Semiconductor device with capacitor and method of manufacturing thereof

Abstract

A semiconductor device having a capacitor and a method of manufacturing thereof are provided, securing a certain capacitance while allowing the size to be reduced. The semiconductor device includes a capacitor lower electrode having an upper surface and including a metal film, a dielectric film deposited on the upper surface of the capacitor lower electrode and having its thickness smaller than that of the capacitor lower electrode, and a capacitor upper electrode deposited on the dielectric film, having its width smaller than that of the capacitor lower electrode and including a metal film.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to semiconductor devices and methods of manufacturing thereof. In particular, the invention relates to a semiconductor device having a capacitor and a method of manufacturing the semiconductor device.

2. Description of the Background Art

An analog or analog•digital LSI (Large Scale Integration) such as analog/digital converter (A/D converter) and digital/analog converter (D/A converter) conventionally contains a capacitor (capacitive element) as a component of a filter circuit or an integrating circuit. FIG. 89 is a schematic cross section of a semiconductor device, conventional analog•digital LSI and the like for example, showing a capacitor portion where a capacitor is formed and an interconnection portion where an interconnection is formed. FIG. 90 is a schematic cross section along line XC—XC in FIG. 89. A conventional semiconductor device is described below in conjunction with FIGS. 89 and 90 .

Referring to FIGS. 89 and 90 , an insulating film 102 is formed on a semiconductor substrate 101 . A capacitor portion 120 includes one electrode 103 a formed of a metal film that is deposited on insulating film 102 . The other electrode 103 b is formed to surround one electrode 103 a with a space therebetween. An interlayer insulating film 108 is formed on one electrode 103 a and the other electrode 103 b . An interlayer insulating film part 108 a is provided as a capacitor dielectric film between one electrode 103 a and the other electrode 103 b . The one electrode 103 a , interlayer insulating film part 108 a and the other electrode 103 b constitute a capacitor.

A contact hole 110 a formed in interlayer insulating film 108 is located in a region on one electrode 103 a . A tungsten plug 111 a fills the inside of contact hole 110 a . An upper-level interconnection 112 a is formed on tungsten plug 111 a . Upper-level interconnection 112 a is electrically connected to one electrode 103 a via tungsten plug 111 a.

An interconnection portion 121 includes a first-level interconnection 103 c formed on insulating film 102 . The first-level interconnection 103 c is constituted of a layer of the same level as that of one electrode 103 a and the other electrode 103 b . Interlayer insulating film 108 is deposited on the first-level interconnection 103 c . A contact hole 110 b is formed in interlayer insulating film 108 in a region on the first-level interconnection 103 c . A tungsten plug 111 b fills the inside of contact hole 110 b . An upper-level interconnection 112 b is formed on tungsten plug 111 b . The upper-level interconnection 112 b is electrically connected to the first-level interconnection 103 c via tungsten plug 111 b.

The conventional semiconductor device as described above has a problem as discussed below. There is an increasing demand for scaling down and enhanced integration of semiconductor devices. The capacitor as shown in FIGS. 89 and 90 must secure a certain capacitance. In order to reduce the area occupied by the capacitor shown in FIGS. 89 and 90 while maintain a required capacitance, the thickness in the direction of height of one electrode 103 a and the other electrode 103 b can be increased to extend the surface area of sidewalls of one electrode 103 a and the other electrode 103 b serving as electrodes, or the distance between one electrode 103 a and the other electrode 103 b can be reduced.

However, when the thickness in the height direction of the one and the other electrodes 103 a and 103 b is increased, etching for fabricating the one and the other electrodes 103 a and 103 b is difficult. Therefore, this is not a realistic approach. On the other hand, when the distance between the one electrode 103 a and the other electrode 103 b is decreased, it would be difficult to reduce the distance smaller than the minimum process dimension of photolithography employed in a manufacturing process of the semiconductor device. Reduction of the area occupied by the capacitor is accordingly restricted.

It has been difficult for the conventional semiconductor device to secure a certain capacitance while reduce the area occupied by the capacitor as explained above.

SUMMARY OF THE INVENTION

One object of the present invention is to provide a semiconductor device having a capacitor enabling a certain capacitance to be secured and simultaneously allowing the size to be reduced, and to provide a method of manufacturing such a semiconductor device.

According to one aspect of the invention, a semiconductor device includes a capacitor lower electrode having an upper surface and including a metal film, a dielectric film deposited on the capacitor lower electrode and having its thickness smaller than that of the capacitor lower electrode, and a capacitor upper electrode deposited on the dielectric film, having its width smaller than that of the capacitor lower electrode and including a metal film.

The capacitor lower electrode, the dielectric film and the capacitor upper electrode are stacked in the vertical direction and accordingly a capacitor can be produced in the vertical direction. It is possible to control the thickness of the dielectric film such that the thickness is significantly smaller than the minimum process dimension of photolithography employed in fabrication of the semiconductor device. Then, with a certain capacitance secured, the thickness of the dielectric film can be made smaller than the conventional one to decrease the surface area of the capacitor upper and lower electrodes. As a result, the capacitor can be reduced in size compared with the conventional capacitor.

The width of the capacitor upper electrode is defined smaller than that of the capacitor lower electrode. It is then possible to obtain an increased alignment margin for photolithography by which the capacitor upper electrode is formed. Occurrence of defect can be avoided, such as short-circuit between the sidewall for example of the capacitor lower electrode and the capacitor upper electrode due to misalignment of the capacitor upper and lower electrodes.

As the capacitor upper and lower electrodes include metal films, a capacitor (capacitive element) can be implemented having a higher precision and less voltage-dependency, compared with a semiconductor device employing semiconductor like polysilicon as a capacitor electrode. A capacitor necessary for a high-precision filter circuit or the like can readily be achieved in this way.

For the semiconductor device according to the one aspect, the capacitor upper electrode may have a sidewall, and the semiconductor device may include a sidewall insulating film formed on the upper surface of the capacitor lower electrode and on the sidewall of the capacitor upper electrode.

The sidewall insulating film provided between the sidewall of the capacitor upper electrode and the upper surface of the capacitor lower electrode can surely prevent short-circuit between the capacitor upper electrode and the capacitor lower electrode.

Further, as discussed later regarding a manufacturing process, the capacitor upper electrode and the sidewall insulating film can be utilized as a mask in etching for fabricating the capacitor lower electrode. Accordingly, the capacitor lower electrode located under the capacitor upper electrode and having its width greater than that of the capacitor upper electrode can surely be formed.

For the semiconductor device according to the one aspect, the sidewall insulating film preferably includes a silicon oxynitride film.

The silicon oxynitride film functions as an ARC (Anti Reflection Coat). A separate ARC is thus made unnecessary by forming the silicon oxynitride film constituting the sidewall insulating film from a region on the capacitor upper electrode to another region and forming on this silicon oxynitride film a photoresist film employed in etching for forming an interconnection or the like on that another region. The manufacturing process can thus be simplified.

For the semiconductor device according to the one aspect, the capacitor lower electrode may include aluminum and the capacitor upper electrode may include tungsten.

When the capacitor lower electrode and the capacitor upper electrode are formed of respective materials different from each other, the capacitor upper electrode can surely be used as a mask in etching for producing the capacitor lower electrode. Misalignment between the capacitor upper and lower electrodes can thus be prevented.

The semiconductor device according to the one aspect may further include a lower interconnection portion constituted of a layer at the same level as that of the capacitor lower electrode, another dielectric film deposited on the lower interconnection portion, an upper interconnection portion deposited on that another dielectric film, having its width smaller than that of the lower interconnection portion and constituted of a layer at the same level as that of the capacitor upper electrode, and an interlayer insulating film formed on the upper interconnection portion. In the interlayer insulating film, a connection hole may be formed that exposes a surface of the upper interconnection portion and reaches the upper surface of the lower interconnection portion. The semiconductor device according to the one aspect may further include a conductive film provided inside the connection hole to electrically connect the upper and lower interconnection portions.

In the process of fabricating the capacitor formed of the capacitor lower electrode, the dielectric film and the capacitor upper electrode, an interconnection can simultaneously be fabricated that is formed of the upper and lower interconnection portions. The upper and lower interconnection portions can serve as one interconnection if the conductive film is used to electrically connect these interconnection portions.

According to another aspect of the invention, a semiconductor device includes a capacitor lower electrode having an upper surface and a sidewall surface and including a metal film, a dielectric film deposited on the capacitor lower electrode to extend from the upper surface to the sidewall surface and having its thickness smaller than that of the capacitor lower electrode, and a capacitor upper electrode deposited on the dielectric film and including a metal film.

The capacitor lower electrode, the dielectric film and the capacitor upper electrode are stacked in the vertical direction and accordingly a capacitor can be produced in the vertical direction. It is possible to control the thickness of the dielectric film such that the thickness is significantly smaller than the minimum process dimension of photolithography employed in fabrication of the semiconductor device. Then, even if the thickness of the dielectric film is made smaller than a conventional one in order to reduce the surface area of the capacitor upper and lower electrodes, a certain capacitance can be secured. The capacitor can thus be reduced in size compared with the conventional capacitor.

The dielectric film is deposited on the capacitor lower electrode to extend from the upper surface to the sidewall surface of the lower electrode. Therefore, even if the position of the capacitor upper electrode shifts and accordingly the capacitor upper electrode extends onto the sidewall surface of the capacitor lower electrode, the dielectric film is present between the capacitor upper and lower electrodes. Prevention is surely possible of short-circuit between the capacitor upper and lower electrodes in this way.

As the capacitor upper and lower electrodes include metal films, a capacitor (capacitive element) can be implemented having a higher precision and less voltage-dependency, compared with a semiconductor device employing semiconductor like polysilicon as a capacitor electrode. A capacitor necessary for a high-precision filter circuit or the like can readily be achieved in this way.

For the semiconductor device according to that another aspect, the capacitor upper electrode may have its width smaller than that of the capacitor lower electrode.

It is then possible to obtain an increased alignment margin for photolithography by which the capacitor upper electrode is formed. Occurrence of defect can be avoided, such as short-circuit between the sidewall for example of the capacitor lower electrode and the capacitor upper electrode due to misalignment of the capacitor upper and lower electrodes.

For the semiconductor device according to that another aspect, the capacitor upper electrode may have its width greater than that of the capacitor lower electrode.

In this case, the capacitor upper electrode is located on the sidewall of the capacitor lower electrode with the dielectric film therebetween. Consequently, the sidewall of the capacitor lower electrode can be utilized as a capacitor electrode, which can increase the capacitance of the capacitor.

According to still another aspect of the invention, a semiconductor device includes an interlayer insulating film having a trench, a capacitor lower electrode filling the inside of the trench and including a metal film, a dielectric film deposited on the capacitor lower electrode and having its thickness smaller than that of the interlayer insulating film, and a capacitor upper electrode deposited on the dielectric film and including a metal film.

The capacitor lower electrode, the dielectric film and the capacitor upper electrode are stacked in the vertical direction and accordingly a capacitor can be produced in the vertical direction. It is possible to control the thickness of the dielectric film such that the thickness is significantly smaller than the minimum process dimension of photolithography employed in fabrication of the semiconductor device. Then, with a certain capacitance secured, the thickness of the dielectric film can be made smaller than the conventional one to decrease the surface area of the capacitor upper and lower electrodes. As a result, the capacitor can be reduced in size compared with the conventional capacitor.

The capacitor lower electrode has a so-called damascene structure that fills the inside of the trench of the interlayer insulating film. When a semiconductor device employs a damascene interconnection as one interconnection, this interconnection can partially be used as a capacitor lower electrode. Then, a capacitor of vertical type can readily be implemented in the semiconductor device having such a damascene interconnection.

As the capacitor upper and lower electrodes include metal films, a capacitor (capacitive element) can be implemented having a higher precision and less voltage-dependency, compared with a semiconductor device employing semiconductor like polysilicon as a capacitor electrode. A capacitor necessary for a high-precision filter circuit or the like can readily be achieved in this way.

According to a further aspect of the invention, a semiconductor device includes one capacitor electrode including a first extension and a second extension horizontally spaced apart from the first extension, and the other capacitor electrode including a third extension located between the first extension and the second extension, opposed to the first extension with a dielectric film therebetween and opposed to the second extension with a dielectric film therebetween and including a fourth extension opposed to the second extension with a dielectric film therebetween that is different from the dielectric film between the second and third extensions, the third and fourth extensions located on different sides of the second extension.

When the first and second extensions and the third and fourth extensions are alternately arranged in this way, the one and the other capacitor electrodes accordingly have the first to fourth extensions with their sidewall surfaces opposing each other that can be utilized as an electrode surface of the capacitor. Specifically, almost all the sidewall surfaces of the second and third extensions can be used as a capacitor electrode surface. In the case of the conventional capacitor shown in FIGS. 89 and 90 , the other electrode is arranged to surround the one electrode so that the outer sidewall surface that is not opposite to the one electrode does not function as a capacitor electrode surface. On the other hand, the capacitor of the present invention has the first extension of the one electrode formed so as to enable the outer sidewall surface of the other electrode (the sidewall surface of the third extension opposing the first extension) to be utilized as a capacitor electrode. The volume of a region occupied by the capacitor is then smaller than occupied by a plurality of such conventional capacitors one of which as shown in FIGS. 89 and 90 provided for securing a certain capacitance. Further, the capacitance of the capacitor can readily be changed since the area of the capacitor electrode surface can easily be varied.

According to a still further aspect of the invention, a semiconductor device includes an interlayer insulating film having a plurality of holes, a plurality of capacitor lower electrodes provided inside the holes of the interlayer insulating film and including a metal film, a dielectric film deposited on the capacitor lower electrodes, and a capacitor upper electrode deposited on the dielectric film and including a metal film.

The capacitor lower electrode, the dielectric film and the capacitor upper electrode are stacked in the vertical direction and accordingly a capacitor can be produced in the vertical direction. It is possible to control the thickness of the dielectric film such that the thickness is significantly smaller than the minimum process dimension of photolithography employed in fabrication of the semiconductor device. Then, with a certain capacitance secured, the thickness of the dielectric film can be made smaller than the conventional one to decrease the surface area of the capacitor upper and lower electrodes. As a result, the capacitor can be reduced in size compared with the conventional capacitor.

The number as well as the cross sectional area of the holes formed in the interlayer insulating film can be changed to facilitate change of the area of the region of the capacitor lower electrodes that is opposite to the dielectric film. As a result, the capacitance of the capacitor can easily be changed.

As the capacitor upper and lower electrodes include metal films, a capacitor (capacitive element) can be implemented having a higher precision and less voltage-dependency, compared with a semiconductor device employing semiconductor like polysilicon as a capacitor electrode. A capacitor necessary for a high-precision filter circuit or the like can readily be achieved in this way.

According to a still further aspect of the invention, a semiconductor device includes a capacitor lower electrode including a metal film, a dielectric film deposited on the capacitor lower electrode and having its thickness smaller than that of the capacitor lower electrode, an interlayer insulating film deposited on the dielectric film and having an opening that exposes the dielectric film, and a capacitor upper electrode provided inside the opening and including a metal film.

The capacitor lower electrode, the dielectric film and the capacitor upper electrode are stacked in the vertical direction and accordingly a capacitor can be produced in the vertical direction. It is possible to control the thickness of the dielectric film such that the thickness is significantly smaller than the minimum process dimension of photolithography employed in fabrication of the semiconductor device. Then, with a certain capacitance secured, the thickness of the dielectric film can be made smaller than the conventional one to decrease the surface area of the capacitor upper and lower electrodes. As a result, the capacitor can be reduced in size compared with the conventional capacitor.

Further, as the capacitor upper electrode is placed inside the opening, the conventionally required process of forming a contact hole for connecting the capacitor upper electrode and an upper-level interconnection after formation of the capacitor upper electrode is unnecessary. The manufacturing process of a semiconductor device can thus be simplified.

As the capacitor upper and lower electrodes include metal films, a capacitor (capacitive element) can be implemented having a higher precision and less voltage-dependency, compared with a semiconductor device employing semiconductor like polysilicon as a capacitor electrode. A capacitor necessary for a high-precision filter circuit or the like can readily be achieved in this way.

For the semiconductor device according to the one aspect, another aspect, still another aspect, further aspect or still further aspects of the invention, the capacitor formed of the capacitor upper electrode, the dielectric film and the capacitor lower electrode is preferably employed in an application specific integrated circuit.

The application specific integrated circuit (ASIC) requires a capacitor to be implemented that has a high precision and no voltage-dependency and can easily be reduced in size. The present invention would be remarkably advantageous, if applied to the ASIC, in enhancement of the performance and scaling down of the ASIC.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of forming a capacitor lower electrode having an upper surface, forming a dielectric film on the upper surface of the capacitor lower electrode, the dielectric film having its thickness smaller than that of the capacitor lower electrode, forming a metal film on the dielectric film, forming a resist film on the metal film, the resist film having its width smaller than that of the capacitor lower electrode, and forming a capacitor upper electrode by partially removing the metal film by means of etching using the resist film as a mask, the capacitor upper electrode having its width smaller than that of the capacitor lower electrode.

In this way, a capacitor in the vertical direction can readily be produced that is constituted of the capacitor lower electrode, the dielectric film and the capacitor upper electrode stacked in the vertical direction.

The resist film used for forming the capacitor upper electrode has its width defined smaller than that of the capacitor lower electrode. Then, an increased alignment margin between the resist film and the capacitor lower electrode can be obtained in a photolithography process for forming the resist film. Accordingly, it is possible to prevent occurrence of defect, such as short-circuit between the sidewall surface for example and the capacitor upper electrode due to misalignment of the capacitor upper and lower electrodes.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of forming a capacitor lower electrode having an upper surface and a sidewall surface, forming a dielectric film deposited on the capacitor lower electrode and extending from the upper surface to the sidewall surface, the dielectric film having its thickness smaller than that of the capacitor lower electrode, forming a metal film on the dielectric film, forming a resist film on the metal film, and forming a capacitor upper electrode by partially removing the metal film by means of etching using the resist film as a mask.

In this way, a capacitor in the vertical direction can readily be produced that is constituted of the capacitor lower electrode, the dielectric film and the capacitor upper electrode stacked in the vertical direction.

The dielectric film extends from the upper surface to the sidewall surface of the capacitor lower electrode. Therefore, when the position of the resist film for forming the capacitor upper electrode shifts and accordingly the capacitor upper electrode extends onto the sidewall surface of the capacitor lower electrode, the dielectric film is present between the capacitor upper electrode and the sidewall of the capacitor lower electrode. It is thus possible to surely prevent short-circuit between the upper and lower electrodes.

Regarding the method of manufacturing a semiconductor device according to the still further aspect of the invention, the step of forming a resist film may include the step of forming a resist film having its width smaller than that of the capacitor lower electrode.

An increased alignment margin is thus secured between the resist film and the capacitor lower electrode in a photolithography process for forming the resist film.

Regarding the method of manufacturing a semiconductor device according to the still further aspect of the invention, the step of forming a resist film may include the step of forming a resist film having its width greater than that of the capacitor lower electrode.

Accordingly, the capacitor upper electrode deposited on the capacitor lower electrode extends from the upper surface to the sidewall surface of the capacitor lower electrode with the dielectric film therebetween. The sidewall surface of the capacitor lower electrode can thus be utilized as a capacitor electrode. An increased capacitance of the capacitor can be achieved in this way.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of forming a lower metal film constituting a capacitor lower electrode, forming a dielectric film on the lower metal film, forming a capacitor upper electrode deposited on the dielectric film and including a metal film, and forming the capacitor lower electrode by partially removing the lower metal film through etching using the capacitor upper electrode as a mask.

In this way, a capacitor in the vertical direction can readily be produced that is constituted of the capacitor lower electrode, the dielectric film and the capacitor upper electrode stacked in the vertical direction.

As the capacitor lower electrode is formed by using the capacitor upper electrode as a mask, misalignment of the capacitor upper and lower electrodes can surely be avoided.

Regarding the method of manufacturing a semiconductor device according to the still further aspect of the invention, in the step of forming the dielectric film, the dielectric film may be formed to extend to a region where an interconnection is formed by using the lower metal film. Further, the method of manufacturing a semiconductor device according to the still further aspect of the invention may further include the step, preceding the step of forming the capacitor lower electrode, of forming a resist film on the dielectric film on the region where an interconnection is formed by using the lower metal film, and forming the interconnection by partially removing the lower metal film by using the resist film as a mask.

In this case, when a material functioning as an ARC (anti reflection coat) is employed as the dielectric film, the step of separately forming an ARC for the resist film formed on the dielectric film is unnecessary. A simpler manufacturing process of the semiconductor device can thus be accomplished.

Regarding the method of manufacturing a semiconductor device according to the still further aspect of the invention, preferably the dielectric film includes a silicon oxynitride film.

The silicon oxynitride film functions as an ARC. Then, the silicon oxynitride film can be used as the capacitor dielectric film to allow the capacitor dielectric film to function as an ARC in an easy manner.

The method of manufacturing a semiconductor device according to the still further aspect of the invention may further include the step, preceding the step of forming the capacitor lower electrode, forming a sidewall film on a sidewall surface of the capacitor upper electrode, and, in the step of forming the capacitor lower electrode, the capacitor upper electrode and the sidewall film may be used as a mask.

The capacitor upper electrode and the sidewall film are utilized as a mask in etching for fabricating the capacitor lower electrode. Then, the capacitor lower electrode located under the capacitor upper electrode and having its width greater than the capacitor upper electrode can surely be produced.

The method of manufacturing a semiconductor device according to the still further aspect of the invention may further include the step, preceding the step of forming the capacitor lower electrode, forming an upper interconnection portion deposited on the dielectric film, having a sidewall surface and constituting an interconnection layer, and may further include the steps of forming an interconnection sidewall film on the sidewall surface of the upper interconnection portion, forming a lower interconnection portion by partially removing the lower metal film through etching using the interconnection sidewall film and the upper interconnection portion as a mask, forming an interlayer insulating film on the upper interconnection portion, forming a connection hole in the interlayer insulating film, the connection hole exposing a surface of the upper interconnection portion and reaching an upper surface of the lower interconnection portion, and forming a conductive film in the connection hole that is electrically connected to the upper and lower interconnection portions.

In the step of fabricating a capacitor formed of the capacitor lower electrode, the dielectric film and the capacitor upper electrode, an interconnection constituted of the upper and lower interconnection portions can simultaneously be produced.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of preparing an interlayer insulating film, forming a trench in the interlayer insulating film, forming a capacitor lower electrode filling the trench and including a metal film, forming a dielectric film deposited on the capacitor lower electrode and having its thickness smaller than that of the interlayer insulating film, and forming a capacitor upper electrode deposited on the dielectric film and including a metal film.

In this way, a capacitor in the vertical direction can be produced that is constituted of the capacitor lower electrode, the dielectric film and the capacitor upper electrode stacked in the vertical direction.

The capacitor lower electrode has a so-called damascene structure that fills the inside of the trench of the interlayer insulating film. When a semiconductor device employs a damascene interconnection as one interconnection, a part of this interconnection can easily be used as a capacitor lower electrode.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of forming a metal film, forming a resist film on the metal film, and forming, by partially removing the metal film using the resist film as a mask, one capacitor electrode including a first extension and a second extension horizontally spaced apart from the first extension and the other capacitor electrode including a third extension located between the first extension and the second extension, opposed to the first extension with a dielectric film therebetween and opposed to the second extension with a dielectric film therebetween and including a fourth extension opposed to the second extension with a dielectric film therebetween that is different from the dielectric film between the second and third extensions, the third and fourth extensions located on different sides of the second extension.

In this way, a capacitor can readily be produced including the one and the other capacitor electrodes with the first to fourth extensions having sidewall surfaces opposing each other that can be utilized as a capacitor electrode surface.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of preparing an interlayer insulating film, forming a plurality of holes in the interlayer insulating film, forming a metal film extending from the inside of the holes onto an upper surface of the interlayer insulating film, forming a plurality of capacitor lower electrodes provided in the holes and including a metal film by removing a part of the metal film located on the upper surface of the interlayer insulating film and forming a depression in the upper surface of the interlayer insulating film in a region where the holes are provided, filling the depression with a dielectric film, and forming a capacitor upper electrode including a metal film on the dielectric film.

In this way, a capacitor in the vertical direction can readily be produced that is constituted of the capacitor lower electrode, the dielectric film and the capacitor upper electrode stacked in the vertical direction.

In the step of forming a plurality of holes in the interlayer insulating film, the number and the cross sectional area of the holes can be changed to easily change the area of a region of the capacitor lower electrode, that is opposite to the dielectric film. The capacitance of the capacitor can thus be changed by an easy way.

According to a still further aspect of the invention, a method of manufacturing a semiconductor device includes the steps of forming a capacitor lower electrode including a metal film, forming a dielectric film deposited on the capacitor lower electrode and having its thickness smaller than that of the capacitor lower electrode, forming an interlayer insulating film on the dielectric film, forming an opening in the interlayer insulating film in a region located on the dielectric film so as to expose the dielectric film, and forming a capacitor upper electrode provided in the opening and including a metal film.

In this way, a capacitor in the vertical direction can readily be produced that is constituted of the capacitor lower electrode, the dielectric film and the capacitor upper electrode stacked in the vertical direction.

The capacitor upper electrode is provided in the opening. Therefore, the step of forming a contact hole, after the step of forming the capacitor upper electrode, for connecting the capacitor upper electrode and an upper-level interconnection is unnecessary which has been required for the conventional semiconductor device.

The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic cross section showing a first embodiment of a semiconductor device according to the present invention.

FIGS. 2-7 are schematic cross sections respectively illustrating first to sixth steps of manufacturing the semiconductor device shown in FIG. 1 .

FIG. 8 is a schematic cross section showing a second embodiment of a semiconductor device according to the invention.

FIGS. 9-13 are schematic cross sections respectively illustrating first to fifth steps of manufacturing the semiconductor device shown in FIG. 8 .

FIG. 14 is a schematic cross section showing a first modification of the second embodiment of the semiconductor device shown in FIG. 8 .

FIG. 15 is a schematic cross section illustrating a method of manufacturing the semiconductor device shown in FIG. 14 .

FIG. 16 is a schematic cross section showing a second modification of the second embodiment of the semiconductor device shown in FIG. 8 .

FIG. 17 is a schematic cross section illustrating a method of manufacturing the semiconductor device shown in FIG. 16 .

FIG. 18 is a schematic cross section showing a third embodiment of a semiconductor device according to the invention.

FIGS. 19-26 are schematic cross sections respectively illustrating first to eighth steps of manufacturing the semiconductor device shown in FIG. 18 .

FIG. 27 is a schematic cross section showing a fourth embodiment of a semiconductor device according to the invention.

FIGS. 28-34 are schematic cross sections respectively illustrating first to seventh steps of manufacturing the semiconductor device shown in FIG. 27 .

FIG. 35 is a schematic cross section showing a fifth embodiment of a semiconductor device according to the invention.

FIGS. 36-43 are schematic cross sections respectively illustrating first to eighth steps of manufacturing the semiconductor device shown in FIG. 35 .

FIG. 44 is a schematic cross section showing a sixth embodiment of a semiconductor device according to the invention.

FIG. 45 is a partially enlarged cross section showing an interconnection portion 21 in FIG. 44 .

FIGS. 46-54 are schematic cross sections respectively illustrating first to ninth steps of manufacturing the semiconductor device shown in FIGS. 44 and 45 .

FIG. 55 is a schematic cross section showing a seventh embodiment of a semiconductor device according to the invention.

FIGS. 56-60 are schematic cross sections respectively illustrating first to fifth steps of manufacturing the semiconductor device shown in FIG. 55 .

FIG. 61 is a schematic cross section showing an eighth embodiment of a semiconductor device according to the invention.

FIG. 62 is a plan view showing a horizontal cross section along line LXII—LXII in FIG. 61 .

FIGS. 63-67 are schematic cross sections respectively illustrating first to fifth steps of manufacturing the semiconductor device shown in FIGS. 61 and 62 .

FIG. 68 is a plan view showing a modification of the eighth embodiment of the semiconductor device shown in FIGS. 61 and 62 .

FIG. 69 is a schematic cross section showing a ninth embodiment of a semiconductor device according to the invention.

FIGS. 70-76 are schematic cross sections respectively illustrating first to seventh steps of manufacturing the semiconductor device shown in FIG. 69 .

FIG. 77 is a schematic cross section showing a tenth embodiment of a semiconductor device according to the invention.

FIGS. 78-86 are schematic cross sections respectively illustrating first to ninth steps of manufacturing the semiconductor device shown in FIG. 77 .

FIGS. 87 and 88 are schematic cross sections respectively illustrating first and second steps of manufacturing a semiconductor device according to an eleventh embodiment of the invention.

FIG. 89 is a schematic cross section showing a semiconductor device such as a conventional analog•digital LSI and the like including a capacitor portion where a capacitor is formed and an interconnection portion where an interconnection is formed.

FIG. 90 is a schematic cross section along line XC—XC in FIG. 89 .

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Embodiments of the present invention are hereinafter described in conjunction with the drawings. It is noted that components identical to or corresponding to each other are represented by the same reference character and description thereof is not repeated here.

First Embodiment

A first embodiment of a semiconductor device according to the present invention is described in conjunction with FIG. 1 .

Referring to FIG. 1 , the semiconductor device is an application-specific integrated circuit (ASIC) that includes a capacitor portion 20 where a capacitor is formed and an interconnection portion 21 where an interconnection is formed. An insulating film 2 is formed on the upper surface of a semiconductor substrate 1 . Capacitor portion 20 includes a lower electrode 3 a formed of a metal film that is deposited on insulating film 2 . A capacitor dielectric film 4 a is deposited on the upper surface of lower electrode 3 a . An upper electrode 6 a formed of a metal film is deposited on capacitor dielectric film 4 a . Lower electrode 3 a has its width W 1 greater than width W 2 of upper electrode 6 a.

In interconnection portion 21 , a first-level interconnection 3 b is formed on insulating film 2 . A dielectric film 4 b is deposited on the upper surface of the first-level interconnection 3 b.

An interlayer insulating film 8 is formed on dielectric film 4 b and upper electrode 6 a . In interlayer insulating film 8 , contact holes 10 a and 10 b are formed respectively in regions located on the first-level interconnection 3 b and upper electrode 6 a . A barrier metal film (not shown) is formed inside contact holes 10 a and 10 b . On this barrier metal film, tungsten plugs 11 a and 11 b are formed respectively to fill contact holes 10 a and 10 b . On tungsten plugs 11 a and 11 b , upper-level interconnections 12 a and 12 b are formed respectively.

In this way, lower electrode 3 a as a capacitor lower electrode, capacitor dielectric film 4 a and upper electrode 6 a as a capacitor upper electrode are deposited in the vertical direction to constitute a capacitor in the vertical direction. The thickness of capacitor dielectric film 4 a can be made significantly smaller than the minimum process dimension in a photolithography process employed for fabrication of a semiconductor device. Then, with a certain capacitance secured, the film thickness of capacitor dielectric film 4 a can be made smaller than the conventional one and accordingly the surface area of upper electrode 6 a and lower electrode 3 a can be made smaller. The size of the capacitor can thus be reduced compared with conventional capacitors.

Further, upper electrode 6 a has its width W 2 defined smaller than width W 1 of lower electrode 3 a . Then, an alignment margin in the photolithography process for fabricating upper electrode 6 a can be increased. As a result, it is possible to prevent any defect from occurring that is short-circuit between a sidewall for example of lower electrode 3 a and upper electrode 6 a due to shift of respective positions of upper electrode 6 a and lower electrode 3 a.

In addition, the metal films forming lower electrode 3 a and upper electrode 6 a enable a capacitor to be implemented that has a less dependency on voltage with a high precision compared with a semiconductor device employing a semiconductor such as polysilicon as a capacitor electrode. In this way, a capacitor required for a high-precision filter circuit can readily be achieved. In particular, the ASIC requires such a capacitor with a high-precision and a less voltage-dependency. Therefore, the present invention can be applied to the ASIC for enhancement of the performance as well as reduction of the size of the ASIC.

Referring to FIGS. 2-7 , a method of manufacturing the semiconductor device according to the invention shown in FIG. 1 is described.

As shown in FIG. 2 , insulating film 2 is formed on the upper surface of semiconductor substrate 1 . A lower-level metal film 3 is formed on insulating film 2 . As lower-level metal film 3 , an aluminum alloy film is deposited by means of sputtering. The lower-level metal film 3 formed of the aluminum alloy film has a thickness of approximately 0.4 μm. A dielectric film 4 is formed on lower-level metal film 3 to form the capacitor dielectric film. As dielectric film 4 , a silicon oxide film can be employed that is formed by means of plasma CVD (Chemical Vapor Deposition). The thickness of dielectric film 4 is approximately 30 nm. Resist films 5 a and 5 b are formed on dielectric film 4 . Although the aluminum alloy film is used as lower-level metal film 3 , a tungsten film for example may be used instead of the aluminum alloy. Although the thickness of lower-level metal film 3 is 0.4 μm here, the thickness of lower-level metal film 3 may be changed appropriately. Instead of the silicon oxide film employed as dielectric film 4 , a silicon nitride film for example may be used. In addition, the thickness of dielectric film 4 , which is 30 nm here, may be changed.

Resist films 5 a and 5 b are used as a mask to partially remove dielectric film 4 and lower-level metal film 3 by means of anisotropic etching. After this, resist films 5 a and 5 b are removed by plasma ashing or the like. In this way, lower electrode 3 a of the capacitor, capacitor dielectric film 4 a and the first-level interconnection 3 b as shown in FIG. 3 are formed. Dielectric film 4 b remains on the upper surface of the first-level interconnection 3 b.

Referring to FIG. 4 , a metal film 6 is formed on capacitor dielectric film 4 a and dielectric film 4 b in order to form the upper electrode. As metal film 6 , an aluminum alloy film can be deposited by means of sputtering. Metal film 6 has a thickness of approximately 0.4 μm. A resist film 7 is formed by photolithography technique on metal film 6 . Resist film 7 is employed for fabricating upper electrode 6 a (see FIG. 1 ), therefore, resist film 7 has its width W 2 corresponding to the width of upper electrode 6 a . Then, width W 2 of resist film 7 is set smaller than width W 1 of lower electrode 3 a . Instead of the aluminum alloy film, any metal film for example tungsten film can be used as metal film 6 . The thickness of metal film 6 can be changed appropriately.

Accordingly, width W 2 of resist film 7 which is made smaller than width W 1 of lower electrode 3 a can increase an alignment margin in the photolithography process for fabricating resist film 7 . Consequently, prevention is surely possible of occurrence of any defect like short-circuit between upper electrode 6 a and lower electrode 3 a due to residue resultant from a subsequent etching process for metal film 6 .

Resist film 7 is then used as a mask, and metal film 6 is partially removed by means of anisotropic etching. After this, plasma ashing is conducted for removing resist film 7 . Accordingly, upper electrode 6 a of the capacitor (see FIG. 5 ) can be produced. Interlayer insulating film 8 is thereafter formed on upper electrode 6 a and dielectric film 4 b . The upper surface of interlayer insulating film 8 is planarized by means of chemical mechanical polishing (CMP). In this way, the structure as shown in FIG. 5 is accomplished.

On the upper surface of interlayer insulating film 8 , a resist film 9 (see FIG. 6 ) is formed. This resist film 9 is used as a mask to remove a part of interlayer insulating film 8 and dielectric film 4 b by means of anisotropic etching and thus contact holes 10 a and 10 b are formed. The structure as shown in FIG. 6 is thus accomplished. At the bottom of contact hole 10 a , the upper surface of upper electrode 6 a is exposed. Further, the upper surface of the first-level interconnection 3 b is exposed at the bottom of contact hole 10 b.

Resist film 9 is then removed. A barrier metal film (not shown) and a tungsten film (not shown) are formed from the inside of contact holes 10 a and 10 b onto the upper surface of interlayer insulating film 8 . The tungsten film and the barrier metal film located on the upper surface of interlayer insulating film 8 are removed by means of dry etching, chemical mechanical polishing or the like. Accordingly, tungsten plugs 11 a and 11 b and a barrier metal film (not shown) are formed to fill the inside of contact holes 10 a and 10 b.

A third-level metal film (not shown) is formed on the upper surface of interlayer insulating film 8 . An aluminum alloy film formed by means of sputtering can be employed as this metal film. The third-level metal film has a thickness of approximately 0.4 μm. A resist film (not shown) is formed on the metal film. This resist film is used as a mask to partially remove the metal film through anisotropic etching. This resist film is thereafter removed. Upper-level interconnections 12 a and 12 b are accordingly formed respectively on tungsten plugs 11 a and 11 b . The semiconductor device as shown in FIG. 1 is thus accomplished. Instead of the aluminum alloy film, a metal film, for example, a tungsten film can be used as the third-level metal film that constitutes upper-level interconnections 12 a and 12 b . The thickness of the third-level metal film can appropriately be changed.

Second Embodiment

Referring to FIG. 8 , a second embodiment of a semiconductor device according to the invention is described.

Referring to FIG. 8 , the semiconductor device has a structure basically similar to that of the semiconductor device shown in FIG. 1 . The semiconductor device shown in FIG. 8 is different from that in FIG. 1 in that a dielectric film 4 including a capacitor dielectric film 4 a is formed on a lower electrode 3 a to extend from the upper surface of lower electrode 3 a to the sidewall thereof.

Further, regarding the semiconductor device shown in FIG. 8 , lower electrode 3 a of the capacitor has its width W 1 substantially equal to width W 2 of an upper electrode 6 a.

In this case, the capacitor in the vertical direction can be formed by depositing lower electrode 4 a as a capacitor lower electrode, capacitor dielectric film 4 a and upper electrode 6 a as a capacitor upper electrode in a similar manner to that of the first embodiment. Then, even if the thickness of capacitor dielectric film 4 a is made smaller than the conventional one to reduce the surface area of upper electrode 6 a and lower electrode 3 a , a certain capacitance can be secured. Accordingly, the capacitor can be reduced in size compared with the conventional capacitor.

In addition, dielectric film 4 including capacitor dielectric film 4 a extends from the part on the upper surface of lower electrode 3 a to the part on the sidewall thereof. Therefore, when the position of upper electrode 6 a changes and accordingly upper electrode 6 a extends onto the sidewall of lower electrode 3 a , dielectric film 4 is present between upper electrode 6 a and lower electrode 3 a . Prevention is thus possible of short-circuit between lower electrode 3 a and upper electrode 6 a.

As lower electrode 3 a and upper electrode 6 a are formed of metal films, a capacitor with a higher precision and a less voltage-dependency can be implemented compared with the capacitor implemented by using semiconductor such as polysilicon as a capacitor electrode.

Referring to FIGS. 9-13 , a method of manufacturing the semiconductor device shown in FIG. 8 is described.

In a similar manner to that of the manufacturing method of the semiconductor device employed in the first embodiment, an insulating film 2 is formed on the upper surface of a semiconductor substrate 1 . A lower-level metal film 3 is formed on insulating film 2 . As this lower-level metal film 3 , an aluminum alloy film produced by means of sputtering can be used. Lower-level metal film 3 has a thickness of approximately 0.4 μm. Instead of the aluminum alloy, tungsten for example can be used as a material for forming lower-level metal film 3 . The thickness of lower-level metal film 3 defined as 0.4 μm here may be changed appropriately. On the upper surface of lower-level metal film 3 , resist films 5 a and 5 b are formed by means of photolithography. Accordingly, the structure as shown in FIG. 9 is accomplished.

Resist films 5 a and 5 b are used as a mask, and lower-level metal film 3 is partially removed through anisotropic etching. After this, resist films 5 a and 5 b are removed by means of plasma ashing or the like. Consequently, lower electrode 3 a (see FIG. 10 ) and a first-level interconnection 3 b (see FIG. 10 ) are fabricated. Dielectric film 4 is formed on lower electrode 3 a and the first-level interconnection 3 b . In this way, the structure shown in FIG. 10 is obtained.

As dielectric film 4 , a silicon oxide film formed by means of plasma CVD can be employed. The thickness of dielectric film 4 is approximately 30 nm here. This thickness of dielectric film 4 may be changed appropriately. Instead of the silicon oxide film as a material for dielectric film 4 , another dielectric film such as silicon nitride film may be employed.

A metal film 6 (see FIG. 11 ) is formed on dielectric film 4 to constitute upper electrode 6 a (see FIG. 8 ). As metal film 6 , an aluminum alloy film formed by means of sputtering is applicable. Metal film 6 has a thickness of approximately 0.4 μm. As a material for metal film 6 , a metal film except for the aluminum alloy film, for example, a tungsten film can be used. On metal film 6 , a resist film 7 (see FIG. 11 ) is formed by means of photolithography. Accordingly, the structure as shown in FIG. 11 is accomplished. It is noted that width WI of lower electrode 3 a and width W 2 of resist film 7 are substantially identical to each other.

Resist film 7 is used as a mask, and metal film 6 is partially removed by means of anisotropic etching to form upper electrode 6 a (see FIG. 12 ). Resist film 7 is thereafter removed by plasma ashing or the like. Then, an interlayer insulating film 8 is formed on upper electrode 6 a and dielectric film 4 as shown in FIG. 12 . The upper surface of interlayer insulating film 8 is planarized by means of chemical mechanical polishing or the like.

In this way, dielectric film 4 is formed to extend from the part on the upper surface of lower electrode 3 a to the part on the sidewall thereof. Then, even if the location of resist film 7 changes and consequently upper electrode 6 a extends onto the sidewall of lower electrode 3 a , there still remains dielectric film 4 between upper electrode 6 a and lower electrode 3 a . Short-circuit between lower electrode 3 a and upper electrode 6 a can thus be prevented.

By process steps similar to those shown in FIGS. 6 and 7 employed in the first embodiment of the invention, contact holes 10 a and 10 b (see FIG. 13 ) are formed in interlayer insulating film 8 and a barrier metal film (not shown) is formed inside contact holes 10 a and 10 b . Tungsten plugs 11 a and 11 b are further formed to fill the inside of contact holes 10 a and 10 b . The structure as shown in FIG. 13 is accordingly obtained.

Upper-level interconnections 12 a and 12 b are formed respectively on tungsten plugs 11 a and 11 b as done in the first embodiment. The semiconductor device as shown in FIG. 8 is accordingly achieved.

A first modification of the second embodiment of the semiconductor device is described in conjunction with FIG. 14 .

Referring to FIG. 14 , the semiconductor device has a structure basically similar to that of the semiconductor device shown in FIG. 8 . Different from the semiconductor device shown in FIG. 8 , width W 2 of upper electrode 6 a is smaller than width WI of lower electrode 3 a as shown in FIG. 14 .

In this case, as accomplished by the first embodiment of the semiconductor device, a greater alignment margin can be obtained with respect to upper electrode 6 a and lower electrode 3 a in photolithography for fabricating upper electrode 6 a . Consequently, it is possible to prevent defect, i.e., of short-circuit between upper electrode 6 a and the sidewall for example of lower electrode 3 a from occurring.

A method of manufacturing the semiconductor device shown in FIG. 14 is described in conjunction with FIG. 15 .

After the steps shown in FIGS. 9 and 10 , a metal film 6 and a resist film 7 are formed as shown in FIG. 15 . The step shown in FIG. 15 corresponds to the step shown in FIG. 11 . As shown in FIG. 15 , width W 2 of resist film 7 is smaller than width W 1 of lower electrode 3 a . Then, alignment margin of resist film 7 and lower electrode 3 a can be increased in photolithography for forming resist film 7 .

Process steps as shown in FIGS. 12 and 13 are thereafter performed to obtain the semiconductor device shown in FIG. 14 .

A second modification of the second embodiment of the semiconductor device is described in conjunction with FIG. 16 .

Referring to FIG. 16 , the semiconductor device has a structure basically similar to that of the semiconductor device shown in FIG. 8 . The former semiconductor device includes an upper electrode 6 a having its width W 2 greater than width W 1 of a lower electrode 3 a.

In this case, upper electrode 6 a is located on the sidewall of lower electrode 3 a via a dielectric film 4 . Then, the sidewall of lower electrode 3 a can also be utilized as a capacitor electrode and accordingly the capacitance of the capacitor can be increased.

Referring to FIG. 17 , a method of manufacturing the semiconductor device shown in FIG. 16 is described.

After the process steps shown in FIGS. 9 and 10 , a metal film 6 and a resist film 7 are formed on dielectric film 4 . Width W 2 of resist film 7 is set greater than width W 1 of lower electrode 3 a . The step shown in FIG. 17 corresponds to that shown in FIG. 11 . In this way, resist film 7 is used as a mask to partially remove metal film 6 through anisotropic etching. Then, upper electrode 6 a formed on lower electrode 3 a extends from the upper surface of lower electrode 3 a onto the sidewall thereof with dielectric film 4 therebetween.

Through the steps shown in FIGS. 12 and 13 , the semiconductor device shown in FIG. 16 is obtained.

Third Embodiment

A third embodiment of a semiconductor device according to the invention is described in conjunction FIG. 18 .

Referring to FIG. 18 , the semiconductor device has a structure basically similar to that of the semiconductor device shown in FIG. 1 . The semiconductor device shown in FIG. 18 includes an upper electrode 6 a , a lower electrode 3 a and a capacitor dielectric film 4 a constituting a capacitor and respective positions of respective sidewalls substantially match. Upper electrode 6 a may be formed of a tungsten film and lower electrode 3 a may be a metal film containing aluminum such as an aluminum alloy film.

In this case, as accomplished by the first embodiment of the semiconductor device according to the invention, reduction is possible of the size of the capacitor by forming a capacitor in the vertical direction. In addition, upper electrode 6 a and lower electrode 3 a formed of metal films can be employed to implement a capacitor with a less voltage-dependency and a high precision. If different materials are used for structuring lower electrode 3 a and upper electrode 6 a respectively, as illustrated with respect to a manufacturing process below, upper electrode 6 a can surely be utilized as a mask in an etching process for generating lower electrode 3 a.

A method of manufacturing the semiconductor device shown in FIG. 18 is described below in conjunction with FIGS. 19-26 .

Referring to FIG. 19 , an insulating film (not shown) is formed on the upper surface of a semiconductor substrate 1 . A lower-level metal film 3 is formed on the insulating film to form the lower electrode. Dielectric film 4 is formed on lower-level metal film 3 in order to constitute the capacitor dielectric film. A metal film 6 is formed on dielectric film 4 to constitute the upper electrode.

Referring to FIG. 20 , a resist film 5 a is formed on metal film 6 by means of photolithography.

This resist film 5 a is used as a mask to partially remove metal film 6 by anisotropic etching. After this, resist film 5 a is removed by means of plasma ashing or the like. Consequently, upper electrode 6 a is formed as shown in FIG. 21 .

Referring to FIG. 22 , photolithography is conducted to form a resist film 5 b on dielectric film 4 for generating a first-level interconnection 3 b . As dielectric film 4 , a silicon oxynitride film (SiON film) is used. Then, this dielectric film 4 can be employed as ARC (Anti Reflection Coat) in formation of resist film 5 b . Consequently, no ARC is necessary on dielectric film 4 when resist film 5 b is formed. A simplified process can thus be accomplished.

Upper electrode 6 a and resist film 5 b are used as a mask to partially remove dielectric film 4 and lower-level metal film 3 by means of isotropic etching and accordingly, capacitor dielectric film 4 a (see FIG. 23 ), lower electrode 3 a (see FIG. 23 ) and the first-level interconnection 3 b (see FIG. 23 ) are formed.

In this way, upper electrode 6 a is used as a mask to fabricate lower electrode 3 a . Therefore, positional displacement of upper electrode 6 a and lower electrode 3 a with respect to each other can surely be prevented.

After this, resist film 5 b and the dielectric film located on the first-level interconnection 3 b is removed. On the first-level interconnection 3 b and upper electrode 6 a , interlayer insulating film 8 (see FIG. 23 ) is formed. The upper surface of interlayer insulating film 8 is planarized by means of chemical mechanical polishing (CMP).

Referring to FIG. 24 , a resist film 9 is formed on the upper surface of interlayer insulating film 8 by means of photolithography.

Resist film 9 is used as a mask to partially remove interlayer insulating film 8 through anisotropic etching. Consequently, contact holes 10 a and 10 b (see FIG. 25 ) are formed. After this, resist film 9 is removed by plasma ashing or the like. Accordingly, the structure as shown in FIG. 25 is achieved.

A barrier metal film (not shown) is thereafter formed to extend from the inside of contact holes 10 a and 10 b onto the upper surface of interlayer insulating film 8 . A tungsten film (not shown) is formed on the barrier metal film. The barrier metal film and the tungsten film located on the upper surface of interlayer insulating film 8 are then removed by means of CMP or the like. Consequently, as shown in FIG. 26 , the barrier metal film located inside contact holes 10 a and 10 b as well as tungsten plugs 11 a and 11 b formed on the barrier metal film to fill the inside of contact holes 10 a and 10 b can be obtained.

After this, upper-level interconnections 12 a and 12 b are formed respectively on tungsten plugs 11 a and 11 b as done in the first and second embodiments of the invention to achieve the semiconductor device shown in FIG. 18 .

Fourth Embodiment

A fourth embodiment of a semiconductor device according to the invention is described in conjunction with FIG. 27 .

Referring to FIG. 27 , the semiconductor device has a structure basically similar to that of the semiconductor device shown in FIG. 1. A difference therebetween is that the semiconductor device shown in FIG. 27 includes sidewall films 38 a and 38 b formed of a dielectric film that are deposited on the sidewall of an upper electrode 6 a of a capacitor. The sum of respective widths of upper electrode 6 a and sidewall films 38 a and 38 b is substantially identical to width W 1 of a lower electrode 3 a . In other words, upper electrode 6 a has its width W 2 smaller than width W 1 of lower electrode 3 a . In this way, the semiconductor device shown in FIG. 27 achieves the same effect as that of the semiconductor device of the first embodiment.

Further, sidewall films 38 a and 38 b serving as sidewall insulating films provided between the sidewall of upper electrode 6 a and the upper surface of lower electrode 3 a make it possible to surely prevent short-circuit between upper electrode 6 a and lower electrode 3 a.

Upper electrode 6 a and sidewall films 38 a and 38 b can be used as a mask for generating lower electrode 3 a by anisotropic etching as illustrated in conjunction with the manufacturing process described later, so as to ensure formation of lower electrode 3 a located below upper electrode 6 a and having a width greater than that of upper electrode 6 a.

It is noted that different materials may be employed for fabricating upper electrode 6 a and lower electrode 3 a respectively. For example, a tungsten film and an aluminum alloy film may be used as respective materials for upper electrode 6 a and lower electrode 3 a . Then, upper electrode 6 a can be utilized as a mask for fabricating lower electrode 3 a in an etching process.

A method of manufacturing the semiconductor device shown in FIG. 27 is discussed below in conjunction with FIGS. 28-34 .

After the manufacturing process steps shown in FIGS. 19-21 , an insulating film 38 which constitutes sidewall films 38 a and 38 b (see FIG. 27 ) is formed on upper electrode 6 a and dielectric film 4 as shown in FIG. 28 .

Insulating film 38 is then partially removed by means of anisotropic etching to form sidewall films 38 a and 38 b on the sidewall of upper electrode 6 a (see FIG. 29 ). A resist film 5 b is formed on dielectric film 4 on a region where a first-level interconnection 3 b (see FIG. 27 ) should be formed. The structure shown in FIG. 29 is thus accomplished.

Upper electrode 6 a and sidewall films 38 a and 38 b are thus employed as a mask used by etching for fabricating lower electrode 3 a . Accordingly, lower electrode 3 a can surely be formed that is located below upper electrode 6 a and having a width greater than that of upper electrode 6 a.

Upper electrode 6 a , sidewall films 38 a and 38 b and resist film 5 b are used as a mask to partially remove dielectric film 4 and lower-level metal film 3 by means of anisotropic etching. Resist film 5 b is thereafter removed. Consequently, lower electrode 3 a , capacitor dielectric film 4 a and the first-level interconnection 3 b are produced as shown in FIG. 30 . It is noted that there remains dielectric film 4 b on the first-level interconnection 3 b . In this way, upper electrode 6 a , and sidewall films 38 a and 38 b are employed as a mask for forming lower electrode 3 a to make width W 1 of lower electrode 3 a greater than width W 2 of upper electrode 6 a.

Different materials are employed as respective materials for metal films constituting upper electrode 6 a and lower electrode 3 a respectively. As a condition of etching lower-level metal film 3 , preferably an etching condition is employed such that the etching rate for the material constituting lower-level metal film 3 is sufficiently high while this etching removes substantially no material constituting upper electrode 6 a.

As shown in FIG. 31 , an interlayer insulating film 8 is deposited on upper electrode 6 a , sidewall films 38 a and 38 b and dielectric film 4 b . The upper surface of interlayer insulating film 8 is planarized by means of CMP or the like.

A resist film 9 is thereafter formed on the upper surface of interlayer insulating film 8 as shown in FIG. 32 .

Resist film 9 is used as a mask to partially remove interlayer insulating film 8 and dielectric film 4 b by anisotropic etching and accordingly contact holes 10 a and 10 b (see FIG. 33 ) are formed. Resist film 9 is thereafter removed. The structure as shown in FIG. 33 is accordingly obtained.

As the process shown in FIG. 26 , a barrier metal film (not shown) located inside contact holes 10 a and 10 b and tungsten plugs 11 a and 11 b filling respective inner portions of contact holes 10 a and 10 b are formed. As a result, the structure as shown in FIG. 34 is achieved.

The semiconductor device shown in FIG. 27 can be obtained by depositing upper-level interconnections 12 a and 12 b ( FIG. 27 ) on tungsten plugs 11 a and 11 b respectively in a similar manner to that of the third embodiment.

Fifth Embodiment

A fifth embodiment of a semiconductor device according to the invention is described below in conjunction with FIG. 35 .

Referring to FIG. 35 , the semiconductor device shown has its structure basically similar to that of the semiconductor device shown in FIG. 27 . The semiconductor device in FIG. 35 is different from that in FIG. 27 in that sidewall films 38 a and 38 b are formed on the sidewalls of an upper electrode 6 a and a capacitor dielectric film 4 a . Further, an insulating film 38 c remains on a first-level interconnection 3 b that is formed of a layer at the same level as that of sidewall films 38 a and 38 b . Sidewall films 38 a and 38 b and insulating film 38 c are formed of a silicon oxynitride film. These films are formed of a layer of the same level, which means that sidewall films 38 a and 38 b and insulating films 38 c are obtained by processing a single insulating film 38 (see FIG. 37 ).

The semiconductor device shown in FIG. 35 also provides an effect similar to that of the fourth embodiment of the semiconductor device according to the invention.

The silicon oxynitride film constituting sidewall films 38 a and 38 b and insulating film 38 c functions as ARC (Anti Reflection Coat). Then, the silicon oxynitride film constituting sidewall films 38 a and 38 b and insulating film 38 c can be employed as ARC for a resist film used for producing the first-level interconnection 3 b.

A method of manufacturing the semiconductor device shown in FIG. 35 is discussed below in conjunction with FIGS. 36-43 .

Process steps are performed that are similar to those of the manufacturing method of the semiconductor device according to the third embodiment shown in FIGS. 19 and 20 . A resist film 5 a (see FIG. 20 ) is used as a mask to partially remove a metal film 6 and a dielectric film 4 (see FIG. 20 ) thereby produce an upper electrode 6 a and a capacitor dielectric film 4 a (see FIG. 36 ). Resist film 5 a is thereafter removed. The structure as shown in FIG. 36 is thus obtained.

As shown in FIG. 37 , an insulating film 38 is formed on upper electrode 6 a and the upper surface of lower-level metal film 3 . A silicon oxynitride film is employed as insulating film 38 .

As shown in FIG. 38 , a resist film 5 b is formed on insulating film 38 on a region where the first-level interconnection 3 b (see FIG. 35 ) should be formed.

Here, the silicon oxynitride film serves as ARC as discussed above. Therefore, a separately prepared ARC for resist film 5 b can be made unnecessary by forming insulating film 38 made of the silicon oxynitride film that extends from the portion on upper electrode 6 a to the region where the first-level interconnection 3 b should be formed so as to form sidewall films 38 a and 38 b and depositing resist film 5 b on the silicon oxynitride film. The manufacturing process can thus be simplified.

Resist film 5 b is used as a mask to partially remove insulating film 38 by anisotropic etching and accordingly an insulating film 38 c is formed. At this time, sidewall films 38 a and 38 b (see FIG. 39 ) are also formed on the sidewalls of upper electrode 6 a and capacitor dielectric film 4 a . Resist film 5 b is thereafter removed. Upper electrode 6 a , sidewall films 38 a and 38 b and insulating film 38 c are used as a mask to partially remove lower-level metal film 3 by anisotropic etching. In this way, the structure as shown in FIG. 39 is obtained. This anisotropic etching produces lower electrode 3 a and the first-level interconnection 3 b.

Referring to FIG. 40 , an interlayer insulating film 8 is formed on upper electrode 6 a , sidewall films 38 a and 38 b and insulating film 38 c . The upper surface of interlayer insulating film 8 is planarized by means of CMP or the like.

As shown in FIG. 41 , a resist film 9 is formed on the upper surface of interlayer insulating film 8 as done in the step shown in FIG. 32 .

Resist film 9 is used as a mask to partially remove interlayer insulating film 8 and insulating film 38 c through anisotropic etching thereby form contact holes 10 a and 10 b (see FIG. 42 ). Resist film 9 is thereafter removed. In this way, the structure as shown in FIG. 42 is achieved.

Referring to FIG. 43 , a barrier metal film (not shown) located inside contact holes 10 a and 10 b as well as tungsten plugs 11 a and 11 b located to fill respective inner portions of contact holes 10 a and 10 b are formed in a manner similar to that of the manufacturing method of the semiconductor device according to the fourth embodiment of the invention shown in FIG. 34 .

Upper-level interconnections 12 a and 12 b (see FIG. 35 ) are formed on tungsten plugs 11 a and 11 b respectively so that the semiconductor device as shown in FIG. 35 is produced.

Sixth Embodiment

A sixth embodiment of a semiconductor device according to the invention is described in conjunction with FIGS. 44 and 45 .

Referring to FIGS. 44 and 45 , the semiconductor device has its structure basically similar to that of the semiconductor device shown in FIG. 27 . The semiconductor device shown in FIGS. 44 and 45 is different in the structure of interconnection portion 21 from that of the semiconductor device shown in FIG. 27 . Specifically, the semiconductor device shown in FIGS. 44 and 45 includes an interconnection portion 21 including a dielectric film 4 b provided on a first-level interconnection 3 b . An upper interconnection 6 b formed of a layer of the same level as that of upper electrode 6 a is provided on dielectric film 4 b . Sidewall films 38 d and 38 e are formed on the sidewalls of upper interconnection 6 b . The first-level interconnection 3 b and upper interconnection 6 b are electrically connected by a barrier metal film (not shown) and tungsten plug 11 b filling the inside of contact hole 10 b so as to function as one interconnection. More specifically, contact hole 10 b has its sidewall having its part where the upper surface and the sidewall surface of upper interconnection 6 b are exposed and its bottom wall where the upper surface of the first-level interconnection 3 b is partially exposed. The barrier metal film and tungsten plug 11 b are electrically connected respectively to the upper surface of the first-level interconnection 3 b and the upper surface and the sidewall surface of upper interconnection 6 b . As shown in FIG. 45 , contact hole 10 b extends through sidewall film 38 e and dielectric film 4 b to reach the upper surface of the first level interconnection 3 b.

The semiconductor device shown in FIGS. 44 and 45 can thus achieve an effect similar to that of the first embodiment of the semiconductor device according to the invention.

In the process step of forming a capacitor in the vertical direction that is formed of lower electrode 3 a , capacitor dielectric film 4 a and upper electrode 6 a , an interconnection can be formed simultaneously with formation of the capacitor, the interconnection being constructed of upper interconnection 6 b as an upper interconnection part and the first-level interconnection 3 b as a lower interconnection part. Tungsten plug 11 b as a conductive film can be used to electrically connect upper interconnection 6 b and the first-level interconnection 3 b thereby utilize upper interconnection 6 b and the first-level interconnection 3 b as one interconnection.

A method of manufacturing the semiconductor device shown in FIGS. 44 and 45 is described in conjunction with FIGS. 46-54 .

After the process steps shown in FIG. 19 , resist films 5 a and 5 b are formed on metal film 6 as shown in FIG. 46 .

Resist films 5 a and 5 b are used as a mask to partially remove metal film 6 by anisotropic etching. Resist films 5 a and 5 b are thereafter removed. As shown in FIG. 47 , upper electrode 6 a and upper interconnection 6 b are fabricated.

As shown in FIG. 48 , insulating film 38 is formed on upper electrode 6 a , upper interconnection 6 b and dielectric film 4 .

Insulating film 38 is partially removed by anisotropic etching to form sidewall films 38 a and 38 b located on the sidewalls of upper electrode 6 a and sidewall films 38 d and 38 e located on the sidewalls of upper interconnection 6 b.

Upper electrode 6 a , upper interconnection 6 b and sidewall films 38 a , 38 b , 38 d and 38 e are used as a mask to partially remove dielectric film 4 and lower-level metal film 3 by means of anisotropic etching. Consequently, lower electrode 3 a , capacitor dielectric film 4 a , the first-level interconnection 3 b and dielectric film 4 b are formed as shown in FIG. 50 . The presence of sidewall films 38 a and 38 b allows width W 1 of lower electrode 3 a to be greater than width W 2 of upper electrode 6 a . Further, the first-level interconnection 3 b has its width greater than that of upper interconnection 6 b.

As shown in FIG. 51 , interlayer insulating film 8 is formed on upper electrode 6 a and upper interconnection 6 b . Interlayer insulating film 8 has its upper surface planarized by means of CMP or the like.

As shown in FIG. 52 , a resist film 9 is formed on the upper surface of interlayer insulating film 8 . Resist film 9 is used as a mask to partially remove interlayer insulating film 8 , sidewall film 38 e and dielectric film 4 b by anisotropic etching and accordingly contact holes 10 a and 10 b (see FIG. 53 ) are formed. Resist film 9 is thereafter removed. Accordingly, the structure as shown in FIG. 53 is achieved.

At this time, contact hole 10 b has its sidewall where a part of the upper surface as well as the sidewall surface of upper interconnection 6 b are exposed. Simultaneously, the upper surface of the first-level interconnection 3 b is partially exposed on the bottom of contact hole 10 b.

Referring to FIG. 54 , a barrier metal film (not shown) and tungsten plugs 11 a and 11 b filling respectively the inside of contact holes 10 a and 10 b are formed in a manner similar to the step shown in FIG. 43 .

As discussed above, in the step of forming a capacitor of vertical type that is constituted of lower electrode 3 a , capacitor dielectric film 4 a and upper electrode 6 a , an interconnection can be produced simultaneously with the formation of the capacitor, the interconnection including upper interconnection 6 b and the first-level interconnection 3 b connected electrically by tungsten plug 11 b as a conductor.

Upper-level interconnections 12 a and 12 b (see FIG. 44 ) are thereafter formed to achieve the semiconductor device as shown in FIGS. 44 and 45 .

Seventh Embodiment

A seventh embodiment of a semiconductor device according to the present invention is described in conjunction with FIG. 55 .

Referring to FIG. 55 , the semiconductor device includes a capacitor portion 20 and an interconnection portion 21 . Capacitor portion 20 includes a via hole 27 and a trench 26 connected to the upper part of via hole 27 that are formed in an interlayer insulating film 25 deposited on a semiconductor substrate (not shown). A barrier metal film 28 is deposited on the walls of trench 26 and via hole 27 . On barrier metal film 28 , a metal film 29 is formed to fill trench 26 and via hole 27 . As a material for barrier metal film 28 , titanium nitride (TiN) can be employed. As a material for metal film 29 , tungsten may be used for example. Barrier metal film 28 and the metal film 29 serve as a lower electrode 31 of the capacitor. The position of the upper surface of barrier metal film 28 and metal film 29 is almost identical to that of interlayer insulating film 25 . Lower electrode 31 is fabricated by means of so-called dual damascene process.

A capacitor dielectric film 30 is deposited on lower electrode 31 . An upper electrode 32 a formed of a metal film is deposited to cover capacitor dielectric film 30 . On upper electrode 32 a formed of the metal film, an interlayer insulating film 33 is formed. A contact hole 34 a is formed in interlayer insulating film 33 in the region located on upper electrode 32 a . A barrier metal film 37 a is formed on the wall of contact hole 34 a . On barrier metal film 37 a , a tungsten plug 11 a is formed to fill contact hole 34 a . An upper-level interconnection 12 a is formed on tungsten plug 11 a.

Interconnection portion 21 includes an interconnection 32 b formed of a metal film and of a layer at the same level as that of upper electrode 32 a on interlayer insulating film 25 . On interconnection 32 b , interlayer insulating film 33 is formed. A contact hole 34 b is formed in interlayer insulating film 33 in the region located on interconnection 32 b . A barrier metal film 37 b is formed on the wall of contact hole 34 b . A tungsten plug 11 b is formed on barrier metal film 37 b to fill the inside of contact hole 34 b . An upper-level interconnection 12 b is formed on tungsten plug 11 b.

A capacitor in the vertical direction can thus be produced by depositing in the vertical direction lower electrode 31 as a capacitor lower electrode, capacitor dielectric film 30 , and upper electrode 32 a as a capacitor upper electrode. Then, as the semiconductor device according to the first embodiment, a certain capacitance can be secured while the surface area of upper electrode 32 a and lower electrode 31 can further be reduced by providing a smaller thickness of the dielectric film and accordingly the capacitor can be reduced in size compared with the conventional capacitor.

In addition, the lower electrode has a so-called damascene structure where the electrode fills the inside of the trench of the interlayer insulating film. Therefore, for a semiconductor device employing a damascene interconnection as its interconnection, such an interconnection can partially be used as lower electrode 31 . For this type of semiconductor device employing the damascene interconnection, a capacitor of vertical type can readily be implemented.

Since lower electrode 31 and upper electrode 32 a contain metal films, a capacitor with a high precision and a less voltage-dependency can be achieved compared with the semiconductor device using semiconductor such as polysilicon as the capacitor electrode.

A method of manufacturing the semiconductor device shown in FIG. 55 is discussed below in conjunction with FIGS. 56-60 .

Referring to FIG. 56 , interlayer insulating film 25 is formed on the semiconductor substrate (not shown).

Referring to FIG. 57 , trench 26 and via hole 27 connected to trench 26 are formed in interlayer insulating film 25 for conducting dual damascene method.

A barrier metal film (not shown) is deposited by means of sputtering, CVD or the like to extend from the portion on the wall of trench 26 and via hole 27 to the portion on the upper surface of interlayer insulating film 25 .

On this barrier metal film, a metal film (not shown) such as tungsten is deposited by means of sputtering, CVD or the like that fills the inside of trench 26 and via hole 27 and extends to the part on the upper surface of interlayer insulating film 25 . After this, by means of CMP, the metal film and the barrier metal film located on the upper surface of interlayer insulating film 25 are removed. In this way, as shown in FIG. 58 , barrier metal film 28 and metal film 29 are formed. Barrier metal film 28 and metal film 29 constitute lower electrode 31 of the capacitor.

A dielectric film (not shown) is deposited to extend from the part on metal film 29 to the part on the upper surface of interlayer insulating film 25 . As this dielectric film, a silicon oxide film may be employed that is deposited by means of CVD or the like. The silicon oxide film functioning as a dielectric film has a thickness of approximately 30 nm. A resist film (not shown) is thereafter deposited on the dielectric film by means of photolithography. This resist film is used as a mask to partially remove the dielectric film. The resist film is then removed. Consequently, capacitor dielectric film 30 is formed that is located on lower electrode 31 as shown in FIG. 59 .

A metal film (not shown) is thereafter formed that extends from the part on capacitor dielectric film 30 to the part on the upper surface of interlayer insulating film 25 . As this metal film, an aluminum film may be employed that is deposited by means of sputtering. On the metal film such as the aluminum film, a resist film (not shown) is formed by means of photolithography. This resist film is used as a mask to partially remove the metal film through anisotropic etching. The resist film is then removed. Accordingly, interconnection 32 b and upper electrode 32 a formed of the metal film are formed. Here, capacitor dielectric film 30 has its width greater than that of lower electrode 31 . Further, upper electrode 32 a has its width greater than that of capacitor dielectric film 30 .

Interlayer insulating film 33 (see FIG. 55 ) is thereafter deposited on upper electrode 32 a and interconnection 32 b . A resist film (not shown) is formed on interlayer insulating film 33 . This resist film is used as a mask to partially remove interlayer insulating film 33 by anisotropic etching thereby form contact holes 34 a and 34 b (see FIG. 55 ). A barrier metal film (not shown) is formed that extends from the inside of contact holes 34 a and 34 b onto the upper surface of interlayer insulating film 33 . A titanium nitride film for example may be employed as the barrier metal film that is deposited by means of sputtering, CVD or the like. On the barrier metal film, a tungsten film (not shown) is formed that fills the inside of contact holes 34 a and 34 e and extends onto the upper surface of interlayer insulating film 33 . The tungsten film and the barrier metal film located on the upper surface of interlayer insulating film 33 are removed by means of CMP or the like. Accordingly, barrier metal films 37 a and 37 b and tungsten plugs 11 a and 11 b are formed in contact holes 34 a and 34 b . Upper-level interconnections 12 a and 12 b (see FIG. 55 ) are thereafter formed respectively on tungsten plugs 11 a and 11 b . The semiconductor device as shown in FIG. 55 having the capacitor in the vertical direction can thus be achieved.

Eighth Embodiment

An eighth embodiment of a semiconductor device according to the invention is explained in conjunction with FIGS. 61 and 62 .

Referring to FIGS. 61 and 62 , the semiconductor device includes a capacitor portion 20 and an interconnection portion 21 . Capacitor portion 20 includes one electrode 36 a and the other electrode 36 b formed on an interlayer insulating film 25 . As seen from FIG. 62 , one electrode 36 a includes extensions 39 a , 39 c and 39 e . The other electrode 36 b includes extensions 39 b , 39 d and 39 f . These extensions 39 a - 39 f are arranged opposite to each other with a part of an interlayer insulating film 33 therebetween, which serves as a capacitor dielectric film. In the region located under the other electrode 36 b , a contact hole 35 a is formed in interlayer insulating film 25 . A barrier metal film 28 a and a metal film 29 a are formed inside contact hole 35 a . Metal film 29 a is electrically connected to the other electrode 36 b . A contact hole 34 a is further formed in interlayer insulating film 33 in the region located on one electrode 36 a . In contact hole 34 a , a barrier metal film 37 a and a tungsten plug 11 a are formed. In the region located on tungsten plug 11 a , an upper-level interconnection 12 a is formed. Upper-level interconnection 12 a and one electrode 36 a are electrically connected via barrier metal film 37 a and the tungsten plug 11 .

Interconnection portion 21 includes a contact hole 35 b formed in interlayer insulating film 25 . A barrier metal film 28 b and a metal film 29 b are formed inside contact hole 35 b . An interconnection 36 c is formed in the region located on metal film 29 b . Interconnection 36 c is constituted of the layer at the same level as that of one electrode 36 a and the other electrode 36 b as understood from the manufacturing method discussed below. On interconnection 36 c , a contact hole 34 b is formed in interlayer insulating film 33 . A barrier metal film 37 b and a tungsten plug 11 b are formed inside contact hole 34 b . An upper-level interconnection 12 b is formed on tungsten plug 1 b.

In this way, extensions 39 a , 39 c and 39 e as first and second extended portions and extensions 39 b , 39 d and 39 f as third and fourth extended portions are interleaved. Therefore, sidewalls opposite to each other of extensions 39 a - 39 f of one electrode 36 a as one capacitor electrode and the other electrode 36 b as the other capacitor electrode can be utilized as electrode surfaces of the capacitor. Specifically, almost all the sidewall surfaces of extensions 39 b - 39 e can be employed as capacitor electrode surfaces. The volume of the region occupied by the capacitor can thus be decreased compared with the semiconductor device as shown in FIGS. 89 and 90 having a plurality of conventional capacitors arranged for ensuring a certain capacitance.

A method of manufacturing the semiconductor device shown in FIGS. 61 and 62 is described in conjunction with FIGS. 63-67 .

Interlayer insulating film 25 (see FIG. 63 ) is formed on a semiconductor substrate (not shown). Interlayer insulating film 25 is deposited by means of CVD or the like. A resist film (not shown) is formed on interlayer insulating film 25 by photolithography. This resist film is used as a mask to remove a part of interlayer insulating film 25 by anisotropic etching to produce contact holes 35 a and 35 b (see FIG. 63 ). The resist film is thereafter removed. The structure as shown in FIG. 63 is thus obtained.

A barrier metal film (not shown) is formed that extends from the inside of contact holes 35 a and 35 b onto the upper surface of interlayer insulating film 25 . A titanium nitride film deposited by means of sputtering, CVD or the like can be applicable to this barrier metal film. A metal film (not shown) is formed on the barrier metal film. The metal film is formed to fill the inside of contact holes 35 a and 35 b . Tungsten or the like can be used as a material for the metal film. The metal film and the barrier metal film located on the upper surface of interlayer insulating film 25 are removed by means of CMP or the like. In this way, barrier metal films 28 a and 28 b and metal films 29 a and 29 b are formed within contact holes 35 a and 35 b as shown in FIG. 64 .

A metal film (not shown) is deposited on interlayer insulating film 25 by sputtering or the like. On the metal film, a resist film (not shown) is formed through photolithography. This resist film is used as a mask to partially remove the metal film through anisotropic etching. The resist film is then removed. In this way, as shown in FIG. 65 , one electrode 36 a , the other electrode 36 b and interconnection 36 c formed of a metal film are formed to constitute a capacitor in the lateral direction. The other electrode 36 b is located to contact metal film 29 a formed in contact hole 35 a.

Interlayer insulating film 33 (see FIG. 66 ) is formed on one electrode 36 a , the other electrode 36 b and interconnection 36 c . CVD or the like may be used for generating interlayer insulating film 33 . A resist film (not shown) is formed on interlayer insulating film 33 by photolithography. The resist film is used as a mask to partially remove interlayer insulating film 33 by anisotropic etching thereby form contact holes 34 a and 34 b (see FIG. 66 ). The resist film is then removed. The structure as shown in FIG. 66 is thus achieved.

Contact hole 34 a has its bottom where the upper surface of one electrode 36 a is partially exposed. Further, contact hole 34 b has its bottom where the upper surface of interconnection 36 c is exposed.

By a method similar to that employed for producing barrier metal film 28 b and metal films 29 a and 29 b , barrier metal films 37 a , 37 b and tungsten plugs 11 a and 11 b are formed in contact holes 34 a and 34 b . The structure as shown in FIG. 67 is thus accomplished.

Upper-level interconnections 12 a and 12 b (see FIG. 61 ) are thereafter deposited on tungsten plugs 11 a and 11 b to fabricate the semiconductor device as shown in FIGS. 61 and 62 .

The capacitance of the capacitor in the lateral direction included in the capacitor portion can be changed as shown in FIG. 68 for example by changing the number of extensions 39 a - 39 p and accordingly changing the area of the region functioning as a capacitor electrode. In this way, the capacitance of the capacitor can readily be changed. FIG. 68 is a plan view showing a modification of the eighth embodiment of the semiconductor device that corresponds to FIG. 62 .

Ninth Embodiment

A ninth embodiment of a semiconductor device according to the invention is explained below in conjunction with FIG. 69 .

Referring to FIG. 69 , the semiconductor device includes a capacitor portion 20 and an interconnection portion 21 . In capacitor portion 20 , an insulating film 2 is deposited on a semiconductor substrate 1 . On insulating film 2 , a lower-level interconnection 3 c for capacitor is formed. An interlayer insulating film 8 is deposited on capacitor lower-level interconnection 3 c . Contact holes 13 a - 13 g are formed in interlayer insulating film 8 in the region located on capacitor lower-level interconnection 3 c . Tungsten films 14 a - 14 g are formed to fill the inside of contact holes 13 a - 13 g . A depression portion 16 with its upper surface lower than the upper surface of interlayer insulating film 8 is formed in the region located on contact holes 13 a - 13 g . In depression portion 16 , a silicon oxide film 17 a (hereinafter referred to as SOG film) formed by means of spin-on-glass method is deposited as a capacitor dielectric film. An upper electrode 18 a formed of a metal film is formed on the SOG film 17 a.

In interconnection portion 21 , a first-level interconnection 3 b is formed on insulating film 2 . In the region on interconnection 3 b , a contact hole 13 h is formed in interlayer insulating film 8 . A tungsten film 14 h is formed to fill the inside of contact hole 13 h . An upper-level interconnection 18 b is deposited on tungsten film 14 h . Preferably, a barrier metal film (not shown) is formed on the walls of contact holes 13 a - 13 h.

In this way, a capacitor in the vertical direction can be produced by arranging in the vertical direction tungsten films 14 a - 14 g serving as a capacitor lower electrode, SOG film 17 a serving as a dielectric film and upper electrode 18 a serving as a capacitor upper electrode. As the first embodiment of the semiconductor device according to the invention, with a certain capacitance ensured, the thickness of SOG film 17 a can be made smaller than the conventional one to reduce the area of the region of tungsten films 14 a - 14 g , opposite to SOG film 17 a , that corresponds to the surface area of the capacitor lower electrode, as well as the surface area of upper electrode 18 a . Accordingly, the capacitor can be reduced in size compared with the conventional capacitor.

The number of contact holes 13 a - 13 g that are holes formed in interlayer insulating film 8 or the cross sectional area thereof can be changed to vary the area of the portion, opposing SOG film 17 a , of tungsten films 14 a - 14 g in an easy manner. It is then possible to readily change the capacitance of the capacitor.

Further, tungsten films 14 a - 14 g serving as a capacitor lower electrode and upper electrode 18 a contain a metal film. Then, compared with the semiconductor device employing semiconductor such as polysilicon as a capacitor electrode, a capacitor with a high precision and a less voltage-dependency can be achieved.

A method of manufacturing the semiconductor device shown in FIG. 69 is described in conjunction with FIGS. 70-76 .

Referring to FIG. 70 , insulating film 2 is deposited on semiconductor substrate 1 . Metal film 3 is formed on insulating film 2 . An aluminum alloy film can be used that is formed by means of sputtering as this metal film 3 . Metal film 3 has a thickness of approximately 0.4 μm. The material and thickness of metal film 3 can arbitrarily be changed. Further, tungsten may be employed as a material for metal film 3 .

Resist films 5 a and 5 b are formed on metal film 3 by photolithography.

Resist films 5 a and 5 b are used as a mask to partially remove metal film 3 by anisotropic etching. Resist films 5 a and 5 b are thereafter removed. In this way, lower-level interconnection 3 c and first-level interconnection 3 b for the capacitor are formed as shown in FIG. 71 .

On capacitor lower-level interconnection 3 c and first-level interconnection 3 b , interlayer insulating film 8 (see FIG. 72 ) is deposited. The upper surface of interlayer insulating film 8 is planarized by means of CMP or the like. Photolithography is used for generating a resist film (not shown) on interlayer insulating film 8 . The resist film is used as a mask to partially remove interlayer insulating film 8 by anisotropic etching thereby produce contact holes 13 a - 13 h (see FIG. 72 ). Tungsten film 14 (see FIG. 72 ) is formed by means of sputtering or CVD that extends from the inside of contact holes 13 a - 13 h onto the upper surface of interlayer insulating film 8 . The structure as shown in FIG. 72 is thus obtained. Tungsten film 14 has its thickness of approximately 400 nm. The thickness of tungsten film 14 may arbitrarily be changed.

The number of contact holes 13 a - 13 g to be formed as well as the cross sectional area thereof can be varied to easily change the area of the portion of tungsten films 14 a - 14 g (see FIG. 69 ) that faces the SOG film 17 a (see FIG. 69 ) serving as a dielectric film. In this way, the capacitance of the capacitor can readily be changed.

By CMP, tungsten film 14 located on the upper surface of interlayer insulating film 8 is removed. Erosion occurs in the process of CMP in the region where contact holes 13 a - 13 g are formed close to each other. As a result, depression portion 16 is formed in the upper surface of interlayer insulating film 8 . Here, the process conditions of the CMP are adjusted to define the depth from the upper surface 15 of interlayer insulating film 8 to the bottom surface of depression portion 16 as 50 nm. It is noted that the process conditions of CMP can be changed to arbitrarily change the depth of depression portion 16 . Then, the structure as shown in FIG. 73 is produced.

Referring to FIG. 74 , an SOG is applied and thereafter a predetermined annealing process is applied to form SOG film 17 that constitutes the capacitor dielectric film. The thickness of the applied SOG is 0.5 μm. The thickness of the applied SOG film 17 may arbitrarily be changed. Here, the SOG film is employed as a capacitor dielectric film. However, another dielectric material may be used that can fill depression portion 16 .

Referring to FIG. 75 , SOG film 17 (see FIG. 74 ) is removed from the region except for depression portion 16 by means of CMP or the like. Then, SOG film 17 a remains in depression portion 16 that serves as the capacitor dielectric film.

Referring to FIG. 76 , metal film 18 is formed on SOG film 17 a . As metal film 18 , an aluminum alloy film may be employed that is formed by sputtering. Metal film 18 has a thickness of 0.4 μm. The material and thickness of metal film 18 can arbitrarily be changed. Resist films 19 a and 19 b are formed on metal film 18 by photolithography.

Resist films 19 a and 19 b are used as a mask to partially remove metal film 18 by anisotropic etching. Resist films 19 a and 19 b are thereafter removed. Upper electrode 18 a and upper-level interconnection 18 b (see FIG. 69 ) are accordingly formed. The semiconductor device shown in FIG. 69 can thus be produced.

Tenth Embodiment

A tenth embodiment of a semiconductor device according to the invention is discussed in conjunction with FIG. 77 .

Referring to FIG. 77 , the semiconductor device has its structure basically identical to that of the semiconductor device shown in FIG. 27. A difference therebetween is that the semiconductor device shown in FIG. 77 has a capacitor portion 20 including a contact hole 22 for an upper electrode so as to expose the upper surface of a capacitor dielectric film 4 a . A tungsten film 23 a is formed inside contact hole 22 for upper electrode. On tungsten film 23 a , an upper-level interconnection 24 a is formed filling the inside of contact hole 22 for the upper electrode and extending onto the upper surface of interlayer insulating film 8 to serve as an upper electrode of the capacitor.

In interconnection portion 21 , a contact hole 10 is formed in interlayer insulating film 8 in the region located on a first-level interconnection 3 b . A tungsten film 23 b fills the inside of contact hole 10 . An upper-level interconnection 24 b is formed on tungsten film 23 b.

In this way, a capacitor in the vertical direction can be produced as done in the first embodiment of the invention by depositing in the vertical direction lower electrode 3 a as a capacitor lower electrode, capacitor dielectric film 4 a , tungsten film 23 a as a capacitor upper electrode and upper-layer interconnection 24 a . Accordingly, with a certain capacitance secured, the area of tungsten film 23 a that is opposite to capacitor dielectric film 4 a as well as the surface area of lower electrode 3 a can be reduced by reducing the thickness of capacitor dielectric film 4 a to be smaller than the conventional one. As a result, the capacitor can be reduced in size compared with the conventional capacitor.

Further, tungsten film 23 a as a capacitor upper electrode and upper-level interconnection 24 a are arranged within upper electrode contact hole 22 serving as an opening portion. Therefore, no process is necessary for forming a contact hole, after forming the capacitor upper electrode, in order to connect the upper electrode and the upper-level interconnection, the process having been required conventionally in the manufacturing process. In this way, the process of manufacturing the semiconductor device can be simplified.

Further, as lower electrode 3 a , tungsten film 23 a and upper-level interconnection 24 a are formed of respective metal films, a capacitor with a higher precision and a less voltage-dependency can be achieved compared with the semiconductor device employing semiconductor such as polysilicon as a capacitor electrode.

A method of manufacturing the semiconductor device is described in conjunction with FIGS. 78-86 .

Referring to FIG. 78 , an insulating film (not shown) is formed on semiconductor substrate 1 . Lower-level metal film 3 is formed on the insulating film. Dielectric film 4 is deposited on lower-level metal film 3 .

Referring to FIG. 79 , resist films 5 a and 5 b are formed by photolithography on dielectric film 4 . As dielectric film 4 , a material serving as ARC (Anti Reflection Coat), for example, a silicon oxynitride film can be employed to make it unnecessary to separately form ARC from dielectric film 4 under resist films 5 a and 5 b.

Resist films 5 a and 5 b are used as a mask to partially remove dielectric film 4 and lower-level metal film 3 by anisotropic etching. Resist films 5 a and 5 b are then removed. As shown in FIG. 80 , lower electrode 3 a , capacitor dielectric film 4 a , the first-level interconnection 3 b and dielectric film 4 b are accordingly generated.

Referring to FIG. 81 , interlayer insulating film 8 is deposited on capacitor dielectric film 4 a and dielectric film 4 b.

Referring to FIG. 82 , a resist film 7 is formed on interlayer insulating film 8 by photolithography.

Resist film 7 is used as a mask to partially remove interlayer insulating film 8 and dielectric film 4 b by anisotropic etching thereby produce contact hole 10 (see FIG. 83 ). Resist film 7 is thereafter removed. Accordingly, the structure as shown in FIG. 83 is produced.

Referring to FIG. 84 , a resist film 9 is formed on interlayer insulating film 8 by photolithography.

Resist film 9 is used as a mask to partially remove interlayer insulating film 8 by anisotropic etching thereby form contact hole 22 (see FIG. 85 ) for the upper electrode. Resist film 9 is thereafter removed. The structure as shown in FIG. 85 is then obtained.

A tungsten film is formed that extends from the inside of upper electrode contact hole 22 and contact hole 10 onto the upper surface of interlayer insulating film 8 . The tungsten film located on the upper surface of interlayer insulating film 8 is removed by means of CMP or the like thereby implement the structure as shown in FIG. 86 .

A metal film is formed on tungsten films 23 a and 23 b . A resist film is formed on the metal film by photolithography. The resist film is used as a mask to partially remove the metal film by anisotropic etching. The resist film is then removed. In this way, upper-level interconnections 24 a and 24 b (see FIG. 27 ) are formed. The semiconductor device shown in FIG. 77 is produced accordingly.

Tungsten film 23 a serving as the capacitor upper electrode is provided in upper electrode contact hole 22 . Upper electrode contact hole 22 also functions as a connection hole with upper-level interconnection 24 a . The step of forming a contact hole for connecting the capacitor upper electrode and the upper-level interconnection, which has been required as the step following the step of forming the capacitor upper electrode, is unnecessary.

Eleventh Embodiment

An eleventh embodiment of a semiconductor device has its structure basically identical to that of the semiconductor device shown in FIG. 77 .

A method of manufacturing the semiconductor device is described in conjunction with FIGS. 87 and 88 .

The process steps illustrated in FIGS. 78-81 are performed. After this, as shown in FIG. 87 , a resist film 7 is formed on an interlayer insulating film 8 by means of photolithography. A hole pattern is formed in resist film 7 for generating a contact hole 10 and a contact hole 22 for the upper electrode.

Resist film 7 is used as a mask to partially remove interlayer insulating film 8 and a dielectric film 4 b by anisotropic etching to produce contact hole 22 (see FIG. 88 ) for the upper electrode and contact hole 10 (see FIG. 88 ). At this time, etching conditions are adjusted to allow dielectric film 4 b to be etched in the hole having a shorter diameter like contact hole 10 and not to allow dielectric film 4 a to be etched in a hole with a relatively large diameter like upper electrode contact hole 22 .

For example, it is supposed here that the shape of contact hole 10 in plan view is a circle having a diameter of 0.2 μm and the shape of upper electrode contact hole 22 in plan view is a square of 2 μm×2 μm. In this case, conditions employed are that a two-frequency parallel plate RIE (Reaction Ion Etching) apparatus is used, the pressure within a reaction chamber is 4 Pa, RF power (top/bottom) is 1400 W/1400W, carbon tetrafluoride gas (CF 4 ), trifluromethane gas (CHF 3 ), oxygen gas (O 2 ), and argon gas (Ar) are used as reaction gas, the flow rate of CF 4 is 0.01 liter/min (10 sccm), the flow rate of CHF 3 is 0.03 liter/min (30 sccm), the flow rate of O 2 is 0.009 liter/min (9 sccm) and the flow rate of Ar is 0.4 liter/min (400 sccm). Under these conditions, etching can be performed such that capacitor dielectric film 4 a is not etched in contact hole 22 for upper electrode while dielectric film 4 b is etched in contact hole 10 as discussed above.

Accordingly, upper electrode contact hole 22 and contact hole 10 can simultaneously be produced and consequently the manufacturing process can be simplified compared with the manufacturing method of the tenth embodiment of the invention.

Resist film 7 is thereafter removed. The structure as shown in FIG. 88 is achieved.

A step similar to that shown in FIG. 86 is performed to produce the semiconductor device shown in FIG. 77 similar to that of the tenth embodiment.

Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.

Claims

1. A semiconductor device comprising:a capacitor lower electrode having an upper surface and formed from a metal film layer; a dielectric film deposited on the upper surface of said capacitor lower electrode and having its thickness smaller than that of said capacitor lower electrode; a capacitor upper electrode deposited on said dielectric film, having its width smaller than that of said capacitor lower electrode and including a metal film, wherein said capacitor upper electrode has a sidewall; a sidewall insulating film formed on the upper surface of said capacitor lower electrode and on the sidewall of said capacitor upper electrode; and an interconnection layer formed from the same metal film layer as the capacitor lower electrode.

2. The semiconductor device according to claim 1, wherein said sidewall insulating film includes a silicon oxynitride film.

3. The semiconductor device according to claim 1, whereinsaid capacitor lower electrode includes aluminum, and said capacitor upper electrode includes tungsten.

4. The semiconductor device according to claim 1,wherein said interconnection layer is a lower interconnection portion constituted of a layer at the same level as that of said capacitor lower electrode and further comprising: another dielectric film deposited on said lower interconnection portion; an upper interconnection portion deposited on said another dielectric film, having its width smaller than that of said lower interconnection portion, and constituted of a layer at the same level as that of said capacitor upper electrode; an interlayer insulating film formed on said upper interconnection portion, a connection hole being formed in said interlayer insulating film to expose lower surface of said upper interconnection portion and reach an upper surface of said lower interconnection portion; and a conductive film provided inside and connection hole to electrically connect said upper interconnection and said lower interconnection portion.