Patent Application
20160265140
The present invention relates to a single crystal substrate, a manufacturing method for the single crystal substrate, a manufacturing method for a single crystal substrate with a multilayer film, and an element manufacturing method.
A nitride semiconductor represented by gallium nitride (GaN) has a wide band gap and is capable of blue light emission, and hence the nitride semiconductor is widely used in a light emitting diode (LED), a semiconductor laser (LD), and the like. In recent years, an effort to further increase the luminous efficiency and luminance has been actively made.
The structure of a typical nitride semiconductor light emitting element has a double hetero structure in which, on a sapphire substrate, a buffer layer made of GaN, an n-type contact layer made of n-type GaN, an n-type cladding layer made of n-type AlGaN, an active layer made of n-type InGaN, a p-type cladding layer made of p-type AlGaN, and a p-type contact layer made of p-type GaN are stacked in this order. The active layer contains In of a single quantum well (SQW) structure having only a well layer made of InxGa1−xN (0≦X≦1) or a multi-quantum well (MQW) structure having the well layer made of InxGa1−xN (0≦X≦1) and a barrier layer made of InyGa1−yN (0≦y≦1, y≦x) (see Patent Literature 1).
It is known that, when the above-mentioned multilayer film is formed on the sapphire substrate, warpage occurs in the sapphire substrate after the film formation due to differences in thermal expansion coefficient and lattice constant between the multilayer film and sapphire. For example, Non Patent Literature 1 discloses the result of a study in which an AlN buffer layer and a GaN layer are epitaxially grown on a sapphire substrate to determine how a thermal stress generated by the film formation is relieved depending on the film thickness of the GaN layer. Non Patent Literature 1 reveals that the warpage of the substrate is increased as the film thickness is increased, and interface defects, microcracks, dislocation, or macrocracks occur correspondingly to the increase, and accordingly the stress is relieved.
In addition,
As has been described above, it is known that the warpage of the sapphire substrate significantly changes through a series of film formation steps, and the quality of the nitride semiconductor film and the uniformity of the emission wavelength are thereby affected. Note that, in reality, the warpage shape and the warpage amount of the sapphire substrate are often set so that the substrate curvature becomes substantially 0 in the InGaN-based active layer by utilizing a difference in thermal expansion coefficient from that of the substrate. With the background described above, in order to control the shape and the warpage amount of the sapphire substrate, various polishing technologies are studied (see Patent Literature 2 and the like).
On the other hand, a technology is known in which, when a light emitting element obtained by stacking nitride semiconductor on a sapphire substrate is divided, a pulsed laser is concentrated onto the internal portion of the sapphire substrate having a thickness of about 80 μm to 90 μm to form a reformed region corresponding to a line for division of the light emitting element (Patent Literature 3). The technology disclosed in Patent Literature 3 is a method of processing the sapphire substrate capable of suppressing a reduction in the luminance of the light emitting element even when the substrate is divided into the individual light emitting elements by applying a laser beam to the sapphire substrate, and an object of the technology is the division of the light emitting element.
[PTL 1] JP 3250438 B
[PTL 2] JP 2006-347776 A
[PTL 3] JP 2008-6492 A
[NPL 1] Jpn. J. Appl. Phys. Vol. 32, (1993), pp. 1528-1533
[NPL 2] J. Cryst. Growth. Vol. 272, Issues 1-4, (2004), pp. 94-99
As has been described above, when, in order to produce various elements such as the light emitting element, the multilayer film in accordance with the element structure is formed on a single crystal substrate such as the sapphire substrate, the substrate after the film formation (single crystal substrate with a multilayer film) is usually warped. On the other hand, in the manufacturing of the element, various subsequent steps are usually further performed on the single crystal substrate with a multilayer film. However, when the subsequent steps are performed in a state in which the substrate with a multilayer film is warped, this has led to variations in quality and a reduction in yield of the element.
For example, when a patterning process is performed on the multilayer film in the subsequent step, the following problem occurs. That is, when the patterning process is performed on the multilayer film, a resist formed on the multilayer film is exposed by using a photomask. At this time, the single crystal substrate with a multilayer film is in a warped state. Therefore, when the focal point of light irradiated for the exposure is set on the surface of the multilayer film positioned at the central portion of the single crystal substrate, the surface of the multilayer film positioned in the vicinity of the end portion of the single crystal substrate becomes out of focus. In this case, variations in exposure occur in the surface of the multilayer film, which lead to variations in quality and a reduction in yield of the element manufactured by performing the subsequent steps.
In addition, in the subsequent step, when the surface of the single crystal substrate with a multilayer film opposite to the surface having the multilayer film formed thereon is to be polished (back lapping process), the surface of the single crystal substrate with a multilayer film having the multilayer film formed thereon needs to be bonded and fixed to a flat polishing board. However, in this case, when the single crystal substrate with a multilayer film is warped, in order to flatten the surface to be subjected to the back lapping process, it is necessary for the bonding process to apply a large pressure to the single crystal substrate with a multilayer film at the time of the bonding. However, as the warpage becomes larger, a larger pressure needs to be applied. As a result, a crack becomes likely to occur in the single crystal substrate with a multilayer film, and the yield is thereby reduced. In order to avoid the occurrence of the above-mentioned problem, it can be conceived to use a thicker single crystal substrate. However, in this method, a polishing amount required for the back lapping process is increased and a polishing time period is prolonged, and hence productivity is lowered and the method lacks practicality.
On the other hand, in a case where the above-mentioned single crystal substrate with a multilayer film is manufactured, in general, the multilayer film is formed by using a substantially flat single crystal substrate with almost no warpage. When the multilayer film is formed on one surface of the single crystal substrate, a stress balance between regions on both sides of a line bisecting the single crystal substrate in a thickness direction thereof is lost by an internal stress resulting from the multilayer film. As a result, it can be said that, when the formation of the multilayer film is completed, the single crystal substrate is warped. In view of the above-mentioned circumstances, it is desirable that a substrate warped in advance be used as the single crystal substrate to be used in manufacturing the single crystal substrate with a multilayer film so that the warpage resulting from the formation of the multilayer film is corrected at the time point when the formation of the multilayer film is ended.
In addition, the above-mentioned warpage occurs at the stage of the film formation step of forming the multilayer film on the single crystal substrate. When fluctuations in warpage behavior of the single crystal substrate during the film formation step are sharp, variations in film thickness and/or film quality occur in each layer constituting the multilayer film. The variations in film thickness and/or film quality have caused variations in quality and a reduction in yield of the above-mentioned various elements.
The present invention has been made in view of the above-mentioned circumstances, and an object thereof is to provide a single crystal substrate capable of correcting warpage resulting from the formation of a multilayer film, a manufacturing method for the single crystal substrate, a manufacturing method for a single crystal substrate with a multilayer film using the single crystal substrate, and an element manufacturing method using the manufacturing method for a single crystal substrate with a multilayer film.
The above-mentioned object is attained by the present invention as follows.
Specifically, according to the present invention, there is provided a single crystal substrate, including a heat-denatured layer provided in one of two regions including a first region and a second region obtained by bisecting the single crystal substrate in a thickness direction of the single crystal substrate, in which the single crystal substrate is warped convexly toward a side of a surface of the one of the two regions provided with the heat-denatured layer.
Further, in a single crystal substrate according to an embodiment of the present invention, the one of the two regions provided with the heat-denatured layer is preferably the first region.
Further, in a single crystal substrate according to another embodiment of the present invention, the one of the two regions provided with the heat-denatured layer is preferably the second region.
Further, in a single crystal substrate according to still another embodiment of the present invention, when a relative position of the heat-denatured layer in the thickness direction of the single crystal substrate is assumed to be 0% at a surface on a side of the first region and 100% at a surface on a side of the second region, the heat-denatured layer is preferably provided in a range of 5% or more and less than 50% in the thickness direction of the single crystal substrate.
Further, in a single crystal substrate according to still another embodiment of the present invention, when a relative position of the heat-denatured layer in the thickness direction of the single crystal substrate is assumed to be 0% at a surface on a side of the first region and 100% at a surface on a side of the second region, the heat-denatured layer is preferably provided in a range of more than 50% and 95% or less in the thickness direction of the single crystal substrate.
Further, in a single crystal substrate according to still another embodiment of the present invention, the heat-denatured layer is preferably formed by laser irradiation.
Further, in a single crystal substrate according to still another embodiment of the present invention, the heat-denatured layer is preferably provided in parallel to both surfaces of the single crystal substrate.
Further, in a single crystal substrate according to still another embodiment of the present invention, in a planar direction of the single crystal substrate, the heat-denatured layer is preferably provided to have at least one pattern shape selected from the following shapes:
i) a shape in which a plurality of polygons identical in shape and size are regularly disposed;
ii) a shape in which a plurality of circles or ellipses identical in shape and size are regularly disposed;
iii) a concentric shape;
iv) a shape formed so as to be substantially point-symmetric with respect to a center point of the single crystal substrate;
v) a shape formed so as to be substantially linearly-symmetric with respect to a straight line passing through the center point of the single crystal substrate;
vi) a stripe shape; and
vii) a spiral shape.
Further, in a single crystal substrate according to still another embodiment of the present invention, the shape in which the plurality of polygons identical in shape and size are regularly disposed is preferably a lattice shape.
Further, in a single crystal substrate according to still another embodiment of the present invention, the lattice shape is preferably formed of a pattern in which a pitch between lines constituting the pattern is in a range of 50 μm to 2,000 μm.
Further, in a single crystal substrate according to still another embodiment of the present invention, the single crystal substrate preferably has a curvature in a range of 200 km−1 or less.
Further, in a single crystal substrate according to still another embodiment of the present invention, a material of the single crystal substrate is preferably sapphire.
Further, in a single crystal substrate according to still another embodiment of the present invention, the single crystal substrate preferably has a diameter of 50 mm or more and 300 mm or less.
Further, in a single crystal substrate according to still another embodiment of the present invention, the single crystal substrate preferably has a thickness of 0.05 mm or more and 5.0 mm or less.
Further, according to the present invention, there is provided a manufacturing method for a single crystal substrate, including performing at least a heat-denatured layer formation step in which a heat-denatured layer is formed in one of two regions including a first region and a second region obtained by bisecting a single crystal substrate in a thickness direction of the single crystal substrate, the heat-denatured layer being formed by irradiating a laser from a side of one surface of the single crystal substrate before a laser irradiation process, thereby manufacturing the single crystal substrate which is warped convexly toward a side of a surface of the one of the two regions provided with the heat-denatured layer.
Further, in a manufacturing method for a single crystal substrate according to an embodiment of the present invention, the region in which the heat-denatured layer is formed is preferably the first region.
Further, in a manufacturing method for a single crystal substrate according to another embodiment of the present invention, it is preferred to irradiate the laser to the single crystal substrate from a surface of the single crystal substrate on a side of the first region.
Further, in a manufacturing method for a single crystal substrate according to still another embodiment of the present invention, the region in which the heat-denatured layer is formed is preferably the second region.
Further, in a manufacturing method for a single crystal substrate according to still another embodiment of the present invention, it is preferred to irradiate of the laser to the single crystal substrate from a surface of the single crystal substrate on a side of the second region.
Further, in a manufacturing method for a single crystal substrate according to still another embodiment of the present invention, it is preferred to perform the laser irradiation so as to satisfy at least one of irradiation conditions A and B described below.
Further, according to the present invention, there is provided a manufacturing method for a single crystal substrate with a multilayer film, the single crystal substrate including a heat-denatured layer provided in one of two regions including a first region and a second region obtained by bisecting the single crystal substrate in a thickness direction of the single crystal substrate, the single crystal substrate being warped convexly toward a side of a surface of the one of the two regions provided with the heat-denatured layer, the manufacturing method including performing at least a multilayer film formation step in which a multilayer film including two or more layers is formed on a surface of the single crystal substrate on a side of the second region.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to an embodiment of the present invention, the region in which the heat-denatured layer is formed is preferably the first region.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to another embodiment of the present invention, it is preferred to form the heat-denatured layer, when a relative position of the heat-denatured layer in the thickness direction of the single crystal substrate is assumed to be 0% at a surface on a side of the first region and 100% at a surface on a side of the second region, so as to be positioned in a range of 5% or more and less than 50% in the thickness direction of the single crystal substrate.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, the region in which the heat-denatured layer is formed is preferably the second region.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to form the heat-denatured layer, when a relative position of the heat-denatured layer in the thickness direction of the single crystal substrate is assumed to be 0% at a surface on a side of the first region and 100% at a surface on a side of the second region, so as to be positioned in a range of more than 50% and 95% or less in the thickness direction of the single crystal substrate.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to perform at least a heat-denatured layer formation step in which the heat-denatured layer is formed in the first region of the two regions including the first region and the second region obtained by bisecting the single crystal substrate in the thickness direction of the single crystal substrate, the heat-denatured layer being formed by irradiating a laser from a side of one surface of the single crystal substrate, thereby producing the single crystal substrate which is warped convexly toward the side of the surface of the first region, and to thereafter perform the multilayer film formation step on the single crystal substrate.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to irradiate the laser to the single crystal substrate from the surface of the single crystal substrate on the side of the first region.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to perform at least a heat-denatured layer formation step in which the heat-denatured layer is formed in the second region of the two regions including the first region and the second region obtained by bisecting the single crystal substrate in the thickness direction of the single crystal substrate, the heat-denatured layer is formed in the first region by irradiating a laser from a side of one surface of the single crystal substrate, thereby producing the single crystal substrate which is convexly warped toward the side of the surface of the second region, and to thereafter perform the multilayer film formation step on the single crystal substrate.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to irradiate of the laser to the single crystal substrate from a surface of the single crystal substrate on a side of the second region.
In a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to perform the laser irradiation so as to satisfy at least one of irradiation conditions A and B described below.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to form the heat-denatured layer so as to be in parallel to the multilayer film.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to form, in a planar direction of the single crystal substrate, the heat-denatured layer so as to have at least one pattern shape selected from the following shapes:
i) a shape in which a plurality of polygons identical in shape and size are regularly disposed;
ii) a shape in which a plurality of circles or ellipses identical in shape and size are regularly disposed;
iii) a concentric shape;
iv) a shape formed so as to be substantially point-symmetric with respect to a center point of the single crystal substrate;
v) a shape formed so as to be substantially linearly-symmetric with respect to a straight line passing through the center point of the single crystal substrate;
vi) a stripe shape; and
vii) a spiral shape.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, the shape in which the plurality of polygons identical in shape and size are regularly disposed is preferably a lattice shape.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, it is preferred to form the lattice shape into a pattern in which a pitch between lines constituting the pattern is in a range of 50 μm to 2,000 μm.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, the single crystal substrate provided with the heat-denatured layer before the formation of the multilayer film preferably has a curvature in a range of 200 km−1 or less.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, a material of the single crystal substrate is preferably sapphire.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, the single crystal substrate preferably has a diameter of 50 mm or more and 300 mm or less.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to still another embodiment of the present invention, the single crystal substrate preferably has a thickness of 0.05 mm or more and 5.0 mm or less.
Further, in a manufacturing method for a single crystal substrate with a multilayer film according to another embodiment of the present invention, at least one of the two or more layers constituting the multilayer film is preferably a nitride semiconductor crystal layer.
Further, according to the present invention, there is provided an element manufacturing method, including: performing at least a multilayer film formation step in which a multilayer film including two or more layers is formed on a surface of a single crystal substrate on a side of a second region, thereby manufacturing a single crystal substrate with a multilayer film, the single crystal substrate including a heat-denatured layer provided in one of two regions including a first region and the second region obtained by bisecting the single crystal substrate in a thickness direction of the single crystal substrate, the single crystal substrate being warped convexly toward a side of a surface of the one of the two regions provided with the heat-denatured layer; and performing at least an element portion formation step of performing at least a patterning process on the multilayer film of the single crystal substrate with a multilayer film to produce an element portion functioning as an element selected from the group consisting of a light emitting element, a photovoltaic element, and a semiconductor element, thereby manufacturing the element including the element portion and the single crystal substrate having a size substantially corresponding to a size of the element portion.
According to the present invention described above, it is possible to provide the single crystal substrate capable of correcting the warpage resulting from the formation of the multilayer film, the manufacturing method for the single crystal substrate, the manufacturing method for the single crystal substrate with a multilayer film using the single crystal substrate, and the element manufacturing method using the manufacturing method for the single crystal substrate with a multilayer film.
[
[
[
[
[
[
[
[
[
[
[
[
[
[
(Single Crystal Substrate, Manufacturing Method for Single Crystal Substrate, and Manufacturing Method for Single Crystal Substrate with Multilayer Film)
A single crystal substrate according to an embodiment of the present invention (hereinafter, simply referred to as “substrate” as needed) has a feature that a heat-denatured layer is provided in one of two regions including a first region and a second region obtained by bisecting the substrate in a thickness direction thereof, and that the substrate is warped convexly toward the side of a surface of the region provided with the heat-denatured layer. In addition, a manufacturing method for a single crystal substrate with a multilayer film according to this embodiment using the single crystal substrate according to this embodiment has a feature that the single crystal substrate with a multilayer film is manufactured by performing at least a multilayer film formation step in which a multilayer film including two or more layers is formed on a surface of the single crystal substrate according to this embodiment on the side of the second region. The region provided with the heat-denatured layer is set to be one of the first region and the second region.
Herein, it is possible to correct the warpage resulting from the formation of the multilayer film in a case where the multilayer film is formed by using the single crystal substrate according to this embodiment. In this case, it is basically desirable that the single crystal substrate with a multilayer film become as flat as possible through the correction of the warpage, but it is sufficient that the degree of the warpage is slightly reduced while the direction of the warpage resulting from the formation of the multilayer film remains unchanged. Alternatively, the warpage resulting from the formation of the multilayer film may be corrected so that the direction of the warpage resulting from the formation of the multilayer film is reversed and the single crystal substrate is warped in the opposite direction. Note that, in a case where the single crystal substrate with a multilayer film becomes substantially flat through the correction of the warpage resulting from the formation of the multilayer film, when the element is produced by performing the subsequent step after the formation of the multilayer film on the single crystal substrate according to this embodiment, it becomes easier to suppress variations in quality or improve the yield of the element than in a case where the element is produced by performing the subsequent step after the formation of the multilayer film on the conventional single crystal substrate.
In the case where the multilayer film is formed by using the single crystal substrate according to this embodiment, the reason why the warpage resulting from the multilayer film can be corrected is that the heat-denatured layer is provided in the first region of the single crystal substrate according to this embodiment, and the multilayer film is formed on the surface on the side of the second region at the time of the formation of the multilayer film.
As has been described above, through formation of the multilayer film on the warped single crystal substrate according to this embodiment so as to cancel out the warpage, it is possible to correct the warpage of the single crystal substrate with a multilayer film resulting from the multilayer film. Note that, from this, it is expected that, even when the single crystal substrate having a curved shape similar to that of the substrate warped by polishing is used instead of the single crystal substrate that is warped by forming the heat-denatured layer, it is possible to achieve the same effect as that described above. However, normal polishing is performed on a flat substrate, and hence it is extremely difficult to produce the single crystal substrate having the curved shape similar to that of the substrate warped by polishing. In addition, when lens polishing is utilized, it is possible to easily obtain the single crystal substrate having the curved shape similar to that of the substrate warped by polishing. However, in this case, a crystal plane exposed on the polished surface varies in the surface of the substrate. On the other hand, in a case where the film formation is performed on the single crystal substrate for the purpose of producing some sort of an element, in general, a crystalline film is epitaxially grown in many cases by utilizing the crystal plane exposed on the surface of the single crystal substrate. In view of the need for the above-mentioned single crystal substrate, it is hardly conceivable, in the first place, to form the multilayer film by using the single crystal substrate curved by the lens polishing, which lacks practicality and flexibility.
In addition, it is also expected that it is possible to obtain the same effect as that described above by, besides the polishing, warping the substrate by forming a composition denatured layer on the surface of the single crystal substrate through ion implantation. However, ion implantation is limited to a region in the vicinity of the substrate surface, and hence the control range of the warpage of the single crystal substrate is expected to be extremely smaller as compared with a case where the heat-denatured layer is provided at an arbitrary position in the first region. In addition to this, ion implantation needs to be performed under a reduced pressure environment, and hence productivity thereof is extremely low. In view of the above-mentioned points, the method using ion implantation seems to extremely lack practicality.
Note that, the “heat-denatured layer” to be formed in the single crystal substrate according to this embodiment refers to a layer formed by locally heating a region in a part of the single crystal substrate. When the heat-denatured layer is formed in one of regions obtained by bisecting the single crystal substrate in the thickness direction, the heat-denatured layer has the action of warping the single crystal substrate so that the surface on the side of the region on which the heat-denatured layer is formed becomes convex.
A formation method for the heat-denatured layer is not particularly limited, but usually there is used a method in which the single crystal substrate is irradiated with a laser. In this case, by multiphoton absorption of atoms present in a region irradiated with the laser, the region is locally heated and some sort of denaturalization such as a change in crystal structure or crystallinity with respect to that in the surrounding region occurs. Accordingly, the heat-denatured layer is formed. That is, it is possible to manufacture the single crystal substrate according to this embodiment that is warped convexly toward the side of the surface of the first region by performing at least a heat-denatured layer formation step in which the heat-denatured layer is formed in the first region of the two regions including the first region and the second region obtained by bisecting the substrate in the thickness direction thereof, the heat-denatured layer being formed by irradiating the laser from the side of one surface of the single crystal substrate before a laser irradiation process. Subsequently, after the heat-denatured layer formation step, a multilayer film formation step is performed. Note that, from the viewpoint of suppressing the absorption loss of laser light, when the heat-denatured layer is formed in the first region, usually, the laser irradiation is preferably performed from the surface on the side of the first region, but the laser irradiation may also be performed from the surface on the side of the second region as needed.
—Laser Irradiation Condition—
Note that, the irradiation of the laser may be performed under any irradiation condition as long as the heat-denatured layer can be formed. However, in general, it is preferred to use a pulsed laser that intermittently emits laser light because the pulsed laser can concentrate energy in a short time width and hence can obtain a high peak output. Thus, the irradiation of the pulsed laser is preferably performed in ranges 1) and 2) described below.
1) laser wavelength: 200 nm to 5,000 nm
2) pulse width: the order of femtoseconds to the order of nanoseconds (1 fs to 1,000 ns)
Herein, the laser wavelength and the pulse width are appropriately selected in consideration of the light transmittance/light absorption performance resulting from the material of the single crystal substrate as the target of the laser irradiation, the size and pattern precision of the heat-denatured layer formed in the single crystal substrate, and a practically usable laser apparatus. However, in the laser irradiation, it is especially preferable to select Irradiation Condition A described below.
Note that, in Irradiation Condition A, the laser having the wavelength shorter than that in Irradiation Condition B is used. As a result, when the laser irradiation is performed under the same conditions except for the laser wavelength and the pulse width, Irradiation Condition A can reduce a laser process time period required to obtain substantially the same level of the effect of correcting the warpage as compared with Irradiation Condition B. In addition, as the laser wavelength to be used, it is suitable to select a wavelength longer than an absorption edge wavelength of the single crystal substrate as the target of the laser irradiation.
Herein, when the single crystal substrate is a sapphire substrate, Irradiation Condition A or B described above can be used. In this case, conditions other than the laser wavelength and the pulse width are preferably selected in ranges described below from the viewpoint of, for example, practicality and mass productivity.
Herein, when the single crystal substrate is an Si substrate, Irradiation Condition B described above can be used. In this case, conditions other than the laser wavelength are preferably selected in ranges described below from the viewpoint of, for example, practicality and mass productivity.
Further, when the single crystal substrate is a GaAs substrate, Irradiation Condition B described above can be used. In this case, conditions other than the laser wavelength are preferably selected in ranges described below from the viewpoint of, for example, practicality and mass productivity.
Further, when the single crystal substrate is a crystal substrate, Irradiation Condition B described above can be used. In this case, conditions other than the laser wavelength are preferably selected in ranges described below from the viewpoint of, for example, practicality and mass productivity.
Note that, Table 1 shows examples of laser irradiation conditions when the heat-denatured layer is formed in each of an Si substrate, a GaAs substrate, and a crystal substrate. When the laser irradiation is performed, the surface of the single crystal substrate on the side to be irradiated with the laser is especially preferably in the state of a mirror plane (surface roughness Ra of approximately 1 nm or less). In order to bring the surface to be irradiated with the laser into the state of the mirror plane, for example, mirror polishing can be performed.
In addition, with provision of the heat-denatured layer in the second region of the single crystal substrate according to this embodiment, fluctuations in warpage behavior of the single crystal substrate occurring during the film formation step of forming the multilayer film on the single crystal substrate are suppressed, and the warpage of the single crystal substrate at an arbitrary film formation stage during the film formation step can be reduced to 0. Consequently, in each layer constituting the multilayer film, the occurrence of variations in film thickness and/or film quality is prevented. Due to the prevention of variations in film thickness and/or film quality, variations in quality and a reduction in yield of various elements are prevented. A method of forming the heat-denatured layer provided in the second region is not particularly limited, but usually, a method in which laser irradiation is performed on the single crystal substrate is used. It is possible to produce a single crystal substrate according to another embodiment of the present invention that is warped convexly toward the side of the surface of the second region by performing at least the heat-denatured layer formation step in which the heat-denatured layer is formed in the second region. After the heat-denatured layer formation step, the multilayer film formation step is performed. Note that, from the viewpoint of suppressing the absorption loss of the laser light, when the heat-denatured layer is formed in the second region, usually, the laser irradiation is preferably performed from the surface on the side of the second region, but the laser irradiation may also be performed from the surface on the side of the first region as needed.
—Specific Example of Heat-Denatured Layer Formation Step—
Next, a specific example of the heat-denatured layer formation step is described with reference to the drawings. Each of
As illustrated in the upper part of
Herein, as one example illustrated in
In addition, as illustrated in the upper part of
Herein, the heat-denatured layer formation step to the second region 10U is also performed in a state in which the single crystal substrate before laser processing 10A is fixed to the sample stage (not shown). Subsequently, from the surface opposite to the side on which the sample stage of the single crystal substrate before laser processing 10A fixed to the sample stage is disposed, the laser is irradiated by the laser irradiation apparatus 30. At this time, the laser is concentrated onto the internal portion of the region corresponding to the second region 10U, and the laser irradiation apparatus 30 and the single crystal substrate before laser processing 10A are moved relative to each other in the horizontal direction. In this manner, the heat-denatured layer 28 is formed. Through appropriate selection of the movement speed of the laser irradiation apparatus 30 relative to the single crystal substrate before laser processing 10A (scanning speed of the sample stage, for example, when the sample stage is movable) and the pulse rate of the laser, it is possible to control the intervals among the individual heat-denatured layers 28A, 28B, 28C, and 28D in the planar direction of the single crystal substrate after laser processing 10B.
—Warpage of Single Crystal Substrate with Multilayer Film after Multilayer Film Formation Step is Performed—
Next, description is given of an example of a warpage state of the single crystal substrate with a multilayer film obtained after forming the multilayer film on the single crystal substrate after laser processing 10B according to this embodiment, which is warped, in contrast to a warpage state of the single crystal substrate with a multilayer film obtained after forming the multilayer film on the conventional substantially flat single crystal substrate before laser processing 10A, which is not warped.
A single crystal substrate with a multilayer film 30A illustrated in
In contrast to this, a single crystal substrate with a multilayer film 30B illustrated in
Further, a single crystal substrate with a multilayer film 30C illustrated in the lower part of
A single crystal substrate with a multilayer film 30C illustrated in the lower part of
As illustrated in
In order to avoid the occurrence of the above-mentioned problem, in the thickness direction of the single crystal substrate after laser processing 10B, the heat-denatured layer 20 is preferably provided in parallel to the multilayer film 40. Note that, in this case, as shown in
Note that, regarding the position of presence of the heat-denatured layer 20 in the thickness direction of the single crystal substrate after laser processing 10B, the individual heat-denatured layers 20A, 20B, 20C, and 20D are preferably present all at the same position, but the individual heat-denatured layers may also be present at different positions. In this case, the individual heat-denatured layers 20A, 20B, 20C, and 20D may be disposed at different positions in the thickness direction of the single crystal substrate after laser processing 10B so that, also in view of the disposition positions of the individual heat-denatured layers 20A, 20B, 20C, and 20D in the planar direction of the substrate, the shape of the single crystal substrate with a multilayer film 30B is not distorted or the effect of correcting the warpage resulting from providing the heat-denatured layer 20 is not significantly reduced. In addition, the length of the heat-denatured layer 20 in the thickness direction of the single crystal substrate after laser processing 10B is determined depending on the spot size, the irradiation energy (laser power/pulse rate), and the pulse width of the laser, and is usually in a range of several micrometers to several tens of micrometers.
In order to avoid the occurrence of the above-mentioned problems, in the planar direction of the single crystal substrate after laser processing 10B, the heat-denatured layer 20 is preferably provided to have the following pattern shapes. That is, it is preferred that, in the planar direction of the single crystal substrate after laser processing 10B, the heat-denatured layer 20 be provided to have at least one pattern shape selected from the following shapes i) to vii). In this case, the warpage of the single crystal substrate with a multilayer film 30B resulting from the multilayer film 40 can be corrected more effectively to suppress the distortion thereof as well.
i) a shape in which a plurality of polygons identical in shape and size are regularly disposed;
ii) a shape in which a plurality of circles or ellipses identical in shape and size are regularly disposed;
iii) a concentric shape;
iv) a shape formed so as to be substantially point-symmetric with respect to a center point of the single crystal substrate;
v) a shape formed so as to be substantially linearly symmetric with respect to a straight line passing through the center point of the single crystal substrate;
vi) a stripe shape; and
vii) a spiral shape.
Note that, among the pattern shapes i) to vii) described above, from the viewpoint that it is possible to more uniformly correct the warpage of the single crystal substrate with a multilayer film 30B resulting from the multilayer film 40 and further reduce the distortion of the shape, the pattern shapes i) to iv) are more preferable.
In addition, when the heat-denatured layer 20 is formed, from the viewpoint that laser scanning, that is, the movement of the laser irradiation apparatus 30 relative to the single crystal substrate before laser processing 10A is relatively simple as compared with other pattern shapes so as to facilitate the laser process, the pattern shape is preferably i) the shape in which the plurality of polygons identical in shape and size are regularly disposed. Further, as i) the shape in which the plurality of polygons identical in shape and size are regularly disposed, a shape in which a plurality of quadrangles identical in shape and size are regularly disposed so that four sides constituting each quadrangle coincide with any one of four sides of an adjacent quadrangle, that is, a lattice shape is especially preferable. In this case, it is only necessary to perform the laser scanning in vertical and lateral directions. Thus, the laser process can be further facilitated, and the designing of the warpage amount control and the shape control of the single crystal substrate with a multilayer film 30B can also be further facilitated.
Herein, the pitch between the lines constituting the pattern forming the lattice shape is preferably in a range of 50 μm to 2,000 μm, and more preferably in a range of 100 μm to 1,000 μm. With the setting of the pitch to 50 μm or more, it is possible to suppress an unnecessary increase in time period required for the laser process and, with the setting of the pitch to 2,000 μm or less, it is possible to more reliably correct the warpage of the single crystal substrate with a multilayer film 30B resulting from the multilayer film 40.
Note that, in the example illustrated in
In addition, in a case where the heat-denatured layer 28 is provided in the second region 10U, in the thickness direction of the single crystal substrate after laser processing 10B, the heat-denatured layer 28 is preferably provided in parallel to the multilayer film 40. Note that, in this case, when the relative position of the heat-denatured layer 28 in the thickness direction of the single crystal substrate after laser processing 10B is assumed to be 0% at the surface on the side of the first region 10D and 100% at the surface on the side of the second region 10U, the heat-denatured layer 28 is preferably provided in a range of more than 50% and 95% or less in the thickness direction of the single crystal substrate after laser processing 10B. Further, the heat-denatured layer 28 is more preferably provided in a range of 80% or more and 95% or less. With provision of the heat-denatured layer 28 in the ranges of values described above, it is possible to reduce the warpage of the single crystal substrate after laser processing 10B at an arbitrary film formation stage during the formation of the multilayer film 40 to 0, and also suppress the deformation of the single crystal substrate with a multilayer film 30A. Note that, in
Note that, regarding the position of presence of the heat-denatured layer 28 in the thickness direction of the single crystal substrate after laser processing 10B, the individual heat-denatured layers 28A, 28B, 28C, and 28D are preferably present all at the same position, but the individual heat-denatured layers may also be present at different positions. In this case, the individual heat-denatured layers 28A, 28B, 28C, and 28D may be disposed at different positions in the thickness direction of the single crystal substrate after laser processing 10B so that, also in view of the disposition positions of the individual heat-denatured layers 28A, 28B, 28C, and 28D, the shape of the single crystal substrate with a multilayer film 30C is not distorted or the effect of providing the heat-denatured layer 28 is not significantly reduced. In addition, the length of the heat-denatured layer 28 in the thickness direction of the single crystal substrate after laser processing 10B is determined depending on the spot size, the irradiation energy (laser power/pulse rate), and the pulse width of the laser, and is usually in a range of several micrometers to several tens of micrometers.
Further, in the planar direction of the single crystal substrate after laser processing 10B, the heat-denatured layer 28 is preferably provided to have at least one pattern shape selected from the following shapes i) to vii) similarly to the heat-denatured layer 20:
i) a shape in which a plurality of polygons identical in shape and size are regularly disposed;
ii) a shape in which a plurality of circles or ellipses identical in shape and size are regularly disposed;
iii) a concentric shape;
iv) a shape formed so as to be substantially point-symmetric with respect to a center point of the single crystal substrate;
v) a shape formed so as to be substantially linearly symmetric with respect to a straight line passing through the center point of the single crystal substrate;
vi) a stripe shape; and
vii) a spiral shape.
Note that, among the pattern shapes i) to vii) described above, from the viewpoint that it is possible to more uniformly correct the warpage of the single crystal substrate with a multilayer film 30C resulting from the multilayer film 40 and further reduce the distortion of the shape, the pattern shapes i) to iv) are more preferable.
In addition, when the heat-denatured layer 28 is formed, from the viewpoint that laser scanning, that is, the movement of the laser irradiation apparatus 30 relative to the single crystal substrate before laser processing 10A is relatively simple as compared with other pattern shapes so as to facilitate the laser process, the pattern shape is preferably i) the shape in which the plurality of polygons identical in shape and size are regularly disposed. Further, as i) the shape in which the plurality of polygons identical in shape and size are regularly disposed, a shape in which a plurality of quadrangles identical in shape and size are regularly disposed so that four sides constituting each quadrangle coincide with any one of four sides of an adjacent quadrangle, that is, a lattice shape is especially preferable. In this case, it is only necessary to perform the laser scanning in vertical and lateral directions. Thus, the laser process can be further facilitated, and the designing of the warpage amount control and the shape control of the single crystal substrate with a multilayer film 30C can also be further facilitated.
Herein, the pitch between the lines constituting the pattern forming the lattice shape is preferably in a range of 50 μm to 2,000 μm, and more preferably in a range of 100 μm to 1,000 μm. With the setting of the pitch to 50 μm or more, it is possible to suppress an unnecessary increase in time period required for the laser process and, with the setting of the pitch to 2,000 μm or less, it is possible to more effectively realize the setting of the warpage of the single crystal substrate after laser processing 10B to 0 at an arbitrary film formation stage during the film formation of the multilayer film 40.
The disposition pattern shape of the heat-denatured layer 28 includes various shapes illustrated in
Note that, through appropriate selection and combination, in accordance with the degree of the warpage resulting from the multilayer film 40, of i) the length of the heat-denatured layer 28 in the thickness direction of the single crystal substrate after laser processing 10B, ii) the disposition position of the heat-denatured layer 28 in the thickness direction of the single crystal substrate after laser processing 10B, and iii) the disposition pattern shape of the heat-denatured layer 28 in the planar direction of the single crystal substrate after laser processing 10B, it is possible to not only correct the warpage resulting from the multilayer film 40 of the single crystal substrate with a multilayer film 30C but also reduce the warpage of the single crystal substrate after laser processing 10B at an arbitrary film formation stage during the formation of the multilayer film to 0.
—Curvature of Single Crystal Substrate after Laser Processing—
On the other hand, as illustrated in the lower part of
Table 2 shows examples of the curvature of the warpage of the single crystal substrate after laser processing and examples of the embodiment in which the curvature of the warpage is 200 km−1 or less. From Table 2, each single crystal substrate before laser processing (before being processed) had a curvature of 10 km−1 or 11 km−1, and had a concave shape. That is, the heat-denatured layer was provided in the first region, the side of the substrate surface of the first region was convex, and the side of the substrate surface of the other region was concave. It was found that, with provision of the heat-denatured layer 20 at a process pitch of 100 μm or more in the single crystal substrate before laser processing (before being processed), it was possible to control the curvature of the single crystal substrate after laser processing (after being processed) to be 200 km−1 or less. In addition, it was found that, even with the same process pitch, through formation of the heat-denatured layer at a position closer to the side of the first region than to the side of the second region in the thickness direction of the single crystal substrate, the curvature of the single crystal substrate was further increased. Further, it was found that, even when the heat-denatured layer was formed at the same position in the thickness direction of the single crystal substrate, the curvature of the single crystal substrate having a smaller process pitch was larger than that of the single crystal substrate having a larger process pitch.
In addition, as illustrated in the middle part of
—Single Crystal Substrate—
As a material constituting the single crystal substrate before laser processing 10A to be used in the production of the single crystal substrate after laser processing 10B, there can be used any known single crystal material capable of forming the heat-denatured layers 20 and 28 by laser irradiation. Examples of the material include sapphire, nitride semiconductor, Si, GaAs, crystal, and SiC. Note that, the single crystal substrate with a multilayer film according to this embodiment uses a single crystal substrate made of a single crystal material. However, even when a substrate made of a polycrystalline material (for example, a quartz substrate) or a substrate made of a non-crystalline material (for example, a glass substrate) is used instead of the above-mentioned substrate, it is also possible to obtain a flat substrate with a multilayer film in which the warpage resulting from the multilayer film is corrected.
In addition, as the single crystal substrate before laser processing 10A, a single crystal substrate having at least one mirror-polished surface is usually used, and a single crystal substrate having both surfaces which are mirror-polished may also be used. In a case where only one surface is mirror-polished, the single crystal substrate after laser processing 10B is usually produced by performing the laser irradiation from the side of this surface, and then the multilayer film 40 is formed after the surface on the side of the second region 10U is mirror-polished. Further, as the single crystal substrate before laser processing 10A to be used in the production of the single crystal substrate after laser processing 10B, from the viewpoint of ease of production and availability of a substrate, there is used a substrate in which no heat-denatured layer is formed by the laser process or no composition denatured layer is formed by ion implantation, and which usually has the warpage amount of approximately 0, that is, is substantially flat, in a state in which no film is formed.
The shape of the single crystal substrate 10 in the planar direction is not particularly limited, and the shape thereof may be, for example, a square or the like. However, from the viewpoint of easy application to the manufacturing lines for various known elements, a circular shape is preferable, and a circular shape provided with an orientation flat plane is especially preferable.
When the single crystal substrate 10 has the circular shape or the circular shape provided with the orientation flat plane, the diameter of the single crystal substrate 10 is preferably 50 mm or more, more preferably 75 mm or more, and further preferably 100 mm or more. In a case where the diameter is set to 50 mm or more, when the single crystal substrate with a multilayer film 30A is produced by forming the multilayer film 40 by using the single crystal substrate before laser processing 10A, as the diameter is increased, a difference in height (warpage amount) is increased between the vicinity of the central portion of the single crystal substrate with a multilayer film 30A and the vicinity of the end portion thereof in the vertical direction when the single crystal substrate with a multilayer film 30A is assumed to be placed on a flat surface. However, when the single crystal substrate with a multilayer film 30B or 30C is produced by forming the multilayer film 40 by using the single crystal substrate after laser processing 10B, it is possible to correct such large warpage and easily reduce the warpage amount, and hence it is possible to reduce an adverse effect on the subsequent step. Note that, the upper limit value of the diameter is not particularly limited but, from the viewpoint of practicality, is preferably 300 mm or less.
In addition, the thickness of the single crystal substrate 10 is preferably 5.0 mm or less, preferably 3.0 mm or less, and more preferably 2.0 mm or less. In a case where the thickness thereof is set to 5.0 mm or less, the thickness is small, and hence the rigidity of the single crystal substrate after laser processing 10B is reduced and the single crystal substrate after laser processing 10B becomes likely to be deformed. In this case, in the single crystal substrate with a multilayer film 30A obtained by forming the multilayer film 40 by using the single crystal substrate before laser processing 10A, the warpage amount becomes likely to be increased. However, in a case where the multilayer film 40 is formed by using the single crystal substrate after laser processing 10B, the warpage amount of the single crystal substrate after laser processing 10B may be adjusted in consideration of an increase in warpage that occurs when the above-mentioned single crystal substrate before laser processing 10A is used. In this manner, the warpage amount of the single crystal substrate with a multilayer film 30B to be produced can be easily controlled to be in the vicinity of 0. Alternatively, the warpage of the single crystal substrate with a multilayer film 30C at an arbitrary film formation stage during the formation of the multilayer film can be set to 0. Therefore, it is possible to reduce an adverse effect on the subsequent step even when the diameter of the single crystal substrate 10 is increased. Further, because of the circumstances described above, when it is necessary in the subsequent step to polish the single crystal substrate after laser processing 10B to a predetermined thickness by polishing on the surface of the side of the first region 10D of the single crystal substrate with a multilayer film 30B or 30C, it is possible to form the multilayer film 40 by using the single crystal substrate after laser processing 10B having a smaller thickness so that a polishing allowance is further reduced in such a range that the adverse effect on the subsequent step is not increased. In this case, it is possible to reduce a time period required for polishing in the subsequent step, to thereby improve productivity in the subsequent step.
The lower limit value of the thickness is not particularly limited but, in view of securing a region where the heat-denatured layer 20 or 28 can be formed, is preferably 0.05 mm or more and preferably 0.1 mm or more. In a case where the single crystal substrate 10 has the circular shape or the circular shape provided with the orientation flat plane, when the diameter is 50 mm or more and 100 mm or less, the thickness is preferably 0.3 mm or more and, when the diameter is more than 100 mm, the thickness is preferably 0.5 mm or more.
—Multilayer Film—
In the description of this application, the “multilayer film” refers to a film including two or more layers. In addition to this, the “multilayer film” means a film in which each layer constituting the multilayer film does not have a stepped portion extending through a film of the uppermost layer formed of continuous layers identical in film thickness in the planar direction of the single crystal substrate. The layer structure of the multilayer film 40, and the film thickness, the material, and the crystallinity/non-crystallinity of each layer constituting the multilayer film 40 are appropriately selected in accordance with the type of an element to be produced by further performing a subsequent process on the single crystal substrate with a multilayer film 30B or 30C manufactured with use of the single crystal substrate 10B according to this embodiment and in accordance with the manufacturing process used when the element is manufactured.
However, at least one of the layers constituting the multilayer film 40 is preferably a crystalline layer. Further, from the viewpoint that epitaxial growth can be caused by using the crystal plane exposed on the film formation surface of the single crystal substrate after laser processing 10B, among the individual layers constituting the multilayer film 40, at least the layer that directly comes into contact with the film formation surface of the single crystal substrate after laser processing 10B is preferably a crystalline layer, and all of the layers constituting the multilayer film 40 may also be crystalline layers. Note that, epitaxial growth includes homoepitaxial growth and heteroepitaxial growth that include the same composition or a mixed crystal. Furthermore, the material of each layer constituting the multilayer film 40 is also appropriately selected in accordance with the element to be produced. However, in view of that the substrate used for manufacturing the single crystal substrate after laser processing 10B is made of an inorganic material such as a sapphire, the material constituting each layer is preferably an inorganic material such as a metal material, a metal oxide material, or an inorganic semiconductor material, and all layers are desirably made of those inorganic materials. However, when the MOCVD method is used as a film formation method, there is a possibility that a minute amount of organic matter of an organic metal origin is mixed into the inorganic material.
Specific examples of each layer constituting the multilayer film 40 may include, as the layer suitable for the manufacturing of elements using various types of nitride semiconductor such as a light emitting element used in a surface emitting laser or the like, a light receiving element used in an optical sensor or a solar cell, and a semiconductor element used in an electronic circuit or the like, for example, GaN-based, AlGaN-based, and InGaN-based nitride semiconductor crystal layers. In this case, as the substrate used for manufacturing the single crystal substrate after laser processing 10B, it is suitable to use the sapphire substrate. In addition, as a specific example of the layer structure of the multilayer film 40, for example, in a case where a light emitting element using the nitride semiconductor is produced as the element, the sapphire substrate in which the heat-denatured layers 20 and 28 are formed can be used as the single crystal substrate after laser processing 10B, and there can be adopted a layer structure in which, from the side of the sapphire substrate, a buffer layer made of GaN, an n-type contact layer made of n-type GaN, an n-type cladding layer made of n-type AlGaN, an active layer made of n-type InGaN, a p-type cladding layer made of p-type AlGaN, and a p-type contact layer made of p-type GaN are laminated in the stated order.
The film thickness of the multilayer film 40 is appropriately selected depending on the element to be produced. In general, as the film thickness of the multilayer film 40 is increased, the warpage amount of the single crystal substrate with a multilayer film 30A, which is obtained by forming the multilayer film 40 on the single crystal substrate before laser processing 10A, is also increased. Conventionally, the effect on variations in element quality and the yield of the element becomes marked. In addition, in this case, a crack becomes likely to occur in the multilayer film 40 due to a brittle fracture resulting from the warpage after the film formation. However, the multilayer film 40 may be formed by using the single crystal substrate after laser processing 10B that is produced so as to have a predetermined warpage amount through the laser irradiation so that the warpage amount of the single crystal substrate with a multilayer film 30B after the formation of the multilayer film 40 can be controlled to be in the vicinity of 0. In this manner, it is possible to more reliably suppress the occurrence of the above-mentioned problem. Note that, the upper limit of the film thickness of the multilayer film 40 is not particularly limited. In addition, the number of layers of the multilayer film may be any number equal to or more than two, and the number of layers can appropriately be selected depending on the type of the element to be produced.
The film formation method for the multilayer film 40 is not particularly limited, and it is possible to use known film formation methods. It is also possible to adopt a different film formation method and/or a different film formation condition for each of the layers constituting the multilayer film 40 to form the film. Examples of the film formation method include a liquid phase deposition method such as a plating method, but it is preferable to use a vapor phase deposition method such as a sputtering method or a chemical vapor deposition (CVD) method. When a semiconductor crystal layer such as a nitride semiconductor crystal layer is formed for producing a light emitting element or the like, it is more preferable to use the vapor phase deposition method such as a metal organic chemical vapor deposition (MOCVD) method, a hydride vapor phase epitaxy (HVPE) method, or a molecular beam epitaxy (MBE) method. Note that, the surface of the single crystal substrate after laser processing 10B on which the multilayer film 40 is formed is especially preferably in the state of the mirror plane (surface roughness Ra of approximately 1 nm or less). In order to bring the surface on which the multilayer film 40 is formed into the state of the mirror plane, for example, mirror polishing can be performed.
—Specific Example of Multilayer Film Formation Step—
Next, as a specific example of a case where the multilayer film 40 is formed, description is made, with reference to the drawings, of a case where the sapphire substrate in which the heat-denatured layers 20 and 28 are formed by the laser irradiation (sapphire substrate after laser processing) is used as the single crystal substrate after laser processing 10B, and the multilayer film 40 is formed on one surface of the sapphire substrate after laser processing by laminating a plurality of nitride semiconductor layers by epitaxial growth.
First, thermal cleaning is performed on a surface on the side of the second region 10U (hereinafter referred to as “film formation surface 52”) of a sapphire substrate after laser processing 50 (single crystal substrate after laser processing 10B) before the start of the film formation (
Next, the warpage behavior of the single crystal substrate 10 in the multilayer film formation step is described.
Note that, the warpage behavior of the sapphire substrate during the multilayer film formation step as shown in
Among three Spectrums representing changes in warpage behavior shown in
In addition, sections indicated as (a) to (e) along the horizontal axis of
Next, the change in the warpage behavior of Spectrum A shown in
Then, in (c) the process of forming the n-GaN layer 62, the temperature of the sapphire substrate before laser processing is increased to about 1,000° C. again, and the n-GaN layer 62 is formed. In this process, the sapphire substrate before laser processing is warped in such a direction that the film formation surface becomes concave due to a difference in lattice constant between gallium nitride and sapphire, and the absolute value of the curvature is slightly increased.
Next, in (d) the process of forming the InGaN-based active layer 64A (64), the temperature of the sapphire substrate before laser processing is reduced to about 700° C. to 800° C., and the InGaN-based active layer 64A (64) is formed. Lastly, in (e) the process of cooling down the sapphire substrate before laser processing on which the multilayer film 70 is formed, the sapphire substrate before laser processing is warped convexly toward the side of the film formation surface due to a difference in thermal expansion coefficient between the multilayer film 70 and the sapphire substrate before laser processing, and the absolute value of the curvature is increased. The state in which the sapphire substrate before laser processing is warped convexly toward the side of the film formation surface is maintained even after the end of the cooling down to the vicinity of room temperature. However, the above-mentioned warpage can be corrected by using the sapphire substrate after laser processing 50 during the formation of the multilayer film 70 and, through optimization of the disposition pattern of the heat-denatured layer 20, the curvature can be set to a value in the vicinity of 0 as shown by Spectrum C. In this case, even when various subsequent steps such as patterning and back lapping processes are performed in order to obtain the light emitting element such as an LED chip, it is possible to reliably suppress variations in quality and a reduction in yield of the light emitting element that result from the warpage.
Herein, when a light emitting element such as an LED chip is manufactured by performing predetermined subsequent processes by using the sapphire substrate after laser processing 50 with the multilayer film 70 illustrated in
However, when the substrate used for the formation of the multilayer film 70 is changed from the conventional sapphire substrate, on which the laser processing is not performed, to the sapphire substrate after laser processing 50, as shown in Spectrums B and C, the curvature in Process (d) becomes less than 0. Therefore, in a case where the multilayer film 70 is formed by using the sapphire substrate after laser processing 50, while there is an advantage that (1) the adverse effect on the subsequent step can be reduced by suppressing the warpage of the sapphire substrate after laser processing 50 provided with the multilayer film 70 after the film formation, there is also a disadvantage that (2) the uniformity of the temperature in the surface of the substrate is reduced by the increase in the absolute value of the curvature in Process (d) and, as a result, the yield of the light emitting element is reduced. However, as one method for eliminating the disadvantage, in Process (d), it is possible to heat the sapphire substrate after laser processing 50 by utilizing a heater having a curved shape corresponding to the direction and the curvature of the warpage of the sapphire substrate after laser processing 50 in Process (d) (for example, see E. Armour et. al., semiconductor TODAY Compounds & Advanced Silicon, Vol. 4, Issue 3, April/May 2009, “LED growth compatibility between 2″, 4″ and 6″ sapphire”). In this case, even when the formation of the multilayer film 70 is performed by using the sapphire substrate after laser processing 50, the above-mentioned advantage can be obtained while the above-mentioned disadvantage is avoided.
In addition, in Process (c), in each of Spectrums A to C, after 4,000 s, the absolute value of the curvature is increased with the lapse of time. Such change is not desirable because variations in the film quality and film thickness are caused in the film thickness direction of the n-GaN layer 62 as the base layer of the InGaN-based active layer 64A (64). In this case, after Process (a) is performed, it is preferable to form the AlN layer instead of performing Process (b). With this, in Process (c), the absolute value of the curvature is increased with the lapse of time, and the curvature can be maintained at a substantially constant level.
Further, a specific example of a case where the heat-denatured layer 28 is formed in the second region 10U and the multilayer film 40 is formed is as illustrated in
Note that, the warpage behavior of the sapphire substrate during the multilayer film formation step as shown in
Among three Spectrums each representing a change in warpage behavior shown in
In addition, sections (a) to (e) shown along the horizontal axis of
Next, the change in warpage behavior of Spectrum A shown in
Then, in (c) the process of forming the n-GaN layer 62, the temperature of the sapphire substrate before laser processing is increased to about 1,000° C. again, and the n-GaN layer 62 is formed. In this process, the sapphire substrate before laser processing is warped concavely with respect to the film formation surface due to a difference in lattice constant between gallium nitride and sapphire, and the absolute value of the warpage amount is slightly increased.
Next, in (d) the process of forming the arbitrary GaN-based barrier layer 64B (64), the temperature of the sapphire substrate before laser processing is increased to about 1,100° C. to 1,200° C., and the GaN-based barrier layer 64B (64) is formed. Then, lastly, in (e) the process of cooling down the sapphire substrate before laser processing on which the multilayer film 70 is formed, the sapphire substrate before laser processing is warped convexly toward the side of the film formation surface due to a difference in thermal expansion coefficient between the multilayer film 70 and the sapphire substrate before laser processing, and the absolute value of the curvature is increased. In addition, the state in which the sapphire substrate before laser processing is warped convexly toward the side of the film formation surface is maintained even after the sapphire substrate before laser processing is cooled down to the vicinity of room temperature and the cooling down is ended.
Herein, in a case where a semiconductor element such as a high electron mobility transistor (HEMT) is manufactured by performing predetermined subsequent processes by using the sapphire substrate after laser processing 50 with the multilayer film 70, the uniformity of the film thickness of the GaN-based barrier layer 64B (64) and of the composition (film quality) in the GaN-based barrier layer 64B (64) influences element performance, and by extension influences the manufacturing yield of the semiconductor element. The uniformity of the film thickness of the GaN-based barrier layer 64B (64) and of the composition in the GaN-based barrier layer 64B (64) is influenced by fluctuations in warpage behavior of the single crystal substrate during the film formation step. Consequently, in (d) the process of forming the GaN-based barrier layer 64B (64) of
When the substrate used for the formation of the multilayer film 70 is changed from the conventional sapphire substrate, on which the laser processing is not performed, to the sapphire substrate 50 having been subjected to the laser processing on the second region thereof, as shown by Spectrums B and C, the warpage amount in Process (d) becomes 0 or becomes close to 0. Therefore, when the multilayer film 70 is formed by using the sapphire substrate after laser processing 50, there is an effect that it is possible to suppress variations in film thickness and/or film quality of the multilayer film 70.
Note that, the AlN layer may be formed instead of performing Process (b) after Process (a) is performed. With the formation of the AlN layer, it is possible to maintain the warpage amount at a substantially constant level in Process (c).
(Element Manufacturing Method)
By performing various subsequent steps on the single crystal substrates with a multilayer film 30B and 30C as exemplified in
In this case, in a manufacturing method for an element using the single crystal substrate with a multilayer film 30B or 30C manufactured by the manufacturing method for a single crystal substrate with a multilayer film according to this embodiment, specifically, by successively performing at least steps (1) to (4) described below, it is possible to produce the element including the element portion and the single crystal substrate having the size substantially corresponding to the element portion.
(1) An element portion formation step of patterning the multilayer film of the single crystal substrate with a multilayer film to form individual element portions.
(2) A polishing step of polishing, at least until the heat-denatured layer formed in the heat-denatured layer formation step is removed, the surface of the single crystal substrate with the element portions on which the element portions are not formed, the single crystal substrate with the element portions having the element portions formed on the one surface thereof.
(3) A line-for-division formation step of applying a laser along a boundary line between the individual element portions from the side of the surface polished in the polishing step to form a line for division.
(4) A division step of applying an external force along the line for division formed in the line-for-division formation step to divide the single crystal substrate with the element portions based on each element portion.
Herein, when (3) the line-for-division formation step and (4) the division step are performed, it is possible to use the technology described in Patent Literature 3.
Note that, when the heat-denatured layer 20 or 28 in the single crystal substrate after laser processing 10B is formed into the lattice pattern, it is theoretically possible to perform the division step by using, after the heat-denatured layer 20 or 28 is polished in the polishing step to such an extent that the heat-denatured layer 20 or 28 is not completely removed, the heat-denatured layer remaining in the single crystal substrate after laser processing 10B as the line for division. However, it is not possible to confirm the positions at which the element portions are present and to perform alignment for the laser irradiation before the multilayer film 40 is individualized into individual element portions. Consequently, in the above-mentioned method in which the heat-denatured layer 20 or 28 functioning also as the line for division is formed before the individual element portions are produced, it is difficult to accurately form the line for division in correspondence to the individual element portions. That is, in the above-mentioned method, the line for division is more prone to be deviated from the boundary line between two adjacent element portions. Thus, the above-mentioned method tends to lack practicality. Consequently, when the division step is performed by using the heat-denatured layer formed by the laser irradiation, it is especially preferable to perform the above-mentioned steps (1) to (4) in this order.
When the line-for-division formation step is performed, as the laser irradiation condition, it is especially desirable to select Irradiation Condition B described above. In the case of Irradiation Condition A in which the laser wavelength is in the ultraviolet region, the laser energy resulting from the laser wavelength is large, and hence the width of the line for division to be formed is large and the width becomes likely to be varied in the length direction of the line. As a result, in the division step, there are cases where it becomes difficult to perform linear and accurate division.
First, by performing the patterning process on the multilayer film 40 formed on the single crystal substrate after laser processing 10B, which is illustrated in the lower part of
The present invention is described hereinbelow by using Examples, but the present invention is not limited only to the following Examples.
(Production of Sample for Evaluation)
By performing the laser irradiation process on the conventional sapphire substrate on which no pre-process had been performed (sapphire substrate before laser processing), the sapphire substrate after laser processing 50 was produced. Next, as illustrated in
—Sapphire Substrate—
As the sapphire substrate before laser processing, a circular sapphire substrate provided with an orientation flat plane (diameter: 4 inches (100 mm), thickness: 650 μm) was used. Note that, the sapphire substrate had both surfaces subjected to mirror-polishing.
—Formation Condition for Heat-Denatured Layer—
First, the sapphire substrate before laser processing was fixed onto a flat sample stage by vacuum suction. In this state, the heat-denatured layer 20 was formed by performing laser irradiation under the following irradiation conditions from the side of the surface (non-film formation surface 54) of the sapphire substrate before laser processing opposite to the surface on which the sample stage was disposed, and the sapphire substrate after laser processing 50 was obtained. Note that, during the laser irradiation, the sapphire substrate before laser processing was fixed onto the sample stage so that the scanning direction of the sample stage in the vertical direction corresponded to the orientation flat plane of the sapphire substrate before laser processing. Subsequently, the sample stage was scanned relative to the laser irradiation apparatus in the vertical and lateral directions, and the heat-denatured layer 20 was formed so as to have the lattice pattern in the planar direction of the sapphire substrate before laser processing. Then, by changing the scanning speed of the sample stage, a sample in which the pitch between lines constituting the lattice pattern was changed was also produced.
—Layer Structure and Film Formation Condition for Multilayer Film—
As illustrated in
(1) Thermal Cleaning After the sapphire substrate was disposed in an MOCVD apparatus, thermal cleaning of the film formation surface was performed for about 120 seconds at a substrate temperature of 1,100° C.
(2) Formation of Low-Temperature Buffer Layer 60
The low-temperature buffer layer 60 (gallium (Ga), nitrogen (N)) was formed to a film thickness of 30 nm at a substrate temperature during the film formation of 530° C. and a film formation rate of 0.16 nm/s.
(3) Formation of n-GaN Layer 62
The n-GaN layer 62 was formed to a film thickness of 3,500 nm at a substrate temperature during the film formation of 1,050° C. and a film formation rate of 2,000 nm/s.
(4) Formation of InGaN-Based Active Layer 64A (64)
The InGaN-based active layer 64A (64) was formed to a film thickness of 408 nm at a substrate temperature during the film formation of 750° C. and a film formation rate of 10 nm/s.
(5) Cooling Down
The sapphire substrate having one surface on which the low-temperature buffer layer 60, the n-GaN layer 62, and the InGaN-based active layer 64A (64) were formed in the stated order was cooled down to the vicinity of room temperature.
(Evaluation Result)
—Evaluation of Warpage Amount and Warpage Direction—
Table 3 shows the result of evaluation of the warpage amounts and the warpage directions, when viewed from the side of the surface on which the multilayer film was to be formed, before and after the laser irradiation before the formation of the multilayer film, and the warpage amounts and the warpage directions, when viewed from the film formation surface side, after the formation of the multilayer film. Note that, Samples 1 and 2 and Comparative Example correspond to Spectrums C, B, and A shown in
As shown in Table 3, in Comparative Example in which the multilayer film 70 was formed by using the sapphire substrate before laser processing, the sapphire substrate was warped convexly toward the side of the film formation surface and the warpage amount was 75 μm. However, in Sample 2 in which the multilayer film 70 was formed by using the sapphire substrate after laser processing, the warpage amount was reduced to 25 μm. In addition, in Sample 1 in which the heat-denatured layer 20 was formed with the pitch between lines set narrower than that of Sample 2, the warpage amount was 0 μm. From these results, it was found that, when the multilayer film 70 was formed by using the sapphire substrate after laser processing 50, it was possible to correct the warpage resulting from the multilayer film 70 and reduce the warpage amount, and even achieve a flat state.
(Production of Sample for Evaluation)
As a sample for evaluation, a sample in which the multilayer film 70 including three layers was formed on one surface of the sapphire substrate 50 similar to that illustrated in
—Sapphire Substrate—
As the sapphire substrate 50, a circular sapphire substrate provided with an orientation flat plane (diameter: 2 inches (50.8 mm), thickness: 430 μm) was used. Note that, the sapphire substrate 50 had one mirror-polished surface, and the multilayer film 70 was formed by using the mirror-polished surface as the film formation surface 52. In addition, the warpage amount of the sapphire substrate 50 under a state in which no film formation processing or laser irradiation processing was performed was in a range of ±10 μm.
—Formation Condition for Heat-Denatured Layer—
The second heat-denatured layer 28 was formed by performing the laser irradiation from the side of the film formation surface 52 under the following irradiation conditions in a state in which the sapphire substrate 50 was disposed on the flat sample stage so that the film formation surface 52 was positioned as the upper surface and in which the sapphire substrate 50 was fixed by vacuum suction. Note that, during the laser irradiation, the sapphire substrate 50 was fixed onto the sample stage so that the scanning direction of the sample stage in the vertical direction corresponded to the orientation flat plane of the sapphire substrate 50. Subsequently, the sample stage was scanned relative to the laser irradiation apparatus in the vertical and lateral directions, and the heat-denatured layer 28 was thereby formed so as to have the lattice pattern in the planar direction of the sapphire substrate 50. Herein, the pitch between lines was changed by changing the scanning speed of the sample stage.
—Layer Structure and Film Formation Condition of Multilayer Film—
The multilayer film 70 including three layers was formed on the film formation surface 52 of the sapphire substrate 50 having the heat-denatured layer 28 formed therein. Specific film formation conditions were as follows, and the processes were performed in the order of (1) to (5) described below.
(1) Thermal Cleaning
After the sapphire substrate 50 was disposed in an MOCVD apparatus, thermal cleaning of the film formation surface 52 was performed for about 120 seconds at a substrate temperature of 1,100° C.
(2) Formation of Low-Temperature Buffer Layer 60
The low-temperature buffer layer 60 was formed to a film thickness of 30 nm at a substrate temperature during the film formation of 530° C. and a film formation rate of 0.16 nm/s.
(3) Formation of n-GaN Layer 62
The n-GaN layer 62 was formed to a film thickness of 3,500 nm at a substrate temperature during the film formation of 1,050° C. and a film formation rate of 2,000 nm/s.
(4) Formation of AlGaN-Based Barrier Layer 64C (GaN-Based Layer 64)
The AlGaN-based barrier layer 64C (64) was formed to a film thickness of 30 nm at a substrate temperature during the film formation of 1,150° C. and a film formation rate of 0.2 nm/s.
(5) Cooling Down
The sapphire substrate 50 having one surface on which the low-temperature buffer layer 60, the n-GaN layer 62, and the AlGaN-based barrier layer 64C (64) were formed in the stated order was cooled down to the vicinity of room temperature.
(Evaluation Result)
—Evaluation of Warpage Amount and Warpage Direction—
Table 4 shows the results of evaluation on the warpage amounts and the warpage directions, when viewed from the side of the film formation surface 52, before and after the laser irradiation before the formation of the multilayer film, on the warpage amount and the warpage direction, when viewed from the film formation surface side, during the formation of the multilayer film, and on the warpage amount and the warpage direction, when viewed from the film formation surface side, after the formation of the multilayer film. In addition,
The above-mentioned processes (1) to (5) were sequentially performed on the side of the film formation surface 52 of the single crystal substrate 50 having the heat-denatured layer 28 formed therein. At this time, it was possible to confirm that, during the film formation step for the AlGaN-based barrier layer 64C (64) indicated by the reference symbol (d) in
In addition, it was possible to confirm that, during the film formation step for the n-GaN layer indicated by the reference symbol (c) in
As shown in Table 5, among three conventional sapphire substrates on which no pre-process was performed (sapphire substrates before laser processing) (Samples 1 to 3), only one sapphire substrate was provided with the heat-denatured layer 20 by performing the laser irradiation process in the first region before the formation of the multilayer film, to thereby produce the sapphire substrate after laser processing of Sample 3. Next, the multilayer film was formed on the sapphire substrates before laser processing of Samples 1 and 2 and the sapphire substrate after laser processing of Sample 3.
On the sapphire substrates before laser processing of Samples 1 and 2, an LT-GaN film and an AlN film was formed, respectively. On the other hand, on the sapphire substrate after laser processing of Sample 3, the AlN film was formed.
(Evaluation Result)
—Evaluation on Warpage Amount and Warpage Direction—
Table 5 shows the results of evaluation on the warpage amounts and the warpage directions, when viewed from the side of the surface on which the multilayer film was to be formed, before and after the laser irradiation before the formation of the AlN film, and on the warpage amount and the warpage direction, when viewed from the film formation surface side, after the formation of the AlN film, as Sample 3 (processed substrate before epitaxial growth+AlN). In addition, as comparative examples, Table 5 shows Sample 1 (STD+LT-GaN) in which the LT-GaN film was formed on the conventional sapphire substrate (sapphire substrate before laser processing) and Sample 2 (STD+AlN) in which the AlN film was formed on the conventional sapphire substrate.
As shown in Table 5, in each of Sample 1 (STD+LT-GaN) and Sample 2 (STD+AlN) in which the laser processing before the film formation was not performed, the sapphire substrate was warped convexly toward the film formation surface side after the film formation, and the warpage amount was 60 μm or 80 μm. However, in Sample 3 (processed substrate before epitaxial growth+AlN) in which the AlN film was formed by using the sapphire substrate after laser processing, the warpage amount was reduced to 10 μm. In particular, it was found that, in spite of the formation of the same AlN film, it was possible to reduce the warpage amount of the sapphire substrate after the film formation to one eighth of that of Sample 2.
The present application is a continuation application of U.S. patent application Ser. No. 13/582,587, filed on Oct. 31, 2012, the entire contents of which are incorporated herein by reference and priority to which is hereby claimed. Application Ser. No. 13/582,587 is the U.S. National stage of application No. PCT/JP2011/055076 filed on Mar. 4, 2011. Priority under 35 U.S.C. §119(a) and 35 U.S.C. §365(b) is hereby claimed from Japanese Application No. 2010-049859, filed Mar. 5, 2010, the disclosure of which are also incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13582587 | Oct 2012 | US |
| Child | 15163717 | US |