M-Zn oxide target or the like can be used.
In particular, when the oxide film 230A is deposited, part of oxygen contained in the sputtering gas is supplied to the insulator 224 in some cases. Thus, the proportion of oxygen contained in the sputtering gas is higher than or equal to 70%, preferably higher than or equal to 80%, further preferably 100%.
In the case where the oxide film 230B is deposited by a sputtering method and the proportion of oxygen contained in the sputtering gas for deposition is higher than 30% and lower than or equal to 100%, preferably higher than or equal to 70% and lower than or equal to 100%, an oxygen-excess oxide semiconductor is formed. A transistor including an oxygen-excess oxide semiconductor for its channel formation region can have relatively high reliability. Note that one embodiment of the present invention is not limited thereto. In the case where the oxide film 230B is deposited by a sputtering method and the proportion of oxygen contained in the sputtering gas for deposition is higher than or equal to 1% and lower than or equal to 30%, preferably higher than or equal to 5% and lower than or equal to 20%, an oxygen-deficient oxide semiconductor is formed. A transistor including an oxygen-deficient oxide semiconductor for its channel formation region can have relatively high field-effect mobility. Furthermore, when the deposition is performed while the substrate is being heated, the crystallinity of the oxide film can be improved.
In this embodiment, the oxide film 230A is deposited by a sputtering method using an oxide target with In:Ga:Zn=1:3:4 [atomic ratio]. In addition, the oxide film 230B is deposited by a sputtering method using an oxide target with In:Ga:Zn=4:2:4.1 [atomic ratio], an oxide target with In:Ga:Zn=1:1:1 [atomic ratio], or an oxide target with In:Ga:Zn=1:1:2 [atomic ratio]. Note that the oxide films are preferably formed so as to have characteristics required for the oxide 230a and the oxide 230b by selecting the deposition conditions and the atomic ratios as appropriate.
The insulating film 224A, the oxide film 230A, and the oxide film 230B are preferably deposited by a sputtering method without exposure to the air. For example, a multi-chamber deposition apparatus can be used. As a result, entry of hydrogen into the insulating film 224A, the oxide film 230A, and the oxide film 230B in intervals between deposition steps can be inhibited.
Next, heat treatment is preferably performed. The heat treatment can be performed in a temperature range where the oxide film 230A and the oxide film 230B do not become polycrystals, i.e., at a temperature higher than or equal to 250° C. and lower than or equal to 650° C., preferably higher than or equal to 400° C. and lower than or equal to 600° C. Note that the heat treatment is performed in a nitrogen gas or inert gas atmosphere, or an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more. For example, in the case where the heat treatment is performed in a mixed atmosphere of a nitrogen gas and an oxygen gas, the proportion of the oxygen gas may be approximately 20%. The heat treatment may be performed under reduced pressure. Alternatively, the heat treatment may be performed in an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more in order to compensate for released oxygen, after heat treatment is performed in a nitrogen gas or inert gas atmosphere.
The gas used in the above heat treatment is preferably highly purified. For example, the amount of moisture contained in the gas used in the above heat treatment is 1 ppb or less, preferably 0.1 ppb or less, and further preferably 0.05 ppb or less. The heat treatment performed using a highly purified gas can prevent entry of moisture or the like into the oxide film 230A, the oxide film 230B, and the like as much as possible.
In this embodiment, as the heat treatment, treatment at a temperature of 400° C. for one hour is performed with a flow rate ratio of a nitrogen gas and an oxygen gas to 4 slm:1 slm. By the heat treatment using the oxygen gas, impurities such as carbon, water, and hydrogen in the oxide film 230A and the oxide film 230B can be reduced, for example. The reduction of impurities in the films improves the crystallinity of the oxide film 230B, thereby offering a dense structure with higher density. Thus, crystalline regions in the oxide film 230A and the oxide film 230B are expanded, so that in-plane variations of the crystalline regions in the oxide film 230A and the oxide film 230B can be reduced. Accordingly, an in-plane variation of electrical characteristics of the transistor 200 can be reduced.
By performing the heat treatment, hydrogen in the insulator 216, the insulating film 224A, the oxide film 230A, and the oxide film 230B moves into the insulator 222 and is absorbed by the insulator 222. In other words, it can be said that hydrogen in the insulator 216, the insulating film 224A, the oxide film 230A, and the oxide film 230B diffuses into the insulator 222. Accordingly, the hydrogen concentration in the insulator 222 increases, and the hydrogen concentrations in the insulator 216, the insulating film 224A, the oxide film 230A, and the oxide film 230B decrease.
In particular, the insulating film 224A functions as a gate insulator of the transistor 200, and the oxide film 230A and the oxide film 230B function as the channel formation region of the transistor 200. Thus, the transistor 200 preferably includes the insulating film 224A, the oxide film 230A, and the oxide film 230B with reduced hydrogen concentrations to have favorable reliability.
Next, a conductive film 242A is deposited over the oxide film 230B (see
Next, an insulating film 271A is deposited over the conductive film 242A (see
Note that the conductive film 242A and the insulating film 271A are preferably deposited by a sputtering method without exposure to the air. For example, a multi-chamber deposition apparatus can be used. As a result, the amounts of hydrogen in the conductive film 242A and the insulating film 271A can be reduced, and furthermore, entry of hydrogen into the films in intervals between deposition steps can be inhibited. In the case where a hard mask is provided over the insulating film 271A, a film to be the hard mask can be successively formed without exposure to the air.
Next, the insulating film 224A, the oxide film 230A, the oxide film 230B, the conductive film 242A, and the insulating film 271A are processed into island shapes by a lithography method to form the insulator 224, the oxide 230a, the oxide 230b, a conductive layer 242B, and an insulating layer 271B (see
Note that in the lithography method, first, a resist is exposed to light through a mask. Next, a region exposed to light is removed or left using a developing solution, so that a resist mask is formed. Then, etching process through the resist mask is conducted, whereby a conductor, a semiconductor, an insulator, or the like can be processed into a desired shape. The resist mask may be formed through, for example, exposure of the resist to KrF excimer laser light, ArF excimer laser light, EUV (Extreme Ultraviolet) light, or the like. Alternatively, a liquid immersion technique may be employed in which a gap between a substrate and a projection lens is filled with liquid (e.g., water) in light exposure. Alternatively, an electron beam or an ion beam may be used instead of the light. Note that a mask is unnecessary in the case of using an electron beam or an ion beam. Note that the resist mask can be removed by a dry etching process such as ashing, a wet etching process, a wet etching process after a dry etching process, or a dry etching process after a wet etching process.
In addition, a hard mask formed of an insulator or a conductor may be used under the resist mask. In the case of using a hard mask, a hard mask with a desired shape can be formed in the following manner: an insulating film or a conductive film that is the material of the hard mask is formed over the conductive film 242A, a resist mask is formed thereover, and then the hard mask material is etched. The etching of the conductive film 242A and the like may be performed after removing the resist mask or with the resist mask remaining. In the latter case, the resist mask sometimes disappears during the etching. The hard mask may be removed by etching after the etching of the conductive film 242A and the like. Meanwhile, the hard mask is not necessarily removed when the hard mask material does not affect later steps or can be utilized in later steps. In this embodiment, the insulating layer 271B is used as a hard mask.
Here, the insulating layer 271B functions as a mask for the conductive layer 242B; thus, as illustrated in
Furthermore, as illustrated in
Not being limited to the above, the insulator 224, the oxide 230a, the oxide 230b, the conductive layer 242B, and the insulating layer 271B may have side surfaces that are substantially perpendicular to the top surface of the insulator 222. With this structure, a plurality of the transistors 200 can be provided with high density in a small area.
A by-product generated in the above etching step is sometimes formed in a layered manner on the side surfaces of the insulator 224, the oxide 230a, the oxide 230b, the conductive layer 242B, and the insulating layer 271B. In this case, the layered by-product is formed between the insulator 275 and the insulator 224, the oxide 230a, the oxide 230b, the conductive layer 242B, and the insulating layer 271B. Hence, the layered by-product formed in contact with the top surface of the insulator 222 is preferably removed.
Next, the insulator 275 is formed to cover the insulator 224, the oxide 230a, the oxide 230b, the conductive layer 242B, and the insulating layer 271B (see
In this manner, the oxide 230a, the oxide 230b, and the conductive layer 242B can be covered with the insulator 275 and the insulating layer 271B, which have a function of inhibiting diffusion of oxygen. This structure can suppress direct diffusion of oxygen from the insulator 280 or the like into the insulator 224, the oxide 230a, the oxide 230b, and the conductive layer 242B in a later step.
Next, an insulating film to be the insulator 280 is deposited over the insulator 275. The insulating film can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like. A silicon oxide film may be deposited by a sputtering method as the insulating film, for example. When the insulating film to be the insulator 280 is deposited by a sputtering method in an atmosphere containing oxygen, the insulator 280 containing excess oxygen can be formed. By using a sputtering method that does not need to use a molecule containing hydrogen as a deposition gas, the hydrogen concentration in the insulator 280 can be reduced. Note that heat treatment may be performed before the insulating film is deposited. The heat treatment may be performed under reduced pressure, and the insulating film may be successively deposited without exposure to the air. The treatment can remove moisture and hydrogen adsorbed onto the surface of the insulator 275 and the like, and further can reduce the moisture concentration and the hydrogen concentration in the oxide 230a, the oxide 230b, and the insulator 224. For the heat treatment, the above heat treatment conditions can be used.
Next, the insulating film to be the insulator 280 is subjected to CMP treatment, so that the insulator 280 with a flat top surface is formed (see
Then, part of the insulator 280, part of the insulator 275, part of the insulating layer 271B, and part of the conductive layer 242B are processed to form an opening reaching the oxide 230b. The opening is preferably formed to overlap with the conductor 205. The insulator 271a, the insulator 271b, the conductor 242a, and the conductor 242b are formed through the formation of the opening (see
As illustrated in
The part of the insulator 280, the part of the insulator 275, the part of the insulating layer 271B, and the part of the conductive layer 242B can be processed by a dry etching method or a wet etching method. Processing by a dry etching method is suitable for microfabrication. The processing may be performed under different conditions. For example, the part of the insulator 280 may be processed by a dry etching method, the part of the insulator 275 and the part of the insulating layer 271B may be processed by a wet etching method, and the part of the conductive layer 242B may be processed by a dry etching method.
Here, impurities might be attached onto the side surface of the oxide 230a, the top surface and the side surface of the oxide 230b, the side surface of the conductor 242, the side surface of the insulator 280, and the like or the impurities might be diffused thereinto. A step of removing the impurities may be performed. In addition, a damaged region might be formed on the surface of the oxide 230b by the above dry etching. The damaged region may be removed. The impurities come from components contained in the insulator 280, the insulator 275, part of the insulating layer 271B, and the conductive layer 242B; components contained in a member of an apparatus used to form the opening; and components contained in a gas or a liquid used for etching, for instance. Examples of the impurities include hafnium, aluminum, silicon, tantalum, fluorine, and chlorine.
In particular, impurities such as aluminum and silicon hinder the oxide 230b from becoming a CAAC-OS. It is thus preferable to reduce or remove impurity elements such as aluminum and silicon, which hinder the oxide from becoming a CAAC-OS. For example, the concentration of aluminum atoms in the oxide 230b and in the vicinity thereof is lower than or equal to 5.0 atomic %, preferably lower than or equal to 2.0 atomic %, further preferably lower than or equal to 1.5 atomic %, still further preferably lower than or equal to 1.0 atomic %, and yet further preferably lower than 0.3 atomic %.
Note that in a metal oxide, a region that is hindered from becoming a CAAC-OS by impurities such as aluminum and silicon and becomes an amorphous-like oxide semiconductor (a-like OS) is referred to as a non-CAAC region in some cases. In the non-CAAC region, the density of the crystal structure is reduced to form a large amount of VOH; thus, the transistor is likely to be normally on. Hence, the non-CAAC region in the oxide 230b is preferably reduced or removed.
In contrast, the oxide 230b preferably has a layered CAAC structure. In particular, the CAAC structure preferably reaches a lower edge portion of a drain in the oxide 230b. Here, in the transistor 200, the conductor 242a or the conductor 242b, and its vicinity function as a drain. In other words, the oxide 230b in the vicinity of the lower edge portion of the conductor 242a (conductor 242b) preferably has a CAAC structure. In this manner, the damaged region of the oxide 230b is removed and the CAAC structure is formed also in the edge portion of the drain, which significantly affects the drain breakdown voltage, so that variation in the electrical characteristics of the transistor 200 can be further suppressed. In addition, the reliability of the transistor 200 can be improved.
In order to remove impurities and the like attached to the surface of the oxide 230b in the above etching step, cleaning treatment is performed. Examples of the cleaning method include wet cleaning using a cleaning solution or the like (which also can be referred to as wet etching process), plasma treatment using plasma, and cleaning by heat treatment, and any of these cleanings may be performed in combination as appropriate. The cleaning treatment sometimes makes the groove portion deeper.
As the wet cleaning, cleaning treatment may be performed using an aqueous solution in which ammonia water, oxalic acid, phosphoric acid, hydrofluoric acid, or the like is diluted with carbonated water or pure water; pure water; carbonated water; or the like. Alternatively, ultrasonic cleaning using such an aqueous solution, pure water, or carbonated water may be performed. Alternatively, such cleaning methods may be performed in combination as appropriate.
Note that in this specification and the like, in some cases, an aqueous solution in which hydrofluoric acid is diluted with pure water is referred to as diluted hydrofluoric acid, and an aqueous solution in which ammonia water is diluted with pure water is referred to as diluted ammonia water. The concentration, temperature, and the like of the aqueous solution may be adjusted as appropriate in accordance with an impurity to be removed, the structure of a semiconductor device to be cleaned, or the like. The concentration of ammonia in the diluted ammonia water is higher than or equal to 0.01% and lower than or equal to 5%, preferably higher than or equal to 0.1% and lower than or equal to 0.5%. The concentration of hydrogen fluoride in the diluted hydrofluoric acid is higher than or equal to 0.01 ppm and lower than or equal to 100 ppm, preferably higher than or equal to 0.1 ppm and lower than or equal to 10 ppm.
For the ultrasonic cleaning, a frequency higher than or equal to 200 kHz is preferably used and a frequency higher than or equal to 900 kHz is further preferably used. When such a frequency is used, damage to the oxide 230b and the like can be reduced.
The cleaning treatment may be performed a plurality of times, and the cleaning solution may be changed in every cleaning treatment. For example, the first cleaning treatment may use diluted hydrofluoric acid or diluted ammonia water and the second cleaning treatment may use pure water or carbonated water.
As the cleaning treatment in this embodiment, wet cleaning using diluted ammonia water is performed. The cleaning treatment can remove impurities that are attached onto the surfaces of the oxide 230a, the oxide 230b, and the like or diffused into the oxide 230a, the oxide 230b, and the like. Furthermore, the crystallinity of the oxide 230b can be increased.
After the etching or the cleaning, heat treatment may be performed. The heat treatment can be performed at higher than or equal to 100° C. and lower than or equal to 450° C., preferably higher than or equal to 350° C. and lower than or equal to 400° C. Note that the heat treatment is performed in a nitrogen gas or inert gas atmosphere, or an atmosphere containing an oxidizing gas at 10 ppm or more, 1% or more, or 10% or more. For example, the heat treatment is preferably performed in an oxygen atmosphere. Accordingly, oxygen can be supplied to the oxide 230a and the oxide 230b to reduce oxygen vacancies VO. In addition, the crystallinity of the oxide 230b can be improved by the heat treatment. The heat treatment may be performed under reduced pressure. Alternatively, the heat treatment may be performed in a nitrogen atmosphere without exposure to the air successively after heat treatment is performed in an oxygen atmosphere.
Next, an insulating film 252A is formed (see
When the insulating film 252A is deposited by an ALD method, ozone (03), oxygen (02), water (H2O), or the like can be used as the oxidizer. When ozone (03), oxygen (02), or the like, which does not contain hydrogen, is used as an oxidizer, the amount of hydrogen diffusing into the oxide 230b can be reduced.
In this embodiment, aluminum oxide is deposited for the insulating film 252A by a thermal ALD method.
Next, it is preferable to perform microwave treatment in an atmosphere containing oxygen (see
Dotted lines in
The microwave treatment is preferably performed under reduced pressure, and the pressure may be higher than or equal to 10 Pa and lower than or equal to 1000 Pa, preferably higher than or equal to 300 Pa and lower than or equal to 700 Pa. The treatment temperature may be lower than or equal to 750° C., preferably lower than or equal to 500° C., and is approximately 400° C., for example. The oxygen plasma treatment can be followed successively by heat treatment without exposure to the air. For example, the heat treatment may be performed at higher than or equal to 100° C. and lower than or equal to 750° C., preferably higher than or equal to 300° C. and lower than or equal to 500° C.
Furthermore, the microwave treatment is performed using an oxygen gas and an argon gas, for example. Here, the oxygen flow rate ratio (O2/(O2+Ar)) is higher than 0% and lower than or equal to 100%. The oxygen flow rate ratio (O2/(O2+Ar)) is preferably higher than 0% and lower than or equal to 50%. The oxygen flow rate ratio (O2/(O2+Ar)) is further preferably higher than or equal to 10% and lower than or equal to 40%. The oxygen flow rate ratio (O2/(O2+Ar)) is still further preferably higher than or equal to 10% and lower than or equal to 30%. The carrier concentration in the region 230bc can be reduced by thus performing the microwave treatment in an atmosphere containing oxygen. In addition, the carrier concentrations in the region 230ba and the region 230bb can be prevented from being excessively reduced by preventing an excess amount of oxygen from being introduced into the chamber in the microwave treatment.
As illustrated in
By contrast, the conductor 242a and the conductor 242b are provided over the region 230ba and the region 230bb illustrated in
As illustrated in
Furthermore, the insulator 252 having a barrier property against oxygen is provided in contact with the side surfaces of the conductor 242a and the conductor 242b. Thus, formation of oxide films on the side surfaces of the conductor 242a and the conductor 242b by the microwave treatment can be inhibited.
In the above manner, oxygen vacancies and VOH can be selectively removed from the region 230bc in the oxide semiconductor, whereby the region 230bc can be an i-type or substantially i-type region. Furthermore, supply of an excess amount of oxygen to the region 230ba and the region 230bb functioning as the source region and the drain region can be inhibited and the n-type conductivity can be maintained. As a result, a change in the electrical characteristics of the transistor 200 can be inhibited, and thus a variation in the electrical characteristics of the transistors 200 in the substrate plane can be inhibited.
In the microwave treatment, thermal energy is directly transmitted to the oxide 230b in some cases owing to an electromagnetic interaction between the microwave and a molecule in the oxide 230b. The oxide 230b might be heated by this thermal energy. Such heat treatment is sometimes referred to as microwave annealing. When microwave treatment is performed in an atmosphere containing oxygen, an effect equivalent to that of oxygen annealing is sometimes obtained. In the case where hydrogen is contained in the oxide 230b, it is probable that the thermal energy is transmitted to the hydrogen in the oxide 230b and the hydrogen activated by the energy is released from the oxide 230b.
Next, an insulating film 250A is deposited (see
The insulating film 250A can be deposited by a sputtering method, a CVD method, a PECVD method, an MBE method, a PLD method, an ALD method, or the like. The insulating film 250A is preferably deposited by a deposition method using a gas in which hydrogen atoms are reduced or removed. This can reduce the hydrogen concentration in the insulating film 250A. The hydrogen concentration in the insulating film 250A is preferably reduced because the insulating film 250A becomes the insulator 250a that faces the oxide 230b with the insulator 252 with a small thickness therebetween, in a later step.
In this embodiment, silicon oxynitride is deposited as the insulating film 250A by a PECVD method.
In the case where the insulator 250 has a two-layer structure as illustrated in
After the insulating film 250A is deposited, microwave treatment may be performed (see
Heat treatment may be performed while the reduced pressure is maintained after each of microwave treatment after the deposition of the insulating film 252A and the insulating film 250A and microwave treatment after the deposition of the insulating film to be the insulator 250b. Such treatment enables hydrogen in the insulating film 252A, the insulating film 250A, the insulating film to be the insulator 250b, the oxide 230b, and the oxide 230a to be removed efficiently. Part of hydrogen is gettered by the conductor 242 (the conductor 242a and the conductor 242b) in some cases. Alternatively, the step of performing microwave treatment and then performing heat treatment with the reduced pressure being maintained may be repeated a plurality of cycles. The repetition of the heat treatment enables hydrogen in the insulating film 252A, the insulating film 250A, the insulating film to be the insulator 250b, the oxide 230b, and the oxide 230a to be removed more efficiently. Note that the temperature of the heat treatment is preferably higher than or equal to 300° C. and lower than or equal to 500° C. The microwave treatment, i.e., the microwave annealing, may also serve as the heat treatment. The heat treatment is not necessarily performed in the case where the oxide 230b and the like are adequately heated by the microwave annealing.
Furthermore, the microwave treatment modifies the film quality of the insulating film 252A, the insulating film 250A, and the insulating film to be the insulator 250b, thereby inhibiting diffusion of hydrogen, water, impurities, and the like. Accordingly, hydrogen, water, impurities, and the like can be inhibited from diffusing into the oxide 230b, the oxide 230a, and the like through the insulator 252 in a later step such as deposition of a conductive film to be the conductor 260 or later treatment such as heat treatment.
Next, an insulating film 254A is deposited (see
Next, a conductive film to be the conductor 260a and a conductive film to be the conductor 260b are deposited in this order. The conductive film to be the conductor 260a and the conductive film to be the conductor 260b can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like. In this embodiment, titanium nitride is deposited as the conductive film to be the conductor 260a by an ALD method, and tungsten is deposited as the conductive film to be the conductor 260b by a CVD method.
Then, the insulating film 252A, the insulating film 250A, the insulating film 254A, the conductive film to be the conductor 260a, and the conductive film to be the conductor 260b are polished by CMP treatment until the insulator 280 is exposed, whereby the insulator 252, the insulator 250, the insulator 254, and the conductor 260 (the conductor 260a and the conductor 260b) are formed (see
Then, heat treatment may be performed under conditions similar to those for the above heat treatment. In this embodiment, treatment is performed at a temperature of 400° C. in a nitrogen atmosphere for one hour. The heat treatment can reduce the moisture concentration and the hydrogen concentration in the insulator 250 and the insulator 280. After the heat treatment, the insulator 282 may be deposited successively without exposure to the air.
Next, the insulator 282 is formed over the insulator 252, the insulator 250, the conductor 260, and the insulator 280 (see
In this embodiment, as the insulator 282, aluminum oxide is deposited by a pulsed DC sputtering method using an aluminum target in an atmosphere containing an oxygen gas. The use of the pulsed DC sputtering method can achieve more uniform film thickness and improve the sputtering rate and film quality.
The insulator 282 is deposited by a sputtering method in an atmosphere containing oxygen, whereby oxygen can be added to the insulator 280 during the deposition. Thus, excess oxygen can be contained in the insulator 280. At this time, the insulator 282 is preferably deposited while the substrate is being heated.
Next, an etching mask is formed over the insulator 282 by a lithography method and part of the insulator 282, part of the insulator 280, part of the insulator 275, part of the insulator 222, and part of the insulator 216 are processed until the top surface of the insulator 214 is exposed (see
Next, heat treatment may be performed. The heat treatment is performed at higher than or equal to 250° C. and lower than or equal to 650° C., preferably higher than or equal to 350° C. and lower than or equal to 600° C. The heat treatment is preferably performed at a temperature lower than that of the heat treatment performed after the deposition of the oxide film 230B. Note that the heat treatment is performed in an atmosphere of a nitrogen gas or an inert gas. By performing the heat treatment, part of oxygen added to the insulator 280 is diffused into the oxide 230 through the insulator 250 and the like.
By performing the heat treatment, oxygen contained in the insulator 280 and hydrogen bonded to the oxygen can be released to the outside from the side surface of the insulator 280 formed by the processing of the insulator 282, the insulator 280, the insulator 275, the insulator 222, and the insulator 216. Note that the hydrogen bonded to oxygen is released as water. Thus, unnecessary oxygen and hydrogen contained in the insulator 280 can be reduced.
In a region of the oxide 230 that overlaps with the conductor 260, the insulator 252 is provided to be in contact with the top surface and the side surface of the oxide 230. Since the insulator 252 has a barrier property against oxygen, diffusion of an excess amount of oxygen to the oxide 230 can be suppressed. This allows oxygen to be supplied to the region 230bc and the vicinity thereof such that an excess amount of oxygen is not supplied thereto. Accordingly, oxygen vacancies and VOH formed in the region 230bc can be reduced while oxidation of the side surface of the conductor 242 due to excess oxygen can be inhibited. Thus, the transistor 200 can have good electrical characteristics and higher reliability.
On the other hand, in the case where the transistors 200 are integrated at a high density, the volume of the insulator 280 becomes excessively small with respect to one transistor 200 in some cases. In this case, the amount of oxygen diffused into the oxide 230 becomes significantly small in the heat treatment. When the oxide 230 is heated while being in contact with the oxide insulator (e.g., the insulator 250) which does not contain sufficient oxygen, oxygen contained in the oxide 230 might be released. However, in the transistor 200 described in this embodiment, the insulator 252 is provided in contact with the top surface and side surfaces of the oxide 230 in the region of the oxide 230 that overlaps with the conductor 260. Since the insulator 252 has a barrier property against oxygen, release of the oxygen from the oxide 230 can be reduced also in the heat treatment. Thus, the amount of oxygen vacancies and VOH formed in the region 230bc can be reduced. Thus, the transistor 200 can have good electrical characteristics and higher reliability.
As described above, in either case of a large or small amount of oxygen supplied from the insulator 280 in the semiconductor device of this embodiment, the transistor can have good electrical characteristics and high reliability. Thus, a semiconductor device with a reduced variation in the electrical characteristics of the transistors 200 in the substrate plane can be provided.
Next, the insulator 283 is formed over the insulator 282 (see
Next, the insulator 274 is formed over the insulator 283. The insulator 274 can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like. In this embodiment, as the insulator 274, silicon oxide is deposited by a CVD method.
Next, the insulator 274 is polished by CMP treatment until the insulator 283 is exposed, whereby the top surface of the insulator 274 is planarized (see
Next, the insulator 285 is formed over the insulator 274 and the insulator 283 (see
In this embodiment, as the insulator 285, silicon oxide is deposited by a sputtering method.
Subsequently, openings reaching the conductor 242 are formed in the insulator 271, the insulator 275, the insulator 280, the insulator 282, the insulator 283, and the insulator 285 (see
Subsequently, an insulating film to be the insulator 241 is deposited and the insulating film is subjected to anisotropic etching, so that the insulator 241 is formed (see
For anisotropic etching for the insulating film to be the insulator 241, a dry etching method may be employed, for example. When the insulator 241 is provided on the sidewall portions of the openings, passage of oxygen from the outside can be inhibited and oxidation of the conductor 240a and the conductor 240b to be formed next can be prevented. Furthermore, impurities such as water and hydrogen contained in the insulator 280 and the like can be prevented from diffusing into the conductor 240a and the conductor 240b.
Next, a conductive film to be the conductor 240a and the conductor 240b is deposited. The conductive film to be the conductor 240a and the conductor 240b desirably has a stacked-layer structure which includes a conductor having a function of inhibiting passage of impurities such as water and hydrogen. For example, a stack of tantalum nitride, titanium nitride, or the like and tungsten, molybdenum, copper, or the like can be employed. The conductive film to be the conductor 240a and the conductor 240b can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like.
Then, part of the conductive film to be the conductor 240a and the conductor 240b is removed by CMP treatment to expose the top surface of the insulator 285. As a result, the conductive film remains only in the openings, so that the conductor 240a and the conductor 240b having flat top surfaces can be formed (see
Next, a conductive film to be the conductor 246 is deposited. The conductive film to be the conductor 246 can be deposited by a sputtering method, a CVD method, an MBE method, a PLD method, an ALD method, or the like.
Then, the conductive film to be the conductor 246 is processed by a lithography method, so that the conductor 246a in contact with the top surface of the conductor 240a and the conductor 246b in contact with the top surface of the conductor 240b are formed. At this time, part of the insulator 285 in a region where the insulator 285 does not overlap with the conductor 246a or the conductor 246b is sometimes removed.
Through the above process, the semiconductor device including the transistor 200 illustrated in
A microwave treatment apparatus that can be used for the above manufacturing method of the semiconductor device is described below.
First, a structure of a manufacturing apparatus that hardly allows entry of impurities in manufacturing a semiconductor device or the like is described with reference to
Furthermore, the atmosphere-side substrate transfer chamber 2702 is connected to the load lock chamber 2703a and the unload lock chamber 2703b, the load lock chamber 2703a and the unload lock chamber 2703b are connected to the transfer chamber 2704, and the transfer chamber 2704 is connected to the chamber 2706a, the chamber 2706b, the chamber 2706c, and the chamber 2706d.
Note that gate valves GV are provided in connecting portions between the chambers so that the chambers other than the atmosphere-side substrate supply chamber 2701 and the atmosphere-side substrate transfer chamber 2702 can be each independently kept in a vacuum state. Furthermore, the atmosphere-side substrate transfer chamber 2702 is provided with a transfer robot 2763a, and the transfer chamber 2704 is provided with a transfer robot 2763b. With the transfer robot 2763a and the transfer robot 2763b, a substrate can be transferred inside the manufacturing apparatus 2700.
The back pressure (total pressure) in the transfer chamber 2704 and each of the chambers is, for example, lower than or equal to 1×10−4 Pa, preferably lower than or equal to 3×10−5 Pa, further preferably lower than or equal to 1×10−5 Pa. Furthermore, the partial pressure of a gas molecule (atom) having a mass-to-charge ratio (m/z) of 18 in the transfer chamber 2704 and each of the chambers is, for example, lower than or equal to 3×10−5 Pa, preferably lower than or equal to 1×10−5 Pa, further preferably lower than or equal to 3×10−6 Pa. Furthermore, the partial pressure of a gas molecule (atom) having m/z of 28 in the transfer chamber 2704 and each of the chambers is, for example, lower than or equal to 3×10−5 Pa, preferably lower than or equal to 1×10−5 Pa, further preferably lower than or equal to 3×10−6 Pa. Furthermore, the partial pressure of a gas molecule (atom) having m/z of 44 in the transfer chamber 2704 and each of the chambers is, for example, lower than or equal to 3×10−5 Pa, preferably lower than or equal to 1×10−5 Pa, further preferably lower than or equal to 3×10−6 Pa.
Note that the total pressure and the partial pressure in the transfer chamber 2704 and each of the chambers can be measured using a mass analyzer. For example, Qulee CGM-051, a quadrupole mass analyzer (also referred to as Q-mass) produced by ULVAC, Inc. can be used.
Furthermore, the transfer chamber 2704 and the chambers each desirably have a structure in which the amount of external leakage or internal leakage is small. For example, the leakage rate in the transfer chamber 2704 and each of the chambers is less than or equal to 3×10−6 Pa·m3/s, preferably less than or equal to 1×10−6 Pa·m3/s. Furthermore, for example, the leakage rate of a gas molecule (atom) having m/z of 18 is less than or equal to 1×10−7 Pa·m3/s, preferably less than or equal to 3×10−8 Pa·m3/s. Furthermore, for example, the leakage rate of a gas molecule (atom) having m/z of 28 is less than or equal to 1×10−5 Pa·m3/s, preferably less than or equal to 1×10−6 Pa·m3/s. Furthermore, for example, the leakage rate of a gas molecule (atom) having m/z of 44 is less than or equal to 3×10−6 Pa·m3/s, preferably less than or equal to 1×10−6 Pa·m3/s.
Note that a leakage rate can be derived from the total pressure and partial pressure measured using the above-described mass analyzer. The leakage rate depends on external leakage and internal leakage. The external leakage refers to inflow of gas from the outside of a vacuum system through a minute hole, a sealing defect, or the like. The internal leakage is due to leakage through a partition, such as a valve, in a vacuum system or released gas from an internal member. Measures need to be taken from both aspects of external leakage and internal leakage in order that the leakage rate can be set to less than or equal to the above-described value.
For example, open/close portions of the transfer chamber 2704 and each of the chambers are preferably sealed with a metal gasket. For the metal gasket, metal covered with iron fluoride, aluminum oxide, or chromium oxide is preferably used. The metal gasket achieves higher adhesion than an O-ring and can reduce the external leakage. Furthermore, with the use of passive metal covered with iron fluoride, aluminum oxide, chromium oxide, or the like, the release of gas containing impurities released from the metal gasket is inhibited, so that the internal leakage can be reduced.
Furthermore, for a member of the manufacturing apparatus 2700, aluminum, chromium, titanium, zirconium, nickel, or vanadium, which releases a small amount of gas containing impurities, is used. Furthermore, an alloy containing iron, chromium, nickel, and the like covered with the above-described metal, which releases a small amount of gas containing impurities, may be used. The alloy containing iron, chromium, nickel, and the like is rigid, resistant to heat, and suitable for processing. Here, when surface unevenness of the member is reduced by polishing or the like to reduce the surface area, the release of gas can be reduced.
Alternatively, the above-described member of the manufacturing apparatus 2700 may be covered with iron fluoride, aluminum oxide, chromium oxide, or the like.
The member of the manufacturing apparatus 2700 is preferably formed using only metal when possible, and in the case where a viewing window formed of quartz or the like is provided, for example, the surface is preferably thinly covered with iron fluoride, aluminum oxide, chromium oxide, or the like to inhibit release of gas.
An adsorbed substance present in the transfer chamber 2704 and each of the chambers does not affect the pressure in the transfer chamber 2704 and each of the chambers because it is adsorbed onto an inner wall or the like; however, it causes a release of gas when the transfer chamber 2704 and each of the chambers are evacuated. Thus, although there is no correlation between the leakage rate and the exhaust rate, it is important that the adsorbed substance present in the transfer chamber 2704 and each of the chambers be desorbed as much as possible and exhaust be performed in advance with the use of a pump having high exhaust capability. Note that the transfer chamber 2704 and each of the chambers may be subjected to baking to promote desorption of the adsorbed substance. By the baking, the desorption rate of the adsorbed substance can be increased about tenfold. The baking is performed at higher than or equal to 100° C. and lower than or equal to 450° C. At this time, when the adsorbed substance is removed while an inert gas is introduced into the transfer chamber 2704 and each of the chambers, the desorption rate of water or the like, which is difficult to desorb simply by exhaust, can be further increased. Note that when the inert gas to be introduced is heated to substantially the same temperature as the baking temperature, the desorption rate of the adsorbed substance can be further increased. Here, a rare gas is preferably used as the inert gas.
Alternatively, treatment for evacuating the transfer chamber 2704 and each of the chambers is preferably performed a certain period of time after a heated inert gas such as a rare gas, heated oxygen, or the like is introduced to increase the pressure in the transfer chamber 2704 and each of the chambers. The introduction of the heated gas can desorb the adsorbed substance in the transfer chamber 2704 and each of the chambers, and impurities present in the transfer chamber 2704 and each of the chambers can be reduced. Note that this treatment is effective when repeated more than or equal to 2 times and less than or equal to 30 times, preferably more than or equal to 5 times and less than or equal to 15 times. Specifically, an inert gas, oxygen, or the like at a temperature higher than or equal to 40° C. and lower than or equal to 400° C., preferably higher than or equal to 50° C. and lower than or equal to 200° C. is introduced, so that the pressure in the transfer chamber 2704 and each of the chambers can be kept to be higher than or equal to 0.1 Pa and lower than or equal to 10 kPa, preferably higher than or equal to 1 Pa and lower than or equal to 1 kPa, further preferably higher than or equal to 5 Pa and lower than or equal to 100 Pa within the time range of 1 minute to 300 minutes, preferably 5 minutes to 120 minutes. After that, the transfer chamber 2704 and each of the chambers are evacuated within the time range of 5 minutes to 300 minutes, preferably 10 minutes to 120 minutes.
Next, the chamber 2706b and the chamber 2706c are described with reference to a schematic cross-sectional view illustrated in
The chamber 2706b and the chamber 2706c are chambers in which microwave treatment can be performed on an object, for example. Note that the chamber 2706b is different from the chamber 2706c only in the atmosphere in performing the microwave treatment. The other structures are common and thus collectively described below.
The chamber 2706b and the chamber 2706c each include a slot antenna plate 2808, a dielectric plate 2809, a substrate holder 2812, and an exhaust port 2819. Furthermore, a gas supply source 2801, a valve 2802, a high-frequency generator 2803, a waveguide 2804, a mode converter 2805, a gas pipe 2806, a waveguide 2807, a matching box 2815, a high-frequency power source 2816, a vacuum pump 2817, and a valve 2818 are provided outside the chamber 2706b and the chamber 2706c, for example.
The high-frequency generator 2803 is connected to the mode converter 2805 through the waveguide 2804. The mode converter 2805 is connected to the slot antenna plate 2808 through the waveguide 2807. The slot antenna plate 2808 is placed in contact with the dielectric plate 2809. Furthermore, the gas supply source 2801 is connected to the mode converter 2805 through the valve 2802. Then, gas is transferred to the chamber 2706b and the chamber 2706c through the gas pipe 2806 that runs through the mode converter 2805, the waveguide 2807, and the dielectric plate 2809. Furthermore, the vacuum pump 2817 has a function of exhausting gas or the like from the chamber 2706b and the chamber 2706c through the valve 2818 and the exhaust port 2819. Furthermore, the high-frequency power source 2816 is connected to the substrate holder 2812 through the matching box 2815.
The substrate holder 2812 has a function of holding a substrate 2811. For example, the substrate holder 2812 has a function of an electrostatic chuck or a mechanical chuck for holding the substrate 2811. Furthermore, the substrate holder 2812 has a function of an electrode to which electric power is supplied from the high-frequency power source 2816. Furthermore, the substrate holder 2812 includes a heating mechanism 2813 therein and has a function of heating the substrate 2811.
As the vacuum pump 2817, a dry pump, a mechanical booster pump, an ion pump, a titanium sublimation pump, a cryopump, a turbomolecular pump, or the like can be used, for example. Furthermore, in addition to the vacuum pump 2817, a cryotrap may be used. The use of the cryopump and the cryotrap is particularly preferable because water can be efficiently exhausted.
Furthermore, for example, the heating mechanism 2813 may be a heating mechanism that uses a resistance heater or the like for heating. Alternatively, a heating mechanism that uses heat conduction or heat radiation from a medium such as a heated gas for heating may be used. For example, RTA (Rapid Thermal Annealing) such as GRTA (Gas Rapid Thermal Annealing) or LRTA (Lamp Rapid Thermal Annealing) can be used. In GRTA, heat treatment is performed using a high-temperature gas. An inert gas is used as the gas.
Furthermore, the gas supply source 2801 may be connected to a purifier through a mass flow controller. As the gas, a gas whose dew point is −80° C. or lower, preferably −100° C. or lower is preferably used. For example, an oxygen gas, a nitrogen gas, or a rare gas (an argon gas or the like) is used.
As the dielectric plate 2809, silicon oxide (quartz), aluminum oxide (alumina), or yttrium oxide (yttria) is used, for example. Furthermore, another protective layer may be further formed on a surface of the dielectric plate 2809. For the protective layer, magnesium oxide, titanium oxide, chromium oxide, zirconium oxide, hafnium oxide, tantalum oxide, silicon oxide, aluminum oxide, yttrium oxide, or the like is used. The dielectric plate 2809 is exposed to an especially high density region of high-density plasma 2810 described later; thus, provision of the protective layer can reduce the damage. Consequently, an increase in the number of particles or the like during the treatment can be inhibited.
The high-frequency generator 2803 has a function of generating a microwave at, for example, higher than or equal to 0.3 GHz and lower than or equal to 3.0 GHz, higher than or equal to 0.7 GHz and lower than or equal to 1.1 GHz, or higher than or equal to 2.2 GHz and lower than or equal to 2.8 GHz. The microwave generated by the high-frequency generator 2803 is propagated to the mode converter 2805 through the waveguide 2804. The mode converter 2805 converts the microwave propagated in the TE mode into a microwave in the TEM mode. Then, the microwave is propagated to the slot antenna plate 2808 through the waveguide 2807. The slot antenna plate 2808 is provided with a plurality of slot holes, and the microwave passes through the slot holes and the dielectric plate 2809. Then, an electric field is generated below the dielectric plate 2809, and the high-density plasma 2810 can be generated. In the high-density plasma 2810, ions and radicals corresponding to the gas species supplied from the gas supply source 2801 are present. For example, oxygen radicals are present.
At this time, the quality of a film or the like over the substrate 2811 can be modified by the ions and radicals generated in the high-density plasma 2810. Note that it is preferable in some cases to apply a bias to the substrate 2811 side using the high-frequency power source 2816. As the high-frequency power source 2816, an RF (Radio Frequency) power source with a frequency of 13.56 MHz, 27.12 MHz, or the like may be used, for example. The application of a bias to the substrate side allows ions in the high-density plasma 2810 to efficiently reach a deep portion of an opening portion of the film or the like over the substrate 2811.
For example, in the chamber 2706b or the chamber 2706c, oxygen radical treatment using the high-density plasma 2810 can be performed by introducing oxygen from the gas supply source 2801.
Next, the chamber 2706a and the chamber 2706d are described with reference to a schematic cross-sectional view illustrated in
The chamber 2706a and the chamber 2706d are chambers in which an object can be irradiated with an electromagnetic wave, for example. Note that the chamber 2706a is different from the chamber 2706d only in the kind of the electromagnetic wave. The other structures have many common portions and thus are collectively described below.
The chamber 2706a and the chamber 2706d each include one or more lamps 2820, a substrate holder 2825, a gas inlet 2823, and an exhaust port 2830. Furthermore, a gas supply source 2821, a valve 2822, a vacuum pump 2828, and a valve 2829 are provided outside the chamber 2706a and the chamber 2706d, for example.
The gas supply source 2821 is connected to the gas inlet 2823 through the valve 2822. The vacuum pump 2828 is connected to the exhaust port 2830 through the valve 2829. The lamp 2820 is provided to face the substrate holder 2825. The substrate holder 2825 has a function of holding a substrate 2824. Furthermore, the substrate holder 2825 includes a heating mechanism 2826 therein and has a function of heating the substrate 2824.
As the lamp 2820, a light source having a function of emitting an electromagnetic wave such as visible light or ultraviolet light may be used, for example. A light source having a function of emitting an electromagnetic wave which has a peak at a wavelength longer than or equal to 10 nm and shorter than or equal to 2500 nm, longer than or equal to 500 nm and shorter than or equal to 2000 nm, or longer than or equal to 40 nm and shorter than or equal to 340 nm, for example, can be used.
As the lamp 2820, a light source such as a halogen lamp, a metal halide lamp, a xenon arc lamp, a carbon arc lamp, a high-pressure sodium lamp, or a high-pressure mercury lamp can used, for example.
For example, part or the whole of electromagnetic wave emitted from the lamp 2820 can modify the quality of a film or the like over the substrate 2824 when being absorbed by the substrate 2824. For example, generation or reduction of defects, removal of impurities, or the like can be performed. Note that generation or reduction of defects, removal of impurities, or the like can be efficiently performed while the substrate 2824 is heated.
Alternatively, for example, the electromagnetic wave emitted from the lamp 2820 may generate heat in the substrate holder 2825 to heat the substrate 2824. In this case, the substrate holder 2825 does not need to include the heating mechanism 2826 therein.
For the vacuum pump 2828, refer to the description of the vacuum pump 2817. Furthermore, for the heating mechanism 2826, refer to the description of the heating mechanism 2813. Furthermore, for the gas supply source 2821, refer to the description of the gas supply source 2801.
A microwave treatment apparatus that can be used in this embodiment is not limited to the above. A microwave treatment apparatus 2900 illustrated in
The substrate provided in the quartz tube 2901 is irradiated with the microwave generated by the high-frequency generator 2803, through the waveguide 2804. The vacuum pump 2817 is connected to the exhaust port 2819 through the valve 2818 and can adjust the pressure inside the quartz tube 2901. The gas supply source 2801 is connected to the gas pipe 2806 through the valve 2802 and can introduce a desired gas into the quartz tube 2901. The heating means 2903 can heat the substrate 2811 in the quartz tube 2901 to a desired temperature. Alternatively, the heating means 2903 may heat the gas which is supplied from the gas supply source 2801. With the use of the microwave treatment apparatus 2900, the substrate 2811 can be subjected to heat treatment and microwave treatment at the same time. Alternatively, the substrate 2811 can be heated and then subjected to microwave treatment. Alternatively, the substrate 2811 can be subjected to microwave treatment and then heat treatment.
All of the substrate 2811_1 to the substrate 2811_n may be substrates to be treated where a semiconductor device or a storage device is to be formed, or some of the substrates may be dummy substrates. For example, the substrate 2811_1 and the substrate 2811_n may be dummy substrates and the substrate 2811_2 to the substrate 2811_n−1 may be substrates to be treated. Alternatively, the substrate 2811_1, the substrate 2811_2, the substrate 2811_n−1, and the substrate 2811_n may be dummy substrates and the substrate 2811_3 to the substrate 2811_n−2 may be substrates to be treated. A dummy substrate is preferably used, in which case a plurality of substrates to be treated can be uniformly treated at the time of microwave treatment or heat treatment and a variation between the substrates to be treated can be reduced. For example, a dummy substrate is preferably placed over the substrate to be treated which is the closest to the high-frequency generator 2803 and the waveguide 2804, in which case the substrate to be treated is inhibited from being directly exposed to a microwave.
With the use of the above-described manufacturing apparatus, film quality modification or the like can be performed while the entry of impurities into an object is inhibited.
Examples of the semiconductor device of one embodiment of the present invention are described below with reference to
A of each drawing is a top view of the semiconductor device. Moreover, B of each drawing is a cross-sectional view corresponding to a portion indicated by dashed-dotted line A1-A2 in A of each drawing. Furthermore, C of each drawing is a cross-sectional view corresponding to a portion indicated by dashed-dotted line A3-A4 in A of each drawing. Furthermore, D of each drawing is a cross-sectional view corresponding to a portion indicated by dashed-dotted line A5-A6 in A of each drawing. Note that for clarity of the drawing, some components are omitted in the top view of A of each drawing.
Note that in the semiconductor device illustrated in A to D of each drawing, components having the same functions as the components included in the semiconductor device described in <Structure example of semiconductor device> are denoted by the same reference numerals. Note that the materials described in detail in <Structure example of semiconductor device> can also be used as component materials of the semiconductor devices in this section.
The semiconductor device illustrated in
For example, in the case where oxygen can be supplied sufficiently to the oxide 230 by the microwave treatment or the like as illustrated in
The semiconductor device illustrated in
The oxide 243 preferably has a function of inhibiting passage of oxygen. The oxide 243 having a function of inhibiting passage of oxygen is preferably placed between the oxide 230b and the conductor 242 functioning as the source electrode and the drain electrode, in which case the electric resistance between the conductor 242 and the oxide 230b can be reduced. Such a structure can improve the electrical characteristics, the field-effect mobility, and the reliability of the transistor 200 in some cases.
A metal oxide containing the element M may be used as the oxide 243. In particular, aluminum, gallium, yttrium, or tin is preferably used as the element M. The concentration of the element Min the oxide 243 is preferably higher than that in the oxide 230b. Furthermore, gallium oxide may be used for the oxide 243. A metal oxide such as an In-M-Zn oxide may be used as the oxide 243. Specifically, the atomic ratio of the element M to In in the metal oxide used as the oxide 243 is preferably greater than the atomic ratio of the element M to In in the metal oxide used as the oxide 230b. The thickness of the oxide 243 is preferably greater than or equal to 0.5 nm and less than or equal to 5 nm, further preferably greater than or equal to 1 nm and less than or equal to 3 nm, still further preferably greater than or equal to 1 nm and less than or equal to 2 nm. The oxide 243 preferably has crystallinity. In the case where the oxide 243 has crystallinity, release of oxygen from the oxide 230 can be favorably inhibited. When the oxide 243 has a hexagonal crystal structure, for example, release of oxygen from the oxide 230 can sometimes be inhibited.
A semiconductor device illustrated in
An example of the semiconductor device that is one embodiment of the present invention is described below with reference to
Note that in the semiconductor device illustrated in
The semiconductor device 500 illustrated in
The semiconductor device 500 includes a plurality of transistors 200 and a plurality of opening regions 400 arranged in a matrix. In addition, a plurality of conductors 260 functioning as gate electrodes of the transistors 200 are provided to extend in the y-axis direction. The opening regions 400 are provided in regions not overlapping with the oxide 230 or the conductor 260. The sealing portion 265 is formed so as to surround the plurality of transistors 200, the plurality of conductors 260, and the plurality of opening regions 400. Note that the number, the position, and the size of the transistors 200, the conductors 260, and the opening regions 400 are not limited to those illustrated in
As illustrated in
Such a structure enables the plurality of transistors 200 to be surrounded by the insulator 283, the insulator 214, and the insulator 212. One or more of the insulator 283, the insulator 214, and the insulator 212 preferably function as a barrier insulating film against hydrogen. Accordingly, entry of hydrogen contained in the region outside the sealing portion 265 into a region in the sealing portion 265 can be inhibited.
As illustrated in
As illustrated in
When heat treatment is performed in such a state that the opening region 400 is formed and the insulator 280 is exposed in the opening portion of the insulator 282, part of oxygen contained in the insulator 280 can be made to diffuse outwardly from the opening region 400 while oxygen is supplied to the oxide 230. This enables oxygen to be sufficiently supplied to the region functioning as the channel formation region and its vicinity in the oxide semiconductor from the insulator 280 containing oxygen to be released by heating, and also prevents an excess amount of oxygen from being supplied thereto.
At this time, hydrogen contained in the insulator 280 can be bonded to oxygen and released to the outside through the opening region 400. The hydrogen bonded to oxygen is released as water. Thus, the amount of hydrogen contained in the insulator 280 can be reduced, and hydrogen contained in the insulator 280 can be prevented from entering the oxide 230.
In
According to one embodiment of the present invention, a novel transistor can be provided. According to another embodiment of the present invention, a semiconductor device with a small variation in transistor characteristics can be provided. According to another embodiment of the present invention, a semiconductor device with favorable electrical characteristics can be provided. According to another embodiment of the present invention, a semiconductor device with favorable reliability can be provided. According to another embodiment of the present invention, a semiconductor device with high on-state current can be provided. According to another embodiment of the present invention, a semiconductor device with a high field-effect mobility can be provided. According to another embodiment of the present invention, a semiconductor device with favorable frequency characteristics can be provided. According to another embodiment of the present invention, a semiconductor device that can be miniaturized or highly integrated can be provided. According to another embodiment of the present invention, a semiconductor device with low power consumption can be provided.
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this embodiment, a manufacturing method of a capacitor of one embodiment of the present invention is described with reference to
As illustrated in
First, as illustrated in
Next, as illustrated in
After the deposition of the silicon oxynitride, microwave-excitation treatment is preferably performed in an atmosphere containing oxygen. Performing microwave-excitation treatment can effectively reduce the hydrogen concentration in the stacked film and the interface of the stacked film.
Next, as illustrated in
Next, as illustrated in
Heat treatment is preferably performed after the deposition of the insulator 150. The heat treatment is performed in a nitrogen atmosphere, the heat treatment temperature is higher than or equal to 300° C. and lower than or equal to 550° C., and the heat treatment time is longer than or equal to 2 hours and shorter than or equal to 16 hours.
Note that the heat treatment does not necessarily follow the deposition of the insulator 150. For example, some deposition steps and/or some processing steps may be performed after the deposition of the insulator 150, and then the heat treatment may be performed.
By performing the heat treatment, hydrogen in silicon oxynitride used for the insulator 130a or the insulator 130b is absorbed by aluminum oxide used for the insulator 130a or the insulator 130b. In other words, hydrogen in the silicon oxynitride used for the insulator 130a or the insulator 130b is diffused into the aluminum oxide used for the insulator 130a or the insulator 130b.
In the above manner, silicon oxynitride used for the insulator 130a or the insulator 130b with reduced hydrogen concentration can be formed. By the above manufacturing method, a capacitor with reduced leak current can be manufactured.
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this embodiment, one embodiment of a semiconductor device is described with reference to
The transistor 200 is a transistor in which a channel is formed in a semiconductor layer including an oxide semiconductor. Since the transistor 200 has low off-state current, a storage device that uses the transistor 200 can retain stored data for a long time. In other words, such a storage device does not require refresh operation or has extremely low frequency of the refresh operation, which leads to a sufficient reduction in power consumption of the storage device.
In the semiconductor device illustrated in
The storage device illustrated in
The transistor 300 is provided on a substrate 311 and includes a conductor 316 functioning as a gate, an insulator 315 functioning as a gate insulator, a semiconductor region 313 formed of part of the substrate 311, and a low-resistance region 314a and a low-resistance region 314b functioning as a source region and a drain region. The transistor 300 may be a p-channel transistor or an n-channel transistor.
Here, in the transistor 300 illustrated in
Note that the transistor 300 illustrated in
The capacitor 100 is provided above the transistor 200. The capacitor 100 includes a conductor 110 functioning as a first electrode, a conductor 120 functioning as a second electrode, and an insulator 130 functioning as a dielectric.
For example, a conductor 112 and the conductor 110 provided over the conductor 240 can be formed at the same time. Note that the conductor 112 has a function of a plug or a wiring that is electrically connected to the capacitor 100, the transistor 200, or the transistor 300. The conductor 112 corresponds to the conductor 246 described in the above embodiment, and the description of the conductor 246 can be referred to for the details of the conductor 112.
Although the conductor 112 and the conductor 110 having a single-layer structure are illustrated in
The insulator 130 can be provided as stacked layers or a single layer using, for example, silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, aluminum oxide, aluminum oxynitride, aluminum nitride oxide, aluminum nitride, hafnium oxide, hafnium oxynitride, hafnium nitride oxide, hafnium nitride, hafnium-zirconium oxide, or the like.
For example, for the insulator 130, a stacked-layer structure of a material with high dielectric strength such as silicon oxynitride and a high permittivity (high-k) material is preferably used. In the capacitor 100 having such a structure, a sufficient capacitance can be ensured owing to the high permittivity (high-k) insulator, and the dielectric strength can be increased owing to the insulator with high dielectric strength, so that the electrostatic breakdown of the capacitor 100 can be inhibited.
Examples of an insulator that is the high permittivity (high-k) material (a material having a high relative permittivity) include gallium oxide, hafnium oxide, zirconium oxide, an oxide containing aluminum and hafnium, an oxynitride containing aluminum and hafnium, an oxide containing silicon and hafnium, an oxynitride containing silicon and hafnium, and a nitride containing silicon and hafnium.
Examples of a material with high dielectric strength (a material having a low relative permittivity) include silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, porous silicon oxide, and a resin.
Wiring layers provided with an interlayer film, a wiring, a plug, and the like may be provided between the components. A plurality of wiring layers can be provided in accordance with design. Here, a plurality of conductors functioning as plugs or wirings are collectively denoted by the same reference numeral in some cases. Furthermore, in this specification and the like, a wiring and a plug electrically connected to the wiring may be a single component. That is, there are cases where part of a conductor functions as a wiring and part of a conductor functions as a plug.
For example, an insulator 320, an insulator 322, an insulator 324, and an insulator 326 are sequentially stacked over the transistor 300 as interlayer films. A conductor 328, a conductor 330, and the like that are electrically connected to the capacitor 100 or the transistor 200 are embedded in the insulator 320, the insulator 322, the insulator 324, and the insulator 326. Note that the conductor 328 and the conductor 330 function as a plug or a wiring.
The insulators functioning as interlayer films may also function as planarization films that cover uneven shapes therebelow. For example, a top surface of the insulator 322 may be planarized by planarization treatment using a chemical mechanical polishing (CMP) method or the like to improve planarity.
A wiring layer may be provided over the insulator 326 and the conductor 330. For example, in
Similarly, a conductor 218, a conductor (the conductor 205) included in the transistor 200, and the like are embedded in an insulator 210, the insulator 212, the insulator 214, and the insulator 216. Note that the conductor 218 has a function of a plug or a wiring that is electrically connected to the capacitor 100 or the transistor 300. In addition, an insulator 150 is provided over the conductor 120 and the insulator 130.
Here, like the insulator 241 described in the above embodiment, an insulator 217 is provided in contact with a side surface of the conductor 218 functioning as a plug. The insulator 217 is provided in contact with an inner wall of an opening formed in the insulator 210, the insulator 212, the insulator 214, and the insulator 216. That is, the insulator 217 is provided between the conductor 218 and each of the insulator 210, the insulator 212, the insulator 214, and the insulator 216. Note that the conductor 205 and the conductor 218 can be formed in parallel; thus, the insulator 217 is sometimes formed in contact with the side surface of the conductor 205.
As the insulator 217, an insulator such as silicon nitride, aluminum oxide, or silicon nitride oxide may be used, for example. Since the insulator 217 is provided in contact with the insulator 210, the insulator 212, the insulator 214, and the insulator 222, entry of impurities such as water and hydrogen into the oxide 230 through the conductor 218 from the insulator 210, the insulator 216, or the like can be inhibited. In particular, silicon nitride is suitable because of its high blocking property against hydrogen. Moreover, oxygen contained in the insulator 210 or the insulator 216 can be prevented from being absorbed by the conductor 218.
The insulator 217 can be formed in a manner similar to that of the insulator 241. For example, silicon nitride can be deposited by a PEALD method and an opening reaching the conductor 356 can be formed by anisotropic etching.
Examples of an insulator that can be used for an interlayer film include an insulating oxide, an insulating nitride, an insulating oxynitride, an insulating nitride oxide, an insulating metal oxide, an insulating metal oxynitride, and an insulating metal nitride oxide.
For example, when a material with a low relative permittivity is used for the insulator functioning as an interlayer film, parasitic capacitance generated between wirings can be reduced. Thus, a material is preferably selected depending on the function of an insulator.
For example, as the insulator 150, the insulator 210, the insulator 352, the insulator 354, and the like, an insulator with a low relative permittivity is preferably included. For example, the insulator preferably includes silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, porous silicon oxide, a resin, or the like. Alternatively, the insulator preferably has a stacked-layer structure of a resin and silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, or porous silicon oxide. When silicon oxide or silicon oxynitride, which is thermally stable, is combined with a resin, the stacked-layer structure can have thermal stability and a low relative permittivity. Examples of the resin include polyester, polyolefin, polyamide (e.g., nylon and aramid), polyimide, polycarbonate, and acrylic.
When a transistor using an oxide semiconductor is surrounded by an insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen, the electrical characteristics of the transistor can be stable. Thus, the insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen can be used for the insulator 214, the insulator 212, the insulator 350, and the like.
As the insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen, a single layer or stacked layers of an insulator containing, for example, boron, carbon, nitrogen, oxygen, fluorine, magnesium, aluminum, silicon, phosphorus, chlorine, argon, gallium, germanium, yttrium, zirconium, lanthanum, neodymium, hafnium, or tantalum may be used. Specifically, as the insulator having a function of inhibiting passage of oxygen and impurities such as hydrogen, a metal oxide such as aluminum oxide, magnesium oxide, gallium oxide, germanium oxide, yttrium oxide, zirconium oxide, lanthanum oxide, neodymium oxide, hafnium oxide, or tantalum oxide; silicon nitride oxide; silicon nitride; or the like can be used.
As the conductor that can be used for a wiring or a plug, a material containing one or more kinds of metal elements selected from aluminum, chromium, copper, silver, gold, platinum, tantalum, nickel, titanium, molybdenum, tungsten, hafnium, vanadium, niobium, manganese, magnesium, zirconium, beryllium, indium, ruthenium, and the like can be used. Alternatively, a semiconductor with high electrical conductivity, typified by polycrystalline silicon containing an impurity element such as phosphorus, or silicide such as nickel silicide may be used.
For example, for the conductor 328, the conductor 330, the conductor 356, the conductor 218, the conductor 112, and the like, a single layer or stacked layers of conductive material such as a metal material, an alloy material, a metal nitride material, or a metal oxide material that is formed using the above materials can be used. It is preferable to use a high-melting-point material that has both heat resistance and conductivity, such as tungsten or molybdenum, and it is preferable to use tungsten. Alternatively, it is preferable to use a low-resistance conductive material such as aluminum or copper. The use of a low-resistance conductive material can reduce wiring resistance.
<Wiring or Plug in Layer Provided with Oxide Semiconductor>
In the case where an oxide semiconductor is used in the transistor 200, an insulator including an excess-oxygen region is provided in the vicinity of the oxide semiconductor in some cases. In that case, an insulator having a barrier property is preferably provided between the insulator including the excess-oxygen region and a conductor provided in the insulator including the excess-oxygen region.
For example, in
That is, providing the insulator 241 can inhibit excess oxygen contained in the insulator 224 and the insulator 280 from being absorbed by the conductor 240. In addition, the insulator 241 can inhibit diffusion of hydrogen, which is an impurity, into the transistor 200 through the conductor 240.
The insulator 241 is preferably formed using an insulating material having a function of inhibiting diffusion of oxygen and impurities such as water and hydrogen. For example, silicon nitride, silicon nitride oxide, aluminum oxide, hafnium oxide, or the like is preferably used. In particular, silicon nitride is preferable because of its high blocking property against hydrogen. Other than that, a metal oxide such as magnesium oxide, gallium oxide, germanium oxide, yttrium oxide, zirconium oxide, lanthanum oxide, neodymium oxide, or tantalum oxide can be used, for example.
As described in the above embodiment, the transistor 200 may be sealed with the insulator 212, the insulator 214, the insulator 282, and the insulator 283. Such a structure can inhibit entry of hydrogen contained in the insulator 274, the insulator 150, or the like into the insulator 280 or the like.
Here, the conductor 240 penetrates the insulator 283 and the insulator 282, and the conductor 218 penetrates the insulator 214 and the insulator 212; however, as described above, the insulator 241 is provided in contact with the conductor 240, and the insulator 217 is provided in contact with the conductor 218. This can reduce the amount of hydrogen entering the inside of the insulator 212, the insulator 214, the insulator 282, and the insulator 283 through the conductor 240 and the conductor 218. In this manner, the transistor 200 is sealed with the insulator 212, the insulator 214, the insulator 282, the insulator 283, the insulator 241, and the insulator 217, so that impurities such as hydrogen contained in the insulator 274 or the like can be inhibited from entering from the outside.
A dicing line (sometimes referred to as a scribe line, a dividing line, or a cutting line) which is provided when a large-sized substrate is divided into semiconductor elements so that a plurality of semiconductor devices are each taken as a chip is described below. Examples of a dividing method include the case where a groove (a dicing line) for dividing the semiconductor elements is formed on the substrate, and then the substrate is cut along the dicing line to divide (split) it into a plurality of semiconductor devices.
Here, for example, as illustrated in
That is, in the opening provided in the insulator 282, the insulator 280, the insulator 275, the insulator 222, and the insulator 216, the insulator 214 is in contact with the insulator 283.
For example, an opening may be provided in the insulator 282, the insulator 280, the insulator 275, the insulator 222, the insulator 216, and the insulator 214. With such a structure, in the opening provided in the insulator 282, the insulator 280, the insulator 275, the insulator 222, the insulator 216, and the insulator 214, the insulator 212 is in contact with the insulator 283. Here, the insulator 212 and the insulator 283 may be formed using the same material and the same method. When the insulator 212 and the insulator 283 are formed using the same material and the same method, the adhesion therebetween can be increased. For example, silicon nitride is preferably used.
With the structure, the transistors 200 can be surrounded by the insulator 212, the insulator 214, the insulator 282, and the insulator 283. Since at least one of the insulator 212, the insulator 214, the insulator 282, and the insulator 283 has a function of inhibiting diffusion of oxygen, hydrogen, and water, even when the substrate is divided into circuit regions each of which is provided with the semiconductor elements described in this embodiment to be processed into a plurality of chips, entry and diffusion of impurities such as hydrogen and water from the direction of the side surface of the divided substrate into the transistor 200 can be prevented.
With the structure, excess oxygen in the insulator 280 and the insulator 224 can be prevented from diffusing to the outside. Accordingly, excess oxygen in the insulator 280 and the insulator 224 is efficiently supplied to the oxide where the channel is formed in the transistor 200. The oxygen can reduce oxygen vacancies in the oxide where the channel is formed in the transistor 200. Thus, the oxide where the channel is formed in the transistor 200 can be an oxide semiconductor with a low density of defect states and stable characteristics. That is, the transistor 200 can have a small variation in the electrical characteristics and higher reliability.
Note that although the capacitor 100 of the storage device illustrated in
The capacitor 100 illustrated in
The conductor 115 functions as a lower electrode of the capacitor 100, the conductor 125 functions as an upper electrode of the capacitor 100, and the insulator 145 functions as a dielectric of the capacitor 100. The capacitor 100 has a structure in which the upper electrode and the lower electrode face each other with the dielectric sandwiched therebetween on a side surface as well as a bottom surface of the opening in the insulator 150 and the insulator 142; thus, the capacitance per unit area can be increased. Thus, the deeper the opening is, the larger the capacitance of the capacitor 100 can be. Increasing the capacitance per unit area of the capacitor 100 in this manner can promote miniaturization or higher integration of the semiconductor device.
An insulator that can be used as the insulator 280 can be used as the insulator 152. The insulator 142 preferably functions as an etching stopper at the time of forming the opening in the insulator 150 and can be formed using an insulator that can be used as the insulator 214.
The shape of the opening formed in the insulator 150 and the insulator 142 when seen from above may be a quadrangular shape, a polygonal shape other than a quadrangular shape, a polygonal shape with rounded corners, or a circular shape including an elliptical shape. Here, the area where the opening and the transistor 200 overlap each other is preferably large in the top view. Such a structure can reduce the area occupied by the semiconductor device including the capacitor 100 and the transistor 200.
The conductor 115 is placed in contact with the opening formed in the insulator 142 and the insulator 150. A top surface of the conductor 115 is preferably substantially level with a top surface of the insulator 142. Furthermore, a bottom surface of the conductor 115 is in contact with the conductor 110 through an opening in the insulator 130. The conductor 115 is preferably deposited by an ALD method, a CVD method, or the like; for example, a conductor that can be used for the conductor 205 is used.
The insulator 145 is placed to cover the conductor 115 and the insulator 142. The insulator 145 is preferably deposited by an ALD method or a CVD method, for example. The insulator 145 can be provided to have stacked layers or a single layer using, for example, silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, zirconium oxide, aluminum oxide, aluminum oxynitride, aluminum nitride oxide, aluminum nitride, hafnium oxide, hafnium oxynitride, hafnium nitride oxide, or hafnium nitride. As the insulator 145, an insulating film in which zirconium oxide, aluminum oxide, and zirconium oxide are stacked in this order can be used, for example.
For the insulator 145, a material with high dielectric strength, such as silicon oxynitride, or a high permittivity (high-k) material is preferably used. Alternatively, a stacked-layer structure of a material with high dielectric strength and a high permittivity (high-k) material may be used.
Examples of an insulator that is the high permittivity (high-k) material (a material having a high relative permittivity) include gallium oxide, hafnium oxide, zirconium oxide, an oxide containing aluminum and hafnium, an oxynitride containing aluminum and hafnium, an oxide containing silicon and hafnium, an oxynitride containing silicon and hafnium, and a nitride containing silicon and hafnium. The use of such a high-k material can ensure sufficient capacitance of the capacitor 100 even when the insulator 145 has a large thickness. When the insulator 145 has a large thickness, generation of leak current between the conductor 115 and the conductor 125 can be inhibited.
Examples of the material with high dielectric strength include silicon oxide, silicon oxynitride, silicon nitride oxide, silicon nitride, silicon oxide to which fluorine is added, silicon oxide to which carbon is added, silicon oxide to which carbon and nitrogen are added, porous silicon oxide, and a resin. For example, it is possible to use an insulating film in which silicon nitride (SiNx) deposited by a PEALD method, silicon oxide (SiOx) deposited by a PEALD method, and silicon nitride (SiNx) deposited by a PEALD method are stacked in this order. Alternatively, an insulating film in which zirconium oxide, silicon oxide deposited by an ALD method, and zirconium oxide are stacked in this order can be used. The use of such an insulator with high dielectric strength can increase the dielectric strength and inhibit electrostatic breakdown of the capacitor 100.
The conductor 125 is placed to fill the opening formed in the insulator 142 and the insulator 150. The conductor 125 is electrically connected to the wiring 1005 through a conductor 140 and a conductor 153. The conductor 125 is preferably deposited by an ALD method, a CVD method, or the like and may be formed using a conductor that can be used as the conductor 205, for example.
The conductor 153 is provided over an insulator 154 and is covered with an insulator 156. The conductor 153 can be formed using a conductor that can be used for the conductor 112, and the insulator 156 can be formed using an insulator that can be used for the insulator 152. Here, the conductor 153 is in contact with a top surface of the conductor 140 and functions as a terminal of the capacitor 100, the transistor 200, or the transistor 300.
The capacitor device 292 includes the conductor 242b; the insulator 271b provided over the conductor 242b; the insulator 275 provided in contact with a top surface of the insulator 271b, a side surface of the insulator 271b, and a side surface of the conductor 242b; and a conductor 294 over the insulator 275. In other words, the capacitor device 292 forms an MIM (Metal-Insulator-Metal) capacitor. Note that one of a pair of electrodes included in the capacitor device 292, i.e., the conductor 242b, can also serve as the source electrode of the transistor. The dielectric layer included in the capacitor device 292 can also serve as a protective layer provided in the transistor, i.e., the insulator 271 and the insulator 275. Thus, the manufacturing process of the capacitor device 292 can also serve as part of the manufacturing process of the transistor, improving the productivity of the semiconductor device. Furthermore, one of a pair of electrodes included in the capacitor device 292, that is, the conductor 242b, also serves as the source electrode of the transistor; therefore, the area in which the transistor and the capacitor device are placed can be reduced.
Note that the conductor 294 can be formed using, for example, a material that can be used for the conductor 242.
Examples of a semiconductor device of one embodiment of the present invention including the transistor 200 and the capacitor device 292, which are different from the ones described above in <Structure example of memory device>, are described below with reference to
An example of a semiconductor device 600 of one embodiment of the present invention including a transistor 200a, a transistor 200b, a capacitor device 292a, and a capacitor device 292b is described below with reference to
The semiconductor device 600 has a line-symmetric structure with respect to dashed-dotted line A3-A4 as illustrated in
The examples of the components of the semiconductor device illustrated in
In the above description, the transistor 200a, the transistor 200b, the capacitor device 292a, and the capacitor device 292b are given as examples of components of the semiconductor device; however, the semiconductor device described in this embodiment is not limited thereto. For example, as illustrated in
As illustrated in
When the transistor 200a, the transistor 200b, the capacitor device 292a, and the capacitor device 292b are formed to have the structures described in this embodiment as described above, the area of the cell can be reduced and the semiconductor device including a cell array can be miniaturized or highly integrated.
Furthermore, the cell array may have a stacked-layer structure instead of a single-layer structure.
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this embodiment, a storage device including a transistor in which an oxide is used as a semiconductor (hereinafter, sometimes referred to as an OS transistor) and a capacitor (hereinafter, sometimes referred to as an OS memory apparatus) of one embodiment of the present invention is described with reference to
The column circuit 1430 includes, for example, a column decoder, a precharge circuit, a sense amplifier, a write circuit, and the like. The precharge circuit has a function of precharging wirings. The sense amplifier has a function of amplifying a data signal read from a memory cell. Note that the wirings are connected to the memory cell included in the memory cell array 1470, and are described later in detail. The amplified data signal is output as a data signal RDATA to the outside of the storage device 1400 through the output circuit 1440. The row circuit 1420 includes, for example, a row decoder and a word line driver circuit, and can select a row to be accessed.
As power supply voltages from the outside, a low power supply voltage (VSS), a high power supply voltage (VDD) for the peripheral circuit 1411, and a high power supply voltage (VIL) for the memory cell array 1470 are supplied to the storage device 1400. Control signals (CE, WE, and RE), an address signal ADDR, and a data signal WDATA are also input to the storage device 1400 from the outside. The address signal ADDR is input to the row decoder and the column decoder, and the data signal WDATA is input to the write circuit.
The control logic circuit 1460 processes the control signals (CE, WE, and RE) input from the outside, and generates control signals for the row decoder and the column decoder. The control signal CE is a chip enable signal, the control signal WE is a write enable signal, and the control signal RE is a read enable signal. Signals processed by the control logic circuit 1460 are not limited thereto, and other control signals are input as necessary.
The memory cell array 1470 includes a plurality of memory cells MC arranged in a matrix and a plurality of wirings. Note that the number of wirings that connect the memory cell array 1470 to the row circuit 1420 depends on the structure of the memory cell MC, the number of memory cells MC in a column, and the like. The number of wirings that connect the memory cell array 1470 to the column circuit 1430 depends on the structure of the memory cell MC, the number of memory cells MC in a row, and the like.
Note that
A first terminal of the transistor M1 is connected to a first terminal of the capacitor CA. A second terminal of the transistor M1 is connected to a wiring BIL. The gate of the transistor M1 is connected to a wiring WOL. The back gate of the transistor M1 is connected to a wiring BGL. A second terminal of the capacitor CA is connected to a wiring LL.
The wiring BIL functions as a bit line, and the wiring WOL functions as a word line. The wiring LL functions as a wiring for applying a predetermined potential to the second terminal of the capacitor CA. In the time of data writing and data reading, the wiring LL may be at a ground potential or a low-level potential. The wiring BGL functions as a wiring for applying a potential to the back gate of the transistor M1. When a given potential is applied to the wiring BGL, the threshold voltage of the transistor M1 can be increased or decreased.
Here, the memory cell 1471 illustrated in
The circuit structure of the memory cell MC is not limited to that of the memory cell 1471, and the circuit structure can be changed. For example, as in a memory cell 1472 illustrated in
In the case where the semiconductor device described in any of the above embodiments is used in the memory cell 1471 and the like, the transistor 200 can be used as the transistor M1, and the capacitor 100 can be used as the capacitor CA. When an OS transistor is used as the transistor M1, the leak current of the transistor M1 can be extremely low. That is, with the use of the transistor M1, written data can be retained for a long time, and thus the frequency of the refresh operation for the memory cell can be decreased. Alternatively, refresh operation for the memory cell can be unnecessary. In addition, since the transistor M1 has extremely low leak current, multi-level data or analog data can be retained in the memory cell 1471, the memory cell 1472, and the memory cell 1473.
In the DOSRAM, when the sense amplifier is provided below the memory cell array 1470 so that they overlap each other as described above, the bit line can be shortened. This reduces bit line capacitance, which can reduce the storage capacitance of the memory cell.
A first terminal of the transistor M2 is connected to a first terminal of the capacitor CB. A second terminal of the transistor M2 is connected to a wiring WBL. The gate of the transistor M2 is connected to the wiring WOL. The back gate of the transistor M2 is connected to the wiring BGL. A second terminal of the capacitor CB is connected to a wiring CAL. A first terminal of the transistor M3 is connected to a wiring RBL. A second terminal of the transistor M3 is connected to a wiring SL. A gate of the transistor M3 is connected to the first terminal of the capacitor CB.
The wiring WBL functions as a write bit line, the wiring RBL functions as a read bit line, and the wiring WOL functions as a word line. The wiring CAL functions as a wiring for applying a predetermined potential to the second terminal of the capacitor CB. In the time of data writing and data reading, a high-level potential is preferably applied to the wiring CAL. In the time of data retaining, a low-level potential is preferably applied to the wiring CAL. The wiring BGL functions as a wiring for applying a potential to the back gate of the transistor M2. The threshold voltage of the transistor M2 can be increased or decreased by applying a given potential to the wiring BGL.
Here, the memory cell 1474 illustrated in
The circuit structure of the memory cell MC is not limited to that of the memory cell 1474, and the circuit structure can be changed as appropriate. For example, as in a memory cell 1475 illustrated in
In the case where the semiconductor device described in any of the above embodiments is used in the memory cell 1474 and the like, the transistor 200 can be used as the transistor M2, the transistor 300 can be used as the transistor M3, and the capacitor 100 can be used as the capacitor CB. When an OS transistor is used as the transistor M2, the leak current of the transistor M2 can be extremely low. Consequently, with the use of the transistor M2, written data can be retained for a long time, and thus the frequency of the refresh operation for the memory cell can be decreased. Alternatively, refresh operation for the memory cell can be unnecessary. In addition, since the transistor M2 has extremely low leak current, multi-level data or analog data can be retained in the memory cell 1474. The same applies to the memory cell 1475 to the memory cell 1477.
Note that the transistor M3 may be a transistor containing silicon in a channel formation region (hereinafter, sometimes referred to as a Si transistor). The Si transistor may be either an n-channel transistor or a p-channel transistor. A Si transistor has higher field-effect mobility than an OS transistor in some cases. Therefore, a Si transistor may be used as the transistor M3 functioning as a reading transistor. Furthermore, the transistor M2 can be stacked over the transistor M3 when a Si transistor is used as the transistor M3, in which case the area occupied by the memory cell can be reduced, leading to high integration of the storage device.
Alternatively, the transistor M3 may be an OS transistor. When an OS transistor is used as each of the transistor M2 and the transistor M3, the circuit of the memory cell array 1470 can be formed using only n-channel transistors.
The transistor M4 is an OS transistor with a back gate, and the back gate is electrically connected to the wiring BGL. Note that the back gate and a gate of the transistor M4 may be electrically connected to each other. Alternatively, the transistor M4 does not necessarily include the back gate.
Note that each of the transistor M5 and the transistor M6 may be an n-channel Si transistor or a p-channel Si transistor. Alternatively, the transistor M4 to the transistor M6 may be OS transistors. In that case, the circuit of the memory cell array 1470 can be formed using only n-channel transistors.
In the case where the semiconductor device described in any of the above embodiments is used in the memory cell 1478, the transistor 200 can be used as the transistor M4, the transistors 300 can be used as the transistor M5 and the transistor M6, and the capacitor 100 can be used as the capacitor CC. When an OS transistor is used as the transistor M4, the leak current of the transistor M4 can be extremely low.
Note that the structures of the peripheral circuit 1411, the memory cell array 1470, and the like described in this embodiment are not limited to the above. The arrangement and functions of these circuits and the wirings, circuit components, and the like connected to the circuits can be changed, removed, or added as needed. The storage device of one embodiment of the present invention operates fast and can retain data for a long time.
The structure, method, and the like described in this embodiment can be used in an appropriate combination with any of other structures, methods, and the like described in this embodiment or the other embodiments.
In this embodiment, an example of a chip 1200 on which the semiconductor device of the present invention is mounted is described with reference to
As shown in
A bump (not illustrated) is provided on the chip 1200, and as illustrated in
Storage devices such as a DRAM 1221 and a flash memory 1222 may be provided over the motherboard 1203. For example, the DOSRAM described in the above embodiment can be used as the DRAM 1221. In addition, for example, the NOSRAM described in the above embodiment can be used as the flash memory 1222.
The CPU 1211 preferably includes a plurality of CPU cores. In addition, the GPU 1212 preferably includes a plurality of GPU cores. Furthermore, the CPU 1211 and the GPU 1212 may each include a memory for temporarily storing data. Alternatively, a common memory for the CPU 1211 and the GPU 1212 may be provided in the chip 1200. The NOSRAM or the DOSRAM described above can be used as the memory. Moreover, the GPU 1212 is suitable for parallel computation of a number of data and thus can be used for image processing or product-sum operation. When an image processing circuit or a product-sum operation circuit using an oxide semiconductor of the present invention is provided in the GPU 1212, image processing or product-sum operation can be performed with low power consumption.
In addition, since the CPU 1211 and the GPU 1212 are provided on the same chip, a wiring between the CPU 1211 and the GPU 1212 can be shortened, and the data transfer from the CPU 1211 to the GPU 1212, the data transfer between memories included in the CPU 1211 and the GPU 1212, and the transfer of arithmetic operation results from the GPU 1212 to the CPU 1211 after the arithmetic operation in the GPU 1212 can be performed at high speed.
The analog arithmetic unit 1213 includes one or both of an A/D (analog/digital) converter circuit and a D/A (digital/analog) converter circuit. Furthermore, the product-sum operation circuit may be provided in the analog arithmetic unit 1213.
The memory controller 1214 includes a circuit functioning as a controller of the DRAM 1221 and a circuit functioning as an interface of the flash memory 1222.
The interface 1215 includes an interface circuit for an external connection device such as a display device, a speaker, a microphone, a camera, or a controller. Examples of the controller include a mouse, a keyboard, and a game controller. As such an interface, a USB (Universal Serial Bus), an HDMI (registered trademark) (High-Definition Multimedia Interface), or the like can be used.
The network circuit 1216 includes a network circuit such as a LAN (Local Area Network). The network circuit 1216 may further include a circuit for network security.
The circuits (systems) described above can be formed in the chip 1200 through the same manufacturing process. Therefore, even when the number of circuits needed for the chip 1200 increases, there is no need to increase the number of steps in the manufacturing process; thus, the chip 1200 can be manufactured at low cost.
The motherboard 1203 provided with the package board 1201 on which the chip 1200 including the GPU 1212 is mounted, the DRAMs 1221, and the flash memory 1222 can be referred to as a GPU module 1204.
The GPU module 1204 includes the chip 1200 using SoC technology, and thus can have a small size. In addition, the GPU module 1204 is excellent in image processing, and thus is suitably used in a portable electronic device such as a smartphone, a tablet terminal, a laptop PC, or a portable (mobile) game machine. Furthermore, the product-sum operation circuit using the GPU 1212 can perform a method such as a deep neural network (DNN), a convolutional neural network (CNN), a recurrent neural network (RNN), an autoencoder, a deep Boltzmann machine (DBM), or a deep belief network (DBN); hence, the chip 1200 can be used as an AI chip or the GPU module 1204 can be used as an AI system module.
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this embodiment, examples of electronic components and electronic devices in which the storage device or the like described in the above embodiment is incorporated are described.
First,
The storage device 720 includes a driver circuit layer 721 and a storage circuit layer 722.
The electronic component 730 using the storage device 720 as a high bandwidth memory (HBM) is illustrated as an example. An integrated circuit (a semiconductor device) such as a CPU, a GPU, or an FPGA can be used as the semiconductor device 735.
As the package board 732, a ceramic substrate, a plastic substrate, a glass epoxy substrate, or the like can be used. As the interposer 731, a silicon interposer, a resin interposer, or the like can be used.
The interposer 731 includes a plurality of wirings and has a function of electrically connecting a plurality of integrated circuits with different terminal pitches. The plurality of wirings have a single-layer structure or a layered structure. The interposer 731 has a function of electrically connecting an integrated circuit provided on the interposer 731 to an electrode provided on the package board 732. Accordingly, the interposer is sometimes referred to as a “redistribution substrate” or an “intermediate substrate”. A through electrode may be provided in the interposer 731 to be used for electrically connecting the integrated circuit and the package board 732. In the case of using a silicon interposer, a TSV (Through Silicon Via) can also be used as the through electrode.
A silicon interposer is preferably used as the interposer 731. The silicon interposer can be manufactured at lower cost than an integrated circuit because it is not necessary to provide an active element. Moreover, since wirings of the silicon interposer can be formed through a semiconductor process, the formation of minute wirings, which is difficult for a resin interposer, is easily achieved.
An HBM needs to be connected to many wirings to achieve a wide memory bandwidth. Therefore, wirings of an interposer on which an HBM is mounted are required to be formed minute and highly dense. For this reason, a silicon interposer is preferably used as the interposer on which an HBM is mounted.
In a SiP, an MCM, or the like using a silicon interposer, a decrease in reliability due to a difference in expansion coefficient between an integrated circuit and the interposer is less likely to occur. Furthermore, a surface of a silicon interposer has high planarity, and a poor connection between the silicon interposer and an integrated circuit provided on the silicon interposer is less likely to occur. It is particularly preferable to use a silicon interposer for a 2.5D package (2.5-dimensional mounting) in which a plurality of integrated circuits are arranged side by side on the interposer.
A heat sink (radiator plate) may be provided to overlap the electronic component 730. In the case of providing a heat sink, the heights of integrated circuits provided on the interposer 731 are preferably the same. In the electronic component 730 of this embodiment, the heights of the storage device 720 and the semiconductor device 735 are preferably the same, for example.
An electrode 733 may be provided on the bottom portion of the package board 732 to mount the electronic component 730 on another substrate.
The electronic component 730 can be mounted on another substrate by various mounting methods not limited to BGA and PGA. For example, a mounting method such as SPGA (Staggered Pin Grid Array), LGA (Land Grid Array), QFP (Quad Flat Package), QFJ (Quad Flat J-leaded package), or QFN (Quad Flat Non-leaded package) can be employed.
The structure, method, and the like described in this embodiment can be used in an appropriate combination with any of other structures, methods, and the like described in this embodiment or the other embodiments.
In this embodiment, application examples of the storage device using the semiconductor device described in the above embodiment are described. The semiconductor device described in the above embodiment can be applied to, for example, storage devices of a variety of electronic devices (e.g., information terminals, computers, smartphones, e-book readers, digital cameras (including video cameras), video recording/reproducing devices, and navigation systems). Here, the computers refer not only to tablet computers, notebook computers, and desktop computers, but also to large computers such as server systems. Alternatively, the semiconductor device described in the above embodiment is applied to a variety of removable storage devices such as memory cards (e.g., SD cards), USB memories, and SSDs (solid state drives).
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
The semiconductor device of one embodiment of the present invention can be used as a processor such as a CPU and a GPU or a chip.
The GPU or the chip of one embodiment of the present invention can be mounted on a variety of electronic devices. Examples of electronic devices include a digital camera, a digital video camera, a digital photo frame, an e-book reader, a mobile phone, a portable game machine, a portable information terminal, and an audio reproducing device in addition to electronic devices provided with a relatively large screen, such as a television device, a monitor for a desktop or notebook information terminal or the like, digital signage, and a large game machine like a pachinko machine. When the GPU or the chip of one embodiment of the present invention is provided in the electronic device, the electronic device can include artificial intelligence.
The electronic device of one embodiment of the present invention may include an antenna. When a signal is received by the antenna, the electronic device can display a video, data, or the like on a display portion. When the electronic device includes the antenna and a secondary battery, the antenna may be used for contactless power transmission.
The electronic device of one embodiment of the present invention may include a sensor (a sensor having a function of measuring force, displacement, position, speed, acceleration, angular velocity, rotational frequency, distance, light, liquid, magnetism, temperature, a chemical substance, sound, time, hardness, an electric field, current, voltage, power, radioactive rays, flow rate, humidity, a gradient, oscillation, odor, or infrared rays).
The electronic device of one embodiment of the present invention can have a variety of functions. For example, the electronic device can have a function of displaying a variety of data (a still image, a moving image, a text image, and the like) on the display portion, a touch panel function, a function of displaying a calendar, date, time, and the like, a function of executing a variety of software (programs), a wireless communication function, and a function of reading out a program or data stored in a recording medium.
When the chip of one embodiment of the present invention is applied to the information terminal 5100, the information terminal 5100 can execute an application utilizing artificial intelligence. Examples of the application utilizing artificial intelligence include an application for recognizing a conversation and displaying the content of the conversation on the display portion 5102; an application for recognizing letters, figures, and the like input to the touch panel of the display portion 5102 by a user and displaying them on the display portion 5102; and an application for performing biometric authentication using fingerprints, voice prints, or the like.
Like the information terminal 5100 described above, when the chip of one embodiment of the present invention is applied to the notebook information terminal 5200, the notebook information terminal 5200 can execute an application utilizing artificial intelligence. Examples of the application utilizing artificial intelligence include design-support software, text correction software, and software for automatic menu generation. Furthermore, with the use of the notebook information terminal 5200, novel artificial intelligence can be developed.
Note that although
Using the GPU or the chip of one embodiment of the present invention in a game machine such as the portable game machine 5300 and the stationary game machine 5400 achieves a low-power-consumption game machine. Moreover, heat generation from a circuit can be reduced owing to low power consumption; thus, the influence of heat generation on the circuit, a peripheral circuit, and a module can be reduced.
Furthermore, when the GPU or the chip of one embodiment of the present invention is applied to the portable game machine 5300, the portable game machine 5300 including artificial intelligence can be achieved.
In general, the progress of a game, the actions and words of game characters, and expressions of an event and the like occurring in the game are determined by the program in the game; however, the use of artificial intelligence in the portable game machine 5300 enables expressions not limited by the game program. For example, it becomes possible to change expressions such as questions posed by the player, the progress of the game, time, and actions and words of game characters.
In addition, when a game requiring a plurality of players is played on the portable game machine 5300, the artificial intelligence can create a virtual game player; thus, the game can be played alone with the game player created by the artificial intelligence as an opponent.
Although the portable game machine and the stationary game machine are illustrated as examples of game machines in
The GPU or the chip of one embodiment of the present invention can be applied to a large computer.
The supercomputer 5500 includes a rack 5501 and a plurality of rack-mount computers 5502. The plurality of computers 5502 are stored in the rack 5501. The computer 5502 includes a plurality of substrates 5504 on which the GPU or the chip shown in the above embodiment can be mounted.
The supercomputer 5500 is a large computer mainly used for scientific computation. In scientific computation, an enormous amount of arithmetic operation needs to be processed at a high speed; hence, power consumption is large and chips generate a large amount of heat. Using the GPU or the chip of one embodiment of the present invention in the supercomputer 5500 achieves a low-power-consumption supercomputer. Moreover, heat generation from a circuit can be reduced owing to low power consumption; thus, the influence of heat generation on the circuit, a peripheral circuit, and a module can be reduced.
Although a supercomputer is illustrated as an example of a large computer in
The GPU or the chip of one embodiment of the present invention can be applied to an automobile, which is a moving vehicle, and the periphery of a driver's seat in the automobile.
The display panel 5701 to the display panel 5703 can provide a variety of kinds of information by displaying a speedometer, a tachometer, mileage, a fuel gauge, a gear state, air-condition setting, and the like. In addition, the content, layout, or the like of the display on the display panels can be changed as appropriate to suit the user's preference, so that the design quality can be increased. The display panel 5701 to the display panel 5703 can also be used as lighting devices.
The display panel 5704 can compensate for view obstructed by the pillar (a blind spot) by showing an image taken by an imaging device (not illustrated) provided for the automobile. That is, displaying an image taken by the imaging device provided outside the automobile leads to compensation for the blind spot and an increase in safety. In addition, displaying an image to compensate for a portion that cannot be seen makes it possible for the driver to confirm the safety more naturally and comfortably. The display panel 5704 can also be used as a lighting device.
Since the GPU or the chip of one embodiment of the present invention can be applied to a component of artificial intelligence, the chip can be used for an automatic driving system of the automobile, for example. The chip can also be used for a system for navigation, risk prediction, or the like. A structure may be employed in which the display panel 5701 to the display panel 5704 display navigation information, risk prediction information, or the like.
Note that although an automobile is described above as an example of a moving vehicle, the moving vehicle is not limited to an automobile. Examples of the moving vehicle include a train, a monorail train, a ship, and a flying vehicle (a helicopter, an unmanned aircraft (a drone), an airplane, and a rocket), and these moving vehicles can each include a system utilizing artificial intelligence when the chip of one embodiment of the present invention is applied to each of these moving vehicles.
When the chip of one embodiment of the present invention is applied to the electric refrigerator-freezer 5800, the electric refrigerator-freezer 5800 including artificial intelligence can be achieved. Utilizing the artificial intelligence enables the electric refrigerator-freezer 5800 to have a function of automatically making a menu based on foods stored in the electric refrigerator-freezer 5800, expiration dates of the foods, or the like, a function of automatically adjusting temperature to be appropriate for the foods stored in the electric refrigerator-freezer 5800, and the like.
Although the electric refrigerator-freezer is described in this example as a household appliance, examples of other household appliances include a vacuum cleaner, a microwave oven, an electric oven, a rice cooker, a water heater, an IH cooker, a water server, a heating-cooling combination appliance such as an air conditioner, a washing machine, a drying machine, and an audio visual appliance.
The electronic devices, the functions of the electronic devices, the application examples of artificial intelligence, their effects, and the like described in this embodiment can be combined as appropriate with the description of another electronic device.
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this example, a transistor including an oxide semiconductor and a capacitor over the transistor were fabricated, and then the cross sections thereof were observed.
The transistor was fabricated by the manufacturing method described as an example in Embodiment 1.
A single crystal silicon wafer was used as a substrate. In addition, a silicon oxide was formed on the surface of the substrate by thermal oxidation treatment. Over the silicon oxide, a back gate electrode, a back gate insulator, a semiconductor layer, a source electrode and a drain electrode (S/D electrode), a top gate insulator, and a top gate electrode were formed in this order. An In—Ga—Zn oxide film (IGZO) was used for the semiconductor layer.
A protective layer was formed over the transistor, an opening reaching the source electrode or the drain electrode was formed in part of the protective layer, and a plug (also referred to as a via) was formed by embedding a conductor in the opening.
The capacitor was formed over the protective layer. A lower electrode, a dielectric layer, and an upper electrode were formed in this order as the capacitor. The lower electrode was formed over and in contact with the plug. Lastly, a second protective layer was formed to cover the capacitor.
The cross sections of the transistor and the capacitor which were fabricated in the above-described manner were observed with a scanning transmission electron microscope (STEM).
Furthermore, the electrical characteristics of the fabricated transistor were evaluated, and it was found that there was no influence due to the formation of the capacitor after the formation of the transistor, and favorable electrical characteristics were obtained.
At least part of the structure, method, and the like described in this example can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this example, metal-insulator-metal (MIM) capacitors with different structures were fabricated, and the leak current thereof was evaluated.
Here, three kinds of samples (Sample A1 to Sample A3) were fabricated. The capacitor of each sample has a stacked-layer structure in which a lower electrode, a dielectric layer, and an upper electrode are stacked in this order. In each of Sample A1 to Sample A3, a stacked film of a titanium nitride film and a tungsten film was used as each of the upper electrode and the lower electrode.
In Sample A1, an 8-nm-thick silicon oxynitride film was used as the dielectric layer. A relative permittivity εr of the dielectric layer in Sample A1 is 4.1.
In Sample A2, a stacked film in which an approximately 7-nm-thick silicon oxynitride film and an approximately 14-nm-thick aluminum oxide film were stacked was used as the dielectric layer. A relative permittivity εr of the dielectric layer in Sample A2 is 6.63.
In Sample A3, a stacked film in which an approximately 4-nm-thick zirconium oxide film, an approximately 0.5-nm-thick aluminum oxide film, and an approximately 4-nm-thick zirconium oxide film were stacked was used as a dielectric layer. A relative permittivity εr of the dielectric layer in Sample A3 is 24.9.
Sample A3 having the highest relative permittivity was found to have the highest leak current. In addition, it was confirmed that Sample A2 having a comparatively high relative permittivity had the lowest leak current.
Next, leak current of a capacitor similar to that of Sample A2 was evaluated by changing the thickness of a dielectric layer.
Here, three kinds of capacitors were fabricated; the thicknesses of the silicon oxynitride films used for the dielectric layers of each capacitors were 7 nm, 10 nm, and 14 nm.
At least part of the structure, method, and the like described in this example can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
In this example, a TEG (Test Element Group) sample for measuring off-state current and a TEG sample for measuring capacitor leak current each including the transistor 200 illustrated in
First, a structure of the TEG sample for measuring off-state current including the transistor 200 is described. As illustrated in
As the oxide 230a, 10-nm-thick In—Ga—Zn oxide deposited by a DC sputtering method was used. In the deposition of the oxide 230a, a target with In:Ga:Zn=1:3:4 [atomic ratio] was used.
As the oxide 230b, 15-nm-thick In—Ga—Zn oxide deposited by a DC sputtering method was used. In the deposition of the oxide 230b, a target with In:Ga:Zn=1:1:2 [atomic ratio] was used.
As the insulator 252, 1-nm-thick aluminum oxide deposited by an ALD method was used. As the insulator 250, 5-nm-thick silicon oxynitride deposited by a CVD method was used. The insulator 254 had a two-layer structure; as the first layer of the insulator 254, 1.5-nm-thick hafnium oxide deposited by an ALD method was used. As the second layer of the insulator 254, 1-nm-thick silicon nitride deposited by an ALD method was used. Both after the deposition of the insulator 250 and after the deposition of the first layer of the insulator 254, microwave treatment was performed. In the microwave treatment, an argon gas and an oxygen gas were used as treatment gases, the treatment temperature was 400° C., and the treatment time was 600 seconds.
Note that the sample includes the conductor 240 as well as the above components. After the fabrication, the sample was subjected to heat treatment in a nitrogen atmosphere at a temperature of 400° C. for 8 hours. In the above manner, the TEG sample for measuring off-state current including the transistor 200 was fabricated.
Next,
One of a source and a drain of the transistor M1 is electrically connected to the terminal A. In addition, the other of the source and the drain of the transistor M1 is electrically connected to the node ND. A gate of the transistor M1 is electrically connected to the terminal B. In addition, one of a source and a drain of the transistor M2 is electrically connected to the node ND. The other of the source and the drain of the transistor M2 is electrically connected to the terminal D. A gate of the transistor M2 is electrically connected to the terminal C. A bottom gate of the transistor M2 is electrically connected to the terminal E. The reading circuit RC is electrically connected to the node ND. The reading circuit RC can read the potential of the node ND constantly.
Next, a method of measuring the off-state current is described. First, a potential V11 which brings the transistor M1 into an on state is applied to the terminal B to bring the transistor M1 into an on state. Then, a potential V12 is applied to the terminal A until the potential of the node ND becomes V12. In this example, V12 was set to 1.2 V. Next, a potential V13 which brings the transistor M1 into an off state is applied to the terminal B to bring the transistor M1 into an off state. Note that the transistor M2 is in an off state by applying a potential −2 V, a potential −3 V, a potential 0 V to the terminal C, the terminal E, and the terminal D, respectively.
In this manner, the reading circuit RC reads a potential change of the node ND over the time elapsed after the transistor M1 is turned off, whereby the leak current, that is, the off-state current of the transistor M2 can be calculated. Specifically, the calculation is performed using Ioff=CND×ΔVND/t, where Ioff is the off-state current, CND is the capacitance of the node ND, ΔVND is the potential change of the node ND, and t is the elapsed time. The transistor M1 has a design value of a channel length of 500 nm and the channel width of 60 nm, and the channel width of the transistor M1 is 1/20000 of that of the transistor M2; thus, the off state current of the transistor M1 is negligible.
In a measurement environment at a temperature of 150° C., the potential change ΔVND of the node ND in an elapsed time of 1 hour was read; in a measurement environment at a temperature of 125° C., the potential change ΔVND of the node ND in an elapsed time of 1 hour was read; in a measurement environment at a temperature of 100° C., the potential change ΔVND of the node ND in an elapsed time of 2 hours was read; and in a measurement environment at a temperature of 85° C., the potential change ΔVND of the node ND in an elapsed time of 4 hours was read.
Next, a structure of the TEG sample for measuring capacitor leak current including the transistor 200 is described. The TEG sample for measuring capacitor leak current includes components of a capacitor in addition to the components of the TEG sample for measuring off-state current described in [Measurement of off-state current] above.
As the conductor 110a, 30-nm-thick tungsten deposited by a sputtering method was used. As the conductor 110b, 5-nm-thick titanium nitride deposited by a CVD method was used. Note that the conductor 110a and the conductor 110b each function as a lower electrode of the capacitor.
As the insulator 130a, 14-nm-thick aluminum oxide deposited by an ALD method was used. As the insulator 130b, 7-nm-thick silicon oxynitride deposited by a CVD method was used. Note that the insulator 130a and the insulator 130b each function as a dielectric of the capacitor.
As the conductor 120a, 10-nm-thick titanium nitride deposited by a CVD method was used. As the conductor 120b, 20-nm-thick tungsten deposited by a sputtering method was used. Note that the conductor 120a and the conductor 120b each function as an upper electrode of the capacitor.
As the insulator 150a, 5-nm-thick aluminum oxide deposited by an ALD method was used. As the insulator 150b, 35-nm-thick aluminum oxide deposited by a sputtering method was used. Note that the insulator 150a and the insulator 150b each function as a passivation film. After the formation of the capacitor, heat treatment was performed in a nitrogen atmosphere at a temperature of 400° C. for 8 hours. In the above manner, the TEG sample for measuring capacitor leak current was fabricated.
Next,
One of the source and the drain of the transistor M1 is electrically connected to the terminal A. The other of the source and the drain of the transistor M1 is electrically connected to the node ND. The gate of the transistor M1 is electrically connected to the terminal B. One electrode of the capacitor CS is electrically connected to the node ND. The other electrode of the capacitor CS is electrically connected to the terminal D. The reading circuit RC is electrically connected to the node ND. The reading circuit RC can read the potential of the node ND constantly.
Next, a method for measuring the capacitor leakage is described. First, a potential V11 which brings the transistor M1 into an on state is applied to the terminal B to bring the transistor M1 into an on state. Then, the potential V12 is applied to the terminal A until the potential of the node ND becomes V12. In this example, the V12 was set to 1.2 V. Next, the potential V13 which brings the transistor M1 into an off state is applied to the terminal B to bring the transistor M1 into an off state. The terminal D was supplied with 0 V.
In this manner, the reading circuit RC reads a potential change of the node ND over the time elapsed after the transistor M1 is turned off, whereby leak current of the capacitor CS can be calculated. Specifically, the calculation is performed using ICS=CCS×ΔVND/t, where ICS is the capacitor leak current, CCS is the capacitance of the capacitor CS, ΔVND is the potential change of the node ND, and t is the elapsed time. Note that the potential change of the node ND due to the off-state current of the transistor M1 is negligibly small.
In a measurement environment at a temperature of 150° C., the potential change ΔVND of the node ND in an elapsed time of 1 hour was read; in a measurement environment at a temperature of 125° C., the potential change ΔVND of the node ND in an elapsed time of 4 hours was read; and in a measurement environment at a temperature of 100° C., the potential change ΔVND of the node ND in an elapsed time of 8 hours was read.
At least part of the structure, method, and the like described in this example can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
Hereinafter, evaluation results of leak current of fabricated capacitors subjected to microwave-excitation treatment will be described.
Here, three kinds of samples (Sample B1 to Sample B3) were fabricated. In each of Sample B1 to Sample B3, a stacked film of a titanium nitride film and a tungsten film was used as each of an upper electrode and a lower electrode.
In Sample B1, a stacked film in which a 7-nm-thick silicon oxynitride film and an approximately 14-nm-thick aluminum oxide film are stacked was used as a dielectric layer. After the deposition of the silicon oxynitride film, surface treatment was performed on a surface of the film by microwave-excitation treatment.
In Sample B2, a stacked film in which an approximately 14-nm-thick aluminum oxide film and an approximately 7-nm-thick silicon oxynitride film were stacked was used as a dielectric layer. After the deposition of the silicon oxynitride film, surface treatment was performed on a surface of the film by microwave-excitation treatment.
Sample B3 is a sample that uses a stacked film similar to that of Sample B2 as a dielectric layer and was not subjected to another microwave-excitation treatment.
At least part of the structure, method, and the like described in this example can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
Hereinafter, evaluation results of hydrogen concentration in a fabricated stacked film subjected to microwave-excitation treatment will be described.
As the layer L1, a silicon oxide film formed by performing thermal oxidization on the substrate surface was used. As the layer L2, a titanium nitride film deposited by a CVD method was used. As the layer L3, a silicon oxynitride film deposited by a plasma CVD method was used. As the layer L4, an aluminum oxide film deposited by an ALD method was used.
Here, a sample subjected to microwave-excitation treatment after the deposition of the silicon oxynitride film was Sample C1, and a sample not subjected to microwave-excitation treatment was Sample C2.
Next, the hydrogen concentration of each sample was evaluated. The hydrogen concentration was measured by secondary ion mass spectrometry (SIMS).
As shown in
From the above, it was confirmed that microwave-excitation treatment can effectively reduce the hydrogen concentration in a stacked film and an interface in the stacked film. Furthermore, it was found that such reduction in hydrogen concentration is effective for reduction in the leak current.
At least part of the structure, method, and the like described in this embodiment can be implemented in appropriate combination with any of those in the other embodiments, the other examples, and the like described in this specification.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-143496 | Aug 2020 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2021/057428 | 8/12/2021 | WO |