Claims
- 1. A method for producing a fine grained diamond film by a chemical vapor deposition (CVD) process comprising depositing a diamond film onto a smooth surface of a heated substrate wherein a diamond growth surface is exposed to a flowing hydrogen and hydrocarbon gas mixture, a hot filament in the path of said flowing gas mixture, said depositing being carried out by passing said gas mixture over at least one filament, said filament being at a temperature between about 1700 to about 2400 degrees Centigrade and being substantially parallel to said surface a distance of about 0.2 to 2 centimeters from said surface, said depositing said diamond film being carried out under conditions of temperature, pressure, and gas concentration which promote the growth of a diamond coating on the surface of the substrate, said substrate temperature being maintained between about 850 to 950 degrees Centigrade, hydrocarbon content being within the range of 0.1 to 2.5 percent of the total volume of said gas mixture, and nitrogen content being selected within a range from about 4 to about 6 volume percent of the total volume for inhibiting the formation and growth of crystal facets in the diamond film whereby said diamond film is deposited uniformly into a single layer having a grain size of less than 1 micron, a Raman graphite peak at 1580 cm.sup.-1 and a sp.sup.2 bond Raman broad peak between 1360-15 cm.sup.-1, said single layer having no Raman signature at 1332 cm.sup.-1 wherein the final growth surface of which is a smooth continuous layer of diamond grains having an average size of less than 1 micron which are bonded together without gaps there-between and whose exposed surfaces are rounded,
- said single layer of polycrystalline diamond has no Raman signature at 1332 cm.sup.-1.
- 2. A method as in claim 1, wherein the hydrocarbon is methane.
- 3. A method according to claim 2, wherein the concentration of hydrogen and methane is about 90 to about 99.5 vol. %, respectively.
- 4. A method according to claim 1, wherein the nitrogen content is about 5 vol. %.
- 5. A method according to claim 1, wherein the surface of the substrate on which the diamond film is deposited is polished.
- 6. A method for producing a fine-grained CVD diamond film according to claim 1 comprising removing said diamond film from said substrate.
- 7. A method for producing a fine-grained CVD diamond film according to claim 6 wherein said substrate has a different coefficient of expansion than that of said diamond film, and said substrate and said deposited diamond film are cooled to separate said substrate from said diamond film.
- 8. A method for producing a fine-grained CVD diamond film according to claim 1 wherein said filament comprises tungsten and has a diameter of about 0.017 to one centimeter.
Parent Case Info
This is a continuation of application Ser. No. 07/897,124, filed on Jun. 11, 1992, now abandoned.
US Referenced Citations (8)
Foreign Referenced Citations (7)
Number |
Date |
Country |
0284190 |
Sep 1988 |
EPX |
0254312 |
Nov 1990 |
EPX |
59-143498 |
Aug 1984 |
JPX |
60-141697 |
Jul 1985 |
JPX |
63-210010 |
Aug 1988 |
JPX |
63-256596 |
Feb 1989 |
JPX |
2-125874 |
May 1990 |
JPX |
Non-Patent Literature Citations (1)
Entry |
Bachmann, P. K. et al. "Emerging Technology of Diamond Thin Films" Chemical & Engineering News May 15, 1989 pp. 24-38. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
897124 |
Jun 1992 |
|