This application is the U.S. national phase of International Application No. PCT/GB2004/003106 filed Jul. 16, 2004 published in English Jan. 27, 2005 as International Publication No. WO 2004/009081 A1, which application claims priority to Great Britain Application No. 0316658.4 filed Jul. 16, 2003, the contents of which are incorporated by reference herein.
Silicon carbide heating elements conventionally are manufactured in the form of solid rods or cylindrical tubes, typically in diameters between 3 mm and 110 mm diameter. Other cross sections are also possible, such as square or rectangular tubes, but are not in common use.
Elements of a tubular cross-section are more economical to produce, using less silicon carbide than solid elements, and most silicon carbide elements used in industrial furnaces feature a tubular construction.
Silicon carbide furnace heating elements should be distinguished from electrical igniters, which are designed to produce a rapid increase and decrease in heat so as to ignite a combustible material. Igniters need to be small to provide such rapid heating and cooling. Furnace heating elements are required to provide electrical heat at elevated temperatures and for prolonged periods (e.g. several years at temperature). The design criteria for furnace heating elements and electrical igniters are thus extremely different.
The power availability of any radiant heating elements is a function of its radiating surface area, and the capability of any given element type is usually expressed in watts per square cm of that radiating surface.
In the case of tubular silicon carbide elements, only the external surface area is considered as useful radiating surface as there is no radiative heat transfer from the inner surfaces of the tube to the surroundings.
Silicon carbide is a relatively expensive ceramic material, particularly in the grades used in the manufacture of high temperature electric heating elements, so the use of less material would have a significant cost benefit
The applicant has realised that if the ratio between the useful radiating surface and the cross-sectional area of the heating elements is increased, additional power may be provided from an element of similar cross-sectional area to a conventional tubular or solid element, or alternatively a similar power from a smaller and lighter element, while using less mass of silicon carbide.
Accordingly the present invention provides a strip form silicon carbide furnace heating element.
Preferably the heating elements are non-hollow.
Preferably the heating elements have a cross-sectional aspect ratio of greater than 3:1, more preferably greater than 5:1, yet more preferably greater than 10:1.
By aspect ratio is meant the ratio of the width to thickness of the strip.
Further features of the invention are made clear in the claims in the light of the following illustrative description, and with reference to the drawings in which:—
In
In
Additionally, the overall area of the tube 1 is πD2/4 whereas that of the strip 2 is πDW. So the ratio of area of strip to tube is 4 W/D. For a tube of diameter 40 mm and wall thickness 5 mm this results in a ratio of the overall area of the strip to tube of 0.5. By reducing the overall area of the element, a smaller hole in a furnace wall can be considered.
This heating section may be flat, but for many uses, it is anticipated that the heating section will be bent one or more times, particularly out of the plane of the strip, to suit installation in various types of equipment, but especially in indirect electric resistance furnaces.
Other shapes of element are envisaged where one or more heating sections may be shaped with more than one bent section in order to conform with the shape of the equipment into which the element(s) will be fitted and/or provide convenient connection to either single phase or 3-phase electric power supply. For example, a W shaped element can readily be made. For a 3-phase heating element three strips may be joined to form a star or other configuration.
In
In
Silicon carbide elements of substantially U-shape are known, and have previously been manufactured using a tubular or solid cylindrical heating section. The bend may be formed either by casting in a mould having the shape of the U, for example by slip-casting, but slip-casting is a non-preferred and relatively expensive method of manufacture for silicon carbide heating elements.
Casting techniques limit the particle size of silicon carbide material that conveniently can be used in manufacture, and where material with coarse grains is required, casting is not seen as a practical manufacturing method. Also, should it be desired to manufacture the heating elements in a high density, reaction-bonded grade of material, then again, slip-casting is a non-preferred route of manufacture, as the casting material or slip must contain both silicon carbide and carbon, and it is not easy to cast such bodies in a controlled or repeatable fashion.
Where volume production of silicon carbide elements is required, the method of manufacture preferred is by extrusion, where silicon carbide grains, or mixtures of silicon carbide and carbon, are blended with binders and plasticisers, so they can be extruded through suitable dies, or die and pin sets, where hollow sections are to be produced. [There may be applications where it could be advantageous for the strip to be hollow (less material required, lighter in weight, easier to bond if 3-piece, lower potential for thermal shock) and the present invention contemplates hollow strips.] Extrusion is a closely controlled and repeatable process, suitable for volume production of high quality electric heating elements in silicon carbide.
As the extruded material must be plastic, in order to extrude, then it is possible to change its shape by bending or forming after extrusion has taken place, but before drying and firing. Consideration has been given to bending or forming conventional rods or tubes from which silicon carbide elements normally may be produced, but there is a major disadvantage inherent in this procedure: Bending the shape extends the length of the exterior circumference of the bend, and reduces the length of the interior circumference. Consequently, material on the outside of the curve is stretched, reducing its density, and material on the inside of the face is compressed, increasing the density or crumpling the material.
With substantially laminar heating sections the thickness of the cross section can be made rather small, thus minimising the difference in circumference between the inner and outer lengths of the curve, and thus minimising changes in the material density, and any distortion or disruption of the extruded material. Advantageously, by bending only out of the plane of the strip (and not bending in the plane of the strip) distortion or disruption of the extruded material can be minimised.
For test purposes the applicant has made silicon carbide heating elements by extrusion having cross sections of 5 mm thickness and 45 mm width (aspect ratio 9:1) and 3 mm thickness and 36 mm width (aspect ratio 12:1).
Once formed, the strip shaped elements can be subject to any of the normal processing steps for silicon carbide heating elements—e.g. impregnation, glazing, metallisation of terminals.
In the present invention a strip-form silicon carbide heating element is provided having a higher radiating surface area to volume ratio than a conventional tubular element.
Number | Date | Country | Kind |
---|---|---|---|
0316658.4 | Jul 2003 | GB | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/GB2004/003106 | 7/16/2004 | WO | 00 | 1/10/2006 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2005/009081 | 1/27/2005 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
650234 | Fitzgerald | May 1900 | A |
2431326 | Heyroth | Nov 1947 | A |
2546142 | Watson | Mar 1951 | A |
3094679 | O'Connor et al. | Jun 1963 | A |
3859501 | Matys | Jan 1975 | A |
3875477 | Fredriksson et al. | Apr 1975 | A |
3964943 | Andersen | Jun 1976 | A |
4272639 | Beck | Jun 1981 | A |
4555358 | Matsushita et al. | Nov 1985 | A |
5965051 | Hirayama et al. | Oct 1999 | A |
6090733 | Otsuki et al. | Jul 2000 | A |
6214755 | Otsuki et al. | Apr 2001 | B1 |
6250127 | Polese et al. | Jun 2001 | B1 |
20060061020 | Wynn | Mar 2006 | A1 |
Number | Date | Country |
---|---|---|
1264787 | Aug 2000 | CN |
11 24 166 | Feb 1962 | DE |
0301457 | Oct 1983 | DE |
301457 | Oct 1983 | DE |
1124166 | Jul 2005 | DE |
1109423 | Jun 2001 | EP |
513728 | Oct 1939 | GB |
989502 | Apr 1965 | GB |
1222887 | Feb 1971 | GB |
1222887 | Feb 1971 | GB |
1279478 | Jun 1972 | GB |
1423136 | Jan 1976 | GB |
1459252 | Dec 1976 | GB |
1 497 871 | Jan 1978 | GB |
1497871 | Jan 1978 | GB |
54-87950 | Jul 1979 | JP |
540087950 | Jul 1979 | JP |
1100888 | Apr 1989 | JP |
4-81934 | Jul 1992 | JP |
4230985 | Aug 1992 | JP |
5315056 | Nov 1993 | JP |
08-219648 | Aug 1996 | JP |
9-213462 | Aug 1997 | JP |
090213462 | Aug 1997 | JP |
9255428 | Sep 1997 | JP |
10302940 | Nov 1998 | JP |
2000048936 | Feb 2000 | JP |
2001-77183 | Mar 2001 | JP |
2001-181047 | Jul 2001 | JP |
2001-257056 | Sep 2001 | JP |
2002-203662 | Jul 2002 | JP |
2002338366 | Nov 2002 | JP |
2003073168 | Mar 2003 | JP |
2003277929 | Oct 2003 | JP |
2003327478 | Nov 2003 | JP |
2005149973 | Jun 2005 | JP |
1043007 | Sep 1983 | SU |
WO 9512093 | May 1995 | WO |
WO 03075613 | Sep 2003 | WO |
Number | Date | Country | |
---|---|---|---|
20060198420 A1 | Sep 2006 | US |