Stent with collagen

Information

  • Patent Grant
  • 6391052
  • Patent Number
    6,391,052
  • Date Filed
    Wednesday, October 29, 1997
    27 years ago
  • Date Issued
    Tuesday, May 21, 2002
    22 years ago
Abstract
A method of depositing collagen coatings on a metal surface, namely metal stents, by electrodeposition.
Description




BACKGROUND OF THE INVENTION




This invention relates to vascular prostheses of improved biocompatability and more specifically to stents in combination with a collagen material. Such a combination provides an endovascular stent which protects the vascular wall and forms a non-thrombogenic cushion for the stent in the vascular lumen.




It also relates to stents in combination with a collagen liner material. Such a combination provides an endoluminal stent which engages the luminal wall and in the case of vascular applications, forms a non-thrombogenic surface as well as providing for the growth of endothelial cells, as well as a reservoir or point of attachment for therapeutic agents in any application.




It also relates to combinations of both of the foregoing arrangements.




Broadly, it relates to stents associated with an outer covering of collagen material and/or a luminal liner of same. It also relates to a method of applying collagen to the interior of a vessel or the like as a liner by using a stent.




Stents are generally tubular in configuration, are open ended, and are radially expandable between a generally unexpanded insertion diameter and an expanded implantation diameter which is greater than the unexpanded insertion diameter. Such intravascular implants are used for maintaining vascular patency in humans and animals.




Stents are typically placed or implanted by a mechanical transluminal procedure. One common procedure for implanting a stent is to first open the region of the vessels with a balloon catheter and then place the stent in a position that bridges the treated portion of the vessel by means of a placement catheter.




Prior art patents refer to the construction and design of stents as well as apparatus for positioning stents within a vessel. In general, for example, such patents disclose a technique for positioning an elongated cylindrical stent at a region of an aneurysm, stenosis or the like. The stent expands as necessary to an implanted configuration after insertion with the aid of a catheter.




Specifically, U.S. Pat. No. 4,733,665 to Palmaz which issued Mar. 29, 1988, discloses a number of stent configurations for implantation with the aid of a catheter. The catheter includes means for mounting and retaining the stent, preferably on an inflatable portion of the catheter. The stent is implanted by positioning it within the blood vessel and monitoring its position on a viewing monitor. Once the stent is properly positioned, the catheter is expanded and the stent separated from the catheter body. The catheter can then be withdrawn from the subject, leaving the stent in place within the blood vessel. U.S. Pat. No. 4,950,227 to Savin et al., which issued on Aug. 21, 1990 is similar.




Another similar U.S. Pat. No. 5,019,090 discloses a generally cylindrical stent and a technique for implanting it using a deflated balloon catheter to position the stent within a vessel. Once the stent is properly positioned the balloon is inflated to press the stent against the inner wall linings of the vessel. The balloon is then deflated and withdrawn from the vessel, leaving the stent in place.




A patent to Dotter, U.S. Pat. No. 4,503,569 which issued Mar. 12, 1985 discloses a spring stent which expands to an implanted configuration with a change in temperature. The spring stent is implanted in a coiled orientation and heated to cause the spring to expand due to the characteristics of the shape memory alloy from which the stent is made. Similarly, U.S. Pat. No. 4,512,338 to Balko et al., which issued Apr. 23, 1985, discloses a shape memory alloy stent and method for its delivery and use other kinds of self-expanding stents are known in the art.




The delivery and expansion of the stent of the invention is the same as that already known in the art and practiced with the stent of

FIGS. 1 and 6

. U.S. Pat. No. 5,195,984 to Schatz, issued Mar. 23, 1993, describes a typical balloon expansion procedure for an expandable stent. This patent is incorporated in its entirety herein by reference. That patent describes a catheter having an expandable inflatable portion associated therewith. In a conventional manner, the catheter and stent are delivered to a desired location within a body passageway at which it is desired to expand the stent for implantation. Fluoroscopy, and or other conventional techniques may be utilized to insure that the catheter and graft are delivered to the desired location. The stent is then controllably expanded and deformed by controllably expanding the expandable inflatable portion of catheter, typically a balloon. As a result the stent is deformed radially outwardly into contact with the walls of the body passageway. In this regard, the expandable inflatable portion of the catheter may be a conventional angioplasty balloon as is already known in the art. After the desired expansion and deformation of the stent has been accomplished, the angioplasty balloon may be deflated and the catheter removed in a conventional manner from the passageway.




Also, this invention is useful in self-expanding stents such as those disclosed in U.S. Pat. Nos. 4,732,152 and 4,848,343, both of which are incorporated herein by reference.




All of the above-identified patents are incorporated herein by reference.




SUMMARY OF THE INVENTION




In one preferred form a metal or other stent is delivered for vascular implantation with a covering sleeve of collagen material. If the stent is of the variable diameter type, the sleeve may be stretched into place or otherwise positioned between the stent and the vascular wall when the stent is seated or deployed. A drug or other agent such as heparin or the like may be included in the collagen for release after stent deployment.




In another preferred form a metal or other stent is delivered for vascular implantation with a luminal liner of collagen material. A drug or other agent such as heparin or the like may be included in the collagen as a surface treatment or for release after stent deployment.




In yet another preferred form, a stent is provided with both an inner collagen liner and outer collagen coating.











BRIEF DESCRIPTION OF THE FIGURES





FIG. 1

shows a stent and covering sleeve combination being formed according to the invention.





FIG. 2

is a fragmentary showing of collagen with a fabric support.





FIG. 3

shows an example of another self-expanding stent configuration useful in the invention.





FIG. 4

shows another stent configuration useful in the invention.





FIGS. 5 and 6

show a flexible stent configuration which may incorporate a covering sleeve according to the invention.





FIG. 7

is similar to

FIG. 1

, showing a combination being formed including an internal liner and an external sleeve for a stent, according to the invention.





FIG. 8

is a showing of an alternate mode of manufacture of the invention by molding the collagen to the stent.





FIG. 9

shows a stent and an internal liner sleeve combination being formed according to the invention.





FIGS. 10

shows a bilayer collagen material in schematic and fragmentary form.





FIGS. 11

,


12


, and


13


are schematic longitudinal cross-sectional views of a stent carrying inner and outer layers of collagen material.





FIG. 14

is a showing of an alternate stent/liner arrangement.





FIG. 15

shows an optional technique for forming the stent/liner arrangement by molding.





FIGS. 16

,


17


, and


18


, schematically show the stretch of a collagen stent being oriented on a bias with respect to a stent.





FIGS. 19 and 20

show a coated stent,

FIG. 20

being a cross-sectional view of FIG.


19


.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT




Referring now to

FIG. 1

, a tubular metal stent generally indicated at


10


is shown being combined with a covering sleeve of collagen material generally indicated at


12


to provide the combination stent/sleeve generally indicated at


14


for the purpose of vascular implantation.




Stent


10


is of the type, typically of a metal such as for example stainless steel, nitinol, superelastic alloys and other metals or a suitable polymeric plastic and may be of a fixed diameter or of a variable diameter, the latter being more preferred and well known in the art. The variable diameter type are usually either balloon expandable or self-expanding, both of which are also known in the art. Examples of the former type are shown in U.S. Pat. No. 4,733,665, U.S. Pat. No. 4,739,762 and U.S. Pat. No. 4,776,337, all of which are incorporated herein by reference. The latter type is preferred for the purposes of this invention at present, i.e., self-expanding, particularly those made of Nitinol an example of which is discussed in the U.S. Pat. Nos. 4,503,569 and 4,512,338, also incorporated herein by reference. Also, for example, useful stents are shown in co-pending application Ser. No. 08/246,320 filed May 19, 1994 entitled “Improved Tissue Supporting Devices”. The content of this application is incorporated herein by reference.




In any event, generally a stent provides a supporting framework structure which may take many forms. Typically stents are open or perforate and may be comprised of a network of struts or wire-like structure. Stent


10


is comprised of struts.




Collagen sleeve


12


shown in

FIG. 1

may be comprised of collagen per se or it


12




a


may be carried on a support


12




b


as shown in

FIG. 2

, support


12




b


being of DACRON® fabric or the like as is known and disclosed for example in U.S. Pat. Nos. 5,256,418, 5,201,764 and 5,197,977, the entire content of which are all incorporated herein by reference, particularly those portions which relate to the formation of collagen tubes. The Support


12




b


may be a fabric, woven or braided, and may also be of polyester, polyethylene, polyurethane or PTFE. The term “collagen material” is used herein to refer to both supported and unsupported collagen for the sleeve element of this invention.




The preferred collagen at present appears, for the purposes of this invention, to be that composed of bovine or porcine Type I or Type IV collagen and combinations thereof in bilayer sheet-like form. The collagen may also be made of Type III or combinations of any of the various types. U.S. Pat. Nos. 4,837,379; 4,902,508; 4,950,483; 4,956,178; 5,106,949; 5,110,604, 5,256,418; 5,275,826; 5,281,422 and 5,024,841 relate to collagen compositions and production useful in this invention and are incorporated herein by reference. Collagen can be extracted from various structural tissues as is known in the art and reformed into sheets or tubes and dried onto a stent. Generally, the thickness of these sheets or tubes will range from about 5 to 200 microns. One preferred collagen at present is that disclosed in U.S. Pat. No. 4,902,508 coated as described in U.S. Pat. No. 5,275,826 to provide bilayer SIS as described further hereinbelow. Another preferred collagen is that described as a “collagen construct” in U.S. Pat. No. 5,256,418, particularly in which the permeable substrate is also collagen.




Cells of the blood vessel wall synthesize and secrete several kinds of macromolecules forming extracellular matrix. The components of this matrix comprise several large proteins that may be synthetically constructed to form films, tubes or multilayer sheets or other constructs. Among these biological components are collagens of several types, elastin, glycosaminoglycans (GAGS), fibronectin and laminin. Collagens are three chain glycoproteins with molecular weights of about 300,000. Elastin is an insoluble nonpolar amine acid rich crosslinked protein. The GAGs are linear chain polysaccharides with various negative charges with various molecular weights ranging from thousands to millions. Included in the GAGs are heparin and heparin sulfate, dermatin sulfate and chondroitin sulfate. Fibronectin is a 440,000 MW 2-chain adhesive glycoprotein that acts as a substrate for many cell types and in cell-cell interactions. Laminin is a 2 chain glycoprotein of MW about 850,000 and acts as a basement membrane structure for cellular-molecular interactions. Each of these macromolecules may be combined in a multitude of combinations to form composites. These are all natural materials that serve specific functions and are exposed to blood under normal repair conditions. It is therefore expected that, if a covering sleeve for a stent were made of these macromolecules and used in the course of intervention, repair of a blood vessel would proceed more naturally than if a similar device were constructed of synthetic polymers such as polyethylene, polyteraphthalate or polyurethanes. Such materials are also referred to herein generally as “collagen”. The term “collagen” herein thus refers to not only the specific class of macromolecules known as collagen but those natural materials that normally or naturally form membranes with collagen such as laminin, keratin, glycosaminoglycans, proteoglycans, pure carbohydrates, fibrin, fibronectin, hyaluronic acid or the like, and other natural materials that come into contact with collagen that can be made into film, including albumin, globulins, and other blood borne proteins. Tubular films made from any combination of the above materials will provide substantially the same purpose as that of pure collagen.




The interaction of blood with the differing membrane components described above determines subsequent reactions in the repair of blood vaseulature. The initial thrombus formation adhesion and activation of platelets and the initial events related to intimal hyperplasia such as damage to the internal elastic lamina are among those events. These events are natural components of the repair process. Normally these events do not hamper the flow conditions of blood except in the cases of severe trauma. Microthrombi constantly form and disperse on blood vessel surfaces so it would be advantageous to form stent or graft coverings of materials that are accustomed to having thrombus form so that subsequent lysis reactions of those thrombi can proceed in a natural and unobtrusive manner. A sleeve or liner made of these macromolecular components forming a protective layer will prove advantageous when used with stents. Metal or polymeric stents which will provide mechanical stability to the arterial wall to hold up dissected tissue may also be used to hold a sleeve comprised of collagen.




Nevertheless, because anything not formed in the body as a natural component may elicit extreme and unexpected responses as blood vessel closure due to thrombus formation or spasm and because damage to blood vessels by the act of insertion itself of a device may be extreme and unduly injurious to the blood vessel surface, it is prudent to protect against such events. The materials described above are capable of being manipulated to become hydrophilic or hydrophobic with thicknesses ranging from about 5 to several hundred microns. They can be made water soluble, insoluble and with various porosities. They can also be constructed to have regions of various hydrophilicity and porosity. Porosity control is well known.




As such, stent sleeves or liners constructed of these materials can be used for reservoirs for pharmaceutical agents and the like. Hydrophilic drugs such as heparin or hirudin to protect against coagulation or hydrophobic drugs such as prostaglandins or aspirin and vitamin E may be used to protect against platelet activation. Vitamin E and other anti oxidants such as sodium ascorbate, phendies, carbazoles, and tocotrienols may be used to protect against oxidation. Most preferably, the collagen material will include a quantity of drug material such as heparin which may be incorporated into the collagen in known manner for release after placement of the stent. Generally, the drug materials may include the known antitirombic agents, antibacterial and/or antimicrobial agents, antifungal agents and the like.




During the formation process of the sleeve or sheet, various components may be added to the solution prior to drying or may be added separately after formation of the device. Heparin may be directly added to the forming solution as may be aspirin. Benzalkonium heparin, a modified form of heparin which makes it more hydrophobic may be used to coat the formed device or film from a solution of alcohol. Prostaglandins PGI2 or PGE2 may be added from a solution of propanol or propanol/methylene chloride onto a collagen sleeve formed from an aqueous base. Vitamin E may be added from even less polar solutions as chloroform. RGD peptide, thrombolmiodulin, TPA (Tissue Plasminogen Activator) and Urokinase are examples of bioactive proteins which may be added. Gene therapy agents such as antiplatelet and antibody fragments, for example GB2B3A may be included. Other agents could be similarly added. The term “agents” is used herein to include all such additives.




Vitamin E is a known antioxidant. It is used in polymers and as a drug. It could also be used in biodegradable stents for multiple purposes. In those polymeric type stents that require some form of energy as heat or light to be delivered it could serve to protect the polymers therein against unwanted oxidation caused by the energy source. Also, because tissue damage is caused by oxidation originating from cellular components as macrophages and neutrophils, Vitamin E could serve to protect the tissue as it leached from implanted devices. It could also serve to protect the polymer during extrusion or heat forming as pressing films. It could also serve to plasticize the material in place of using other non FDA approved materials. It is therefore contemplated that Vitamin E may also be used in combination with the stent or collagen material or the like in this invention for several purposes.




A primary result of the use of a collagen sleeve made of natural components is that cellular regrowth of endothelium will take place onto a natural substrate that is essentially undamaged and uniform and protects against tissue flaps and exposure of necrotic or arthrosclerotic tissue to blood. In this regard, the sleeve provides biological protection.




Metal stents are known to sometimes physically damage tissue upon expansion. A sleeve made of a biological material is naturally soft by comparison to the metals or polymers used to construct stents. A sleeve comprised of collagen may be made sufficiently thick and durable so that it will prevent or at a minimum reduce any damage caused by the struts or other elements of any of the metal stents to the remaining healthy endothelium and the internal elastic lamina. The porosity of the sleeve may permit diffusion of essential fluid components from the blood to the surviving tissue below. In this regard, the benefit of the biological tissue protection by the sleeve and the physical protection provided are additive.




Both the biological and physical advantages as described herein can not be provided by synthetic sleeves as Dacron or PTFE.




In the case of a fixed diameter stent, the sleeve may be fitted to the stent rather closely for ease of vascular placement. However, in the case of variable diameter stents, the sleeve being somewhat elastic will fit the constricted stent and stretch with it upon deployment or it may be relatively loose fitting to accommodate the expanded stent upon deployment without any additional stress. Alternatively and most preferably, the stent may be expanded temporarily and the collagen placed thereon. The collagen may then be hydrated and the stent contracted to its unexpanded configuration. Then the collagen is dehydrated and it fits tightly to the stent.




A sleeve or a liner may be made to be more elastic by altering the crosslink density of the collagen. This can be accomplished in a variety of ways.




Collagen sleeves may be prepared to have a very low crosslink density. The crosslink density may be increased in a variety of ways, dehydration, radiation exposure or heating are some examples of ways. Chemical agents which react with the collagen, such as short chain dialdehydes or formaldehyde may be employed to crosslink the collagen. The avoidance of the aforementioned processes can assure a non-crosslinked structure and result in somewhat elastic material. Crosslinking with the appropriate reagents can also enhance the elasticity of the collagen sleeve. Such reagents are the long chain difunctional molecules C


12


and higher such as polyether or aliphatic dialdehydes, activated diesters such as N-hydroxy succinimide esters and diacid chlorides. These active esters will react with amines present on the collagen chains thus bridging them by a flexible link which allows expansion without failure and tearing. Also, with amine functionality protected as an amide, the interchain, irreversible amide formation, which results from dehydration, is prevented.




A variety of stent types may be used in the invention. Some examples are shown in

FIGS. 3-6

. In

FIG. 3

there is shown a braided self-expanding stent generally designated


40


. As is clear from the Figure, stent


40


has a cylindrical configuration. The stent may be manufactured in a braiding machine, wherein the stainless steel monofilaments consist of a plurality of wires, each having a thickness of, for example, 0.08 mm.

FIG. 4

shows yet another stent configuration


50


which may be used in this invention. Other examples of this type of stent are disclosed in U.S. Pat. No. 4,655,771; U.S. Pat. No. 4,732,152; U.S. Pat. No. 4,954,126 and U.S. Pat. No. 5,061,275; all of which are incorporated herein by reference.




Referring now to

FIGS. 5 and 6

an articulated stent


60


is shown with three stent segments


62


and two interconnecting hinge elements


64


. Stent segments


62


are each made of individual wire elements welded together. Hinges


64


may be made of biocompatible spring material and may be of a smaller diameter than those used in forming stent segments


62


. Hinges


64


are welded at each end to stent segments


62


using either laser or resistance welding techniques. Hinges


64


are preferably both attached to the same side of stent segments


62


. Stent


60


, shown in

FIG. 5

, may be installed in an artery


66


with a sleeve


12


as shown in FIG.


6


and may be bent as shown.




Other stent configurations and materials will be apparent to those familiar with this art.




Collagen sleeves may be made to cover both sides of the stent, inside and out so that its surfaces are entirely encompassed by collagen.




An example of one such embodiment is shown in

FIG. 7

which comprises a tubular stent generally indicated at


10


combined with an inner sleeve


13


of collagen material and an outer sleeve


12


of collagen material which provide in combination a stent/sleeve generally indicated at


15


for the purpose of vascular implantation. In some cases, it is preferred that the collagen sleeve


13


be joined to the interior surface of the stent by a suitable means such as collagen gel which acts as an adhesive, particularly when the stent is of the variable diameter type. Such gels are known in the art.




EXAMPLE




Method for the preparation of the sleeve stent of FIG.


7


.




1. SIS sheet is stretched about 50% while allowed to air dry.




2. Dry SIS sheet is wrapped onto an inflated, standard angioplasty balloon, moistening along the seam to ensure proper adhesion.




3. A tubular stent is then placed over the SIS.




4. A second sheet of SIS is wrapped over the exterior of the stent. This sheet may be wetted to facilitate handling. The SIS which resides inside the stent may be wetted with a small amount of distilled water immediately preceding this wrapping procedure also.




5. Open cell foam sheeting is then wrapped onto the outer second layer of collagen, followed by a wrap of dialysis tubing. This radial pressure insures continuous contact and adhesion between the collagen layers.




6. The entire construction is then immersed in water momentarily to wet the collagen.




7. The entire combination is then heated to about 40°-70° C. for about 0.5 -3 hours, then cooled to room temperature. The purpose of this heat treatment is to bond the collagen layers together. It may optionally be accomplished by use of a chemical cross-linking agent.




8. The resultant device is liberated from the balloon after the dialysis tubing and foam are removed. Any excess collagen material is then trimmed from the ends of the covered stent.




A cast or molded version is shown being manufactured in

FIG. 8

which includes a cylindrical mold


80


into which a cylindrical stent


82


is placed on end. Preferably, mold


80


will be porous, such as a porous ceramic, so as to allow water to be drawn through the mold to facilitate set-up of the poured collagen. A collagen gel solution


83


is then poured into mold


80


around stent


82


and inside of stent


82


and allowed to set-up. Upon set-up, the stent embedded in collagen is removed from the mold and a longitudinal hole may be formed through the collagen inside the stent to provide a longitudinal opening therethrough. Otherwise, a mandrel or mold insert may be used for this purpose as well.




In other embodiments, the collagen material may be coated onto the stent surfaces as desired by spraying or dip coating or an electrophoretic technique or the like. The electrophoretic technique is a preferred coating technique and may be accomplished, for example, in a solution of acetic acid, acetone, water and collagen with a metal stent as the cathode, at a potential of about three volts. This process bears some resemblance to modern electroplating, where positively charged metal ions are reduced to their corresponding metal at the negatively charged cathode. In the case of collagen, the biomolecule is dissolved or suspended in an acidic solution. The acid imparts a positive charge to the protein, collagen, and allows it to travel in an electrical field. By attaching a metal object to the negative electrode of a power source, and then immersing both the positive and negative electrodes in the acidic collagen solution, a layer of collagen will form on the negatively charged surface. The result is a coated stent of the type shown in

FIGS. 19 and 20

which will preferably include openings in the coating coincident with the openings in the stent.




EXAMPLE




Collagen Coated Stent (Type IV) via Electrodeposition




A. A solution of Sigma type IV human collagen (50 mg) was placed in a polypropylene tube with 3 ml water, 1 ml of acetic acid and 2 ml of acetone. This mixture was homogenized to a viscous solution via high shear mixing for ca. 3 minutes. The solution was diluted with water, then filtered through a cotton plug. The solution was allowed to stand for 1 hour to eliminate air bubbles.




B. A cylindrical container was fashioned out of polypropylene and charged with 1 ml of the above prepared solution A. To this container was added a nitinol substrate attached to the negative lead of a variable voltage power supply which was set at 3 volts. The positive electrode was furnished with a 0.010 inch diameter wire which was placed ca. 4 mm from the substrate. The power supply was turned on and gas evolution was immediately evident on the surfaces of each electrode. This was maintained for several minutes, then the electrodes were removed from the collagen solution. An even gelatinous mass was evident on the substrate, which contained several bubbles. Upon standing for 1 to 2 minutes, the bubbles were gone, and the electrodes were once again placed in the bath. After three additional minutes of treatment, the substrate was withdrawn from the bath and allowed to dry. The coating appeared to be continuous via visual inspection.




Another coating technique is shown in U.S. Pat. No. 5,275,826 which is incorporated herein by reference.




Referring now to

FIG. 9

, a tubular metal stent generally indicated at


10


carries within it a cylindrical liner or inner sleeve of collagen material generally indicated at


12


to provide a combination stent/liner generally indicated at


14


for the purpose of vascular implantation.




Stent


10


, as already described hereinabove, is of any type, typically a metal such as for example stainless steel, nitinol, superelastic alloys and other metals or a suitable polymer or any other suitable material and may be of a fixed diameter or of a variable diameter, the latter being more preferred and well known in the art. The content of this application is incorporated herein by reference.




Collagen liner


12


as described hereinbefore, may be of collagen per se or it may be applied directly to the stent or it may be carried as


12




c


on a support


12




d


as shown in

FIG. 10

for application to a stent.




When the collagen liner is comprised of two different materials which are joined together as shown in

FIG. 10

, it may be referred to as a bilayer structure. When placed in a stent, layer


12




c


is placed luminally with layer


12




d


contacting the inner surface of the stent. Layer


12




d


, which may be in contact with the vessel wall through openings in the stent in such an arrangement, is preferably strong and enables the inner luminal layer


12




c


itself to have the structural integrity necessary to ensure ease of loading, delivery and deployment. Layer


12




c


may for example be comprised of a collagenous material in the range of 5 to 200 microns thick. Such a biologically derived material may be harvested from a donor source, cleaned of unwanted tissues and formed into the tube by wrapping it around a mandrel and bonding the material to itself. Synthetic materials may be used to comprise the support of layer


12




d


of the liner, however, vascular graft materials such as PTFE, woven dacron, polyurethane and the like may also be used. Resorbable polymers (PLLA, PGA, PDLLA, PHB, polyanhydrides) are another choice for the support layer


12




d


of the liner


12


. These materials may be formed into a tube by extrusion, solvent casting, injection molding, etc. or spinning into fibers and weaving into a tubular structure. A tube of one of the aforementioned polymers may also be constructed by a non-woven fiber technique.




The innermost or luminal side, i.e., layer


12




c


of the liner serves a different function than the support layer


12




d


. The luminal surface or layer


12




c


must be a substrate for the growth of endothelial cells, as well as a reservoir for therapeutic agents. Preferred material is fibular Type I collagen and/or porcine Type IV collagen in the range of 5-200 microns thick, although fibrin may also be used for this purpose. Highly hydrated materials, such as cross linked hydrogels meet the drug holding requirement for the luminal portion of the liner, examples of which are polyethers, polyalcohols, polypyrollidones, polypeptides, polyacids and the like. The layer


12


may also be a mixture of the above materials with a drug binding, ionic or covalent, molecule. One such molecule would be protamine, which effectively ionically binds heparin. These polymers can also be treated with growth factors, such as RGD peptides to promote endothelialization. The preferred method of drug incorporation would involve the preparation of a solution of the therapeutic agent and allowing the dehydrated luminal side of the sleeve to swell with the solution. Upon evaporation of he carrier solvent, the drug would be made to reside in the matrix which comprises the inner layer of the liner, i.e., layer


12




c


. The device may act as a sponge to soak-up a drug in solution and to elute it from the stent upon implantation.




The term “collagen” or “collagen material” should also be understood to include the material referred to as Small Intestine Submucosa (SIS) which has particular use in this invention, alone and in combination with other collagen material such as Type I. SIS is comprised of a bilayer structure in which one layer is predominantly (stratum compactum) Type IV and the second layer is a mixture of Type I (muscularis mucosa) and Type III material. It is described in detail in U.S. Pat. Nos. 4,902,508; 4,956,178 and 5,281,422, all of which are incorporated herein by reference. The luminal side of the SIS as used in preferred embodiments of this invention are predominantly a Type IV collagen material.




As with other collagen material, SIS may be used herein with or without a support layer such as a layer


12




d


as shown in FIG.


10


. It may also be used as the support layer


12




c


in combination with a layer


12




d


of Type I collagen as shown in FIG.


10


. SIS functions well without a support layer because it is itself a multi-layer structure.




In yet another embodiment, an SIS layer may be combined with a Type I layer to provide a one-way flow structure with reservoir arrangement as shown schematically in FIG.


11


. In this arrangement, a cylindrical wire mesh stent


10


carries a tubular bilayer liner generally indicated at


12


comprised of two layers


12




c


and


12




d


. Layer


12




c


contacts the inner surface of stent


10


and is a Type I collagen material and may carry a drug or the like, acting as a reservoir. Luminal layer


12




d


is SIS material and inherently functions to allow flow of drug from layer


12




c


into the luminal interior of the stent through the luminal layer


12




d


of stent


10


but does not permit appreciable fluid flow into layer


12




c


from the interior of the stent.




Variations of this

FIG. 11

arrangement are shown in

FIGS. 12 and 13

. In

FIG. 12

, stent


10


carries an inner or luminal liner made up of layers


12




c


and


12




d


as described for FIG.


11


and an outer layer of the same combination to allow predominantly one-way flow of drug to the luminal interior of the stent and to the surface against which the stent rests when implanted.




In

FIG. 13

, stent


10


carries an exterior layer


12


of unsupported SIS material and an inner liner comprised of layers


12




c


and


12




d


as in

FIGS. 11 and 12

. Layer


12




c


is Type I material acting as a drug reservoir as previously shown in Figures


11


and


12


. Layer


12




d


is of SIS acting as the one-way flow-through for drugs and the like from layer


12




c


, as before.




As pointed out hereinabove, cells of the blood vessel wall synthesize and secrete several kinds of macromolecules forming extracellular matrix. Each of these macromolecules may be combined in a multitude of combinations to form composites. Such materials as already pointed out, are referred to herein generally as “collagen”.




A primary result of the use of a collagen liner made of natural components is that cellular regrowth of endothelium will take place onto a natural surface that is essentially undamaged and uniform. In this regard, the liner provides biological protection.




The liner may be tightly fitted to the stent in much the same way as described hereinabove with reference to the outer sleeve arrangement.




The liner may be attached to the stent in a wide variety of ways. The basic goal of attachment in the preferred form is to provide a stent device in which the supporting stent framework is substantially, if not completely, isolated from the blood flow by the liner. This can be achieved by placing liner


12


in the inside dimension of the stent


10


and cuffing the ends of the liner over the ends of the stent as shown at


16


in FIG.


14


. This is an especially preferred arrangement. Cuffs


16


may either be under or over the outer sleeve. Cuffs


16


may be sutured to the stent, sutured from one cuff to the other, or otherwise bonded to the stent or to the liner itself. The collagen material may be welded, by the application of localized heat and pressure, or the application of a concentrated solution of collagen material which acts like glue.




The liner may also be attached to the stent by the use of pledgets (not shown). The pledget (or small swatch of material) can be placed on the outside of the stent. The liner, which resides on the luminal or inner surface of the stent, may be bonded to the pledget in a variety of ways. Among these are suturing, gluing and heat welding. In the case of a combination of liner with outer sleeve, these means of attachment may be used as well.




The liner may be placed in the stent via several methods. The stent may be made porous or perforated, thus allowing the liner material to act as a forming mandrel for a collagen sleeve. The collagen may also be precipitated onto the stent. This method would require the stent to be heated in a solution of collagen. The collagen forms a matrix on the surface of the stent, then when properly annealed, the collagen assumes a fibular, well organized structure conducive for the attachment and growth of cells.




A technique is indicated in

FIG. 15

in which the collagen


12


is cast inside the stent


10


in a manner similar to that described in connection with FIG.


8


. Upon set-up, the stent with a liner of cast collagen is removed from the mold and a hole may be formed through the collagen to provide a longitudinal opening therethrough. Otherwise, a mandrel or mold insert (not shown) may be used for this purpose also. Holes may also be formed through the stent walls in the collagen if the stent is perforated or the like.




The liner may be attached to the stent by any of several design features which may be incorporated into the stent. By providing the stent with hooks, or other similar topography (not shown), the sleeve may be readily attached to the stent. The sleeve material may be impaled on such barbs, thus securing the sleeve. With hooks of the appropriate size, the collagen material may not be perforated, but rather embedded in the holding topography.




As can be seen from the foregoing, the invention provides in one embodiment a stent in which collagen liner material is placed within and/or on the outside of the stent thereby reducing thrombus formation and therapeutically treating the vessel when a suitable agent is included in the collagen.




It is to be understood that the collagen material referred to herein as layers may be in the form of sheets associated with the stent or deposited thereon, i.e., as a coating.




Thus, the collagen material may be coated onto the stent surfaces as desired by spraying or dip coating or electrodeposition or the like or attached in other ways as described above. Such a coating might be about 1-50 microns thick. A coated stent is shown in

FIG. 19

, which will preferably be perforate as shown.




A collagen coated stent may also have a collagen sleeve over the collagen coating or under the collagen coating. For example, one may place a stent into a collagen sleeve, as shown in

FIG. 1

, with an interference fit. The inside of the stent may then be coated with collagen so that the stent and interior of the sleeve are covered and bonded together. Preferably, in such an arrangement, the sleeve will be SIS and the coating Type I or Type IV. It is also possible in the case of an open-work stent such as shown in

FIG. 1

or


3


, to coat the stent struts with collagen, place a collagen sleeve either over or inside the stent, or both, and then heat bond the sleeve and/or liner to the coating. This would preferably be done with Type IV collagen, especially SIS or with fibrin.




In some applications it may be desirable to include perforations in the collagen for fluid movement through the stentcollagen wall. Such an arrangement is readily obtained as stents are generally open or perforate with respect to their structure and perforations may be readily formed in a collagen liner, the perforations extending through the stent openings. Perforation in collagen liners of about 10-60 microns in diameter have been found satisfactory. The distribution of the perforations may be such as to be evenly spaced, such as at 30-60 micron spacing and to occupy about one-half of the liner surface areas. This, of course, may vary.




Lastly, there is a preferred orientation for placing collagen on the stent when the collagen is used in the form of a sheet which is wrapped around the stent or a tube inserted in the stent. It has been discovered that sheet collagen has the ability to stretch but that its stretchability is predominantly unidirectional. That is, most of the stretch is exhibited in one primary direction in a sheet. This is shown schematically by the parallel arrows


100


in

FIG. 16

for a sheet of collagen


110


which typically shows little or no stretch in a direction normal to the arrows.




It has been discovered that the collagen sheet, when used as a sleeve or liner on a stent which undergoes expansion and/or contraction, can be better accommodated if the collagen sheet is associated with the stent on a “bias”. This will be more fully explained by reference to

FIGS. 17 and 18

. If a piece of collagen sheet


110




a


is taken from sheet


110


in the orientations shown in

FIG. 17

, it can be seen that the stretch direction indicated by the arrows


100


is on a bias with respect to sheet


110




a


. In this case, the bias is 45° relative to the edges of sheet


110




a


. If sheet


110




a


is oriented normally with respect to a stent


120


as shown in

FIG. 18

, i.e., the edges of sheet


110




a


are normal to the longitudinal dimension of stent


120


, when sheet


110




a


is wrapped around stent


120


to form a sleeve or rolled up (in direction shown at


112


in

FIG. 18

) into a tube for insertion into stent


120


as a liner, the stretch properties of sheet


110




a


will be on a bias with respect to the longitudinal dimension of stent


120


, in this case the bias is 45°, which is a preferred bias. Other degrees of bias are acceptable but 45° is preferred.




It can be seen from the foregoing that due to the variable dimensions in both diameter and length which occurs with stents, such an arrangement better accommodates collagen sleeves and liners to dimensional changes in both directions without disruption at seams and without tears in the material.




One preferred type of stent for use in this invention is one of the type disclosed in related application 08/246,320, filed May 19, 1994, the entire content of which is incorporated herein by reference.





FIGS. 19 and 20

show a coated stent generally indicated at


140


, the collagen coating


142


being best seen in FIG.


20


. Coating


142


is shown on both the inside and outside surfaces of the stent although it may be on either as well.




It can be seen from the above that the invention also provides a treatment method of implanting a stent in which collagen material is placed between the stent and the vessel wall thereby reducing thrombus formation and therapeutically treating the vessel when a suitable agent is included in the collagen.




The above Examples and disclosure are intended to be illustrative and not exhaustive. These examples and description will suggest many variations and alternatives to one of ordinary skill in this art. All these alternatives and variations are intended to be included within the scope of the attached claims. Those familiar with the art may recognize other equivalents to the specific embodiments described herein which equivalents are also intended to be encompassed by the claims attached hereto.



Claims
  • 1. A method of applying a collagen coating on a stent having a metal surface, comprising the steps of:immersing the stent in an aqueous electrolyte solution including collagen, an electrical potential being established between the anode and cathode adequate to sustain electrodeposition of the collagen from the solution onto the metal surface of the stent coating the metal surface with collagen by electrodeposition, the stent functioning as a cathode in an anode/cathode pair; and placing a tubular material about the stent or within the stent.
  • 2. The method of claim 1 wherein the tubular material comprises collagen.
  • 3. The method of claim 2 wherein during the placing step, the tubular material is placed about the stent.
  • 4. The method of claim 2 wherein during the placing step, the tubular material is placed within the stent.
  • 5. The method of claim 1 wherein the stent is a self-expanding stent.
  • 6. The method of claim 1 wherein the stent is a balloon-expandable stent.
  • 7. The method of claim 2 wherein the tubular material includes a therapeutic agent.
  • 8. The method of claim 7 wherein the therapeutic agent comprises heparin.
  • 9. The method of claim 2 wherein the tubular material is perforated.
  • 10. The method of claim 9 wherein the perforations are about 10-60 microns in diameter.
  • 11. The method of claim 1 wherein the tubular material comprises at least two types of collagen.
  • 12. The method of claim 11 wherein the tubular material is in the form of a bilayer.
  • 13. The method of claim 11 wherein the tubular material includes Type I and Type IV layers.
  • 14. A method of applying a collagen coating on an expandable stent, wherein the expandable stent has as metal surface, comprising the steps of:coating the metal surface with collagen by electrodeposition, wherein the expandable stent is expandable from a collapsed delivery diameter to an expanded deployment diameter, such that the delivery diameter is reduced from the deployment diameter, wherein the stent functions as a cathode in an anode/cathode pair and is immersed in an aqueous electrolyte solution including collagen and an electrical potential is established between the anode and cathode adequate to sustain electrodeposition of the collagen from the solution onto the metal surface of the stent, wherein the stent is inflation expandable from a collapsed delivery diameter to an expanded deployment diameter, such that the delivery diameter is reduced from the deployment diameter, and covering the stent with a sleeve of collagen material.
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of application Ser. No. 08/429,308, filed on Apr. 26, 1995, now U.S. Pat. No. 5,693,085, which is a continuation-in-part of application Ser. No. 08/350,223, filed on Dec. 6, 1994, now abandoned, which is a continuation-in-part of application Ser. No. 08/235,300, filed on Apr. 29, 1994, now abandoned, the disclosures of which are hereby incorporated by reference in their entirety.

US Referenced Citations (194)
Number Name Date Kind
3272204 Artandi et al. Sep 1966 A
3276448 Kronenthal Oct 1966 A
3425418 Chvapil et al. Feb 1969 A
3563228 Seiderman Feb 1971 A
3625745 Wright et al. Dec 1971 A
3688317 Kurtz Sep 1972 A
3758396 Vieth et al. Sep 1973 A
3764018 Shaw et al. Oct 1973 A
3839175 Keyes Oct 1974 A
3892648 Phillips et al. Jul 1975 A
3955012 Okamura et al. May 1976 A
3962414 Michaels Jun 1976 A
4047252 Liebig et al. Sep 1977 A
4082507 Sawyer Apr 1978 A
4104444 Hammer et al. Aug 1978 A
4190909 Ablaza Mar 1980 A
4252759 Yannas et al. Feb 1981 A
4286341 Greer et al. Sep 1981 A
4313231 Koyomada Feb 1982 A
4319363 Ketharanathan Mar 1982 A
4373009 Winn Feb 1983 A
4378017 Kosgi et al. Mar 1983 A
4390519 Sawyer Jun 1983 A
4390599 Broyles Jun 1983 A
4404970 Sawyer Sep 1983 A
4416028 Eriksson et al. Nov 1983 A
4434797 Silander Mar 1984 A
4466139 Ketharanathan Aug 1984 A
4474181 Schenck Oct 1984 A
4478658 Wittwer Oct 1984 A
4503569 Dotter Mar 1985 A
4512338 Balko et al. Apr 1985 A
4539716 Bell Sep 1985 A
4546500 Bell Oct 1985 A
4578067 Cruz, Jr. Mar 1986 A
4578079 Ruoslabti et al. Mar 1986 A
4581028 Fox, Jr. et al. Apr 1986 A
4591456 Huc et al. May 1986 A
4605406 Cahalan et al. Aug 1986 A
4606910 Sawyer Aug 1986 A
4614517 Ruoslahti et al. Sep 1986 A
4624822 Arru et al. Nov 1986 A
4629458 Pinchuk Dec 1986 A
4629459 Ionescu et al. Dec 1986 A
4641653 Rockey Feb 1987 A
4655771 Wallstein Apr 1987 A
4656130 Shoshan Apr 1987 A
4678468 Hiroyoshi Jul 1987 A
4690973 Noishiki et al. Sep 1987 A
4704131 Noishiki et al. Nov 1987 A
4713446 DeVore et al. Dec 1987 A
4732152 Wallsten et al. Mar 1988 A
4733665 Palmaz Mar 1988 A
4739762 Palnaz Apr 1988 A
4740207 Kreamer Apr 1988 A
4743258 Ikada et al. May 1988 A
4747848 Maini May 1988 A
4759758 Gabbay Jul 1988 A
4763653 Rockey Aug 1988 A
4772285 Ksander et al. Sep 1988 A
4773899 Spears Sep 1988 A
4774091 Yamahira et al. Sep 1988 A
4776337 Palmaz Oct 1988 A
4777049 Magrudre et al. Oct 1988 A
4784161 Skalsky et al. Nov 1988 A
4784659 Fleckenstein et al. Nov 1988 A
4787900 Yannas Nov 1988 A
4795458 Regan Jan 1989 A
4798606 Pinchuk Jan 1989 A
4801299 Brendel et al. Jan 1989 A
4804382 Turina et al. Feb 1989 A
4812120 Flanagan et al. Mar 1989 A
4814120 Huc et al. Mar 1989 A
4820302 Woodroof Apr 1989 A
4822361 Okita et al. Apr 1989 A
4826478 Schocket May 1989 A
4833200 Noishiki et al. May 1989 A
4835102 Bell et al. May 1989 A
4837379 Weinberg Jun 1989 A
4842575 Hoffman, Jr. et al. Jun 1989 A
4848343 Wallsten et al. Jul 1989 A
4849141 Fujioka et al. Jul 1989 A
4871361 Kira Oct 1989 A
4877030 Beck et al. Oct 1989 A
4880429 Stone Nov 1989 A
4902289 Yannas Feb 1990 A
4902290 Fleckenstein et al. Feb 1990 A
4902508 Badylak et al. Feb 1990 A
4911713 Sauvage et al. Mar 1990 A
4923380 Huc et al. May 1990 A
4923464 DiPisa, Jr. May 1990 A
4950227 Savin et al. Aug 1990 A
4950433 Ksander et al. Aug 1990 A
4950483 Ksander et al. Aug 1990 A
4954126 Wallsten Sep 1990 A
4956173 Badylak et al. Sep 1990 A
4956178 Badylak et al. Sep 1990 A
4960423 Smith Oct 1990 A
4969458 Wiktor Nov 1990 A
4969890 Sugita et al. Nov 1990 A
4973304 Graham et al. Nov 1990 A
4976734 Urry et al. Dec 1990 A
4979959 Guire Dec 1990 A
4984581 Stice Jan 1991 A
4986831 King et al. Jan 1991 A
4994388 Hillegas et al. Feb 1991 A
4996154 Gabriels, Jr. Feb 1991 A
5009655 Dignault, Jr. et al. Apr 1991 A
5011692 Fujioka Apr 1991 A
5012809 Shulze May 1991 A
5019090 Pinchuk May 1991 A
5019393 Ito et al. May 1991 A
5023082 Friedman et al. Jun 1991 A
5024841 Chu et al. Jun 1991 A
5026381 Li Jun 1991 A
5028597 Kodama et al. Jul 1991 A
5029574 Shimamura et al. Jul 1991 A
5037377 Alonso Aug 1991 A
5037427 Harada et al. Aug 1991 A
5059211 Stack et al. Oct 1991 A
5061275 Wallsten et al. Oct 1991 A
5061276 Tu et al. Oct 1991 A
5071407 Termin et al. Dec 1991 A
5077215 McAuslan et al. Dec 1991 A
5078681 Kawashima Jan 1992 A
5078735 Mobin-Uddin Jan 1992 A
5085632 Ikada et al. Feb 1992 A
5089005 Harada Feb 1992 A
5090959 Samson et al. Feb 1992 A
5100429 Sinofsky et al. Mar 1992 A
5106949 Kemp et al. Apr 1992 A
5108424 Hoffman, Jr. et al. Apr 1992 A
5110064 Chu et al. May 1992 A
5110604 Chu et al. May 1992 A
5116317 Carson, Jr. et al. May 1992 A
5125925 Lundahl Jun 1992 A
5127408 Parsons et al. Jul 1992 A
5131907 Williams et al. Jul 1992 A
5131908 Dardik et al. Jul 1992 A
5147370 McNamara et al. Sep 1992 A
5147389 Lane Sep 1992 A
5151105 Kwan-Gett Sep 1992 A
5157111 Pachence Oct 1992 A
5162430 Rhee et al. Nov 1992 A
5167233 Eberle et al. Dec 1992 A
5178616 Uemiya et al. Jan 1993 A
5182259 Kita Jan 1993 A
5188532 Goldenberg Feb 1993 A
5192311 King et al. Mar 1993 A
5195984 Schatz Mar 1993 A
5197977 Hoffman, Jr. et al. Mar 1993 A
5197978 Hess Mar 1993 A
5197979 Quintero et al. Mar 1993 A
5201764 Kelman et al. Apr 1993 A
5205921 Shirkanzadeh Apr 1993 A
5207705 Trudell et al. May 1993 A
5207709 Picha May 1993 A
5213580 Steplan et al. May 1993 A
5219361 Von Recum et al. Jun 1993 A
5230693 Williams et al. Jul 1993 A
5234456 Silvestrini Aug 1993 A
5234457 Andersen Aug 1993 A
5236704 Fujioka et al. Aug 1993 A
5256418 Kemp et al. Oct 1993 A
5256764 Tang et al. Oct 1993 A
5258042 Mehta Nov 1993 A
5258044 Lee Nov 1993 A
5263983 Yoshizato et al. Nov 1993 A
5275326 Badylak et al. Jan 1994 A
5275826 Badylak et al. Jan 1994 A
5281422 Badylak et al. Jan 1994 A
RE34544 Spears Feb 1994 E
5282823 Schwartz et al. Feb 1994 A
5286829 Fedorov et al. Feb 1994 A
5292802 Rhee et al. Mar 1994 A
5298255 Sawamoto et al. Mar 1994 A
5302168 Hess Apr 1994 A
5304121 Sahatjan Apr 1994 A
5304595 Rhee et al. Apr 1994 A
5306500 Rhee et al. Apr 1994 A
5316023 Palmaz et al. May 1994 A
5326370 Love et al. Jul 1994 A
5328955 Rhee et al. Jul 1994 A
5334171 Kaldany Aug 1994 A
5334201 Cowan Aug 1994 A
5334217 Das Aug 1994 A
5336258 Quintero et al. Aug 1994 A
5336518 Narayanan et al. Aug 1994 A
5342387 Summers Aug 1994 A
5360443 Barone et al. Nov 1994 A
5376376 Li Dec 1994 A
5383928 Scott et al. Jan 1995 A
5389106 Tower Feb 1995 A
5464650 Berg et al. Nov 1995 A
Foreign Referenced Citations (21)
Number Date Country
0 150 608 Aug 1985 EP
0 274 846 Jul 1988 EP
0361957 Sep 1989 EP
0 361 957 Apr 1990 EP
0403139 May 1990 EP
0418035 Nov 1990 EP
0 403 139 Dec 1990 EP
1 418 035 Mar 1991 EP
0 182 689 Dec 1991 EP
0 493 788 Jul 1992 EP
0 493 788 Jul 1992 EP
027484681 Sep 1994 EP
0 621 015 Oct 1994 EP
2 187 463 Sep 1987 GB
WO 8201647 May 1982 WO
WO 9306791 Apr 1993 WO
WO9306791 Apr 1993 WO
WO 9315785 Aug 1993 WO
WO 9320757 Oct 1993 WO
WO 9321860 Nov 1993 WO
WO9321860 Nov 1993 WO
Non-Patent Literature Citations (30)
Entry
U.S. application No. 08/235,300, Buscemi et al., filed Apr. 29, 1994.
U.S. application No. 08/350,223, Buirge et al., filed Dec. 6, 1994.
U.S. application No. 08/429,308, Buirge et al., filed Apr. 26, 1995.
Journal of Vascular Surgery, vol. 18, No. 2, Aug. 1993, pp. 299-302, Percutancous transfemoral insertion of a stented graft to repair a traumatic femoral arteriovenous fistula, Michael L. Marin, MD. et al.
Journal of Vascular Surgery, vol. 18, No. 6, Dec. 1993, pp. 1056-1059, Transluminal placement of a prosthetic graft-stent device for treatment of a subclavian artery ancurysm, James May, MS. FRACS, FACS, et al.
Journal of Vascular Surgery, vol. 19, No. 4, Apr. 1994, pp. 585-593. The role of circulating cells in the healing of vascular prostheses, Stewart M. Scott, MD. et al.
Journal of Vascular Surgery, vol. 19, No. 4, Apr. 1994, pp. 754-757. Transfemoral endoluminal stented graft repair of poplitcal artery ancurysm, Michael L. Marin, MD, et al.
The American Surgeon, vol. 54, No. 6, Jun. 1988, pp. 324-325, Comparison Between Externally Stented and Unstented PTFE Vascular Grafts, Margaret M. Dunn, M.D., et al.
Asaio Journal, vol. 39, No. 3, Jul.-Sep. 1993, pp. M758-M761, Development of an Expandable Intra-aortic Prosthesis for Experimental Aortic Dissection, Masaaki Kato, et al.
Asaio Journal, vol. 39, No. 3, pp. M518-M521, Development of a Chronic Endothelialized Transcatheter Implantable Intr-aortic Graft, Masaaki Kato, et al.
AJR: 151, Oct. 1988, pp. 673-676, Self-Expanding Graft: An Experimental Study in Dogs, Tetsuya Yoshioka, et al.
Radiology, vol. 163, May 1987, 163(2), pp. 357-360, Percutaneous Endovascular Graft: Experimental Evaluation1, David D. Lawrence, Jr., MD. et al.
Circulation, vol. 77, No. 1, Jan. 1988, pp. 188-199, Implantation of balloon-expandable intravascular grafts by catheterization in pulmonary arteries and systemic veins, Charles E. Mullins, M.D., et al.
Journal of Vascular Surgery, vol. 19, No. 4, Apr. 1994, pp. 754-757, Transfemoral endoluminal stented graft repair of a poplitcal artery aneurysm, Michael L. Marin, MD, et al.
The American Surgeon, vol. 54, No. 6, Jun. 1988, pp. 324-325, Comparison Between Externally Stented and Unstented PTFE Vascular Grafts, Margaret M. Dunn, M.D., et al.
Asaio Journal, vol. 39, No. 3, Jul.-Sep. 1993, pp. M758-M761, Development of an Expandable Intra-aortic Prosthesis for Experimental Aortic Dissection, Masaaki Kato, et al.
Asaio Journal, vol. 39, No. 3, pp. M518-M521, Development of a Chronic Endothelialized Transcatheter Implantable Intra-aortic Graft, Masaaki Kato, et al.
AJR: 151, Oct. 1988, pp. 673-676, Self-Expanding Graft: An Experimental Study in Dogs, Tetsuya Yoshioka, et al.
Radiology, vol. 163, May 1987, 163(2), pp. 357-360, Percautaneous Endovascular Graft: Experimental Evaluation1. David D. Lawrence, Jr., MD. et al.
Circulation, vol. 77, No. 1, Jan. 1988, pp. 188-199, Implantation of balloon-expandable intravascular grafts by Catheterization in pulmonary arteries and systemic veins, Charles E. Mullins, M.D., et al.
Journal of Vascular Surgery, vol. 18, No. 2, Aug. 1993, pp. 299-302, Percutancous transfemoral insertion of a stented graft to repair a traumatic femoral arteriovenous fistula, Michael L. Marin, MD. et al.
Journal of Vascular Surgery, vol. 18, No. 6, Dec. 1993, pp. 1056-1059, Transluminal placement of a prosthetic graft-stent device for treatment of a subclavian artery aneurysm, James May, MS, FRACS, FACS, et al.
Journal of Vascular Surgery, vol. 19, No. 4, Apr. 1994, pp. 585-593, The role of circulating cells in the healing of vascular prostheses, Stewart M. Scott, MD, et al.
Restenosis Summit VI, Poster Session Call for Abstracts, Biosynthetic Collegen Coated Endovascular Prostheses: Concept Feasibility, Paul Termin DVM PhD, Rob M. Carr BS, Organogenesis, Canton MA.
Restenosis Summit VI, Poster Session Call for Abstracts, Biosynthetic Collagen Coated Endovacular Prostheses: Concept Feasibility, Paul Tennin DVM PhD. Rob M. Carr BS, Organogenesis, Canton MA.
Journal of Pediatric Surgery, British Association of Paediatric Surgeons, vol. 27, No. 7, Jul. 1992, A New Oesophageal Tube: Assessment of Collagne/Viceryl Composite Membrane, pp. 856-858, by A. MacDonald, R. Carachi, and A. Gibson.
Journal of Intraventional Cardiology, vol. 5, No. 3, Sep. 1992, A New Bioabsorbable Intravascular Stent: In Vitro Assessment of Hemodvnamic and Morphometric Characteristics, pp. 187-194, by Jonathan D. Bier, M.D., Paul Zalesky, Ph.D., Shu-Tung Li, Ph.D., Harvey Sadken, M.D., and David O. Williams, Ph.D.
Abbott, W.M. et al., “Evaluation and Performance Standards for Aterial Prostheses”, Journal of Vascular Surgery, 1993; 17:746-756.
Haimovici, Henry, “Patch Graft Angioplasty”, Vascular Surgery, edition pp. 287-292.
American National Standard for Vascular Graft Prostheses, by the Association for the Advancement of Medical Instrumentation, approved Jul. 7, 1986.
Continuations (1)
Number Date Country
Parent 08/429308 Apr 1995 US
Child 08/960276 US
Continuation in Parts (2)
Number Date Country
Parent 08/350223 Dec 1994 US
Child 08/429308 US
Parent 08/235300 Apr 1994 US
Child 08/350223 US