Sublimating process for cleaning and protecting lithography masks

Abstract

Spraying a surface of a reticle with carbon dioxide snow cleans the surface and removes particles. Further spraying the surface of the reticle with carbon dioxide snow at a temperature below a carbon dioxide sublimation temperature forms a solid carbon dioxide layer on the surface. The solid carbon dioxide layer prevents particles from contacting the surface of the reticle. The solid carbon dioxide layer may be removed, and the reticle may be used in a extreme ultraviolet lithography tool.

Description

BACKGROUND

A microchip manufacturing process may deposit various material layers on a wafer and form a photosensitive film or photoresist on one or more deposited layers. A lithography tool may transmit light through transmissive optics or reflect light from reflective optics to a reticle or patterned mask. Light from the reticle transfers a patterned image onto the photoresist. Portions of the photoresist which are exposed to light may be removed. Portions of the wafer which are not protected by the remaining photoresist may be etched to form transistor features.

The semiconductor industry may continue to reduce the size of transistor features to increase transistor density and improve transistor performance. This reduction in transistor feature size has driven a reduction in the wavelength of light used in lithography tools to define smaller transistor features on a photoresist.

DESCRIPTION OF DRAWINGS

FIG. 1 illustrates an example of a lithography tool.

FIGS. 2A-2G illustrate a technique for using carbon dioxide (CO₂) snow to clean and protect a reticle, which may be used with the lithography tool of FIG. 1.

DETAILED DESCRIPTION

Extreme Ultraviolet lithography (EUVL) may use a radiation wavelength of approximately 11-15 nanometers (nm). An EUV lithography tool may print a pattern on a photoresist with dimensions which are smaller than dimensions achieved by other lithography tools. An EUV lithography tool may also be called a “lithographic exposure system,” an “EUV scanner” or an “EUV stepper.”

FIG. 1 illustrates an example of a lithography tool 100, such as an Extreme Ultraviolet lithography (EUVL) tool. The lithography tool 100 may include a laser 102, an electric discharge or laser produced plasma source 104, condenser optics 106, a reflective reticle 107 with a pattern, and reflective reduction optics 108. The laser 102 may produce radiation which reflects off the reticle 107 (also called a mask) to form a patterned image on an object 110. The object 110 may be a silicon wafer with a photoresist layer.

It may be difficult to keep a surface of the reticle 107 clean as the reticle 107 is made and transported to a site of the lithography tool 100. Handling an unprotected reticle 107 may produce particle contamination and defects on the reticle surface. As the reticle 107 is installed in the lithography tool 100, it may be difficult to protect the reticle 107 from particle contamination. A particle falling on the reticle 107 may reduce the yield for an object 110 processed by the lithography tool 100. A reticle used in an extreme ultraviolet lithography (EUVL) tool may be especially sensitive to particle contamination because EUV lithography uses very small wavelengths (11-15 nanometers). Some reticle cleaning methods, such as a liquid cleaning process, may not be suitable for use inside the lithography tool 100.

A pellicle may be designed to protect the reticle 107 from particles. But pellicle materials and adhesives may absorb extreme ultraviolet radiation and degrade after repeated exposure. The use of a removable pellicle or cover may add undesirable particle defects to the reticle 107.

The present application relates to using carbon dioxide (CO₂) to clean and protect a reticle. A removable CO₂ protective layer may be created on the reticle.

FIGS. 2A-2G illustrate a technique for using carbon dioxide (CO₂) snow (described herein) to clean and protect the reticle 107 of FIG. 1, such as an EUVL reticle. FIG. 2A illustrates particles 202 on a surface 200 of the reticle 107 before the reticle 107 is installed in the lithography tool 100 (FIG. 1). Particles 202 may fall on the reticle 107 during fabrication (e.g., at a “mask shop”) and during handling of the reticle 107.

FIG. 2B illustrates a nozzle 204 spraying “CO₂ snow” 206 onto the surface 200 of the reticle 107 at a grazing angle (i.e., less than 90 degrees) to clean the reticle 107. A CO₂ snow cleaning device may be obtained from Applied Surface Technologies of New Providence, N.J.

“CO₂ snow” may be used to clean micron and sub-micron particles from sensitive optics. CO₂ snow cleaning may remove carbon and hydrocarbon-based contamination. There may be more than one technique of CO₂ snow cleaning. CO₂ snow cleaning may include expansion of either liquid or gaseous CO₂ through an orifice inside a nozzle. This expansion may lead to nucleation of small dry ice particles and a high velocity gas carrier stream. Upon impact with a dirty surface, the dry ice media may remove micron and submicron particles and hydrocarbons by momentum transfer via a transient solvent or a freeze fracture mechanism. The CO₂ high-velocity gas may blow the contaminants away.

The CO₂ snow 206 in FIG. 2B may clean the reticle surface 200 (i.e., remove particles 202) before the reticle 107 is placed in the lithography tool 100. CO₂ snow cleaning of the reticle 107 may be better than liquid cleaning because CO₂ snow cleaning may not leave a residue (e.g., chemicals) on the surface 200. CO₂ snow cleaning of the reticle 107 may avoid scratching or eroding the surface 200. FIG. 2C illustrates a cleaned reticle 107.

FIG. 2D illustrates a cleaned reticle 107 placed on a stage or mount 208 and subjected to a cooling cycle. The cooling cycle may use a temperature which is sufficiently low to prevent CO₂ in FIG. 2E from sublimating into a gas.

CO₂ may sublimate, i.e., change from a solid phase directly to a gas phase without a liquid phase, at a specific temperature. The sublimation temperature of CO₂ may be about −109.3 degrees Fahrenheit or −78.5 degrees Celsius. For example, a block of “dry ice” may sublimate from a solid to a gas.

FIG. 2E illustrates a nozzle 210 spraying CO₂ snow 212 onto the surface 200 of the cooled reticle 107 at a substantially normal (90-degree) angle to form a solid CO₂ protective layer 214. The temperature around the reticle 107 may be held sufficiently low (e.g., −109.3 degrees F. or −78.5 degrees Celsius) to maintain the solid CO₂ protective layer 214 and prevent CO₂ from sublimating into a gas. The CO₂ protective layer 214 may protect the reticle 107 from particle contamination as the reticle 107 is transported.

FIG. 2F illustrates a thermoelectrically-cooled carrier 216 adapted to allow the reticle 107 and its CO₂ protective layer 214 to be transported to a site of the lithography tool 100. The carrier 216 may maintain a temperature around the reticle 107 to prevent the CO₂ protective layer 214 from sublimating into a gas. After the carrier 216 and reticle 107 are transported to a site with the lithography tool 100, the carrier 216 may be removed.

FIG. 2G illustrates the reticle 107 with the CO₂ protective layer 214 on a stage 218 in the lithography tool 100. Before being used by the lithography tool 100, the reticle 107 may be warmed to a selected temperature (e.g., room temperature or a temperature above −109.3 degrees F. or −78.5 degrees Celsius) to sublimate the CO₂ protective layer 214. CO₂ may not leave a residue on the reticle 107 and may not damage the reticle 107.

A nozzle 220 may spray CO₂ or some other gas 222 at a grazing angle to clean the surface 200 of the reticle 107.

FIG. 2G illustrates the reticle 107 on the stage 218 in the lithography tool 100. The reticle 107 is cleaned and ready to be used for lithography.

In an embodiment, the techniques described above may form a CO₂ protective layer on a reticle, and then a pellicle may be placed over the reticle. The pellicle may be removable. The CO₂ protective layer may be removed inside the lithography tool 100 with or without removing the pellicle.

A number of embodiments have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the application. Accordingly, other embodiments are within the scope of the following claims.

Claims

1. A method comprising: applying carbon dioxide to a surface of a reticle; and forming a solid carbon dioxide layer on the surface of the reticle at a temperature below a sublimation temperature of carbon dioxide, the solid carbon dioxide layer preventing particles from contacting the surface of the reticle.

2. The method of claim 1, wherein said applying comprises spraying the surface of the reticle with carbon dioxide and removing particles from the surface with carbon dioxide snow.

3. The method of claim 1, wherein said applying comprises spraying carbon dioxide snow at a grazing angle with respect to the surface of the reticle.

4. The method of claim 1, further comprising cooling the reticle to a temperature below a sublimation temperature of carbon dioxide before said forming a solid carbon dioxide layer on the surface of the reticle.

5. The method of claim 1, wherein said forming a solid carbon dioxide layer on the surface of the reticle comprises spraying carbon dioxide snow at a substantially 90 degree angle with respect to the surface of the reticle.

6. The method of claim 1, further comprising: enclosing the reticle with the solid carbon dioxide layer in a carrier; and maintaining a temperature around the reticle below a sublimation temperature of carbon dioxide.

7. The method of claim 1, further comprising removing the carrier and inserting the reticle with the solid carbon dioxide layer in a lithography tool.

8. The method of claim 1, further comprising raising a temperature around the reticle above a carbon dioxide sublimation temperature.

9. The method of claim 1, further comprising removing the solid carbon dioxide layer from the surface of the reticle.

10. The method of claim 1, further comprising spraying the surface of the reticle with carbon dioxide inside a lithography tool.

11. The method of claim 1, further comprising reflecting radiation off the surface of the reticle in a lithography tool.

12. The method of claim 1, further comprising reflecting extreme ultraviolet radiation off the surface of the reticle in a lithography tool.

13. An apparatus comprising: a reticle with a layer of carbon dioxide formed on a surface of the reticle, the carbon dioxide layer preventing particles from contacting the surface of the reticle.

14. The apparatus of claim 13, further comprising a carrier enclosing the reticle, the carrier being adapted to maintain a temperature around the reticle below a sublimation temperature of carbon dioxide.

15. A system comprising: a device adapted to apply carbon dioxide onto a surface of a reticle; and optics adapted to direct radiation from a source to the surface of the reticle to an object.

16. The system of claim 15, wherein the device is adapted to spray carbon dioxide onto the surface of the reticle at an angle less than 90 degrees with respect to the surface of the reticle.

17. The system of claim 15, wherein the device is adapted to spray carbon dioxide snow onto the surface of the reticle at a temperature above a carbon dioxide sublimation temperature.