Spheroidal titanium metallic powders with custom microstructures

Information

  • Patent Grant
  • 12214420
  • Patent Number
    12,214,420
  • Date Filed
    Friday, December 2, 2022
    2 years ago
  • Date Issued
    Tuesday, February 4, 2025
    14 days ago
Abstract
Methodologies, systems, and devices are provided for producing metal spheroidal powder products. By utilizing a microwave plasma, control over spheriodization and resulting microstructure can be tailored to meet desired demands.
Description
TECHNICAL FIELD

The present disclosure is generally directed towards producing metal spheroidal powder products. More particularly, the present disclosure is directed towards techniques for producing metal spheroidal powder products (e.g., Ti powders, Ti alloy powders, Ti compound powders) using a microwave generated plasma.


BACKGROUND

An important aspect of preparing some forms of industrial powders is the spheroidization process, which transforms irregularly shaped or angular powders produced by conventional crushing methods, into spherical low-porosity particles. Spherical powders are homogenous in shape, denser, less porous, have a high and consistent flowability, and high tap density. Such powders exhibit superior properties in applications such as injection molding, thermal spray coatings, additive manufacturing, etc.


Creating spheroidal metallic powders, especially metallic powders containing Ti, can pose a number of challenges. Achieving the desired spheroidal shape, the desired level of porosity (e.g., no porosity to very porous, and the desired composition and microstructure can be difficult.


Conventional spheroidization methods employ thermal arc plasma described in U.S. Pat. No. 4,076,640 issued Feb. 28, 1978 and radio-frequency generated plasma described in U.S. Pat. No. 6,919,527 issued Jul. 19, 2005. However, these two methods present limitations inherent to the thermal non-uniformity of radio-frequency and thermal arc plasmas.


In the case of thermal arc plasma, an electric arc is produced between two electrodes generates a plasma within a plasma channel. The plasma is blown out of the plasma channel using plasma gas. Powder is injected from the side, either perpendicularly or at an angle, into the plasma plume, where it is melted by the high temperature of the plasma. Surface tension of the melt pulls it into a spherical shape, then it is cooled, solidified and is collected in filters. An issue with thermal arc plasma is that the electrodes used to ignite the plasma are exposed to the high temperature causing degradation of the electrodes, which contaminates the plasma plume and process material. In addition, thermal arc plasma plume inherently exhibit large temperature gradient. By injecting powder into the plasma plume from the side, not all powder particles are exposed to the same process temperature, resulting in a powder that is partially spheroidized, non-uniform, with non-homogeneous porosity.


In the case of radio-frequency inductively coupled plasma spheroidization, the plasma is produced by a varying magnetic field that induces an electric field in the plasma gas, which in turn drives the plasma processes such as ionization, excitation, etc. . . . to sustain the plasma in cylindrical dielectric tube. Inductively coupled plasmas are known to have low coupling efficiency of the radio frequency energy into the plasma and a lower plasma temperature compared to arc and microwave generated plasmas. The magnetic field responsible for generating the plasma exhibits a non-uniform profile, which leads to a plasma with a large temperature gradient, where the plasma takes a donut-like shape that exhibiting the highest temperature at the edge of the plasma (close to the dielectric tube walls) and the lowest temperature in the center of the donut. In addition, there is a capacitive component created between the plasma and the radio frequency coils that are wrapped around the dielectric tube due to the RF voltage on the coils. This capacitive component creates a large electric field that drives ions from the plasma towards the dielectric inner walls, which in turn leads to arcing and dielectric tube degradation and process material contamination by the tube's material.


To be useful in additive manufacturing or powdered metallurgy (PM) applications that require high powder flow, metal powder particles should exhibit a spherical shape, which can be achieved through the process of spheroidization. This process involves the melting of particles in a hot environment whereby surface tension of the liquid metal shapes each particle into a spherical geometry, followed by cooling and re-solidification. Also, spherical powders can be directly produced by various techniques. In one such technique, a plasma rotating electrode (PRP) produces high flowing and packing titanium and titanium alloy powders but is deemed too expensive. Also, spheroidized titanium and titanium alloys have been produced using gas atomization, which uses a relatively complicated set up an may introduce porosity to the powder. Spheroidization methods of irregular shape powders include TEKNA's (Sherbrook, Quebec, Canada) spheroidization process using inductively coupled plasma (ICP), where angular powder obtained from Hydride-Dehydride (HDH) process is entrained within a gas and injected though a hot plasma environment to melt the powder particles. However, this method suffers from non uniformity of the plasma, which leads to incomplete spheroidization of feedstock. The HDH process involves several complex steps, including hydrogenation dehydrogenation, and deoxidation before the powder is submitted to spheroidization. This process is a time consuming multi-step process, which drives up the cost of metal powders made through these methods.


From the discussion above, it is therefore seen that there exists a need in the art to overcome the deficiencies and limitations described herein and above.


SUMMARY

The shortcomings of the prior art are overcome and additional advantages are provided through the use of a microwave generated plasma torch and selecting and controlling cooling processing parameters to generate spheroidized metallic particles with a desired microstructure. Exemplary embodiments of the present technology are directed to spheroidal titanium (e.g., titanium and titanium alloy) particles and methods for preparing such particles.


In one aspect, the present disclosure relates to spheroidized particles including titanium. The spheroidized particles are prepared by a process including: introducing a titanium based feed material (e.g., feed material includes titanium, such as titanium particles or titanium alloy powders) including particles into a microwave plasma torch; melting and spheroidizing the feed material within a plasma generated by the microwave plasma torch; exposing the spheroidized particles to an inert gas; and setting one or more cooling processing variables to tailor the microstructure of the spheroidized particles including titanium. The above aspect includes one or more of the following features. In one embodiment, the titanium based feed material includes a titanium alloy. In another embodiment, the spheroidized particles are Ti Al6-V4 (i.e., Ti 6-4). In another embodiment, melting and spheroidizing of the feed material occurs within a substantially uniform temperature profile between about 4,000K and 8,000K. In another embodiment, the feed material has a particle size of no less than 1.0 micrometers and no more than 300 micrometers. In another embodiment, one or more cooling processing variables are set to create a martensitic microstructure in the spheroidized particles. In another embodiment, one or more cooling processing variables are set to create a Widmanstätten microstructure in the spheroidized particles. In another embodiment, one or more cooling processing variables are set to create an equiaxed microstructure in the spheroidized particles. In another embodiment, one or more cooling processing variables are set to create at least two regions, each region having a different microstructure. In another embodiment, the at least two regions include a core portion and a skin portion. In another embodiment, the skin portion has a microstructure that is different from the feed material's microstructure.


In another aspect, the present disclosure relates to a method of tailoring microstructure of spheroidized metallic particles. The method includes introducing a metal feed material including particles into a microwave plasma torch. The method also includes melting and spheroidizing the feed material within a plasma generated by the microwave plasma torch; exposing the spheroidized particles to an inert gas; and setting one or more cooling processing variables to tailor the microstructure of the spheroidized metallic particles. The above aspect includes one or more of the following features. In one embodiment, the metal feed material includes a titanium based feed material. In another embodiment, melting and spheroidizing of the feed material occurs within a substantially uniform temperature profile between about 4,000K and 8,000K. In another embodiment, the feed material has a particle size of no less than 1.0 micrometers and no more than 300 micrometers. In another embodiment, setting one or more cooling processing variables includes selecting and controlling a cooling gas flow rate. In another embodiment, setting one or more cooling processing variables includes selecting and controlling a residence time of the particles of feed materials within the plasma. In another embodiment, setting one or more cooling processing variables includes selecting and controlling a cooling gas composition. In another embodiment, the cooling gas composition is selected to provide high thermal conductivity. In another embodiment, one or more cooling processing variables are set to create a martensitic microstructure in the spheroidized particles. In another embodiment, one or more cooling processing variables are set to create a Widmanstätten microstructure in the spheroidized particles. In another embodiment, one or more cooling processing variables are set to create an equiaxed microstructure in the spheroidized particles. In another embodiment, one or more cooling processing variables are set to create at least two regions, each region having a different microstructure. In another embodiment, the at least two regions include a core portion and a skin portion. In another embodiment, the skin portion has a microstructure that is different from the feed material's microstructure.


In another aspect, the present disclosure relates to a method of modifying at least one of particle shape or microstructure of a titanium based feed stock. The method includes selecting a composition of the titanium based metal feed stock; determining a desired microstructure for a final product; selecting cooling process parameters based upon desired microstructure and composition of the titanium based metal feed stock; melting at least a surface portion of particles of the titanium based metal feed stock in a plasma having a substantially uniform temperature profile at between 4,000K and 8,000K to spheriodize the feed stock; exposing the spheroidized particles to an inert gas; and setting and applying the selected cooling processing parameters to create spheroidized particles with the desired microstructure. The above aspect includes one or more of the following features. In one embodiment, selecting the composition of the titanium based metal feed material includes determining an alloying composition of a titanium based feed stock source. In another embodiment, the particles of the titanium based metal feed stock have a particle size of no less than 1.0 micrometers and no more than 300 micrometers. In another embodiment, setting and applying the selected cooling processing parameters includes controlling a cooling gas flow rate. In another embodiment, setting and applying the selected cooling processing parameters include controlling a residence time of the particles of the titanium based metal feed stock in the plasma. In another embodiment, setting and applying the selected cooling processing parameters includes controlling a cooling gas composition. In another embodiment, the cooling gas composition is selected to provide high thermal conductivity. In another embodiment, the cooling processing parameters are selected to create a martensitic microstructure in the spheroidized particles. In another embodiment, the cooling processing parameters are selected to create a Widmanstätten microstructure in the spheroidized particles. In another embodiment, the cooling processing parameters are selected to create an equiaxed microstructure in the spheroidized particles. In another embodiment, the cooling processing parameters are selected to create at least two regions, each region having a different microstructure or crystal structure. The at least two regions can include a core portion and a skin portion. In another embodiment, the skin portion has a microstructure that is different from the feed stock's microstructure. In another embodiment, the titanium based metal feed stock has a α-phase crystal structure and the spheroidized particles includes one or more regions of a β-phase crystal structure. In another embodiment, the titanium based metal feed stock has a single phase structure and the spheroidized particles have a multiphase structure.


Embodiments of the above aspects may include one or more of the following features. The various spheroidized particles, processes used to create the spheroidized particles, and methods of producing metal or metal alloy powders in accordance with the present technology can provide a number of advantages. For example, the particles, processes for forming the particles and methods disclosed herein can be used in a continuous process that spheroidizes, and allows for control over the final microstructure of the particles. Such embodiments can reduce the cost of spheroidizing metal powders by reducing the number of processing steps, which in turn, reduces the energy per unit volume of processed material and can increase the consistency of the final product. Reduction in the number of processing steps also reduces the possibility for contamination by oxygen and other contaminants. Additionally, the continuous processes disclosed herein improve the consistency of the end products by reducing or eliminating variations associated with typical batch-based processing of particles. The present technology can achieve additional improvements in consistency due to the homogeneity and control of the energy source (i.e., plasma process). Specifically, if the plasma conditions are well controlled, particle agglomeration can be reduced, if not totally eliminated, thus leading to a better particle size distribution (on the same scale as the original feed materials).


In addition to the advantage of consistent end product, the present methods and resulting powders have the advantage of control and the ability to tailor the microstructure of the end product. While not wishing to be bound by theory, it is believed that the methods disclosed herein provide control over heating and cooling processing conditions. As a result, by controlling and, in some embodiments, monitoring, at least one cooling processing variable (e.g., cooling gas flow rate, residence time in cooling gas, and composition of cooling gas) a desired microstructure, which may be different from the original microstructure can be obtained. Further, novel multiphase microstructures can be created. That is, spheroidal particles can be processed by controlling heating and/or cooling conditions to create a core with one microstructure and a shell with a different microstructure. Some embodiments have the advantage of being able to modify or change the microstructure of the feed stock material to a desired microstructure, which may be a single phase or multiphase material.


Additional features and advantages are realized through the techniques of the present technology. The recitation herein of desirable objects or aspects which are met by various embodiments of the present technology is not meant to imply or suggest that any or all of these objects or aspects are present as essential features, either individually or collectively, in the most general embodiment of the present technology or in any of its more specific embodiments.





BRIEF DESCRIPTION OF THE DRAWINGS

The features and advantages of the present disclosure will be more fully understood from the following description of exemplary embodiments when read together with the accompanying drawings, in which:



FIG. 1 illustrates an example method of producing spheroidal metallic and metallic alloy particles according to the present disclosure, compared against a conventional method for producing similar particles.



FIG. 2 illustrates another example method of producing dehydrogenated spheroidal particles according to the present disclosure.



FIG. 3 illustrates another example method of producing dehydrogenated spheroidal particles from metal hydride material according to the present disclosure.



FIG. 4 illustrates an exemplary microwave plasma torch that can be used in the production of spheroidal and dehydrogenated metal or metal alloy powders, according to embodiments of the present disclosure.



FIG. 5 illustrates an exemplary method of producing titanium based (e.g., titanium, titanium alloy) spheroidal particles having a desired microstructure.



FIG. 6 illustrates an exemplary method of modifying a particle microstructure according to embodiments of the present disclosure.



FIG. 7 illustrates an exemplary particle modified according to embodiments of the present disclosure.





DETAILED DESCRIPTION

One aspect of the present disclosure involves a process of spheroidization of metals and metal alloy hydrides using a microwave generated plasma. The process uses readily available existing pre-screened or non-prescreened raw materials made of metal hydrides as feedstock. The powder feedstock is entrained in inert and/or reducing and/or oxidizing gas environment and injected into the microwave plasma environment. Upon injection into a hot plasma, the feedstock is simultaneously dehydrogenated and spheroidized and released into a chamber filled with an inert gas and directed into hermetically sealed drums where is it stored. This process can be carried out at atmospheric pressure, in a partial vacuum, or at a slightly higher pressure than atmospheric pressure. In alternative embodiments, the process can be carried out in a low, medium, or high vacuum environment. The process can run continuously and the drums are replaced as they fill up with spheroidized dehydrogenated and deoxidized metal or metal alloy particles. The process not only spheroidizes the powders, but also eliminates the dehydrogenation steps from the traditional process of manufacturing metal and metal alloy powders using Hydride-De-hydride (HDH) process, which leads to cost reduction. By reducing the number of processing steps and providing a continuous process, the possibilities for contamination of the material by oxygen and other contaminants is reduced. Furthermore, provided the homogeneity of the microwave plasma process, particle agglomeration is also reduced, if not totally eliminated, thus leading to at least maintaining the particle size distribution of the original hydride feed materials.


In the powdered metallurgy industry, the Hydride-Dehydride (HDH) process is used to resize large metallic or metallic alloy pieces down to a finer particle size distribution through crushing, milling, and screening. Metal and alloy powders are manufactured using the HDH process, where bulk feedstock, such as coarse metal powders or metal/metal alloy scraps, etc., are heated in a hydrogen-containing atmosphere at high temperature (˜700° C.) for a few days. This leads to the formation of a brittle metal hydride, which can readily be crushed into a fine power and sifted to yield a desired size distribution determined by the end user. To be useful in powdered metallurgy, hydrogen must be dissociated and removed from the metal by heating the metal hydride powder within vacuum for a period of time. The dehydrogenated powder must then be sifted to remove large particle agglomerations generated during process due to sintering. The typical resulting powder particles have an irregular or angular shape. The powder is submitted to a deoxidation process to remove any oxygen picked up by the powder during sifting and handling. Conventional HDH processes produce only coarse and irregular shaped particles. Such HDH processes must be followed by a spheroidization process to make these particles spheroidal.


Conventional HDH processes are primarily carried out as solid-state batch processes. Typically, a volume of metal powder is loaded into a crucible(s) within a vacuum furnace. The furnace is pumped down to a partial vacuum and is repeatedly purged with inert gas to eliminate the presence of undesired oxygen. Diffusion of the inert gas through the open space between the powder particles is slow making it difficult to fully eliminate oxygen, which otherwise contaminates the final product. Mechanical agitation may be used to churn powder allowing for more complete removal of oxygen. However, this increases the complexity of the system and the mechanical components require regular maintenance, ultimately increasing cost.


Following oxygen purging the, hydrogenation may begin. The furnace is filled with hydrogen gas and heated up to a few days at high temperature to fully form the metal hydride. The brittle nature of the metal hydride allows the bulk material to be crushed into fine powders which are then screened into desired size distributions.


The next step is dehydrogenation. The screen hydride powder is loaded into the vacuum furnace then heated under partial vacuum, promoting dissociation of hydrogen from the metal hydride to form H2 gas and dehydrided metal. Dehydrogenation is rapid on the particle surface where H2 can readily leave the particles. However, within the bulk of the powder, H2 must diffuse through the bulk of the solid before it reaches surface and leave the particle. Diffusion through the bulk is a rate-limiting process “bottle-neck” requiring relatively long reaction time for complete dehydrogenation. The time and processing temperatures required for dehydrogenation are sufficient to cause sintering between particles, which results in the formation of large particle agglomerations in the final product. Post-process sifting eliminates the agglomerations, which adds process time and cost to the final product. Before the powder can be removed from the furnace, it must be sufficiently cooled to maintain safety and limit contamination. The thermal mass of the large furnaces may take many hours to sufficiently cool. The cooled powders must then be spheroidized in a separate machine. Generally this is carried out within an RF plasma, which are known to exhibit large temperature gradients resulting in partially spheroidized products.


Techniques are disclosed herein for manufacturing spheroidal metal and metal alloy powder products in a continuous process that simultaneously dehydrogenates and spheroidizes feed materials. According to exemplary embodiments, the dehydrogenation and spheroidization steps of an HDH process can be simplified to a single processing step using a microwave generated plasma. Such embodiments can reduce the cost of spheroidizing metal powders by reducing the number of processing steps, reducing the energy per unit volume of processed material, and increasing the consistency of the final product. Reduction in the number of processing steps also reduces the possibility for powder contamination by oxygen and other contaminants. Additionally, the continuous dehydrogenation processes disclosed herein improves the consistency of the end products by reducing or eliminating variations associated with typical batch-based dehydrogenation processes.


The rate of cooling of the dehydrogenated, deoxidized, and spheroidized metal and metal alloys can be controlled to strategically influence the microstructure of the powder. For example, rapid cooling of α-phase titanium alloys facilitates an acicular (martensite) structure. Moderate cooling rates produce a Widmanstätten microstructure, and slow cooling rates form an equiaxed microstructure. By controlling the process parameters such as cooling gas flow rate, residence time, cooling gas composition etc., microstructure of the metal and metal alloys can be controlled. In general, process parameters such as power density, flow rates, and residence time of the powder in the plasma dependent on the powder material's physical characteristics, such as, for example, the melting point, thermal conductivity, and particle size distribution. In some embodiments, the power density can range from about 20 W/cm3 to 500 W/cm3. In certain embodiments, the total gas flow rate can range from about 0.1 cfm (cubic feet per minute) to 50 cfm. In embodiments, the residence time can be tuned from about 1 milliseconds to 10 seconds. The precise cooling rates required to form these structures is largely a function of the type and quantity of the alloying elements within the material.


The rate of cooling, especially when combined with the consistent and uniform heating capabilities of a microwave plasma plume, allow for control over the final microstructure. As a result, the above methods can be applied to processing metal (e.g., titanium and titanium alloys such as Ti 6-4) feed stock. In particular, while certain methods herein have described the use of a metal hydride feed stock, the control over microstructure is not limited thereto. In particular, methods of the present technology and powders created by the present technology include the use of non-hydrided sources. For example, titanium metal and various titanium metal alloys can be utilized as the feed stock source. These materials can be crushed or milled to create particles for treatment within a microwave plasma torch.


Cooling processing parameters include, but are not limited to, cooling gas flow rate, residence time of the spheroidized particles in the hot zone, and the composition or make of the cooling gas. For example, the cooling rate or quenching rate of the particles can be increased by increasing the rate of flow of the cooling gas. The faster the cooling gas is flowed past the spheroidized particles exiting the plasma, the higher the quenching rate-thereby allowing certain desired microstructures to be locked-in. Residence time of the particles within the hot zone of the plasma can also be adjusted to provide control over the resulting microstructure. That is, the length of time the particles are exposed to the plasma determines the extent of melting of the particle (i.e., surface of the particle melted as compared to the inner most portion or core of the particle). Consequently, the extent of melting effects the extent of cooling needed for solidification and thus it is a cooling process parameter. Microstructural changes can be incorporated throughout the entire particle or just a portion thereof depending upon the extent of particle melting. Residence time can be adjusted by adjusting such operating variables of particle injection rate and flow rate (and conditions, such as laminar flow or turbulent flow) within the hot zone. Equipment changes can also be used to adjust residence time. For example, residence time can be adjusted by changing the cross-sectional area of the hot zone. For instance, for the same gas flow rates, a larger cross-sectional area of the plasma torch and/or extension tube in an afterglow region (e.g., region about plasma 11 in FIG. 4, the cross-sectional area being at least partially defined by the inner wall) will lead to a lower particle velocity, whereas a smaller cross-sectional area will lead to a higher velocity, thus lowering residence time in the hot zone.


Another cooling processing parameter that can be varied or controlled is the composition of the cooling gas. Certain cooling gases are more thermally conductive than others. For example helium is considered to be a highly thermally conductive gas. The higher the thermal conductivity of the cooling gas, the faster the spheriodized particles can be cooled/quenched. By controlling the composition of the cooling gas (e.g., controlling the quantity or ratio of high thermally conductive gasses, such as helium, to lesser thermally conductive gases, such as argon) the cooling rate can be controlled.


As is known in metallurgy, the microstructure of a metal is determined by the composition of the metal and heating and cooling/quenching of the material. In the present technology, by selecting (or knowing) the composition of the feed stock material, and then exposing the feed stock to a plasm that has the uniform temperature profile and control there over as provided by the microwave plasma torch, followed by selecting and controlling the cooling parameters control over the microstructure of the spheroidized metallic particle is achieved. In addition, the phase of the metallic material depends upon the compositions of the feed stock material (e.g., purity, composition of alloying elements, etc.) as well thermal processing. Titanium has two distinct phases known as the alpha phase (which has a hexagonal close packed crystal structure) and a beta phase which has a body centered cubic structure. Titanium can also have a mixed α+β phase. The different crystal structures yield different mechanical responses. Because titanium is allotropic it can be heat treated to yield specific contents of alpha and beta phases. The desired microstructure is not only a description of the grains (e.g., martensitic vs. equiaxed) but also the amount and location of different phases throughout.


In one exemplary embodiment, inert gas is continually purged surrounding a powdered metal feed to remove oxygen within a powder-feed hopper. A continuous volume of powder feed is then entrained within an inert gas and fed into the microwave generated plasma for dehydrogenation or for composition/maintaining purity of the spheroidized particles. In one example, the microwave generated plasma may be generated using a microwave plasma torch, as described in U.S. Patent Publication No. US 2013/0270261, and/or U.S. Patent Publication No. US 2008/0173641 (issued as U.S. Pat. No. 8,748,785), each of which is hereby incorporated by reference in its entirety. In some embodiments, the particles are exposed to a uniform temperature profile at between 4,000 and 8,000 K within the microwave generated plasma. Within the plasma torch, the powder particles are rapidly heated and melted. Liquid convection accelerates H2 diffusion throughout the melted particle, continuously bringing hydrogen (H2) to the surface of the liquid metal hydride where it leaves the particle, reducing the time each particle is required to be within the process environment relative to bulk processes. As the particles within the process are entrained within an inert gas, such as argon, generally contact between particles is minimal, greatly reducing the occurrence of particle agglomeration. The need for post-process sifting is thus greatly reduced or eliminated, and the resulting particle size distribution could be practically the same as the particle size distribution of the input feed materials. In exemplary embodiments, the particle size distribution of the feed materials is maintained in the end products.


Within the plasma, the melted metals are inherently spheroidized due to liquid surface tension. As the microwave generated plasma exhibits a substantially uniform temperature profile, more than 90% spheroidization of particles could be achieved (e.g., 91%, 93%, 95%, 97%, 99%, 100%), eliminating the need for separate dehydrogenation steps. In embodiments, which do not include dehydrogenation, both spheroidization and tailoring (e.g., changing, manipulating, controlling) microstructure are addressed or, in some instances, partially controlled, by treating with the microwave generated plasma. After exiting the plasma, the particles are cooled before entering collection bins. When the collection bins fill, they can be removed and replaced with an empty bin as needed without stopping the process.


Embodiments of the present disclosure are directed to producing particles that are substantially spherical or spheroidal or have undergone significant spheroidization. In some embodiments, spherical, spheroidal or spheroidized particles refer to particles having a sphericity greater than a certain threshold. Particle sphericity can be calculated by calculating the surface area of a sphere As,ideal with a volume matching that of the particle, V using the following equation:







r
ideal

=



3

V


4

π


3








A

s
,
ideal


=

4

π


r
ideal
2






and then comparing that idealized surface area with the measured surface area of the particle, As,actual:






Sphericity
=


A

s
,
ideal



A

s
,
actual







In some embodiments, particles can have a sphericity of greater than 0.5, 0.6, 0.7, 0.75, 0.8, 0.9, 0.91, 0.95, or 0.99 (or greater than about 0.5, about 0.6, about 0.7, about 0.75, about 0.8, about 0.8, about 0.91, about 0.95, or about 0.99). In some embodiments, particles can have a sphericity of 0.75 or greater or 0.91 or greater (or about 0.75 or greater or about 0.91 or greater). In some embodiments, particles can have a sphericity of less than 0.5, 0.6, 0.7, 0.75, 0.8, 0.9, 0.91, 0.95, or 0.99 (or less than about 0.5, about 0.6, about 0.7, about 0.75, about 0.8, about 0.8, about 0.91, about 0.95, or about 0.99). In some embodiments, a particle is considered to be spherical, spheroidal or spheroidized if it has a sphericity at or above any of the aforementioned sphericity values, and in some preferred embodiments, a particle is considered to be spherical if its sphericity is at or about 0.75 or greater or at or about 0.91 or greater.


In some embodiments, a median sphericity of all particles within a given powder can be greater than 0.5, 0.6, 0.7, 0.75, 0.8, 0.9, 0.91, 0.95, or 0.99 (or greater than about 0.5, about 0.6, about 0.7, about 0.75, about 0.8, about 0.8, about 0.91, about 0.95, or about 0.99). In some embodiments, a median sphericity of all particles within a given powder can be less than 0.5, 0.6, 0.7, 0.75, 0.8, 0.9, 0.91, 0.95, or 0.99 (or less than about 0.5, about 0.6, about 0.7, about 0.75, about 0.8, about 0.8, about 0.91, about 0.95, or about 0.99). In some embodiments, a powder is considered to be spheroidized if all or a threshold percentage (as described by any of the fractions below) of the particles measured for the given powder have a median sphericity greater than or equal to any of the aforementioned sphericity values, and in some preferred embodiments, a powder is considered to be spheroidized if all or a threshold percentage of the particles have a median sphericity at or about 0.75 or greater or at or about 0.91 or greater.


In some embodiments, the fraction of particles within a powder that can be above a given sphericity threshold, such as described above, can be greater than 50%, 60%, 70%, 80%, 90%, 95%, or 99% (or greater than about 50%, about 60%, about 70%, about 80%, about 90%, about 95%, or about 99%). In some embodiments, the fraction of particles within a powder that can be above a given sphericity threshold, such as described above, can be less than 50%, 60%, 70%, 80%, 90%, 95%, or 99% (or less than about 50%, about 60%, about 70%, about 80%, about 90%, about 95%, or about 99%).


Particle size distribution and sphericity may be determined by any suitable known technique such as by SEM, optical microscopy, dynamic light scattering, laser diffraction, manual measurement of dimensions using an image analysis software, for example from about 15-30 measures per image over at least three images of the same material section or sample, and any other techniques.


Referring to FIG. 1, shown is a comparison of a conventional process for producing spheroidized titanium powder (100) versus a method (200) in accordance with the present technology. The process flow (101) on the left of FIG. 1 presents an example process that combines a HDH process (100) with spheroidization of titanium powders. The process starts with Ti raw material (step a, 105) that is hydrogenated (step b, 110), and then crushed and sifted to size (step c, 115). Pure titanium is recovered through dehydrogenation (step d, 120). It is then screened for agglomerations and impurities, and then sifted to the size specified by the customer (step e, 125). The powder then goes through a deoxidation step to reduce or eliminate oxygen that it picked up during the sifting and screening processes. Deoxidation is required especially for small particle sizes, such as particles below 50 microns, where the surface to volume ratio is substantial (step f, 130). The titanium particles are then spheroidized (step g, 135) and collected (step h, 140). A similar process can be used to create a Ti alloy, such as Ti 6-4, instead of pure titanium powder.


As discussed above, some embodiments of the present disclosure combine the dehydrogenation and spheroidization steps shown on the left side of FIG. 1 (101, 130, 135) in favor of a single step to produce spheroidized metals and/or metal alloys from corresponding hydride feedstock. An example of this technique is illustrated in the process flow (201) shown on the right side of FIG. 1. The method starts with a crushed and sifted metal hydride feed material (i.e., step c, 115, without performing the dehydride step). In this particular embodiment, the feed material is a titanium hydride powder, and the powder resulting from process 200 is a spherical titanium powder. (It is noted that process 200 can also be used with crushed and sifted metal alloy hydride feed material, such as titanium alloy hydride feed material, and the powder resulting from completion of process 200 is a spherical metal alloy powder, such as a spherical titanium alloy powder.) The powder is entrained within an inert gas and injected into a microwave generated plasma environment exhibiting a substantially uniform temperature profile between approximately 4,000 K and 8,000 K and under a partial vacuum. The hermetically sealed chamber process can also run at atmospheric pressure or slightly above atmospheric pressure to eliminate any possibility for atmospheric oxygen to leak into the process. The particles are simultaneously melted and dehydrogenated in the plasma, spheroidized due to liquid surface tension, re-solidifying after exiting the plasma (200). The particles are then collected in sealed drums in an inert atmosphere (140). Within the plasma, the powder particles are heated sufficiently to melt and cause convection of the liquid metal, causing dissociation of the hydrogen according to the reversible reaction where M=an arbitrary metal:








M
x



H
y






(
x
)


M

+


(

y
2

)



H
2







Within the partial vacuum, dissociation of hydrogen from the metal to form hydrogen gas is favored, driving the above reaction to the right. The rate of dissociation of hydrogen from the liquid metal is rapid, due to convection, which continually introduces H2 to the liquid surface where it can rapidly leave the particle.



FIG. 2 is a flow chart illustrating an exemplary method (250) for producing spherical powders, according to an embodiment of the present disclosure. In this embodiment, the process (250) begins by introducing a feed material into a plasma torch (255). In some embodiments, the plasma torch is a microwave generated plasma torch or an RF plasma torch. Within the plasma torch, the feed materials are exposed to a plasma causing the materials to melt, as described above (260). During the same time (i.e., time that feed material is exposed to plasma), hydrogen within the feed material dissociates from the metal, resulting in dehydrogenation (260a). Simultaneously the melted materials are spheroidized by surface tension, as discussed above (260b). Note that the step 260 includes 260a and 260b. That is, by exposing the feed material to the plasma both dehydrogenation and spheroidization are achieved; no separate or distinct processing steps are needed to achieve dehydrogenation and spheroidization. After exiting the plasma, the products cool and solidify, locking in the spherical shape and are then collected (265).



FIG. 3 is a flow chart illustrating another exemplary method (300) for producing spherical powders, according to another embodiment of the present disclosure. In this example, the method (300) begins by introducing a substantially continuous volume of filtered metal hydride feed materials into a plasma torch. As discussed above, the plasma torch can be a microwave generated plasma or an RF plasma torch (310). In one example embodiment, an AT-1200 rotating powder feeder (available from Thermach Inc.) allows a good control of the feed rate of the powder. In an alternative embodiment, the powder can be fed into the plasma using other suitable means, such as a fluidized bed feeder. The feed materials may be introduced at a constant rate, and the rate may be adjusted such that particles do not agglomerate during subsequent processing steps. In another exemplary embodiment, the feed materials to be processed are first sifted and classified according to their diameters, with a minimum diameter of 1 micrometers (μm) and a maximum diameter of 22 μm, or a minimum of 22 μm and a maximum of 44 μm, or a minimum of 44 μm and a maximum of 70 μm, or a minimum of 70 μm and a maximum of 106 μm, or a minimum of 106 μm and a maximum of 300 μm. As will be appreciated, these upper and lower values are provided for illustrative purposes only, and alternative size distribution values may be used in other embodiments. This eliminates recirculation of light particles above the hot zone of the plasma and also ensures that the process energy present in the plasma is sufficient to melt the particles without vaporization. Pre-screening allows efficient allocation of microwave power necessary to melt the particles without vaporizing material.


Once introduced into the microwave plasma torch, the feed materials can be entrained within an axis-symmetric laminar and/or turbulent flow toward a microwave or RF generated plasma (320). In exemplary embodiments, each particle within the process is entrained within an inert gas, such as argon. In some embodiments, the metal hydride materials are exposed to a partial vacuum within the plasma (330).


Within the plasma, the feed materials are exposed to a substantially uniform temperature profile and are melted (340). In one example, the feed materials are exposed to a uniform temperature profile of approximately between 4,000 and 8,000 K within the plasma. Melting the feed materials within the plasma brings hydrogen to the surface of the liquid metal hydride where it can leave the particle, thus rapidly dehydrogenating the particles (350). The H2 acts as a reducing agent, which may simultaneously deoxidize the metal. Surface tension of the liquid metal shapes each particle into a spherical geometry (360). Thus, dehydrogenated and spherical liquid metal particles are produced, which cool and solidify into dehydrogenated and spherical metal powder products upon exiting the plasma (370). These particles can then be collected into bins (380). In some embodiments, the environment and/or sealing requirements of the bins are carefully controlled. That is, to prevent contamination or potential oxidation of the powders, the environment and or seals of the bins are tailored to the application. In one embodiment, the bins are under a vacuum. In one embodiment, the bins are hermetically sealed after being filled with powder generated in accordance with the present technology. In one embodiment, the bins are back filled with an inert gas, such as, for example argon. Because of the continuous nature of the process, once a bin is filled, it can be removed and replaced with an empty bin as needed without stopping the plasma process.


The methods and processes in accordance with the invention (e.g., 200, 250, 300) can be used to make spherical metal powders or spherical metal alloy powders. For example, if the starting feed material is a titanium hydride material, the resulting powder will be a spherical titanium powder. If the starting feed material is a titanium alloy hydride material, the resulting powder will be a spherical titanium alloy powder. In one embodiment that features the use of a starting titanium alloy hydride material, the resulting spherical titanium alloy powder comprises spherioidized particles of Ti Al6-V4, with between 4% to 7% weight aluminum (e.g., 5.5 to 6.5% Al) and 3% to 5% weight vanadium (e.g., 3.5 to 4.5% vanadium).



FIG. 4 illustrates an exemplary microwave plasma torch that can be used in the production of spheroidal and dehydrogenated metal or metal alloy powders, according to embodiments of the present disclosure. As discussed above, metal hydride feed materials 9, 10 can be introduced into a microwave plasma torch 3, which sustains a microwave generated plasma 11. In one example embodiment, an entrainment gas flow and a sheath flow (downward arrows) may be injected through inlets 5 to create flow conditions within the plasma torch prior to ignition of the plasma 11 via microwave radiation source 1. In some embodiments, the entrainment flow and sheath flow are both axis-symmetric and laminar, while in other embodiments the gas flows are swirling. The feed materials 9 are introduced axially into the microwave plasma torch, where they are entrained by a gas flow that directs the materials toward the plasma. As discussed above, the gas flows can consist of a noble gas column of the periodic table, such as helium, neon, argon, etc. Within the microwave generated plasma, the feed materials are melted, as discussed above, in order to dehydrogenate and spheroidize the materials. Inlets 5 can be used to introduce process gases to entrain and accelerate particles 9, 10 along axis 12 towards plasma 11. First, particles 9 are accelerated by entrainment using a core laminar gas flow (upper set of arrows) created through an annular gap within the plasma torch. A second laminar flow (lower set of arrows) can be created through a second annular gap to provide laminar sheathing for the inside wall of dielectric torch 3 to protect it from melting due to heat radiation from plasma 11. In exemplary embodiments, the laminar flows direct particles 9, 10 toward the plasma 11 along a path as close as possible to axis 12, exposing them to a substantially uniform temperature within the plasma. In some embodiments, suitable flow conditions are present to keep particles 10 from reaching the inner wall of the plasma torch 3 where plasma attachment could take place. Particles 9, 10 are guided by the gas flows towards microwave plasma 11 were each undergoes homogeneous thermal treatment. Various parameters of the microwave generated plasma, as well as particle parameters, may be adjusted in order to achieve desired results. These parameters may include microwave power, feed material size, feed material insertion rate, gas flow rates, plasma temperature, residence time and cooling rates. In some embodiments, the cooling or quenching rate is not less than 10+3 degrees C./sec upon exiting plasma 11. As discussed above, in this particular embodiment, the gas flows are laminar; however, in alternative embodiments, swirl flows or turbulent flows may be used to direct the feed materials toward the plasma.



FIG. 5 illustrates an exemplary method (500) of producing spheroidized titanium particles with a tailored or desired microstructure. Method 500 includes several processing steps to treat metallic feed materials such as, for example, titanium feed materials (e.g., titanium or titanium alloys) to create spheroidized metallic particles with a desired microstructure. In step 510, metallic (e.g., titanium based) feed materials comprising particles are feed into a plasma torch. The particles can be produced from crushing, pulverizing, or milling feed stock materials. In general, the feed stock particles have an average particle size of between 1 micron and 300 microns. In step 515, the feed stock particles are exposed to a microwave generated plasma to melt at least the surface portion of the particles. The melted portions of the particles allow for spheriodization of the particles. In step 520, the spheroidized particles are exposed to an inert gas such helium, nitrogen, argon or combinations/mixtures thereof. In step 525, the cooling processing variables/conditions are set and maintained to achieve a desired microstructure. For example, in embodiments in which a martensitic microstructure is desired throughout the entire particle, the cooling processing conditions are set for rapid cooling. As a result, the residence time of the particles in the hot zone is selected to allow for melting of the entire feedstock particle, the cooling gas flow rate is set to a fastest rate, and the amount of helium forming the composition of the cooling gas is set to a maximum available. After exposing the spheroidized particles to the selected cooling conditions, the spherical powders are collected in step 530.



FIG. 6 illustrates an exemplary method (600) of modifying metallic feed stock material to have a spheroidized shape and a desired microstructure. The method of 600 includes several processing steps to treat metallic feed materials such as, for example, titanium feed materials (e.g., titanium or titanium alloys) to create spheroidized metallic particles with a desired microstructure. In this method, knowledge of the chemical composition of the feed stock (e.g., 99.9% pure titanium, Ti-6Al-4V, etc.) is used in combination with control over thermal processing conditions to achieve spheroidal particles with a desired microstructure different than the metallic feed stock material. In step 610, the composition of the Ti-based feed stock material is selected or analyzed to determine its composition. In step 615, a desired microstructure of a final product is determined. For example, it may be determined that an α-phase 99% pure Ti equiaxed microstructure throughout the spheroidized particle is desired. As a result, a slower rate of cooling will be required than that used to produce a martensitic microstructure. Cooling processing parameters will be selected (step 620), such as cooling gas flow rate, residence time, and/or composition of cooling gas to achieve such a microstructure based upon the composition of the feed stock materials. In general, the microstructure of the final product will differ from the original feed stock material. That is an advantage of the present method is to be able to efficiently process feed materials to create spheroidized particles with a desired microstructure. After selecting or determining the cooling parameters, the feed stock particles are melted in the microwave generated plasma to spheriodize the particles in step 625. The spheroidized particles are exposed to an inert gas (step 630) and the determined or selected cooling parameters are applied to form the desired microstructure.


The desired microstructure of the spheroidized particle (end product) can be tailored to meet the demands and material characteristics of its use. For example, the desired microstructure may be one that provides improved ductility (generally associated with the α-phase). In another example, the desired microstructure may be associated with the inclusion of α+β phase or regions of a with islands of β phase or vice-versa. Without wishing to be bound by theory, it is believe that the methods of the present disclosure allow for control over the phase of the spheroidized particles as the microwave generated plasma has a uniform temperature profile, fine control over the hot zone, and the ability to select and adjust cooling processing parameters.


Using the methods of the present technology, various microstructures, crystal structures and regions of differing microstructure and/or crystal structures can be produced. Accordingly, new spheroidal titanium particles can be produced efficiently. For example, due to the abilities to control the hot zone and cooling processing parameters, the present technology allows an operator to create multiple regions within the spheroidal particle. FIG. 7 shows such an embodiment. This figures illustrates a spheroidal particle which has two distinct regions. The outer or shell region 715 and an inner core 710. The original titanium feed material for this particle was a pure titanium α-phase powder. The feed material was exposed to the plasma under conditions (temperature, residence time, etc.) such that only a surface portion of the particle melted, so that spheriodization could occur. Cooling rates applied allowed for the transformation of the shell region to transform to β-phase, leaving the core to retain the α-phase.


In another embodiment, not shown, the entire feed stock particle can be melted and cooling parameters can be selected and applied to create a crystal structure that has the same phase as the feed stock material (e.g., retains α-phase) or is transformed to a new phase or mixture of phases. Similarly, cooling processing parameters can be selected and applied to create spheroidal particles that have the same microstructure throughout the particle or various microstructures in two or more regions (e.g., shell region, core region).


In describing exemplary embodiments, specific terminology is used for the sake of clarity and in some cases reference to a figure. For purposes of description, each specific term is intended to at least include all technical and functional equivalents that operate in a similar manner to accomplish a similar purpose. Additionally, in some instances where a particular exemplary embodiment includes a plurality of system elements, device components or method steps, those elements, components or steps may be replaced with a single element, component or step. Likewise, a single element, component or step may be replaced with a plurality of elements, components or steps that serve the same purpose. Moreover, while exemplary embodiments have been shown and described with references to particular embodiments thereof, those of ordinary skill in the art will understand that various substitutions and alterations in form and detail may be made therein without departing from the scope of the invention. Further still, other functions and advantages are also within the scope of the invention.

Claims
  • 1. A method of modifying a particle shape and a microstructure of a feedstock, the method comprising: melting at least a surface portion of particles of feedstock comprising titanium in a plasma to spheroidize the particles; andsetting and applying cooling processing parameters to create spheroidized particles with a microstructure,wherein the cooling process parameters comprise one or more of a cooling gas flow rate, a residence time of the feedstock, and a cooling gas composition, andwherein the cooling processing parameters are selected to create at least two regions in the spheroidized particles, each region having a different microstructure or crystal structure, wherein the cooling processing parameters are selected to create an equiaxed microstructure in the spheroidized particles.
  • 2. The method of claim 1, wherein the particles of the feedstock have a particle size of no less than 1.0 micrometers and no more than 300 micrometers.
  • 3. The method of claim 1, wherein setting and applying the cooling processing parameters comprises controlling a cooling gas flow rate.
  • 4. The method of claim 1, wherein setting and applying the selected cooling processing parameters comprises controlling a cooling gas composition.
  • 5. The method of claim 1, wherein the at least two regions include a core portion and a skin portion.
  • 6. The method of claim 5, wherein the skin portion has a microstructure that is different from the microstructure of the feedstock.
  • 7. A method of modifying a particle shape and a microstructure of a feedstock, the method comprising: melting at least a surface portion of particles of the feedstock comprising titanium in a plasma to spheroidize the particles; andsetting and applying cooling processing parameters to create spheroidized particles with a microstructure,wherein the cooling process parameters comprise one or more of a cooling gas flow rate, a residence time of the feedstock, and a cooling gas composition, andwherein the cooling processing parameters are selected to create a martensitic microstructure, a Widmanstätten microstructure, and/or an equiaxed microstructure in the spheroidized particles.
  • 8. The method of claim 7, wherein the particles of the feedstock have a particle size of no less than 1.0 micrometers and no more than 300 micrometers.
  • 9. The method of claim 7, wherein setting and applying the selected cooling processing parameters comprises controlling a cooling gas flow rate.
  • 10. The method of claim 7, wherein setting and applying the selected cooling processing parameters comprises controlling a cooling gas composition.
  • 11. The method of claim 7, wherein the cooling processing parameters are selected to create a martensitic microstructure in the spheroidized particles.
  • 12. The method of claim 7, wherein the cooling processing parameters are selected to create a Widmanstätten microstructure in the spheroidized particles.
  • 13. The method of claim 7, wherein the cooling processing parameters are selected to create an equiaxed microstructure in the spheroidized particles.
  • 14. The method of claim 7, wherein the cooling processing parameters are selected to create at least two regions in the spheroidized particles.
  • 15. The method of claim 14, wherein each region has a different microstructure or crystal structure.
  • 16. The method of claim 14, wherein the at least two regions include a core portion and a skin portion.
  • 17. The method of claim 16, wherein the skin portion has a microstructure that is different from the microstructure of the feedstock.
RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 17/301,880, filed Apr. 16, 2021 (US Patent Publication No. 2021/0252599), which is a continuation of U.S. patent application Ser. No. 16/012,370, filed Jun. 19, 2018 (US Patent Publication No. 2018/0297122), which is a continuation in part of U.S. patent application Ser. No. 15/381,336 (US Patent Publication No. US 2017/0173699), which claims priority to and the benefit of U.S. Provisional Patent Application No. 62/268,186, filed Dec. 16, 2015. Each of the foregoing applications is incorporated herein by reference in its entirety.

US Referenced Citations (477)
Number Name Date Kind
1699205 Emil et al. Jan 1929 A
2892215 Gerhard et al. Jun 1959 A
3290723 John et al. Dec 1966 A
3293334 Bylund et al. Dec 1966 A
3434831 Knopp Mar 1969 A
3466165 Rhys et al. Sep 1969 A
RE26879 Kelso May 1970 E
3652259 Knopp Mar 1972 A
3802816 Kaufmann Apr 1974 A
3845344 Rainer Oct 1974 A
3909241 Cheney et al. Sep 1975 A
3966374 Honnorat et al. Jun 1976 A
3974245 Cheney et al. Aug 1976 A
4076640 Forgensi et al. Feb 1978 A
4177026 Honnorat et al. Dec 1979 A
4212837 Kubo et al. Jul 1980 A
4221554 Oguchi et al. Sep 1980 A
4221775 Anno Sep 1980 A
4423303 Hirose et al. Dec 1983 A
4431449 Dillon et al. Feb 1984 A
4439410 Santen et al. Mar 1984 A
4544404 Yolton et al. Oct 1985 A
4569823 Westin Feb 1986 A
4599880 Stepanenko et al. Jul 1986 A
4611108 Leprince et al. Sep 1986 A
4670047 Kopatz et al. Jun 1987 A
4692584 Caneer, Jr. Sep 1987 A
4705560 Kemp et al. Nov 1987 A
4711660 Kemp et al. Dec 1987 A
4711661 Kemp et al. Dec 1987 A
4714587 Eylon et al. Dec 1987 A
4731110 Kopatz et al. Mar 1988 A
4731111 Kopatz et al. Mar 1988 A
4772315 Johnson et al. Sep 1988 A
4778515 Kemp et al. Oct 1988 A
4780131 Kemp et al. Oct 1988 A
4783216 Kemp et al. Nov 1988 A
4783218 Kemp et al. Nov 1988 A
4787934 Johnson et al. Nov 1988 A
4802915 Kopatz et al. Feb 1989 A
4836850 Kemp et al. Jun 1989 A
4859237 Johnson et al. Aug 1989 A
4923509 Kemp et al. May 1990 A
4943322 Kemp et al. Jul 1990 A
4944797 Kemp et al. Jul 1990 A
4952389 Szymanski et al. Aug 1990 A
5041713 Weidman Aug 1991 A
5095048 Takahashi et al. Mar 1992 A
5114471 Johnson et al. May 1992 A
5131992 Church et al. Jul 1992 A
5200595 Boulos et al. Apr 1993 A
5290507 Runkle Mar 1994 A
5292370 Tsai et al. Mar 1994 A
5376475 Ovshinsky et al. Dec 1994 A
5411592 Ovshinsky et al. May 1995 A
5431967 Manthiram et al. Jul 1995 A
5518831 Tou et al. May 1996 A
5676919 Kawamura et al. Oct 1997 A
5750013 Lin May 1998 A
5776323 Kobashi Jul 1998 A
5958361 Laine et al. Sep 1999 A
5980977 Deng et al. Nov 1999 A
5989648 Phillips Nov 1999 A
6027585 Patterson et al. Feb 2000 A
6221125 Soda et al. Apr 2001 B1
6261484 Phillips et al. Jul 2001 B1
6274110 Kim et al. Aug 2001 B1
6329628 Kuo et al. Dec 2001 B1
6334882 Aaslund Jan 2002 B1
6376027 Lee et al. Apr 2002 B1
6409851 Sethuram et al. Jun 2002 B1
6428600 Flurschuetz et al. Aug 2002 B1
6543380 Sung-Spitzl Apr 2003 B1
6551377 Leonhardt Apr 2003 B1
6569397 Yadav et al. May 2003 B1
6579573 Strutt et al. Jun 2003 B2
6589311 Han et al. Jul 2003 B1
6652822 Phillips et al. Nov 2003 B2
6676728 Han et al. Jan 2004 B2
6689192 Phillips et al. Feb 2004 B1
6752979 Talbot et al. Jun 2004 B1
6755886 Phillips et al. Jun 2004 B2
6780219 Singh et al. Aug 2004 B2
6793849 Gruen et al. Sep 2004 B1
6805822 Takei et al. Oct 2004 B2
6838072 Kong et al. Jan 2005 B1
6869550 Dorfman et al. Mar 2005 B2
6902745 Lee et al. Jun 2005 B2
6919257 Gealy et al. Jul 2005 B2
6919527 Boulos et al. Jul 2005 B2
6989529 Wiseman Jan 2006 B2
7066980 Akimoto et al. Jun 2006 B2
7091441 Kuo Aug 2006 B1
7108733 Enokido Sep 2006 B2
7125537 Liao et al. Oct 2006 B2
7125822 Nakano et al. Oct 2006 B2
7175786 Celikkaya et al. Feb 2007 B2
7182929 Singhal et al. Feb 2007 B1
7220398 Sutorik et al. May 2007 B2
7235118 Bouaricha et al. Jun 2007 B2
7285194 Uno et al. Oct 2007 B2
7285307 Hohenthanner et al. Oct 2007 B2
7297310 Peng et al. Nov 2007 B1
7297892 Kelley et al. Nov 2007 B2
7344776 Kollmann et al. Mar 2008 B2
7357910 Phillips et al. Apr 2008 B2
7368130 Kim et al. May 2008 B2
7374704 Che et al. May 2008 B2
7375303 Twarog May 2008 B2
7431750 Liao et al. Oct 2008 B2
7442271 Asmussen et al. Oct 2008 B2
7491468 Okada et al. Feb 2009 B2
7517513 Sarkas et al. Apr 2009 B2
7524353 Johnson et al. Apr 2009 B2
7534296 Swain et al. May 2009 B2
7572315 Boulos et al. Aug 2009 B2
7622211 Vyas et al. Nov 2009 B2
7629553 Fanson et al. Dec 2009 B2
7700152 Laine et al. Apr 2010 B2
7776303 Hung et al. Aug 2010 B2
7806077 Lee et al. Oct 2010 B2
7828999 Yubuta et al. Nov 2010 B2
7901658 Weppner et al. Mar 2011 B2
7931836 Xie et al. Apr 2011 B2
7939141 Matthews et al. May 2011 B2
8007691 Sawaki et al. Aug 2011 B2
8043405 Johnson et al. Oct 2011 B2
8092941 Weppner et al. Jan 2012 B2
8101061 Suh et al. Jan 2012 B2
8168128 Seeley et al. May 2012 B2
8178240 Wang et al. May 2012 B2
8192865 Buiel et al. Jun 2012 B2
8193291 Zhang Jun 2012 B2
8211388 Woodfield et al. Jul 2012 B2
8268230 Cherepy et al. Sep 2012 B2
8283275 Heo et al. Oct 2012 B2
8303926 Luhrs et al. Nov 2012 B1
8329090 Hollingsworth et al. Dec 2012 B2
8329257 Larouche et al. Dec 2012 B2
8338323 Takasu et al. Dec 2012 B2
8389160 Venkatachalam et al. Mar 2013 B2
8420043 Gamo et al. Apr 2013 B2
8439998 Ito et al. May 2013 B2
8449950 Shang et al. May 2013 B2
8478785 Jamjoom et al. Jul 2013 B2
8492303 Bulan et al. Jul 2013 B2
8529996 Bocian et al. Sep 2013 B2
8592767 Rappe et al. Nov 2013 B2
8597722 Albano et al. Dec 2013 B2
8623555 Kang et al. Jan 2014 B2
8658317 Weppner et al. Feb 2014 B2
8685593 Dadheech et al. Apr 2014 B2
8728680 Mikhail et al. May 2014 B2
8735022 Schlag et al. May 2014 B2
8748785 Jordan et al. Jun 2014 B2
8758957 Dadheech et al. Jun 2014 B2
8784706 Shevchenko et al. Jul 2014 B2
8822000 Kumagai et al. Sep 2014 B2
8840701 Borland et al. Sep 2014 B2
8877119 Jordan et al. Nov 2014 B2
8911529 Withers et al. Dec 2014 B2
8919428 Cola et al. Dec 2014 B2
8945431 Schulz et al. Feb 2015 B2
8951496 Hadidi et al. Feb 2015 B2
8956785 Dadheech et al. Feb 2015 B2
8968587 Shin et al. Mar 2015 B2
8968669 Chen Mar 2015 B2
8980485 Lanning et al. Mar 2015 B2
8999440 Zenasni et al. Apr 2015 B2
9023259 Hadidi et al. May 2015 B2
9065141 Merzougui et al. Jun 2015 B2
9067264 Moxson et al. Jun 2015 B2
9079778 Kelley et al. Jul 2015 B2
9085490 Taylor et al. Jul 2015 B2
9101982 Aslund Aug 2015 B2
9136569 Song et al. Sep 2015 B2
9150422 Nakayama et al. Oct 2015 B2
9193133 Shin et al. Nov 2015 B2
9196901 Se-Hee et al. Nov 2015 B2
9196905 Tzeng et al. Nov 2015 B2
9206085 Hadidi et al. Dec 2015 B2
9242224 Redjdal et al. Jan 2016 B2
9259785 Hadidi et al. Feb 2016 B2
9293302 Risby et al. Mar 2016 B2
9321071 Jordan et al. Apr 2016 B2
9322081 McHugh et al. Apr 2016 B2
9352278 Spatz et al. May 2016 B2
9356281 Verbrugge et al. May 2016 B2
9368772 Chen et al. Jun 2016 B1
9412998 Rojeski et al. Aug 2016 B2
9421612 Fang et al. Aug 2016 B2
9425463 Hsu et al. Aug 2016 B2
9463435 Schulz et al. Oct 2016 B2
9520600 Dadheech et al. Dec 2016 B2
9624565 Lee et al. Apr 2017 B2
9630162 Sunkara et al. Apr 2017 B1
9643891 Hadidi et al. May 2017 B2
9700877 Kim et al. Jul 2017 B2
9705136 Rojeski Jul 2017 B2
9718131 Boulos et al. Aug 2017 B2
9735427 Zhang Aug 2017 B2
9738788 Gross et al. Aug 2017 B1
9751129 Boulos et al. Sep 2017 B2
9768033 Ranjan et al. Sep 2017 B2
9776378 Choi Oct 2017 B2
9782791 Redjdal et al. Oct 2017 B2
9782828 Wilkinson Oct 2017 B2
9796019 She et al. Oct 2017 B2
9796020 Aslund Oct 2017 B2
9831503 Sopchak Nov 2017 B2
9871248 Rayner et al. Jan 2018 B2
9879344 Lee et al. Jan 2018 B2
9899674 Hirai et al. Feb 2018 B2
9917299 Behan et al. Mar 2018 B2
9932673 Jordan et al. Apr 2018 B2
9945034 Yao et al. Apr 2018 B2
9947926 Kim et al. Apr 2018 B2
9981284 Guo et al. May 2018 B2
9991458 Rosenman et al. Jun 2018 B2
9999922 Struve Jun 2018 B1
10011491 Lee et al. Jul 2018 B2
10050303 Anandan et al. Aug 2018 B2
10057986 Prud'homme et al. Aug 2018 B2
10065240 Chen Sep 2018 B2
10079392 Huang et al. Sep 2018 B2
10116000 Federici et al. Oct 2018 B1
10130994 Fang et al. Nov 2018 B2
10167556 Ruzic et al. Jan 2019 B2
10170753 Ren et al. Jan 2019 B2
10193142 Rojeski Jan 2019 B2
10244614 Foret Mar 2019 B2
10319537 Claussen et al. Jun 2019 B2
10333183 Sloop Jun 2019 B2
10350680 Yamamoto et al. Jul 2019 B2
10411253 Tzeng et al. Sep 2019 B2
10439206 Behan et al. Oct 2019 B2
10442000 Fukada et al. Oct 2019 B2
10461298 Herle Oct 2019 B2
10477665 Hadidi et al. Nov 2019 B2
10493524 She et al. Dec 2019 B2
10522300 Yang Dec 2019 B2
10526684 Ekman et al. Jan 2020 B2
10529486 Nishisaka Jan 2020 B2
10543534 Hadidi et al. Jan 2020 B2
10593985 Sastry et al. Mar 2020 B2
10610929 Fang et al. Apr 2020 B2
10637029 Gotlib Vainshtein et al. Apr 2020 B2
10638592 Foret Apr 2020 B2
10639712 Barnes et al. May 2020 B2
10647824 Hwang et al. May 2020 B2
10655206 Moon et al. May 2020 B2
10665890 Kang et al. May 2020 B2
10668566 Smathers et al. Jun 2020 B2
10669437 Cox et al. Jun 2020 B2
10688564 Boulos et al. Jun 2020 B2
10707477 Sastry et al. Jul 2020 B2
10717150 Aleksandrov et al. Jul 2020 B2
10727477 Kim et al. Jul 2020 B2
10741845 Yushin et al. Aug 2020 B2
10744590 Maier et al. Aug 2020 B2
10756334 Stowell et al. Aug 2020 B2
10766787 Sunkara et al. Sep 2020 B1
10777804 Sastry et al. Sep 2020 B2
10858255 Koziol et al. Dec 2020 B2
10858500 Chen et al. Dec 2020 B2
10892477 Choi et al. Jan 2021 B2
10930473 Paukner et al. Feb 2021 B2
10943744 Sungail et al. Mar 2021 B2
10944093 Paz et al. Mar 2021 B2
10964938 Rojeski Mar 2021 B2
10987735 Hadidi et al. Apr 2021 B2
10998552 Lanning et al. May 2021 B2
11031641 Gupta et al. Jun 2021 B2
11050061 Kim et al. Jun 2021 B2
11072533 Shevchenko et al. Jul 2021 B2
11077524 Smathers et al. Aug 2021 B2
11108050 Kim et al. Aug 2021 B2
11116000 Sandberg et al. Sep 2021 B2
11130175 Parrish et al. Sep 2021 B2
11130994 Shachar et al. Sep 2021 B2
11133495 Gazda et al. Sep 2021 B2
11148202 Hadidi et al. Oct 2021 B2
11167556 Shimada et al. Nov 2021 B2
11170753 Nomura et al. Nov 2021 B2
11171322 Seol et al. Nov 2021 B2
11183682 Sunkara et al. Nov 2021 B2
11193142 Angelidaki et al. Dec 2021 B2
11196045 Dadheech et al. Dec 2021 B2
11219884 Takeda et al. Jan 2022 B2
11244614 He et al. Feb 2022 B2
11245065 Ouderkirk et al. Feb 2022 B1
11245109 Tzeng et al. Feb 2022 B2
11254585 Ekman et al. Feb 2022 B2
11273322 Zanata et al. Mar 2022 B2
11273491 Barnes et al. Mar 2022 B2
11299397 Lanning et al. Apr 2022 B2
11311938 Badwe et al. Apr 2022 B2
11319537 Dames et al. May 2022 B2
11333183 Desai et al. May 2022 B2
11335911 Lanning et al. May 2022 B2
11350680 Rutkoski et al. Jun 2022 B2
11411253 Busacca et al. Aug 2022 B2
11439206 Santos Sep 2022 B2
11442000 Vaez-Iravani et al. Sep 2022 B2
11461298 Shemmer et al. Oct 2022 B1
11465201 Barnes et al. Oct 2022 B2
11471941 Barnes et al. Oct 2022 B2
11477665 Franke et al. Oct 2022 B2
11577314 Hadidi et al. Feb 2023 B2
11590568 Badwe et al. Feb 2023 B2
11611130 Wrobel et al. Mar 2023 B2
11633785 Badwe et al. Apr 2023 B2
20010016283 Shiraishi et al. Aug 2001 A1
20010021740 Lodyga et al. Sep 2001 A1
20020112794 Sethuram et al. Aug 2002 A1
20030027021 Sharivker et al. Feb 2003 A1
20030129497 Yamamoto et al. Jul 2003 A1
20030172772 Sethuram et al. Sep 2003 A1
20030186128 Singh et al. Oct 2003 A1
20030207978 Yadav et al. Nov 2003 A1
20040013941 Kobayashi et al. Jan 2004 A1
20040045807 Sarkas et al. Mar 2004 A1
20040060387 Tanner-Jones Apr 2004 A1
20040123699 Liao et al. Jul 2004 A1
20050025698 Talbot et al. Feb 2005 A1
20050163696 Uhm et al. Jul 2005 A1
20050242070 Hammer Nov 2005 A1
20050260786 Yoshikawa et al. Nov 2005 A1
20060040168 Sridhar Feb 2006 A1
20060141153 Kubota et al. Jun 2006 A1
20060145124 Hsiao et al. Jul 2006 A1
20060291827 Suib et al. Dec 2006 A1
20070077350 Hohenthanner et al. Apr 2007 A1
20070089860 Hou et al. Apr 2007 A1
20070209758 Sompalli et al. Sep 2007 A1
20070221635 Boulos et al. Sep 2007 A1
20070259768 Kear et al. Nov 2007 A1
20080029485 Kelley et al. Feb 2008 A1
20080182114 Kim et al. Jul 2008 A1
20080220244 Wai et al. Sep 2008 A1
20080286490 Bogdanoff et al. Nov 2008 A1
20080296268 Mike et al. Dec 2008 A1
20080305025 Vitner et al. Dec 2008 A1
20090074655 Suciu Mar 2009 A1
20090093553 Kleine et al. Apr 2009 A1
20090155689 Zaghib et al. Jun 2009 A1
20090202869 Sawaki et al. Aug 2009 A1
20090258255 Terashima et al. Oct 2009 A1
20090305132 Gauthier et al. Dec 2009 A1
20100007162 Han et al. Jan 2010 A1
20100096362 Hirayama et al. Apr 2010 A1
20100176524 Burgess et al. Jul 2010 A1
20110006254 Richard et al. Jan 2011 A1
20120015284 Merzougui et al. Jan 2012 A1
20120027955 Sunkara et al. Feb 2012 A1
20120034135 Risby Feb 2012 A1
20120048064 Kasper et al. Mar 2012 A1
20120051962 Imam et al. Mar 2012 A1
20120074342 Kim et al. Mar 2012 A1
20120100438 Fasching et al. Apr 2012 A1
20120122017 Mills May 2012 A1
20120230860 Ward-Close et al. Sep 2012 A1
20120240726 Kim et al. Sep 2012 A1
20120294919 Jaynes et al. Nov 2012 A1
20130032753 Yamamoto et al. Feb 2013 A1
20130071284 Kano et al. Mar 2013 A1
20130078508 Tolbert et al. Mar 2013 A1
20130084474 Mills Apr 2013 A1
20140202286 Yokoyama et al. Jul 2014 A1
20140272430 Kalayaraman Sep 2014 A1
20140322632 Sugimoto et al. Oct 2014 A1
20140373344 Takada et al. Dec 2014 A1
20150000844 Woo Jan 2015 A1
20150101454 Shimizu et al. Apr 2015 A1
20150167143 Luce et al. Jun 2015 A1
20150171455 Mills Jun 2015 A1
20150255767 Aetukuri et al. Sep 2015 A1
20150259220 Rosocha et al. Sep 2015 A1
20150333307 Thokchom et al. Nov 2015 A1
20160028088 Romeo et al. Jan 2016 A1
20160045841 Kaplan et al. Feb 2016 A1
20160152480 Jang et al. Jun 2016 A1
20160285090 Ozkan et al. Sep 2016 A1
20160287113 Hebert et al. Oct 2016 A1
20160308244 Badding et al. Oct 2016 A1
20160332232 Forbes et al. Nov 2016 A1
20160351910 Albano et al. Dec 2016 A1
20170009328 Germann et al. Jan 2017 A1
20170070180 Mills Mar 2017 A1
20170113935 Pennington et al. Apr 2017 A1
20170120339 Aslund May 2017 A1
20170125842 Meguro et al. May 2017 A1
20170151609 Elsen et al. Jun 2017 A1
20170176977 Huang et al. Jun 2017 A1
20170179477 Walters et al. Jun 2017 A1
20170368604 Wilkinson Dec 2017 A1
20170373344 Hadidi et al. Dec 2017 A1
20180022928 Blush Jan 2018 A1
20180083264 Soppe Mar 2018 A1
20180104745 L'Esperance et al. Apr 2018 A1
20180159178 Weisenstein et al. Jun 2018 A1
20180169763 Dorval et al. Jun 2018 A1
20180214956 Larouche et al. Aug 2018 A1
20180241956 Suzuki Aug 2018 A1
20180248175 Ghezelbash et al. Aug 2018 A1
20180277849 Gayden Sep 2018 A1
20180346344 Chen et al. Dec 2018 A1
20180366707 Johnson et al. Dec 2018 A1
20180375149 Beck et al. Dec 2018 A1
20190001416 Larouche et al. Jan 2019 A1
20190061005 Kelkar Feb 2019 A1
20190084290 Stoyanov et al. Mar 2019 A1
20190125842 Grabowski May 2019 A1
20190127835 Yang et al. May 2019 A1
20190160528 McGee et al. May 2019 A1
20190165413 Furusawa May 2019 A1
20190173130 Schuhmacher et al. Jun 2019 A1
20190218650 Subramanian et al. Jul 2019 A1
20190271068 Sungail et al. Sep 2019 A1
20190292441 Hill et al. Sep 2019 A1
20190334206 Sastry et al. Oct 2019 A1
20190341650 Lanning et al. Nov 2019 A9
20190348202 Sachdev et al. Nov 2019 A1
20190362936 Van Den Berg et al. Nov 2019 A1
20190389734 Dietz et al. Dec 2019 A1
20200067128 Chmiola et al. Feb 2020 A1
20200136176 Chen Apr 2020 A1
20200153037 Renna et al. May 2020 A1
20200198977 Hof et al. Jun 2020 A1
20200203706 Holman et al. Jun 2020 A1
20200207668 Cavalli et al. Jul 2020 A1
20200220222 Watarai et al. Jul 2020 A1
20200223704 Neale et al. Jul 2020 A1
20200227728 Huang et al. Jul 2020 A1
20200254432 Shirman et al. Aug 2020 A1
20200276638 King et al. Sep 2020 A1
20200288561 Huh Sep 2020 A1
20200314991 Duanmu et al. Oct 2020 A1
20200335754 Ramasubramanian et al. Oct 2020 A1
20200335781 Oshita et al. Oct 2020 A1
20200350565 Oshita et al. Nov 2020 A1
20200358093 Oshita et al. Nov 2020 A1
20200358096 Paulsen et al. Nov 2020 A1
20200388857 Sunkara et al. Dec 2020 A1
20200391295 Dorval et al. Dec 2020 A1
20200395607 Tzeng Dec 2020 A1
20200407858 Sano et al. Dec 2020 A1
20210047186 Ifuku et al. Feb 2021 A1
20210075000 Holman et al. Mar 2021 A1
20210085468 Ryd et al. Mar 2021 A1
20210139331 Kang et al. May 2021 A1
20210146432 Badwe et al. May 2021 A1
20210187614 Tsubota et al. Jun 2021 A1
20210226302 Lanning et al. Jul 2021 A1
20210253430 Zaplotnik et al. Aug 2021 A1
20210273292 Yun et al. Sep 2021 A1
20210276094 Sobu et al. Sep 2021 A1
20210296731 Wrobel et al. Sep 2021 A1
20210310110 Stowell et al. Oct 2021 A1
20210344059 Ekman et al. Nov 2021 A1
20210367264 Hadidi et al. Nov 2021 A1
20210408533 Holman et al. Dec 2021 A1
20220041457 Pullen et al. Feb 2022 A1
20220095445 Shang et al. Mar 2022 A1
20220118517 Hadidi et al. Apr 2022 A1
20220127145 Ding et al. Apr 2022 A1
20220134431 Badwe et al. May 2022 A1
20220143693 Larouche et al. May 2022 A1
20220223379 Holman et al. Jul 2022 A1
20220228288 Holman et al. Jul 2022 A1
20220267216 Holman et al. Aug 2022 A1
20220314325 Badwe Oct 2022 A1
20220324022 Badwe Oct 2022 A1
20230001375 Kozlowski et al. Jan 2023 A1
20230001376 Kozlowski et al. Jan 2023 A1
20230032362 Holman et al. Feb 2023 A1
20230144075 Badwe et al. May 2023 A1
Foreign Referenced Citations (230)
Number Date Country
2003211869 Sep 2003 AU
2014394102 Jun 2020 AU
2947531 Nov 2015 CA
1188073 Jul 1998 CN
1653869 Aug 2005 CN
1675785 Sep 2005 CN
1967911 May 2007 CN
101191204 Jun 2008 CN
101391307 Mar 2009 CN
101728509 Jun 2010 CN
101716686 Feb 2011 CN
102179521 Sep 2011 CN
102394290 Mar 2012 CN
102412377 Apr 2012 CN
102427130 Apr 2012 CN
102664273 Sep 2012 CN
102723502 Oct 2012 CN
102867940 Jan 2013 CN
102983312 Mar 2013 CN
103121105 May 2013 CN
103402921 Nov 2013 CN
102554242 Dec 2013 CN
103456926 Dec 2013 CN
103682372 Mar 2014 CN
103682383 Mar 2014 CN
103700815 Apr 2014 CN
103874538 Jun 2014 CN
103956520 Jul 2014 CN
104064736 Sep 2014 CN
104084592 Oct 2014 CN
104209526 Dec 2014 CN
104218213 Dec 2014 CN
204156003 Feb 2015 CN
104485452 Apr 2015 CN
104752734 Jul 2015 CN
104772473 Jul 2015 CN
103515590 Sep 2015 CN
105514373 Apr 2016 CN
106159316 Nov 2016 CN
106450146 Feb 2017 CN
106493350 Mar 2017 CN
206040854 Mar 2017 CN
106684387 May 2017 CN
106784692 May 2017 CN
107093732 Aug 2017 CN
107579241 Jan 2018 CN
108134104 Jun 2018 CN
108145170 Jun 2018 CN
108217612 Jun 2018 CN
108649190 Oct 2018 CN
108907210 Nov 2018 CN
108963239 Dec 2018 CN
109167070 Jan 2019 CN
109301212 Feb 2019 CN
109616622 Apr 2019 CN
109742320 May 2019 CN
109888233 Jun 2019 CN
110153434 Aug 2019 CN
110299516 Oct 2019 CN
110790263 Feb 2020 CN
110993908 Apr 2020 CN
111099577 May 2020 CN
111342163 Jun 2020 CN
111370751 Jul 2020 CN
111403701 Jul 2020 CN
111515391 Aug 2020 CN
111970807 Nov 2020 CN
112259740 Jan 2021 CN
112331947 Feb 2021 CN
112397706 Feb 2021 CN
112421006 Feb 2021 CN
112421048 Feb 2021 CN
112447977 Mar 2021 CN
112768709 May 2021 CN
112768710 May 2021 CN
112768711 May 2021 CN
112864453 May 2021 CN
113097487 Jul 2021 CN
113104838 Jul 2021 CN
113764688 Dec 2021 CN
113871581 Dec 2021 CN
114388822 Apr 2022 CN
114744315 Jul 2022 CN
114824297 Jul 2022 CN
115394976 Nov 2022 CN
10335355 Nov 2004 DE
102009033251 Sep 2010 DE
102010006440 Aug 2011 DE
102011109137 Feb 2013 DE
102018132896 Jun 2020 DE
0256233 Feb 1988 EP
2292557 Mar 2011 EP
3143838 Mar 2017 EP
3474978 May 2019 EP
2525122 Oct 1983 FR
2591412 Jun 1987 FR
2595745 Dec 2021 GB
202011017775 Oct 2021 IN
10-172564 Jun 1998 JP
11-064556 Mar 1999 JP
2001-348296 Dec 2001 JP
2004-505761 Feb 2004 JP
2004-193115 Jul 2004 JP
2004-311297 Nov 2004 JP
2004-362895 Dec 2004 JP
2005-015282 Jan 2005 JP
2005-072015 Mar 2005 JP
2005-076052 Mar 2005 JP
2005-135755 May 2005 JP
2005-187295 Jul 2005 JP
2005-222956 Aug 2005 JP
2005-272284 Oct 2005 JP
2006-040722 Feb 2006 JP
2007-113120 May 2007 JP
2007-138287 Jun 2007 JP
2007-149513 Jun 2007 JP
2007-238402 Sep 2007 JP
2008-230905 Oct 2008 JP
2008-243447 Oct 2008 JP
2009-187754 Aug 2009 JP
2010-024506 Feb 2010 JP
2010-097914 Apr 2010 JP
2011-108406 Jun 2011 JP
2011-222323 Nov 2011 JP
2011-258348 Dec 2011 JP
2012-046393 Mar 2012 JP
2012-151052 Aug 2012 JP
2013-062242 Apr 2013 JP
2013-063539 Apr 2013 JP
2013-076130 Apr 2013 JP
2015-048269 Mar 2015 JP
2015-122218 Jul 2015 JP
2016-029193 Mar 2016 JP
2016-047961 Apr 2016 JP
6103499 Mar 2017 JP
2017-524628 Aug 2017 JP
2018-141762 Sep 2018 JP
2018-190563 Nov 2018 JP
2019-516020 Jun 2019 JP
2020-121898 Aug 2020 JP
2021-061089 Apr 2021 JP
2021-061090 Apr 2021 JP
2021-116191 Aug 2021 JP
10-2007-0076686 Jul 2007 KR
10-2009-0070140 Jul 2009 KR
10-1133094 Apr 2012 KR
10-2017-0039922 Apr 2017 KR
10-2017-0045181 Apr 2017 KR
10-2018-0001799 Jan 2018 KR
10-2018-0035750 Apr 2018 KR
10-1907912 Oct 2018 KR
10-1907916 Oct 2018 KR
10-1923466 Nov 2018 KR
10-2101006 Apr 2020 KR
10-2124946 Jun 2020 KR
10-2020-0131751 Nov 2020 KR
10-2021-0057253 May 2021 KR
2744449 Mar 2021 RU
521539 Feb 2003 TW
200823313 Jun 2008 TW
1329143 Aug 2010 TW
201411922 Mar 2014 TW
0377333 Sep 2003 WO
2004054017 Jun 2004 WO
2004089821 Oct 2004 WO
2005039752 May 2005 WO
2006100837 Sep 2006 WO
2010095726 Aug 2010 WO
2011082596 Jul 2011 WO
2011090779 Jul 2011 WO
2012023858 Feb 2012 WO
2012114108 Aug 2012 WO
2012144424 Oct 2012 WO
2012162743 Dec 2012 WO
2013017217 Feb 2013 WO
2014011239 Jan 2014 WO
2014110604 Jul 2014 WO
2014153318 Sep 2014 WO
2015064633 May 2015 WO
2015174949 Nov 2015 WO
2016048862 Mar 2016 WO
2016091957 Jun 2016 WO
2017074081 May 2017 WO
2017074084 May 2017 WO
2017080978 May 2017 WO
2017091543 Jun 2017 WO
2017106601 Jul 2017 WO
2017118955 Jul 2017 WO
2017130946 Aug 2017 WO
2017158349 Sep 2017 WO
2017177315 Oct 2017 WO
2017178841 Oct 2017 WO
2017223482 Dec 2017 WO
2018133429 Jul 2018 WO
2018141082 Aug 2018 WO
2019045923 Mar 2019 WO
2019052670 Mar 2019 WO
2019095039 May 2019 WO
2019139773 Jul 2019 WO
2019243870 Dec 2019 WO
2019246242 Dec 2019 WO
2019246257 Dec 2019 WO
2020009955 Jan 2020 WO
2020041767 Feb 2020 WO
2020041775 Feb 2020 WO
2020091854 May 2020 WO
2020132343 Jun 2020 WO
2020223358 Nov 2020 WO
2020223374 Nov 2020 WO
2021029769 Feb 2021 WO
2021046249 Mar 2021 WO
2021085670 May 2021 WO
2021115596 Jun 2021 WO
2021118762 Jun 2021 WO
2021127132 Jun 2021 WO
2021191281 Sep 2021 WO
2021245410 Dec 2021 WO
2021245411 Dec 2021 WO
2021263273 Dec 2021 WO
2022005999 Jan 2022 WO
2022032301 Feb 2022 WO
2022043701 Mar 2022 WO
2022043702 Mar 2022 WO
2022043704 Mar 2022 WO
2022043705 Mar 2022 WO
2022067303 Mar 2022 WO
2022075846 Apr 2022 WO
2022107907 May 2022 WO
2022133585 Jun 2022 WO
2022136699 Jun 2022 WO
Non-Patent Literature Citations (121)
Entry
“Build Boldly”, Technology Demonstration, 6K Additive, [publication date unknown], in 11 pages.
“High-entropy alloy”, Wikipedia, webpage last edited Dec. 29, 2022 (accessed Jan. 17, 2023), in 16 pages. URL: https://en.wikipedia.org/wiki/High-entropy_alloy.
Ajayi, B. et al., “A rapid and scalable method for making mixed metal oxide alloys for enabling accelerated materials discovery”, Journal of Materials Research, Jun. 2016, vol. 31, No. 11, pp. 1596-1607.
Ajayi, B. P. et al., “Atmospheric plasma spray pyrolysis of lithiated nickel-manganese-cobalt oxides for cathodes in lithium ion batteries”, Chemical Engineering Science, vol. 174, Sep. 14, 2017, pp. 302-310.
Ali, M. et al., Spray Flame Synthesis (SFS) of Lithium Lanthanum Zirconate (LLZO) Solid Electrolyte, Materials, vol. 14, No. 13, 2021, pp. 1-13.
Australian Office Action, re AU Application No. 2016370962, mailed May 29, 2020.
Barbis et al., “Titanium powders from the hydride-dehydride process.” Titanium Powder Metallurgy. Butterworth-Heinemann, 2015. pp. 101-116.
Bardos, L., et al., “Differences between microwave and RF activation of nitrogen for the PECVD process”, J. Phys. D: Appl. Phys., vol. 15, 1982, pp. 79-82.
Bardos, L., et al., “Microwave Plasma Sources and Methods in Processing Technology”, IEEE Press, 2022, 10 pages.
Bobzin, K. et al., “Modelling and Diagnostics of Multiple Cathodes Plasma Torch System for Plasma Spraying”, Frontiers of Mechanical Engineering, Sep. 2011, vol. 6, pp. 324-331.
Bobzin, K. et al., “Numerical and Experimental Determination of Plasma Temperature during Air Plasma Spraying with a Multiple Cathodes Torch”, Journal of Materials Processing Technology, Oct. 2011, vol. 211, pp. 1620-1628.
Boulos, M. I., “The inductively coupled radio frequency plasma.” Journal of High Temperature Material Process, Jan. 1997, vol. 1, pp. 17-39.
Boulos, M., “Induction Plasma Processing of Materials for Powders, Coatings, and Near-Net-Shape Parts”, Advanced Materials & Processes, Aug. 2011, pp. 52-53, in 3 pages.
Boulos, M., “Plasma power can make better powders”, Metal Powder Report, May 2004, vol. 59(5), pp. 16-21.
Canadian Office Action, re CA Application No. 3009630 mailed Oct. 19, 2022.
Carreon, H. et al., “Study of Aging Effects in a Ti—6Al—4V alloy with Widmanstatten and Equiaxed Microstructures by Non-destructive Means”, AIP Conference Proceedings 1581, 2014 (published online Feb. 17, 2015), pp. 739-745.
Chang, S. et al., “One-Step Fast Synthesis of Li4Ti5012 Particles Using an Atmospheric Pressure Plasma Jet”, Journal of the American Ceramic Society, Dec. 26, 2013, vol. 97, No. 3, pp. 708-712.
Chen, G. et al., “Spherical Ti—6Al—4V Powders Produced by Gas Atomization”, Key Engineering Materials, vol. 704, Aug. 2016, pp. 287-292. URL: https://www.scientific.net/KEM.704.287.
Chikumba et al., “High Entropy Alloys: Development and Applications” 7th International Conference on Latest Trends in Engineering & Technology (ICLTET'2015) Nov. 26-27, 2015 Irene, Pretoria (South Africa).
Chinese Office Action, re CN Application No, 201680082035.1, mailed Sep. 2, 2020.
Chinese Office Action, re CN Application No. 201680082035.1, mailed Mar. 11, 2021.
Chinese Office Action, re CN Application No. 201680082035.1, mailed Sep. 7, 2021.
Choi, S. I., et al., “Continuous process of carbon nanotubes synthesis by decomposition of methane using an arc-jet plasma”, Thin Solid Films, 2006, vol. 506-507, 2006, pp. 244-249.
Coldwell, D. M. et al., “The reduction of SiO.sub.2 with Carbon in a Plasma”, Journal of Electrochemical Society, Jan. 1977, vol. 124, pp. 1686-1689.
Collin, J. E., et al., “Ionization of methane and it's electronic energy levels”, Canadian Journal of Chemistry, 2011, vol. 45, No. 16, pp. 1875-1882.
Dearmiti, C., “26. Functional Fillers for Plastics”, in Applied Plastics Engineering Handbook—Processing and Materials, ed., Myer Kuiz, Elsevier, 2011, pp. 455-468.
Decker, J., et al., “Sample preparation protocols for realization of reproducible characterization of single-wall carbon nanotubes”, Metrologia, 2009, vol. 46, No. 6, pp. 682-692.
Ding, F., et al., “Nucleation and Growth of Single-Walled Carbon Nanotubes: A Molecular Dynamics Study”, J. Phys. Chem. B, vol. 108, 2004, pp. 17369-17377.
Ding, F., et al., “The Importance of Strong Carbon-Metal Adhesion for Catalytic Nucleation of Single-Walled Carbon Nanotubes”, Nano Letters, 2008, vol. 8, No. 2, pp. 463-468.
Dolbec, R., “Recycling Spherical Powders”, Presented at Titanium 2015, Orlando, FL, Oct. 2015, in 20 pages.
Dors, M., et al., “Chemical Kinetics of Methane Pyrolysis in Microwave Plasma at Atmospheric Pressure”, Plasma Chem Plasma Process, 2013, vol. 34, No. 2, pp. 313-326.
Eremin, A., et al., “The Role of Methyl Radical in Soot Formation”, Combustion Science and Technology, vol. 191, No. 12, 2008, pp. 2226-2242.
European Office Action, re EP Application No. 16876747.3, dated Jan. 26, 2021.
European Office Action, re EP Application No. 16876747.3, dated Jun. 12, 2019.
European Office Action, re EP Application No. 16876747.3, dated May 18, 2020.
European Office Action, re EP Application No. 16876747.3, dated Sep. 8, 2021.
European Office Action, re EP Application No. 17816316.8, dated Feb. 5, 2020.
European Office Action, re EP Application No. 18923334.9, dated Dec. 12, 2022.
European Office Action, re EP Application No. 18923334.9, dated Dec. 9, 2021.
European Office Action, re EP Application No. 19735153.9, dated Dec. 12, 2022, 11 pages.
European Office Action, re EP Application No. 19740115, dated Mar. 2, 2023, 6 pages.
Finckle, J. R., et al., “Plasma Pyrolysis of Methane to Hydrogen and Carbon Black”, Industrial Engineering and Chemical Research, 2002. vol. 41, No. 6, 2002, pp. 1425-1435.
Fu, D., et al., “Direct synthesis of Y-junction carbon nanotubes by microwave-assisted pyrolysis of methane”, Materials Chemistry and Physics, vol. 118, vol. 2-3, 2009, pp. 501-505.
Fuchs, G.E. et al., “Microstructural evaluation of as-solidified and heat-treated y-TiAl based powders”, Materials Science and Engineering, 1992, A152, pp. 277-282.
Gleiman, S. et al., “Melting and spheroidization of hexagonal boron nitride in a microwave-powered, atmospheric pressure nitrogen plasma”, Journal of Materials Science, Aug. 2002, vol. 37(16), pp. 3429-3440.
Grace, J. et al., “Connecting particle sphericity and circularity”, Particuology, vol. 54, 2021, pp. 1-4, ISSN 1674-2001, https://doi .org/10.1016/j.partic.2020.09.006. (Year: 2020).
Gradl, P. et al., “GRCop-42 Development and Hot-fire Testing Using Additive Manufacturing Powder Bed Fusion for Channel-Cooled Combustion Chambers”, 55th AIAA/SAE/ASEE Joint Propulsion Conference 2019, Aug. 2019, pp. 1-26.
Haghighatpanah, S., et al., “Computational studies of catalyst-free single walled carbon nanotube growth”, J Chem Phys, vol. 139, No. 5, 10 pages, Aug. 6, 2013.
Haneklaus, N., et al., “Stop Smoking—Tube-In-Tube Helical System for Flameless Calcination of Minerals,” Processes, vol. 5, No. 4, Nov. 3, 2017, pp. 1-12.
He et al., “A precipitation-hardened high-entropy alloy with outstanding tensile properties” Acta Materialia 102, Jan. 2016, pp. 187-196.
Suryanarayana, C. et al., “Rapid solidification processing of titanium alloys”, International Materials Reviews, 1991, vol. 36, pp. 85-123.
Suryanarayana, C., “Recent Developments in Mechanical Alloying”, Reviews on Advanced Materials Science, Aug. 2008, vol. 18(3), pp. 203-211.
Tang, H. P. et al., “Effect of Powder Reuse Times on Additive Manufacturing of Ti—6Al—4V by Selective Electron Beam Melting”, JOM, Mar. 2015, vol. 67, pp. 555-563.
Van Laar, J. H. et al., “Spheroidization of Iron Powder in a Microwave Plasma Reactor”, Journal of the Southern African Institute of Mining and Metallurgy, Oct. 2016, vol. 116, No. 10, pp. 941-946.
Veith, M. et al., “Low temperature synthesis of nanocrystalline Y3Al5012 (YAG) and Ce-doped Y3Al5012 via different sol-gel methods.” J. Mater Chem, (1999) 9: 3069-3079.
Walter et al., “Microstructural and mechanical characterization of sol gel-derived Si—O—C glasses” Journal of the European Ceramic Society, vol. 22, Issue 13, Dec. 2002, pp. 2389-2400.
Wang, H., et al., “A detailed kinetic modeling study of aromatics formation in laminar premixed acetylene and ethylene flames” Combustion and Flame, vol. 110, No. 1-2, 1997, pp. 173-221.
Wang, J. et al., “Preparation of Spherical Tungsten and Titanium Powders by RF Induction Plasma Processing”, Rare Metals, Jun. 2015 (published online May 31, 2014), vol. 34, No. 6, pp. 431-435.
Wang, Y. et al., “Developments in Nanostructured Cathode Materials for High-Performance Lithium-Ion Batteries”, Advanced Materials, Jun. 2008, pp. 2251-2269.
Yang et al., “Preparation of Spherical Titanium Powders from Polygonal Titanium Hydride Powders by Radio Frequency Plasma Treatment” Materials Transactions, vol. 54, No. 12 (2013) pp. 2313 to 2316.
Zavilopulo, A. N., et al., “Ionization and Dissociative Ionization of Methane Molecules”, Technical Physics, vol. 58, No. 9, 2013, pp. 1251-1257.
Zeng, X., et al., “Growth and morphology of carbon nanostructures by microwave-assisted pyrolysis of methane”, Physica E., vol. 42, No. 8, 2010, pp. 2103-2108.
Zhang , K., Ph.D., “The Microstructure and Properties of Hipped Powder Ti Alloys”, a thesis submitted to The University of Birmingham, College of Engineering and Physical Sciences, Apr. 2009, in 65 pages.
Zhang et al. “High thickness tungsten coating with low oxygen content prepared by air plasma spray”. Cailliao Gongcheng. (2014) (5) 23-28 {Year: 2014).
Zhang et al., Microstructures and properties of high-entropy alloys, Progress in Materials Science, vol. 61, 2013, pp. 1-93.
Zhang, H., et al., “Plasma activation of methane for hydrogen production in a N2 rotating gliding arc warm plasma: A chemical kinetics study”, Chemical Engineering Journal, vol. 345, 2018, pp. 67-78.
Zhang, J., et al., “Flexible and ion-conducting membrane electrolytes for solid-state lithium batteries: Dispersion of garnet nanoparticles in insulating polyethylene oxide”, Nano Energy, vol. 28, 2016, pp. 447-454.
Zhang, Y. D. et al., “High-energy cathode materials for Li-ion batteries: A review of recent developments”, Science China Technological Sciences, Sep. 2015, vol. 58(11), pp. 1809-1828.
Zhang, Y. S. et al., “Core-shell structured titanium-nitrogen alloys with high strength, high thermal stability and good plasticity”, Scientific Reports, Jan. 2017, vol. 7, in 8 pages.
Zhong, R., et al., “Continuous preparation and formation mechanism of few-layer graphene by gliding arc plasma”, Chemical Engineering Journal, vol. 387, 2020, 10 pages.
Zielinski, A et al., “Modeling and Analysis of a Dual-Channel Plasma Torch in Pulsed Mode Operation For Industrial Space, and Launch Applications”, IEEE Transactions on Plasma Science, Jul. 2015, vol. 43(7), pp. 2201-2206.
Houmes et al., “Microwave Synthesis of Ternary Nitride Materials”, Journal of Solid State Chemistry, vol. 130, Issue 2, May 1997, pp. 266-271.
Huo, H., et al., “Composite electrolytes of polyethylene oxides/garnets interfacially wetted by ionic liquid for room-temperature solid-state lithium battery”, Journal of Power Sources, vol. 372, 2017, pp. 1-7.
International Preliminary Report on Patentability and Written Opinion, re PCT Application No. PCT/US2016/067100, mailed Jun. 28, 2018.
International Preliminary Report on Patentability and Written Opinion, re PCT Application No. PCT/US2019/037956, mailed Dec. 30, 2020.
International Search Report and Written Opinion, re PCT Application No. PCT/2020/065536, mailed Mar. 5, 2021.
International Search Report and Written Opinion, re PCT Application No. PCT/IB2018/054523, mailed Nov. 2, 2018.
International Search Report and Written Opinion, re PCT Application No. PCT/US2016/067100, mailed Mar. 22, 2017.
International Search Report and Written Opinion, re PCT Application No. PCT/US2017/039049, mailed on Oct. 31, 2017.
International Search Report and Written Opinion, re PCT Application No. PCT/US2019/037956, mailed Oct. 1, 2019.
International Search Report and Written Opinion, re PCT Application No. PCT/US2019/037979, mailed Aug. 22, 2019.
Irle, S., et al., “Milestones in molecular dynamics simulations of single-walled carbon nanotube formation: A brief critical review”, Nano Research, 2009, vol. 2, No. 10, pp. 755-767.
Ivasishin, et al., “Innovative Process for Manufacturing Hydrogenated Titanium Powder for Solid State Production of R/M Titanium Alloy Components” Titanium 2010, Oct. 3-6, 2010, 27 pages.
Japanese Office Action, re JP Application No. 2022-537613, dated Apr. 18, 2023, 9 pages.
Jasek, O., et al., “Microwave plasma-based high temperature dehydrogenation of hydrocarbons and alcohols as a single route to highly efficient gas phase synthesis of freestanding graphene”, Nanotechnology, 2021, vol. 32, 11 pages.
Jasinski, M., et al., “Atmospheric pressure microwave plasma source for hydrogen production”, International Journal of Hydrogen Energy, vol. 38, Issue 26, 2013, pp. 11473-11483.
Jasinski, M., et al., “Hydrogen production via methane reforming using various microwave plasma sources”, Chem. Listy, 2008, vol. 102, pp. s1332-s1337.
Jia, H. et al., “Hierarchical porous silicon structures with extraordinary mechanical strength as high-performance lithium-ion battery anodes”, Nature Communications, Mar. 2020, vol. 11, in 9 pages. URL: https://doi.ora/10.1038/s41467-020-15217-9.
Kassel, L. S., “The Thermal Decomposition of Methane”, Journal of the American Chemical Society, vol. 54, No. 10, 1932, pp. 3949-3961.
Kerscher, F., et al., “Low-carbon hydrogen production via electron beam plasma methane pyrolysis: Techno-economic analysis and carbon footprint assessment”, International Journal of Hydrogen Energy, vol. 46, Issue 38, 2021, pp. 19897-19912.
Kim, K. S., et al., “Synthesis of single-walled carbon nanotubes by induction thermal plasma”, Nano Research, 2009, vol. 2, No. 10, pp. 800-817.
Ko, M. et al., “Challenges in Accommodating Volume Change of Si Anodes for Li-Ion Batteries”, Chem Electro Chem, Aug. 2015, vol. 2, pp. 1645-1651. URL: https://doi.org/10.1002/celc.201500254.
Kotlyarov, V. I. et al, “Production of Spherical Powders on the Basis of Group IV Metals for Additive Manufacturing”, Inorganic Materials: Applied Research, Pleiades Publishing, May 2017, vol. 8, No. 3, pp. 452-458.
Kumal, R. R., et al., “Microwave Plasma Formation of Nanographene and Graphitic Carbon Black”, C, 2020, vol. 6, No. 4, 10 pages.
Laine, R. M. et al., “Making nanosized oxide powders from precursors by flame spray pyrolysis”, Key Engineering Materials, Jan. 1999, vol. 159-160, pp. 17-24.
Lee, D. H., et al., “Comparative Study of Methane Activation Process by Different Plasma Sources”, Plasma Chem. Plasma Process., vol. 33, No. 4, 2013, pp. 647-661.
Lee, D. H., et al., “Mapping Plasma Chemistry in Hydrocarbon Fuel Processing Processes”, Plasma Chem. Plasma Process., vol. 33, No. 1, 2013, pp. 249-269.
Li, L. et al., “Spheroidization of silica powders by radio frequency inductively coupled plasma with Ar—H2 and Ar—N2 as the sheath gases at atmospheric pressure”, International Journal of Minerals, Metallurgy, and Materials, Sep. 2017, vol. 24(9), pp. 1067-1074.
Li, X. et al., “Mesoporous silicon sponge as an anti-pulverization structure for high-performance lithium-ion battery anodes”, Nature Communications, Jul. 2014, vol. 5, Article No. 4105, in 7 pages. URL: httDs://doi.orq/10.1038/ncomms5105.
Li, Z. et al., “Strong and Ductile Non-Equiatomic High-Entropy Alloys: Design, Processing, Microstructure, and Mechanical Properties”, The Journal of the Minerals, Metals & Materials Society, Aug. 2017, vol. 69(1), pp. 2099-2106. URL: https://doi.org/10.1007/s11837-017-2540-2.
Lin, M., “Gas Quenching with Air Products' Rapid Gas Quenching Gas Mixture”, Air Products, Dec. 31, 2007, in 4 pages. URL: https://www.airproducts.co.uk/-/media/airproducts/files/en/330/330-07-085-us-gas-quenching-with-air-products-rapid-gas-quenching-gas-mixture.pdf.
Liu, Y., et al., “Advances of microwave plasma-enhanced chemical vapor deposition in fabrication of carbon nanotubes: a review”, J Mater Sci., vol. 55, 2021, pp. 12559-12583.
Majewksi, T., “Investigation of W—Re—Ni heavy alloys produced from plasma spheroidized powders”, Solid State Phenomena, Mar. 2013, vol. 199, pp. 448-453.
Moisan, M. et al., “Waveguide-Based Single and Multiple Nozzle Plasma Torches: the Tiago Concept”, Plasma Sources Science and Technology, Jun. 2001, vol. 10, pp. 387-394.
Moldover, M. R. et al., “Measurement of the Universal Gas Constant R Using a Spherical Acoustic Resonator”, Physical Review Letters, Jan. 1988, vol. 60(4), pp. 249-252.
Muoio, C. et al., “Phase Homogeneity in Y2O3—MgO Nanocomposites Synthesized by Thermal Decomposition of Nitrate Precursors with Ammonium Acetate Additions” J_ Am. Ceram. Soc., 94[12] 4207-4217, 2011.
Murugan et al. “Nanostructured a/ß-tungsten by reduction of WO3 under microwave plasma”, Int. Journal of Refractory Metals and Hard Materials 29 (2011) 128-133. (Year: 2011).
Nichols, F. A., “On the spheroidization of rod-shaped particles of finite length”, Journal of Materials Science, Jun. 1976, vol. 11, pp. 1077-1082.
Nyutu, E. et al., “Ultrasonic Nozzle Spray in Situ Mixing and Microwave-Assisted Preparation of Nanocrystalline Spinel Metal Oxides: Nickel Ferrite and Zinc Aluminate”, Journal of Physical Chemistry C, Feb. 1, 2008, vol. 112, No. 5, pp. 1407-1414.
Ohta, R. et al., “Effect of PS-PVD production throughput on Si nanoparticles for negative electrode of lithium ion batteries”, Journal of Physics D: Applied Physics, Feb. 2018, vol. 51(1), in 7 pages.
Olsvik, O., et al., “Thermal Coupling of Methane—A Comparison Between Kinetic Model Data and Experimental Data”, Thermochimica Acta., vol. 232, No. 1, 1994, pp. 155-169.
Or, T. et al., “Recycling of mixed cathode lithium-ion batteries for electric vehicles: Current status and future outlook”, Carbon Energy, Jan. 2020, vol. 2, pp. 6-43. URL: https://doi.org/10.1002/cey2.29.
Park et al. “Preparation of spherical WTaMoNbV refractory high entropy alloy powder by inductively-coupled thermal plasma”, Materials Letters 255 (2019) 126513 (Year: 2019).
Popescu et al.. “New TiZrNbTaFe high entropy alloy used for medical applications” IOP Conference Series: Materials Science and Engineering 400. Mod Tech 2018 (2018), 9 pages.
Pulsation Reactors—Thermal Processing for Extraordinary Material Properties, retrieved from https://www.ibu-tec.com/facilities/pulsation-reactors/, retrieved on Mar. 18, 2023, pp. 5.
Reig, L. et al., “Microstructure and Mechanical Behavior of Porous Ti—6Al—4V Processed by Spherical Powder Sintering”, Materials, Oct. 23, 2013, vol. 6, pp. 4868-4878.
Sastry, S.M.L. et al., “Rapid Solidification Processing of Titanium Alloys”, Journal of Metals (JOM), Sep. 1983, vol. 35, pp. 21-28.
Savage, S. J. et al., “Production of rapidly solidified metals and alloys”, Journal of Metals (JOM), Apr. 1984, vol. 36, pp. 20-33.
Seehra, M. S., et al., “Correlation between X-ray diffraction and Raman spectra of 16 commercial graphene-based materials and their resulting classification”, Carbon N Y., 2017, vol. 111, pp. 380-384.
Sheng, Y. et al., “Preparation of Micro-spherical Titanium Powder by RF Plasma”, Rare Metal Materials and Engineering, Jun. 2013, vol. 42, No. 6, pp. 1291-1294.
Sheng, Y. et al., “Preparation of Spherical Tungsten Powder by RF Induction Plasma”, Rare Metal Materials and Engineering, Nov. 2011, vol. 40, No. 11, pp. 2033-2037.
Related Publications (1)
Number Date Country
20230211407 A1 Jul 2023 US
Provisional Applications (1)
Number Date Country
62268186 Dec 2015 US
Continuations (2)
Number Date Country
Parent 17301880 Apr 2021 US
Child 18061250 US
Parent 16012370 Jun 2018 US
Child 17301880 US
Continuation in Parts (1)
Number Date Country
Parent 15381336 Dec 2016 US
Child 16012370 US