Patent Application
20190035519
The present invention relates to a superconducting wire having good critical current characteristics.
MgB2, as a metal-based superconductor, which has the highest critical temperature of about 40 K, is expected to be applied as a superconducting wire or a superconducting magnet.
A general preparation method of a superconducting wire is a powder-in-tube (PIT method). In this method, a metal tube is filled with base powder, a diameter reduction is performed by a method of drawing, and thereby it is possible to prepare a single-core wire (wire having one superconducting filament). In addition, when a metal tube is filled with single-core wires and is subjected to the diameter reduction again, a multi-core wire (wire having a plurality of superconducting filaments) is obtained. A method of using MgB2 as the base powder is referred to as an ex situ method. A method of using a mixture of magnesium powder and boron as the base powder is referred to as an in situ method.
When a superconducting wire is used, it is desirable that the superconducting wire has a high critical current density. The critical current density means upper limit current density at which it is possible to perform energization with zero resistance. The critical current density of a superconductor is determined by flux pinning. Lines of magnetic flux are quantized and infiltrate into a (type-II) superconductor, and the Lorentz force acts on the lines of magnetic flux during energization. When the lines of magnetic flux make movement due to the Lorentz force, a loss occurs. Therefore, in order to obtain the high critical current density of the superconductor, it is necessary to introduce defects or inhomogeneities to the superconductor such that the lines of magnetic flux has pinning.
In MgB2, the flux pinning is likely to mainly occur on a crystal grain boundary. In order to increase the flux pinning of the crystal grain boundary, it is effective to reduce crystallinity and to decrease a grain size. MgB2 has high crystallinity at a temperature range of 800° C. or above and is likely to achieve grain growth. However, in terms of flux pinning, synthesis at a low temperature of 700° C. or below is effective to achieve high critical current density of MgB2 (for example, see NPT 1).
On the other hand, a problem arises in that it is difficult to obtain microstructure of MgB2 which is dense to have good continuousness in the PIT method. In the ex situ method, after the diameter reduction, a heat treatment is performed in order to sinter MgB2 powder. At this time, in order to sufficiently bond the powder, it is effective to perform the heat treatment at a high temperature from 800° C. to 900° C. However, as described above, it is not preferable to perform the heat treatment at the high temperature in terms of the flux pinning. In the in situ method, after the diameter reduction, a heat treatment for synthesizing MgB2 from magnesium and boron. At this time, even at a heat treatment at a low temperature of 700° C. or below, MgB2 having good powder bonding is produced. However, since a reaction of producing MgB2 from magnesium and boron is a volume contraction reaction, many voids are formed, and a problem is pointed out in that a final filling rate of MgB2 is low. Since magnesium is dispersed in a region of boron powder such that MgB2 is produced, in the in situ method, a space, in which magnesium powder is originally present, becomes a void, and characteristic microstructure, in which a large number of tens of micrometers of voids are dispersed, is obtained (For example, see NPL 2).
As described above, the characteristics and problems of the most general in situ method and ex situ method in the PIT method are described; however, various attempts to obtain high critical current density, in addition to the methods described above, have been made. As an example, high-energy mixing of magnesium powder and boron powder is performed by using a planetary ball mill apparatus, and thereby an attempt to increase the reactivity of the powders has been made. Hereinafter, this method will be referred to as a mechanical milling method. In the mechanical milling method, there have been reports that a part of MgB2 is produced by mixing energy even when the heat treatment is not performed, MgB2 synthesized in this manner has a high reactivity, and the high critical current density is obtained (for example, see NPLs 3, 4, 5, and 6 and PTL 1).
PTL 1: Japanese Patent No. 4259806
NPL 1: Supercond. Sci. Technol. 21 (2008) 015008
NPL 2: Jpn. J. Appl. Phys. 51 (2012) 010105
NPL 3: Supercond. Sci. Technol. 22 (2009) 125017
NPL 4: Appl. Phys. Lett. 91 (2007) 082507
NPL 5: Supercond. Sci. Technol. 23 (2010) 065001
NPL 6: Supercond. Sci. Technol. 26 (2013) 025005
As described above, the reports that the high critical current density is obtained in the mechanical milling method have been made; however, a shape of tape-shaped wire is used in most of the reports. Although there have been some reports of using a round wire, the critical current density is not at all high. In addition, there has been a report that, with a tape wire obtained by the mechanical milling method, a value of the critical current density significantly changes depending on an angle formed between a tape surface and an external magnetic field (for example, see NPL 5).
In an application to a magnetic resonance imaging (MRI) apparatus in which high magnetic field homogeneity is demanded, it is preferable to use a shape of which a round or angular cross section is highly symmetrical. A tape wire having a high aspect ratio is difficult to secure dimensional accuracy of winding wire. Additionally, it is not highly preferable that a wire having critical current density that is anisotropic to a magnetic field direction impose restriction to coil design. Here, an aspect ratio (width/thickness) of a typical MgB2 tape wire is about 10. In addition, anisotropy of the critical current density of the MgB2 tape wire depends on a temperature and a magnetic field; however, some MgB2 tape wires have the anisotropy of about 10 to 100.
According to the present invention, an object thereof is to provide a wire which has a round or angular shape with good symmetry, in which anisotropy of critical current density is not generated, and which exhibits potential of high critical current density obtained by a mechanical milling.
A superconducting wire according to the present invention includes: a MgB2 filament. Number density of voids each having a major axis of 10 μm or larger is 5 to 500 mm−2 on a longitudinal section of the superconducting wire. An average value of angles (defined from 0 to 90 degrees) formed between the major axis of each of the voids and an axis of the superconducting wire is 60 degrees or larger.
The MgB2 wire of the present invention has a round or angular cross-sectional shape which is used without imposing restriction to design of a superconducting device and exhibits potential of the high critical current density by the mechanical milling method.
In order to achieve the object described above, the present invention prepares MgB2 wire by the following procedure. High-energy mixing of magnesium powder and boron powder is performed by using a planetary ball mill apparatus. At this time, it is preferable that mixing energy is set to the extent that the boron powder is dispersed in the magnesium powder, and production of MgB2 is not caused (to the extent that a production peak of MgB2 is not generated in at least powder X-ray diffraction). A metal tube is filled with mixed powder and is reduced in diameter. At this time, at least some of processing steps, like cassette rolling or groove rolling, employ a processing method, in which a portion of a processing jig which comes into direct contact with the wire is not fixed but rotates. Otherwise, in a case of using a technique like drawing in which a portion of a jig that comes into direct contact with the wire is immovable, a processing material is processed while being heated at a degree of temperature at which MgB2 does not substantially produced.
A precursor prepared in such a method (a state before heat treatment is performed before MgB2 is produced) has the following characteristics. Particles of boron are dispersed in a matrix of magnesium in a portion of the precursor of a MgB2 filament in a longitudinal section of the precursor of the MgB2 wire, and number density of voids each having a major axis of 10 μm or larger is in a range of 5 to 500 mm−2. The void is likely to be oriented to a direction perpendicular to an axial direction of the wire.
In addition, the MgB2 wire has a round or angular cross-sectional shape which is used without imposing restriction to design of the superconducting device and exhibits potential of the high critical current density by the mechanical milling method. An aspect ratio of the MgB2 wire of the embodiment is 3 or lower. An aspect ratio (width/thickness) of a typical MgB2 tape wire is about 10.
In addition, anisotropy of the critical current density is 2 or lower at every temperature·magnetic field region. Here, when θ represents an angle formed between an axis of the MgB2 wire and an external magnetic field, and Jc(θ) represents dependence of Jc on θ, the anisotropy of the critical current density is defined as a ratio of the maximum value and the minimum value of Jc(θ).
In addition, the MgB2 wire prepared in this method has the following characteristics. The number density of voids each having the major axis of 10 μm or larger in the portion of the MgB2 filament is, specifically, in a range of 5 to 500 mm−2 in the longitudinal section of the MgB2 wire. The void is likely to be oriented to a direction perpendicular to the axial direction of the wire.
In a case of preparing a multi-core wire, after single-core wires are prepared, a plurality of the single-core wires are embedded in a metal tube, and a diameter reduction is performed. At some of processing steps after the wires are put in, like cassette rolling or groove rolling, employ a processing method, in which a portion of a processing jig which comes into direct contact with the wire is not fixed but rotates. Otherwise, in a case of using a technique like drawing in which a portion of a jig that comes into direct contact with the wire is immovable, a processing material is processed while being heated at a degree of temperature at which MgB2 does not substantially produced. At this time, a sectional configuration, in which iron is disposed around a MgB2 filament, and a material having hardness higher than pure copper is disposed on the outermost circumference, may be employed.
Magnesium powder having a grain size of smaller than 200 mesh and purity of 99.8% and boron powder having a grain size of smaller than 250 nm and purity of 98.5% were used as base powders.
The magnesium powder and the boron powder are weighed to have Stoichiometric composition (a mole ratio of 2:1), and two types of mixed powders I and M are prepared. The mixed powder I is obtained by containing base powder together with a stainless steel ball having a diameter of 10 mm in a plastic container and mixing by a ball mill device. The mixed powder M is obtained by containing 7 g of base powder together with 30 zirconia balls each having a diameter of 10 mm in a zirconia container having a volume of 80 ml and mixing in conditions of 400 rpm for six hours by a planetary ball mill device .
Heat treatment was performed in conditions of a temperature of 600° C. for three hours in an argon atmosphere, in order to produce MgB2. The wires prepared from both of mixed powders I and M are called Wire-I and Wire-M, respectively.
The mixed powder M was prepared in the same method as that in Comparative Example 1. An iron tube having an outer diameter of 18 mm and an inner diameter of 13.5 mm was filled with the mixed powder M, the iron tube was reduced to have a diameter of 0.8 mm by drawing. Subsequently, the iron tube was reduced to have a diameter of 0.5 mm by cassette rolling.
Heat treatment was performed in conditions of a temperature of 600° C. for three hours in an argon atmosphere, in order to produce MgB2. The prepared wire is called Wire-MR.
The critical current density of the three MgB2 wires prepared in Comparative Example 1 and Example 1 was evaluated. While the temperature of the wires was controlled by spraying of helium gas and heating by a heater, an external magnetic field was applied in a perpendicular direction to an axis of the wire, and current-voltage characteristics were achieved by a DC four-terminal method. A critical current is defined as a current value obtained when a voltage of 1 μV/cm is generated, and the critical current density is defined as a value obtained by dividing the critical current by a cross-sectional area of a MgB2 filament on a cross section of the wire.
Microstructure of the three MgB2 wires prepared in Comparative Example 1 and Example 1 was observed. The wire was dried and polished after resin filling, and then a smooth wire-longitudinal-section sample was prepared by cross-section polisher processing (CP processing). The sample was observed with a scanning electron microscope.
Hereinafter, only voids each having the major axis of 10 μm or larger are targets, and number density n of the voids and an average value θM of angles θ (0°≤θ≤0°) formed between the axis of the wire and the major axis of each of the voids are considered. Here, the voids each having the major axis of 10 μm or larger within a visual field by SEM observation are numbered (i=1, 2, 3, . . . , and N). When an angle formed between a major axis of an i-th void and the axis of the wire is θi, θM is defined by Expression (1).
θM=σθi/N (1)
Results of obtaining n and θM of the three wires are shown in Table 1. The values are results of obtaining lengths of the major axes of the voids MgB2 and angles between the axis of the wire and the major axis of each of the voids and averaging the lengths and angles in a plurality of square regions having a length of 300 μm per side of the MgB2 filament. Wire-I and Wire-M had a high number density of the voids, and Wire-MR had a low number density of the voids. Hence, the high critical current density of Wire-MR is considered to be obtained due to the dense MgB2 filament and an increase in the ratio of a sectional area which can be an effective current path. Wire-I and Wire-M have the same degree of the number density of voids; however, Wire-I has the higher critical current density. This difference is due to a difference of θM. In other words, since Wire-M has large θM, and thus the voids are oriented to a direction orthogonal to the axis of the wire, in which the voids are more likely to block the current path, a ratio of the sectional area which becomes the effective current path is decreased, and thus the critical current density is considered to be decreased.
Microstructure on longitudinal sections of the three wires before the heat treatment (that is, precursors of the MgB2 wires) prepared in Comparative Example 1 and Example 2 was observed.
An observation result of the microstructure suggests that following phenomenon occurs in a process of preparing the wire. A mixing method of base powders influences the distribution of magnesium and boron. In the ball mill mixing of Wire-I, the base particles are mixed as the particles maintain their original shapes. In the drawing, the magnesium particles are subjected to plastic deformation and are elongated in the axial direction of the wire. On the other hand, since the boron particles are hard, the filling rate thereof is increased while the boron particles are repeatedly redisposed without being deformed; however, gaps between boron particles remain until the end. When the heat treatment for synthesizing MgB2 is performed, magnesium is diffused into the regions filled with the boron particles, and MgB2 is produced. However, such a reaction is a volume contraction reaction, and thus the regions, where magnesium is present, remains as voids. When high-energy mixing is performed by using planetary ball milling like Wire-M, the boron particles are kneaded with the magnesium particles in the process of mixing, and powder having a structure in which magnesium as a matrix contains boron is obtained. Powder filled portions are elongated by the drawing; however, plastic deformability of the magnesium particles containing the boron is degraded. Therefore, many voids oriented to the direction perpendicular to the axial direction of the wire are formed without sufficient elongation in the process of the drawing, and thus a filament having bad continuousness is obtained. The voids remain even after the heat treatment and results in a decrease in critical current density. The number density of the voids is very low in Wire-MR, and this suggests that the cassette rolling is effective to block the voids.
The conditions of a planetary ball mill process for preparing the mixed powder are described in detail above; however, what is important is that powder having a structure, in which magnesium as the matrix contains boron, is used. When the powder having the structure is obtained, regardless of conditions of the planetary ball mill process, a method other than the planetary ball mill process maybe used. In the planetary ball mill process, the smaller the number of rotations, the smaller the revolution radius, the lower the ratio of total weight of balls to total weight of powder, the larger the inner diameter of the ball, and the shorter the processing time, the more the magnesium and the boron are mixed as maintaining the original shapes. On the other hand, in the planetary ball mill process, when the number of rotations is too large, the revolution radius is too large, the ratio of total weight of balls to total weight of powder is too high, the inner diameter of the ball is too small, and the processing time is too long, the magnesium and the boron react with each other, and MgB2 is produced. Hence, such parameters need to be set within an appropriate range in the planetary ball mill process. NPL 6 discloses a relationship between the conditions of the planetary ball mill process and the mixing energy and discloses that the mixing is performed with energy of 108 J/kg per unit weight of powder, thereby producing a phase of MgB2 during the mixing, and such powder is used, thereby increasing the critical current density of the MgB2 wire. However, the present invention significantly differs from NPL 6 in that the mixing energy in the present invention is lower than 107 J/kg, and thus the mixing is performed in a range in which the production of MgB2 does not occur. In addition, it is checked that production of MgB2 does not actually occur in the powder after the substantial mixing.
Here, the process is referred to as the cassette rolling; however, the process may be referred to as various ways such as a roll forming process, roll forming, cold roll forming, and cold rolling. All of the processes are performed by causing a target object to pass between a plurality of rotating processing jigs and performing deformation processing (diameter reduction). Compared to the drawing in which the wire receives the force from the fixed dies, the cassette rolling is considered to be effective in that a small frictional force is generated between the target object and the dies, damage to filling powder is small because the target object is elongated while the center of the target object is compressed, and the powder is better compressed to be densified.
The high critical current density is realized by adding the cassette rolling to the wire subjected to the mechanical milling method; however, the characteristics of the microstructure are that the number of coarse void is small (n is small) and the coarse voids are oriented to a direction perpendicular to a longitudinal direction of the wire (θM is large).
In Example 1, the outer diameter was reduced from 18.0 mm to 0.8 mm in the drawing, and the outer diameter was reduced from 0.8 mm to 0.5 mm in the cassette rolling. In other words, the processing method was switched during the reduction at the diameter of 0.8 mm, and thereby it was checked that n is small. In the example, the outer diameter, where the processing method was switched, was changed. As a result, when the outer diameter, where the processing method was switched, was larger, it was observed that n tend to be smaller. However, even in a case where the entire process is configured of the cassette rolling, a value of n is 5 mm−2. In addition, in a condition in which n exceeds 500 mm−2, the critical current density is not substantially changed from that of Wire-I, and thus employment of the mechanical milling method is not highly superior. In addition, regarding the value of θM, no systematic change is observed with respect to the outer diameter where the processing method is switched, and an evaluated sample at this time satisfies θM≥50°.
Conditions of the number density and shapes of voids are described. Wire-I, Wire-M, and Wire-MR were representative examples; however, as a result of preparing the wires a plurality of times, it was found that the wires prepared under the same conditions has unique characteristics. In both of a case where the powder is mixed by the ball mill device and a case where the powder is mixed by the planetary ball mill device (mechanical milling), the number density of voids is within a numerical value of about 1.0×103 mm−2 or higher. In the case where the powder is mixed by the planetary ball mill device, the number density of voids varies within a range of 5 to 500 mm−2 through a step of reducing the diameter of the metal tube by further causing the metal tube filled with the mixed powder to pass between the plurality of rotating processing jigs.
In the case where the powder is mixed by the ball mill device, an average value of angles (defined from 0 to 90 degrees) formed between the major axis of each of the voids and the axis of the wire (or the precursor) is smaller than 50 degrees. In the case where the powder is mixed by the planetary ball mill device (mechanical milling), the average value of the angles is 50 degrees or larger.
As described above, a difference in directions of the voids is due to a difference in mechanism of forming the voids. In the case where the powder is mixed by the ball mill device, the energy that is applied to the powder is low, and thus the mixing is performed as magnesium and boron maintain their original shapes. When the metal tube is filled with the mixed powder and is subjected to the drawing, the soft magnesium is stretched and elongated in the longitudinal direction of the wire. Since the magnesium is diffused into the regions of the boron powder by the heat treatment, and MgB2 is produced, the regions in which the magnesium is originally present is changed to voids. The voids reflect the original shape of the magnesium and has a shape extending in the longitudinal direction of the wire, and an angle formed between the major axis of the void and the wire is small. On the other hand, in the case where the powder is mixed by the planetary ball mill device, the energy that is applied to the powder is high, and thus boron particles are kneaded in magnesium. Particles obtained by dispersing boron into a parent phase of magnesium is harder than pure magnesium particles and are difficult to perform plastic deformation. When the process is performed by filling the metal tube with the mixed powder, gaps are likely to be formed between powders adjacent in the longitudinal direction of the wire. In particular, since a force of a tensile component in the longitudinal direction of the wire is strong in the drawing, the voids between the powders are remarkably formed. Since the process proceeds such that the powder is stretched in the longitudinal direction while being crushed in a radial direction of the wire in the cassette rolling, slight deformation occurs even in hard powder, gaps between powder is filled, and thus the number density of voids is small.
It has been known that a crystalline boron site is substituted with carbon atoms in MgB2, thereby shortening a mean free path of electrons, and the critical current density of a high-magnetic field range is improved by improving an upper critical field. In the example, boron carbide powder having a grain size of 50 nm was added. The powder was weighed so as to obtain composition of Mg+1.80B+0.04B4C, and a wire was prepared in the same method of preparing Wire-MR.
In Example 3, fine boron carbide powder was added. Here, the added substance is not limited to the boron carbide, the same effect is obtained even when carbon powder or metallic carbide powder is added. In general, substitution efficiency of carbon depends on a grain size or a type of added material; however, since the powder is mixed by applying high energy by the planetary ball mill device in the mechanical milling method, the substitution efficiency tends to be high even with a material of which substitution efficiency is degraded in a common mixing method and is not suitable for the added material.
In the comparative example, the mechanical milling method is applied to manufacturing of a multi-core wire.
A copper-iron composite tube having an outer diameter of 18 mm and an inner diameter of 13 mm was prepared. The copper-iron composite tube is formed of copper on an outer side and iron on an inner side thereof. After the composite tube is filled with mixed powder M, the composite tube is subjected to the drawing to obtain the outer diameter of 12 mm. Next, a wire was processed to have a hexagonal cross section having an opposite side length of 10.2 mm through hexagonal dies, and a hexagonal wire was prepared. Eight hexagonal wires were disposed around a hexagonal copper rod having a cross-sectional shape, in which an opposite side length was 10.2 mm. After an outer side of the eight hexagonal wires was covered with a copper tube having an outer diameter of 40 mm and an inner diameter of 32 mm, a copper wire was inserted into a gap, and an embedded member was prepared. This embedded member was reduced to have an outer diameter of 8 mm in the drawing and to have an outer diameter of 1.5 mm in the cassette rolling, and a multi-core wire was prepared. Heat treatment was performed on the multi-core wire in conditions of a temperature of 600° C. for three hours in an argon atmosphere, in order to produce MgB2.
In Comparative Example 2, materials of an outer-layer member of the hexagonal wire, the hexagonal rod at the center, and the outer-layer member of the embedded member were changed, and a multi-core wire was prepared. The outer-layer member of the hexagonal wire and the hexagonal rod at the center are made of iron, and the outer-layer member of the embedded member is a Monel-copper composite tube. Here, the Monel-copper composite tube is formed of Monel on an outer side and copper on an inner side thereof.
The eight MgB2 filaments had substantially the same shape, no particular breaking was recognized even in the iron on the outer circumference of the MgB2 filament, and it was found that good sectional shapes are obtained.
Deformability of the mixed powder prepared by the mechanical milling method is degraded because boron is contained in magnesium as described above. Therefore, the mixed powder pierces the barrier layer 14 in the process in some cases. Form a result of this time, when all of the MgB2 filaments 15 have a configuration shown in
It is important that a material of the barrier layer 14 does not substantially react with the magnesium when the heat treatment for producing MgB2 is performed. In a case of a configuration in which the material that reacts with the magnesium is brought into contact with the MgB2 filament, a lack of magnesium for producing MgB2 occurs. Examples of materials which do not substantially react with magnesium include niobium, tantalum, titanium, and the like, in addition to iron, and the materials may be used as the material for a main component of the barrier layer 14.
In a case where a material of the outermost layer is soft like copper, the MgB2 filament 15 is likely to have a defect in shape, and covering the stabilizing layer 16 with a high-strength material such as Monel as in the example is effective. Nickel, cupronickel, iron, or the like, in addition to Monel, may be used as a material of the outermost layer 17. It is preferable that the material of the outermost layer 17 has Vickers hardness higher than copper.
In the example, the multi-core wire having eight filaments is described; however, it is possible to call a wire having at least two filaments as the superconducting multi-core wire. In addition, the wire may have more than eight filaments. In the superconducting wire, the filament has a small diameter, and thus it is preferable that a large number of filaments are used such that it is possible to avoid a problem of magnetic instability or an AC loss. As an example,
In preparing the MgB2 wire using the mixed powder by the mechanical milling method, it is important to add the cassette rolling instead of the drawing. This is because the cassette rolling is effective to improve the filling rate of the mixed powder by the mechanical milling method after the deformability of the mixed powder is degraded. As long as there is a technique in which it is possible to improve the filling rate of the mixed powder by the mechanical milling method, there is no need to be limited to the cassette rolling.
For example, magnesium is hexagonal metal, and thus a sliding surface is limited. Therefore, it is difficult to perform processing on magnesium; however, when magnesium is heated to a temperature of 150° C. or above, the processibility is improved. The mixed powder obtained by the mechanical milling method has the structure in which boron is dispersed into the matrix of magnesium. Therefore, when the deformability of the matrix is improved by warm processing, the processibility is improved. Hence, even without using the cassette rolling, it is possible to obtain good microstructure of MgB2 by warm drawing.
However, when a temperature for the warm drawing is too high, brittle MgB2 is produced by the reaction of magnesium and boron, and thus the processibility deteriorates. Therefore, it is preferable that the processing temperature is 500° C. at the highest.
In the example, two methods of preparing a superconducting coil using the superconducting wire of the embodiment are described.
A first method is a wind·and·react method, in which the superconducting wire is wound around a bobbin, and then the heat treatment is added as necessary. In a case of preparing the superconducting coil, it is not possible to increase an excitation speed of the coil when a short circuit occurs between the superconducting wires. Therefore, it is preferable that the superconducting wire is covered with an insulation material. In the wind·and·react method in which the heat treatment is performed in a post-process, a material such as glass material that withstands the heat treatment is used as the insulation material. Then, after the heat treatment is performed, the superconducting wire is fixed by performing resin impregnation as necessary.
A second method is a react·and·wind method, in which the superconducting wire is subjected to the heat treatment, and then the superconducting wire is wound around a bobbin. In this case, it is possible to cover the superconducting wire with the insulation material after the heat treatment, and it is possible to use enamel or the like that does not have heat resistance as the insulation material. After the superconducting wire is wound around the bobbin, the superconducting wire is fixed by performing resin impregnation as necessary.
In the example, a configuration of an MRI 200 using the superconducting wire of the embodiment is described.
A superconducting coil 102 using the superconducting wire, along with a persistent current circuit switch 103, is stored in a cryostat 109 and is cooled in a refrigerant or a refrigerator. Persistent current flowing in a circuit that makes the superconducting coil 102 and the persistent current circuit switch 103 generates a magnetostatic field having high time stability at a position of a measurement target. The higher the magnetostatic field intensity, the higher the nuclear magnetic resonance, and the frequency resolution is improved. A time-varying current is supplied to a gradient coil 111 from an amplifier 112 for a gradient magnetic field, and a magnetic field having a spatial distribution is generated at a position of a measurement target 110. Further, an oscillating field having a nuclear magnetic resonance frequency is applied to the measurement target 110 by using a radio frequency (RF) antenna 113 and a RF transmitting/receiving device 114, a resonance signal that is emitted from the measurement target is received, and it is possible to perform tomographic imaging of the measurement target.
In the example, a vertical magnetic field open MRI using the superconducting wire of the embodiment is described.
The MRI includes a pair of magnetostatic field generating units 121 and a connecting member 122, the units and the member are connected such that a central axis Z directing a vertical magnetic field is a rotation target axis. A space formed by the pair of magnetostatic field generating units and the connecting member is referred to as an imaging region 123. A gradient magnetic field generating portion is present in a state in which the imaging region is narrowed. In addition, the MRI includes a bed 126 on which the measurement target is placed and a transport mechanism 127 that transmits a measurement target 125 to the imaging region. Further, the MRI includes a RF oscillator 128 that irradiates the imaging region with an electromagnetic wave having resonance frequency which cause a nuclear magnetic resonance phenomenon to the measurement target, a receiving coil 129 that receives a nuclear magnetic resonance signal, a control device 130 that controls units of the MRI, and an analysis device 131 that analyzes the signal, as the other constituent units not shown in the perspective view.
The pair of magnetostatic field generating units each includes the superconducting coil and generates a uniform magnetostatic field in the imaging region by the superconducting coil. The gradient magnetic field generating portion superimposes gradient magnetic fields in three directions which are orthogonal to the imaging region by any case of switching, on the uniform magnetostatic field such that the magnetic field intensity is gradient in the imaging region. The superimposed gradient magnetic fields imparts positional information to the nuclear magnetic resonance signal, the nuclear magnetic resonance phenomenon appears in a region of interest (a slice plane having a thickness of 1 mm in usual) over the imaging region, and an tomographic image of the measurement target is achieved.
Here, an example of the vertical magnetic field open MRI is described; however, the embodiment can be also applied to a horizontal magnetic field type MRI. In addition, the embodiment can be also applied to a nuclear magnetic resonance (NMR) analyzing apparatus.
The MgB2 wire according to the present invention has a high filling rate of MgB2 and the high critical current density. In a case where a superconducting device such as MRI by using the MgB2 wire is prepared, the following effects are achieved. Since it is possible to perform an operation with high current density, it is possible to reduce material costs of the wires, and this results in a cost reduction of the superconducting device. In addition, since it is possible to perform the operation at a higher temperature, it is possible to reduce a cost for cooling such as electricity charges of the refrigerator. Further, there is no need to use liquid helium, thereby making it simple to handle the device, simplifying a liquid helium tank or an insulation structure. Therefore, it is possible to reduce costs of the superconducting device and to expand a space that a subject enters in the MRI.
1: dies
2: hole
3: roll
4: roll fixing jig
5: groove
6: filament
7: metal outer-layer member
8: void
9: magnesium particles
10: region filled with boron particles
11: uniform structure
12: boron particles
13: matrix of magnesium
14: barrier layer
15: MgB2 filament
16: stabilizing layer
17: outermost layer
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-013904 | Jan 2016 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2017/000370 | 1/10/2017 | WO | 00 |