Sodium copper titanate compositions containing a rare earth, yttrium or bismuth

Abstract

This invention provides compositions of the formula Na0.5M0.5Cu3Ti4O12 wherein M=La—Lu, Y, Bi or mixtures thereof. These compositions have high dielectric constant and low loss over a frequency range of from about 1 kHz to about 1 MHz.

Description

[0001] This application claims the benefit of U.S. Provisional Application No. 60/328,758, filed on Oct. 12, 2001.

FIELD OF THE INVENTION

[0002] This invention relates to novel compositions of the formula Na0.5M0.5Cu3Ti4O12 wherein M is La—Lu, Y, Bi or mixtures thereof.

BACKGROUND OF THE INVENTION

[0003] The use of dielectric materials to increase capacitance is well known and long-used. Known capacitor dielectrics fall into two categories. One category of dielectrics has a relatively temperature-independent dielectric constant but the value of the dielectric constant is low, e.g. 5-10. Materials such as electrical porcelain and mica fall into this category. Another category of dielectrics has a very high dielectric constant, e.g. 1000 or more, but they are quite frequency dependent. An example is barium titanate (BaTiO3).

[0004] Since the capacitance is proportional to the dielectric constant, high dielectric constant materials are desired. In order to perform acceptably in electronic circuits, the dielectric must have a dielectric constant that exhibits minimal frequency dependence. It is also desirable to have the loss or dissipation factor as small as possible. The materials of this invention meets those needs.

SUMMARY OF THE INVENTION

[0005] This invention provides compositions of the formula Na0.5M0.5Cu3Ti4O12 wherein M is La—Lu, Y, Bi or mixtures thereof. These compositions have high dielectric constant and low loss over a frequency range of from 1 kHz to 1 MHz and are especially useful in capacitors in electronic devices such as phase shifters, matching networks, oscillators, filters, resonators, and antennas comprising interdigital and trilayer capacitors, coplanar waveguides and microstrips.

BRIEF DESCRIPTION OF THE DRAWING

[0006] FIG. 1 shows the variation of dielectric constant and loss factor for the compositions of Examples 2, 4, 6 and 7.

DETAILED DESCRIPTION OF THE INVENTION

[0007] The compositions of this invention, Na0.5M0.5Cu3Ti4O12, wherein M is La—Lu, Y, Bi or mixtures thereof, have dielectric properties that provide advantages in electronic devices requiring a high dielectric constant with minimal frequency dependence and low loss. “La—Lu” is defined as all the lanthanide (rare earth) elements with atomic numbers from 57 through 71.

[0008] The compositions of this invention can be synthesized by the following procedure. Stoichiometric amounts of the starting materials are thoroughly mixed. The starting materials M2O3 (M is La—Lu, Y, Bi or mixtures thereof), CuO, TiO2 and Na2CO3 are preferred. The mixed powder of starting materials is calcined at about 900° C. for about 12 hours. The calcined powder is reground and pressed to about 12.7 mm diameter/1-2 mm thick disks. The disks are sintered in air at about 950° C. for 24 hours. In both the calcining and sintering steps, the rate of temperature increase is about 200° C./hour from room temperature (i.e. about 20-25° C.) to the calcining or sintering temperature. The rate of temperature decrease is about 150° C./hour from the calcining or sintering temperature to room temperature.

[0009] All of the Na0.5M0.5Cu3Ti4O12 phases of this invention crystallize in a cubic perovskite-related Im3 structure.

[0010] Dielectric measurements can be carried out on the disk samples. The faces of the disk-shaped samples are polished with a fine-grit sand or emery paper. Silver paint electrodes are applied on the faces and dried at about 70-100° C. The capacitance and the dielectric loss measurements can be performed by the two-terminal method using Hewlett-Packard 4275A and 4284A LCR bridges at a temperature of about 25° C. over a frequency range of from about 1 kHz to about 1 MHz. The capacitance (C) and the dissipation factor are read directly from the bridge. The dielectric constant (K) is calculated from the measured capacitance (C) in picofarads from the relationship K=(100*C*t)/(8.854*A), where t is thickness of the disk shaped sample in cm, A is the area of the electrode in cm2, and * indicates multiplication

[0011] The advantageous effects of this invention are demonstrated by a series of examples, as described below. The embodiments of the invention on which the examples are based are illustrative only, and do not limit the scope of the invention.

EXAMPLES 1-7

[0012] The compositions Na0.5M0.5Cu3Ti4O12 of Examples 1-7 wherein M is La, Sm, Gd, Dy, Yb, Bi and Y, respectively, were made using the following procedure. For each Example, appropriate amounts of the starting oxides Na2CO3, M2O3, CuO and TiO2 were weighed according to the stoichiometric ratios and mixed thoroughly in an agate mortar. The gram amounts of the starting materials used are shown in Table 1.

TABLE 1
Ex.	Composition	Na2CO3	M2O3	CuO	TiO2
1	Na0.5La0.5Cu3Ti4O12	0.0647	0.1989	0.5828	0.7803
			(La2O3)
2	Na0.5Sm0.5Cu3Ti4O12	0.0641	0.2110	0.5777	0.7736
			(Sm2O3)
3	Na0.5Gd0.5Cu3Ti4O12	0.0638	0.2182	0.5747	0.7696
			(Gd2O3)
4	Na0.5Dy0.5Cu3Ti4O12	0.0635	0.2237	0.5725	0.7665
			(Dy2O3)
5	Na0.5Yb0.5Cu3Ti4O12	0.0630	0.2345	0.5680	0.7605
			(Yb2O3)
6	Na0.5Bi0.5Cu3Ti4O12	0.0614	0.2700	0.5532	0.7407
			(Bi2O3)
7	Na0.5Y0.5Cu3Ti4O12	0.0672	0.1433 (Y2O3)	0.6059	0.8113

[0013] In each Example, the mixed powder was calcined at about 900° C. for 12 hours. The calcined powder was reground and pressed to 12.7 mm diameter/1-2 mm thick disks. The disks were sintered in air at about 950° C. for 24 hours. In both the calcining and sintering steps, the temperature was increased from room temperature to the calcining or sintering temperature at a rate of about 200° C./hour, and the temperature was decreased from the calcining or sintering temperature to room temperature at a rate of about 150° C./hour.

[0014] X-ray powder diffraction patterns were recorded with a Siemens D5000 diffractometer. The data showed all samples crystallized in a cubic perovskite-related Im3 structure. The measured lattice parameters are listed in Table 2.

TABLE 2
			Dielectric	Dielectric
		Lattice	Constant	Loss, tan □
		Parameter	(105 Hz) @ 298	(105 Hz) @ 298
Ex.	Composition	(nm)	K	K
1	Na0.5La0.5Cu3Ti4O12	0.7420	3560	0.074
		(1)
2	Na0.5Sm0.5Cu3Ti4O12	0.7395	2263	0.047
		(1)
3	Na0.5Gd0.5Cu3Ti4O12	0.7388	2645	0.054
		(1)
4	Na0.5Dy0.5Cu3Ti4O12	0.7379	2049	0.035
		(1)
5	Na0.5Yb0.5Cu3Ti4O12	0.7361	2048	0.059
		(1)
6	Na0.5Bi0.5Cu3Ti4O12	0.7412	2952	0.065
		(1)
7	Na0.5Y0.5Cu3Ti4O12	0.7385	2375	0.048
		(1)

[0015] The disk samples were polished to produce flat uniform surfaces and electroded with silver paint. The painted samples were dried at about 70-100° C. overnight. Capacitance and loss tangent measurements were done at room temperature using a HP-4284A LCR meter over a frequency range of from 1 kHz to 1 MHz. Dielectric constant and loss data measured at a temperature of about 25° C. (298 K) and a frequency of about 105 Hz are listed in Table 2. The dielectric constants are high and the loss factors are low. Variations of dielectric constant and loss factor over a range of frequency from about 103 Hz to about 106 Hz for the samples of Examples 2, 4, 6 and 7 are shown in FIG. 1. The dielectric constants and loss factors have minimal frequency dependence over 3 orders of magnitude change in frequency.

Claims

1. A composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La—Lu, Y, Bi or mixtures thereof.

2. A composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La—Lu.

3. A composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Y.

4. A composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Bi.

5. The composition of claim 1, wherein M is La, Sm, Gd, Dy, Yb, Y or Bi.

6. The composition of claim 1, wherein M is La.

7. The composition of claim 1, wherein M is Sm.

8. The composition of claim 1, wherein M is Gd.

9. The composition of claim 1, wherein M is Dy.

10. The composition of claim 1, wherein M is Yb.

11. A method of providing a dielectric comprising providing a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La—Lu, Y, Bi or mixtures thereof as the dielectric.

12. The method of claim 11 wherein M is Y or Bi.

13. An electronic device containing a capacitor with a dielectric material, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La—Lu, Y, Bi or mixtures thereof.

14. An electronic device containing a capacitor with a dielectric material, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La—Lu.

15. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La, Sm, Gd, Dy, Yb, Y or Bi.

16. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is La.

17. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Sm.

18. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Gd.

19. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Dy.

20. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Yb.

21. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Y.

22. The electronic device of claim 13, wherein said dielectric material is comprised of a composition of the formula Na0.5M0.5Cu3Ti4O12, wherein M is Bi.