SiOx:Si composite articles and methods of making same

Information

  • Patent Grant
  • 7658822
  • Patent Number
    7,658,822
  • Date Filed
    Thursday, August 11, 2005
    18 years ago
  • Date Issued
    Tuesday, February 9, 2010
    14 years ago
Abstract
Article are made from silicon oxide and electrically conductive doped silicon materials that are joined in a protective environment to yield a composite SiOx:Si material that exhibits the properties of SiOx and yet is electrically conductive due to the presence of the Si. Articles from such composite materials find many uses, such as for targets for DC and/or AC sputtering processes to produce silicon oxide thin films for touch-screen application, barrier thin films in LCD displays and optical thin films used in a wide variety of applications.
Description
BACKGROUND OF THE INVENTION

1. Technical Field


This invention relates to articles made of material compositions primarily composed of electrically non-conductive oxide silicon material in combination with fractions of materials that render the overall article electrically conductive.


2. Related Art


One important commercial application for such material compositions is thin film technology. Many architectural, automotive, integrated circuit, flat panel display and optical devices require thin films of oxide silicons (SiOx), such as silicon dioxide (SiO2).


One of the principal methods for producing such thin films is by a physical vapor deposition process known as radio frequency (RF) sputtering. This method utilizes non-conductive silicon dioxide material as the source material for the creation of the silicon dioxide thin film coatings. A high frequency ac-voltage, typically 13.56 MHz is applied capacitively to the target. In one phase, gas ions of the plasma are accelerated toward the target and cause material at the surface of the target to be detached as a result of the bombardment with the gas ions. In the other phase, the charge on the target surface is neutralized with the result that no sputtering occurs during this periodic phase. Although this method produces suitable silicon dioxide thin film coatings, it has the limitations of requiring the use of expensive and complex high frequency power supplies, low deposition rates for the formation of the SiO2 thin film coatings, and inherent limitations on the uniformity of SiO2 coatings that can be created with such method.


Direct current (DC), including pulsed DC, or medium to low frequency alternating current (AC) sputtering processes do not have such limitations. However, DC and AC processes require the use of silicon as the source material for the SiO2 coating. To utilize silicon as the deposition source material, it must be made sufficiently electrically conductive either by doping with a suitable dopant such as boron, or by the addition of small amounts of aluminum or other suitable metals. To use such silicon targets to create SiO2 thin films via DC or AC sputtering also requires that large amounts of oxygen be introduced into the sputtering process. The resultant process is referred to as reactive sputtering. The oxygen reacts with the silicon during the sputtering process to yield SiO2. To create SiO2 films typically requires that O2 gas pressure be 30- 50% of the total gas pressure in the vacuum chamber. This can result in a significant process mismatch in terms of the oxygen requirements, as compared to that required for other sputtered thin films which may be deposited using the same vacuum vessel. The presence of significant levels of O2 in the chamber further slows the rate of deposition through collisions with the sputtered material. In addition, SiO2 films made by DC and AC sputtering from silicon or Si:Al targets generally are not sufficiently dense and crystalline as a result of the characteristics of reactive deposition to render them suitable for many semi-conductor, flat panel and opto-electronics applications. The SiO2 film compositions produced by such reactive processes generally exhibit less useful optical, mechanical and chemical durability properties compared to those produced by RF sputtering of non-conductive SiO2 targets.


SUMMARY OF THE INVENTION

It is an object of the present invention to produce articles from SiOx-based material compositions that include a sufficient amount of silicon to render the composition electrically conductive. The SiOx:Si material compositions of this invention are suitable for any application calling for electrically conductive SiOx-based material. One such use is as a target material for use in DC or AC sputtering processes to produce high quality SiOx thin film coatings with the addition of only small amounts of O2 during the deposition process, since the presence of SiOx in the target material serves as a source of oxygen in the vessel thereby decreasing the amount of oxygen gas that typically needs to be fed into the vessel during reactive sputtering DC or AC processes. This enables the production efficiencies of DC and AC sputtering to be used to produce SiOxcoatings equivalent to those produced by the less efficient and more costly RF sputtering method.


The SiOx:Si material of the invention is composed of the constituent materials of electrically non-conductive SiOx and an amount of Si that has been doped and combined with the SiOx in a manner that physically unites the materials to render the overall SiOx-based composition electrically conductive. In some embodiments, there can be the addition of one or more metals in amounts smaller than that of the Si component. These material compositions, although primarily composed of insulating silicon dioxide, exhibit good electrical conductivity while retaining many of the other intrinsic material properties of the silicon dioxide. Such materials can be fabricated in solid bulk forms such as plates, rods and tubes. In addition these bulk materials can be reduced to powder form with such powders retaining the electrically conductive properties of the bulk material for use alone or with other materials in the formation of various articles of manufacture.


Accordingly, it is an object of the present invention to produce articles from composite SiOx:Si material which, although primarily composed of insulating SiOx material, has good electrical conductivity due to the presence of the Si material. This material may find use in many applications which require the optical, thermal, mechanical, or chemical properties of SiOx but which also require electrical conductivity to be useful. The electronic properties of this material can be adjusted based on the ratio of the constituents of electrically conductive doped Si, SiOx and in some embodiments small fractions of various metals.





BRIEF DESCRIPTION OF THE DRAWINGS

These and other features and advantages of the present invention will become more readily appreciated when considered in connection with the following detailed description and appended drawing, wherein:



FIG. 1 is a schematic illustration of an article made of the Si:SiOx material.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The present invention is directed to the manufacture of articles from composite silicon oxide:silicon (SiOx:Si) material that is rendered conductive by the selection of starting materials and the process by which they are combined to form the composite.


According to the fundamental principals of the present invention, the process starts out with SiOx powder which in and of itself is substantially electrically non-conductive, but which is combined with electrically conductive Si in a manner that protects the Si against substantial oxidation while uniting it to the SiOx material to render the overall composite electrically conductive while preserving the characteristics of each of the SiOx and Si materials.


The Si forms a three-dimensional network or grid through the bulk of the Si:SiOx material that establishes a conductive pathway. These interconnected silicon grains thus exist as a conductive lattice in the presence of the non-conductive SiOx grains which are united to the Si grains to render the overall material conductive while still preserving the desirable optical characteristics of SiOx material.


One approach contemplated by the invention starts out with a blend of SiOx (e.g., SiO2) and conductive Si powders. The blended powder is compacted and fused to form an article which has the properties of being similar to silicon oxide but with low resistivity, and thus they find use in many applications calling for conductive glass articles. For example, one particular usage for such a material is as a sputtering target suitable use in a DC or AC thin film sputtering process.


According to this first presently preferred embodiment of the invention, the conductive silicon component of the powder blend is prepared by crushing and then grinding doped silicon crystal to powder (such as boren p-type doped silicon). As is well known to those skilled in the art, the doping of the silicon material is achieved by adding a suitable n or p dopant to the molten silicon prior to growing the single or poly phase crystal of silicon. The concentration and uniformity of these dopant atoms determine the specific electrical characteristics of the silicon.


The invention contemplates that various approaches can be employed to blend the particles of silicon oxide and conductive silicon and that variations can occur in the size of the particles and the ratio of the silicon oxide to doped silicon particles in order to alter the electrical conductive properties or resistivity of the end product. In the first presently preferred embodiment, the composition of the base silicon oxide powder is greater than 50% by weight, and that of the conductive silicon powder is greater than 10% by weight, with the silicon oxide preferably making up the majority of the powder blend. According to a presently preferred process, the powders may be blended together in a pot using zirconia balls as milling media until the particle size of the blended powder is reduced to less than 5 μm. Once the powder has been sufficiently blended, it is preferably placed in a metal containment unit and then heated under vacuum conditions to eliminate residual moisture. Following heating to drive off the moisture, the containment unit is preferably sealed and then placed in a hot isostatic chamber and then heated to a sufficient temperature and pressure to densify and fuse the silicon oxide and doped silicon particles. For this purpose, the container is preferably one which can withstand the heat and pressure of the hot isostatic-pressing environment, but which flows plastically under the heat and pressure so as to consolidate and densify the powder material contained within the container. Once densified, the resultant fused, densified article of silicon oxide-doped silicon material is removed from the container. The resulting composition is preferably densified to at least 90% of theoretical density, and preferably at least 95% of full theoretical density, and still more preferably greater than 99% of full theoretical density. According to a preferred process, the powder is subjected to hot isostatic pressure (HIP) at temperatures of between 1200 to 1450° C. and under pressures exceeding 20 kpsi. More particularly, the preferred process involves hot isostatic press heating to 1000° C. under vacuum conditions and then gradually applying the pressure to more than 20 kpsi while increasing the temperature to between 1200 to 1350° C. According to a further feature of the invention, the resultant sintered and fused article has a resistivity value of less than 200Ω·cm. Preferably, the article or target has resistivity less than 150106 ·cm and still more preferably below 20Ω·cm and still further more preferably at or below 10Ω·cm. Accordingly, the range of resistivity contemplated by the invention is in the range of about 10Ω·cm or less to about 200Ω·cm.


This material can be prepared by regrinding the sintered SiOx:Si material resulting from the process described above, after which it can be used to form articles by various means such a compacting and sintering in a protective atmosphere that does not oxidize the Si. The SiOx:Si material may alternatively be formed directly in particulate form by a process in which SiOx particles are coated with molten electrically conductive Si in a protective non-oxidizing atmosphere such as argon to cause the Si to substantially cover the SiOx particles while protecting the molten Si against oxidation in the process. The resultant composite particles can be mixed with other such particles and/or blended with an amount of uncoated silicon oxide particles and thereafter sintered to form an article. The amount of the conductive composite particles will be that amount which is needed to achieve the desired electrical conductivity properties. For example, the invention contemplates that enough of the composite particles are present to provide a conductive path through the bulk of the sintered material.


Once the article is prepared, it can be used in a number of different applications, such as a target in a direct current (DC) or low to medium frequency alternating (AC) sputtering process for producing silicon oxide coatings.


The invention contemplates that various manufacturing methods can be used to prepare the material that yield the same desirable characteristics and properties described above. These alternative methods can be used with or without the hot isostatic pressing. Such additional processes include vacuum plasma spraying of the Si material onto the SiOx material in an inert gas atmosphere to preclude oxidizing the Si; vacuum casting (“melt casting”) of the materials to connect Si grains of the blend in the presense of the SiOx grains to yield a conductive network; vacuum hot pressing of the materials in an inert gas atmosphere; and inert gas microwave melting and solidification.


The invention also contemplates various post-treatment methods for rendering the Si conductive in the company of SiO2. In this case the Si is alone in powder form or united with the SiOx in reground powder form, with the Si initially being non-conductive. One alternative approach for making the silicon conductive is by means of thermal gas diffusion in non-oxygen atmosphere using a gas such as Arsine, AsH3 composition. Another approach is ion implantation with dopants such as Boron. It is also contemplated that the dopant such as Arsenic, Gallium, or Phosphorous could be added in powder form to reground non-conductive Si:SiOx powder and then sintered in a non-oxygen atmosphere. Still another approach to post-treatment doping of initially non-conductive Si is to mix metal powder such as Al, Mg, Sn, In, Mn, Zn, Bi, Cd, Se, and/or Ga with reground non-conductive Si:SiOx powder and then sinter in a non-oxygen atmosphere.


The invention also contemplates that additional material can be added to the Si:SiOx in order to tailor the end properties. For example, to improve density, one could add Al, Mg, Sn, In, Zn, Bi, Sr, Cd, Se and/or Ga. To improve ductility, one could add Al, Mg, Sn, In, Zn, Ga, Se and/or Cd. To alter the refractive index of the Si:SiOx material, on could add Al and/or Sr. To improve toughness, one could add Al, Mg and/or Se. In each case, the base Si:SiOx material is itself electrically conductive.


Obviously, many modifications and variations of the present invention are possible in light of the above teachings. It is, therefore, to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described. The invention is defined by the claims.

Claims
  • 1. A method of making an article, comprising: preparing a homogeneous mixture of a plurality of grains of conductive doped silicon and a plurality of grains of at least one oxide of silicon and compacting and sintering the mixture to form a three-dimensional network of conductive doped silicon grains throughout the bulk of the article that are fused to one another and wherein the grains of the at least one oxide of silicon are intermixed with and fused directly to the interconnected network of grains of the conductive silicon throughout the three-dimensional network in a manner that yields a monolithic fused composite material that has a resistivity of about 200Ω·cm or less throughout the bulk of the material.
  • 2. The method of claim 1 including compacting the composite material to at least 90% of full theoretical density.
  • 3. The method of claim 2 including providing the Si initially in powder form and the SiOx initially in powder form.
  • 4. The method of claim 3 including sizing the Si and SiOx powders to less than about 5 μm.
  • 5. The method of claim 4 including providing an initial blend of the Si and SiOx particles in relative amounts such that the SiOx powder comprises at least about 50% by weight of the blend.
  • 6. The method of claim 4 including providing an initial blend of the Si and SiOx particles in relative amounts such that the SiOx powder comprises at least about 50% by weight of the blend but no more than about 80% by weight of the blend.
  • 7. The method of claim 1 including adding at least one metal additive material selected from the group consisting of: Al, Mg, Sn, In, Mn, Zn, Bi, Sr, Cd, Se and Ga.
  • 8. The method of claim 1 wherein there is only one oxide of silicon and it consists of SiO2.
US Referenced Citations (16)
Number Name Date Kind
3849344 McMurtry et al. Nov 1974 A
4375443 Kipperman et al. Mar 1983 A
4451969 Chaudhuri Jun 1984 A
4859553 Jansen et al. Aug 1989 A
5320729 Narizuka et al. Jun 1994 A
6177284 Horii et al. Jan 2001 B1
6616890 McPhillips Sep 2003 B2
6730934 Yamada et al. May 2004 B2
6911163 Abe Jun 2005 B2
7037581 Aramata et al. May 2006 B2
20020190048 McPhillips Dec 2002 A1
20030118905 Fukuoka et al. Jun 2003 A1
20040182700 Natsume et al. Sep 2004 A1
20070034500 Stevenson et al. Feb 2007 A1
20070034837 Stevenson et al. Feb 2007 A1
20070037404 Stevenson et al. Feb 2007 A1
Foreign Referenced Citations (12)
Number Date Country
60-178618 Aug 1985 JP
05-005177 Jul 1991 JP
04-028858 Jan 1992 JP
04028858 Jan 1992 JP
05-005117 Jan 1993 JP
10-062776 Mar 1998 JP
2002-313307 Oct 2002 JP
2004-119615 Apr 2004 JP
2004119615 Apr 2004 JP
2004323324 Nov 2004 JP
WO 03082769 Oct 2003 WO
WO 2004048289 Jun 2004 WO
Related Publications (1)
Number Date Country
20070037404 A1 Feb 2007 US