Patent Application
20120202917
This invention is in the field of crosslinked polymers, in particular methods for stress-relief in crosslinked polymers and materials resulting from the methods.
Cross-linked, gelled polymers have an “infinite” molecular weight and are described as thermosets, implying a network that cannot be melted or molded (Billlmeyer, F. W., 1984, Textbook of Polymer Science, 3rd ed., Wiley, New York 436). This description is true for most chemically cross-linked polymers; however several cross-linked networks are known to undergo bond cleavage or depolymerization at high temperatures or under various chemical or other treatments (Adhikari, B. et al., Prog. Polym. Sci., 2000, 25, 909). Although such treatments are useful for recycling purposes, there is an associated degradation in the mechanical properties of the polymers.
“Crack-healing” networks, such as those that use groups in the polymer backbone able to undergo thermoreversible Diels-Alder reactions, are able to relieve stress without mechanical degradation (Chen, X. et al., 2002, Science, 295, 1698). These reactions must be performed at elevated temperatures, making them unsuitable for thermally sensitive applications.
Reversible bond cleavage is also known to occur during some polymerization processes. Some controlled free radical polymerization techniques employ degenerative chain transfer agents such as reversible addition-fragmentation chain transfer (RAFT) agents and iniferters. As part of the RAFT process, the RAFT agent adds to an active chain. At that point, the RAFT agent may fragment, with part of the RAFT agent remaining attached to the end of the chain (now dormant) and the other part forming a new radical. Similarly, in processes employing iniferters, iniferter fragments attached to chains are attached at the chain ends.
In one aspect, the invention provides methods for inducing reversible cleavage of polymer chains in a polymeric material or during polymerization to form a polymeric material. Reversible cleavage of the polymer backbone is capable of relieving stress as the bonds reform in a less stressed state. The methods of the invention can be applied to a variety of polymeric materials, including, but not limited to, polymeric coatings, dental materials, fiber reinforced materials, and optical materials.
The invention provides methods for relief of stress in crosslinked polymers. The stress relief may be of varying degrees, and need not be complete relief of all stress in the material. The stress may be internal, external, or a combination thereof. Internal stress buildup during polymerization of a crosslinked network is a typical result of polymerization shrinkage. Internal stress buildup may decrease the ultimate mechanical properties of the cured polymer and/or limit its applications. For example, in polymeric coatings and dental materials, internal stress may warp or crack the material or the underlying substrate.
The invention also provides monomer mixtures and polymerization methods for forming a crosslinked polymer network which can provide for relaxation of internal stress during polymerization.
In an embodiment, the invention provides mixtures comprising a first monomer comprising an addition-fragmentation chain cleavage group in the polymer backbone and a plurality of polymerizable groups and a second monomer or oligomer comprising a plurality of polymerizable groups and not comprising an addition-fragmentation chain cleavage group. The mixture may further comprise a source of free radicals or cations. The molar ratio of addition-fragmentation to polymerizable functional groups of the monomer(s) may be from 0.0025 to 0.1 (i.e. 0.25% to 10%), 0.0025 to 0.05 (i.e. 0.25% to 5%), 0.005 to 0.05 (i.e. 0.5% to 5%), 0.005 to 0.025 (i.e. 0.5% to 2.5%), 0.01 to 0.15 (1% to 15%), 0.02 to 0.15 (2% to 15%) 0.05 to 0.15 (5% to 15%), 0.075 to 0.15 (7.5% to 15%) or 0.1 to 0.15 (10% to 15%). The molar ratio of the first monomer to initiator may be from 0.05 to 10% or 1% to 5%.
In an embodiment the invention provides a mixture for forming a polymeric material comprising a crosslinked network of polymer chains, the mixture comprising
In an embodiment, the first monomer is linear or aliphatic, rather than cyclic. In an embodiment, the first monomer comprises a reversible addition fragmentation chain cleavage group linked to a plurality of polymerizable end groups by alkylene (divalent hydrocarbon) or ether linker groups. In an embodiment, the ether linker is —O-alkylene- or is formed of a plurality of —O-alkylene- groups. In an embodiment, the ether linker is —OCH2CH2— or is formed of a plurality of —OCH2CH2- units. In another embodiment, the linker group is a linear alkylene group which is —CH2— or is formed of a plurality of —CH2— repeat units. In an embodiment, the reversible addition fragmentation chain cleavage group is a thiocarbonylthio group. The thiocarbonylthio group may be a trithiocarbonate group or a dithioester such as an aromatic dithioester. In an embodiment, the first monomer may be as shown in Formula 21 or 22, with the polymerizable groups being acrylate or methacrylate groups. In an embodiment, the molecular weight of the first monomer is from 400-800 amu.
In an embodiment, the second monomer comprises at least two acrylate or methacrylate end groups. The second monomer may further comprise a bisphenol A-derived group or a urethane group. In an embodiment, the mixture does not include an additional diluent or solvent for the second monomer. In an embodiment, the molecular weight of the second monomer is from 200-800 amu.
In an embodiment, the invention provides a dental restorative composition comprising an acrylate or methacrylate monomer comprising a reversible addition fragmentation chain cleavage group, a methacrylate monomer or oligomer not comprising a reversible addition fragmentation chain cleavage group, filler particles, and a free radical initiator. The amount of filler particles may be 45 to 85% by weight (wt %) of the composition. The filler particles may be inorganic particles or surface treated inorganic particles. Suitable inorganic materials particles for use in the invention include, but are not limited to, barium containing glass, strontium containing glass, zirconia silicate and/or amorphous silica having a size ranging from 0.005 to 5.0 micrometers or 0.01 to 1.0 micrometers. In different embodiments, the methacrylate monomer or oligomer not including a reversible addition fragmentation chain cleavage group may be BIS-GMA-based or urethane methacrylate-based.
The acrylate or methacrylate monomer comprising a reversible addition fragmentation chain cleavage group may act as a reactive diluent which may be used to lower the viscosity and make the composition pourable at ordinary room temperatures such as at about 20°-25° C. In an embodiment, the monomer(s) comprising reactive addition fragmentation chain cleavage groups is/are the only reactive diluent(s) present in the composition. In an embodiment, the weight percentage of the monomer comprising the reversible addition fragmentation chain cleavage group may be from 1 to 30 wt % of the monomer component of the composition. In another embodiment, the acrylate or methacrylate monomer comprising the reversible addition fragmentation chain cleavage group may be combined with an additional acrylate or methacrylate monomer which also acts as a reactive diluent. This additional acrylate or methacrylate monomer may be, for example, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, iso-propyl methacrylate, n-butyl methacrylate, iso-butyl methacrylate, sec-butyl methacrylate, tert-butyl methacrylate, the amyl methacrylates, ethylene dimethacrylate, butylene dimethacrylate, ethylene glycol monomethacrylate, ethylene glycol dimethacrylate, triethylene glycol dimethacrylate or tetraethylene glycol dimethacrylate.
In an embodiment, the invention provides methods for forming crosslinked polymeric materials. In an embodiment, the method comprises the steps of:
In an embodiment, the invention provides a method for forming a dental restorative material, the method comprising the steps of
The methods of the invention also can provide photoinduced plasticity, actuation and equilibrium shape changes without any accompanying residual stress. Polymeric materials such as these that are able to respond “on demand” with control of stress, shape and plasticity are critical to the development of microdevices, biomaterials and polymeric coatings.
The methods of the invention can achieve stress relief, photoinduced plasticity, actuation or equilibrium shape changes without any substantial permanent degradation in the mechanical properties of the material. In addition, the methods of the invention can alter the topology of the network without permanently changing the network connectivity.
The invention also provides polymeric materials capable of reversible chain cleavage and linear multifunctional monomers useful in making these materials. The invention further provides methods of making polymeric materials capable of reversible chain cleavage. Polymeric materials made by the processes of the invention can have reduced levels of internal stress when compared to polymeric materials made by conventional polymerization processes.
Reversible cleavage of the polymer backbone is enabled by incorporation of “reversible chain cleavage” groups or functionalities into the polymer backbone. Under the appropriate conditions, the reversible chain cleavage groups are activated, leading to reversible cleavage of the polymer backbone. At least some of the reversible chain cleavage groups are incorporated mid-chain. Depending on the nature of the chain cleavage group, the chain cleavage group may be activated through reaction with either a free radical or a cation. If the reversible chain cleavage group is an iniferter, the iniferter may be activated by light or heat.
The invention provides methods for inducing reversible chain cleavage in a polymeric material comprising a crosslinked network of polymer chains. As used herein, a polymeric material comprises a polymer and may further comprise non-polymeric additives. In the present invention, a multiplicity or plurality of the polymer chains incorporate at least one reversible chain cleavage group in the polymer backbone. Reversible chain cleavage groups incorporated in side chains or at the chain ends, rather than in the backbone, are not effective in producing stress relief. Crosslinked polymer networks may be characterized by the gel-point conversion, a critical transition point where there is a single sample spanning macromolecule. The gel-point conversion is defined mathematically as the conversion where the weight average molecular weight diverges. The polymerization mechanism used to form the crosslinked polymeric material may be any mechanism known to the art, including step-reaction (thiol-ene) and chain-reaction. In different embodiments, the crosslinked polymeric materials of the invention may have at least 50%, 60%, 70%, 80% or 90% conversion of the polymerizable functional groups. The conversion of polymerizable functional groups may be measured with infrared absorption spectroscopy.
As used herein, in a reversible chain cleavage process both chain cleavage and chain recombination occur. Recombination may occur through simple reversal of the chain cleavage reaction. In addition, the products of the chain cleavage reaction at one cleavage location are capable of participating in additional chain cleavage reactions, allowing combination of chain fragments from different cleavage locations and chain rearrangement. For example, the reversible chain cleavage process may be an addition-fragmentation process in which a radical reacts with an in-chain addition-fragmentation functionality to form an intermediate, which in turn fragments to reform the initial functionality and a new radical. The new radical may further react with another in-chain functionality or the initial functionality may further react with another radical generated by a different addition-fragmentation event. Chain rearrangement resulting from the reversible chain cleavage process can alter the topology of the network. In the absence of radical termination events or other side reactions, the number of reversible chain cleavage groups, and hence network strands, remains unchanged.
As used herein, a reversible chain cleavage group is capable of both breaking and forming in-chain bonds. In an embodiment, the reversible chain cleavage group is a chain transfer group which undergoes addition-fragmentation type chain transfer. As used herein, “addition-fragmentation” is either a two-step or concerted chain transfer mechanism wherein addition of a radical or cation is followed by fragmentation to generate a new radical or cation species. Scheme 1 illustrates a reaction mechanism for addition-fragmentation chain transfer within a polymer backbone incorporating an allyl sulfide functionality. In Scheme 1, an allyl sulfide group in the backbone reacts with a thiyl radical generated from a previous chain cleavage event, resulting in cleavage of the backbone and formation of a different thiyl radical (a R3 containing radical). The R3 containing thiol radical shown in Scheme 1 is capable of reacting with an allyl sulfide group located at another chain position. The reformed allyl sulfide functionality is capable of reacting with another thiyl radical generated by chain cleavage.
Suitable addition-fragmentation functionalities or agents for use in the invention include conventional reversible addition-fragmentation chain transfer (RAFT) agents, allyl sulfides, dithiocarbamates, trithiocarbonates and thiuram disulfides. RAFT agents are known to those skilled in the art. Examples of RAFT agents are given in U.S. Pat. No. 6,153,705, and published international applications WO 98/01478, WO 99/35177, WO 99/31144 and WO 98/58974. Allylic sulfide chain transfer groups are described by Meijs et al. (1998, Macromolecules, 21(10), 3122-3124). Suitable addition-fragmentation chain transfer agents include trithiocarbonate or allyl sulfide functionalities.
WO 98/01478 discloses that free radical polymerizations when carried out in the presence of certain chain transfer agents of the following structure:
have living characteristics and provide polymers of controlled molecular weight and low polydispersity.
WO 98/01478 also discloses thiocarbonylthio compounds selected from
having a chain transfer constant greater than about 0.1 wherein Z is selected from the group consisting of hydrogen, chlorine, optionally substituted alkyl, optionally substituted aryl, optionally substituted heterocyclyl, optionally substituted alkylthio, optionally substituted alkoxycarbonyl, optionally substituted aryloxycarbonyl (—COORy), carboxy (—COOH), optionally substituted acyloxy (—O2CRy), optionally substituted carbamoyl (—CON(Ry)2), cyano (—CN), dialkyl- or diaryl-phosphonato [—P(═O)O(Ry)2], dialkyl- or diaryl-phosphinato [—P(═O)(Ry)2], and a polymer chain formed by any mechanism, Z′ is a m-valent moiety derived from a member of the group consisting of optionally substituted alkyl, optionally substituted aryl and a polymer chain; where the connecting moieties are selected from the group that consists of aliphatic carbon, aromatic carbon, and sulfur, R is selected from the group consisting of optionally substituted alkyl; an optionally substituted saturated, unsaturated or aromatic carbocyclic or heterocyclic ring; optionally substituted alkylthio; optionally substituted alkoxy; optionally substituted dialkylamino; an organometallic species; and a polymer chain prepared by any polymerization mechanism; in the compounds of Formulas 2 and 3, R. is a free radical leaving group that initiates free radical polymerization; Ry is selected from the group consisting of optionally substituted C1-C18 alkyl, C2-C18 alkenyl, aryl, heterocyclyl, aralkyl, alkaryl wherein the substituents are independently selected from the group that consists of epoxy, hydroxy, alkoxy, acyl, acyloxy, carboxy (and salts), sulfonic acid (and salts), alkoxy- or aryloxycarbonyl, isocyanato, cyano, silyl, halo, and dialkylamino; p is 1 or an integer greater than 1; when p≧2, then R═Rx, m is an integer ≧2; and Rx is a p-valent moiety derived from a member of the group consisting of optionally substituted alkyl, optionally substituted aryl and a polymer chain; where the connecting moieties are selected from the group consisting of aliphatic carbon, aromatic carbon, silicon, and sulfur; in the compounds of Formulas 2 and 3, Rx. is a free radical leaving group that initiates free radical polymerization.
WO 99/31144 discloses the sulfur based CTA (chain transfer agent) of formula 4 below:
wherein when D is D1 of the following formula 5 below:
then p′ is in the range of from 1 to 200, E is Z″ and said transfer agent is of the following formula 6 below:
wherein when D is D2 of the following formula 7 below:
then p′ is in the range of from 1 to 200, E is E1 or E2 and said transfer agent is of the following formula 8 below:
wherein when D is D3 of the following formula 9 below:
then p″ is in the range of from 2 to 200, E is Z′, E1 or E2 and said transfer agent is of the following formula 10 below:
or
wherein when D is D4 of the following formula 11 below:
—S—R″ Formula 11
then E is E3 or E4 and said transfer agent is of the following formula 12:
where in all of the above:
wherein G and J are independently selected from the group consisting of hydrogen, substituted or unsubstituted alkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted alkoxy, substituted or unsubstituted acyl, substituted or unsubstituted aroyl, substituted or unsubstituted aryl, substituted or unsubstituted heteroaryl, substituted or unsubstituted alkenyl, substituted or unsubstituted alkylsulfonyl, substituted or unsubstituted alkylsulfinyl, substituted or unsubstituted alkylphosphonyl, substituted or unsubstituted arylsulfonyl, substituted or unsubstituted arylsulfinyl, substituted or unsubstituted arylphosphonyl; and
wherein G′ is selected from the group consisting of substituted or unsubstituted alkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted aryl;
wherein p″″ is between 2 and 200, G″ is Z″'and J′ is independently selected from the group consisting of hydrogen, substituted or unsubstituted alkyl, substituted or unsubstituted alkenyl, substituted or unsubstituted alkoxy, substituted or unsubstituted acyl, substituted or unsubstituted aroyl, substituted or unsubstituted aryl, substituted or unsubstituted heteroaryl, substituted or unsubstituted alkenyl, substituted or unsubstituted alkylsulfonyl, substituted or unsubstituted alkylsulfinyl, substituted or unsubstituted alkylphosphonyl, substituted or unsubstituted arylsulfonyl, substituted or unsubstituted arylsulfinyl, substituted or unsubstituted arylphosphonyl; and
U.S. Pat. No. 6,153,705 discloses compounds of the general formula
q being between 2 and 10, preferably between 2 and 5, Ra and Rb, which are identical or different, represent: an optionally substituted alkyl, acyl, aryl, alkene or alkyne group (i), or an optionally substituted, saturated or unsaturated, carbon-containing or aromatic ring (ii), or an optionally substituted, saturated or unsaturated heterocycle (iii), it being possible for these groups and rings (i), (ii) and (iii) to be substituted with substituted phenyl groups, substituted aromatic groups, or groups: alkoxycarbonyl or aryloxycarbonyl (—COORc), carboxy (—COOH), acyloxy (—O2CRc), carbamoyl (CON(Rc)2), cyano (—CN), alkylcarbonyl, alkylarylcarbonyl, arylcarbonyl, arylalkylcarbonyl, phthalimido, maleimido, succinimido, amidino, guanidimo, hydroxyl (—OH), amino (—N(Rc)2), halogen, allyl, epoxy, alkoxy (—ORc), S-alkyl, S-aryl, groups having a hydrophilic or ionic character, such as the alkali metal salts of carboxylic acids, the alkali metal salts of sulphonic acid, polyalkylene oxide chains (PEO, PPO), cationic substituents (quaternary ammonium salts), Rc representing an alkyl or aryl group, a polymer chain, Za is S or P, Zb is O, S or P.
Each reversible addition-fragmentation chain transfer agent is activated by reaction with a free radical or cation, the reaction being addition of the free radical or cation to the chain transfer agent. The reversible chain cleavage process is initiated by activating a source of free radicals or cations (other than the addition -fragmentation chain transfer agent); this source may also be termed a reversible chain cleavage initiator. At a later stage in the process, radicals or cations capable of activating the reversible addition-fragmentation chain transfer agents are also generated during the fragmentation steps. To obtain the desired amount of reversible chain cleavage, it may be desirable to continue to activate the source of free radicals or cations after the start of the reversible chain cleavage process. The recurring chain transfer reactions amplify the effects of each generated radical and lead to reaction diffusion of radicals through the cross-linked matrix.
When the reversible chain cleavage group is an addition-fragmentation group, a source of free radicals or cations is present during the polymerization process and is optionally incorporated into the polymeric material. A source of free radicals or cations is incorporated into the polymeric material if the reversible chain cleavage groups are to be activated after polymerization.
In an embodiment, the source of free radicals is a photoinitiator or a thermally activated initiator. In another embodiment, the source of free radicals is an iniferter, which may or may not be incorporated in the polymer chains. Use of an iniferter as the source of free radicals is expected to provide a virtually endless source of radicals, since iniferters are expected to be depleted significantly more slowly than more traditional radical sources. In another embodiment the source of free radicals is a redox system. In another embodiment, the source of cations is a photoacid generator such as a diaryliodonium or triaryl sulfonium salts. As used herein, the source of free radicals or cations is activated when it produces free radicals or cations. In an embodiment, the source of radicals or cations is activated so as to produce a greater concentration of radicals or cations than would be produced by ambient conditions. For example, a photoinitiator or iniferter may be activated by an artificial light source such as a UV lamp rather than by simple exposure to sunlight. The source of free radicals or cations may consist of a combination of different sources of free radicals or cations. In an embodiment, the source of free radicals comprises two photoinitiators which are activated by different wavelengths of light. In this embodiment, one photoinitiator may be activated during the polymerization process and the other activated subsequent to polymerization. For example, one photoinitiator may be a photoinitiator active in the visible region of the spectrum and the other may be active in the near ultraviolet.
The source of free radicals or cations may be activated by any method known to the art, including exposure to light, heat, or an electron beam. The time for which the free radical/cation source is activated and the concentration of the free radical/cation source can influence the amount of backbone cleavage which occurs. The source of free radicals or cations can be activated during polymerization, following polymerization, or both.
The reversible chain cleavage initiators are present in an amount effective to produce the desired amount of reversible chain cleavage. In one embodiment where the polymeric material is made by polymerization of a mixture comprising at least one monomer containing an in-chain reversible chain cleavage group, the amount of reversible chain initiator provided in the mixture is greater than the amount that would typically be used for polymerization of a similar mixture comprising a similar monomer not containing an in-chain reversible chain cleavage group. As described above a combination of initiators may also be used to ensure that sufficient initiator remains after polymerization is complete. The effective amount of reversible chain initiator will depend on the efficiency of the system, the time for during which reverse chain cleavage occurs, and the amount of impurities in the system. In an embodiment, the concentration of the source of free radicals or cations is between 0.1 wt % and 5.0 wt %.
In another embodiment, the reversible chain cleavage group is a reactive group which undergoes reversible fragmentation and recombination. Chain cleavage occurs during the fragmentation step. In this embodiment, the reversible chain cleavage group is activated by exposure to conditions which initiate fragmentation of the reversible chain cleavage group. No separate source of free radicals or cations (other than the reversible chain cleavage group) is required. Suitable reactive groups useful for this embodiment include iniferters. Iniferter compounds are known to those skilled in the art and include, but are not limited to, dithiocarbamates and thiuram disulfides. Iniferters contain a chemical bond that will homolytically cleave under appropriate thermal or photolytic conditions, forming either one sulfur centered and one carbon centered radical or two sulfur centered radicals. Rearrangement of the network connectivity occurs when radicals generated by two different chain cleavage events recombine. In this embodiment, during the cleavage event the crosslink density can temporarily decrease, but returns to normal after recombination.
In another embodiment, the polymeric material incorporates a plurality of chemically different reversible chain cleavage groups. For example, the polymeric material may incorporate two chemically different reversible addition-fragmentation chain transfer groups or may incorporate at least one reversible addition-fragmentation chain transfer group and at least one fragmentation and recombination group. For example, including an addition-fragmentation functionality in combination with an iniferter as a source of free radicals has the potential to allow the production of unlimited plasticity in the material which wouldn't be possible with a conventional initiator. A conventional initiator would be expected to run out after a certain light dose (for a photoinitiator) or time (for a thermal initiator).
In an embodiment, the reversible chain cleavage group can be incorporated into the polymer backbone by polymerization of a monomer comprising the chain cleavage group. The monomer comprising the chain cleavage group may be a ring opening monomer or a linear monomer. Ring opening monomers suitable for the practice of the invention include, but are not limited to, cyclic allylic sulfides. Cyclic allylic sulfide monomers capable of free-radical ring-opening polymerization are reported by Evans and Rizzardo (Evans, R. et al., 2001, J. Polym. Sci. A, 39, 202) and in U.S. Pat. No. 6,043,361 to Evans et al.
Linear monomers suitable for the practice of the invention include multifunctional monomers containing an addition-fragmentation chain transfer functionality in their backbone, as shown in Formula 20.
A1-Y-A2 Formula 20
In Formula 20, A1 and A2 each independently comprise at least one polymerizable group. Examples of polymerizable groups include, but are not limited to, acrylates, methacrylates, oxiranes(epoxies), amines, vinyl ethers, vinylics, allyl ethers, allylics, thiols, styrenics, isocyanates, and hydroxides, and combinations thereof. In an embodiment, the polymerizable group is selected from the group consisting of acrylates, methacrylates, vinyl ethers, and allyl ethers. Y is a reversible chain cleavage group. A1, A2 and Y may be attached together with any suitable linker group such as a C1-C10 alkyl chain that may be optionally substituted with cyclic or aromatic functionalities or such as an ether. In an embodiment, the multifunctional monomer is a difunctional monomer. These linear monomers may be made by synthetic methods known to those skilled in the art.
In an embodiment, the difunctional monomer contains a trithiocarbonate addition-fragmentation chain transfer functionality in its backbone. Each of the in-chain sulfur atoms may be bonded to a tertiary carbon, which is in turn bonded to a linking group, the linking group being bonded to a polymerizable group (e.g. the polymerizable groups (PGs) are end groups). Such a difunctional monomer may be described by Formula 21 or 22
where L1-L4 are linking groups and PG1 and PG2 are polymerizable groups. In an embodiment, R4, R5, R6, and R7, independently, can be the same or different and can be a linear or branched alkyl group having from 1 to 6 carbon atoms, a linear or branched alkyl group having from 1 to 6 carbon atoms and substituted with an aryl group or substituted aryl group or an aryl group or a substituted aryl group, having from 1 to 6 substituents on the aryl ring. In an embodiment, the substituent on the aryl ring may be an alkyl group having from one to 6 atoms, fluorine, chlorine, a cyano group, or an ether having a total or 2 to 20 carbon atoms. In an embodiment, R4, R5, R6, and R7 are methyl or phenyl. In formula 21, L1 and L2, independently, can be the same or different and can be an ether group or an alkylene group. The ether linker may have 1-12, 2-10, 4-8 or 6 carbon atoms. In an embodiment, the linking group is —(CH2—CH2-O)g— where g is an integer from 1 to 6 (where an oxygen atom in the repeat unit is bound to the carbonyl carbon). In an embodiment, L1 is —CH2CH2O— or formed of a plurality of —CH2CH2O— repeat units and L2 is —OCH2CH2— or formed of a plurality of —OCH2CH2— repeat units (where an oxygen atom in the repeat unit is bound to the carbonyl carbon). In formula 22, L3 and L4, independently, can be the same or different and can be an ether group or an alkylene group. In formulas 21 and 22 PG1 and PG2 can be the same or different and can be acrylate CH2═CHCOO— or methacrylate CH2═C(CH3)COO—.
In an embodiment, the linear multifunctional monomer is as shown in Formula 23:
In an embodiment, A1 and A2 comprise polymerizable groups which are both acrylate, methacrylate, or vinyl ether groups. In Formula 23, Y of formula 20 is an allyl disulfide functionality.
Use of linear monomers rather than cyclic ring-opening monomers in the practice of the invention can have several advantages. The use of linear monomers allows much greater flexibility as to potential monomer structure and can allow for increased glass transition temperatures. The monomer synthesis process can also be simplified. The polymerization reaction can also be much faster and higher crosslink densities can be achieved, allowing attainment of higher glass transition temperatures. Materials with higher transition temperatures are more useful for structural purposes which require a hard glassy material rather than a soft rubbery material.
In another embodiment, the reversible chain cleavage group can be incorporated into the polymer backbone by copolymerization of a first monomer comprising the reversible chain cleavage group with at least one other monomer. The other monomer(s) to be copolymerized with the first monomer can be any monomer known to the art, so long as it can be successfully copolymerized with the first monomer. The amount of the first monomer is selected to provide the desired amount of reversible chain cleavage group incorporation into the polymer backbone. The selection of the amount of the first monomer depends in part on the desired amount of stress relief and the desired mechanical or chemical properties of the copolymer.
Monomers suitable for the practice of the invention include those which are capable of forming cross-linked networks of polymer chains, either singly or in combination with one or more other monomers. In an embodiment, suitable monomers for the practice of the invention include, but are not limited to: ethylene oxides (for example, PEO), ethylene glycols (for example, PEG), vinyl acetates (for example, PVA), vinyl pyrrolidones (for example, PVP), ethyloxazolines (for example, PEOX), amino acids, saccharides, proteins, anhydrides, vinyl ethers, thiols, amides, carbonates, phenylene oxides (for example, PPO), acetals, sulfones, phenylene sulfides (for example, PPS), esters, fluoropolymers, imides, amide-imides, etherimides, ionomers, aryletherketones, olefins, styrenes, vinyl chlorides, ethylenes, acrylates, methacrylates, amines, phenols, acids, nitriles, acrylamides, maleates, benzenes, epoxies, cinnamates, azoles, silanes, chlorides, epoxides, lactones, isocyanates, hydroxides and amides.
In an embodiment, a monomer with acrylate or methacrylate polymerizable groups may also comprise at least one bisphenol A-derived group. As used herein, a monomer including a bisphenol A-derived group includes the group:
Suitable methacrylate monomers with bisphenol A-derived “cores” include Bisphenol A ethoxylate dimethacrylate (BisEMA) and bisphenol A glycidyl methacrylate (BisGMA), bisphenol A dimethacrylate (bis-DMA) Suitable acrylate monomers with bisphenol A-derived cores include Bisphenol A ethoxylate diacrylate. In an embodiment, the monomer is Bis-GMA based monomer or oligomer represented by the Formula 24
where f is from 1-10, 1-5, or 1-3. In another embodiment, the Bis-GMA based monomer may be a modified bis-GMA type monomer or oligomer. For example, the OH groups of a bis-GMA type monomer may be reacted with alkyl isocyanates as described by Khatri et al. ACS Polymer Preprints 41 (2). 1724-1725, hereby incorporated by reference.
In an embodiment, a monomer with acrylate or methacrylate polymerizable groups may also comprise at least one urethane group. In an embodiment, the monomer comprises from 2-4 or 2-6 urethane groups. Hydrogen bonding between urethane groups can enhance the toughness of the polymer. Such monomers can be aliphatic or aromatic. Examples of acrylates/methacrylates with urethane groups include, but are not limited to 7,7,9-trimethyl-4,13-dioxo-3,14-dioxa-5,12-diazahexadecane-1,16-diyl bis(2-methylacrylate) and 2-((((5-(((2-(methacryloyloxy)ethoxy)carbonyl)amino)-1,3,3-trimethylcyclohexyl)methyl)carbamoyl)oxy)ethyl methacrylate. In an embodiment, the urethane dimethacrylate has the formula:
The amount of the monomer(s) containing the addition-fragmentation functionality may be referenced to the concentration of the monomer not including the addition-fragmentation functionality, the concentration of polymerizable functional groups or given as its concentration in the monomer mixture. The molar ratio of the addition-fragmentation groups to polymerizable functional groups of the monomer(s) may be from 0.0025 to 0.1 (i.e. 0.25% to 10%), 0.0025 to 0.05 (i.e. 0.25% to 5%), 0.005 to 0.05 (i.e. 0.5% to 5%), or 0.005 to 0.025 (i.e. 0.5% to 2.5%), 0.01 to 0.15 (1% to 15%), 0.02 to 0.15 (2% to 15%) 0.05 to 0.15 (5% to 15%), 0.075 to 0.15 (7.5% to 15%) or 0.1 to 0.15 (10% to 15%). Alternately, the weight percentage of RAFT monomer in the monomer solution may be from 1 to 10 wt %.
The compositions, monomer mixtures and crosslinked polymeric materials of the invention may also comprise filler particles. A variety of inorganic filler materials can be used, including, but not limited to, silica, quartz, glass, silicates such as calcium silicate and zirconium silicate, metal oxide powders such as aluminum or zinc oxide and calcium carbonate. These fillers may be surface treated and for example can have organosilyl groups on their surface. For dental restorative materials, the filler particles may be silanized filler compounds such as barium containing glass, strontium containing glass, zirconia silicate and/or amorphous silica to match the color and opacity to a particular use or tooth. The filler is typically in the form of particles with a size ranging from 0.01 to 5.0 micrometers. The amount of filler particles may be 45 to 85% by weight (wt %) of the monomer mixture.
One measure of the relative number of reversible chain cleavage groups in the crosslinked polymer network is the ratio of the number of reversible chain transfer groups to the number of crosslinks in the network. This ratio is selected based partly on the desired extent of reversible chain cleavage in the network and partly on the desired mechanical properties of the material (e.g. the elastic modulus). In different embodiments, the ratio of the number of reversible chain transfer groups to the number of crosslinks in the network is greater than or equal to one-quarter, greater than or equal to one-half, greater than or equal to one, greater than or equal to one and one-half, or greater than or equal to two.
The invention also provides methods for making polymeric materials. In an embodiment, the method comprises the steps of forming a mixture comprising one or more monomers, wherein at least one monomer is characterized by Formulas 20, 21, 22 or 23 and subjecting the mixture to polymerization conditions. If the reversible chain cleavage group is an addition-fragmentation group, the mixture further comprises a source of free radicals or cations. As used herein, polymerization conditions are those conditions that cause the at least one monomer to form a polymer, such as temperature, pressure, atmosphere, ratio of starting components used in the polymerization mixture, reaction time, or external stimuli of the polymerization mixture. The polymerization process can be carried out in bulk, or solution, or other conventional polymerization modes. The process is operated at any of the reaction conditions appropriate to the polymerization mechanism.
The polymerization mechanism may be any mechanism known to the art, including step-reaction and chain-reaction. When the reversible chain cleavage agent is an addition-fragmentation chain transfer agent, the polymerization process is conducted in the presence of a free radical/cation source to ensure that the free radical/cation source is incorporated in the polymeric material. However, depending on the nature of the polymerization process, the free radical/cation source may or not be activated during polymerization. In an embodiment, the method for making the polymeric material forms a mixture of a monomer described by Formula 20, wherein Y is an addition-fragmentation agent activated by free radicals, and a source of free radicals, but the source of free radicals is not activated as part of the polymerization conditions. The combination of the monomer(s) and the free radical/cation source may be selected to produce reversible chain cleavage during the polymerization process. For example, if the polymerization mechanism involves free-radical polymerization an addition-fragmentation chain transfer group such as an allyl sulfide is likely to lead to chain transfer during the polymerization process. If chain transfer occurs during polymerization, the reversible chain-cleavage group incorporated into the backbone may differ somewhat from the reversible chain-cleavage group present in the monomer (e.g. the R groups may change).
The combination of the monomer and the free radical/cation source may also be selected so that reversible chain cleavage does not occur during the polymerization process, in which case the free radical/cation source is present during polymerization to ensure its incorporation into the polymeric material. If the polymerization mechanism does not involve free radicals, an addition-fragmentation chain transfer functionality such as an allyl sulfide will not usually lead to chain transfer during the polymerization process. For example, divinyl ether functionalized monomers containing an addition-fragmentation chain transfer group can be cationically photopolymerized at wavelengths different than those which activate a photoinitiator free radical source. Similarly, epoxy amine systems in which at least one monomer incorporates a reversible chain cleavage group can be polymerized without activating the reversible chain cleavage group. However, chain transfer can be “forced” in this type of system by activating a source of radicals or cations that is not required for the curing process (e.g. by activating a photoinitiator during the curing process).
If reversible chain cleavage is to occur after polymerization, the polymerized material is exposed to conditions sufficient to cause activation of the reversible chain cleavage group. If the reversible chain cleavage group is an addition-fragmentation chain transfer group, polymerized material is also exposed to conditions sufficient to cause activation of the source of free radicals or cations. The free radicals or cations produced can react with the reversible chain-cleavage groups, thereby activating the reversible chain-cleavage groups. Reaction of a chain transfer group with the free radical or cation produced by the free radical/cation source can result in generation of a free radical different than that produced by the free radical/cation source; this newly generated free radical can react with other reversible chain transfer groups in turn.
The end result of the polymerization process is a polymeric material comprising a crosslinked network of polymer chains. In an embodiment, the present invention provides polymeric materials capable of reversible chain cleavage subsequent to polymerization. In the polymeric materials of the invention, a plurality or multiplicity of the polymer chains incorporate at least one reversible chain cleavage group in the polymer backbone. If the reversible chain cleavage group is an addition-fragmentation chain transfer group, the polymeric material further comprises an effective amount of a free radical/cation source. The novel crosslinked polymeric materials of the invention are not intended to include previously reported polymeric materials which contain in-chain allyl sulfide groups or thiuram disulfide groups, such as the materials reported by Evans and Rizzardo (Evans, R. et al., 2001, J. Polym. Sci. A, 39, 202) and in U.S. Pat. No. 6,043,361 to Evans et al. or the thiuram disulfide containing materials reported by Clouet in U.S. Pat. No. 5,658,986 and publication WO 91/05779. Some of these previously reported materials may include residual levels of thermal initiators or photoinitiators following polymerization.
When stress relief occurs during polymerization, the invention can provide methods of making crosslinked polymeric materials with lower shrinkage stress than materials made without the use of reversible addition-fragmentation monomers. In an embodiment, the crosslinked polymeric materials resulting from this process have a shrinkage stress level less than 1.5 MPa, 1.0 MPa, or 0.75 MPa.
The invention also provides methods of making crosslinked polymeric materials capable of reversible chain cleavage. In an embodiment, the methods involve polymerizing a monomer with a mid-chain addition-fragmentation group. However, the polymerization conditions may vary. For example, polymerization may take place in the presence of a source of free radicals or cations although the polymerization does not occur through free radical polymerization. In addition, the polymerization may involve the monomers of Formulas 20, 21, 22 or 23.
The invention provides methods for relief or reduction of stress in crosslinked polymers. The stress relief may be of varying degrees, and need not be complete relief of all stress in the material. For example, the amount of stress reduction can range from less than one percent to nearly one hundred percent. The stress may be internal, external, or a combination thereof. In an embodiment, the methods of the invention can also be used to produce materials which have lower internal stress than would be produced with polymerization techniques previously known to the art.
The amount of stress relaxation depends upon the number of reversible chain cleavage groups in the material, the amount of time during which reversible chain cleavage occurs, and the conditions under which reversible chain cleavage occurs (e.g. when reversible chain cleavage is initiated by a photoinitiator, the intensity of the light source). For a given material under a given initial stress, the stress level in the material can decrease more rapidly at the start of the stress relaxation process and then level out at longer times. One measure of the amount of stress relief is the percent change in stress in a material having a constant initial stress level, either at a set time or after the stress level has started to level out. In this embodiment, the reduction in stress obtained after 5 minutes can be greater than or equal to 10%, greater than or equal to 20%, or greater than or equal to 30%. The reduction in stress obtained at longer times can be greater than or equal to 90%. Another indicator of the amount of stress relief is the amount of creep, or the amount of deformation which occurs under constant load, due to the stress relaxation process. A third indicator of the amount of stress relief is the percent change in the stress level in a material under constant strain. In this embodiment, the reduction in stress obtained after 5 minutes can be greater than or equal to 20%, greater than or equal to 30%, or greater than or equal to 40%. The reduction in stress obtained at longer times can be greater than or equal to 90%. The reduction in stress as a function of time can be obtained through mechanical testing techniques known to those skilled in the art. In some cases, such as for rubbery samples, the stress can “even out” over more than the irradiated portion of the sample. For materials which display visco-elastic behavior the strain rate should be selected appropriately.
Reversible chain cleavage within the polymeric material can reduce the level of internal stress in the material. Internal stress buildup during polymerization of a crosslinked network is a typical result of polymerization shrinkage. As used herein, internal stress is the stress that exists in a solid when no force is applied.
Reversible chain cleavage within the polymeric material after polymerization can also allow actuation of the material in response to light. In this case, either the reversible chain cleavage group or the reversible chain cleavage initiator is light activated. In an embodiment, a stress is evenly placed throughout an optically thick sample followed by irradiation of only one side of the sample so that radicals are produced and the stress is relieved preferentially on the irradiated side. A stress gradient is therefore introduced through the sample thickness (see
Photoinduced actuation has several advantages over more common thermally-induced shape memory. The lack of a need for a temperature rise to instigate a phase change leading to actuation is important in numerous thermally sensitive applications. Additionally, photopatterning may be utilized in both the formation and release of the temporary shape, thus actuation patterns may be achieved which are unobtainable via thermal methods. For example, the sample can be masked, strained in tension and irradiated on both sides in an alternating pattern. The resultant shape may be released in any chosen arbitrary pattern, given appropriately designed and patterned light exposure.
Photoinduced actuation via this addition-relaxation chain transfer process is able to avoid several of the limitations posed by the previously described photoinduced actuation methods ((Eisenbach, C. D., 1980, Polymer 21(10), 1175-1179) (Finkelmann, H. et al., 2001, Phys. Rev. Lett 87(1), 15501-15504) (Li, M.-H. et al., 2003, Adv. Mater. 15(7-8), 569-572) (Ikeda, T. et al., 2003, Adv. Mater. 15(3), 201-205(Athanassiou, A., et al. 2005, Adv. Mater. 17(8), 988-992) (Lendlein, A. et al., 2005, Nature 434, 879-882)). Every other system described in these references exhibits a photon to reaction event ratio no greater than one, where one photon either causes one photoisomerization reaction or one bond cleavage. Conversely, while one photon in the process described here leads to at most a single cleavage event of a photoinitiator molecule, the two radicals formed as a result of the photoinitiator cleavage can lead to many chain transfer events, i.e. network strand breakage and reformation. Additionally, a large range of photoinitiating systems with photoactivities ranging from the ultraviolet to the near infrared are available (Fouassier, J.-P., 1995, Photoinitiation, Photopolymerization, and Photocuring: fundamentals and applications, Hanser, Munich), thus inherent limitations imposed on the usable wavelengths for other systems are readily avoidable.
In one embodiment which allows rapid photoinduced actuation via stress relaxation, the network has the following characteristics: the network has a glass transition temperature (Tg) below room temperature (so adequate chain mobility exists at working temperatures), a sufficiently high crosslink density (and hence a sufficiently high rubbery modulus), a sufficiently high ability to be elastically strained in tension without breaking (a sufficiently high breaking strain), and should respond rapidly and extensively to relieve stress in only a portion of the network. The combination of high modulus, high breaking strain and the ability to relieve stress in only one part of the polymer material enables the generation of a large amount of internal stress in the material.
It should also be noted that the actuation produced by this system is not limited to photoactivation. Other stimuli able to produce radicals preferentially at one surface, such as chemical species able to induce redox reactions or temperature to induce decomposition of thermal initiators, are capable of producing actuation. While perhaps less controllable than irradiation exposure, these mechanisms increase the flexibility of the current system, allowing it to be applied to a host of applications.
In an embodiment, the methods for relief of stress involve making a polymeric material capable of reversible chain cleavage by the methods of the invention and then inducing reversible chain cleavage in the material.
In an embodiment, the invention provides a method for relieving stress in a crosslinked polymeric material, the method comprising the steps of:
In another embodiment, the invention provides a method for relieving stress in a crosslinked polymeric material, the method comprising the steps of:
The invention also provides similar methods for relieving stress using reversible fragmentation and recombination chain cleavage groups, except that a separate source of free radicals or cations is not required.
The stress relief provided by the methods of the invention enables the material to be “molded” and subsequently destressed, allowing for arbitrary shapes to be obtained after cure.
The methods of the invention can be used to selectively relieve stress or to introduce stress gradients in a cross-linked material. Selective actuation of the source of free radicals or cations in a portion of the material can lead to relief of stress in that portion only. For example, irradiation of one side of an optically thick material under stress can cause relief of stress in the irradiated portion only, which releases stress preferentially on the exposed side. The ability to selectively relieve stress in different portions of the material also allows shape-change or actuation phenomena. For example, irradiation of one side of a thin specimen of optically thick material can cause curvature of specimen, with the specimen warping away from the direction of irradiation. Irradiation of the other side of the specimen releases the curvature. As used herein, in an optically thick material the light intensity is significantly attenuated as the light passes through the material. In an embodiment, the attenuation is at least 10%.
The invention therefore also provides methods for photoactuation of polymeric materials capable of reversible chain cleavage. In an embodiment, a photoactuation method includes the steps of introducing an internal stress gradient into an optically thick material capable of reversible chain cleavage and then releasing at least part of the internal stress by irradiating the material. The internal stress gradient may be introduced into the material part by placing it under external tensile stress, irradiating part of the material, and then releasing the external stress.
Every formulation or combination of components described or exemplified can be used to practice the invention, unless otherwise stated. Specific names of compounds are intended to be exemplary, as it is known that one of ordinary skill in the art can name the same compounds differently. When a compound is described herein such that a particular isomer or enantiomer of the compound is not specified, for example, in a formula or in a chemical name, that description is intended to include each isomers and enantiomer of the compound described individual or in any combination. When a group of substituents is disclosed herein, it is understood that all individual members of those groups and all subgroups, including any isomers and enantiomers of the group members, and classes of compounds that can be formed using the substituents are disclosed separately. When a Markush group or other grouping is used herein, all individual members of the group and all combinations and subcombinations possible of the group are intended to be individually included in the disclosure.
One of ordinary skill in the art will appreciate that methods, starting materials, and synthetic methods, other than those specifically exemplified can be employed in the practice of the invention without resort to undue experimentation. All art-known functional equivalents, of any such methods, starting materials, and synthetic methods, are intended to be included in this invention. Whenever a range is given in the specification, for example, a temperature range, a time range, or a composition range, all intermediate ranges and subranges, as well as all individual values included in the ranges given are intended to be included in the disclosure.
As used herein, “comprising” is synonymous with “including,” “containing,” or “characterized by,” and is inclusive or open-ended and does not exclude additional, unrecited elements or method steps. As used herein, “consisting of” excludes any element, step, or ingredient not specified in the claim element. As used herein, “consisting essentially of” does not exclude materials or steps that do not materially affect the basic and novel characteristics of the claim. Any recitation herein of the term “comprising”, particularly in a description of components of a composition or in a description of elements of a device, is understood to encompass those compositions and methods consisting essentially of and consisting of the recited components or elements. The invention illustratively described herein suitably may be practiced in the absence of any element or elements, limitation or limitations which is not specifically disclosed herein.
The terms and expressions which have been employed are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the appended claims.
In general the terms and phrases used herein have their art-recognized meaning, which can be found by reference to standard texts, journal references and contexts known to those skilled in the art. Any preceding definitions are provided to clarify their specific use in the context of the invention.
All patents and publications mentioned in the specification are indicative of the levels of skill of those skilled in the art to which the invention pertains. All references cited herein are hereby incorporated by reference to the extent that there is no inconsistency with the disclosure of this specification. Some references provided herein are incorporated by reference herein to provide details concerning additional starting materials, additional methods of synthesis, additional methods of analysis and additional uses of the invention.
The base network was formed from a stoichiometric mixture of pentaerythritol tetra(3-mercaptopropionate) (PETMP) and triethyleneglycol divinylether (TEGDVE) which produces a rubbery network with a glass transition temperature of approximately −25° C. This monomer system was modified with the addition of varying concentrations of the ring opening monomer 2-methyl-7-methylene-1,5-dithiacyclooctane (MDTO) as a comonomer.
Resins were formulated with two photoinitiators, one active in the visible region of the spectrum (Irgacure 784 (a titanocene derivative from Ciba Specialty Chemicals)) at 0.1 wt % and one active in the near ultraviolet (Irgacure 819 (a phenylphosphine oxide derivative from Ciba)) at 0.25 wt %, unless otherwise stated. The visible photoinitiator photolyses rapidly and photobleaches significantly during the curing stage, thus the ultraviolet photoinitiator was included in the formulation to ensure residual photoinitiator capable of introducing radicals in each specimen upon irradiation. Each resin consisted of a stoichiometric ratio of PETMP and TEGDVE as well as varying concentrations of MDTO.
Specimens for stress relaxation experiments had approximate dimensions of 60 mm long×7 mm wide×0.9 mm thick. These specimens were mounted in a MTS Synergie 100 mechanical tester fitted with a 10 N load cell and the initial gap between the grips was set to 40 mm. For the ‘constant initial stress’ experiments, a strain rate of 0.0064 min−1 was applied until a stress of 0.15 MPa was achieved then the strain was maintained for the remainder of the experiment. The specimen was then irradiated (320-500 nm, 20 mW·cm−2) for 15 minutes, starting 60 seconds after the stress of 0.15 MPa was achieved.
Results presented in
The ratio of cross-links to allyl sulfide groups was as follows:
0 wt % MDTO 1:0, 25 wt % MDTO 1.17:1, 50 wt % MDTO 0.390:1, 75 wt % MDTO 0.130:1.
Stress gradients through specimens were introduced by irradiating rectangular, optically thick specimens on one side only that were under tension. These specimens were almost equivalent to those used in the stress relaxation experiments; however, they contained 0.1 wt % Irgacure 784 and 2.5 wt % Irgacure 819 before polymerization to yield a significant optical gradient through the specimen thickness. They were irradiated at 365 nm, 20 mW·cm−2 for 15 seconds while under a strain of 0.0375.
Synthesis of a Dimethacrylate Containing an Addition-Fragmentation Functionality (2-methylene-propane-1,3-di(thioethyl methacrylate) (MDTMA)) Synthesis of 2-[2-(2-hydroxy-ethylsulfanylmethyl)-allylsulfanyl]-ethanol: 3-Mercapto-2-(mercaptomethyl)-1-propene was synthesized according to the literature method (Evans, R. A. and Rizzardo, E. 2000, Macromolecules, 33(18), 6722-6731. Sodium (8.05 g, 0.35 mol) was dissolved in dry methanol under nitrogen and refluxed. Solutions of 3-mercapto-2-(mercaptomethyl)-1-propene (18.35 g, 0.15 mol) in 30 ml methanol and 2-chloroethanol (27.20 g, 0.34 mol) in 30 ml methanol were added simultaneously to the methanolic sodium solution and allowed to reflux for three hours. The methanol was then evaporated off, water was added and the solution was extracted with ethyl acteate. The ethyl acetate extract was washed with water, dried over calcium chloride, filtered and evaporated to yield 26.21 g (66% yield). Under nitrogen, 2-[2-(2-hydroxy-ethylsulfanylmethyl)-allylsulfanyl]-ethanol (12.98 g, mol) and triethylamine (16.38 g, mol) were dissolved in dichloromethane in an ice bath and methacryloyl chloride (16.94 g, mol) was added dropwise. The solution was allowed to stir overnight while the bath warmed to room temperature.
Synthesis of an Acrylate Containing an Addition-Fragmentation Functionality (2-methylene-propane-1,3-di(thioethyl acrylate) (MDTA))_Under nitrogen, 2-[2-(2-hydroxy-ethylsulfanylmethyl)-allylsulfanyl]-ethanol (12.60 g, mol) and triethylamine (15.92 g, mol) were dissolved in dichloromethane in an ice bath and acryloyl chloride (14.24 g, mol) was added dropwise. The solution was allowed to stir overnight while the bath warmed to room temperature.
Synthesis of 2-methylene-propane-1,3-di(thioethyl vinyl ether) (MDTVE) 2-Methylene-propane-1,3-di(thioethylvinylether) (MDTVE) was synthesized from 3-mercapto-2-(mercaptomethyl)-1-propene and 2-chloroethyl vinyl ether in a manner analogous to that described in the literature Evans, R. A. and Rizzardo, E. 2001, J. Polym. Sci A, Polym. Chem., 39(1), 202-215). The crude oil was purified by bulb-to-bulb distillation.
Polymerizations involving divinyl ether monomers containing the addition-fragmentation functionality can be partially decoupled from stress relaxation by cationically photopolymerizing the divinyl ether containing the addition-fragmentation functionality while varying either the concentration of a radical photoinitiator or using a radical photoinitiator absorbing at a different wavelength.
Conversion versus time was measured for a dimethacrylate containing an addition-fragmentation chain transfer functionality (MDTMA) formulated with 0.25 wt % Irgacure 819 and irradiated at 400-500 nm, 5 mW·cm−2 at room temperature was found to be approximately 70% at 16 minutes. The corresponding conversion for tetraethylene glycol dimethacrylate (TETGDMA) was approximately 80% at 16 minutes. The irradiation was started at t=1 minute.
The polymer studied was formed from 75 wt % of a stoichiometric mixture of pentaerythritol tetra(3-mercaptopropionate) (PETMP) and 2-methylene-propane-1,3-di(thioethyl vinyl ether) (MDTVE) and 25 wt % of 2-methyl-7-methylene-1,5-dithiacyclooctane (MDTO) which produces a rubbery crosslinked network with a Tg of −22° C. and a tensile modulus at room temperature of 9.5 MPa. The monomers used to produce the Tetrathiol/Divinyl Ether/MDTO materials are shown in Scheme 2. Monomers used were ((A) PETMP; (B) MDTVE; (C) MDTO) and (D) addition-fragmentation mechanism through the polymer backbone of the resultant polymer.
Resins were formulated with two photoinitiators, Irgacure 819 (a phenylphosphine oxide derivative active in the blue and near ultraviolet from Ciba Specialty Chemicals) at 1.0 wt % and Irgacure 651 (a dialkoxy acetophenone derivative active in the near ultraviolet from Ciba) at 2.0 wt %. The specimens were fully cured under irradiation for ten minutes at 400-500 nm at room temperature. The visible photoinitiator photolyses rapidly and photobleaches significantly during the curing stage, thus the ultraviolet photoinitiator was included in the formulation to ensure residual photoinitiator capable of introducing radicals in each specimen upon irradiation.
A light intensity gradient through the sample was produced by formulating the resin with an ultraviolet absorber (0.5 wt % Tinuvin 328 a hydroxyphenylbenzotriazole derivative ultraviolet absorber from Ciba). A control network not containing the ultraviolet absorber was also produced. Addition of a strongly UV absorbing compound to the standard formulation enabled the transmittance through the 0.15 mm thick fully cured samples to be readily decreased (from 57% transmittance at 365 nm for a sample without Tinuvin 328 to 0.038% transmittance at 365 nm for a sample with 0.5 wt % Tinuvin 328) without changing other material properties.
The rate of stress relaxation due to chain transfer through the allyl sulfide functionalities increases at elevated functional group concentrations(Scott, T. et al., 2005, Science 308, 1615). A network produced from a stoichiometric PETMP/MDTVE mixture possesses one allyl sulfide group per crosslink. The addition of 25 wt % MDTO to the PETMP/MDTVE mixture produces a network with approximately two allyl sulfide groups per crosslink. Although an elastomer produced only from a stoichiometric mixture of PETMP and MDTVE is able to produce the desired stress relaxation, the addition of MDTO greatly enhanced the rate and extent of stress relaxation to emphasize the observed phenomenon.
The tetrathiol/divinyl ether/MDTO materials used were those described in Example 5.
The decrease in the overall stress relaxation rate in the sample containing 0.5 wt % Tinuvin 328 resulted from a reduction in the average light intensity. Though the average stress relaxation rate is lower, the relaxation rate at the incident side remains just as rapid. Uniquely, because the rate of stress relaxation is directly proportional to the light intensity, the stress relaxation rate at the unirradiated side is reduced by 1500 times for a sample containing 0.5 wt % Tinuvin 328 when compared with a sample without any UV absorber.
During the irradiation of the previously unirradiated side, the stress release results in the polymer bending away from the light and decreasing the angle of curvature (θ in
Methods: A trithiocarbonate dimethacrylate (TTCDMA) monomer, capable of undergoing radical-mediated RAFT, was mixed with 70 wt % BisGMA (bisphenylglycidyl dimethacrylate) and compared to a conventional dental resin comprised of TEGDMA (triethylene glycol dimethacrylate) and 70 wt % BisGMA. The shrinkage stress and methacrylate conversion were simultaneously measured during polymerization. The fracture toughness and elastic modulus were measured to evaluate the effect of the TTCDMA monomer on the mechanical properties. All the materials used herein were evaluated as a composite, including 75 wt % silica fillers. ANOVA (CI 95%) was conducted to assess the differences between the means.
Summary of Results: The TTCDMA composite exhibited a 65% stress reduction compared with TEGDMA-BisGMA though the reaction rate was slower than the conventional dental composite, owing to the additional RAFT reaction. The fracture toughness and elastic modulus of the TTCDMA-based composite were not significantly different than in the TEGDMA-based composite, while the Tg was decreased by 30° C. to 155±2° C.
Significance: Despite only replacing the reactive-diluent, significant and dramatic stress reduction was observed while maintaining the elastic modulus and fracture toughness. This new RAFT-capable monomer shows great promise to replace the reactive diluent in BisGMA-based dental materials.
Introduction: Polymer-based composites have been vastly improved over the past few decades; however, volume shrinkage and the associated stress that evolve during curing remain a critical drawback, as they leads to microcracking, microleakage, and secondary caries (Burke F J T, et al. Quintessence International, 1999; 30:234-242). During the polymerization of dimethacrylate-based resins, which represent the primary polymerizable component of dental composites, a large stress arises due to the nature of the monomer-polymer densification process. Once the resin undergoes a transition from a liquid-like to a solid-like material (i.e., sol-to-gel transition), the shrinkage stress is no long capable of being dissipated and begins to build throughout the remainder of the polymerization. Methacrylate-based polymerizations are particularly susceptible to stress development owing to both the low gel-point conversion (Kleverlaan C J and Feilzer A J., Dent Mater, 2005; 21:1150-1157) as well as the large amount of volume shrinkage per double bond that occurs (Dewaele M, et al., Dent Mater, 2006; 22:359-365).
There have been several approaches to reduce stress (Bowman CNet al. J Dent Res, 2011; 90:402-416) that utilize different polymerizable functional groups and/or different polymerization mechanisms to reduce the volume shrinkage and/or delay the gel point, including thiol-ene (Carioscia J A et al., Dent Mater, 2005; 21:1137-1143; Lu H, et al. Dent Mater, 2005; 21:1129-1136) and thiol-yne reactions (Fairbanks B D, et al. Macromolecules, 2009; 42:211-217; Chan J W, et al. Macromolecules, 2010; 43:4937-4942), polymerization-induced phase separation (Lee T Y, et al., J Polym Sci Pol Chem, 2009; 47:2509-2517) and ring-opening polymerizations. (Ge J H et al. Macromolecules, 2006; 39:8968-8976; Stansbury J W. et al. Polymers of Biological and Biomedical Significance, 1994; 540:171-183). The incorporation of a reversible covalent bond, which undergoes addition-fragmentation chain transfer (AFCT—e.g., see
The trithiocarbonate functional group is frequently used as a reversible addition-fragmentation chain transfer (RAFT) agent to synthesize polymers having low polydispersity (Mayadunne RTA et al., Macromolecules, 2000; 33:243-245) Unlike the allyl sulfide functional group, the trithiocarbonate functional group is capable of fully reversible AFCT when reacting with a carbon-centered radical, such as those present in a methacrylate polymerization (
Materials: The monomers and photoinitiator used in this study are shown in
Methods Composite samples (2 mm thickness) were irradiated at 70 mW/cm2 intensity with 400-500 nm light (Acticure 4000) for 20 minutes to observe the conversion of the methacrylate functional group during polymerization. The methacrylate conversion was determined by monitoring the infrared absorption peak centered at 6166 cm−1 (C═C—H stretching, overtone) using Fourier transform infrared (FTIR) spectroscopy (Nicolet 750). Specimens for fracture toughness test were prepared by photocuring composites at the same irradiation condition with the IR experiments in a cuboid mold (25 mm length*2.5 mm width*5.5 mm thickness) having a 2 mm razor blade which is positioned vertically across the mold to form the initial crack in the test specimen. After the specimens are separated from the mold, the specimen surface was ground with sandpaper to create uniform dimension and remove defects. Fracture toughness was measured by using a Mechanical Test System (MTS, The 858 Mini Bionix II Test System) using a 3-point bending test procedure with 20 mm span and 1 mm/minute rate. The elastic moduli (E′) and glass transition temperature (Tg) of the polymerized samples were determined by dynamic mechanical analysis (DMA) (TA Instruments Q800). DMA experiments were performed at a strain and frequency of 0.1% and 1 Hz, respectively, and scanning the temperature twice at ramp rate of 2° C./minute. The Tg was assigned as the temperature at the tan delta peak maximum (Ferrillo R G and Achorn P J, Journal of Thermal Analysis and calorimetry, 2000; 60:377-390) of the second heating scan. This methodology does not measure the Tg of the as cured sample due to changes in conversion that occur during the first thermal scan. Rather, the measurement is indicative of the maximum Tg achieved under these conditions. (Scott T F et al., Macromolecules, 2003; 36:6066-6074; Zhu S et al, Macromolecules, 1990; 23:1144-1150) Specimens used for DMA experiments were prepared by sandwiching the uncured composite in a rectangular mold (2 mm gap) and irradiating under the same conditions used for the FTIR experiments. The shrinkage stress was monitored using tensometry (Paffenbarger Research Center, American Dental Association Health Foundation) (Lu, 2005; Lu H et al, Journal of Materials Science-Materials in Medicine, 2004; 15:1097-1103), which was equipped with optical fibers which enable simultaneous monitoring of the reaction progression via FTIR spectroscopy. Uncured composite was injected between two glass rods which are positioned in a 9 cm beam length of the stainless steel beam. Samples were covered with a plastic sheath to prevent oxygen inhibition of the methacrylate during polymerization. ANOVA (CI 95%) was conducted to determine differences between the means for all the reported results.
Results: Fracture toughness and DMA measurements of the BisGMA-TEGDMA and BisGMA-TTCDMA composites are presented in
The reaction kinetics for the BisGMA-TEGDMA and BisGMA-TTCDMA composites were monitored for 20 minutes during irradiation (
Discussion: The TTCDMA monomer was designed to have a similar molecular structure with TEGDMA, targeting its use as a reactive diluent to replace TEGDMA while simultaneously adding RAFT capability to promote stress relaxation. Since the RAFT reaction is favorable when the leaving radical group is stable, the TTCDMA core, which replaces ethylene glycol, was designed to have a dimethyl substituted carbon adjacent to the trithiocarbonate; therefore, the carbon-sulfur fragmentation product (
As shown in
Conclusion: BisGMA-TEGDMA and trithiocarbonate-containing BisGMA-TTCDMA-based composites were investigated to demonstrate stress relaxation via RAFT. The trithiocarbonate functional group was implemented to successfully induce RAFT which led to network rearrangement. Ultimately, the inclusion of this mechanism resulted in a 65% stress reduction as compared to the standard BisGMA-TEGDMA composite. Fracture toughness of the TTCDMA-based composite was slightly higher though not significantly different from the TEGDMA-based composite even though the TTCDMA-based composite has dramatically reduced stress. In summary, the RAFT mechanism for stress relaxation via the inclusion of trithiocarbonates and similar RAFT moieties has potential for replacing conventional dimethacrylate materials with nearly identical mechanical properties but stress levels that are a fraction of current composites.
This application is a continuation in part application of U.S. application Ser. No. 13/109,400, filed May 17, 2011, which is a continuation application of U.S. patent application Ser. No. 11/815,914, now U.S. Pat. No. 7,943,680, which is the U.S. National Stage of International Application PCT/US06/04756, filed Feb. 10, 2006, which in turn claims the benefit of U.S. Provisional Application No. 60/651,737, filed Feb. 10, 2005 and U.S. Provisional Application No. 60/763,564, filed Jan. 31, 2006, all of which are incorporated by reference in their entirety to the extent not inconsistent with the disclosure herein.
This invention was made with government support under grant number DE010959 awarded by the National Institutes of Health. The government has certain rights in the invention.
| Number | Date | Country | |
|---|---|---|---|
| 60651737 | Feb 2005 | US | |
| 60763564 | Jan 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11815914 | Apr 2008 | US |
| Child | 13109400 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13109400 | May 2011 | US |
| Child | 13344328 | US |