This invention relates to a method for hiding stains in medical dressings and other textile substrates. The method includes applying a metallic silver coating to a textile substrate via a plasma enhanced chemical vapor deposition (PECVP) process. The metallic silver coating effectively hides any stain that comes into direct contact with the treated substrate by transferring the liquid beneath the surface of the coating. The invention also relates to textile substrates containing metallic silver coatings.
There is a need for medical dressings for skin, wound and burn care that can hide stains. Stain release property upon washing is common for textile application, however, hiding stains of a textile material during application is uncommon. Even transparent liquids, such as water and sweat, change the optical property of the surface of a textile substrate and such liquids often result in visible staining. In this invention, polyester fabric (as one example) has been coated with a very thin layer of metallic silver using plasma enhanced chemical vapor deposition (PECVD) process, which has been demonstrated to hide the stain by transferring the liquid completely beneath the surface.
In one aspect, the invention relates to a stain hiding fabric comprised of a textile substrate having a wound contact surface and a non-wound contact surface, wherein the wound contact surface contains a metallized silver coating having a thickness in the range from 1% to 60%, based on the total thickness of the textile substrate.
In another aspect, the invention relates to a method for making a stain hiding fabric comprising the following steps: (a) providing a textile substrate having a wound contact and a non-wound contact surface, (b) exposing the wound contact surface of the textile substrate to a plasma enhanced chemical vapor deposition (“PECVD”) process, and (c) allowing the PECVD process to add a metallic silver coating to the wound contact surface of the textile substrate.
In a further aspect, the invention relates to a method for hiding stains in a textile substrate comprising the following steps: (a) providing a textile substrate having a wound contact and a non-wound contact surface, (b) exposing the wound contact surface of the textile substrate to a plasma enhanced chemical vapor deposition (“PECVD”) process, (c) allowing the PECVD process to add a metallic silver coating to the wound contact surface of the textile substrate to form a coated textile substrate, wherein the metallic silver coating has an exterior surface facing outward from the textile substrate and an interior surface facing inward to the textile substrate, (d) exposing the exterior surface of the metallic silver coating to an aqueous liquid, and (e) allowing the aqueous liquid to move from the exterior surface of the metallic silver coating to the interior surface of the metallic silver coating.
The present invention described herein is a method for hiding stains in medical dressings and other textile substrates. The method includes applying a thin layer of silver to the surface of a textile substrate via plasma enhanced chemical vapor deposition (“PECVD”). Further, the invention includes textile substrates containing a surface coating of silver capable of effectively hiding stains encountered during use.
Liquids can interact with two main types of solid surfaces, high-energy solids and low-energy solids. The relative energy of a solid rely on the bulk nature of the solid itself. Solids such as metals, glasses, and ceramics are known as ‘hard solids’ because the chemical bonds that hold them together are very strong. Thus, it takes a large input of energy to break these solids (alternatively large amount of energy is required to cut the bulk and make two separate surfaces so high surface energy), so they are termed “high energy.” Most molecular liquids achieve complete wetting with high-energy surfaces. In case of good quality conformal metallic coating, any underlying materials is almost isolated and thus will have very limited absorbency of any liquid. With good quality metal coating, it has been discovered that excellent wetting, with a limited absorbency surface, can be achieved and transfers any liquid underneath the surface very efficiently and effectively hides the stain.
In the specific case of textile materials, solids are weak molecular crystals where the molecules are held together essentially by physical forces (e.g., van der Waals and hydrogen bonds). Since these solids are held together by weak forces, a very low input of energy is required to break them, thus they are termed “low energy.” Depending on the type of liquid chosen, low-energy surfaces can permit either complete or partial wetting. Since these materials have high absorbency, they tend to absorb and hold a large quantity on liquid on the surface.
The process of plasma enhanced chemical vapor deposition is known for applying coatings to surfaces of substrates such as, for example, in semiconductors and high-performance optical glass applications. Typically, these substrates are non-porous in nature. In contrast, the invention described herein is using the PECVD process to apply a metallic silver coating to porous substrates, such as textile substrates.
The PECVD process is disclosed in US Patent Application Publication No. 2015/0291830 to Galbreath et al., which is entirely incorporated by reference herein. In one aspect of the present invention, only one side of the textile substrate is treated via PECVD. Thus, only one side of the treated textile substrate (the wound facing side or wound contact side) contains a metallic silver coating. As a result, one surface of the treated textile substrate (the non-wound facing side) is free from metallic silver (i.e. the non-wound facing side does not contain silver and has not been treated with PECVD).
The term “metallic’ is intended to include elemental metals and compounds thereof. In one aspect of the invention, metallic silver is coated onto the surface of a textile substrate. The source of silver for deposition onto the textile substrate includes aqueous solutions of silver salt (such as silver nitrate), silver oxide, silver nanoparticles, or other silver-containing compounds. In one aspect of the invention, silver ions (e.g. Ag+) are reduced to silver (e.g. Ag0) according to known reactions and applied as a coating to the surface of a substrate. On average, the silver coating is present on the fibers at the surface of the textile substrate in a range from about 200 to 300 angstroms, i.e. 20 nm to 30 nm.
Textile substrates include materials selected from synthetic fiber, natural fiber, man-made fiber using natural constituents, inorganic fiber, glass fiber, and a blend of any of the foregoing. By way of example only, synthetic fibers may include polyester, acrylic, polyamide, polyolefin, polyaramid, polyurethane, or blends thereof. More specifically, polyester may include polyethylene terephthalate, polytrimethylene terephthalate, polybutylene terephthalate, polylactic acid, or combinations thereof. Polyamide may include nylon 6, nylon 6,6, or combinations thereof. Polyolefin may include polypropylene, polyethylene, or combinations thereof. Polyaramid may include poly-p-phenyleneteraphthalamide (i.e., Kevlar®), poly-m-phenyleneteraphthalamide (i.e., Nomex®), or combinations thereof. Exemplary natural fibers include wool, cotton, linen, ramie, jute, flax, silk, hemp, or blends thereof. Exemplary man-made materials using natural constituents include regenerated cellulose (i.e., rayon), lyocell, or blends thereof.
The material comprising the textile substrate may be formed from staple fiber, filament fiber, slit film fiber, or combinations thereof. The fiber may be exposed to one or more texturing processes. The fiber may then be spun or otherwise combined into yarns, for example, by ring spinning, open-end spinning, air jet spinning, vortex spinning, or combinations thereof. Accordingly, the textile substrate will generally be comprised of interlaced fibers, interlaced yarns, loops, or combinations thereof.
The textile substrate may be comprised of fibers or yarns of any size, including microdenier fibers or yarns (fibers or yarns having less than one denier per filament). The fibers or yarns may have deniers that range from less than about 0.1 denier per filament to about 2000 denier per filament or, more preferably, from less than about 1 denier per filament to about 500 denier per filament.
Further, the textile substrate may be partially or wholly comprised of multi-component or bi-component fibers or yarns in various configurations such as, for example, islands-in-the-sea, core and sheath, side-by-side, or pie configurations. Depending on the configuration of the bi-component or multi-component fibers or yarns, the fibers or yarns may be splittable along their length by chemical or mechanical action.
Additionally, the fibers and/or yarns may include additives coextruded therein, may be precoated with any number of different materials, including those listed in greater detail below, and/or may be dyed or colored to provide other aesthetic features for the end user with any type of colorant, such as, for example, poly(oxyalkylenated) colorants, as well as pigments, dyes, tints, and the like. Other additives may also be present on and/or within the target fiber or yarn, including antistatic agents, brightening compounds, nucleating agents, antioxidants, UV stabilizers, fillers, permanent press finishes, softeners, lubricants, curing accelerators, and the like. The fibers and/or yarns comprising the textile substrate may be dyed or undyed. If the fibers are dyed, they may be solution dyed. The weight and density of textile substrate will vary depending on the desired aesthetics and performance requirements of its intended end-use.
The textile substrate may be selected from the group consisting of woven material, nonwoven material, knitted material, and combinations thereof.
Turning to the Figures,
Stain hiding fabric 400 includes wound facing surface 401 comprising a metallized silver coating having a thickness in the range from 1% to 60%, or from 5% to 40%, or from 10% to 35%, or from 20% to 40%, based on the total thickness of the fabric. The fiber content of stain hiding fabric 400 may also be as follows: 15% to 30% polyester fiber, 55% to 75% nylon fiber, and 10% to 20% spandex fiber.
With respect to the metallic silver coating, it is noted that the coating is a conformal coating as is known to those skilled in the art of metal coatings. Conformal coatings are typically very thin coatings applied to surfaces. The SEM image included as
The invention may be further understood by reference to the following examples which are not to be construed as limiting the scope of the present invention.
Two fabrics were evaluated for stain hiding properties. Example 1 was a 100% polyester pique knit fabric. One side of Example 1 was coated with metallic silver using the PECVD process. The surface that was coated with metallic silver was the surface intended to be the wound facing (or wound contact) surface of the fabric.
Example 2 was a jersey knit fabric comprised of 21% polyester fiber, 65% nylon fiber, and 14% spandex fiber. Based on its knit construction, one surface of Example 1 was primarily comprised of polyester fiber, and the opposite surface was comprised of primarily nylon fiber. The surface comprised primarily of polyester fiber was coated with metallic silver using the PECVD process. The surface that was coated with metallic silver was the surface intended to be the wound facing (or wound contact) surface of the fabric.
Additional details regarding samples tested are shown in Table 1 below:
All samples were evaluated for stain hiding properties. Control samples were also prepared and evaluated. Control 1 was the same as Example 1, except without the silver coating. Control 2 was the same as Example 2, except without the silver coating. Each sample was exposed to simulated wound fluid (“SWF”) that contained no dye, SWF containing red dye, and SWF containing blue dye.
Simulated wound fluid (“SWF”) was prepared by adding 16.60 g NaCl and 0.56 g CaCl2 to a 2 L volumetric flask. The flask was then filled to volume (2000 mL total) with deionized water. The flask was then capped and shaken until all of the salts were completely dissolved. The simulated wound fluid is comprised of 0.142M (142 mM) NaCl (aq) and 0.0025M (2.5 mM) CaCl2 (aq).
Several drops of each fluid preparation were added to the surface of each sample. Each sample was then visually evaluated for its ability to hide stains.
Based on qualitative assessment, the stain hiding property of Example 2 was greater than Example 1. In addition, the stain hiding property of Example 1 was better than all of the Control samples.
The knit constriction of Example 1 was different from Example 2. The fabric of Example 1 was equally dense with the yarns on both, face and back. The polyester side of Example 2 contained fluffy, low-density loops. Thus, when the metallic silver was coated on the low-density side, with even lower loading of silver (1562 ppm of silver in Example 2 vs. 2242 ppm of silver in Example 1), thickness coverage with silver coating for Example 2 (37.3%) was significantly higher than that of Example 1 (21.2%). Scanning electron microscopy (“SEM”)/energy dispersive spectroscopy (“EDS”) analysis confirmed the presence of silver on the wound contact/wound facing side of the fabric and no silver on the non-wound contact/non-wound facing side of the fabric.
Examples 1 and 2 were tested for antimicrobial efficacy against Gram positive bacteria (e.g. methicillin resistant Staphylococcus aureus, “MRSA”) and Gram negative bacteria (e.g. Pseudomonas aeruginosa). They were also tested for antifungal efficacy (e.g. Candida albicans). Examples 1 and 2 exhibited good antimicrobial efficacy against both Gram positive and Gram negative bacteria and good antifungal efficacy. Test result are provided in Table 2 and
P. aeruginosa
C. albicans
All references, including publications, patent applications, and patents, cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.
The use of the terms “a” and “an” and “the” and similar referents in the context of describing the subject matter of this application (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the subject matter of the application and does not pose a limitation on the scope of the subject matter unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the subject matter described herein.
Preferred embodiments of the subject matter of this application are described herein, including the best mode known to the inventors for carrying out the claimed subject matter. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the subject matter described herein to be practiced otherwise than as specifically described herein. Accordingly, this disclosure includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the present disclosure unless otherwise indicated herein or otherwise clearly contradicted by context.
This application claims priority to U.S. Provisional Patent Application No. 62/851,683, entitled “Stain Hiding Fabric With Metallic Coating,” which was filed on May 23, 2019, and is entirely incorporated by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2934066 | Stowasser | Apr 1960 | A |
| 3922888 | Patterson | Dec 1975 | A |
| 5271998 | Duckett | Dec 1993 | A |
| 5955175 | Culler | Sep 1999 | A |
| 6800573 | Van De Ven et al. | Oct 2004 | B2 |
| 6824819 | Vogt et al. | Nov 2004 | B2 |
| 8834686 | McClure et al. | Sep 2014 | B2 |
| 20030157147 | Hoge et al. | Aug 2003 | A1 |
| 20060127462 | Canada | Jun 2006 | A1 |
| 20070203442 | Bechert et al. | Aug 2007 | A1 |
| 20120276332 | Conolly et al. | Nov 2012 | A1 |
| 20130299428 | Bikel | Nov 2013 | A1 |
| 20150291830 | Galbreath et al. | Oct 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 108251779 | Jul 2018 | CN |
| 201201638 | Jun 2014 | EA |
| 201201638 | Jun 2014 | EA |
| H10-110257 | Apr 1998 | JP |
| H110257 | Apr 1998 | JP |
| 2005290585 | Oct 2005 | JP |
| 20090123445 | Dec 2009 | KR |
| WO02070245 | Sep 2002 | WO |
| WO03053484 | Jul 2003 | WO |
| WO2006096098 | Sep 2006 | WO |
| WO2006100480 | Sep 2006 | WO |
| WO2013021409 | Feb 2013 | WO |
| Entry |
|---|
| “JPH10110257_Machine Translation” is a machine translation of JP H10-110257A. (Year: 1998). |
| Yuranova, T., et al. “Antibacterial textiles prepared by RF-plasma and vacuum-UV mediated deposition of silver.” Journal of Photochemistry and Photobiology A: Chemistry, vol. 161, No. 1, Nov. 17, 2003, pp. 27-34, https://doi.org/10.1016/s1010-6030(03)00204-1. (Year: 2003). |
| “EA201201638A1_Machine Translation” is a machine translation of EA201201638A1. (Year: 2014). |
| International Search Report Application No. PCT/US2020/031571, dated Jul. 20, 2020. |
| Number | Date | Country | |
|---|---|---|---|
| 20200370171 A1 | Nov 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62851683 | May 2019 | US |