Patent Grant
9333682
This application claims the benefit of Korean Patent Application No. 10-2012-0006803, filed on Jan. 20, 2012, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.
1. Field
The present disclosure relates to stamps, methods of fabricating the stamps, and imprint methods using the same.
2. Description of the Related Art
Nanoimprint lithography (NIL) is a technology of pressing a stamp onto an imprint resist layer of a substrate to transfer a nano-pattern formed on a surface of the stamp to the imprint resist layer. In NIL, the nano-pattern is formed due to a direct contact between the stamp and the imprint resist layer. NIL is divided into thermal NIL and ultraviolet (UV)-curable NIL according to external energy used to form a pattern. A representative example of UV-curable NIL is step and flash imprint lithography (S-FIL). S-FIL is a technology of coating a UV-curable liquid imprint resin on a substrate, pressing a transparent stamp onto the imprint resin, and curing the imprint resin by using UV rays, thereby performing an imprint process.
Productivity, uniformity, and accuracy of S-FIL depends on various factors. For instance, how well a resin is coated, spread into a pattern, cured, aligned, uniformly pressed, etc. To improve these various factors, development of a resin and components of an NIL system is required.
Provided is a stamp, methods of fabricating the stamp, and imprint methods using the same.
Additional aspects will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented embodiments.
According to an example embodiment, a stamp includes a transparent body having an inner chamber containing an inlet/outlet tube configured to have a fluid injected and removed therefrom.
The transparent body may be formed of a material capable of being internally processed by using a laser to form the inner chamber and the inlet/outlet tube on the inside of the transparent body.
The transparent body may be formed of quartz.
The inner chamber may have a shape in which at least a portion of a surface of the inner chamber is one of flat, convex, and concave, if the fluid is not injected.
The inner chamber may have a circular or polygonal shape.
The stamp may be configured for use in a nanoimprint process.
According to another example embodiment, a method of fabricating a stamp includes internally processing a transparent body by using a laser to form an inner chamber in the transparent body; and forming in the transparent body an inlet/outlet tube configured to have a fluid injected and removed therefrom.
The internal processing may be performed by using a femtosecond laser.
According to another example embodiment, an imprint method includes injecting the fluid into the inner chamber of the stamp to increase an internal pressure of the inner chamber and thus to inflate the transparent body of the stamp; coating a resin on a substrate; and contacting the stamp, in which the transparent body is inflated, with the substrate coated with the resin.
The imprint method may further include reducing the pressure of the inner chamber of the transparent body after the stamp contacts the substrate coated with the resin.
These and/or other aspects will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings of which:
Reference will now be made in detail to embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. In this regard, the present embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the embodiments are merely described below, by referring to the figures, to explain aspects of the present description.
Referring to
The transparent body 20 may have a seamless single body structure. The transparent body 20 may be formed of a material capable of being internally processed by using a laser to form the inner chamber 30 and the inlet/outlet tube 35. For example, the transparent body 20 may be formed of quartz.
The stamp 10 may have an inner pressing system and is formed by internally processing a transparent blank, e.g., a quartz blank, by using a laser, e.g., a femtosecond laser, so as to form the inner chamber 30 and the inlet/outlet tube 35 through which a fluid flows into or out of the inner chamber 30. By forming the stamp 10 in this manner, the transparent body 20 has a seamless single body structure and the inner chamber 30 and the inlet/outlet tube 35 may be obtained such that when the fluid is injected into the inner chamber 30 an internal pressure of the inner chamber 30 may be rapidly adjusted resulting in conformal contact characteristics with a substrate may be improved.
When a femtosecond laser is used, since an inner part of a transparent blank may be easily processed to a level of about 1 μm, the inner chamber 30 may be formed relatively closely to the lower surface 21 of the stamp 10 (where the uneven part 50 is formed). Also, due to the laser processing, the inner chamber 30 may have a small size. Further, due to the laser processing, the inner chamber 30 may be formed to have various shapes, e.g., a three-dimensional (3D) shape.
When the internal pressure of the inner chamber 30 is increased, a thin portion of the transparent body 20 under the inner chamber 30 may be easily inflated and thus conformal contact characteristics with a substrate may be improved.
Since the inner chamber 30 is formed in the transparent body 20 and thus the stamp 10 may have flat outer surfaces except for the lower surface 21 where the uneven part 50 is formed, the stamp 10 may be easily handled by using a typical handling device and may have a simple structure merely required to externally connect a passage for flowing a fluid such as a gas or a liquid. Also, since the transparent body 20 is formed as a seamless single body, a complicated gas leakage prevention device may not be required.
The inner chamber 30 may have various shapes. The inner chamber 30 may have a shape in which at least a portion of a surface of the inner chamber 30 relatively close to the uneven part 50, i.e., a bottom surface of the inner chamber 30, is flat, convex, or concave as illustrated in
Also, the inner chamber 30 may have overly a circular shape as illustrated in
The uneven part 50 may be formed on the lower surface 21 of the transparent body 20. For example, a pedestal 25 may protrude on the lower surface 21 of the transparent body 20 and the uneven part 50 may be formed on the pedestal 25. The pedestal 25 may be single body with the transparent body 20. That is, when the transparent blank is formed, the transparent blank may be processed to have the pedestal 25. Alternatively, the pedestal 25 may be additionally formed as a transparent layer on the transparent blank before the laser processing is performed, or on the transparent body 20 including the inner chamber 30 and the inlet/outlet tube 35 after the laser processing is performed. In this case, the pedestal 25 may be formed of a transparent material the same as or different from the material of the transparent body 20.
The uneven part 50 may be formed of a material the same as or different from the material of the transparent body 20. The uneven part 50 may include one or more protrusions P1. A plurality of protrusions P1 may be spaced apart from each other. An empty space between two neighboring protrusions P1 forms a “recess”. The uneven part 50 may have a structure in which the protrusions P1 and the recesses are alternately disposed. The protrusions P1 may have a nano-size width. That is, the width of the protrusions P1 may be about several to several hundred nm, e.g., about several to several ten nm. The distance between the protrusions P1 may also be about several to several hundred nm, e.g., about several to several ten nm.
When the uneven part 50 has an uneven pattern including protrusions P1 that are spaced apart from one another by a nanoscale distance then the stamp 10 may be used in a nanoimprint process. That is, when the stamp 10 in which an uneven pattern having the nanoscale protrusions P1 is formed on the uneven part 50 is used, a nanoimprint pattern may be formed.
The above-described stamp 10 may be obtained by laser processing a seamless transparent blank to form the inner chamber 30 and the inlet/outlet tube 35 through which a fluid flows into or out of the inner chamber 30, and forming the uneven part 50 on the lower surface 21 of the transparent body 20.
According to the above-described stamp 10, in a step and flash imprint lithography (S-FIL) process, when the fluid such as a gas or a liquid is injected into the inner chamber 30 to increase the internal pressure of the inner chamber 30 and thus to inflate a thin portion of the transparent body 20 under the inner chamber 30, conformal contact characteristics with a substrate may be improved such that a resin may be rapidly coated.
According to the above-described stamp 10, the internal pressure of the inner chamber 30 may be rapidly adjusted because the inner chamber 30 has a relatively small size and the stamp 10 may be easily handled by using a typical blank handling device because a central portion of the stamp 10 is not recessed. Also, since a femtosecond laser allows processing to a level of about 1 μm, the inner chamber 30 may be formed relatively closely to the lower surface 21 of the stamp 10, that is, where an imprint pattern is formed, and may be formed to have a 3D shape.
Initially, as illustrated in
Then, when a fluid such as a gas or a liquid is injected into the inner chamber 30 of the stamp 10 through the inlet/outlet tube 35, as illustrated in
When a resin 80 is coated on a substrate 70, as illustrated in
When the stamp 10 is separated form the resin layer 90 after the resin layer 90 is pressed by the stamp 10, an inverse imprint pattern of the pattern of the uneven part 50 of the stamp 10 may be formed. Before the stamp 10 is separated, a desired (or, alternatively predetermined) curing process may be performed on the resin layer 90. That is, the stamp 10 may be separated after the resin layer 90 is cured. In this case, since the stamp 10 is overall transparent, the resin layer 90 may be cured, for example, by irradiating UV rays.
When the nanoscale protrusions P1 are formed on the uneven part 50, the imprint process may be a nanoimprint process and thus a nanoimprint pattern may be formed.
As described above, an imprint pattern, e.g., a nanoimprint pattern, may be formed by coating the resin 80 on the substrate 70, pressing the transparent stamp 10 onto the resin 80, and then curing the resin 80. Here, the stamp 10 may also be used in, for example, a thermal imprint method using heat to cure the resin layer 90. In this case, the stamp 10 may not be limited to a transparent material.
According to the above-described imprint method using the stamp 10, conformal contact between the substrate 70 and the stamp 10 may be achieved, a time taken to coat the resin 80 may be reduced, and thus productivity of an S-FIL process may be improved when compared to imprint methods using a conventional stamp.
Also, since the inner chamber 30 is formed in the stamp 10, the stamp 10 may be easily handled by using an existing transparent blank handling device.
Furthermore, since a femtosecond laser allows processing of quartz to a level of about 1 μm, the inner chamber 30 may be formed relatively closely to the uneven part 50 and may have a relatively small size, and thus a portion of the transparent body 20 under the inner chamber 30 may be easily deformed, and thus an internal pressure of the inner chamber 30 may be rapidly adjusted.
Although the inner chamber 30 is formed relatively closely to the lower surface 21 of the stamp 10 in the above descriptions, the inner chamber 30 of the stamp 10 may be formed in an upper portion of the stamp 10 or may be formed in a vertical direction.
For example, as illustrated in
Here, even when the inner chamber 30 is formed in the upper portion of the stamp 10, as illustrated in
As described above, according to one or more of the above example embodiments, when an inner chamber is formed in a lower portion of a stamp, in an S-FIL process, since a fluid such as a gas or a liquid is injected into the inner chamber of the stamp to increase an internal pressure of the inner chamber and thus to inflate a thin portion of a transparent body under the inner chamber, conformal contact characteristics with a substrate may be improved such that a resin may be rapidly coated. Also, when the inner chamber is formed in an upper portion of the stamp, it is possible to press further uniformly. Furthermore, when the inner chamber is formed in a vertical direction, accurate alignment may be achieved.
It should be understood that the example embodiments described therein should be considered in a descriptive sense only and not for purposes of limitation. Descriptions of features or aspects within each embodiment should typically be considered as available for other similar features or aspects in other embodiments.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2012-0006803 | Jan 2012 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 7803308 | GanapathiSubramanian et al. | Sep 2010 | B2 |
| 20010048900 | Bardell et al. | Dec 2001 | A1 |
| 20040009673 | Sreenivasan et al. | Jan 2004 | A1 |
| 20100072652 | GanapathiSubramanian et al. | Mar 2010 | A1 |
| 20100244326 | Tokue et al. | Sep 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 100887381 | Feb 2009 | KR |
| 1020090017469 | Feb 2009 | KR |
| 20100107390 | Oct 2010 | KR |
| WO-2009099630 | Aug 2009 | WO |
| Entry |
|---|
| Qin, S.-J., and W.J. Li, Micromachining of complex channel systems in 3D quartz substrates using Q-switched Nd:YAG laser, Applied Physics A, vol. 74, issue 6 (Jun. 2002), pp. 773-777. |
| Number | Date | Country | |
|---|---|---|---|
| 20130187309 A1 | Jul 2013 | US |