Silver halide color photographic light-sensitive material comprising a solid particle dispersion of a spectral sensitizing dye, and having a total coating wt of Ag less than 4 G/M.sup.2

FIELD OF THE INVENTION
This invention relates to a silver halide color photographic light-sensitive material and, particularly, to a silver halide color photographic light-sensitive material excellent in preservability and processability, that is a satisfactorily silver-saving color photographic light-sensitive material.
BACKGROUND OF THE INVENTION
The recent technical progress of a silver halide color photographic light-sensitive materials (hereinafter sometimes referred to as a `color light-sensitive material` or simply a `light-sensitive material`) has been remarkable. It is the matter of course on the one hand that the improvements of photographic characteristics such as sensitivity and image-quality have been required as heretofore, and on the other hand that every product has recently been required further to have a global environmental aptitude from the viewpoints of a resource-saving, an energy-saving and environmental issues.
For the saving of resources, a light-sensitive material has been demanded to save a coating weight of silver as much as possible, from the viewpoint for making effective use of a valuable silver resource as a raw material of silver halide grains applicable to a light-sensitive material. However, in a low silver-containing light-sensitive material, it has been difficult to save a silver content drastically, because the drastic saving thereof results in deterioration in image-qualities, particularly a graininess, and it also induces lowering of a contrast gradation and a color density, which are necessary for photographic characteristics.
Generally, when reducing an silver coating weight from a color light-sensitive material, there have been some instances where a coupler amount is increased in or a highly developable silver halide is introduced into a light-sensitive material so as to enhance a color density. Each of these measures is rather unfavorable for a processing stability of a light-sensitive material. Particularly, in such a processing system as a mini-lab that has recently been on the rise, the demands from a mini-lab for the processing stability of a light-sensitive material have been particularly getting increased more than ever, because a rapid and low-replenishing process has been the main process.
From the viewpoint of a quality control, the essential factors include not only variations in sensitivity, and image-quality produced by a processing fluctuations, but also a characteristic change produced during a period from the delivery of the light-sensitive material to the development process (so-called shelf-life). According to the studies performed by the present inventors, it has become clear that an ordinary negative type light-sensitive material for picture-taking use is hardly affected by the environmental conditions when the silver coating weight of the light-sensitive material is not less than 4.5 g/m.sup.2, but some kind of storage stabilities are seriously affected by the environmental conditions when the silver coating weight thereof is not more than 4.5 g/m.sup.2 so as to deteriorate the photographic characteristics thereof.
On the other hand, it has been well-known to spectrally sensitize a silver halide emulsion applicable to a color light-sensitive material. Most of the spectral sensitizing dyes used for the spectral sensitization are insoluble in water. It is generally known in the art to dissolve a sensitizing dye in a solvent and then to add the solution to a silver halide emulsion.
As for the solvents for a sensitizing dye, particularly, a water-miscible organic solvent has so far been used. For example, alcohol, ketone, nitrile and alkoxy alcohol have been used for. The typical examples thereof include methanol, ethanol, n-propyl alcohol, isopropyl alcohol, ethylene glycol, propylene glycol, 1,3-propane-diol, acetone, acetonitrile, 2-methoxy-ethanol and 2-ethoxy-ethanol.
There is a widely known technique in which a surfactant is used for dissolving a sensitizing dye. Such a surfactant as mentioned above include, for example, an anionic type surfactant, a cationic type surfactant, a nonionic type surfactant and an amphoteric type surfactant.
However, when making use of a conventionally ordinary sensitizing technique is applied to a silver halide emulsion having a relatively small silver content, it is not satisfactorily cope with a shelf-life, a processing stability and so forth. Therefore, an improvement thereof has been demanded so far.
A technique for mechanically dispersing an organic dye in an aqueous medium is known in Japanese Patent Publication Open to Public Inspection (hereinafter referred to as JP OPI Publication) No. 3-288842/1991. However, this technique is to prevent an organic dye from diffusing in a photographic light-sensitive material. It is only a dispersion-addition technique and the purpose of making use of this technique is quite different from the purpose of making a spectrally sensitizing dye adsorbed uniformly and effectively to the surfaces of silver halide grains.
Accordingly, the present inventors have variously studied on low silver coverage light-sensitive materials capable of contributing the saving of resources so as to provide a light-sensitive material excellent in shelf-life and processing stability. As the results, they have discovered that such a light-sensitive material as mentioned above can be provided by mechanically dispersing a sensitizing dye in a system having no organic solvent nor surfactant and then by adding the resulting dispersion to the light-sensitive material.
SUMMARY OF THE INVENTION
It is an object of the invention to provide a color light-sensitive material excellent in processing stability and storage stability without any deterioration of graininess, and, at the same time, the light-sensitive material has a relatively low coating weight of silver and capable of contributing to the saving of resources.
The above-mentioned object of the invention can be achieved with the following silver halide color photographic light-sensitive material.
A silver halide color photographic light-sensitive material comprising a support bearing a blue-sensitive silver halide emulsion layer, a green-sensitive silver halide emulsion layer and a red-sensitive silver halide emulsion layer and at least one hydrophilic colloidal layers substantially having no light-sensitivity; wherein the total coating amount of silver of the silver halide color photographic light-sensitive material is not more than 4.0 g/m.sup.2 and the photographic sensitivity thereof is not lower than 25 in terms of ISO speed, and a silver halide emulsion contained in at least one of the color-sensitive layers is spectrally sensitized by adding a substantially water-insoluble spectrally sensitizing dye in the form of solid particle dispersion without making use of any organic solvent.
DETAILED DESCRIPTION OF THE INVENTION
A total amount of silver coated on a support is essential for the invention. An amount of silver can be measured in a fluorescent X-ray method. A total coating amount of silver include silver halide and colloidal silver each having substantially no light-sensitivity. In the present invention, a total coating amount of silver coated on a silver halide color photographic light-sensitive material is characteristically not more than 4.0 g/m.sup.2.
Concerning a silver halide color photographic light-sensitive material, such a study as those on how to save a silver coating amount as much as possible has also been progressed by making effective utilization of valuable silver resources.
However, when a silver amount is drastically descreased in a light-sensitive material, there raises such a problem that a color density is lowered, and particularly that a contrast gradation necessary for a picture-taking light-sensitive material is lost, so that the light-sensitive material can hardly be constituted. In a light-sensitive material of the invention, a total amount of silver coated thereon is to be within the range of, preferably, 1.5 to 4.0 g/m.sup.2 and, more preferably, 2.5 to 4.0 g/m.sup.2.
As for a halide composition of silver halide grains useful to be applied to the invention, they have preferably not less than 3 mol % of the silver iodide content of the whole silver halide emulsion layer constituting a light-sensitive material. Therefore, they may have the above-mentioned specific silver iodide content as a light-sensitive material as a whole, provided that silver halide grains contained in some layer may be out of the above-mentioned specific range of the silver iodide content.
In the invention, it is characterized in that a support is provided thereon with at least one each of red-sensitive, green-sensitive and blue-sensitive layers, respectively. Each of the light-sensitive layers may comprise plural layers. Each of the light-sensitive layers may comprise, preferably, one to five layers and, particularly, two or three layers. When the color-sensitive layer comprises plural layers, it is preferred to be comprised of plural layers such as those having substantially the same color-sensitivity, but having the different photographic speeds; e.g., a high-speed layer, a medium-speed layer and a low-speed layer. The expression, `substantially the same color-sensitivity`, herein means that the blue-sensitivity, green-sensitivity or red-sensitivity of the plural layers is the same with each other, provided that the spectral sensitivity shall not be required to be completely the same with each other. The layers are also allowed to have either one of the so-called normal-layer arrangement and a inverted layer arrangement.
It is also allowed to coat a layer substantially having no light-sensitivity between the respective light-sensitive layers.
There is no special limitation to the grain sizes of silver halide applicable to the invention. However, the grain-sizes thereof are to be within the range of, preferably, 0.1 to 3 .mu.m and, particularly, 0.2 to 2 .mu.m, from the viewpoints of an image property and a processability varied by the developability differences produced by grain-sizes, as well as the viewpoint of a graininess. As for the structure of silver halide grains, core/shell type silver halide grains are preferred. The term, a `core/shell type`, herein means that the silver halide composition of a silver halide grain is different between the inside of a grain and the surface thereof.
Furthers, monodisperse grains are preferred. As a whole of silver halide grains contained in each of silver halide emulsion layers, a variation coefficient defined by a ratio S/r of a standard grain-size deviation (S) to an average grain-size (r) is to be, preferably, not higher than 0.4, more preferably, :not higher than 0.33, further, not higher than 0.25 and, particularly, not higher than 0.20.
The term, `an average grain-size (r)`, is herein defined by the following formula 1, provided that the number of grains having a grain-size ri is ni (in the case of cubic silver halide grains, ri is the length of a side and, in the cases of grains having other configurations than a cube, ri is the length of a side converted into a cube having the same volume as that of each grain.). A standard deviation (S) of a grain-size is represented by the following formula 2. ##EQU1##
A monodisperse core/shell type silver halide emulsion applicable to the invention such as those mentioned above can be prepared in the known processes disclosed in JP OPI Publication Nos. 59-177353/1984, 60-138538/1985, 59-52238/1984, 60-143331/1985, 60-35726/1985 and 60-25853/1985.
In the invention, tabular-shaped grains may also be used.
A silver halide emulsion of the invention can be prepared in the manner that the pAg and pH of a liquid phase in which silver halide grains are nucleated and grown up, and the temperature and stirring of the liquid phase are each so controlled as to get into the respective specific patterns; that an addition of a halide such as sodium chloride, potassium bromide and potassium iodide, and an addition of silver nitrate are controlled; and that an emulsion preparation apparatus is used in a double-jet method. Besides, a finely grained emulsion comprising silver halide fine grains having substantially no light-sensitivity and having a grain-size of 0.01 to 0.2 .mu.m may be prepared in the same manner as mentioned above so as to be used in a protective layer and an interlayer.
The expression, `substantially no light-sensitivity`, herein means a sensitivity of not higher than 1/50 of the sensitivity of the lowest sensitive grains contained in a light-sensitive emulsion layer.
For obtaining a wide exposure-latitude in the invention, a plurality of silver halide emulsions each having the different grain-sizes or the different halide compositions may be mixed in the same component layer in any proportions.
As for the blended silver halide grains each having the different grain-sizes, it is preferable to make combination use of silver halide grains having larger grain-size, which have an average grain-size within the range of 0.2 to 2.0 .mu.m, and silver halide grains having smaller average grain-size, which have an average grain-size within the range of 0.05 to 1.0 .mu.m. It is also allowed to make combination use of not less than one kind of silver halide grains having an intermediate average grain-size. It is further preferable that the average grain-size of silver halide grains having larger average grain-size is to be within the range of 1.5 to 40 times as large as the average grain-size of silver halide grains having smaller average grain-size.
In the embodiment of the invention, the photographic sensitivity is not lower than 25 in terms of ISO speed.
The photographic sensitivity of a light-sensitive material used in the invention is determined by the following test method which corresponds to,the test method of ISO speed. (corresponding to JIS K 7614-1981)
(1) Testing Conditions
Tests are carried out in a room conditioned at 20.degree..+-.5.degree. C. and 60.+-.10% relative humidity. Prior to testing, a test sample of a light-sensitive material is allowed to stand for at least 1 hour.
(2) Exposing
1) The relative spectral energy distribution of the standard light at the exposed surface is as follows:
TABLE 1______________________________________Wavelength (nm) Relative Spectral Energy .sup.(1)______________________________________360 2370 8380 14390 23400 45410 57420 63430 62440 81450 93460 97470 98480 101490 97500 100540 102550 103560 100570 97580 98590 90600 93610 94620 92630 88640 89650 86660 86670 89680 85690 75700 77______________________________________ Notes .sup.(1) : shown in values relative to the value at 560 nm which is set a 100.
2) The illumination intensity at the exposed surface is varied using an optical wedge, whose fluctuation in spectral transmission density in the wavelength range of 360 to 700 nm should be, at its every portion, less than 10% for the light below 400 nm and less than 5% for the light above 400 nm.
3) The exposing time is 1/100 second.
(3) Processing
1) Exposed light-sensitive material samples are kept at 20.degree..+-.5.degree. C. and 60.+-.10% relative humidity till these are subjected to processing.
2) Processing is completed within the period ranging from 30 minutes to 6 hours after exposing.
3) Processing is carried out in accordance with Eastman Kodak Company's Processing C-41 described in British Journal of Photography Annual 1988, pp. 196-198.
(4) Densitometry
Densities are expressed in log.sub.10 (.PHI..sub.0 /.PHI.), where .PHI..sub.0 is an illuminating light flux for densitometry and .PHI. is a transmitted light flux at a measured portion. The geometrical requirement in densitometry is that the illuminating light flux is a parallel light flux in normal direction, and the whole light flux transmitted and diffused to a semi-sphere is taken as the transmitted light flux. When measurements are made otherwise, correction must be made by use of a standard density specimen. At a measurement, the emulsion layer side is faced with the light-receiving apparatus side. In carrying out the densitometry, status M densities of blue, green and red are used,, and their spectral characteristics are controlled so as to give the values shown in Tables 1 and 2 as the overall characteristics of a light source used for thermometer, an optical system, an optical filter and a light-receiving apparatus.
TABLE 2______________________________________Status M Density Spectral Characteristics(in logarithms, the peak value is standardized to 5.00)Wavelength nm Blue Green Red______________________________________400 -0.40 -6.29 -55.1410 2.10 -5.23 -52.5420 4.11 -4.17 -49.9430 4.63 -3.11 -47.3440 4.37 -2.05 -44.7450 5.00 -0.99 -42.1460 4.95 0.07 -39.5470 4.74 1.13 -36.9480 4.34 2.19 -34.3490 3.74 3.14 -31.7500 2.99 3.79 -29.1510 1.35 4.25 -26.5520 -0.85 4.61 -23.9530 -3.05 4.85 -21.3540 -5.25 4.98 -18.7550 -7.45 4.98 -16.1560 -9.65 4.80 -13.5570 -11.9 4.44 -10.9580 -14.1 3.90 -8.29590 -16.3 3.15 -5.69600 -18.5 2.22 -3.09610 -20.7 1.05 -0.49620 -22.9 -0.15 2.11630 -25.1 -1.35 4.48640 -27.3 -2.55 5.00650 -2.95 -3.75 4.90660 -31.7 -4.95 4.58670 -33.9 -6.15 4.25680 -36.1 -7.35 3.88690 -38.3 -8.55 3.49700 -4.05 -9.75 3.10710 -42.7 -10.9 2.69720 -44.9 -12.2 2.27730 -47.1 -13.4 1.86740 -49.3 -14.6 1.45750 -51.5 -15.8 1.05______________________________________
(5) Determination of Specific Photographic Sensitivity
Using values measured under the conditions shown in paragraphs (1) to (4), the specific photographic sensitivity is determined by the following procedure:
1) Exposures corresponding to the densities higher than respective minimum densities of blue, green and red by 0.15, which are expressed in lux-sec, are referred to as H.sub.B, H.sub.G and H.sub.R, respectively.
2) Of H.sub.B and H.sub.R, the larger one (one lower in sensitivity) is referred to as H.sub.s.
3) The photographic sensitivity S is calculated using the following equation: ##EQU2##
The invention can be applied to a variety of color photographic light-sensitive materials represented by a color negative film and color positive film each for general use.
In a color photographic light-sensitive material of the invention, total thickness of the whole hydrophilic colloidal layers on the emulsion layer side of the light-sensitive material is, preferably not thicker than 24 .mu.m, more preferably not thicker than 20 .mu.m and, particularly not thicker than 18 .mu.m. The layer swelling speed T.sub.1/2 is preferably not longer than 30 seconds and, more preferably not longer than 20 seconds. A layer thickness means that measured under the conditions at 25.degree. C. and 55%RH (for 2 hours). The swelling speed T.sub.1/2 can be measured in a manner as well-known in the art.
The swelling speed T.sub.1/2 can be controlled by adding a hardener to gelatin as a binder, or by changing an aging condition after coating. A degree of swell is preferable to be within the range of 150 to 400%, and it can be calculated from the maximum swelled layer thickness obtained under the above-mentioned conditions in accordance with a formula: (The maximum swelled layer thickness-Layer thickness) /Layer thickness.
A substantially water-insoluble spectrally sensitizing dye for photographic use, which are applicable to the invention, is added in an aqueous system without making present any organic solvent and/or any surfactant therein in an amount exceeding the solubility thereof and mechanically dispersed in the form of fine solid particles having sizes of not larger than 1 .mu.m.
In contrast to the technique disclosed in the foregoing JP OPI Publication No. 3-288842/1991, the invention is to make a spectrally sensitizing dye for photographic use adsorbed uniformly and effectively. Therefore, the objects and effects of the invention are different from the above-given technique only for dispersing and adding a spectrally sensitizing dye for photographic use.
In the invention, any one of such an organic solvent as the above-mentioned solvents which have conventionally been used so far is not contained substantially. As aforementioned, any surfactant which has so far been used as a dispersing agent is not substantially contained.
In the invention, the expression, `an aqueous system in which any organic solvent and/or surfactant are not present substantially`, herein means water, and means preferably ion-exchange water.
In the invention, a solubility of a spectrally sensitizing dye in water is to be within the range of 2.times.10.sup.-4 to 4.times.10.sup.-2 mols/liter and, preferably, 1.times.10.sup.-3 to 4.times.10.sup.-2 mols/liter.
To be more concrete, when a solubility is lower than the above-mentioned range, a dispersed particle size becomes remarkably larger and ununiform. It was, therefore, found out that a dispersion was precipitated after completing a dispersion, and that a dye adsorption to silver halide was hindered when a dispersion was added to a silver halide emulsion.
When a solubility is higher than the foregoing range, it was found out in the studies made by the present inventors that a dispersion was deteriorated by unnecessarily increasing the viscosity of a dispersion and then by taking babbles in, so that the dispersion could not be performed with a further higher solubility.
In the invention, the term, `a spectral sensitizing dye`, herein means that, when it is adsorbed to silver halide, an electron transfer to the silver halide is performed by a photoexcitation, provided that no organic dye shall not be included.
Any spectral sensitizing dyes may be used in the invention, provided that they have a solubility to water within the range of 2.times.10.sup.-4 to 4.times.10.sup.-2 mols/liter. They include, preferably, a cyanine dye and, more preferably, a cyanine dye having a hydrophilic group such as --SO.sub.3 H and --COOH.
Now, the typical examples thereof and the solubilities thereof in water will be given below; provided, however, that the invention shall not be limited thereto.
__________________________________________________________________________ Solubility in water in terms of mol/liter__________________________________________________________________________S-1 ##STR1## 13.1 .times. 10.sup.-3S-2 ##STR2## 11.0 .times. 10.sup.-3S-3 ##STR3## 8.21 .times. 10.sup.-3S-4 ##STR4## 5.75 .times. 10.sup.-3S-5 ##STR5## 3.69 .times. 10.sup.-3S-6 ##STR6## 1.6 .times. 10.sup.-3S-7 ##STR7## 1.42 .times. 10.sup.-3S-8 ##STR8## 0.89 .times. 10.sup.-3S-9 ##STR9## 0.37 .times. 10.sup.-3 S-10 ##STR10## 0.30 .times. 10.sup.-3 S-11 ##STR11## 1.38 .times. 10.sup.-3 S-12 ##STR12## 3.13 .times. 10.sup.-3 S-13 ##STR13## 2.23 .times. 10.sup.-3__________________________________________________________________________
In the invention, for mechanically pulverizing and dispersing a spectral sensitizing dye in an aqueous solvent, a variety of dispersing apparatuses may effectively be used. Typically, a high-speed stirrer, a ball-mill, a sand-mill, a colloid-mill, an attriter, a ultrasonic dispersing apparatus, and so forth may be used for. Among them, a high-speed stirrer is preferable in the invention.
A high-speed stirring type dispersing apparatus may also have a dissolver equipped with plural impellers on the vertical shaft thereof, or with a multi-shaft dissolver provided with plural vertical shafts. Besides an dissolver, a high-speed stirring type dispersing apparatus having anchor blades is more preferred.
In a typical example of the operations, after putting water into a tank capable of controlling temperatures, a given amount of powdered spectral sensitizing dye is put therein and is then stirred, pulverized and dispersed by a high-speed stirrer under thermal control for a given time. There is no special limitation to a pH and a temperature when mechanically dispersing the spectral sensitizing dye. However, at a low temperature, a desired particle-size cannot be obtained even when dispersed for a long time; and at a high temperature, there may raise such a problem that any desired photographic characteristics cannot be obtained, because a re-cohesion, a decomposition or the like may be occurred, or that the efficiencies of pulverization and dispersion of solid particles may seriously lowered, because the viscosity of a solution system may be lowered. Accordingly, a dispersion temperature is preferable to be within the range of 15 to 50.degree. C. Further, a number of stirring revolution in dispersing operation is preferable to be within the range of 1000 to 6000 rpm, because, at a low number of revolution, it takes a long time to obtain a desired particle-size and, at a high number of revolution, babbles are taken in so as to lower a dispersion efficiency.
The solid fine particles of a spectral sensitizing dye, which are dispersed in the manner of the invention, has an average particle-size of not larger than 1 .mu.m', herein means that a grain-size calculated out of the volumetric average size of spheres equivalent to the solid fine particles. It can be measured by an ordinary method.
The term, a dispersion, mentioned in the invention herein means a suspension of a spectral sensitizing dye. It is preferable to use a suspension solution containing a spectral sensitizing dye in an amount of 0.2% to 5.0% by weight.
A dispersion of spectral sensitizing dye of the invention may be added directly to a silver halide emulsion, or may be added upon diluting it suitably. In the latter case, water is used as a diluting solution.
In the case of constituting a light-sensitive material of the invention, a silver halide emulsion applicable thereto is generally physically ripened and spectrally sensitized. The additives applicable to the above-mentioned processes are given in Research Disclosure Nos. 17643, 18716 and 318119 (hereinafter abbreviated to as RD17643, RD18716 and RD308119).
The pages and paragraphs where the additives are given are shown in the following table.
______________________________________[Additive] [Page of RD308119] [RD17643] [RD18716]______________________________________Chemical sensitizer 996 III-A 23 648Spectral sensitizer 996 IV-A, B, C, D, 23-24 648-9 H, I, JSupersensitizer 996 IV-A-E, J 23-24 648-9Antifoggant 998 VI 24-25 649Stabilizer 998 VI 24-25 649______________________________________
A chemical sensitization of an emulsion applicable to the invention can be carried out by a sulfur sensitization in which a compound containing a sulfur atom capable of reacting with silver ion or an active gelatin are used; a slenium sensitization in which a selenium compound is used; a reduction-sensitization in which a reducible substance is used; a-noble-metal sensitization in which gold or other noble metals are used; and so forth independently or in combination.
In the invention, for example, a chalcogen sensitizer can be used as a chemical sensitizer. Among them, a sulfur sensitizer and a selenium sensitizer are preferably used.
The sulfur sensitizers include, for example, a thiosulfate, allyl thiocarbamide, thiourea, allyl isothiocyanate, cystine, a p-toluene thiosulfonate and rhodanine.
Besides the above, it is also allowed to use such a sulfur sensitizer as given in U.S. Pat. Nos. 1,574,944, 2,410,689, 2,278,947, 2,728,668, 3,501,313 and 3,656,955; West German Patent Laying Open to Public Inspection of Application (OLS) No. 1,422,869; and JP OPI Publication Nos. 56-24937/1981 and 55-45016/1980.
An amount of a sulfur sensitizer to be added may be varied extending over a wide range under various conditions such as a pH, a temperature and a silver halide grain size. As a measure it is preferable to add it in an amount of the order of approximately 10.sup.-7 mols to 10.sup.-1 mols per mol of silver halide used.
A selenium sensitizer applicable thereto include, for example, an aliphatic isocyanate such as allyl isoselenocyanate; a selenourea; a selenide such as selenoselenide and diethyl selenide. The typical examples thereof are given in U.S. Pat. Nos. 1,574,944, 1,602,592 and 1,623,499. It is also allowed to make combination use of a reduction sensitization.
A reducing agent include, for example, stannous chloride, thiourea dioxide, hydrazine and polyamine. It is also allowed to make combination use of a noble-metal compound other than gold, that includes, for example, a palladium compound.
The silver halide grains of an emulsion applicable to the invention are preferable to contain a gold compound.
The gold compounds preferably applicable to the invention may each have a gold oxidation number of either 1 or 3'. Therefore, a variety of gold compounds may be used.
The typical examples of an aurate include potassium chloroaurate, auric trichloride, potassium auric thiocyanate, potassium iodoaurate, tetracyanoauric acid, ammonium aurothiocyanate, pyridyl trichlorogold, gold sulfide and gold selenide.
A gold compound may be so used as to sensitize silver halide grains, or may also be so used as not substantially contribute to any sensitization.
An amount of a gold compound to be added may be varied according to various conditions. The amount thereof to be added is within the range of 10.sup.-8 mols to 10.sup.-1 mols per mol of silver halide used and, preferably, 10.sup.-7 mols to 10.sup.-2 mols.
These compounds may be added at any points of time such as at the point of time when forming silver halide grains, when carrying out a physical ripening treatment, when carrying out a chemical ripening treatment and after completing a chemical ripening treatment.
The known additives for photographic use each applicable to the invention are given in the foregoing Research Disclosure.
Now, the pages and paragraphs where the additives are given will be shown below.
__________________________________________________________________________[Item] [Pages of RD308119] [RD17643] [RD18716]__________________________________________________________________________Color-stain preventive 1002 VII-I 25 650Dye-image stabilizer 1001 VII-J 25whitening agent 998 V 24UV absorbent 1003 VIII-C, 25-26 XIIICLight absorbent 1003 VIII 25-26Light scattering agent 1003 VIIIFilter dye 1003 VIII 25-26Binder 1003 IX 26 651Antistatic agent 1006 XIII 27 650Layer hardener 1004 X 26 651Plasticizer 1006 XII 27 650Lubricant 1006 XII 27 650Activator.Coating aid 1005 XI 26-27 650Matting agent 1007 XVIDeveloping agent 1011 XXB(contained in a light-sensitive material)__________________________________________________________________________
For preventing photographic characteristics from any deterioration produced by formaldehyde gas, it is preferable to add the following compound to a light-sensitive material; a compound capable of fixing formaldehyde upon making reaction with the formaldehyde, of which is described in U.S. Pat. Nos. 4,411,987 and 4,435,503.
A variety of color couplers may be used in the invention. The typical examples thereof are given in the patents described in the foregoing Research Disclosure (RD) No. 17643, VII-C to G.
The preferable yellow couplers include, for example, those described in U.S. Pat. Nos. 3,933,051, 4,022,620, 4,326,024, 4,401,752 and 4,248,961; JP Examined Publication No. 58-10739/1983; British Patent Nos. 1,425,020 and 1,476,760; U.S. Pat. Nos. 3,973,968, 4,314,023 and 4,511,649; and European Pat. No. 279,473A.
The preferable magenta couplers include, for example, a compounds of the 5-pyrazolone type and the pyrazoloazole type, and the particularly preferable include, for example, those given in U.S. Pat. Nos. 4,310,619 and 4,351,897; European Patent. No. 73,636; U.S. Pat. Nos. 3,061,432 and 3,725,067; U.S. Pat. Nos. 3,061,432 and 3,725,067; Research Disclosure No. 24220 (June, 1984); JP OPI Publication No. 60-33552/1985; Research Disclosure No. 24230 (June, 1984); JP OPI Publication Nos. 60-43659/1985, 61-72238/1986, 60-35730/1985, 55-118034/1980 and 60-185951/1985; U.S. Pat. Nos. 4,500,630, 4,540,654 and 4,556,630; and International Pat. Publication No. WO88/04795.
The cyan couplers include, for example, those of the phenol type and those of the naphthol type and, preferably, those given in U.S. Pat. Nos. 4,502,212, 4,146,396, 4,228,233, 4,296,200, 2,369,929, 2,801,171, 1,772,162, 2,895,826, 3,772,002, 3,758,308, 4,334,011 and 4,327,173; West German Patent (OLS) No. 3,329,729; European Pat. Nos. 121,365A and 249,453A; U.S. Pat. Nos. 3,446,622, 4,333,999, 4,775,616, 4,451,559, 4,427,767, 4,690,889, 4,254,212 and 4,296,199; and JP OPI Publication Nos. 61-42658/1986.
Colored couplers for compensating the unnecessary absorption of a color dye include, preferably, those given in Research Disclosure No. 17643, VII-G; U.S. Pat. No. 4,163,670; JP Examined Publication No. 57-39413/1982; U.S. Pat. Nos. 4,004,929 and 4,138,258; and British Patent No. 1,146,368. It is also preferable to make use of a coupler described in U.S. Pat. No. 4,774,181 capable of compensating the unnecessary absorption of a color dye by a fluorescent dye released in a coupling reaction; and a coupler having a dyeprecursor group as an eliminating group capable of forming a dye upon making reaction with a developing agent, of which described in U.S. Pat. No. 4,777,120.
Couplers comprising a color dye having a suitable diffusibility include, preferably, those given in U.S. Pat. No. 4,366,237; British Patent No. 2,125,570; European Patent No. 96,570; and West German Patent (OLS) No. 3,234,533.
The typical examples of a polymerized dye-forming coupler are given in U.S. Pat. Nos. 3,451,820, 4,080,211, 4,367,282, 4,409,320 and 4,576,910; and British Patent No. 2,102,173.
A coupler capable of releasing a photographically useful residual group upon making a coupling reaction may also preferably be used in the invention. DIR couplers each capable of releasing a development inhibitor include, preferably, those given in the patent indicated in the foregoing RD 17643, VII-F; JP OPI Publication Nos. 57-151944/1982, 57-154234/1982, 60-184248/1985 and 63-37346/1988; and U.S. Pat. Nos. 4,248,962 and 4,782,012.
Couplers capable of releasing imagewise a nucleating agent or a development accelerator in the course of a development process include, preferably, those given in British Patent Nos. 2,097,140 and 2,131,188; and JP OPI Publication No. 59-157638/1984 and 59-170840/1984.
The other couplers applicable to the invention than the above include, for example, competing couplers given in U.S. Pat. No. 4,130,427; polyequivalent couplers given in U.S. Pat. Nos. 4,283,427, 4,338,393 and 4,310,618; DIR redox compound releasable couplers, DIR coupler releasable couplers, DIR coupler releasable redox compound or DIR redox releasable redox compound, each given in JP OPI Publication Nos. 60-185950/1985 and 62-24252/1987; couplers capable of releasing a dye recolored after being eliminated, each given in European Patent No. 173,302A; bleach-accelerator releasable couplers given in RD Nos. 11449 and 24241 and JP OPI Publication No. 61-201247/1986; ligand releasable couplers given in U.S. Pat. No. 4,553,477; couplers capable of releasing a leuco dye given in JP OPI Publication No. 63-75747/1988; and couplers capable of releasing a fluorescent dye, given in U.S. Pat. No. 4,774,181.
Besides the above, a variety of couplers may be used in the invention. The typical examples thereof are given in the following RDs. The pages and paragraphs thereof will be given below.
______________________________________[Item] [Pages of RD308119] [RD17643]______________________________________Yellow coupler 1001 VII-D VII C-GMagenta coupler 1001 VII-D VII C-GCyan coupler 1001 VII-D VII C-GColored coupler 1002 VII-G VII GDIR coupler 1001 VII-F VII FBAR coupler 1002 VII-Fother useful group- 1001 VII-Freleasing coupler______________________________________
The additives applicable to the invention can be added in such a dispersion method as described in RD308119, XIV.
In the invention, it is allowed to use such a support as described in the foregoing RD17643, p. 28, RD18716, pp. 647-8, and RD308119, XIX.
To a light-sensitive material of the invention, it is allowed to provide such an auxiliary layers as a filter layer and an interlayer each described in the foregoing RD308119, VII-K.
With a light-sensitive material of the invention, the pH of the uppermost surface of the photographic component layer thereof is to be within the range of 5.0 to 7.0 and, preferably, 5.5 to 6.5. Such a pH as mentioned above may be measured in the method described in JP OPI Publication No. 61-245153/1986.
Supports suitably applicable to the invention are given in, for example, the foregoing RD No. 17643, p. 28 and, ibid., No. 18716, from the right column on p. 647 to the left column on p. 648.
The typical supports applicable to the invention include paper laminated with polyethylene or the like, polyethylene terephthalate film, baryta paper and cellulose triacetate film. The thickness of a support applicable thereto is ordinarily within the range of 50 to 200 .mu.m.
When making use of a light-sensitive material of the invention in the rolled form, it is preferable to take the form of putting it in a cartridge. The most popular type of the cartridges is that of the 135 format being currently used. Besides, cartridges proposed by the following patents may also be used. (Japanese Utility Model No. 58-67329/1983; JP OPI Publication Nos. 58-181035/1983 and 58-182634/1983; Japanese Utility Model No. 58-195236/1983; U.S. Pat. No. 4,221,479; JP Application Nos. 63-57785/1988, 63-183344/1988 and 63-325638/1988; JP Application Nos. 1-21862/1989, 1-25362/1989, 1-30246/1989, 1-20222/1989, 1-21863/1989, 1-37181/1989, 1-33108/1989, 1-85198/1989, 1-172595/1989, 1-172594/1989 and 1-172593/1989; and U.S. Pat. Nos. 4,846,418, 4,848,693 and 4,832,275)
The invention can be applied to "a roll film patrone for photographic use and a film camera each of the miniature type" disclosed in JP Application No. 4-16934/1992.
For obtaining a dye-image with the use of a light-sensitive material of the invention, a commonly known development process can be carried out after exposing the light-sensitive material to light.
A light-sensitive material of the invention can be developed in any commonly known process such as those described in the foregoing RD17643, pp. 28-29, RD18716, p. 647, and RD308119, XII.

EXAMPLES
Now, the typical examples of the invention will be detailed below. However, the embodiments of the invention shall not be limited thereto.
In the following every example, an amount of each component added to a silver halide photographic light-sensitive material is indicated by a coated amount expressed in terms of g/m.sup.2, provided, however, that a silver halide coating amount is indicated by an equivalent amount of silver, and a sensitizing dye coating amount is indicated by mol per mol of silver halide contained in the same layer.
Example 1
Sample 101 was prepared to be a multilayered color light-sensitive material comprising a subbed cellulose triacetate film support bearing thereon each of layers having the following compositions.
______________________________________Sample 101______________________________________Layer 1: An antihalation layerBlack colloidal silver 0.15UV absorbent (UV-1) 0.30High boiling solvent (Oil-1) 0.16Gelatin 1.64Layer 2: an interlayerGelatin 0.80Layer 3: A low-speed red-sensitive layerSilver iodobromide emulsion A 0.44Silver iodobromide emulsion C 0.11Sensitizing dye (SD-1) 2.6 .times. 10.sup.-5Sensitizing dye (SD-2) 2.6 .times. 10.sup.-5Sensitizing dye (SD-3) 3.l .times. 10.sup.-4Sensitizing dye (SD-4) 2.3 .times. 10.sup.-5Sensitizing dye (SD-5) 2.8 .times. 10.sup.-4Cyan coupler (C-1) 0.35Colored cyan coupler (CC-1) 0.065Compound (GA-1) 2.0 .times. 10.sup.-3High boiling solvent (Oil-1) 0.33Gelatin 0.73Layer 4: A medium-speed red-sensitive layerSilver iodobromide emulsion C 0.39Sensitizing dye (SD-l) 1.3 .times. 10.sup.-4Sensitizing dye (SD-2) 1.3 .times. 10.sup.-4Sensitizing dye (SD-3) 2.5 .times. 10.sup.-4Sensitizing dye (SD-4) 1.8 .times. 10.sup.-5Cyan coupler (C-1) 0.24Colored cyan coupler (CC-1) 0.040DIR compound (D-1) 0.025Compound (GA-1) 1.0 .times. 10.sup.-3High boiling solvent (Oil-1) 0.30Gelatin 0.59Layer 5: A high-speed red-sensitive layerSilver iodobromide emulsion D 0.91Sensitizing dye (SD-1) 8.5 .times. 10.sup.-5Sensitizing dye (SD-2) 9.1 .times. 10.sup.-5Sensitizing dye (SD-3) 1.7 .times. 10.sup.-4Sensitizing dye (SD-4) 2.3 .times. 10.sup.-5Sensitizing dye (SD-6) 1.1 .times. 10.sup.-5Cyan coupler (C-2) 0.10Colored cyan coupler (CC-1) 0.014DIR compound (D-1) 7.5 .times. 10.sup.-3Compound (GA-1) 1.4 .times. 10.sup.-3High boiling solvent (Oil-1) 0.12Gelatin 0.53Layer 6: An interlayerGelatin 1.14Layer 7: A low-speed green-sensitive layerSilver iodobromide emulsion B 0.32Silver iodobromide emulsion C 0.74Sensitizing dye (SD-7) 5.5 .times. 10.sup.-4Sensitizing dye (SD-1) 5.2 .times. 10.sup.-5Sensitizing dye (SD-1) 4.8 .times. 10.sup.-5Magenta coupler (M-1) 0.15Magenta coupler (M-2) 0.37Colored magenta coupler (CM-1) 0.20DIR compound (D-2) 0.020Compound (GA-1) 4.0 .times. 10.sup.-3High boiling solvent (Oil-2) 0.65Gelatin 1.65Layer 8: A high-speed green-sensitive layerSilver iodobromide emulsion E 0.79Sensitizing dye (SD-8) 1.4 .times. 10.sup.-4Sensitizing dye (SD-9) 1.5 .times. 10.sup.-4Sensitizing dye (SD-10) 1.4 .times. 10.sup.-4Sensitizing dye (SD-12) 7.1 .times. 10.sup.-5Magenta coupler (M-2) 0.065Magenta coupler (M-3) 0.025Colored magenta coupler (CM-2) 0.025DIR compound (D-3) 7.0 .times. 10.sup.-4Compound (GA-1) 1.8 .times. 10.sup.-3High boiling solvent (Oil-2) 0.15Gelatin 0.46Layer 9: A yellow filter layerYellow colloidal silver 0.10Compound (SC-1) 0.14Compound (FS-1) 0.20High boiling solvent (oil-2) 0.18Gelatin 1.20Layer 10: A low-speed blue-sensitive layerSilver iodobromide emulsion B 0.27Silver iodobromide emulsion C 0.32Sensitizing dye (SD-11) 5.4 .times. 10.sup.-4Sensitizing dye (SD-12) 2.0 .times. 10.sup.- 4Sensitizing dye (SD-6) 6.5 .times. 10.sup.-5Yellow coupler (Y-1) 0.62Yellow coupler (Y-2) 0.31Compound (GA-1) 4.5 .times. 10.sup.-3High boiling solvent (Oil-2) 0.20Gelatin 1.27Layer 11: A high-speed blue-sensitive layerSilver iodobromide emulsion E 0.66Sensitizing dye (SD-11) 2.8 .times. 10.sup.-4Sensitizing dye (SD-12) 1.1 .times. 10.sup.-4Sensitizing dye (SD-6) 1.l .times. 10.sup.-5Yellow coupler (Y-1) 0.10Compound (GA-1) 2.0 .times. 10.sup.-3High boiling solvent (Oil-2) 0.04Gelatin 0.57Layer 12: Protective layer 1Silver iododbromide emulsion (having 0.30an average grain-size of 0.04 .mu.m and asilver iodide content of 4.0 mol %)UV absorbent (UV-2) 0.030UV absorbent (UV-3) 0.015UV absorbent (UV-4) 0.015UV absorbent (UV-5) 0.015UV absorbent (UV-6) 0.10Compound (FS-1) 0.25High boiling solvent (Oil-1) 0.07High boiling solvent (Oil-3) 0.07Gelatin 1.04Layer 13: Protective layer 2Alkali-soluble matting agent (having 0.15an average particle size of 2 .mu.m)Polymethyl methacrylate (having an 0.04average particle size of 3 .mu.m)Lubricant (WAX-1) 0.04Gelatin 0.55______________________________________
Besides the above-given compositions, there added coating-aid Su-1, dispersing agent Su-2, a viscosity controller, hardeners H-1 and H-2, stabilizer ST-1, antifoggant AF-1, dyes AI-1 and AI-2, two kinds of AF-2 having the molecular weights of 10,000 for one and 20,000 for the other, and antiseptics DI-1, respectively.
The emulsions applied to the emulsions were as follows. The average grain-sizes thereof were indicated by the grain-sizes converted into the diameters of the spheres having the same volumes of the emulsion grain-sizes, respectively. Each of the emulsions was subjected to the optimum gold-sulfur sensitization.
__________________________________________________________________________ Average AgI content Average grain- Variation Ratio of diameterEmulsion name (in mol %) size (in .mu.m) coeffcient Crystal form to thickness__________________________________________________________________________Emulsion A 2.0 0.27 0.14 Normal 1 tetradecahedronEmulsion B 2.0 0.30 0.17 Normal 1 tetradecahedronEmulsion C 8.0 0.38 0.18 Twinned 1.5 octahedronEmulsion D 8.0 0.55 0.15 Twinned 1.5 octahedronEmulsion E 8.0 0.65 0.18 Twinned 1.5 octahedron__________________________________________________________________________C-1 ##STR14##C-2 ##STR15##M-1 ##STR16##M-2 ##STR17##M-3 ##STR18##Y-1 ##STR19##Y-2 ##STR20##CC-1 ##STR21##CM-1 ##STR22##CM-2 ##STR23##D-1 ##STR24##D-2 ##STR25##D-3 ##STR26##Oil-1 ##STR27##Oil-2 ##STR28##Oil-3 ##STR29##GA-1 ##STR30##SC-1 ##STR31##FS-1 ##STR32##UV absorbent ##STR33## (1) (2) (3)UV-1 C.sub.12 H.sub.25 CH.sub.3 HUV-2 H (t)C.sub.4 H.sub.9 HUV-3 (t)C.sub.4 H.sub.9 (t)C.sub.4 H.sub.9 HUV-4 (t)C.sub.4 H.sub.9 CH.sub.3 ClUV-5 (t)C.sub.4 H.sub. 9 (t)C.sub.4 H.sub.9 ClUV-6 ##STR34##SD-1 ##STR35##SD-2 ##STR36##SD-3 ##STR37##SD-4 ##STR38##SD-5 ##STR39##SD-6 ##STR40##SD-7 ##STR41##SD-8 ##STR42##SD-9 ##STR43##SD-10 ##STR44##SD-11 ##STR45##SD-12 ##STR46##H-1 ##STR47##H-2(CH.sub.2CHSO.sub.2 CH.sub.2).sub.2 OAI-1 ##STR48##AI-2 ##STR49##WAX-1 ##STR50##SU-1 ##STR51##SU-2 ##STR52##ST-1 ##STR53##AF-1 ##STR54##AF-2 ##STR55##DI-1 ##STR56## Samples 101 through 110 were each prepared by changing the mannerof adding a spectral sensitizing dye(s) that was to be added whencarrying out a spectral sensitization, or by changing the silver amountswhich were to be coated on each of the red, green and bluelight-sensitive layers, as shown in Table 3. The pH values of theuppermost surfaces of the photographic component layers of every samplewere each adjusted to be 5.9. In the table, the manner in which the
a: A solution prepared by dissolving 10 g of the dye in 2 kg of methanol at 27.degree. C. was added to a silver halide emulsion.
b: A dispersion prepared by dispersing the dye (10 g)
in water (490 g) in the form of solid particles having an average size of 0.2 .mu.m was added to a silver halide emulsion.
TABLE 3__________________________________________________________________________ Sensi- Total tizing Emulsion Emulsion Emulsion Emulsion Emulsion Emulsion Emulsion coating dye & Ag & Ag & Ag & Ag & Ag & Ag & Ag amount of adding amt. of amt. of amt. of amt. of amt. of amt. of amt. of silver ISOSample No. manner Layer 3 Layer 4 Layer 5 Layer 7 Layer 8 Layer 10 Layer 11 (g/m.sup.2) speed__________________________________________________________________________101 a A 0.44 C 0.39 D 0.91 B 0.32 E 0.79 B 0.27 F 0.66 5.50 110(Comparison) C 0.11 C 0.74 C 0.32102 a A 0.37 C 0.33 D 0.76 B 0.27 E 0.67 B 0.23 F 0.56 4.70 108(Comparison) C 0.092 C 0.62 C 0.27103 a A 0.33 C 0.29 D 0.68 B 0.24 E 0.57 B 0.20 F 0.48 4.20 107(Comparison) C 0.082 C 0.54 C 0.24104 b A 0.33 C 0.29 D 0.68 B 0.24 E 0.57 B 0.20 F 0.48 4.20 109(Comparison) C 0.082 C 0.54 C 0.24105 a A 0.29 C 0.26 D 0.56 B 0.21 E 0.45 B 0.18 F 0.38 3.65 100(Comparison) C 0.073 C 0.49 C 0.21106 b A 0.29 C 0.26 D 0.56 B 0.21 E 0.45 B 0.18 F 0.38 3.65 105(Invention) C 0.073 C 0.49 C 0.21107 a A 0.22 C 0.20 D 0.47 B 0.16 E 0.38 B 0.13 F 0.32 3.00 90(Comparison) C 0.055 C 0.36 C 0.16108 b A 0.22 C 0.20 D 0.47 B 0.16 E 0.38 B 0.13 F 0.32 3.00 94(Invention) C 0.055 C 0.36 C 0.16109 a A 0.17 C 0.15 D 0.36 B 0.12 E 0.28 B 0.097 F 0.24 2.40 78(Comparison) C 0.042 C 0.27 C 0.12110 b A 0.17 C 0.15 D 0.36 B 0.12 E 0.28 B 0.097 F 0.24 2.40 81(Invention) C 0.042 C 0.27 C 0.12__________________________________________________________________________ *Value includes nonlight-sensitive silver halide grains and colloidal silver grains each contained in a noncolor-sensitive layer.
The resulting Samples No. 101 through No. 110 were each exposed to white light through a wedge and then developed in the following processing A and B. Thereafter, the RMS values and ISO speeds thereof were each measured.
The RMS values were indicated by the following manner. A density of the minimum density plus 1.0 of each sample was scanned by making use of a microdensitometer having an aperture scanning area of 1800 .mu.m.sup.2 (with a slit width of 10 .mu.m and a slit length of 180 .mu.m) under green light through a Wratten filter manufactured by Eastman Kodak Co., and the standard deviation of the resulting density variations of not less than 1000 sampled pieces subjected to the density measurements were so multiplied by 1000 as to indicate the RMS values, respectively.
The RMS values were each indicated by a value relative to that of Sample No. 101 that was regarded as a value of 100. The smaller the value was, the better the graininess was. The results thereof will be shown in Table 2.
______________________________________Processing AStep Time Temperature______________________________________1. Color developing 3 min. 15 sec. 38.0 .+-. 0.1.degree. C.2. Bleaching 6 min. 30 sec. 38.0 .+-. 3.0.degree. C.3. Washing 3 min. 15 sec. 24.degree. C. to 41.degree. C.4. Fixing 6 min. 30 sec. 38.0 .+-. 3.0.degree. C.5. washing 3 min. 15 sec. 24.degree. C. to 41.degree. C.6. Stabilizing 3 min. 15 sec. 38.0 .+-. 3.0.degree. C.7. Drying .ltoreq.50.degree. C.______________________________________
In each of the processing steps, the compositions of the processing solutions used therein were as follows.
______________________________________<Color developing solution>4-amino-3-methyl-N-ethyl-N-(.beta.-hydroxyethyl)- 4.75 ganiline sulfateSodium sulfite anhydride 4.25 gHydroxylamine.1/2 sulfate 2.00 gPotassium carbonate anhydride 37.5 gSodium bromide 1.30 gTrisodium nitrilotriacetate (monohydrate) 2.50 gPotassium hydroxide 1.00 gAdd water to make 1 literAdjust pH to be 10.1<Bleaching solution>iron ammonium ethylenediamine tetraacetate 100.0 gDiammonium ethylenediamine tetraacetate 10.0 gAmmonium bromide 150.0 gGlacial acetic acid 10.0 gAdd water to make 1 literAdjust pH with aqueous ammonia to be 6.0<Fixing solution>Ammonium thiosulfate 175.0 gSodium sulfite anhydride 8.5 gSodium metasulfite 2.3 gAdd water to make 1 literAdjust pH with acetic acid to be 6.0<Stabilizing solution>Formalin (in an aqueous 37% solution) 1.5 ccKonidux (manufactured by Konica Corp.) 7.5 ccAdd water to make 1 liter______________________________________Processing B Replenishing*Step Time Temperature amount______________________________________Color developing 3 min. 15 sec. 38 .+-. 0.3.degree. C. 700 mlBleaching 45 sec. 38 .+-. 2.0.degree. C. 150 mlFixing 1 min. 30 sec. 38 .+-. 2.0.degree. C. 830 mlStabilizing 60 sec. 38 .+-. 5.0.degree. C. 830 mlDrying 1 min. 58 .+-. 5.0.degree. C. --______________________________________ *Replenishing amounts were each a value per m.sup.2 of a subject lightsensitive material.
The color developing solution, bleaching solution, fixing solution, stabilizing solution and the replenishing solutions thereof were as follows. Color developing solution]
______________________________________[Color developing solution]Water 800 mlPotassium carbonate 30 gSodium hydrogen carbonate 2.5 gPotassium sulfite 3.0 gSodium bromide 1.3 gPotassium iodide 1.2 mgHydroxylamine sulfate 2.5 gSodium chloride 0.6 g4-amino-3-methyl-N-ethyl-N-(.beta.- 4.5 ghydroxylethyl)aniline sulfateDiethylene triamine pentaacetic acid 3.0 gPotassium hydroxide 1.2 gAdd water to make 1 literAdjust pH with potassium hydroxide or 10.06a 20% sulfuric acid to be[Replenishing solution for color developing solution]Water 800 mlPotassium carbonate 35 gSodium hydrogen carbonate 3 gPotassium sulfite 5 gSodium bromide 0.4 gHydroxyl amine sulfate 3.1 g4-amino-3-methyl-N-ethyl-N-(.beta.- 6.3 ghydroxylethyl)aniline sulfatePotassium hydroxide 2 gDiethylene triamine pentaacetic acid 3.0 gAdd water to make 1 literAdjust pH with potassium hydroxide or 10.1820% sulfuric acid to be[Bleaching solution]Water 700 mlIron (III) ammonium 1,3- 125 gdiaminopropane tetraacetateEthylenediamine tetraacetic acid 2 gSodium nitrate 40 gAmmonium bromide 150 gGlacial acetic acid 40 gAdd water to make 1 literAdjust pH with aqueous ammonia or 4.4glacial acetic acid to be[Replenishing solution for bleaching solution]Water 700 mlIron (III) ammonium 1,3- 175 gdiaminopropane tetraacetateEthylenediamine tetraacetic acid 2 gSodium nitrate 50 gAmmonium bromide 200 gGlacial acetic acid 56 gAdjust pH with aqueous ammonia or 4.0glacial acetic acid to beAnd then add water to make 1 liter[Fixing solution]Water 800 mlAmmonium thiocyanate 120 gAmmonium thiosulfate 150 gSodium sulfite 15 gEthylenediamine tetraacetic acid 2 gAdjust pH with aqueous ammonia or 6.2glacial acetic acid to beAnd then add water to make 1 liter[Replenishing solution for fixing solution]Water 800 mlAmmonium thiocyanate 150 gAmmonium thiosulfate 180 gSodium sulfite 20 gEthylenediamine tetraacetic acid 2 gAdjust PH with aqueous ammonia or 6.5glacial acetic acid to beAnd then add water to make 1 liter[Stabilizing solution and the replenishing solution thereof]Water 900 ml ##STR57## 2.0 gDimethylol urea 0.5 gHexamethylene tetramine 0.2 g1,2-benzisothiazoline-3-one 0.1 gSiloxane (L-77 manufactured by UCC) 0.1 gAqueous ammonia 0.5 mlAdd water to make 1 literAdjust pH with aqueous ammonia or 8.550% sulfuric acid to be______________________________________
TABLE 4______________________________________ RMS value RMS valueSample No. (Processing A) (Processing B)______________________________________101 (Comparison) 100 100102 (Comparison) 107 108103 (Comparison) 115 114104 (Comparison) 110 110105 (Comparison) 120 122106 (Invention) 102 100107 (Comparison) 133 128108 (Invention) 103 103109 (Comparison) 144 147110 (Invention) 108 107______________________________________
From the results of Table 4, it is shown that there was almost no deterioration of the graininess of the green-sensitive layers of the samples of the invention in which the silver amounts of the light-sensitive materials were remarkably reduced, and also that the same results were obtained from the blue-sensitive and red-sensitive layers.
Example 2
For evaluating the processability, samples No. 101 through No. 110 prepared in Example 1 were each exposed wedgewise to white light and, in both cases when the foregoing processing B was carried out and when processing C in which the time for carrying out the bleaching step was shortened by one half was carried out, the residual silver amounts (silver retention) produced by a desilvering failure was measured.
When a value of the residual silver amount is not higher than 5 .mu.g/cm.sup.2, the level thereof may raise almost no problem. The results thereof will be shown in Table 5.
TABLE 5______________________________________ Residual silverSample No. amount, .mu.g/cm.sup.2______________________________________101 (Comparison) 10102 (Comparison) 8103 (Comparison) 7104 (Comparison) 7105 (Comparison) 6106 (Invention) 4107 (Comparison) 5108 (Invention) 3109 (Comparison) 4110 (Invention) 2______________________________________
From the results of Table 5, it was shown that the samples of the invention were excellent in processability, particularly in bleachability.
Example 3
For evaluating the preservability, a forced aging tests was carried out. After aging samples No. 101 through No. 110 under the following conditions (a) and (b), each of the samples was exposed wedgewise to white light and was then developed by the foregoing processing A. The density variation of the fog density of the green-sensitive layer of each sample (.DELTA.Fog) was measured between the samples preserved under conditions (b) and (a), and the results thereof were shown in Table 4.
Condition (a): A sample was preserved at 23.degree. C. and 55%RH for one day, and was then refrigerated; and
Condition (b): A sample was preserved under the high-temperature and high-humidity conditions at 40.degree. C. and 80%RH for 7 days.
TABLE 6______________________________________ .DELTA.Fog of green-Sample No. sensitivity______________________________________101 (Comparison) 0.16102 (Comparison) 0.14103 (Comparison) 0.14104 (Comparison) 0.11105 (Comparison) 0.11106 (Invention) 0.06107 (Comparison) 0.08108 (Invention) 0.05109 (Comparison) 0.07110 (Invention) 0.04______________________________________
From the results of Table 6, it was shown that the samples of the invention were excellent in storage stability. The same results were obtained from the blue-sensitive layer and the red-sensitive layer.
Example 4
Processing D were carried out in the same manner as in Example 1, except that 4-amino-3-methyl-N-ethyl-N-(.beta.-hydroxyethyl)aniline sulfate used in Processing B was replaced by 4-amino-3-methyl-N-ethyl-N-(.beta.-methylsulfonyl ethyl)aniline sulfate in the same mols. In the same manner as in Example 1, the RMS values were evaluated. In the same manner as in Example 2, the residual silver amounts were measured. And, in the same manner as in Example 3, the storage stabilities were evaluated. Resultingly, the effects of the invention were obtained.

Number	Name	Date
4474872	Onishi et al.	Oct 1984
4683193	Ihama et al.	Jul 1987
4837140	Ikeda et al.	Jun 1989
4952485	Shibahara et al.	Aug 1990
5057405	Shiba et al.	Oct 1991

Number	Date	Country
423693	Apr 1991	EPX
3246826	Jun 1983	DEX

Silver halide color photographic light-sensitive material comprising a solid particle dispersion of a spectral sensitizing dye, and having a total coating wt of Ag less than 4 G/M.sup.2

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (5)

Foreign Referenced Citations (2)